Investigation of poly(lactide) stereocomplexation between linear poly(L‐lactide) and PDLA‐PEG‐PDLA tri‐block copolymer

In this study, stereocomplexed poly(lactide) (PLA) was investigated by blending linear poly(l ‐lactide) (PLLA) and tri‐block copolymer poly(d ‐lactide) ? (polyethylene glycol) ? poly(d ‐lactide) (PDLA‐PEG‐PDLA). Synthesized PDLA‐PEG‐PDLA tri‐block copolymers with different PEG and PDLA segment lengths were studied and their influences on the degree of sterecomplexation and non‐isothermal crystallization behaviour of the PLLA/PDLA‐PEG‐PDLA blend were examined in detail by DSC, XRD and polarized optical microscopy. A full stereocomplexation between PLLA and PDLA‐PEG_4k‐PDLA200 could be formed when the L/D ratio ranged from 7/3 to 5/5 without the presence of PLA homocrystals. The segmental mobility and length of both PEG and PDLA are the dominating factors in the critical D/L ratio to achieve full stereocomplexation and also for nucleation and spherulite growth during the non‐isothermal crystallization process. For fixed PEG segmental length, the stereocomplexed PLA formed showed first an increasing and then a decreasing melting temperature with increasing PDLA segments due to their intrinsic stiff mobility. Furthermore, the effect of PEG segmental mobility on PLA stereocomplexation was investigated. The results clearly showed that the crystallization temperature and melting temperature of stereocomplexed‐PLA kept increasing with increasing PEG segmental length, which was due to PEG soft mobility in the tri‐block copolymers. However, PEG was not favourable for nucleation but could facilitate the spherulite growth rate. Both the PDLA and PEG segmental lengths in the tri‐block copolymers affect the crystallinity of stereocomplexed‐PLA and the stereocomplexation formation process; they have a different influence on blends prepared by solution casting or the melting method. © 2015 Society of Chemical Industry     

Enhanced crystallization rate and mechanical properties of poly(l‐lactic acid) by stereocomplexation with four‐armed poly(ϵ‐caprolactone)‐block‐poly(d‐lactic acid) diblock copolymer

Poly(l ‐lactic acid) (PLLA) was blended with a series of four‐armed poly(? ‐caprolactone)‐block ‐poly(d ‐lactic acid) (4a‐PCL‐b ‐PDLA) copolymers in order to improve its crystallization rate and mechanical properties. It is found that a higher content of 4a‐PCL‐b ‐PDLA copolymer or longer PDLA block in the copolymer lead to faster crystallization of the blend, which is attributed to the formation of stereocomplex crystallites between PLLA matrix and PDLA blocks of the 4a‐PCL‐b ‐PDLA copolymers. Meanwhile, the PDLA block can improve the miscibility between flexible PCL phase and PLLA phase, which is beneficial for improving mechanical properties. The tensile results indicate that the 10% 4a‐PCL_5k‐b ‐PDLA_5k/PLLA blend has the largest elongation at break of about 72% because of the synergistic effects of stereocomplexation between enantiomeric PLAs, multi‐arm structure and plasticization of PCL blocks. It is concluded that well‐controlled composition and content of 4a‐PCL‐b ‐PDLA copolymer in PLLA blends can significantly improve the crystallization rate and mechanical properties of the PLLA matrix. © 2017 Society of Chemical Industry     

Thermomechanical properties of stereoblock poly(lactic acid)s with different PLLA/PDLA block compositions

