Lean reduction of NO by C3H6 over Ag/alumina derived from Al2O3, AlOOH and Al(OH)3

The effectiveness of Ag/Al₂O₃ catalyst depends greatly on the alumina source used for preparation. A series of alumina-supported catalysts derived from AlOOH, Al₂O₃, and Al(OH)₃ was studied by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), ultraviolet–visible (UV–vis) spectroscopy, diffuse reflectance infrared Fourier transform (DRIFT) spectroscopy, O₂, NO + O₂-temperature programmed desorption (TPD), H₂-temperature programmed reduction (TPR), thermal gravimetric analysis (TGA) and activity test, with a focus on the correlation between their redox properties and catalytic behavior towards C₃H₆-selective catalytic reduction (SCR) of NO reaction. The best SCR activity along with a moderated C₃H₆ conversion was achieved over Ag/Al₂O₃ (I) employing AlOOH source. The high density of Ag–O–Al species in Ag/Al₂O₃ (I) is deemed to be crucial for NO selective reduction into N₂. By contrast, a high C₃H₆ conversion simultaneously with a moderate N₂ yield was observed over Ag/Al₂O₃ (II) prepared from a γ-Al₂O₃ source. The larger particles of Ag_mO (m > 2) crystallites were believed to facilitate the propene oxidation therefore leading to a scarcity of reductant for SCR of NO. An amorphous Ag/Al₂O₃ (III) was obtained via employing a Al(OH)₃ source and 500 °C calcination exhibiting a poor SCR performance similar to that for Ag-free Al₂O₃ (I). A subsequent calcination of Ag/Al₂O₃ (III) at 800 °C led to the generation of Ag/Al₂O₃ (IV) catalyst yielding a significant enhancement in both N₂ yield and C₃H₆ conversion, which was attributed to the appearance of γ-phase structure and an increase in surface area. Further thermo treatment at 950 °C for the preparation of Ag/Al₂O₃ (V) accelerated the sintering of Ag clusters resulting in a severe unselective combustion, which competes with SCR of NO reaction. In view of the transient studies, the redox properties of the prepared catalysts were investigated showing an oxidation capability of Ag/Al₂O₃ (II and V) > Ag/Al₂O₃ (IV) > Ag/Al₂O₃ (I) > Ag/Al₂O₃ (III) and Al₂O₃ (I). The formation of nitrate species is an important step for the deNO_x process, which can be promoted by increasing O₂ feed concentration as evidenced by NO + O₂-TPD study for Ag/Al₂O₃ (I), achieving a better catalytic performance.     

On the nature of the silver phases of Ag/Al2O3 catalysts for reactions involving nitric oxide

The nature of the silver phases of Ag/Al₂O₃ catalysts (prepared by silver nitrate impregnation followed by calcination) was investigated by X-ray diffractograms (XRD), transmission electron microscopy (TEM) and UV–VIS analyses and related to the activity of the corresponding materials for the oxidation of NO to NO₂. The UV–VIS spectrum of the 1.2 wt.% Ag/Al₂O₃ exhibited essentially one band associated with Ag⁺ species and the NO₂ yields measured over this material were negligible. A 10 wt.% Ag/Al₂O₃ material showed the presence of oxidic species of silver (as isolated Ag⁺ cations and silver aluminate), but the UV–VIS data also revealed the presence of some metallic silver. The activity for the NO oxidation to NO₂ of this sample was moderate. The same 10% sample either reduced in H₂ or used for the C₃H₆-selective catalytic reduction (SCR) of NO showed a significantly larger proportion of silver metallic phases and these samples displayed a high activity for the formation of NO₂. These data show that the structure and nature of the silver phases of Ag/Al₂O₃ catalysts can markedly change under reaction feed containing only a fraction of reducing agent (i.e. 500 ppm of propene) in net oxidizing conditions (2.5% O₂). The low activity for N₂ formation during the C₃H₆-SCR of NO (reported in an earlier study) over the high loading sample can, therefore, be related to the presence of metallic silver, which is yet a good catalyst for NO oxidation to NO₂. The reverse observations apply for the oxide species observed over the low loading sample, which is a good SCR catalyst but do not oxidize NO to NO₂.     

