焊接线能量对低碳贝氏体钢焊接接头性能的影响

根据低碳贝氏体钢焊接接头强韧性要求,选择所设计的一种烧结焊剂,采用不同的焊接线能量,对低碳贝氏体钢进行埋弧焊。通过金相分析和力学性能测试等方法,对其焊接接头的组织和性能进行了研究。结果表明:焊接线能量为26.86 kJ/cm时,焊接接头HAZ冲击韧性优异,达254 J,但焊缝区冲击韧性差,仅为86 J。而焊接线能量为29.45kJ/cm时,焊接接头的性能相对优异,焊缝区和HAZ的冲击功分别达167和159 J。在此焊接线能量下,焊缝区组织为粒状贝氏体,并且有弥散分布的夹杂物颗粒析出,单丝埋弧焊焊接线能量为29.45 k J/cm左右时最为适宜。     

低碳贝氏体钢焊接接头力学性能及缺陷分析

根据焊条电弧焊焊接接头抗拉强度和焊缝区冲击韧性试验结果及X射线探伤的焊接缺陷,采用秩和检验法对低碳贝氏体ADB610和WDB620钢进行对比分析研究。研究表明,在焊条电弧焊方法下,2种低碳贝氏体钢焊接接头的抗拉强度和冲击韧性值的分布与均值之间无显著性差异,焊接缺陷尺寸的分布和均值也无显著差异。     

低碳贝氏体钢双面埋弧焊焊接接头组织及硬度分析

对低碳贝氏体钢进行双面埋弧焊焊接,并采用光学显微镜和维氏硬度计对焊接接头的显微组织与维氏硬度进行研究。结果表明:低碳贝氏体钢双面埋弧焊后,接头反面焊的焊缝宽度和余高比正面焊的要高,组织为针状铁素体和粒状贝氏体;HAZ的组织为贝氏体铁素体和粒状贝氏体;母材区域的组织为板条铁素体和粒状贝氏体;HAZ熔合线附近的硬度值最高,远离熔合线硬度降低,并逐渐接近母材金属的硬度;Mn元素的偏析增加了边界阻尼,致使晶粒长大倾向降低,硬度值偏高。     

焊接线能量对高强钢焊接接头组织性能的影响

采用1.3、1.6、1.9 kJ/mm 3种不同线能量对960QT钢进行焊接，研究了线能量对960QT钢焊接接头组织和性能的影响。研究表明，随着线能量的增加，焊接接头强度下降，但塑性提高，焊缝冲击韧性变化不大，热影响区冲击韧性先降低后增大，热影响区冲击韧性均高于焊缝。对3种线能量下960QT高强钢的焊接接头进行金相分析，发现焊缝组织主要为针状铁素体和粒状贝氏体。随着线能量的增加，针状铁素体发生粗化，数量相对减少，粒状贝氏体数量增多。焊接接头热影响区的金相组织主要为板条M/B和粒状贝氏体。随着焊接线能量的增大，冷却速率减小，粒状贝氏体组织数量相对增加，而板条贝氏体组织的数量逐渐减少。     

焊接线能量对高强钢焊接接头组织性能的影响

采用1.3、1.6、1.9 kJ/mm 3种不同线能量对960QT钢进行焊接,研究了线能量对960QT钢焊接接头组织和性能的影响。研究表明,随着线能量的增加,焊接接头强度下降,但塑性提高,焊缝冲击韧性变化不大,热影响区冲击韧性先降低后增大,热影响区冲击韧性均高于焊缝。对3种线能量下960QT高强钢的焊接接头进行金相分析,发现焊缝组织主要为针状铁素体和粒状贝氏体。随着线能量的增加,针状铁素体发生粗化,数量相对减少,粒状贝氏体数量增多。焊接接头热影响区的金相组织主要为板条M/B和粒状贝氏体。随着焊接线能量的增大,冷却速率减小,粒状贝氏体组织数量相对增加,而板条贝氏体组织的数量逐渐减少。     

焊接线能量对WEL-TEN80A钢焊接接头力学性能的影响

分别采用手工电弧焊及埋弧自动焊两种焊接方法，研究了焊接线能量对800MPa级高强钢WELTEN80A的焊接接头性能的影响规律，并确定了其板厚分别为20mm和40mm的焊接最佳线能量范嗣。     

