Structural Changes of Y Zeolites with Different Initial SiO2／Al2O3 Ratios during Hydrothermal Treatment

The effects of the initial framework SiO2/Al2O3 ratio and temperature on the structural changes of NaY zeolites during hydrothermal treatments are studied. Two samples with different framework SiO2/Al2O3 ratios are subjected to hydrothermal treatment at four different temperatures. For zeolite with a lower initial SiO2/Al2O3 ratio of 4.2, mesopores are easily formed because more framework aluminum is detached. Moreover, two kinds of mesopores are produced at a higher temperature due to the interconnection of vacancies and smaller mesopores. For zeolite with a higher initial SiO2/Al2O3 ratio of 6.0, there are less mesopores formed as compared with the lower initial SiO2/Al2O3 ratio sample, but there are some macropores formed. This may be attributed to the isolation of vacancies and the different distributions of aluminum in the crystal lattice of the zeolite. The experiment data show that NaY with the SiO2/Al2O3 ratio of 6.0 retains a high relative crystallinity during the hydrothermal treatment. This proves that a high framework SiO2/Al2O3 ratio benefits the stability of zeolite.     

丁烯异构化探针反应结合IR及CO_2-STD法研究K_2CO_3/Al_2O_3和KNO_3/Al_2O_3的碱性

采用丁烯异构化探针反应结合IR及CO_2-STD等方法,考察了K_2CO_3负载量、焙烧及活化温度、载体和钾盐中阴离子的性质对于钾盐负载型固体碱碱性的影响,并研究了K_2CO_3/AI_2O_3和KNO_3/Al_2O_3的最佳制备/活化条件.实验表明在523K以上,尤其是在673K以上依然吸附CO_2的强碱位才是顺-2-丁烯异构化反应的主要活性位.经773K焙烧和活化的KNO_3/A1_2O_3在顺-2-丁烯异构化反应中具有数倍于K_2CO_3/Al_2O_3的活性,因为其碱性活性位仅仅在反应前的原位活化过程中才产生,未受到大气中CO_2污染而保持着高效率.     

水热处理和硝酸处理对改性Y分子筛性能的影响

采用水热处理和硝酸处理相结合的方法对Y分子筛进行改性,并采用N2吸附-脱附、XRD、NH3-TPD、Py-FTIR、27Al MAS NMR、SEM等方法对改性前后的Y分子筛进行了表征。考察了不同改性方法对Y分子筛的孔结构、晶相结构、酸性以及Y分子筛催化剂加氢裂化性能的影响。实验结果表明,随水热处理温度的升高,Y分子筛的脱铝量增大,比表面积减小,总酸量降低;随硝酸浓度的增加,Y分子筛中的非骨架铝脱除,相对结晶度、比表面积和硅铝比增大。以改性后的Y分子筛制备的加氢裂化催化剂的活性和选择性得到改善,其中Y分子筛经680℃水热处理和0.6 mol/L硝酸处理后制备的加氢裂化催化剂,在保持较高正十二烷转化率的前提下,具有良好的中油(C4~8烃)选择性,中油收率为51.07%。     

含镍HZSM－5／Al_2O_3催化剂的水蒸气处理行为

以量热法、Ｘ射线衍射力手段，考察了以ＺＳＭ－５为酸性组分的Ｎｉ－ＨＺＳＭ－５／Ａｌ＿２Ｏ＿３催化剂在水蒸气处理后性能的变化。试验表明，在所考察的水蒸气处理条件范围内，催化剂的裂解活性随处理苛刻度的增大呈现先升后降的现象，其中以水蒸气处理温度的影响最大，水蒸气处理的压力也有明显的影响。     

V助剂对CuO/Al_2O_3上CO_2加H_2合成甲醇的影响

研究了不同Ｖ 含量助剂对ＣｕＯ／Ａｌ２Ｏ３ 催化剂上ＣＯ２ 加Ｈ２ 合成甲醇的影响,发现Ｖ 助剂在低于５１０Ｋ 时能明显提高催化剂的活性和选择性。Ｘ 射线衍射结果表明,Ｖ 助剂加入后,ＣｕＯ 的分散度明显提高。程序升温还原（ＴＰＲ） 的“ＲＯＲ”法揭示,在ＣｕＯ／Ａｌ２Ｏ３ 催化剂中存在能在室温下被氧化的铜物种,而这种铜物种的含量随Ｖ 负载量的增加而增多。     

