Phase Equilibria in the System FeO-Fe<Subscript>2</Subscript>O<Subscript>3</Subscript>-SiO<Subscript>2</Subscript>

Liquidus data are presented for mixtures in the ternary system FeO-Fe₂O₃-SiO₂ in equilibrium with a gas phase with O₂ pressures ranging from 10^?10.9 to 1 atm. Data obtained are combined with previously published data to construct lines of equal O₂ pressures and lines of equal CO₂/H₂ mixing ratios along the liquidus surface. Courses of crystallization of selected mixtures under conditions of constant total composition, constant O₂ pressures, and constant CO₂/H₂ mixing ratios are discussed.     

Constitution of the FeO-Fe<Subscript>2</Subscript>O<Subscript>3</Subscript>-SiO<Subscript>2</Subscript> System at Slagmaking Temperatures

Liquidus surfaces in the ternary system Fe0-Fe₂O₃-SiO₂ were determined from 1250° to 1450°C by the procedure of equilibrating small samples in platinum crucibles, quenching, and microscopic examination. The experimental results were combined with previously published information to construct a ternary diagram for the system showing the entire temperature-composition range of stability of iron silicate slags. Metallurgical applications of the diagram, especially in copper smelting, are discussed briefly.     

Experimental Study and Thermodynamic Re-optimization of the FeO-Fe<Subscript>2</Subscript>O<Subscript>3</Subscript>-SiO<Subscript>2</Subscript> System

Phase equilibria and thermodynamic data in the FeO-Fe₂O₃-SiO₂ system were critically reviewed. New experiments were undertaken to resolve discrepancies found in previous data. The liquid oxide/slag phase was described using the modified quasichemical model. New optimized parameters of the thermodynamic models for the Gibbs energies of slag and other phases in the selected system were obtained. The new parameters reproduce all available phase equilibria and thermodynamic data within the experimental error limits from 298 K (25 °C) to above the liquidus temperatures at all compositions and oxygen partial pressures from metal saturation to 1 atm of O₂. This study was carried out as part of the development of a self-consistent thermodynamic database for the Al-Ca-Cu-Fe-Mg-Si-O-S multi-component system.     

Experimental study of the Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>-Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> pseudo-binary system

As part of a general contribution to the study of accelerator driven system (ADS) nuclear reactor feasibility, a study of the five-component system Bi-Fe-Hg-O-Pb was undertaken. New results about the quasi-binary Bi₂O₃-Fe₂O₃ are presented in this paper. The phase diagram was reinvestigated by differential scanning calorimetry, x-ray diffraction, and electron probe microanalysis. A new compound was discovered and characterized: Bi₂₅FeO₄₀. Its crystallographic structure was refined. Invariant and transition temperatures are given, as well as phase compositions.     

Up-Date of a Thermodynamic Database of the ZrO<Subscript>2</Subscript>-Gd<Subscript>2</Subscript>O<Subscript>3</Subscript>-Y<Subscript>2</Subscript>O<Subscript>3</Subscript>-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> System for TBC Applications

The thermodynamic database of the ZrO₂-Gd₂O₃-Y₂O₃-Al₂O₃ system is up-dated taking into account new data on lattice stabilities of ZrO₂, Gd₂O₃ and Y₂O₃ and heat capacity measurements for the monoclinic phase Gd₄Al₂O₉ and phase with garnet structure Gd₃Al₅O₁₂. New data for the heat capacities of Gd₂Zr₂O₇ (pyrochlore) and GdAlO₃ (perovskite) as well as on the enthalpy of formation of fluorite solid solutions (Zr_1−x Gd _x )O_2−x/2 were found to be in good agreement with calculated results. In comparison with the previous assessment, taking into account new experimental data resulted in a change of the melting character of the Gd₄Al₂O₉ phase from a peritectic one to a congruent one in the Gd₂O₃-Al₂O₃ system. Correspondently, in the ternary system ZrO₂-Gd₂O₃-Al₂O₃, the melting character of the three-phase assemblage Gd₂O₃ (B), Gd₄Al₂O₉ and GdAlO₃ changed from eutectic to transition type U. The T ₀-lines for T/M and F/T diffusionless transformations and driving force of partitioning to equilibrium assemblage T + F were calculated in the ZrO₂-Gd₂O₃-Y₂O₃ system.     

