Effect of annealing temperature on wettability of TiO2 nanotube array films

Highly ordered TiO₂ nanotube array (TN) films were prepared by anodization of titanium foil in a mixed electrolyte solution of glycerin and NH₄F and then annealed at 200°C, 400°C, 600°C, and 800°C, respectively. The samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), water contact angle (WCA), and photoluminescence (PL). It was found that low temperature (below 600°C) has no significant influence on surface morphology, but the diameter of the nanotube increases from 40 to 50 nm with increasing temperature. At 800°C, the nanotube arrays are completely destroyed and only dense rutile film is observed. Samples unannealed and annealed at 200°C are amorphous. At 400°C, anatase phase appears. At 600°C, rutile phase appears. At 800°C, anatase phase changes into rutile phase completely. The wettability of the TN films shows that the WCAs for all samples freshly annealed at different temperatures are about 0°. After the annealed samples have been stored in air for 1 month, the WCAs increase to 130°, 133°, 135°, 141°, and 77°, respectively. Upon ultraviolet (UV) irradiation, they exhibit a significant transition from hydrophobicity to hydrophilicity. Especially, samples unannealed and annealed at 400°C show high photoinduced hydrophilicity.     

Ni-doped TiO2 nanotubes for wide-range hydrogen sensing

Doping of titania nanotubes is one of the efficient way to obtain improved physical and chemical properties. Through electrochemical anodization and annealing treatment, Ni-doped TiO₂ nanotube arrays were fabricated and their hydrogen sensing performance was investigated. The nanotube sensor demonstrated a good sensitivity for wide-range detection of both dilute and high-concentration hydrogen atmospheres ranging from 50 ppm to 2% H₂. A temperature-dependent sensing from 25°C to 200°C was also found. Based on the experimental measurements and first-principles calculations, the electronic structure and hydrogen sensing properties of the Ni-doped TiO₂ with an anatase structure were also investigated. It reveals that Ni substitution of the Ti sites could induce significant inversion of the conductivity type and effective reduction of the bandgap of anatase oxide. The calculations also reveal that the resistance change for Ni-doped anatase TiO₂ with/without hydrogen absorption was closely related to the bandgap especially the Ni-induced impurity level.     

Anatase–rutile transformation in doped titania under argon and hydrogen atmospheres

Abstract

Pure titania pulp containing amorphous titania was heated at different temperatures and times. Above 650°C anatase phase was evolved and between 900 and 1000°C, anatase–rutile transformation occurred. The anatase–rutile transformation in TiO₂ in the presence of different transition metal oxides, namely Fe₂O₃, Cr₂O₃, NiO, CuO and MnO₂ under argon and hydrogen atmospheres was investigated. The different phases of TiO₂ were determined using powder X-ray diffraction (XRD). The anatase–rutile transformation temperature was found to be lowered in the presence of transition metal oxides. The transformation temperature was found to vary much in argon and hydrogen atmospheres compared to air in the presence of the metal oxides. Also the method of preparation of metal oxide doped TiO₂ influences rutilation. Other methods such as chemical analysis, surface area measurements and crystallite size calculation were used for the characterisation of the samples. The surface area of heated samples was found to be decreased while crystallite size increased due to rutilation on heating. The samples were also observed under a scanning electron microscope to characterise the microstructural changes associated with each thermal treatment and atmosphere. The morphology of doped titania changes much on heating due to phase modification. The atmosphere of heating also has important effect on deciding the morphology of rutilated titania.     

Preparation of hollow TiO2 nanoparticles through TiO2 deposition on polystyrene latex particles and characterizations of their structure and photocatalytic activity

In a mixed solvent of water and ethanol, polystyrene/titanium dioxide (PSt/TiO₂) composite particles of core-shell structure were prepared by hydrolysis of tetrabutyl titanate in the presence of cationic PSt particles or anionic PSt particles surface-treated using γ-aminopropyl triethoxysilane. Hollow TiO₂ particles were obtained through calcination of the PSt/TiO₂ core-shell particles to burn off the PSt core or through dissolution of the core by tetrahydrofuran (THF). An alternative process constituted of preheating the PSt/TiO₂ particles at 200°C to allow partial crystallization followed by calcination or PSt dissolution by THF. The outcome TiO₂ particles thus prepared were examined by TEM, and hollow TiO₂ particles were observed. The crystalline phase structure and phase transformation were characterized, which revealed that preheating before the removal of the PSt core was useful to achieve the desired hollow TiO₂ particles, and the calcination process was beneficial to the formation of anatase and rutile structures. The tests of TiO₂ particles as catalyst in the photodegradation of Rhodamine B demonstrated that a much higher catalytic activity was observed with the TiO₂ hollow particles prepared through calcination combined with preheating.     