Selective catalytic reduction of NO by C3H8 over CoOx/Al2O3: An investigation of structure–activity relationships

A series of CoO_x/Al₂O₃ catalysts was prepared, characterized, and applied for the selective catalytic reduction (SCR) of NO by C₃H₈. The results of XRD, UV–vis, IR, Far-IR and ESR characterizations of the catalysts suggest that the predominant oxidation state of cobalt species is +2 for the catalysts with low cobalt loading (≤2 mol%) and for the catalysts with 4 mol% cobalt loading prepared by sol–gel and co-precipitation. Co₃O₄ crystallites or agglomerates are the predominant species in the catalysts with high cobalt loading prepared by incipient wetness impregnation and solid dispersion. An optimized CoO_x/Al₂O₃ catalyst shows high activity in SCR of NO by C₃H₈ (100% conversion of NO at 723 K, GHSV: 10,000 h⁻¹). The activity of the selective catalytic reduction of NO by C₃H₈ increases with the increase of cobalt–alumina interactions in the catalysts. The influences of cobalt loading and catalyst preparation method on the catalytic performance suggest that tiny CoAl₂O₄ crystallites highly dispersed on alumina are responsible for the efficient catalytic reduction of NO, whereas Co₃O₄ crystallites catalyze the combustion of C₃H₈ only.     

Effect of hydrogen on reaction intermediates in the selective catalytic reduction of NOx by C3H6

Selective catalytic reduction of NO_x by C₃H₆ in the presence of H₂ over Ag/Al₂O₃ was investigated using in situ DRIFTS and GC–MS measurements. The addition of H₂ promoted the partial oxidation of C₃H₆ to enolic species, the formation of –NCO and the reactions of enolic species and –NCO with NO_x on Ag/Al₂O₃ surface at low temperatures. Based on the results, we proposed reaction mechanism to explain the promotional effect of H₂ on the SCR of NO_x by C₃H₆ over Ag/Al₂O₃ catalyst.     

Enhanced activity of metal oxide-doped Ga2O3–Al2O3 for NO reduction by propene

Effect of additives, In₂O₃, SnO₂, CoO, CuO and Ag, on the catalytic performance of Ga₂O₃–Al₂O₃ prepared by sol–gel method for the selective reduction of NO with propene in the presence of oxygen was studied. As for the reaction in the absence of H₂O, CoO, CuO and Ag showed good additive effect. When H₂O was added to the reaction gas, the activity of CoO-, CuO- and Ag-doped Ga₂O₃–Al₂O₃ was depressed considerably, while an intensifying effect of H₂O was observed for In₂O₃- and SnO₂-doped Ga₂O₃–Al₂O₃. Of several metal oxide additives, In₂O₃-doped Ga₂O₃–Al₂O₃ showed the highest activity for NO reduction by propene in the presence of H₂O. Kinetic studies on NO reduction over In₂O₃–Ga₂O₃–Al₂O₃ revealed that the rate-determining step in the absence of H₂O is the reaction of NO₂ formed on Ga₂O₃–Al₂O₃ with C₃H₆-derived species, whereas that in the presence of H₂O is the formation of C₃H₆-derived species. We presumed the reason for the promotional effect of H₂O as follows: the rate for the formation of C₃H₆-derived species in the presence of H₂O is sufficiently fast compared with that for the reaction of NO₂ with C₃H₆-derived species in the absence of H₂O. Although the retarding effect of SO₂ on the activity was observed for all of the catalysts, SnO₂–Ga₂O₃–Al₂O₃ showed still relatively high activity in the lower temperature region.     