氧化钾在K_2O－Cr_2O_3／Al_2O_3脱氢催化剂中的作用

研究了在Ｃｒ２Ｏ３／Ａｌ２Ｏ３中添加Ｋ２Ｏ对异丁烷催化脱氢反应的影响。实验结果表明，Ｋ２Ｏ的加入可使催化剂活性和选择性得到明显提高。Ｋ２Ｏ的作用除了增加脱氢中心Ｃｒ３＋的浓度外，还使反应历程发生了改变，从而抑制了裂解和芳构化副反应的发生，提高了异丁烯的选择性。     

MoO3/Al2O3介孔催化剂在柴油氧化脱硫中的应用

 通过溶胶-凝胶法,以硝酸铝为铝源、蔗糖为模板剂、氨水为沉淀剂,制备了介孔 Al₂O₃,并以其为载体,等体积浸渍法制备了MoO₃/Al₂O₃介孔催化剂。采用 N₂吸附-脱附及X射线衍射对介孔 Al₂O₃和 MoO₃/Al₂O₃催化剂进行了表征。将 MoO₃/Al₂O₃催化剂用于柴油催化氧化脱硫,以 H₂O₂为氧化剂,探讨了 MoO₃负载量以及 H₂O₂用量对其催化柴油氧化脱硫的影响。结果表明,自制的 Al₂O₃载体为具有介孔结构的 γ-Al₂O₃,其比表面积、孔容、平均孔径分别为304.3 m²/g、 0.467 cm³/g 和6.14 nm。MoO₃负载量为20%(质量分数)、H₂O₂与柴油中硫的摩尔比为12、氧化温度为60℃时,柴油的氧化脱硫效果较佳,脱硫率为68.4%。     

不同硅铝比的小晶粒Y分子筛的理化性质及其加氢裂化性能

通过改变导向剂的陈化时间及合成母液的碱度制备出不同硅铝比的小晶粒Y分子筛,考察了硅铝比对小晶粒Y分子筛的性质及其加氢裂化性能的影响;采用XRD,BET,NH3-TPD,SEM等手段表征了小晶粒Y分子筛的晶型、骨架结构、孔结构、酸性和形貌。表征结果显示,随硅铝比的增大,Y分子筛表面的酸量减少,骨架稳定性增强。加氢裂化反应结果表明,与工业Y分子筛相比,以小晶粒Y分子筛为载体的催化剂的裂化活性更高,以硅铝比为5.2的小晶粒Y分子筛为载体的催化剂在保持较高裂化活性的前提下,轻油选择性和化工原料收率较高,是优选的轻油型加氢裂化催化剂的活性组分。     

氧化钾在K_2O－Cr_2O_3／Al_2O_3脱氢催化剂中的作用

研究了在Ｃｒ２Ｏ３／Ａｌ２Ｏ３中添加Ｋ２Ｏ对异丁烷催化脱氢反应的影响。实验结果表明，Ｋ２Ｏ的加入可使催化剂活性和选择性得到明显提高。Ｋ２Ｏ的作用除了增加脱氢中心Ｃｒ３＋的浓度外，还使反应历程发生了改变，从而抑制了裂解和芳构化副反应的发生，提高了异丁烯的选择性。     

催化裂化再生器中Pt/Al_2O_3助燃剂的失活动力学

对催化裂化再生器中使CO完全氧化的Pt/Al2 O3 助燃剂的失活进行了研究。发现Pt/Al2 O3 助燃剂的失活与气流中氧的存在密切相关。GPLE失活动力学模型能很好地拟合试验数据 ,其失活级数为 2。估算了助燃剂的平衡活性 ,结果与工业实际值相符合     