Phase change and crystal growth of TiO2 in metatitanic acid

The transformation of anatase titanium dioxide (TiO₂) to its rutile form generally occurs above 600 °C. The anatase to rutile transformation is influenced by the factors such as heating temperature, heating time and the states of particles of anatase TiO₂. In the calcination of metatitanic acid, the phase transformation of anatase is a key step to form rutile TiO₂ particles with desirable morphological and pigmentary characteristics. However, the precise roles of temperature and time are not clear in the construction of so called calcination intensity for promoting the anatase-rutile transformation to form pigmentary TiO₂ from metatitanic acid. Here we show how the temperature and time have affected the anatase to rutile transformation and the crystal growth of metatitanic acid during the calcination. Through thermal analysis, XRD and SEM measurements, we found that the rutilization in metatitanic acid shows a similar growing trend in the most of phase transformation process. However, the trend of the transformation undergoes an abrupt change when rutilization is approaching to its completion. The changes of the morphology of metatitanic acid are related to the coarsening of the particles in the metatitanic acid during the calcination. Our results demonstrate that anatase to rutile transformation and coarsening of particles are affected by the heating temperature and heating time and the growth of TiO₂ particles can be controlled through calcination intensity.     

Sonosynthesis of nanostructured TiO2 doped with transition metals having variable bandgap

Here is described a sonosynthesis method to produce nanostructured TiO₂ pure and doped (Al, C, Co, Fe and Rh). The synthesized TiO₂ is amorphous and is transformed to anatase, brookite or rutile by heat treatments at temperatures between 100 and 300 °C. Pure TiO₂ can be partially transformed to brookite between 100 and 300 °C. The band gap in all heat treated samples from 100–600 °C is relatively constant, 3.2 eV, except for those doped with Fe. This effect on the band gap is the results of a bi/tri-crystal (anatase:brookite:rutile) framework. Rhodium is the most effective dopant to narrow the band gap, the opposite effect is observed with C. In single phase frameworks the bandgap can be modified ranges from 2.38 to 4.10 eV depending on the dopant. TiO₂ lattices are rigid enough to promote an outwards diffusion of the dopants to the surface of the particles forming nanostructured precipitates. The precipitates develop a network of quantum-dots with sizes between 5 and 10 nm.     

Tunable Nanostructures and Crystal Structures in Titanium Oxide Films

Controllable nanostructures in spin coated titanium oxide (TiO₂) films have been achieved by a very simple means, through change of post deposition annealing temperature. Electron beam imaging and reciprocal space analysis revealed as-deposited TiO₂ films to be characterized by a dominant anatase phase which converts to the rutile form at 600 °C and reverts to the anatase modification at 1,200 °C. The phase changes are also accompanied by changes in the film microstructure: from regular nanoparticles (as-deposited) to nanowires (600 °C) and finally to dendrite like shapes at 1,200 °C. Photoluminescence studies, Raman spectral results, and X-ray diffraction data also furnish evidence in support of the observed solid state phase transformations in TiO₂.     

Self-ordered TiO2 quantum dot array prepared via anodic oxidation

The template-based methods belong to low-cost and rapid preparation techniques for various nanostructures like nanowires, nanotubes, and nanodots or even quantum dots [QDs]. The nanostructured surfaces with QDs are very promising in the application as a sensor array, also called ''fluorescence array detector.'' In particular, this new sensing approach is suitable for the detection of various biomolecules (DNA, proteins) in vitro (in clinical diagnostics) as well as for in vivo imaging.The paper deals with the fabrication of TiO₂ planar nanostructures (QDs) by the process of titanium anodic oxidation through an alumina nanoporous template on a silicon substrate. Scanning electron microscopy observation showed that the average diameter of TiO₂ QDs is less than 10 nm. Raman spectroscopic characterization of self-organized titania QDs confirmed the presence of an anatase phase after annealing at 400°C in vacuum. Such heat-treated TiO₂ QDs revealed a broad emission peak in the visible range (characterized by fluorescence spectroscopy).     