Thermodynamic optimization of the Na<Subscript>2</Subscript>O-B<Subscript>2</Subscript>O<Subscript>3</Subscript> pseudo-binary system

The Na₂O-B₂O₃ system is thermodynamically optimized by means of the CALPHAD method. A two-sublattice ionic solution model, (Na⁺¹)_P(O⁻²,BO₃ ⁻³,B₄O₇ ⁻²,B₃O_4.5)_Q, has been used to describe the liquid phase. All the solid phases were treated as stoichiometric compounds. A set of thermodynamic parameters, which can reproduce most experimental data of both phase diagram and thermodynamic properties, was obtained. Comparisons between the calculated results and experimental data are presented.     

Development and Application of Binary Suspensions in the Ternary System Cr<Subscript>2</Subscript>O<Subscript>3</Subscript>-TiO<Subscript>2</Subscript>-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> for S-HVOF Spraying

Compositions in the system Cr₂O₃-TiO₂-Al₂O₃ are among the most used ceramic materials for thermally sprayed coating solutions. Cr₂O₃ coatings present good sliding wear resistance; Al₂O₃ coatings show excellent insulation behavior and TiO₂ striking corrosion properties. In order to combine these properties, coatings containing more than one oxide are highly interesting. The conventional spraying process is limited to the availability of binary feedstock powders with defined compositions. The use of suspensions offers the opportunity for tailor-made chemical compositions: within the triangle of Cr₂O₃-TiO₂-Al₂O₃, each mixture of oxides can be created. Criteria for the selection of raw materials as well as the relevant aspects for the development of binary suspensions in the Cr₂O₃-TiO₂-Al₂O₃ system to be used as feedstock for thermal spraying are presented. This formulation of binary suspensions required the development of water-based single-oxide suspensions with suitable behavior; otherwise, the interaction between the particles while mixing could lead up to a formation of agglomerates, which affect both the stability of the spray process and the coating properties. For the validation of this formulation procedure, binary Cr₂O₃-TiO₂ and Al₂O₃-TiO₂ suspensions were developed and sprayed using the S-HVOF process. The binary coatings were characterized and discussed in terms of microstructure and microhardness.     

Phase Formation of the Yttrium Aluminates in the Y<Subscript>2</Subscript>O<Subscript>3</Subscript>-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-SiC System

Phase formation sequence of the yttrium aluminates in the Y₂O₃-Al₂O₃-SiC ternary system as temperature increases were investigated via x-ray diffraction (XRD). Results showed that YAM (monoclinic), YAP (perovskite) and YAG (garnet) were the yttrium aluminates presented in the solid-state reacted samples at a fixed Al₂O₃:SiC ratio of 1:1. Formation of the yttrium aluminates depended on the temperature. The YAM, YAP and YAG started to form below 1150 °C, at 1300 °C, and at 1450 °C, respectively. Accordingly, two behavior phase diagrams of the Y₂O₃-Al₂O₃-SiC ternary system were recognized, one is in the temperature range of 1150-1300 °C and the other is in 1300-1450 °C, respectively. Thereafter, the phase equilibrium was reached in the temperature range of 1450-1700 °C. Effects of SiC on the phase formation processes in the ternary system were discussed.     