硫化温度对MoCo/Al2O3催化剂选择性加氢脱硫的影响

以FCC汽油为原料,在中型试验装置上考察230～400℃范围内硫化温度对MoCo/Al2O3催化剂加氢脱硫率及烯烃加氢饱和率、产品辛烷值损失的影响。结果表明,在反应温度260℃下,随着硫化温度的提高,加氢脱硫率由84.4％逐步提高到91.1％;在反应温度280℃下,加氢脱硫率均可维持在96.0％以上,受硫化温度的影响较小。在上述两种情况下,250℃硫化时催化剂的烯烃加氢饱和率最低,辛烷值损失最小。表明250℃下硫化充分且碳含量较少是其FCC汽油加氢脱硫选择性最好的原因。     

凝胶网格共沉淀法制备CuO/ZnO/Al_2O_3及其催化CO_2加氢合成甲醇研究

以琼脂为分散介质采用凝胶网格沉淀法制备了CuO/ZnO/Al2O3催化剂,利用N2吸附-脱附、XRD、H2-TPR、TEM等方法对催化剂进行了表征,研究了其CO2加氢合成甲醇的催化反应性能,并与草酸盐凝胶共沉淀法和传统并流共沉淀法制备的催化剂进行了对比。结果表明:采用凝胶网格共沉淀法制备的催化剂具有较小的颗粒尺寸和较低的还原温度,在2.0MPa、230℃、空速2400mL/(g.h)、V(H2)∶V(CO2)=3∶1的反应条件下进行CO2加氢合成甲醇反应,甲醇的选择性和收率分别为43.12%和6.63%,相对其它两种方法制备的催化剂有比较明显的提高。     

La助剂对甲醇水蒸气转化制氢CuO-ZnO/Al_2O_3催化剂性能的影响

研究了La助剂对CuO -ZnO/Al2 O3催化剂性能的影响 ,得到了活性和稳定性较好的CuO -ZnO -La2 O3/Al2 O3催化剂。应用TPR、XRD、SEM及XPS等方法对催化剂进行了表征 ,结果表明 :La助剂的加入使催化剂表面的Cu组份含量增加并使Cu/Zn摩尔比提高 ;La助剂的加入极大地提高了催化剂的稳定性 ;反应过程中催化剂表面Cu组份含量逐渐下降是催化剂活性下降的直接原因。     

CuO/ZnO/Al2O3和ZSM-5双功能复合催化剂在苯与合成气烷基化制甲苯中的研究

制备了由共沉淀法制备的CuO/ZnO/Al2O3催化剂与ZSM-5混合形成的用于合成气与苯在液相中直接合成甲苯的烷基化反应的双功能复合催化剂,并采用H2-TPR、XRD对催化剂进行了表征。在浆态床反应器中考察反应温度、反应压力、催化剂投加量、ZSM-5硅铝比、ZSM-5与CuO/ZnO/Al2O3的比例对催化剂性能的影响。结果表明:当反应温度为250℃、反应压力为1MPa、苯和催化剂投加量分别20mL和2g、ZSM-5硅铝比为130、ZSM-5与CuO/ZnO/Al2O3的催化剂质量比为1:1时,可达到最佳的反应效果,在8h的反应中,CO的转化率为85.79%,甲苯的选择性为44.91%,甲苯的产量为1.77g。     

二氧化硅负载磷钨钼酸催化合成环己酮乙二醇缩酮

采用溶胶-凝胶法制备了二氧化硅负载磷钨钼酸H3PW6Mo6O40/SiO2催化剂,以环己酮和乙二醇为原料,合成了环己酮乙二醇缩酮.探讨了H3 PW6 Mo6 O40/SiO2对缩酮反应的催化活性,考察了酮醇物质的量比、催化剂用量、带水剂用量、反应时间对产物收率的影响.结果表明,H3 PW6 Mo6O40/SiO2是合成...     

