High Tg Cyclic Olefin Copolymer Gate Dielectrics for N,N′‐Ditridecyl Perylene Diimide Based Field‐Effect Transistors: Improving Performance and Stability with Thermal Treatment

A novel application of ethylene‐norbornene cyclic olefin copolymers (COC) as gate dielectric layers in organic field‐effect transistors (OFETs) that require thermal annealing as a strategy for improving the OFET performance and stability is reported. The thermally‐treated N,N′‐ditridecyl perylene diimide (PTCDI‐C13)‐based n‐type FETs using a COC/SiO₂ gate dielectric show remarkably enhanced atmospheric performance and stability. The COC gate dielectric layer displays a hydrophobic surface (water contact angle = 95° ± 1°) and high thermal stability (glass transition temperature = 181 °C) without producing crosslinking. After thermal annealing, the crystallinity improves and the grain size of PTCDI‐C13 domains grown on the COC/SiO₂ gate dielectric increases significantly. The resulting n‐type FETs exhibit high atmospheric field‐effect mobilities, up to 0.90 cm² V^?1 s^?1 in the 20 V saturation regime and long‐term stability with respect to H₂O/O₂ degradation, hysteresis, or sweep‐stress over 110 days. By integrating the n‐type FETs with p‐type pentacene‐based FETs in a single device, high performance organic complementary inverters that exhibit high gain (exceeding 45 in ambient air) are realized.     

Organic Electronics: High Tg Cyclic Olefin Copolymer Gate Dielectrics for N,N′‐Ditridecyl Perylene Diimide Based Field‐Effect Transistors: Improving Performance and Stability with Thermal Treatment (Adv. Funct. Mater. 16/2010)

A novel application of ethylene‐norbornene cyclic olefin copolymers (COC) as gate dielectric layers in organic field‐effect transistors (OFETs) that require thermal annealing as a strategy for improving the OFET performance and stability is reported. The thermally‐treated N,N′‐ditridecyl perylene diimide (PTCDI‐C13)‐based n‐type FETs using a COC/SiO₂ gate dielectric show remarkably enhanced atmospheric performance and stability. The COC gate dielectric layer displays a hydrophobic surface (water contact angle = 95° ± 1°) and high thermal stability (glass transition temperature = 181 °C) without producing crosslinking. After thermal annealing, the crystallinity improves and the grain size of PTCDI‐C13 domains grown on the COC/SiO₂ gate dielectric increases significantly. The resulting n‐type FETs exhibit high atmospheric field‐effect mobilities, up to 0.90 cm² V^?1 s^?1 in the 20 V saturation regime and long‐term stability with respect to H₂O/O₂ degradation, hysteresis, or sweep‐stress over 110 days. By integrating the n‐type FETs with p‐type pentacene‐based FETs in a single device, high performance organic complementary inverters that exhibit high gain (exceeding 45 in ambient air) are realized.     

Ambient‐Stable,Annealing‐Free,and Ambipolar Organic Field‐Effect Transistors Based on Solution‐Processable Poly(2,2′‐bis(trifluoromethyl)biphenyl‐alt‐2,5‐divinylthiophene) without Long Alkyl Side Chains

An ambipolar conjugated polymer CF₃‐PBTV, poly(2,2′‐bis(trifluoromethyl)biphenyl‐alt‐2,5‐divinylthiophene), consisting of thienylenevinylene as the donor and trifluoromethyl‐substituted biphenyl as the acceptor has been successfully synthesized. CF₃‐PBTV shows solution‐processability without electrically insulating long alkyl side chains. Grazing incidence X‐ray diffraction results suggest a nearly equal population of flat‐on and end‐on domains in CF₃‐PBTV thin film. The excellent ambipolarity of CF₃‐PBTV is demonstrated by well‐equivalent charge mobilities of 0.065 and 0.078 cm² V^?1 s^?1 for p‐ and n‐channel, respectively. The organic field‐effect transistors (OFET) also shows very high on/off ratio (≈10⁷) which is attributed to the relatively large bandgap and low‐lying highest occupied molecular orbital (HOMO) of CF₃‐PBTV. The OFET performance barely changes after the device is stored in ambient conditions for 90 days. The ambient‐stability is attributed to the enhanced oxidative stability from its low‐lying HOMO and the better moisture resistance from its fluorine contents. The performance of CF₃‐PBTV based OFET is annealing independent. It is noteworthy that the solution‐processable, ambipolar, and thienylenevinylene‐containing conjugated polymer without any long alkyl side chains is reported for the first time. And to the best of our knowledge, it is the first ambient‐stable, annealing‐free OFET with well‐equivalent ambipolarity.     