低碳贝氏体钢回火微观组织对钢板性能的影响

通过对低碳贝氏体钢不同回火工艺下金相组织与性能的研究，了解该类型钢的回火特性。在620℃回火时出现硬度峰值，在710℃回火出现硬度谷值，峰值与谷值相差不到20HV10，说明其具有良好的回火稳定性；并得出二次析出和回火组织的转变是造成回火硬度变化的主要原因。     

不同热处理状态9%Ni钢焊接接头的组织与韧性

针对两种不同热处理工艺获得的9%Ni钢,采用手工立焊进行焊接并对其接头的组织和韧性进行了研究.经-196℃低温夏比V形缺口冲击试验、金相组织分析,结果表明,双相区热处理后的9%Ni钢.其接头的低温韧性均高于调质热处理9%Ni钢焊接接头的低温韧性.母材及焊接热影响区中的组织形态及逆转奥氏体的分布是决定接头低温韧性的主要因素;焊缝金属的低温韧性主要与焊条熔敷金属的成分有关.采用小热输入、多层焊、低的层间温度,都可使两种9%Ni钢焊接接头获得较高的低温冲击韧性.     

异种奥氏体钢焊接接头显微组织结构分析

研究了高锰奥氏体钢焊接接头性能和显微组织结构,在熔合线上不同合金元素成线性过渡,其显微组织与母材和焊缝组织相同,均为奥氏体加铁素体,显微硬度分析也证实了这点。说明用Ｎｉ－Ｃｒ奥氏体钢焊接材料焊接高锰奥氏体钢,可获得性能优良的焊接接头。     

焊接方法对9Ni钢焊接接头组织及低温韧性的影响

通过低温冲击试验、断口扫描和金相组织观察,研究了钨极氩弧焊和手工电弧焊两种焊接方法对9Ni钢焊接接头低温韧性的影响.结果表明,钨极氩弧焊焊缝和热影响区组织细小,断口韧窝尺寸大而深,使接头低温韧性高于手工焊接头.实验结果对9Ni钢的实际焊接提供了理论依据,对正确制定焊接工艺具有一定的指导意义.     

线能量对2205双相不锈钢焊接接头耐蚀性和韧性的影响

针对2205双相不锈钢材料，研究了线能量对其焊接接头耐蚀性和冲击韧度的影响，推荐出了12．7mm壁厚材料的焊接线能量范围，且用于某天然气管道T程现场焊接。     

热输入对TCS不锈钢焊接热影响区组织的影响

针对新型铁路车辆用TCS铁素体不锈钢，研究了热输入对其焊接热影响区粗晶区组织特征的影响，并以此提出了其合理的焊接热输入范围为5．8～8．3kJ／cm。     

Investigation on Microstructure and Impact Toughness of Different Zones in Duplex Stainless Steel Welding Joint

This paper investigated on microstructure and impact toughness of different zones in duplex stainless steel welding joint. High-temperature heat-affected zone (HTHAZ) contained coarse ferrite grains and secondary precipitates such as secondary austenite, Cr₂N, and sigma. Intergranular secondary austenite was prone to precipitation in low-temperature heat-affected zone (LTHAZ). Both in weld metal (WM) and in HTHAZ, the austenite consisted of different primary and secondary austenite. The ferrite grains in base metal (BM) presented typical rolling texture, while the austenite grains showed random orientation. Both in the HTHAZ and in the LTHAZ, the ferrite grains maintained same texture as the ferrite in the BM. The secondary austenite had higher Ni but lower Cr and Mo than the primary austenite. Furthermore, the WM exhibited the highest toughness because of sufficient ductile austenite and unapparent ferrite texture. The HTHAZ had the lowest toughness because of insufficient austenite formation in addition to brittle sigma and Cr₂N precipitation. The LTHAZ toughness was higher than the BM due to secondary austenite precipitation. In addition, the WM fracture was dominated by the dimple, while the cleavage was main fracture mode of the HTHAZ. Both BM and LTHAZ exhibited a mixed fracture mode of the dimple and quasi-cleavage.     