Surface properties and reactivity of Cu/γ-Al2O3 catalysts for NO reduction by C3H6: Influences of calcination temperatures and additives

The influences of calcination temperatures and additives for 10 wt.% Cu/γ-Al₂O₃ catalysts on the surface properties and reactivity for NO reduction by C₃H₆ in the presence of excess oxygen were investigated. The results of XRD and XPS show that the 10 wt.% Cu/γ-Al₂O₃ catalysts calcined below 973 K possess highly dispersed surface and bulk CuO phases. The 10 wt.% Cu/γ-Al₂O₃ and 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalysts calcined at 1073 K possess a CuAl₂O₄ phase with a spinel-type structure. In addition, the 10 wt.% La–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K possesses a bulk CuO phase. The result of NO reduction by C₃H₆ shows that the CuAl₂O₄ is a more active phase than the highly dispersed and bulk CuO phase. However, the 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K possesses significantly lower reactivity for NO reduction than the 10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K, although these catalysts possess the same CuAl₂O₄ phase. The low reactivity for NO reduction for 10 wt.% Mn–10 wt.% Cu/γ-Al₂O₃ catalyst calcined at 1073 K is attributed to the formation of less active CuAl₂O₄ phase with high aggregation and preferential promotion of C₃H₆ combustion to CO_x by MnO₂. The engine dynamometer test for NO reduction shows that the C₃H₆ is a more effective reducing agent for NO reduction than the C₂H₅OH. The maximum reactivity for NO reduction by C₃H₆ is reached when the NO/C₃H₆ ratio is one.     

Mean field modelling of NOx storage on Pt/BaO/Al2O3

A mean field model, for storage and desorption of NO_x in a Pt/BaO/Al₂O₃ catalyst is developed using data from flow reactor experiments. This relatively complex system is divided into five smaller sub-systems and the model is divided into the following steps: (i) NO oxidation on Pt/Al₂O₃; (ii) NO oxidation on Pt/BaO/Al₂O₃; (iii) NO_x storage on BaO/Al₂O₃; (iv) NO_x storage on Pt/BaO/Al₂O₃ with thermal regeneration and (v) NO_x storage on Pt/BaO/Al₂O₃ with regeneration using C₃H₆. In this paper, we focus on the last sub-system. The kinetic model for NO_x storage on Pt/BaO/Al₂O₃ was constructed with kinetic parameters obtained from the NO oxidation model together with a NO_x storage model on BaO/Al₂O₃. This model was not sufficient to describe the NO_x storage experiments for the Pt/BaO/Al₂O₃, because the NO_x desorption in TPD experiments was larger for Pt/BaO/Al₂O₃, compared to BaO/Al₂O₃. The model was therefore modified by adding a reversible spill-over step. Further, the model was validated with additional experiments, which showed that NO significantly promoted desorption of NO_x from Pt/BaO/Al₂O₃. To this NO_x storage model, additional steps were added to describe the reduction by hydrocarbon in experiments with NO₂ and C₃H₆. The main reactions for continuous reduction of NO_x occurs on Pt by reactions between hydrocarbon species and NO in the model. The model is also able to describe the reduction phase, the storage and NO breakthrough peaks, observed in experiments.     

Influence of BaO on Pd/Al2O3-based catalysts in C2H4 and CO oxidation as well as in NO reduction

In this study, Pd/Al₂O₃ and Pd/BaO/Al₂O₃ metallic monoliths were used to investigate the effect of BaO in C₂H₄ and CO oxidation as well as in NO reduction. A FT-IR gas analyser was used to study the activity of the catalysts. Several activity experiments carried out with dissimilar feedstreams revealed that BaO enhances CO and C₂H₄ oxidation as well as NO reduction reactions in rich conditions. This effect is due to BaO, which causes a decrease in the ethene poisoning of palladium. In lean conditions BaO is present in the form of Ba(OH)₂ which reacts with oxidised NO releasing water. Therefore, NO was stored during the lean reaction.     