Stereoblock poly(lactic acids) (sb-PLAs), having abundant enantiomeric compositions of poly(l-lactic acid) (PLLA), were successfully synthesized by solid-state polycondensation (SSP) of the melt blends of medium molecular weight prepolymers: both PLLA and poly(d-lactic acid) (PDLA) that had primarily been prepared by melt-polycondensation. The molecular weight of the resultant PLLA-rich sb-PLA was effectively enhanced by the dehydrative coupling of abundant PLLA molecules followed by the increase in homo-chiral crystallinity. These sb-PLA were successfully fabricated into polymer films by solution casting to analyze their crystalline morphology and properties. Both DSC and WAXS revealed preferential stereocomplexation in spite of concomitant homo-chiral crystallization for these sb-PLA. Particularly, exclusive sc crystallization was observed with melt-quenched sb-PLA represented whose PDLA ratio was above 15%. Therefore, the stereoblock structure can suppress the homo-chiral crystallization and increase the sc crystallinity even with the non-equivalent PLLA/PDLA compositions. Their thermal resistivity up to 200 °C was supported by the dynamic mechanical analysis of the sb-PLA films.     

不同构型聚乳酸共混体系的立构复合结晶研究进展

左旋聚乳酸(PLLA)和右旋聚乳酸(PDLA)在共混体系中可形成立构复合(sc)结晶,与聚乳酸(PLA)同质结晶材料相比,sc 结晶材料具有良好的耐热性和耐化学稳定性。因此,sc 结晶是改善PLA 综合性能的一种有效手段。但在PLLA/PDLA 共混体系中,存在各自的同质结晶与两者之间sc 结晶的竞争,所以制备高耐热sc 型PLA 材料的关键之一是理解其sc 结晶的形成条件与机理,进而调控和促进其sc 结晶程度。在PLLA/PDLA 共混物中,sc 结晶受聚合物化学结构、结晶与加工条件等诸多因素影响,其影响规律和机理较复杂。根据PLLA/PDLA共混物sc 结晶行为影响因素的不同,从聚合物分子量、立构规整性、共混比例、分子链拓扑结构、结晶方式与条件、加工助剂和其他组分加入6 个方面出发,详细综述了PLLA/PDLA 共混物sc 结晶及其sc 材料制备的研究进展,以期为高耐热生物基PLA 材料的加工制备提供指导。     

Stereocomplexation of solvent‐cast poly(lactic acid) by addition of non‐solvents

Equimolar blends of poly(L ‐lactic acid) (PLLA) and poly(D ‐lactic acid) (PDLA) were obtained by solution casting from chloroform/methanol mixed solvents and analyzed using wide‐angle X‐ray diffraction (WAXD), differential scanning calorimetry (DSC) and polarizing optical microscopy. Chloroform and methanol are a solvent and non‐solvent, respectively, for poly(lactic acid). The WAXD and DSC results showed that stereocomplex crystallization between PLLA and PDLA occurred in addition to homo‐crystallization. On adding methanol to the casting solution, the stereocomplexation was gradually enhanced while the homo‐crystallization was suppressed. When a large amount of methanol was added, the homo‐crystallization was fully suppressed and the degree of stereocomplex crystallinity reached 90%. Similar results were obtained when another non‐solvent, hexane, was added to the casting solution in place of methanol. The effect of the addition of good and poor solvents such as tetrahydrofuran, ethanol, acetone and ethyl acetate was also studied. Copyright © 2011 Society of Chemical Industry     

The toughening behavior of PLLA and its asymmetric PLLA/PDLA blends with lower optical purity

Linear poly(d ‐lactide) (PDLA) with various molecular weights is synthesized and incorporated into commercial poly(l ‐lactide) (PLLA) with different optical purities. And then, the crystallization, mechanical and thermal properties of the PLLA and PLLA/PDLA cast films are investigated. In the PLLA and PDLA/PLLA specimens with lower optical purity, few homochiral crystallites (HC) form in all the specimens and only a small amount of PLA stereocomplex crystallites (SC) are observed in the blends. The elongation at break of all the specimens is extraordinary high, >300%. Dynamic mechanical analyses indicate that the destruction temperature increases at first, and then depresses as enlarging the molecular weight of PDLA in these blends. For the PLLA and PLLA/PDLA with higher optical purity, more content of HC develops in neat PLLA, and both SC and HC produce in the PLLA/PDLA specimens. However, the strains of neat specimens and binary blends are much lower than that of specimens with lower optical purity. The specimens with higher optical purity exhibit higher destruction temperatures and lower loss factors. The high content of crystals (SC and HC) would act as the physical cross‐linking points and provide a key factor to impede the deformation of neat PLLA and binary blends during stretching, which should result in the fragile behavior of the PLLA and PLLA/PDLA blends with higher optical purity. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 44730.     