Systematic Study of Widely Applicable N‐Doping Strategy for High‐Performance Solution‐Processed Field‐Effect Transistors

A specific design for solution‐processed doping of active semiconducting materials would be a powerful strategy in order to improve device performance in flexible and/or printed electronics. Tetrabutylammonium fluoride and tetrabutylammonium hydroxide contain Lewis base anions, F^? and OH^?, respectively, which are considered as organic dopants for efficient and cost‐effective n‐doping processes both in n‐type organic and nanocarbon‐based semiconductors, such as poly[[N,N′‐bis(2‐octyldodecyl)‐naphthalene‐1,4,5,8‐bis(dicarboximide)‐2,6‐diyl]‐alt‐5,5′‐(2,2′‐bithiophene)] (P(NDI2OD‐T2)) and selectively dispersed semiconducting single‐walled carbon nanotubes by π‐conjugated polymers. The dramatic enhancement of electron transport properties in field‐effect transistors is confirmed by the effective electron transfer from the dopants to the semiconductors as well as controllable onset and threshold voltages, convertible charge‐transport polarity, and simultaneously showing excellent device stabilities under ambient air and bias stress conditions. This simple solution‐processed chemical doping approach could facilitate the understanding of both intrinsic and extrinsic charge transport characteristics in organic semiconductors and nanocarbon‐based materials, and is thus widely applicable for developing high‐performance organic and printed electronics and optoelectronics devices.     

Self Encapsulated Poly(3‐hexylthiophene)‐poly(fluorinated alkyl methacrylate) Rod‐Coil Block Copolymers with High Field Effect Mobilities on Bare SiO2

Conjugated rod‐coil block copolymers provide an interesting route towards enhancing the properties of the conjugated block due to self‐assembly and the interplay of rod‐rod and rod‐coil interactions. Here, we demonstrate the ability of an attached semi‐fluorinated block to significantly improve upon the charge carrier properties of regioregular poly(3‐hexyl thiophene) (rr‐P3HT) materials on bare SiO₂. The thin film hole mobilities on bare SiO₂ dielectric surfaces of poly (3‐hexyl thiophene)‐block‐polyfluoromethacrylates (P3HT‐b‐PFMAs) can approach up to 0.12 cm² V^?1 s^?1 with only 33 wt% of the P3HT block incorporated in the copolymer, as compared to rr‐P3HT alone which typically has mobilities averaging 0.03 cm² V^?1 s^?1. To our knowledge, this is the highest mobility reported in literature for block copolymers containing a P3HT. More importantly, these high hole mobilities are achieved without multistep OTS treatments, argon protection, or post‐annealing conditions. Grazing incidence wide‐angle x‐ray scattering (GIWAX) data revealed that in the P3HT‐b‐PFMA copolymers, the P3HT rod block self‐assembles into highly ordered lamellar structures, similar to that of the rr‐P3HT homopolymer. Grazing incidence small‐angle x‐ray scattering (GISAXS) data revealed that lamellar structures are only observed in perpendicular direction with short PFMA blocks, while lamellae in both perpendicular and parallel directions are observed in polymers with longer PFMA blocks. AFM, GIWAXS, and contact angle measurements also indicate that PFMA block assembles at the polymer thin film surface and forms an encapsulation layer. The high charge carrier mobilities and the hydrophobic surface of the block copolymer films clearly demonstrates the influence of the coil block segment on device performance by balancing the crystallization and microphase separation in the bulk morphological structure.     

