PTC型炭黑/高聚物导电复合材料的研究

正温系数导电高分子材料在工业中得到了广泛的应用。本文综述了炭黑／高聚物导电复合材料ＰＴＣ效应的影响因素,探讨了ＰＴＣ效应稳定化的途径。     

高分子PTC导电复合材料加工流变行为研究

以高分子PTC（正温度系数）导电材料LLDPE／CB、HDPE／CB、PVDF／CB为研究体系,考察了剪切速率、加工温度对复合材料加工流变行为的影响,并分析了3种体系的粘流活化等流变数据,得到了适于3种材料生产的加工条件。     

高密度聚乙烯／石墨PTC导电复合材料的研究

以高密度聚乙烯（PE—HD）为基体材料，选用四种不同粒径的石墨作为导电填充物探讨石墨粒径对复合体系PTC效应的影响，研究了石墨用量、增塑剂添加量和成核剂添加量对高密度聚乙烯佰墨复合体系电学性能及力学性能的影响。结果表明：选用50μm的石墨颗粒作为导电添加剂可以得到具有明显PTC强度的复合材料；正交实验最优化配比为高密度聚乙烯100g，石墨60g，邻苯二甲酸二辛酯25g，滑石粉12g；制备的复合材料弯曲强度为3．5MPa，PTC强度为6．4，与PE-HD／石墨复合材料相比弯曲强度减少了2／3，脆性明显下降，同时保持了较高的PTC强度，具有良好的综合性能。     

炭黑/高聚物导电复合材料PTC效应的研究

正温系数 (Positive Temperature Coefficient)导电高分子材料 (PTC材料 )在工业中得到了广泛的应用。本文探讨了炭黑 高聚物导电复合材料 PTC效应产生与衰退的机理 ,综述了其 PTC效应的影响因素。     

高抗冲聚苯乙烯/炭黑导电复合材料 PTC效应的研究

采用SEM、XRP、DSC和体积膨胀等手段对非结晶形HIPS／CB（聚苯乙烯／炭黑）导电复合材料的导电行为进行分析。实验结果表明，HIPS／CB导电复合材料的渗流区域较窄，炭黑含量为30～40g时，电阻发生急剧降低，在渗流阀值附近导电复合材料的电阻率变化最大，跃迁强度为2.2个数量级；HIPS／CB导电复合材料的PTC起始转变温度在85℃左右，与HIPS的玻璃化转变温度接近，HIPS作为非晶材料其体积膨胀较弱，并不足以单独解释PTC效益。     

聚乙烯/炭黑导电复合材料PTC特性的研究(Ⅱ)--辐射交联对导电复合材料PTC性能的影响

采用^60Coγ-射线对HDPE／CB导电复合材料进行辐射处理，研究了辐射剂量对于该复合材料室温电导率、PTC性能及稳定性的影响。结果发现，在50-300kGy范围内，随着辐射剂量的增加，复合材料的PTC强度增大，且复合材料的稳定性有所提高，NTC效应有所降低；同时，辐射交联对体系的室温电阻率影响不大。DSC测试表明，当辐射剂量为150kGy时，辐射处理对于HDPE的熔点、结晶度影响不大。     

聚乙烯／乙丙橡胶／炭黑高分子导电复合材料的制备

本发明提供了一种液体膨胀橡胶，首先将质量分数为50％～85％的POP和质量分数为1～40％的TDI以及质量分数为2％～40％的丁基橡胶加入反应釜中，在常压下升温至60～90℃，搅拌反应1～3h，降温停放，包装后作为甲组分待用。将质量分数为50％～85％的POP、质量分数为2％～30％的填料、质量分数为5％～30％的交联剂、质量分数为1％～15％的颜料、质量分数为1％～25％的增塑剂搅拌混合后，研磨至其粒度小于40μm，     

填充型多相聚合物导电复合材料的PTC效应

以聚丙烯和低密度聚乙烯共混物为基体,用碳黑为填充材料制备了复合导电材料,导电性能的测试表明多相复合体系的渗滤阈值低于两相复合体系的渗滤阈值。对复合材料PTC效应的分析以及对材料的热性能测试结果表明碳黑在共混体系中的分布。同时探讨了体系碳黑含量的变化对PTC效应的影响。     

高分子PTC材料（上）

综述了高分子ＰＴＣ材料近三十年来的进展,就材料各种电学现象、机理、影响因素及应用情况进行了讨论,并对材料存在的问题及发展方向提出了看法。     

CPE在PE／EVA／CB型PTC材料体系中的作用

本文以聚乙烯／乙烯－醋酸乙烯酯共聚物／炭黑（PE／EVA／CB）体系为研究对象,采用熔融共混挤出成型制样的方法,探讨了氯化聚乙烯（CPE）在体系中的稳定作用,结果表明,在体系中加入CPE可以起到相容剂的作用,能大大改善炭黑在聚合物中的分散,提高材料体系中各相间的结构稳定性,降低材料体系的电阻率,使炭黑和聚合物间的复合更为均一,从而可以在一定程度上提高材料的导电性及稳定性。并在体系中加入2．5％（质量百分比）的CPE时即可收到明显效果。     