Effect of multi‐branched PDLA additives on the mechanical and thermomechanical properties of blends with PLLA

Stereocomplex formation between poly(l ‐lactic acid) (PLLA) and poly(d ‐lactic acid) (PDLA) in the melt state was investigated and altered via the addition of multi‐branched poly(d ‐lactide) (PDLA) additives. Two different multi‐branched PDLA additives, a 3‐arm and 4‐arm star‐shaped polymeric structure, were synthesized as potential heat resistance modifiers and incorporated into PLLA at 5, 10, and 20 (w/w) through melt blending. Mechanical and thermomechanical properties of these blends were compared with linear poly(l ‐lactide) (PLLA) as well as with blends formed by the addition of two linear PDLA analogs that had similar molecular weights to their branched counterparts. Blends with linear PDLA additives exhibited two distinct melting peaks at 170–180°C and 200–250°C which implied that two distinct crystalline domains were present, that of the homopolymer and that of the stereocomplex, the more stable crystalline structure formed by the co‐crystallization of both d ‐ and l ‐lactide enantiomers. In contrast, blends of PLLA with multi‐branched PDLA formed a single broad melting peak indicative of mainly formation of the stereocomplex, behavior which was confirmed by X‐ray diffraction (XRD) analysis. The heat deflection temperature determined by thermal mechanical analysis was improved for all blends compared to neat PLLA, with increases of up to180°C for 20% addition of the 3‐arm PLLA additive. Rheological properties of the blends, as characterized by complex viscosity (η*), remained stable over a wide temperature range. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 132, 42858.     

Poly(L‐lactide)/Poly(D‐lactide)/clay nanocomposites: Enhanced dispersion,crystallization, mechanical properties,and hydrolytic degradation

Poly(L ‐lactide) (PLLA)/poly(D ‐lactide) (PDLA)/clay nanocomposites are prepared via simple melt blending method at PDLA loadings from 5 to 20 wt%. Formation of the stereocomplex crystals in the nanocomposites is confirmed by differential scanning calorimetry and wide‐angle X‐ray diffraction (WAXD). The internal structure of the nanocomposites has been established by using WAXD and transmission electron microscope analyses. The dispersion of clay in the PLLA/PDLA/clay nanocomposites can be improved as a result of increased intensity of shear during melt blending. The overall crystallization rates are faster in the PLLA/PDLA/clay nanocomposites than in PLLA/clay nanocomposite and increase with an increase in the PDLA loading up to 10 wt%; however, the crystallization mechanism and crystal structure of these nanocomposites remain unchanged despite the presence of PDLA. The storage modulus has been apparently improved in the PLLA/PDLA/clay nanocomposites with respect to PLLA/clay nanocomposite. Moreover, it is found that the hydrolytic degradation rates have been enhanced obviously in the PLLA/PDLA/clay nanocomposites than in PLLA/clay nanocomposite. POLYM. ENG. SCI., 54:914–924, 2014. © 2013 Society of Plastics Engineers     

Blends of amorphous and crystalline polylactides with poly(methyl methacrylate) and poly(methyl acrylate): a miscibility study