The mechanism of SO2 effect on NO reduction with propene over In2O3/Al2O3 catalyst

An In₂O₃/Al₂O₃ catalyst shows high activity for the selective catalytic reduction of NO with propene in the presence of oxygen. The presence of SO₂ in feed gas suppressed the catalytic activity dramatically at high temperatures; however it was enhanced in the low temperature range of 473–573 K. In TPD and FT-IR studies, the formation of sulfate species on the surface of the catalyst caused an inhibition of NO_X adsorption sites, and the absorbance ability of NO was suppressed by the presence of SO₂, and the amount of ad-NO₃⁻ species decreased obviously. This leads to a decrease of catalytic activity at higher temperatures. However, addition of SO₂ enhanced the formation of carboxylate and formate species, which can explain the promotional effect of SO₂ at low temperature, because active C₃H₆ (partially oxidized C₃H₆) is crucial at low temperature.     

Improvement of catalytic activity and sulfur-resistance of Ag/TiO2–Al2O3 for NO reduction with propene under lean burn conditions

Ag-based catalysts supported on various metal oxides, Al₂O₃, TiO₂, and TiO₂–Al₂O₃, were prepared by the sol–gel method. The effect of SO₂ on catalytic activity was investigated for NO reduction with propene under lean burn condition. The results showed the catalytic activities were greatly enhanced on Ag/TiO₂–Al₂O₃ in comparison to Ag/Al₂O₃ and Ag/TiO₂, especially in the low temperature region. Application of different characterization techniques revealed that the activity enhancement was correlated with the properties of the support material. Silver was highly dispersed over the amorphous system of TiO₂–Al₂O₃. NO₃⁻ rather than NO₂⁻ or NOx reacted with the carboxylate species to form CN or NCO. NO₂ was the predominant desorption species in the temperature programmed desorption (TPD) of NO on Ag/TiO₂–Al₂O₃. More amount of formate (HCOO⁻) and CN were generated on the Ag/TiO₂–Al₂O₃ catalyst than the Ag/Al₂O₃ catalyst, due to an increased number of Lewis acid sites. Sulfate species, resulted from SO₂ oxidation, played dual roles on catalytic activity. On aged samples, the slow decomposition of accumulated sulfate species on catalyst surface led to poor NO conversion due to the blockage of these species on active sites. On the other hand, catalytic activity was greatly enhanced in the low temperature region because of the enhanced intensity of Lewis acid site caused by the adsorbed sulfate species. The rate of sulfate accumulation on the Ag/TiO₂–Al₂O₃ system was relatively slow. As a consequence, the system showed superior capability for selective adsorption of NO and SO₂ toleration to the Ag/Al₂O₃ catalyst.     

Catalytic oxidation of HCN over a 0.5% Pt/Al2O3 catalyst

The adsorption of HCN on, its catalytic oxidation with 6% O₂ over 0.5% Pt/Al₂O₃, and the subsequent oxidation of strongly bound chemisorbed species upon heating were investigated. The observed N-containing products were N₂O, NO and NO₂, and some residual adsorbed N-containing species were oxidized to NO and NO₂ during subsequent temperature programmed oxidation. Because N-atom balance could not be obtained after accounting for the quantities of each of these product species, we propose that N₂ and was formed. Both the HCN conversion and the selectivity towards different N-containing products depend strongly on the reaction temperature and the composition of the reactant gas mixture. In particular, total HCN conversion reaches 95% above 250 °C. Furthermore, the temperature of maximum HCN conversion to N₂O is located between 200 and 250 °C, while raising the reaction temperature increases the proportion of NO_x in the products. The co-feeding of H₂O and C₃H₆ had little, if any effect on the total HCN conversion, but C₃H₆ addition did increase the conversion to NO and decrease the conversion to NO₂, perhaps due to the competing presence of adsorbed fragments of reductive C₃H₆. Evidence is also presented that introduction of NO and NO₂ into the reactant gas mixture resulted in additional reaction pathways between these NO_x species and HCN that provide for lean-NO_x reduction coincident with HCN oxidation.     

