Sol–Gel Electrophoretic Deposition for the Growth of Oxide Nanorods

By combining sol–gel processing with electrophoretic deposition, we have developed a new method for the growth of oxide nanorods. Both single metal oxides (TiO₂, SiO₂) and complex oxides—BaTiO₃, Sr₂Nb₂O₇, and Pb(Zr_0.52Ti_0.48)O₃—have been grown by this method. Uniformly sized nanorods 45–200 nm in diameter and 10 μm in length can be grown over large areas with near unidirectional alignment. The nanorods have the desired stoichiometric chemical composition and crystal structure, after firing to 500–700 °C for up to one hour.     

Microfluidics: Nanostructuring of Titania Thin Films by a Combination of Microfluidics and Block‐Copolymer‐Based Sol–Gel Templating (Small 7/2011)

Sol–gel templating of titania thin films with the amphiphilic diblock copolymer poly(dimethyl siloxane)‐block‐methyl methacrylate poly(ethylene oxide) is combined with microfluidic technology to control the structure formation. Due to the laminar flow conditions in the microfluidic cell, a better control of the local composition of the reactive fluid is achieved. The resulting titania films exhibit mesopores and macropores, as determined with scanning electron microscopy, X‐ray reflectivity, and grazing incidence small angle X‐ray scattering. The titania morphology has three features that are beneficial for application in photovoltaics: 1) a large surface‐to‐volume ratio important for charge generation with disordered hexagonally arranged mesopores of 25 nm size and a film porosity of up to 0.79, 2) enhanced light scattering that enables the absorption of more light, and 3) a dense titania layer with a thickness of about 6 nm at the substrate (bottom electrode) to prevent short circuits. An optical characterization complements the structural investigation.     

Sol–gel derived N-doped ZnO thin films

N-doped ZnO (NZO) thin films have been prepared by a sol–gel method and their electrical and optical properties have been investigated. The prepared NZO films were p-type, and had excellent electrical properties. They had an optical transparency above 85% in the visible range. The UV absorption edge was red-shifted with increasing N-doping concentration. Two emission bands were observed in the photoluminescence (PL) spectra, with one band located in the UV range and the other band consisting of green luminescence. Both UV and green emissions were enhanced with increasing N-doping concentration.     

Sol–gel thin film deposition and characterization of a new optically active compound: Er2Ti2O7

This paper reports on the first sol–gel thin film preparation of a new optically active compound: Er₂Ti₂O₇ (ETO). Optical, microstructural and spectroscopic properties of ETO films annealed in a temperature range 300–1000°C are studied. This work shows that the porosity and microstructure of ETO films depend closely on the heat-treatment temperature. Photoluminescence (PL) has been observed for films heat-treated at 600°C or more. The PL decay appears strongly influenced by quenching effects. For thin films treated at 600°C, quenching is essentially due to the presence of hydroxyl groups. After heat-treatment at 800°C or more, quenching can be explained by the high concentration of erbium atoms and by their distribution in the ETO lattice.