ε‐Branched Flexible Side Chain Substituted Diketopyrrolopyrrole‐Containing Polymers Designed for High Hole and Electron Mobilities

Based on the integrated consideration and engineering of both conjugated backbones and flexible side chains, solution‐processable polymeric semiconductors consisting of a diketopyrrolopyrrole (DPP) backbone and a finely modulated branching side chain (ε‐branched chain) are reported. The subtle change in the branching point from the backbone alters the π?π stacking and the lamellar distances between polymer backbones, which has a significant influence on the charge‐transport properties and in turn the performances of field‐effect transistors (FETs). In addition to their excellent electron mobilities (up to 2.25 cm² V^?1 s^?1), ultra‐high hole mobilities (up to 12.25 cm² V^?1 s^?1) with an on/off ratio (I_on/I_off) of at least 10⁶ are achieved in the FETs fabricated using the polymers. The developed polymers exhibit extraordinarily high electrical performance with both hole and electron mobilities superior to that of unipolar amorphous silicon.     

High‐Performance Solution‐Processable Poly(p‐phenylene vinylene)s for Air‐Stable Organic Field‐Effect Transistors

The influence of the substitution pattern (unsymmetrical or symmetrical), the nature of the side chain (linear or branched), and the processing of several solution processable alkoxy‐substituted poly(p‐phenylene vinylene)s (PPVs) on the charge‐carrier mobility in organic field‐effect transistors (OFETs) is investigated. We have found the highest mobilities in a class of symmetrically substituted PPVs with linear alkyl chains (e.g., R¹, R² = n‐C₁₁H₂₃, R³ = n‐C₁₈H₃₇). We have shown that the mobility of these PPVs can be improved significantly up to values of 10^–2 cm² V^–1 s^–1 by annealing at 110 °C. In addition, these devices display an excellent stability in air and dark conditions. No change in the electrical performance is observed, even after storage for thirty days in humid air.     

Donor–Acceptor Poly(3‐hexylthiophene)‐block‐Pendent Poly(isoindigo) with Dual Roles of Charge Transporting and Storage Layer for High‐Performance Transistor‐Type Memory Applications

Field‐effect transistor memories usually require one additional charge storage layer between the gate contact and organic semiconductor channel. To avoid such complication, new donor–acceptor rod–coil diblock copolymers (P3HT₄₄‐b‐Piso_n) of poly(3‐hexylthiophene) (P3HT)‐block‐poly(pendent isoindigo) (Piso) are designed, which exhibit high performance transistor memory characteristics without additional charge storage layer. The P3HT and Piso blocks are acted as the charge transporting and storage elements, respectively. The prepared P3HT₄₄‐b‐Piso_n can be self‐assembled into fibrillar‐like nanostructures after the thermal annealing process, confirmed by atomic force microscopy and grazing‐incidence X‐ray diffraction. The lowest‐unoccupied molecular orbital levels of the studied polymers are significantly lowered as the block length of Piso increases, leading to a stronger electron affinity as well as charge storage capability. The field‐effect transistors (FETs) fabricated from P3HT₄₄‐b‐Piso_n possess p‐type mobilities up to 4.56 × 10^?2 cm² V^?1 s^?1, similar to that of the regioregular P3HT. More interestingly, the FET memory devices fabricated from P3HT₄₄‐b‐Piso_n exhibit a memory window ranging from 26 to 79 V by manipulating the block length of Piso, and showed stable long‐term data endurance. The results suggest that the FET characteristics and data storage capability can be effectively tuned simultaneously through donor/acceptor ratio and thin film morphology in the block copolymer system.     

Kinetically Controlled Crystallization in Conjugated Polymer Films for High‐Performance Organic Field‐Effect Transistors