氟化铵对高温水热超稳Y型分子筛的改性研究

探索了氟化铵法制备高硅铝比超稳Ｙ型分子筛的可能性。系统地考察了反应时同、反应温度、氟化铵溶液加入量及溶液ｐＨ值对处理过程的影响。结果表明，在合适的处理条件下能制备出硅铝比达２０左右的超稳Ｙ型分子筛。改性后超稳Ｙ型分子筛的晶体结构热稳定性增加，脉冲微反试验的正已烷裂解活性下降而烯烃选择性得到提高。     

X射线衍射法测定ZSM－5分子筛硅铝比

用ｘ射线衍射最小二乘法测定ＺＳＭ－５分子筛的晶胞参数，经ＺＳＭ－５分子筛硅铝比与晶胞参数关联的经验公式，得到ＺＳＭ－５分子筛的硅铝比。试验结果表明，该方法测定的ＺＳＭ－５分子筛硅铝比比通常采用的化学分析方法省时、简便、重复性好。     

不同硅/铝比La/ZSM-5分子筛对催化裂化轻汽油异构化/芳构化性能的影响

分别以硅/铝摩尔比为40、200、300、400的ZSM-5分子筛为载体,以金属镧为活性组分,制备一系列催化裂化(FCC)轻汽油异构化/芳构化催化剂,通过X射线衍射(XRD)、N2吸附-脱附、²⁷Al MAS NMR、氨气程序升温脱附(NH₃-TPD)、吡啶红外吸附(Py-FTIR)、扫描电镜(SEM)等手段对其进行表征。以FCC轻汽油为原料,研究了La/ZSM-5分子筛硅/铝摩尔比变化对异构化/芳构化反应性能的影响。结果表明：随着ZSM-5硅/铝摩尔比的增加,其酸强度逐渐降低,B酸与L酸酸量比值减小,芳烃产率呈现先增加后减少的趋势;当硅/铝摩尔比为200时,Brønsted(B)酸与Lewis(L)酸酸量比值最低,FCC轻汽油异构化/芳构化性能最高;在反应温度380 ℃、压力1.0 MPa、氢/油体积比100和体积空速1.0 h^-1的条件下,La/ZSM-5 200分子筛催化剂作用下异构化/芳构化产品与反应原料相比,烯烃体积分数降低32.81百分点,异构烷烃体积分数增加18.24百分点,芳烃体积分数增加到5.97%,辛烷值降低5.38个单位,达成以芳构/异构反应为主的大幅度降烯烃的目标,为京Ⅵ(B)汽油标准的实施提供了技术支持。     

焙烧温度对Al2O3载体及Pd／Al2O3催化剂性能的影响

采用CO2气体成胶制备了Al2O3载体,考察了载体焙烧温度对载体和相应Pd／Al2O3催化剂物理化学性质及催化性能的影响,并采用X射线衍射、BET等技术对载体及催化剂性能进行了表征。结果表明,随焙烧温度的升高,载体的比表面积、孔容减小,平均孔径逐渐增大,孔分布较集中。所制得的拟薄水铝石较纯净。400—800℃焙烧时,Al2O3载体只有γ—Al2O3晶型;1050℃时,主要以θ-Al2O3为主;到1250℃已完全转变为α—Al2O3。Pd／Al2O3催化剂均具有较高的双烯加氢活性和选择性,其中以970℃和1050℃焙烧载体制备的催化剂为最优。     

不同浓度草酸改性对Y分子筛性能的影响

采用水热处理和草酸处理相结合的方法对Y分子筛进行改性,采用N2吸附-脱附、XRD、吡啶吸附FTIR、27Al MAS NMR和SEM等方法对Y分子筛进行了表征,并在微型反应装置上评价了改性Y分子筛制备的催化剂的加氢裂化活性,考察了不同浓度草酸改性对Y分子筛性能的影响。表征结果显示,随草酸浓度的提高,Y分子筛的比表面积、孔体积和孔径逐渐增大;硅铝比均明显提高,相对结晶度增大,晶胞常数减小;总酸量、弱酸酸量、中强酸酸量及B酸酸量均出现不同程度的减小。催化剂的加氢裂化活性评价结果表明,较为适宜的草酸处理浓度为0.20 mol/L。