TiO2 nanotubes and CNT–TiO2 hybrid materials for the photocatalytic oxidation of propene at low concentration

In this work, we investigated titanium dioxide (TiO₂) nanotubes and CNT–TiO₂ hybrid materials for the photocatalytic oxidation (PCO) of propene at low concentration (100 ppmv) in gaseous phase. The materials were prepared via sol–gel method using sacrificial multi-walled carbon nanotubes (CNT) as templates and subsequent heat treatments to obtain the desired crystalline phase (anatase, rutile or a mixture of both) and eventually to remove the carbon template. We also studied rutile nanotubes for the first time and demonstrate that the activity strongly depends on the crystalline composition, following rutile < anatase < anatase/rutile mixture. The enhanced activity of the anatase–rutile mixture is attributed to the decrease in the electron–hole pair recombination due to the multiphasic nature of the particles. The key result of this work is the exceptional performance of the CNT–TiO₂ hybrid, which yielded the highest observed photocatalytic activity. The improved performance is attributed to synergistic effects due to the hybrid nature of the material, resulting in small anatase crystalline sizes (CNT act as heat sinks) and a reduced electron–hole pair recombination rate (CNTs act as electron traps). These results demonstrate the great potential of hybrid materials and stimulate further research on CNT-inorganic hybrid materials in photocatalysis and related areas.     

Lithium-ion battery anode properties of TiO2 nanotubes prepared by the hydrothermal synthesis of mixed (anatase and rutile) particles

From mixed (anatase and rutile) bulk particles, anatase TiO₂ nanotubes are synthesized in this study by an alkaline hydrothermal reaction and a consequent annealing at 300-400 °C. The physical and electrochemical properties of the TiO₂ nanotube are investigated for use as an anode active material for lithium-ion batteries. Upon the first discharge-charge sweep and simultaneous impedance measurements at local potentials, this study shows that interfacial resistance decreases significantly when passing lithium ions through a solid electrolyte interface layer at the lithium insertion/deinsertion plateaus of 1.75/2.0 V, corresponding to the redox potentials of anatase TiO₂ nanotubes. For an anatase TiO₂ nanotube containing minor TiO₂(B) phase obtained after annealing at 300 °C, the high-rate capability can be strongly enhanced by an isotropic dispersion of TiO₂ nanotubes to yield a discharge capacity higher than 150 mAh g⁻¹, even upon 100 cycles of 10 C-rate discharge-charge operations. This is suitable for use as a high-power anode material for lithium-ion batteries.     

Controlled fabrication of Sn/TiO2 nanorods for photoelectrochemical water splitting

In this work, we investigate the controlled fabrication of Sn-doped TiO₂ nanorods (Sn/TiO₂ NRs) for photoelectrochemical water splitting. Sn is incorporated into the rutile TiO₂ nanorods with Sn/Ti molar ratios ranging from 0% to 3% by a simple solvothermal synthesis method. The obtained Sn/TiO₂ NRs are single crystalline with a rutile structure. The concentration of Sn in the final nanorods can be well controlled by adjusting the molar ratio of the precursors. Photoelectrochemical experiments are conducted to explore the photocatalytic activity of Sn/TiO₂ NRs with different doping levels. Under the illumination of solar simulator with the light intensity of 100 mW/cm², our measurements reveal that the photocurrent increases with increasing doping level and reaches the maximum value of 1.01 mA/cm² at −0.4 V versus Ag/AgCl, which corresponds to up to about 50% enhancement compared with the pristine TiO₂ NRs. The Mott-Schottky plots indicate that incorporation of Sn into TiO₂ nanorod can significantly increase the charge carrier density, leading to enhanced conductivity of the nanorod. Furthermore, we demonstrate that Sn/TiO₂ NRs can be a promising candidate for photoanode in photoelectrochemical water splitting because of their excellent chemical stability.     

HIPed TiO2 dense pellets with improved photocatalytic performance

The effects of heating method and temperature on physical, structural and photocatalytic behaviors of TiO₂ pellets prepared by conventional heating and hot isostatic pressing have been evaluated. The pellets of submicron TiO₂ powders were heated to 600, 650, 700, 750 and 1000 °C using both processing methods in order to compare anatase to rutile phase transformation and densification behaviors. Bulk densities and porosities were calculated using the Archimedes method. XRD analysis were performed to calculate anatase/rutile ratios. Microstructures were characterized using SEM. Photocatalytic experiments have been performed under full spectrum irradiation. Degraded methylene blue samples were periodically monitored through UV–vis spectrophotometer to determine degradation kinetics. Anatase to rutile transformation is slightly faster and densification is better for lower temperatures for conventional heating, however HIPing gives better densification above 750 °C as it also retards rutile transformation. Mixed phase structures and HIPed samples showed the best photocatalytic performance which makes this method advantageous.     