Ordering of semiconducting polymers in thin films from the nano to microscale is strongly correlated with charge transport properties as well as organic field‐effect transistor performance. This paper reports a method to control nano to microscale ordering of poly{[N,N′‐bis(2‐octyldodecyl)‐naphthalene‐1,4,5,8‐bis(dicarboximide)‐2,6‐diyl]‐alt‐5,5′‐(2,2′‐bithiophene)} (P(NDI2OD‐T2)) thin films by precisely regulating the solidification rate from the metastable state just before crystallization. The proposed simple but effective approach, kinetically controlled crystallization, achieves optimized P(NDI2OD‐T2) films with large polymer domains, long range ordered fibrillar structures, and molecular orientation preferable for electron transport leading to dramatic morphological changes in both polymer domain sizes at the micrometer scale and molecular packing structures at nanoscales. Structural changes significantly increase electron mobilities up to 3.43 ± 0.39 cm² V^?1 s^?1 with high reliability, almost two orders of enhancement compared with devices from naturally dried films. Small contact resistance is also obtained for electron injection (0.13 MΩ cm), low activation energy (62.51 meV), and narrow density of states distribution for electron transport in optimized thin films. It is believed that this study offers important insight into the crystallization of conjugated polymers that can be broadly applied to optimize the morphology of semiconducting polymer films for solution processed organic electronic devices.     

High‐Mobility Air‐Stable Naphthalene Diimide‐Based Copolymer Containing Extended π‐Conjugation for n‐Channel Organic Field Effect Transistors

A high‐performance naphthalene diimide (NDI)‐based conjugated polymer for use as the active layer of n‐channel organic field‐effect transistors (OFETs) is reported. The solution‐processable n‐channel polymer is systematically designed and synthesized with an alternating structure of long alkyl substituted‐NDI and thienylene–vinylene–thienylene units (PNDI‐TVT). The material has a well‐controlled molecular structure with an extended π‐conjugated backbone, with no increase in the LUMO level, achieving a high mobility and highly ambient stable n‐type OFET. The top‐gate, bottom‐contact device shows remarkably high electron charge‐carrier mobility of up to 1.8 cm² V^?1 s^?1 (I_on/I_off = 10⁶) with the commonly used polymer dielectric, poly(methyl methacrylate) (PMMA). Moreover, PNDI‐TVT OFETs exhibit excellent air and operation stability. Such high device performance is attributed to improved π–π intermolecular interactions owing to the extended π‐conjugation, apart from the improved crystallinity and highly interdigitated lamellar structure caused by the extended π–π backbone and long alkyl groups.     

Low‐Temperature,Nontoxic Water‐Induced Metal‐Oxide Thin Films and Their Application in Thin‐Film Transistors

Here, a simple, nontoxic, and inexpensive “water‐inducement” technique for the fabrication of oxide thin films at low annealing temperatures is reported. For water‐induced (WI) precursor solution, the solvent is composed of water without additional organic additives and catalysts. The thermogravimetric analysis indicates that the annealing temperature can be lowered by prolonging the annealing time. A systematic study is carried out to reveal the annealing condition dependence on the performance of the thin‐film transistors (TFTs). The WI indium‐zinc oxide (IZO) TFT integrated on SiO₂ dielectric, annealed at 300 °C for 2 h, exhibits a saturation mobility of 3.35 cm² V^?1 s^?1 and an on‐to‐off current ratio of ≈10⁸. Interestingly, through prolonging the annealing time to 4 h, the electrical parameters of IZO TFTs annealed at 230 °C are comparable with the TFTs annealed at 300 °C. Finally, fully WI IZO TFT based on YO_x dielectric is integrated and investigated. This TFT device can be regarded as “green electronics” in a true sense, because no organic‐related additives are used during the whole device fabrication process. The as‐fabricated IZO/YO_x TFT exhibits excellent electron transport characteristics with low operating voltage (≈1.5 V), small subthreshold swing voltage of 65 mV dec^?1 and the mobility in excess of 25 cm² V^?1 s^?1.     

Benzodithiophene Copolymer—A Low‐Temperature,Solution‐Processed High‐Performance Semiconductor for Thin‐Film Transistors

Poly(4,8‐didodecyl‐2,6‐bis‐(3‐methylthiophen‐2‐yl)‐benzo[1,2‐b:4,5‐b′]dithiophene) self‐assembled on appropriate substrates from solution and formed highly structured thin films at low temperatures. As an as‐prepared thin‐film semiconductor without thermal annealing, it exhibited excellent field‐effect transistor properties with mobility of ～ 0.15 cm² V^–1 s^–1 in thin‐film transistors.     