Blends of amorphous and crystalline polylactides (PDLA and PLLA) with poly(methyl methacrylate) (PMMA) and poly(methyl acrylate) (PMA) have been prepared. Thermal behaviour and miscibility of these blends along the entire composition interval were studied by differential scanning calorimetry (d.s.c.). The results were compared with those obtained by dynamic mechanical analysis (DMTA). Only one T_g was found in PDLA/PMA and PDLA/PMMA blends, indicating a high degree of miscibility in both systems. Nevertheless, the PDLA/PMMA blend presented enlargements of the T_g width at high PMMA contents. In this case, additional evidence of complete miscibility was obtained by studying the evolution of the enthalpic recovery peaks which appear after different thermal annealing treatments. When the polylactide used was semicrystalline (PLLA), once the thermal history of the blends had been destroyed, crystallization of PLLA was disturbed in both blends PLLA/PMMA and PLLA/PMA, but in a rather different fashion: in the first case crystallization was almost prevented while in the second one it was favoured. This behaviour was explained in terms of the effect of the higher stiffness as indicated by the value of T_g for PMMA compared to that for PMA.     

Isothermal crystallization and spherulite growth behavior of stereo multiblock poly(lactic acid)s: Effects of block length

Stereo multiblock poly(lactic acid)s (PLA)s and stereo diblock poly(lactic acid) (DB) with a wide variety of block length of 15.4–61.9 lactyl units are synthesized, and the effects of block length sequence on crystallization and spherulite growth behavior are investigated at different crystallization temperatures, in comparison with neat poly(L ‐lactide) (PLLA), poly(D ‐lactide) (PDLA), and PLLA/PDLA blend. Only stereocomplex crystallites as crystalline species are formed in the stereo multiblock PLAs and DB, irrespective of block length and crystallization temperature. The maximum crystallinities (33–61%), maximum radial growth rate of spherulites (0.7–56.7 μm min^?1), and equilibrium melting temperatures (182.0–216.5°C) increased with increasing block length but are less than those of PLLA/PDLA blend (67 %, 122.5 μm min^?1, and 246.0°C). The spherulite growth rates and overall crystallization rates of the stereo multiblock PLAs and DB increased with increasing block length and are lower than that of PLLA/PDLA blend. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

Synthesis of multi-arm poly(<Emphasis Type="SmallCaps">l</Emphasis>-lactide) and its modification on linear polylactide

Multi-arm poly(l-lactide)s (PLLAs) were prepared by using alcohols with different numbers of hydroxyl groups as initiator and Sn(Oct)₂ as catalyst. The structure and composition was confirmed by NMR and GPC analysis. A series of blends of PLLA/multi-arm PLLA were prepared by melt-mixing. Several techniques were applied to investigate the effects of multi-arm PLLA on the melt rheology, crystallization, thermal stability, morphology and mechanical properties of the linear PLLA. Multi-arm PLLA enhanced crystallization rate of PLLA as a nucleating agent. Rheological analysis showed that the viscosity of PLLA at low frequencies increased after addition of multi-arm PLLA. In addition, the tensile strength was increased with the increase of multi-arm PLLA and can achieve a maximum. FE-SEM measurements revealed that the surface of blends was homogenous, indicating good compatibility between PLLA and multi-arm PLLA. The results had an important guiding role in PLA modification, which provided an opportunity for generating new PLA blending systems with enhanced properties.     

Relationship between the crystallization behavior of poly(ethylene glycol) and stereocomplex crystallization of poly(L‐lactic acid)/poly(D‐lactic acid)

