高速电弧喷涂铝涂层性能试验研究

本文对高速电弧喷涂铝涂层和普通电弧喷涂铝涂层进行了对比试验研究。结果表明：高速电弧喷涂粒子束更加集中,粒子的飞行速度显著提高,粒子的雾化效果明显改善。高速电弧喷滁铝涂层具有结合强度高、硬度高、孔隙率低、组织致密等特点。     

电弧喷涂防腐蚀涂层研究

介绍了电孤喷涂稀土铝、铝合金涂层抗腐蚀性能试验,高速电弧喷涂锌、铝涂层的防腐蚀性能试验结果.指出喷涂材料和喷涂设备的发展情况,提高了涂层的防腐蚀性能,使电弧喷涂能够在防腐蚀领域得到更广泛的应用.     

高速电弧喷涂镍铝打底层结构与性能研究

高速电弧喷涂技术是近年来发展起来的新型热喷涂技术，该技术具有优势，高效，低成本等特点，本文实验研究了高速电弧喷涂镍铝打底涂层的组织结构和力学性能，涂层的界面结合强度大于40MPa，显微硬度平均值为210HV，表面粗糙度表征参数Ra值为13．11um，涂层孔隙率为2．26％，涂层主要由镍铝合金和镍，铝氧化物组成，高速电弧喷涂镍铝涂层结合强度高，涂层组织致密，是优良的打底涂层。     

铝合金表面电弧喷涂铝涂层工艺与性能

采用电弧喷涂工艺在6061铝合金基体表面喷涂高纯铝涂层,利用金相显微镜对涂层的组织进行观察,分析了基体与涂层的结合方式,测量了涂层的孔隙率.并采用质量分数为5%的NaCl溶液浸泡试验、盐雾试验和电化学试验,检验了涂层的耐腐蚀性.结果表明,利用电弧喷涂技术可以在6061铝合金基体表面形成均匀、致密、孔隙率低、结合良好的高纯铝涂层;高纯铝涂层耐腐蚀性较好,对铝合金基体起到了保护作用,涂层经过封孔工艺处理后保护作用更好.     

稀土对铝及铝合金电弧喷涂层性能影响的研究

本文研究了稀土对铝和铝合金电弧喷涂层性能的影响，对四种丝材涂层的结合强度、孔隙率进行了对比，并利用光学显微镜、扫描电镜观察分析了涂层组织结构。结果表明稀土的加入提高了涂层的结合强度，使孔隙变小、数量减少，明显改善涂层性能。     

稀土对铝及铝合盒电弧喷涂层性能影响的研究

本文研究了稀土对铝和铝合金电弧喷涂层性能的影响，对叫种丝材涂层的结合强度、孔隙率进行了对比，井利用光学显徽镜．扫描电镜观察分析了涂层组织结构。结果表明稀土的加入提高了涂层曲结合强度．使孔隙变小．数量减少，明显改善涂层性能。     

高速电弧喷涂锌涂层性能研究

使用高速电弧喷涂枪和普通电弧喷涂枪分别制备锌涂层。通过对结合强度、孔隙率、粒子尺寸和粒子飞行速度的测试表明,高速电弧喷涂比普通电弧喷涂的粒子尺寸减小,飞行速度提高,制备的锌涂层结合强度高,孔隙率低。对两种锌涂层进行的强化腐蚀试验表明,封孔处理后的高速喷涂锌涂层具有较好的抗腐蚀性能。     

金属喷涂、堆焊与修复——金属喷涂工艺与设备

再制造电弧喷涂成形层的残余应力分析;铝合金表面电弧喷涂铝涂层工艺与性能;碳钢热喷涂渗铝互扩散系数计算;电弧喷涂法制备高耐蚀合金涂层及其性能研究;高速电弧喷涂硼化物金属复合陶瓷工艺参数优化试验研究     

金属喷涂、堆焊与修复

金属喷涂工艺与设备 冷喷涂Au纳米粒子在金属表面沉积过程的分子动力学模拟；降低热喷涂涂层孔隙率的方法；电弧喷涂铝基涂层耐腐蚀性能；电弧喷涂技术在转炉烟罩水冷壁防护上的应用；制备低孔隙超细涂层的高速电弧喷涂枪……     

高速电弧喷涂涂层的性能

分析了高速电弧涂层的结合强度、涂层显微硬度以及涂层孔隙率，并与普通电弧喷涂涂层对比，证明喷涂粒子飞行速度的提高，极大提高了涂层性能。     

Zircon-Based Ceramics Composite Coating for Environmental Barrier Coating

Studies on plasma spraying of zircon (ZrSiO₄) have been carried out by the authors as one of the candidates for an environmental barrier coating (EBC) application, and had reported that substrate temperature is one of the most important factors to obtain crack-free and highly adhesive coating. In this study, several amounts of yttria were added to zircon powder, and the effect of the yttria addition on the structure and properties of the coatings were evaluated to improve the stability of the zircon coating structure at elevated temperature. The coatings obtained were composed of yttria-stabilized zirconia (YSZ), glassy silica, whereas the one prepared from monolithic zircon powder was composed of the metastable high temperature tetragonal phase of zirconia and glassy silica. After the heat treatment over 1200 °C, silica and zirconia formed zircon in all coatings. However, coatings with higher amounts of yttria exhibited lower amounts of zircon. This resulted in the less open porosity of the coating at elevated temperature. These yttria-added coatings also showed good adhesion even after the heat treatment, while monolithic zircon coating pealed off.     

非占位涂料技术中涂层的脱模问题

在非占位涂料技术中,如何实现模样的顺利起模而不破坏涂层是发挥这一技术优势的下措施:合理的设计涂料成分,在涂料表面喷一层过渡层,采用脱模剂以及适当的模样设计,如过渡模法(又称两步法)、模样分块法,采用组芯造型和设计起模机构等.     

彩涂线涂装工艺介绍及常见问题分析

详细介绍了目前国内外彩涂线常用的涂装工艺,并对涂装时容易发生的问题做了具体分析。     

埃文辊涂公司的彩涂钢板

美国的埃文辊涂公司从事涂层板卷生产已有40多年历史。通过高度专业化的加工工艺,在为轧钢车间和服务中心供货业务中已成功地占有一席之地,并已开始向其发源地印第安纳州以外的地方扩展业务。