具有原位导电微纤网络的CB/PET/PE复合材料的力学性能

在前期热塑性塑料原位成纤研究的基础上，尝试利用原位成纤方法制备炭黑(CB)／聚对苯二甲酸乙二醇酯(PET)／高密度聚乙烯(HDPE)原位导电微纤网络复合材料(CEMN)，以期增强复合体系的力学强度。通过对CEMN体系与CB／PE体系的力学性能测试发现，CEMN体系的拉伸强度低于普通CB/PE复合物。为增强复合体系的力学性能，应改变加工过程及降低体系中CB的用量。     

聚烯烃类弹性体导电复合材料的制备与性能研究

将炭黑(CB)和碳纤维(CF)导电粒子加入到新型聚丙烯弹性体(Vistamaxx)与聚丙烯(PP)基体树脂中,共混制备导电复合材料。通过体积电阻率测试、力学性能测试和加工流变性能测试,得到了体积电阻率最低为0.47Ω.cm,拉伸强度为6.6 MPa,断裂伸长率为250%,具有良好加工性能的导电复合材料。     

改性石墨烯对天然橡胶/丁腈橡胶复合材料热性能的影响

采用超声辅助超临界CO2方法制备石墨烯,经3-氨丙基三乙氧基硅烷(APTES)改性后,采用"预混合"的方法,得到硬脂酸/石墨烯母料。通过机械共混法制备天然橡胶(NR)/改性石墨烯(GNs)与丁腈橡胶(NBR)/GNs复合材料。通过分析复合材料的导热性能、热管理性能和压缩生热性能的变化情况,验证石墨烯的性能与硬脂酸/石墨烯"预混合"对石墨烯分散的影响。结果表明,添加3份GNs时,NRC-3、NBRC-3的导热性能分别提升了108%和194%,压缩温升降低了8. 9℃和9. 9℃。该方法制备的石墨烯导热性能优秀,硬脂酸/石墨烯的"预混合"有效改善了石墨烯在聚合物中的分散性。     

Aging and Thermal Studies on Epoxy Resin Modified by Epoxidized Novolacs

Epoxy resins are thermosetting polymers widely used for polymer composites, adhesives, high performance coatings, potting and encapsulation, and numerous other applications. These resins have excellent mechanical and electrical properties, low cure shrinkage, and good adhesion to most substrates. This study is an attempt to improve the thermal and aging characteristics of epoxy resin by blending with other multifunctional epoxies such as EPN and ECN. Bis-phenol A epoxy resins containing 2.5 to 20 wt% of epoxy novolac were cured in the presence of a polyamide hardener and tested for thermal and mechanical properties, hardness, water absorption, etc. Blends containing 10 to 15 wt% of epoxy novolac show substantial improvement in properties such as tensile strength, elongation, and energy absorbed to break. The novolac derived from p-cresol was better than that based on phenol in enhancing the properties. TGA, DSC, and DMA were employed for studying the thermal properties of the modified resin. The study reveals that modification using epoxy phenol and p-cresol novolac resins (EPN and ECN, respectively) improves the aging characteristics of the epoxy resin in addition to overall improvement of the mechanical properties.     

炭黑对橡胶补强机理的研究

本文从容积效应、橡胶链的有限伸长、分子链滑动，表面吸附等几方面对炭黑的补强机理加以研究，指出：炭黑对橡胶的补强机理是物理吸附与化学结合共同作用的结果。     

炭黑填充聚合物基PTC导电复合材料及制品的研究进展

介绍了PTC效应的几种主要机理,讨论了不同基体、填充物和加工工艺对此类复合材料PTC效应的影响,NTC效应产生的主要原因以及减缓或推迟NTC效应的方法,并对其商业推广应用进行了较为深入的探讨.     

Studies on Interfacial Characteristics of Highly Dispersible Silica Reinforced Epoxidized Natural Rubber Compounds

The present work examines the effect of two different specific surface areas of highly dispersible silica (HDS)-reinforced epoxidized natural rubber (ENR) composites. The influences of different blend ratio between ENRs consisting 25 and 50?mol% of epoxidation-based (ENR-25/ENR-50) composites was studied in detail. The primary objective is to investigate the interfacial area of HDS surface involved in filler-to-rubber interaction mechanisms for the better reinforcement. Notable improvement in overall properties of these green composites are corroborated with various meticulous characterization including cure characteristics, specific bound rubber content, physicomechanical, dynamic mechanical properties, etc. Increasing the specific surface area of HDS and their subsequent interface with ENR matrix invokes its superior dispersion. Small angle X-ray scattering (SAXS) has been used to analyze the particles network and clusters establishment in green composites. The present SAXS method provides a unique insight into the cluster formation according to the Beaucage model. However, SAXS results demonstrate that particles networks can be effectively suppressed by increasing specific surface area of HDS.     

LDPE／炭黑复合导电材料性能的研究

总结了１８２批西洋参的鉴别检验，其结果显示外观性状鉴别与薄层色谱鉴别结果相符率为９４．０％。因此西洋参真伪鉴别检验每批样品除进行状检验外还必须做薄层分析，以防止白参掺入或下错结论。