Casting solvent effect on crystallization behavior and morphology of poly(ethylene oxide)/poly(methyl methacrylate)

Poly(ethylene oxide) (PEO)/poly(methyl methacrylate) (PMMA) blends were prepared by casting from either chloroform or benzene solvents. After casting from solvents, all samples used in this study were preheated to 100°C and held for 10 min. Then, the solvent effect on the crystallization behavior and thermodynamic properties were studied by differential scanning calorimeter (DSC). Also, the morphology of spherulite of casting film was studied by polarized optical microscope. From the DSC and polarizing optical microscopy (POM) results, it was found that PEO/PMMA was miscible in the molten state no matter which casting solvent was used. However, the crystallization of PEO in the chloroform‐cast blend was more easily suppressed than it was in the benzene‐cast blend. Relatively, the chloroform‐cast blend showed the greater melting‐point depressing of PEO crystals. Also, the spherulite of chloroform‐cast film showed a coarser birefringence. It was supposed that the chloroform‐cast blend had more homogeneous morphology. It is fair to say that polymer blends, cast from solvent, are not necessarily in equilibrium. However, the benzene‐cast blends still were not in equilibrium even after preheating at 100°C for 10 min. © 2000 John Wiley & Sons, Inc. J Appl Polym Sci 76: 1627–1636, 2000     

Synthesis and Surface Properties of Poly(methyl methacrylate)/Poly(ethylene glycol) Binary Brushes

A new kind of binary polymer brushes was synthesized from two immiscible polymers, PMMA and PEG, on GPS‐modified silicon wafers. Surface composition, layer thickness, coverage, chain density, wetting ability, morphology and protein adsorption of the binary brushes were investigated by XPS, ellipsometry, AFM and contact angle measurements. The results show that both PMMA and PEG were successfully grafted onto the surface. The surface coverage and the chain density of PMMA and PEG brushes can be controlled by modulating the reaction temperature and time. This kind of binary polymer brushes exhibits a distinct microphase‐separated structure and excellent protein‐preventing property.

     

Influence of composition and molecular mass on the morphology,crystallization and melting behaviour of poly(ethylene oxide)/poly(methyl methacrylate) blends

Results are reported on the influence of composition and molecular mass of components on the isothermal growth rate of spherulites, on the overall kinetic rate constant, on the primary nucleation and on the thermal behaviour of poly(ethylene oxide)/poly(methyl methacrylate) blends. The growth rate of PEO spherulites as well as the observed equilibrium melting temperatures decrease, for a given T_c or ΔT, with the increase of PMMA content.Such observations are interpreted by assuming that the polymers are compatible in the undercooled melt, at least in the range of crystallization temperatures investigated. Thermodynamic quantities such as the surface free energy of folding σ_e and the Flory-Huggins parameter χ₁₂ have been obtained by studying the dependence of the radial growth rate G and of the overall kinetic rate constant K from temperature and composition and the dependence of the equilibrium melting temperature depression ΔT_m upon composition, respectively.     

Spherulitic crystallization in blends of poly(ethylene oxide) and poly(methyl methacrylate)

The crystallization kinetics of binary blends of poly(ethylene oxide) and poly(methyl methacrylate) were investigated. The isothermal spherulitic growth rates were measured by means of a polarized light microscope. The temperature and composition dependence on the growth rates have been analysed. The temperature range studied was from 44° to 58°C. The introduction of poly(methyl methacrylate) into poly(ethylene oxide) resulted in a reduction of the spherulitic growth rate as the proportion of poly(methyl methacrylate) was increased from zero to 40% by weight. Results have been analysed using the theoretical equations of Boon and Azcue for the growth rate of polymer-diluent mixtures. The experimental results are in good agreement with this equation. The temperature coefficient is negative as is the case in the crystallization of bulk homopolymers.     