Selective catalytic reduction of NO by hydrocarbons on Ga2O3/Al2O3 catalysts

Catalytic properties of supported gallium oxides have been examined for the selective reduction of NO by CH₄ in excess oxygen. The activity was greatly affected by the support; Ga₂O₃/Al₂O₃ (Al₂O₃ supported Ga₂O₃) and Ga₂O₃–Al₂O₃ mixed oxide exhibited high activity and selectivity as comparable to Ga-ZSM-5, while unsupported Ga₂O₃ and the other supported Ga₂O₃ were ineffective. For Ga₂O₃/Al₂O₃, the activity changed with Ga₂O₃ content, and was highest at about 30 wt% Ga₂O₃, which corresponds to a theoretical monolayer coverage. Gallium oxide highly dispersed on Al₂O₃ is considered to be responsible for the high activity and selectivity. The reaction characteristics of Ga₂O₃/Al₂O₃ were studied and compared with Ga-ZSM-5 and Co-ZSM-5. Ga₂O₃/Al₂O₃ exhibited the highest activity and selectivity at high temperature. In addition, Ga₂O₃/Al₂O₃ showed higher tolerance against water than Ga-ZSM-5. C₃H₈ and C₃H₆ were also evaluated as reducing agents, and Ga₂O₃/Al₂O₃ showed higher activity than Ga-ZSM-5 above 723 K achieving almost complete reduction of NO to N₂.     

Catalytic selective reduction of NO with propylene over Cu-Al2O3 catalysts: influence of catalyst preparation method

NO reduction to N₂ by C₃H₆ was investigated and compared over Cu-Al₂O₃ catalysts prepared by four different methods, namely, the conventional impregnation, co-precipitation, evaporation of a mixed aqueous solution, and xerogel methods. It was found that the catalyst preparation method as well as the Cu content exerts a significant influence on catalyst activity. For the catalysts prepared by the first three preparation methods, with the increase of Cu content from 5 to 15 wt%, the maximum NO reduction conversion decreased slightly, but the temperature for the maximum NO reduction also decreased. For the xerogel Cu-Al₂O₃, there was a significant decrease in NO reduction conversion with the increase of Cu content from 5 to 10 wt%. In the absence of water vapour, the Cu-Al₂O₃ catalyst prepared by the impregnation method exhibited the highest activity toward NO reduction. The purity of alumina support was found to be a crucial factor to the activity of the Cu-Al₂O₃ catalyst prepared by impregnation. In the presence of water vapour, a substantial decrease in NO conversion was observed for the Cu-Al₂O₃ catalysts prepared by the first three methods, especially for the impregnated Cu-Al₂O₃ catalyst. In contrast, the presence of water vapour showed only a minor influence on the xerogel 5 wt% Cu-Al₂O₃ and it showed the highest activity for NO reduction in the presence of 20% water vapour. The xerogel 5 wt% Cu-Al₂O₃ catalyst was also found to be less affected by a 5 wt% sulfate deposition than the Cu-Al₂O₃ catalysts prepared by other methods.     