Growth and characterization of TiO2 nanotubes from sputtered Ti film on Si substrate

In this paper, we present the synthesis of self-organized TiO₂ nanotube arrays formed by anodization of thin Ti film deposited on Si wafers by direct current (D.C.) sputtering. Organic electrolyte was used to demonstrate the growth of stable nanotubes at room temperature with voltages varying from 10 to 60 V (D.C.). The tubes were about 1.4 times longer than the thickness of the sputtered Ti film, showing little undesired dissolution of the metal in the electrolyte during anodization. By varying the thickness of the deposited Ti film, the length of the nanotubes could be controlled precisely irrespective of longer anodization time and/or anodization voltage. Scanning electron microscopy, atomic force microscopy, diffuse-reflectance UV–vis spectroscopy, and X-ray diffraction were used to characterize the thin film nanotubes. The tubes exhibited good adhesion to the wafer and did not peel off after annealing in air at 350 °C to form anatase TiO₂. With TiO₂ nanotubes on planar/stable Si substrates, one can envision their integration with the current micro-fabrication technique large-scale fabrication of TiO₂ nanotube-based devices.     

Decomposition of nonionic surfactant on a nitrogen-doped photocatalyst under visible-light irradiation

A visible-light-active N-containing TiO₂ photocatalysts were prepared from crude amorphous titanium dioxide by heating amorphous TiO₂ in gaseous NH₃ atmosphere. The calcination temperatures ranged from 200 to 1000 °C, respectively. UV–vis/DR spectra indicated that the N-doped catalysts prepared at temperatures <400 °C absorbed only UV light (E_g = 3.3 eV), whereas samples prepared at temperatures ≥400 °C absorbed both, UV (E_g = 3.10–3.31 eV) and vis (E_g = 2.54–2.66 eV) light. The chemical structure of the modified photocatalysts was investigated using FT-IR/DRS spectroscopy. All the spectra exhibited bands indicating nitrogen presence in the catalysts structure. The photocatalytic activity of the investigated catalysts was determined on a basis of a decomposition rate of nonionic surfactant (polyoxyethylenenonylphenol ether, Rokafenol N9). The most photoactive catalysts were those calcinated at 300, 500 and 600 °C. For the catalysts heated at temperatures of 500 and 600 °C Rokafenol N9 removal was equal to 61 and 60%, whereas TOC removal amounted to 40 and 35%, respectively. In case of the catalyst calcinated at 300 °C surfactant was degraded by 54% and TOC was removed by 35%. The phase composition of the most active photocatalysts was as follows: (a) catalyst calcinated at 300 °C—49.1% of amorphous TiO₂, 47.4% of anatase and 3.5% of rutile; (b) catalyst calcinated at 500 °C—7.1% of amorphous TiO₂, 89.4% of anatase and 3.5% of rutile; (c) catalyst calcinated at 600 °C—94.2% of anatase and 5.8% of rutile.     

Hydrothermal synthesis of S-doped TiO2 nanoparticles and their photocatalytic ability for degradation of methyl orange

A simple synthesis route to nanocrystalline S-doped TiO₂ photocatalysts by a hydrothermal method at 180 °C was developed and the photocatalytic activity of the obtained powders for the degradation of methyl orange was studied. The products were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The phase composition (anatase/rutile ratio) and the photocatalytic activity of the final materials were found to be markedly influenced by the amount of the incorporated sulphur. On increasing the S-dopant amount, the anatase/rutile ratio and the photocatalytic activity of the as-prepared powders increased.     

Simple fabrication of N-doped mesoporous TiO2 nanorods with the enhanced visible light photocatalytic activity

N-doped mesoporous TiO₂ nanorods were fabricated by a modified and facile sol–gel approach without any templates. Ammonium nitrate was used as a raw source of N dopants, which could produce a lot of gasses such as N₂, NO₂, and H₂O in the process of heating samples. These gasses were proved to be vitally important to form the special mesoporous structure. The samples were characterized by the powder X-ray diffraction, X-ray photoelectron spectrometer, nitrogen adsorption isotherms, scanning electron microscopy, transmission electron microscopy, and UV-visible absorption spectra. The average length and the cross section diameter of the as-prepared samples were ca. 1.5 μm and ca. 80 nm, respectively. The photocatalytic activity was evaluated by photodegradation of methylene blue (MB) in aqueous solution. The N-doped mesoporous TiO₂ nanorods showed an excellent photocatalytic activity, which may be attributed to the enlarged surface area (106.4 m² g^-1) and the narrowed band gap (2.05 eV). Besides, the rod-like photocatalyst was found to be easy to recycle.     