On the Relation between Morphology and FET Mobility of Poly(3‐alkylthiophene)s at the Polymer/SiO2 and Polymer/Air Interface

The influence of the interface of the dielectric SiO₂ on the performance of bottom‐contact, bottom‐gate poly(3‐alkylthiophene) (P3AT) field‐effect transistors (FETs) is investigated. In particular, the operation of transistors where the active polythiophene layer is directly spin‐coated from chlorobenzene (CB) onto the bare SiO₂ dielectric is compared to those where the active layer is first spin‐coated then laminated via a wet transfer process such that the film/air interface of this film contacts the SiO₂ surface. While an apparent alkyl side‐chain length dependent mobility is observed for films directly spin‐coated onto the SiO₂ dielectric (with mobilities of ≈10^?3 cm² V^?1 s^?1 or less) for laminated films mobilities of 0.14 ± 0.03 cm² V^?1 s^?1 independent of alkyl chain length are recorded. Surface‐sensitive near edge X‐ray absorption fine structure (NEXAFS) spectroscopy measurements indicate a strong out‐of‐plane orientation of the polymer backbone at the original air/film interface while much lower average tilt angles of the polymer backbone are observed at the SiO₂/film interface. A comparison with NEXAFS on crystalline P3AT nanofibers, as well as molecular mechanics and electronic structure calculations on ideal P3AT crystals suggest a close to crystalline polymer organization at the P3AT/air interface of films from CB. These results emphasize the negative influence of wrongly oriented polymer on charge carrier mobility and highlight the potential of the polymer/air interface in achieving excellent “out‐of‐plane” orientation and high FET mobilities.     

Layer‐by‐Layer Conjugated Extension of a Semiconducting Polymer for High‐Performance Organic Field‐Effect Transistor

A donor–acceptor (D–A) semiconducting copolymer, PDPP‐TVT‐29, comprising a diketopyrrolopyrrole (DPP) derivative with long, linear, space‐separated alkyl side‐chains and thiophene vinylene thiophene (TVT) for organic field‐effect transistors (OFETs) can form highly π‐conjugated structures with an edge‐on molecular orientation in an as‐spun film. In particular, the layer‐like conjugated film morphologies can be developed via short‐term thermal annealing above 150 °C for 10 min. The strong intermolecular interaction, originating from the fused DPP and D–A interaction, leads to the spontaneous self‐assembly of polymer chains within close proximity (with π‐overlap distance of 3.55 Å) and forms unexpectedly long‐range π‐conjugation, which is favorable for both intra‐ and intermolecular charge transport. Unlike intergranular nanorods in the as‐spun film, well‐conjugated layers in the 200 °C‐annealed film can yield more efficient charge‐transport pathways. The granular morphology of the as‐spun PDPP‐TVT‐29 film produces a field‐effect mobility (μ _FET) of 1.39 cm² V^?1 s^?1 in an OFET based on a polymer‐treated SiO₂ dielectric, while the 27‐Å‐step layered morphology in the 200 °C‐annealed films shows high μ _FET values of up to 3.7 cm² V^?1 s^?1.     

High‐Mobility Naphthalene Diimide and Selenophene‐Vinylene‐Selenophene‐Based Conjugated Polymer: n‐Channel Organic Field‐Effect Transistors and Structure–Property Relationship

Interdependence of chemical structure, thin‐film morphology, and transport properties is a key, yet often elusive aspect characterizing the design and development of high‐mobility, solution‐processed polymers for large‐area and flexible electronics applications. There is a specific need to achieve >1 cm² V^?1 s^?1 field‐effect mobilities (μ) at low processing temperatures in combination with environmental stability, especially in the case of electron‐transporting polymers, which are still lagging behind hole transporting materials. Here, the synthesis of a naphthalene‐diimide based donor–acceptor copolymer characterized by a selenophene vinylene selenophene donor moiety is reported. Optimized field‐effect transistors show maximum μ of 2.4 cm² V^?1 s^?1 and promising ambient stability. A very marked film structural evolution is revealed with increasing annealing temperature, with evidence of a remarkable 3D crystallinity above 180 °C. Conversely, transport properties are found to be substantially optimized at 150 °C, with limited gain at higher temperature. This discrepancy is rationalized by the presence of a surface‐segregated prevalently edge‐on packed polymer phase, dominating the device accumulated channel. This study therefore serves the purpose of presenting a promising, high‐electron‐mobility copolymer that is processable at relatively low temperatures, and of clearly highlighting the necessity of specifically investigating channel morphology in assessing the structure–property nexus in semiconducting polymer thin films.     