焊接线能量对T91钢焊缝组织及硬度的影响

采用不同的焊接线能量对T91钢进行焊接,并对回火后的焊接接头分别采用三氯化铁盐酸水溶液和硝酸酒精溶液浸蚀,微观组织观察表明,不同焊接线能量下经三氯化铁盐酸水溶液浸蚀后焊接接头均为板条马氏体组织,而经硝酸酒精浸蚀后焊接接头均为索氏体组织,晶界清晰,大线能量焊接会引起焊缝及热影响区晶粒边界碳化物聚集.硬度测试结果表明,大线能量焊接热处理后焊接接头的硬度高于小线能量焊接的焊接接头硬度.     

T92钢焊接接头的组织和韧性研究

通过硬度试验、冲击试验、断口扫描和金相组织脱察,研究了T92钢焊接接头的韧性与组织的关系.结果表明,焊缝的硬度值高,冲击功值低,其断口形貌与焊接热影响区的有显著差异,而焊缝金属组织中粗大的马氏体板条及板条束是导致焊缝韧性明显低于HAZ的主要因素之一.     

Q460NH耐候钢在不同焊接热输入条件下的冲击性能及显微组织变化

为研究不同焊接输入条件对海面建筑用Q460NH钢的冲击性能的影响,分别在不同热输入条件下对Q460NH钢进行焊接,并在-30℃低温对Q460NH钢的冲击功和显微组织进行测试和观察。结果表明:当热输入为21 k J/cm时,Q460NH钢的冲击功达到最大值84 J;当热输入大于21 k J/cm时,Q460NH钢的冲击功呈现下降趋势。针状铁素体的面积分数随着热输入的增加呈先增加后减小的趋势,而侧板条铁素体和晶界铁素体的面积分数随热输入的增加呈先减小后增加的趋势。     

X80管线钢粗晶区在不同焊接热输入下的韧性

采用热模拟技术、力学性能测试手段及显微分析方法,研究了三种X80管线钢焊接粗晶区在不同焊接热输入(E)下冲击韧性和断裂韧性的变化规律.结果表明,当E＞30kJ/cm时,由于粗晶区中多边形铁素体和珠光体的形成,致使其韧性严重恶化;在E＜15kJ/cm条件下,由于马氏体的过饱和固溶作用以及较高冷却速度所形成的高应力状态,使得粗晶区的韧性受到损害;而在E=15～20 kJ/cm条件下,试验钢焊接粗晶区的主要组织为多位向分布的针状铁素体,表现出较好的韧性值.     

大线能量焊接用钢模拟热影响区的组织与性能

研究了一种低碳低合金600MPa级耐大线能量焊接用钢模拟大线能量输入焊接粗晶热影响区（简称CGHAZ）的微观组织及力学性能。结果表明，大线能量模拟CGHAZ具有优良的强韧性配合（σs≥490MPa，σb≥610MPa，-20℃时AKV≥47J）。模拟热循环过程中CGHAZ中的高温稳定的复合夹杂物促使针状铁素体的形成，针状铁素体的数量与输入线能量有关。奥氏体和铁素体晶粒大小及针状铁素体数量显著影响焊接粗晶热影响区的力学性能。     

镁合金TIG焊过程热输入对接头组织的影响

以AZ31镁合金为研究对象,分析了不同焊接热输入对TIG焊接头微观组织的影响.结果表明,当热输入较大时,熔池液态金属的高温停留时间过长,冷却速度慢,焊接接头的过热问题较为严重,从而造成焊缝金属的组织晶粒长大,热影响区的宽度明显变大;而热影响区的粗大晶粒,降低了接头的性能,是接头断裂的危险区.     

E40钢双丝埋弧焊焊缝在不同热输入条件下性能分析

采用我国自行研制的大热输入用钢E40,基于计算机技术在不同热输入条件下对E40进行双丝埋弧焊焊接,对不同条件下焊接热影响区和焊缝处的组织以及性能进行分析研究。结果表明,热输入量和焊缝焊接道次的合理搭配,便可以得到性能效果较好的焊接接头。