Poly(l ‐lactic acid) (PLLA) is a good biomedical polymer material with wide applications. The addition of poly(ethylene glycol) (PEG) as a plasticizer and the formation of stereocomplex crystals (SCs) have been proved to be effective methods for improving the crystallization of PLLA, which will promote its heat resistance. In this work, the crystallization behavior of PEG and PLLA/poly(d ‐lactic acid) (PDLA) in PLLA/PDLA/PEG and PEG‐b‐PLLA/PEG‐b‐PDLA blends has been investigated using differential scanning calorimetry, polarized optical microscopy and X‐ray diffraction. Both SCs and homocrystals (HCs) were observed in blends with asymmetric mass ratio of PLLA/PDLA, while exclusively SCs were observed in blends with approximately equal mass ratio of PLLA/PDLA. The crystallization of PEG was only observed for the symmetric blends of PLLA_39k/PDLA_35k/PEG_2k, PLLA_39k/PDLA_35k/PEG_5k, PLLA_69k/PDLA_96k/PEG_5k and PEG‐b‐PLLA_31k/PEG‐b‐PDLA_27k, where the mass ratio of PLLA/PDLA was approximately 1/1. The results demonstrated that the formation of exclusively SCs would facilitate the crystallization of PEG, while the existence of both HCs and SCs could restrict the crystallization of PEG. The crystallization of PEG is related to the crystallinity of PLLA and PDLA, which will be promoted by the formation of SCs. © 2017 Society of Chemical Industry     

Novel bioresorbable hydrogels prepared from chitosan‐graft‐polylactide copolymers

A series of biodegradable chitosan‐graft‐polylactide (CS‐g‐PLA) copolymers were prepared by grafting of poly(L ‐lactide) (PLLA) or poly(D ‐lactide) (PDLA) precursor to the backbone of chitosan using N,N′‐carbonyldiimidazole as coupling agent. The composition of the copolymers was varied by adjusting the chain length of PLA as well as the ratio of chitosan to PLA. The copolymers synthesized via this ‘graft‐onto’ method present interesting properties as shown by NMR and infrared spectroscopy, gel permeation chromatography and solubility tests. Hydrogels were prepared by mixing water‐soluble CS‐g‐PLLA and CS‐g‐PDLA solutions. Gelation was assigned to stereocomplexation between PLLA and PDLA blocks as evidenced by differential scanning calorimetry and wide‐angle X‐ray diffraction measurements. Thymopentin (TP5) was taken as a model drug to evaluate the potential of these CS‐g‐PLA hydrogels as drug carriers. An initial burst and a final release up to 82% of TP5 were observed from high‐performance liquid chromatography analysis. Copyright © 2011 Society of Chemical Industry     

Recent advances in stereocomplexation of enantiomeric PLA-based copolymers and applications

Poly(lactic acid) or poly(lactide) (PLA) is a biodegradable and biocompatible thermoplastic polymer, being derived from renewable resources such as corn and sugar cane. The building block of PLA, lactic acid is chiral and the polymerization of lactic acids (or lactides) leads to isotatic, syndiotatic and atactic/heterotactic PLA primary structures. The stereoselective interaction between two complementary enantiomeric PLLA and PDLA has led to enhanced physical properties such as mechanical properties, thermal resistance and hydrolytic stability compared with the parent polymers. Progress in controlled and/or living polymerization techniques combined with other new synthetic methodologies has facilitated the preparation of PLA-based copolymers with complex architectures such as diblock, triblock, multiblock, star-shape block, comb-shape block and various PLA-grafted structures. The utilization of stereocomplexation strategy to these newly developed copolymers has opened avenues to access a variety of new materials with unique characteristics, including novel chemical functionalities, bioactivities, and smart (responsive to external stimulus) properties tailored for specific applications. This review presents recent advancements in the synthesis of PLA-based block/graft copolymers having complex architectures, with emphasis on the enhanced material performances induced by PLA stereocomplex formation. The origin of the enhanced thermal mechanical property observed in PLA stereocomplex is first discussed. The strong interaction resulted from stereocomplexation in PLA based copolymers could be exploited not only for fabrication of advanced therapeutic delivery carriers and tissue engineering devices, but also for stabilizing colloidal systems in microparticles, micelles and hydrogels, that further broaden the applications of PLA that could not have been attained with single PLLA or its copolymers. The stereocomplexation could also be used to tailor the interface interactions between fillers and PLA matrix that lead to higher strength and toughness of PLA.     