Material encapsulation in poly(methyl methacrylate) shell: A review

Material encapsulation is a relatively new technique for coating a micro/nanosize particle or droplet with polymeric or inorganic shell. Encapsulation technology has many applications in various fields including drug delivery, cosmetic, agriculture, thermal energy storage, textile, and self-healing polymers. Poly(methyl methacrylate) (PMMA) is widely used as shell material in encapsulation due to its high chemical stability, biocompatibility, nontoxicity, and good mechanical properties. The main approach for micro/nanoencapsulation of materials using PMMA as shell comprises emulsion-based techniques such as emulsion polymerization and solvent evaporation from oil-in-water emulsion. In the present review, we first focus on the encapsulation techniques of liquid materials with PMMA shell by analyzing the effective processing parameters influencing the preparation of PMMA micro/nanocapsules. We then describe the morphology of PMMA capsules in emulsion systems according to thermodynamic relations. The techniques to investigation of mechanical properties of capsule shell and the release mechanisms of core material from PMMA capsules were also investigated. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 48039.     

First results of small and wide angle X-ray scattering of poly(ethylene oxide)/poly(methyl methacrylate) binary blends

Some preliminary small and wide angle X-ray scattering results are reported from isothermally crystallized samples of poly(ethylene oxide)/(methyl methacrylate) binary blends.     

Preparation and characterizations of interpenetrating polymer network hydrogels of poly(ethylene oxide) and poly(methyl methacrylate)

Interpenetrating polymer network (IPN) hydrogels based on poly(ethylene oxide) and poly(methyl methacrylate) were prepared by radical polymerization using 2,2‐dimethyl‐2‐phenylacetophenone and ethylene glycol dimethacrylate as initiators and crosslinkers, respectively. The IPN hydrogels were analyzed for sorption behavior at 25°C and at a relative humidity of 95% using dynamic vapor sorption. The IPN hydrogels exhibited a relatively high equilibrium water content in the range of 13–68%. The state of water in the swollen IPN hydrogels was investigated using differential scanning calorimetry. The free water in the hydrogels increased as the hydrophilic content increased. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 89: 258–262, 2003     

Tacticity effects on the miscibility behavior of poly(methyl methacrylate)/poly(ethylene oxide-b-dimethylsiloxane-b-ethylene oxide) blends

The miscibility of a triblock copolymer poly(ethylene oxide)-poly(dimethylsiloxane)-poly(ethylene oxide) with syndiotactic and isotactic poly(methylmethacrylate) wasstudied. Although isotactic poly(methyl methacrylate) (PMMA) was miscible with poly(ethylene oxide) (PEO) in the pure state, it was immiscible with the PEO end blocks in the copolymer. In comparison, the syndiotactic poly(methyl methacrylate) (sPMMA) was miscible with the PEO blocks as indicated by melting point depression, decrease in crystallinity, and slower rate of spherulite growth of PEO. When blends of the triblock copolymer were cooled to low temperatures, the poly(dimethylsiloxane) (PDMS) middle block which resided in the interlamellar region of PEO spherulites also crystallized; the development of PDMS crystals was clearly suppressed at high sPMMA contents.On leave from Union Chemical Laboratories, Industrial Technology Research Institute, Hsinchu, Taiwan     

Solvent effects on the miscibility of poly(methyl methacrylate)/poly(bisphenol a carbonate) blends

Blends of atactic or syndiotactic poly(methyl methacrylate) (designated as aPMMA or sPMMA) and poly(bisphenol A carbonate) (PC) were prepared from solution casting. Tetrahydrofuran (THF) and chloroform were used as solvent. Experimental results indicated that the as‐cast blends from THF were quite different from the chloroform‐cast ones. After film preparation, THF‐cast blends did not show any visible phase separation. However, chloroform‐cast blends formed a phase‐separated structure. The as‐cast PC from either solvent was not completely amorphous, and had a melting point at 239–242°C, indicating a certain degree of crystallinity. In contrast, the quenched samples of aPMMA/PC blends prepared from the two solvents behaved virtually the same. They both showed aPMMA dissolves better in PC, but PC solubility in aPMMA is very little. Using sPMMA instead of aPMMA to blend with PC, different results were obtained. The quenched sPMMA/PC blends cast from THF showed only one T_g. However, immiscibility (i.e., two T_gs) was found in the same blend system when cast from chloroform. THF was believed to cause the observation of single T_g due to the following kinetic reason. sPMMA and PC were still trapped together even after THF removal in a homogeneous, but nonequilibrium state below the glass transition. Therefore, the quenched sPMMA/PC blends were not truly thermodynamically miscible. From the results of aPMMA or sPMMA with PC, increasing syndiotacticity seemed to improve the miscibility between PMMA and PC. © 2001 John Wiley & Sons, Inc. J Appl Polym Sci 80: 2842–2850, 2001     