Studies on Al<Subscript>2</Subscript>O<Subscript>3</Subscript>/ZrO<Subscript>2</Subscript>/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> high K gate dielectrics applied in a fully depleted SOI MOSFET

Al₂O₃/ZrO₂/Al₂O₃ gate stacks were prepared on ultrathin SOI (Silicon on insulator) substrates by ultrahigh vacuum electron beam evaporation and post-annealed in N₂ at 450°C for 30 min. Three clear nanolaminate layered structure of Al₂O₃(2.1 nm)/ZrO₂(3.5 nm)/Al₂O₃(2.3 nm) was observed with a high-resolution cross-sectional transmission electron microscope (HR-XTEM). High frequency capacitance voltage (C-V) characteristics of a fully depleted (FD) SOI MOS capacitor at 1 and 5 MHz were studied. The minority carriers determine the high frequency C-V properties, which is opposite to the case of bulk MOS capacitors. The series resistance of the SOI substrate is found to be the determinant factor of the high frequency characteristics of FD SOI MOS capacitors. This article is based on a presentation in “The 7th Korea-China Workshop on Advanced Materials” organized by the Korea-China Advanced Materials Cooperation Center and the China-Korea Advanced Materials Cooperation Center, held at Ramada Plaza Jeju Hotel, Jeju Island, Korea on August 24≈27, 2003.     

Structure and electric property comparison between Ge nanoclusters embedded in Al<Subscript>2</Subscript>O<Subscript>3</Subscript> and Al<Subscript>2</Subscript>O<Subscript>3</Subscript>/ZrO<Subscript>2</Subscript>

Metal-insulator-semiconductor (MIS) structures containing Ge nanocrystals embedded in both Al₂O₃ and ZrO₂/Al₂O₃ are fabricated by an ultra-high vacuum electron-beam evaporation method. Secondary ion mass spectroscopy (SIMS) results indicate that Ge embedded in Al₂O₃ diffuses towards the surface of the Al₂O₃ layer after annealing at 800°C in N₂ ambient for 30 min. Ge embedded in ZrO₂/Al₂O₃ is stable, thus inducing less leakage current. Capacitance voltage studies indicate that annealing can effectively passivate the negatively charged trapping centers. Memory effect of the Ge nanoclusters is verified by hysteresis in the C-V curves in the Al₂O₃/Ge+Al₂O₃/Al₂O₃ and ZrO₂/Ge+Al₂O₃/Al₂O₃ samples. This article is based on a presentation in “The 7th Korea-China Workshop On Advanced Materials” organized by the Korea-China Advanced Materials Cooperation Center and the China-Korea Advanced Materials Cooperation Center, held at Ramada Plaza Jeju Hotel, Jeju Island, Korea on August 24–27, 2003.     

Phase Relations in the ZrO<Subscript>2</Subscript>-Nd<Subscript>2</Subscript>O<Subscript>3</Subscript>-Y<Subscript>2</Subscript>O<Subscript>3</Subscript> System: Experimental Study and Advanced Thermodynamic Modeling

Phase equilibria in the ZrO₂-Nd₂O₃-Y₂O₃ system at 1523-1873 K have been investigated by x-ray diffraction (XRD) and scanning electron microscopy combined with energy dispersive x-ray spectroscopy (SEM/EDX). Temperatures of phase transformations were determined by differential thermal analysis. Temperatures of invariant reactions in the ZrO₂-Nd₂O₃ system F = A + Pyr and H = F + A were determined as 1763 and 2118 K respectively and thermodynamic parameters of phases were re-assessed. Phase transformations in ternary systems were determined at 1732 K for composition ZrO₂-48.46Nd₂O₃-5.38Y₂O₃ (mol%) and at 1744 and 1881 K for composition ZrO₂-79.09Nd₂O₃-2.75Y₂O₃ (mol%). They were interpreted using XRD investigation before and after DTA as Pyr + B → F, Pyr → F and A → B, respectively. The solubility of the Y₂O₃ in pyrochlore phase was found to exceed 10 mol%. The thermodynamic parameters of the ZrO₂-Nd₂O₃-Y₂O₃ system were reassessed taking into account solubility of Y₂O₃ in the Nd₂Zr₂O₇ pyrochlore phase (Pyr). It is assumed that Y³⁺ substitutes Nd³⁺ and Zr⁴⁺ in their preferentially occupied sublattices. Ternary parameter was introduced into fluorite phase (F) for better reproducing of phase equilibria. Mixing parameters were reassessed for phase A (Nd₂O₃ based solution), monoclinic phase B and cubic phase C (Y₂O₃ based solution). The isothermal sections calculated for the ZrO₂-Nd₂O₃-Y₂O₃ system are in the reasonable agreement with experimental results.     