Stereocomplex Crystallization Induced Significant Improvement in Transparency and Stiffness–Toughness Performance of Core-Shell Rubber Nanoparticles Toughened Poly(l-lactide) Blends

Toughening modification of poly(l -lactide) (PLLA) with rubber particles is often realized at the cost of transparency, mechanical strength, and modulus because high rubber loadings are generally required for toughening. In this work, a promising strategy to simultaneously improve the transparency and stiffness–toughness performance of poly(butyl acrylate)-poly(methyl methacrylate) (BAMMA) core-shell rubber nanoparticles toughened PLLA blends by utilizing the stereocomplex (SC) crystallization between PLLA and poly(d -lactide) (PDLA) is devised. The results reveal that the construction of SC crystallites in PLLA matrix via melt-mixing PLLA/BAMMA blends with PDLA can prevent BAMMA nanoparticles from aggregation and promote them to form network-like structure at lower contents. As a result, not only higher toughening efficiency with less rubber contents but also superior transparency is achieved in the PLLA/PDLA/BAMMA blends as compared with the PLLA/BAMMA ones where large aggregated BAMMA clusters are formed. Moreover, the outstanding reinforcement of SC crystallites network for PLLA can impart an enhanced tensile strength and modulus to PLLA/PDLA/BAMMA blends, thus improving the stiffness–toughness performance of PLLA/PDLA/BAMMA blends to a higher degree. This work demonstrates that SC crystallization is a promising solution to solve the contradiction between transparency and mechanical properties and then obtain superior comprehensive performances in rubber toughened PLLA blends.     

Importance of Low-Temperature Melt-Mixing on the Construction of Stereocomplex Crystallites with Superior Nucleation Efficiency in Asymmetric Poly(l-lactide)/Poly(d-lactide) Blends

The nucleation efficiency (NE) of stereocomplex crystallites (SCs) formed in asymmetric poly(L-lactide)/poly(D-lactide) (PLLA/PDLA) blends is generally unsatisfactory because the competition between stereocomplexation and chain mixing involved in the melt-mixing process can cause low formation efficiency and even severe aggregation of SCs. Herein, it is attempted to achieve high-efficient formation of finely dispersed SCs particles by designing a unique melt-mixing procedure, where the mixing of PLLA with 0.75 wt% PDLA is first performed at elevated temperatures (far above the melting temperature of SCs) to allow the homogeneous mixing of PLLA/PDLA chains and then at a low temperature (slightly above that of homocrystallites) to permit the full stereocomplexation of the premixed chains. It is found that the SCs formed in the blends exhibit unexpectedly low NEs (e.g., 54.5%), much inferior to that (73.6%) in the counterpart without undergoing premixing. This is because the introduction of premixing leads to a remarkable deterioration in the amount of SCs particles formed, despite decreased particle size, highlighting that the direct mixing at low temperatures of 170–180 °C (about 20–30 °C lower than that used in common melt-processing of PLA) is more effective for the construction of SCs with superior NE. The mechanisms for these striking findings are discussed.     

Supercritical fluid technology parameters affecting size and behavior of stereocomplex polylactide particles and their composites

Polylactide (PLA) is a eco‐friendly and biodegradable material that can be synthesized from renewable resources. PLA features poly(d ‐lactic acid) (PDLA) and poly(l ‐lactic acid) (PLLA) enantiomers. Supercritical fluid (SCF) technology is a very promising method for the stereocomplexation between PDLA and PLLA enantiomers. This study acquires stereocomplex (sc‐)PLA particles with diverse sizes and behaviors by controlling the experimental conditions. Various parameters including polymer concentration, reaction temperature, stirring speed, pressure reducing speed, and final temperature were controlled to adjust size and behavior of sc‐PLA particles. Additionally, we analyzed the effect of subsequent processing following SCF (such as homogenization, mechanical stirring, and sonication) on the size and morphological behavior of sc‐PLA particles. Finally, the mechanical strengths of different PLA composites featuring different sc‐PLA filler sizes were determined. The mechanical strength of PLA composites was significantly improved when using smaller filler sizes. POLYM. ENG. SCI., 58:1193–1200, 2018. © 2017 Society of Plastics Engineers     