聚乙二醇/聚己内酯三嵌段共聚物的合成与表征

以甲苯二异氰酸酯 (TDI)为偶联剂 ,合成了聚乙二醇 (PEG) /聚己内酯 (PCL)两亲性三嵌段共聚物 (PEG-b-PCL -b -PEG ,PECL) ,采用IR、1 H-NMR、DSC和WAXD分析和研究了PECL的结构与性能。实验结果表明 ,PECL的结构和组成与设计相一致 ,结晶度和熔点均低于均聚物 ,且随着PECL中PCL嵌段含量的增加 ,PCL嵌段熔点升高。透射电镜照片显示PECL纳米粒呈核 /壳结构的球形。     

Effect of organoclay in an immiscible poly(ethylene terephtalate) waste/poly(methyl methacrylate) blend

Blends of organically modified montmorillonite (OMMT) with poly(ethylene terephtalate) (PET) waste and poly(methyl methacrylate) (PMMA) were prepared by melt mixing. The morphology of PET/PMMA nanocomposites with different OMMT contents was characterized by transmission electron microscopy (TEM) and X‐ray diffraction (XRD). The nonisothermal crystallization temperatures of nanocomposites were also examined by DSC. TEM observations and XRD patterns revealed that silicate layers were intercalated and well dispersed in the blend. Nanocomposites displayed better mechanical properties when compared with the unfilled blend. DMA analyses also showed efficient mixing of the two immiscible polymers and changes in glass transition temperature with the presence of OMMT. DSC analysis showed an enhancement in crystallization rate of nanocomposites and a decrease in cristallinity. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010     

Preparation of collagen‐immobilized poly(ethylene glycol)/poly(2‐hydroxyethyl methacrylate) interpenetrating network hydrogels for potential application of artificial cornea

To enhance the mechanical strength of poly(ethylene glycol)(PEG) gels and to provide functional groups for surface modification, we prepared interpenetrating (IPN) hydrogels by incorporating poly(2‐hydroxyethyl methacrylate)(PHEMA) inside PEG hydrogels. Formation of IPN hydrogels was confirmed by measuring the weight percent gain of the hydrogels after incorporation of PHEMA, as well as by ATR/FTIR analysis. Synthesis of IPN hydrogels with a high PHEMA content resulted in optically transparent and extensively crosslinked hydrogels with a lower water content and a 6 ～ 8‐fold improvement in mechanical properties than PEG hydrogels. Incorporation of less than 90 wt % PHEMA resulted in opaque hydrogels due to phase separation between water and PHEMA. To overcome the poor cell adhesion properties of the IPN hydrogels, collagen was covalently grafted to the surface of IPN hydrogels via carbamate linkages to hydroxyl groups in PHEMA. Resultant IPN hydrogels were proven to be noncytotoxic and cell adhesion study revealed that collagen immobilization resulted in a significant improvement of cell adhesion and spreading on the IPN hydrogel surfaces. The resultant IPN hydrogels were noncytotoxic, and a cell adhesion study revealed that collagen immobilization improved cell adhesion and spreading on the IPN hydrogel surfaces significantly. These results indicate that PEG/PHEMA IPN hydrogels are highly promising biomaterials that can be used in artificial corneas and a variety of other load‐bearing tissue engineering applications. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011     

Phase behavior and properties of poly(methyl methacrylate)/poly(vinyl acetate) blends prepared via in situ polymerization