NO reduction by CH4 in the presence of O2 over La2O3 supported on Al2O3

Dispersing La₂O₃ on δ- or γ-Al₂O₃ significantly enhances the rate of NO reduction by CH₄ in 1% O₂, compared to unsupported La₂O₃. Typically, no bend-over in activity occurs between 500° and 700°C, and the rate at 700°C is 60% higher than that with a Co/ZSM-5 catalyst. The final activity was dependent upon the La₂O₃ precursor used, the pretreatment, and the La₂O₃ loading. The most active family of catalysts consisted of La₂O₃ on γ-Al₂O₃ prepared with lanthanum acetate and calcined at 750°C for 10 h. A maximum in rate (mol/s/g) and specific activity (mol/s/m²) occurred between the addition of one and two theoretical monolayers of La₂O₃ on the γ-Al₂O₃ surface. The best catalyst, 40% La₂O₃/γ-Al₂O₃, had a turnover frequency at 700°C of 0.05 s⁻¹, based on NO chemisorption at 25°C, which was 15 times higher than that for Co/ZSM-5. These La₂O₃/Al₂O₃ catalysts exhibited stable activity under high conversion conditions as well as high CH₄ selectivity (CH₄ + NO vs. CH₄ + O₂). The addition of Sr to a 20% La₂O₃/γ-Al₂O₃ sample increased activity, and a maximum rate enhancement of 45% was obtained at a SrO loading of 5%. In contrast, addition of SO⁼₄ to the latter Sr-promoted La₂O₃/Al₂O₃ catalyst decreased activity although sulfate increased the activity of Sr-promoted La₂O₃. Dispersing La₂O₃ on SiO₂ produced catalysts with extremely low specific activities, and rates were even lower than with pure La₂O₃. This is presumably due to water sensitivity and silicate formation. The La₂O₃/Al₂O₃ catalysts are anticipated to show sufficient hydrothermal stability to allow their use in certain high-temperature applications.     

Promoting effects of CO2 on dehydrogenation of propane over a SiO2-supported Cr2O3 catalyst

The effects of carbon dioxide on the dehydrogenation of C₃H₈ to produce C₃H₆ were investigated over several Cr₂O₃ catalysts supported on Al₂O₃, active carbon and SiO₂. Carbon dioxide exerted promoting effects only on SiO₂-supported Cr₂O₃ catalysts. The promoting effects of carbon dioxide over a Cr₂O₃/SiO₂ catalyst were to enhance the yield of C₃H₆ and to suppress the catalyst deactivation.     

助剂Ba对Pd/Al_2O_3和Pt/Al_2O_3催化剂的C1-C3烷烃催化燃烧性能的影响

通过浸渍法制备了Al_2O_3负载的Pd和Pt催化剂,考察催化剂的甲烷、乙烷和丙烷催化燃烧活性,以及助剂Ba对催化性能的影响。对于Pd/Al_2O_3催化剂,加入Ba使活性物种PdO颗粒变大和还原温度升高,形成更稳定的PdO活性物种,是Pd-Ba/Al_2O_3催化剂活性提升的主要原因。对于Pt/Al_2O_3催化剂,加入Ba助剂使活性物种Pt0含量降低,PtO_x与Al_2O_3载体相互作用增强,使PtO_x物种更难被还原为Pt~0,导致Pt-Ba/Al_2O_3催化剂活性降低。Pd和Pt催化剂催化烷烃氧化反应活性规律一致:丙烷乙烷甲烷。Pd/Al_2O_3催化剂有利于C—H键活化,Pt/Al_2O_3催化剂有利于C—C键活化。Pt/Al_2O_3催化剂对C1-C3烷烃氧化活性的差别明显大于Pd/Al_2O_3催化剂。Pt/Al_2O_3催化剂对碳比例高的烷烃活性更高。     

Evidence for the formation, isomerization and decomposition of organo-nitrite and -nitro species during the NOx reduction by C3H6 on Ag/Al2O3

The formation of organo-nitrite and -nitro species (R-ONO and R-NO₂) as intermediates during the selective catalytic reduction (SCR) of NO_x by C₃H₆ over Ag/Al₂O₃ was investigated by temperature-programmed desorption (TPD) and in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS). The addition of KBr to Ag/Al₂O₃ catalyses the isomerization of R-NO₂ to R-ONO on KBr-Ag/Al₂O₃, which confirms the presence of R-NO₂ on Ag/Al₂O₃.     