Impact of Morphology on Charge Carrier Transport and Thermoelectric Properties of N‐Type FBDOPV‐Based Polymers

The impact of the chemical structure and molecular order on the charge transport properties of two donor–acceptor copolymers in their neutral and doped states is investigated. Both polymers comprise 3,7‐bis((E)‐7‐fluoro‐1‐(2‐octyl‐dodecyl)‐2‐oxoindolin‐3‐ylidene)‐3,7‐dihydrobenzo[1,2‐b:4,5‐b′]difuran‐2,6‐dione (FBDOPV) as electron‐accepting unit, copolymerized with 9,9‐dioctyl‐fluorene (P(FBDOPV‐F)) or with 3‐dodecyl‐2,2′‐bithiophene (P(FBDOPV‐2T‐C₁₂)). These copolymers possess an amorphous and semi‐crystalline nature, respectively, and exhibit remarkable electron mobilities of 0.065 and 0.25 cm² V^–1 s^–1 in field effect transistors. However, after chemical n‐doping with 4‐(1,3‐dimethyl‐2,3‐dihydro‐1H‐benzoimidazol‐2‐yl)phenyl)dimethylamine (N‐DMBI), electrical conductivities four orders of magnitude higher can be achieved for P(FBDOPV‐2T‐C₁₂) (σ = 0.042 S cm^?1). More charge‐transfer complexes are formed between P(FBDOPV‐F) and N‐DMBI, but the highly localized polaronic states poorly contribute to the charge transport. Doped P(FBDOPV‐2T‐C₁₂) exhibits a negative Seebeck coefficient of –265 µV K^?1 and a thermoelectric power factor (PF) of 0.30 µW m^?1 K^?2 at 303 K which increases to 0.72 µW m^?1 K^?2 at 388 K. The in‐plane thermal conductivity (κ_|| = 0.53 W m^?1 K^?1) on the same micrometer‐thick solution‐processed film is measured, resulting in a figure of merit (ZT) of 5.0 × 10^?4 at 388 K. The results provide important design guidelines to improve the doping efficiency and thermoelectric properties of n‐type organic semiconductors.     

High‐Performance n‐Channel Thin‐Film Field‐Effect Transistors Based on a Nanowire‐Forming Polymer

A new electrontransport polymer, poly{[N,N′‐dioctylperylene‐3,4,9,10‐bis(dicarboximide)‐1,7(6)‐diyl]‐alt‐[(2,5‐bis(2‐ethyl‐hexyl)‐1,4‐phenylene)bis(ethyn‐2,1‐diyl]} (PDIC8‐EB), is synthesized. In chloroform, the polymer undergoes self‐assembly, forming a nanowire suspension. The nanowire's optical and electrochemical properties, morphological structure, and field‐effect transistor (FET) characteristics are investigated. Thin films fabricated from a PDIC8‐EB nanowire suspension are composed of ordered nanowires and ordered and amorphous non‐nanowire phases, whereas films prepared from a homogeneous PDIC8‐EB solution consist of only the ordered and amorphous non‐nanowire phases. X‐ray scattering experiments suggest that in both nanowires and ordered phases, the PDIC8 units are laterally stacked in an edge‐on manner with respect to the film plane, with full interdigitation of the octyl chains, and with the polymer backbones preferentially oriented within the film plane. The ordering and orientations are significantly enhanced through thermal annealing at 200 °C under inert conditions. The polymer film with high degree of structural ordering and strong orientation yields a high electron mobility (0.10 ± 0.05 cm² V^?1 s^?1), with a high on/off ratio (3.7 × 10⁶), a low threshold voltage (8 V), and negligible hysteresis (0.5 V). This study demonstrates that the polymer in the nanowire suspension provides a suitable material for fabricating the active layers of high‐performance n‐channel FET devices via a solution coating process.     