Polymer blends composed of poly(methyl methacrylate) (PMMA) and poly(vinyl acetate) (PVAc) were prepared via radical-initiated polymerization of methyl methacrylate (MMA) in the presence of PVAc. Differential scanning calorimetry and dynamic mechanical analysis were employed to investigate the miscibility and phase behavior of the blends. The PMMA/PVAc blends of in situ polymerization were found to be phase separated and exhibited a two-phase structure, although some chain transferring reaction between the components occurred. The phase separation resulted from the solvent effect of MMA during the in situ polymerization, which was confirmed by the investigation of phase behavior based on solution cast blending. Solubility analysis of the polymerized blends indicated that some chain transferring reaction between the components occurred during the polymerization. An abrupt increase in gel content from 21.2 to 72.4 wt % was observed when the inclusion of PVAc increased from 30 to 40 wt %, and the gel component consisted of the component polymers as shown by infrared spectroscopy studies. The thermogravimetric analysis study indicated that the inclusion of a small amount of PVAc gives rise to a marked stabilization effect on the thermal stability. The PMMA/PVAc blends exhibited increased notched impact properties with the inclusion of 5 wt % PVAc. © 1998 John Wiley & Sons, Inc. J Appl Polym Sci 69: 675–684, 1998     

Properties of mineral filled poly(lactic acid)/poly(methyl methacrylate) blend

This study examines the influence of three different minerals, that is, clay, calcium carbonate, and quartz on the physical, thermal, and mechanical properties of poly(lactic acid) (PLA)/poly(methyl methacrylate) blend. Rheological behavior and phase structure were initially studied by small-amplitude oscillatory shear rheology. Clay- and quartz-filled materials presented an increase in viscosity at low frequency associated with the presence of a yield stress. However, this behavior was not observed for calcium carbonate filled materials due to a matrix degradation effect. To elucidate this aspect, thermal stability and thermal properties were examined by thermogravimetric analysis and differential scanning calorimetry, showing that calcium carbonate promotes degradation of the PLA phase. No nucleating effect was observed in the presence of the minerals. Dynamical mechanical analysis and mechanical characterization revealed an increase of the overall softening temperature and, a reinforcing effect for clay- and quartz-based composites. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 46927.     

Adsorption of heavy‐metal ions on poly(ethylene imine)‐immobilized poly(methyl methacrylate) microspheres

Poly(methyl methacrylate) (PMMA) microspheres carrying poly(ethylene imine) (PEI) were prepared for the removal of heavy‐metal ions (copper, cadmium, and lead) from aqueous solutions with different amounts of these ions (50–600 mg/L) and different pH values (3.0–7.0). Ester groups in the PMMA structures were converted to imine groups in a reaction with PEI as a metal‐chelating ligand in the presence of NaH. The adsorption of heavy‐metal ions on the unmodified PMMA microspheres was very low [3.6 μmol/g for Cu(II), 4.6 μmol/g for Cd(II), and 4.2 μmol/g for Pb(II)]. PEI immobilization significantly increased the heavy‐metal adsorption [0.224 mmol/g for Cu(II), 0.276 mmol/g for Cd(II), and 0.126 mmol/g for Pb(II)]. The affinity order of adsorption (in moles) was Cd(II) > Cu(II) > Pb(II). The adsorption of heavy‐metal ions increased with increasing pH and reached a plateau value around pH 5.5. Their adsorption behavior was approximately described with the Langmuir equation. © 2001 John Wiley & Sons, Inc. J Appl Polym Sci 81: 197–205, 2001     

聚乙二醇存在下苯乙烯/甲基丙烯酸甲酯无皂乳液聚合体系的动态表面张力

利用最大泡压法（MBPM）研究了苯乙烯（St）/甲基丙烯酸甲酯（MMA）在有、无聚乙二醇（PEG）水溶液中进行无皂乳液聚合过程中的动态表面张力变化。发现PEG使体系反应速率变慢,反应50 min,有PEG参与的体系转化率只有49%,而无PEG参与的体系转化率已达到98%以上,接近终点。St/MMA和引发剂形成的聚合物在PEG的作用下,形成了一种具有更强表面活性的聚合物,表面活性水平高于PEG以及无PEG参与聚合体系的聚合物,但弱于混合单体及齐聚物。这种较强表面活性的聚合物在转化率只有5%的时候就已经存在,是聚合物进入粒子堆形成稳定小粒子的动力,并最终使粒子带有足够脱离粒子堆的表面电荷。     

Morphological and infra-red studies on highly oriented poly(vinylidene fluoride)/poly(methyl methacrylate) blends