Effect of Al<Subscript>2</Subscript>O<Subscript>3</Subscript> Content on Electrical Breakdown Properties of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>/Cu Composite

Al₂O₃/Cu composites were prepared by external addition of Al₂O₃, and the effect of Al₂O₃ content on microstructure, density, hardness, electrical conductivity and vacuum electrical breakdown properties was studied. The results show that with increasing Al₂O₃ addition, the density of Al₂O₃/Cu composite significantly decreases, the hardness sharply increases and then slowly decreases, but the electrical conductivity invariably decreases. The vacuum breakdown test shows that with increasing Al₂O₃ addition, the breakdown strength first sharply increases and then decreases when the Al₂O₃ content exceeds 1.2 wt.%; the chopping current always exhibits a decreasing trend and the arc life first increases and then decreases. According to the morphology of arc erosion and analysis, the arc erosion resistance increases and then decreases sharply. In the range of experiments, the optimal arc erosion resistance of Al₂O₃/Cu composite can be obtained with the addition of 1.2 wt.% Al₂O₃.     

Surface modification of LiNi<Subscript>1/3</Subscript>Co<Subscript>1/3</Subscript>Mn<Subscript>1/3</Subscript>O<Subscript>2</Subscript> with Cr<Subscript>2</Subscript>O<Subscript>3</Subscript> for lithium ion batteries

Cr 2 O 3-coated LiNi 1/3 Co 1/3 Mn 1/3 O 2 cathode materials were synthesized by a novel method. The structure and electrochemical properties of prepared cathode materials were measured using X-ray diffraction (XRD), scanning electron microscopy (SEM), charge-discharge tests, cyclic voltammetry (CV), and electrochemical impedance spectroscopy (EIS). The measured results indicate that surface coating with 1.0 wt% Cr 2 O 3 does not affect the LiNi 1/3 Co 1/3 Mn 1/3 O 2 crystal structure (α-NaFeO 2 ) of the cathode material compared to the pristine material, the surfaces of LiNi 1/3 Co 1/3 Mn 1/3 O 2 samples are covered with Cr 2 O 3 well, and the LiNi 1/3 Co 1/3 Mn 1/3 O 2 material coated with Cr 2 O 3 has better electrochemical performance under a high cutoff voltage of 4.5 V. Moreover, at room temperature, the initial discharging capacity of LiNi 1/3 Co 1/3 Mn 1/3 O 2 material coated with 1.0 wt.% Cr 2 O 3 at 0.5C reaches 169 mAh·g 1 and the capacity retention is 83.1% after 30 cycles, while that of the bare LiNi 1/3 Co 1/3 Mn 1/3 O 2 is only 160.8 mAh·g 1 and 72.5%. Finally, the coated samples are found to display the improved electrochemical performance, which is mainly attributed to the suppression of the charge-transfer resistance at the interface between the cathode and the electrolyte.     