The effects of firing conditions on the properties of electrophoretically deposited titanium dioxide films on graphite substrates

Thick anatase films were fabricated on graphite substrates using a method of anodic aqueous electrophoretic-deposition using oxalic acid as a dispersant. Thick films were subsequently fired in air and in nitrogen at a range of temperatures. The morphology and phase composition were assessed and the photocatalytic performance was examined by the inactivation of Escherichia coli in water. It was found that the transformation of anatase to rutile is enhanced by the presence of a graphite substrate through reduction effects. The use of a nitrogen atmosphere allows higher firing temperatures, results in less cracking of the films and yields superior bactericidal performance in comparison with firing in air. The beneficial effects of a nitrogen firing atmosphere on the photocatalytic performance of the material are likely to be a result of the diffusion of nitrogen and carbon into the TiO₂ lattice and the consequent creation of new valence band states.     

CNT@TiO2 nanohybrids for high-performance anode of lithium-ion batteries

This work describes a potential anode material for lithium-ion batteries (LIBs), namely, anatase TiO₂ nanoparticle-decorated carbon nanotubes (CNTs@TiO₂). The electrochemical properties of CNTs@TiO₂ were thoroughly investigated using various electrochemical techniques, including cyclic voltammetry, electrochemical impedance spectroscopy, galvanostatic cycling, and rate experiments. It was revealed that compared with pure TiO₂ nanoparticles and CNTs alone, the CNT@TiO₂ nanohybrids offered superior rate capability and achieved better cycling performance when used as anodes of LIBs. The CNT@TiO₂ nanohybrids exhibited a cycling stability with high reversible capacity of about 190 mAh g^-1 after 120 cycles at a current density of 100 mA g^-1 and an excellent rate capability (up to 100 mAh g^-1 at a current density of 1,000 mA g^-1).     

Properties of sol-gel SnO2/TiO2 electrodes and their photoelectrocatalytic activities under UV and visible light illumination

A visible light active binary SnO₂-TiO₂ composite was successfully prepared by a sol-gel method and deposited on Ti sheet as a photoanode to degrade orange II dye. Titanium and SnO₂ can promote the development of rutile phase of TiO₂ and inhibit the formation of anatase phase of TiO₂. Formation of SnO₂ crystalline is insignificant even when the calcination temperature increases to 700 °C. Heterogenized interface between SnO₂ and TiO₂ inhibits growth of TiO₂ linkage and leads to the particle-filled surface morphology of SnO₂-containing films. The carbonaceous, Ti-O-C bonds and Ti³⁺ species are likely to account for the photoabsorption and photoelectrocatalytic (PEC) activity under visible light illumination. The electrode with 30% SnO₂ exhibits higher photocurrent when compared with those in the region of 0-50%. The 600 °C-calcined SnO₂-TiO₂ electrode indicates higher activity when compared with those at 400, 500, 700 and 800 °C. PEC degradation of orange II follows the Langmuir-Hinshelwood model and takes place much effectively in a solution of pH 3.0 than those in pH 7.0 and pH 11.0.     

Activity of Laccase Immobilized on TiO2-Montmorillonite Complexes

The TiO₂-montmorillonite (TiO₂-MMT) complex was prepared by blending TiO₂ sol and MMT with certain ratio, and its properties as an enzyme immobilization support were investigated. The pristine MMT and TiO₂-MMT calcined at 800 °C (TiO₂-MMT800) were used for comparison to better understand the immobilization mechanism. The structures of the pristine MMT, TiO₂-MMT, and TiO₂-MMT800 were examined by HR-TEM, XRD and BET. SEM was employed to study different morphologies before and after laccase immobilization. Activity and kinetic parameters of the immobilized laccase were also determined. It was found that the TiO₂ nanoparticles were successfully introduced into the MMT layer structure, and this intercalation enlarged the “d value” of two adjacent MMT layers and increased the surface area, while the calcination process led to a complete collapse of the MMT layers. SEM results showed that the clays were well coated with adsorbed enzymes. The study of laccase activity revealed that the optimum pH and temperature were pH = 3 and 60 °C, respectively. In addition, the storage stability for the immobilized laccase was satisfactory. The kinetic properties indicated that laccase immobilized on TiO₂-MMT complexes had a good affinity to the substrate. It has been proved that TiO₂-MMT complex is a good candidate for enzyme immobilization.