Total oxidation of propene and propane over gold–copper oxide on alumina catalysts: Comparison with Pt/Al2O3

Oxidation of propene and propane to CO₂ and H₂O has been studied over Au/Al₂O₃ and two different Au/CuO/Al₂O₃ (4 wt.% Au and 7.4 wt.% Au) catalysts and compared with the catalytic behaviour of Au/Co₃O₄/Al₂O₃ (4.1 wt.% Au) and Pt/Al₂O₃ (4.8 wt.% Pt) catalysts. The various characterization techniques employed (XRD, HRTEM, TPR and DR-UV–vis) revealed the presence of metallic gold, along with a highly dispersed CuO (6 wt.% CuO), or more crystalline CuO phase (12 wt.% CuO).

A higher CuO loading does not significantly influence the catalytic performance of the catalyst in propene oxidation, the gold loading appears to be more important. Moreover, it was found that 7.4Au/CuO/Al₂O₃ is almost as active as Pt/Al₂O₃, whereas Au/Co₃O₄/Al₂O₃ performs less than any of the CuO-containing gold-based catalysts.

The light-off temperature for C₃H₈ oxidation is significantly higher than for C₃H₆. For this reaction the particle size effect appears to prevail over the effect of gold loading. The most active catalysts are 4Au/CuO/Al₂O₃ (gold particles less than 3 nm) and 4Au/Co₃O₄/Al₂O₃ (gold particles less than 5 nm).     

Influence of metal oxides on the catalytic behavior of Au/Al2O3 for the selective reduction of NOx by hydrocarbons

The reduction of NO by propene in the presence of excess oxygen over mechanical mixtures of Au/Al₂O₃ with a bulk oxide has been investigated. The oxides studied were: Co₃O₄, Mn₂O₃, Cr₂O₃, CuO, Fe₂O₃, NiO, CeO₂, SnO₂, ZnO and V₂O₅. Under lean C₃H₆-SCR conditions, these oxides (with the exception of SnO₂) convert selectively NO to NO₂. When mechanically mixed with Au/Al₂O₃, the Mn₂O₃ and Co₃O₄ oxides and, to a much greater extent, CeO₂ act synergistically with this catalyst greatly enhancing its SCR performance. It was found that their synergistic action is not straightforwardly related to their activity for NO oxidation to NO₂. The exhibited catalytic synergy may be due to the operation of either remote control or a bifunctional mechanism. In the later case, the key intermediate must be a short-lived compound and not the NO₂ molecule in gas-phase.     

Reactor and in situ FTIR studies of Pt/BaO/Al2O3 and Pd/BaO/Al2O3 NOx storage and reduction (NSR) catalysts

The reduction of NO under cyclic “lean”/“rich” conditions was examined over two model 1 wt.% Pt/20 wt.% BaO/Al₂O₃ and 1 wt.% Pd/20 wt.% BaO/Al₂O₃ NO_x storage reduction (NSR) catalysts. At temperatures between 250 and 350 °C, the Pd/BaO/Al₂O₃ catalyst exhibits higher overall NO_x reduction activity. Limited amounts of N₂O were formed over both catalysts. Identical cyclic studies conducted with non-BaO-containing 1 wt.% Pt/Al₂O₃ and Pd/Al₂O₃ catalysts demonstrate that under these conditions Pd exhibits a higher activity for the oxidation of both propylene and NO. Furthermore, in situ FTIR studies conducted under identical conditions suggest the formation of higher amounts of surface nitrite species on Pd/BaO/Al₂O₃. The IR results indicate that this species is substantially more active towards reaction with propylene. Moreover, its formation and reduction appear to represent the main pathway for the storage and reduction of NO under the conditions examined. Consequently, the higher activity of Pd can be attributed to its higher oxidation activity, leading both to a higher storage capacity (i.e., higher concentration of surface nitrites under “lean” conditions) and a higher reduction activity (i.e., higher concentration of partially oxidized active propylene species under “rich” conditions). The performance of Pt and Pd is nearly identical at temperatures above 375 °C.