Hydrogen generation from the H<Subscript>2</Subscript>O/H<Subscript>2</Subscript>O<Subscript>2</Subscript> /MnMoO<Subscript>4</Subscript> system

Hydrogen gas as a clean energy resource was found to be largely bubbled from the H₂O/H₂O₂/MnMoO₄ system. The MnMoO₄ powder was synthesized by a sol-gel method and was characterized with x-ray diffraction, transmission electron microscopy, and x-ray photoelectron spectrometry. The efficiency of the hydrogen generation increases with increasing H₂O₂ proportion, amount of MnMoO₄ powder, and intensity of light resource. A mechanism is suggested for hydrogen generation from the H₂O/H₂O₂/MnMoO₄ system.     

Fabrication by Electrophoretic Deposition of Nano-Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> and Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>@SiO<Subscript>2</Subscript> 3D Structure on Carbon Fibers as Supercapacitor Materials

Core–shell nanostructured magnetic Fe₃O₄@SiO₂ with particle size ranging from 3 nm to 40 nm has been synthesized via a facile precipitation method. Tetraethyl orthosilicate was employed as surfactant to prepare core–shell structures from Fe₃O₄ nanoparticles synthesized from pomegranate peel extract using a green method. X-ray diffraction analysis, Fourier-transform infrared and ultraviolet–visible (UV–Vis) spectroscopies, transmission electron microscopy, and scanning electron microscopy with energy-dispersive spectroscopy were employed to characterize the samples. The prepared Fe₃O₄ nanoparticles were approximately 12 nm in size, and the thickness of the SiO₂ shell was?~?4 nm. Evaluation of the magnetic properties indicated lower saturation magnetization for Fe₃O₄@SiO₂ powder (~?11.26 emu/g) compared with Fe₃O₄ powder (~?13.30 emu/g), supporting successful wrapping of the Fe₃O₄ nanoparticles by SiO₂. As-prepared powders were deposited on carbon fibers (CFs) using electrophoretic deposition and their electrochemical behavior investigated. The rectangular-shaped cyclic voltagrams of Fe₃O₄@CF and Fe₃O₄@C@CF samples indicated electrochemical double-layer capacitor (EDLC) behavior. The higher specific capacitance of 477 F/g for Fe₃O₄@C@CF (at scan rate of 0.05 V/s in the potential range of ??1.13 to 0.45 V) compared with 205 F/g for Fe₃O₄@CF (at the same scan rate in the potential range of?~???1.04 to 0.24 V) makes the former a superior candidate for use in energy storage applications.     

Thermal and structural role of additives in P<Subscript>2</Subscript>O<Subscript>5</Subscript>-ZnO-Sb<Subscript>2</Subscript>O<Subscript>3</Subscript> glass for low expansion sealing materials

A glass based on the P₂O₅-ZnO-Sb₂O₃ ternary system was modified with various additives, such as RO (R=Ca, Ba and Mn), B₂O₃ and V₂O₅, for low temperature and low expansion sealing materials. The glass transition temperature (T_g) and coefficient of thermal expansion (CTE) were monitored and reduced with additive compositions of RO. Additional incorporation of B₂O₃ at the expense of RO also showed a similar result. Significant improvement was observed when the glass was modified with V₂O_5. A glass showing T_g<350 °C along with CTE<65×10⁻⁷/°C was found, suggesting a high potential for low temperature sealing materials especially for display applications. The role of the quaternary element within the glass is discussed, along with the structural effect using Raman spectroscopy.     

Preparation and optical properties of Y<Subscript>2</Subscript>O<Subscript>3</Subscript>/SiO<Subscript>2</Subscript> powder

Y(NO3)3 and NH3·H2O were used as a raw materials,and nano-Y2O3 powder was successfully synthesized by a precipitation method.Employing TEOS as a raw material,SiO2 powder was successfully prepared by a alkoxide-hydrolysis method,and a Y2O3/SiO2 composite powder was obtained by coating.The Y2O3,SiO2,and Y2O3/SiO2 powders were characterized using X-ray diffraction(XRD),scanning electron microscopy(SEM),and Fourier transform infrared spectrophotometer(FT-IR);the Y2O3 and Y2O3/SiO2 powders were further examined ...