Highly oriented melt drawn films of poly(vinylidene fluoride) (PVDF) and blends of poly(vinylidene fluoride) and poly(methyl methacrylate) (PMMA) have been studied by transmission electron microscopy, electron diffraction and infra-red spectroscopy. Infra-red spectra show the second moment of the orientation function for PVDF samples to be greater than 0.94. Using such a sample, the transition dipole directions relative to the chain axis have been calculated. Electron microscopic studies of the PVDF/PMMA blends show a transformation for pure PVDF from a lamellar morphology to a mixture of lamellar and needle-like crystals for the 80/20 blend. The 60/40 blend shows a pure needle-like morphology. The β phase content for this blend is dependent upon the composition and thermal history. An increase in the β phase content is observed with the addition of PMMA. After annealing at 110°C, the 50/50 blend shows a lamellar β phase morphology. A significant increase in the segmental orientation of PVDF is also observed.     

聚乳酸/聚乙二醇共混物的结晶与降解行为

针对聚乳酸（PLLA）亲水性差、降解周期长的问题,利用与亲水性高分子聚乙二醇（PEG）共混的方法对其进行改性。采用转矩流变仪制备了不同组成的PLLA/PEG共混物颗粒,系统研究了PLLA/PEG共混物的结晶和熔融、亲水性和在酸碱介质中的降解行为。结果表明,PEG的加入增强了共混物中PLLA的结晶能力,提高了PLLA在降温过程中的熔融结晶温度。PLLA/PEG共混物在等温结晶中表现出比纯PLLA更快的结晶速度。通过改变PLLA/PEG共混物的组成,可调控材料的表面亲水性和降解速率。随着PEG含量的增多,PLLA/PEG共混物的表面接触角降低。PLLA与PLLA/PEG共混物均可在水溶液中降解,共混物的降解速率高于纯PLLA,随着PEG含量的升高和降解液中酸碱浓度的提高,PLLA/PEG共混物的降解速率加快。     

Crystallization behavior and hydrophilicity of poly(vinylidene fluoride)/poly(methyl methacrylate)/poly(vinyl pyrrolidone) ternary blends

Ternary blends composed of matrix polymer poly(vinylidene fluoride) (PVDF) with different proportions of poly(methyl methacrylate) (PMMA)/poly(vinyl pyrrolidone) (PVP) blends were prepared by melt mixing. The miscibility, crystallization behavior, mechanical properties and hydrophilicity of the ternary blends have been investigated. The high compatibility of PVDF/PMMA/PVP ternary blends is induced by strong interactions between the carbonyl groups of the PMMA/PVP blend and the CF₂ or CH₂ group of PVDF. According to the Fourier transform infrared and wide‐angle X‐ray difffraction analyses, the introduction of PMMA does not change the crystalline state (i.e. α phase) of PVDF. By contrast, the addition of PVP in the blends favors the transformation of the crystalline state of PVDF from non‐polar α to polar β phase. Moreover, the crystallinity of the PVDF/PMMA/PVP ternary blends also decreases compared with neat PVDF. Through mechanical analysis, the elongation at break of the blends significantly increases to more than six times that of neat PVDF. This confirms that the addition of the PMMA/PVP blend enhances the toughness of PVDF. Besides, the hydrophilicity of PVDF is remarkably improved by blending with PMMA/PVP; in particular when the content of PVP reaches 30 wt%, the water contact angle displays its lowest value which decreased from 91.4° to 51.0°. Copyright © 2011 Society of Chemical Industry     

Probing the structure of polymer blends by vibrational spectroscopy: the case of poly(ethylene oxide) and poly(methyl methacrylate) blends

The blends of poly(ethylene oxide) (PEO) and poly(methyl methacrylate) (PMMA) are prepared in the form of thin films from solution casting. The Fourier transform infrared spectra of the blends are recorded in the spectral range 400–4000 cm^?1. The spectra are analysed using various recent techniques of vibrational spectroscopy. It is concluded that upon blending PEO takes preferentially a planar zig-zag structure. Furthermore the intermolecular interactions between the molecules of PEO and PMMA in blends are very weak and their compatibility as blends is more ‘physical’ than ‘chemical’. Further, on the basis of the atomic charges transferred from model molecules it is seen that the blending is preferred with isotactic PMMA when compared to syndiotactic PMMA.