Solution‐Processed Ambipolar Field‐Effect Transistor Based on Diketopyrrolopyrrole Functionalized with Benzothiadiazole

Ambipolar charge transport in a solution‐processed small molecule 4,7‐bis{2‐[2,5‐bis(2‐ethylhexyl)‐3‐(5‐hexyl‐2,2′:5′,2″‐terthiophene‐5″‐yl)‐pyrrolo[3,4‐c]pyrrolo‐1,4‐dione‐6‐yl]‐thiophene‐5‐yl}‐2,1,3‐benzothiadiazole (BTDPP2) transistor has been investigated and shows a balanced field‐effect mobility of electrons and holes of up to ～10^?2 cm² V^?1 s^?1. Using low‐work‐function top electrodes such as Ba, the electron injection barrier is largely reduced. The observed ambipolar transport can be enhanced over one order of magnitude compared to devices using Al or Au electrodes. The field‐effect mobility increases upon thermal annealing at 150 °C due to the formation of large crystalline domains, as shown by atomic force microscopy and X‐ray diffraction. Organic inverter circuits based on BTDPP2 ambipolar transistors display a gain of over 25.     

A High‐k Fluorinated P(VDF‐TrFE)‐g‐PMMA Gate Dielectric for High‐Performance Flexible Field‐Effect Transistors

A newly synthesized high‐k polymeric insulator for use as gate dielectric layer for organic field‐effect transistors (OFETs) obtained by grafting poly(methyl methacrylate) (PMMA) in poly(vinylidene fluoride‐trifluoroethylene) (P(VDF‐TrFE)) via atom transfer radical polymerization transfer is reported. This material design concept intents to tune the electrical properties of the gate insulating layer (capacitance, leakage current, breakdown voltage, and operational stability) of the high‐k fluorinated polymer dielectric without a large increase in operating voltage by incorporating an amorphous PMMA as an insulator. By controlling the grafted PMMA percentage, an optimized P(VDF‐TrFE)‐g‐PMMA with 7 mol% grafted PMMA showing reasonably high capacitance (23–30 nF cm^?2) with low voltage operation and negligible current hysteresis is achieved. High‐performance low‐voltage‐operated top‐gate/bottom‐contact OFETs with widely used high mobility polymer semiconductors, poly[[2,5‐bis(2‐octyldodecyl)‐2,3,5,6‐tetrahydro‐3,6‐dioxopyrrolo [3,4‐c]pyrrole‐1,4‐diyl]‐alt‐[[2,2′‐(2,5‐thiophene)bis‐thieno(3,2‐b)thiophene]‐5,5′‐diyl]] (DPPT‐TT), and poly([N,N′‐bis(2‐octyldodecyl)‐naphthalene‐1,4,5,8‐bis(dicarboximide)‐2,6‐diyl]‐alt‐5,5′‐(2,2′‐bithiophene)) are demonstrated here. DPPT‐TT OFETs with P(VDF‐TrFE)‐g‐PMMA gate dielectrics exhibit a reasonably high field‐effect mobility of over 1 cm² V^?1 s^?1 with excellent operational stability.     

Hydrocarbons‐Driven Crystallization of Polymer Semiconductors for Low‐Temperature Fabrication of High‐Performance Organic Field‐Effect Transistors

While many high‐performance polymer semiconductors are reported for organic field‐effect transistors (OFETs), most require a high‐temperature postdeposition annealing of channel semiconductors to achieve high performance. This negates the fundamental attribute of OFETs being a low‐cost alternative to conventional high‐cost silicon technologies. A facile solution process is developed through which high‐performance OFETs can be fabricated without thermal annealing. The process involves incorporation of an incompatible hydrocarbon binder or wax into the channel semiconductor composition to drive rapid phase separation and instantaneous crystallization of polymer semiconductor at room temperature. The resulting composite channel semiconductor film manifests a nano/microporous surface morphology with a continuous semiconductor nanowire network. OFET mobility of up to about 5 cm² V^?1 s^?1 and on/off ratio ≥ 10⁶ are attained. These are hitherto benchmark performance characteristics for room‐temperature, solution‐processed polymer OFETs, which are functionally useful for many impactful applications.