Stereocomplexed polylactides (Neo‐PLA) as high‐performance bio‐based polymers: their formation,properties, and application

Polymeric materials prepared from renewable natural resources are now being accepted as “bio‐based polymers”, because they are superior to the conventional petroleum‐based polymers in reducing the emission of carbon dioxide. Among them, poly(L ‐lactide) (PLLA) prepared by fermentation and polymerization is paid an immediate attention. Although PLLA exhibits a broad range of physico‐chemical properties, its thermal and mechanical properties are somewhat poorer for use as ordinary structural materials. For improving these inferior properties, a stereocomplex form consisting of PLLA and its enantiomer poly(D ‐lactide) (PDLA) has high potential because of showing high melting nature (230 °C). It can be formed by simple polymer blend of PLLA and PDLA or more easily with stereoblock polylactides (sb‐PLA) which are PLLA/PDLA block copolymers. These novel PLA polymers, named “Neo‐PLA”, can provide a wide range of properties that have never be attained with single PLLA. Neo‐PLA retains sustainability or bio‐based nature, because both monomers L ‐ and D ‐lactic acids are manufactured from starch by fermentation. Copyright © 2006 Society of Chemical Industry     

Crystallization of poly(3‐hydroxybutyrate) with stereocomplexed polylactide as biodegradable nucleation agent

Crystallization kinetics behavior and morphology of poly(3‐hydroxybutyrate) (PHB) blended with of 2–10 wt% loadings of poly(L ‐ and D ‐lactic acid) (PLLA and PDLA) stereocomplex crystallites, as biodegradable nucleating agents, were studied using differential scanning calorimetry, polarizing‐light optical microscopy (POM), and wide‐angle X‐ray diffraction (WAXD). Blending PLLA with PDLA at 1:1 weight ratio led to formation of stereocomplexed PLA (sc‐PLA), which was incorporated as small crystalline nuclei into PHB for investigating melt‐crystallization kinetics. The Avrami equation was used to analyze the isothermal crystallization of PHB. The stereocomplexed crystallites acted as nucleation sites in blends and accelerated the crystallization rates of PHB by increasing the crystallization rate constant k and decreasing the half‐time (t_1/2). The PHB crystallization was nucleated most effectively with 10 wt% stereocomplexed crystallites, as evidenced byPOM results. The sc‐PLA complexes (nucleated PHB crystals) exhibit much small spherulite sizes but possess the same crystal cell morphology as that of neat PHB based on the WAXD result. POLYM. ENG. SCI., 2012. © 2012 Society of Plastics Engineers     

Properties of a poly(L‐lactic acid)/poly(D‐lactic acid) stereocomplex and the stereocomplex crosslinked with triallyl isocyanurate by irradiation

A poly(L ‐lactic acid) (PLLA)/poly(D ‐lactic acid) (PDLA) stereocomplex was prepared from an equimolar mixture of commercial‐grade PLLA and PDLA by melt processing for the first time. Crosslinked samples were obtained by the radiation‐induced crosslinking of the poly(lactic acid) (PLA) stereocomplex mixed with triallyl isocyanurate (TAIC). The PLA stereocomplex and its crosslinked samples were characterized by their gel behavior, thermal and mechanical measurements, and enzymatic degradation. The crosslinking density of the crosslinked stereocomplex was described as the gel fraction, which increased with the TAIC content and radiation dose. The maximum crosslinking density was obtained in crosslinked samples of PLA/3% TAIC and PLA/5% TAIC irradiated at doses higher than 30 kGy. The stable crosslinking networks that formed in the irradiated PLA/TAIC substantially suppressed the segmental mobility for the crystallization of single crystals as well as stereocomplex crystals. The crosslinking network also significantly improved the mechanical properties and inhibited the enzymatic degradation of crosslinked PLA/3% TAIC. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci 2008