高氧超电极在电解法生产氯酸盐中的应用

制备了３种氧化涂层电极,分析了涂层物相组成、涂层形貌,测定了电极的电化学性能,研究了这些电极在电解法生产氯酸盐中的应用。结果表明：钌锡锑氧化物涂层电极具有较低析氯电位、较高析氧电位,电解ＮａＣｌ溶液生产ＮａＣｌＯ３具有较高电流效率。     

钛阳极活性涂层组分改进

介绍了TiO2 80%(摩尔分数)·RuO2 20%(摩尔分数)涂层电极的制备,并与TiO2 70%(摩尔分数)·RuO2 30%(摩尔分数)和石墨电极的强化寿命、析氯电位和析氧电位对比,说明该涂层钛电极与TiO2 70%(摩尔分数)·RuO2 30%(摩尔分数)相比,槽电压、析氯电位和析氧电位均相差不大,但强化寿命是TiO2 70%(摩尔分数)·RuO2 30%(摩尔分数)的3倍.     

金属阳极涂层评价试验

测定了钌钛、钌钛锡、钌钛铱３种氧化物涂层电极的氯电位、析氧电位,强化寿命和强化失重等电化性能,综合考虑氯碱工业中隔膜电解用阳极可选择钌钛或钌钛锡涂层。     

Co改性的Ti/IrO2-Co3O4-SnO2-Sb2O5析氧涂层电极性能研究

为提升析氧电极催化性能及使用寿命，通过热解法制备了Co改性的Ti/IrO₂-Co₃O₄-SnO₂-Sb₂O₅四元氧化物电极。采用极化曲线(LSV)、循环伏安曲线(CV)、交流阻抗图谱(EIS)及加速寿命实验研究了电极在硫酸溶液中的析氧催化活性及稳定性。结果表明，随着Co摩尔分数的增大，涂层表面的粗糙度先降低后升高，而电极的析氧活性及加速寿命均先升高后降低；当Co摩尔分数为50%时电极催化活性最佳，而当Co摩尔分数为30%时电极寿命最长，与Ti/IrO₂-SnO₂-Sb₂O₅电极相比寿命提高了约76.7%。电化学测试结果表明，Co改性电极催化活性的提高得益于反应控速步骤的改变、涂层表面反应位点数量的增大及电化学反应阻抗的降低。     

热处理气氛及气流速度对钌钛氧化物阳极性能的影响

在不同的热处理气氛与气流速度下制备了钌钛氧化物金属阳极，测定了电极的析氯电位、析氧电位及强化寿命。并对涂层进行ＸＲＤ与ＳＥＭ分析。实验表明，改变热处理气氛与气流速度可使电极表面边界层中的氧含量发生变化，直接影响金属氧化物电极涂层的微观形貌，结构与组成，从而导致电极析氧活性与强化寿命的改变。热处理时，在边界层中保持较高的氧含量有助于充分形成钌钛氧化物固溶体，提高金属阳极的析氧电位与工作寿命。     

钛基氧化物阳极的制备及电解脱硫废水制氯研究

通过电沉积法和热分解法将活性组分IrSnRuMn分别负载到钛板上制成新型电极,探究活性层Ru、Mn摩尔比对钛基IrSnRuMn氧化物阳极电化学活性及电解脱硫废水制氯的影响。结果表明,当Ru、Mn摩尔比为4∶6时,电极同时具有较好的电化学活性和电解制氯能力,此时电极的析氯电位为1.167 V,析氧电位为1.322 V。在电极间距为4 cm、阳极液pH=7.95、电流密度为20 mA/cm²、电解时间为120 min的条件下,对氯离子的去除效率为38.7%。     

SnO2-Sb2O3-CeO2/Ti电催化电极制备及氧化苯酚研究

采用电沉积制备中间层,热分解制备表层的方法制备了钛基铈掺杂锡锑涂层电极,利用SEM、EMPA、动电位扫描,研究了电极涂层形貌、元素组成分布、选择催化性.结果表明:电极表面涂层颗粒分布均匀,电极涂层有较大的表面积,Sn、Sb、Ce 3种元素分布较均匀;电极有较高的析氧电位.苯酚降解试验表明:低浓度时苯酚和CODCr有较高...     

一种复合氧化物涂层钛电极的电化学性能及其在废水处理中的应用

通过稳态极化曲线和循环伏安曲线,比较了复合氧化物涂层钛电极和镀铂钛电极的析氯和析氧电化学性能;通过循环伏安曲线,分析了复合氧化物涂层钛电极在不同溶液中的电化学性能,初步探索了复合氧化物涂层钛电极的电化学氧化机理;并将复合氧化物涂层钛电极安装在低压高频水处理装置中用于重金属废液和有机废液的电化学降解。结果表明,复合氧化物涂层钛电极相比镀铂钛电极具有更高的析氯和析氧催化活性及析氯和析氧反应效率;复合氧化物涂层钛电极在酸性溶液中析出的铜容易氧化成铜离子,出现铜返溶现象,而析出的镍不容易氧化,很难出现镍返溶现象;复合氧化物涂层钛电极具有较高的电化学催化性能,在电流密度为1 300A·m-2时,连续电解氧化120min后的铜离子去除率达到90%、镍离子去除率达到97%,连续电解氧化200min后的铵离子去除率达到98%、氰根离子去除率达到95%。     

金属阳极四元涂层开发现状浅析

通过分析金属阳极涂层结构，在现有金属阳极三元涂层的基础上，确定了钌、钛、铱、锡四元涂层。对该涂层的电化性能指标及实际运行数据进行了分析，并与三元涂层电化性能指标进行对比，说明了四元涂层在析氯电位、极化率、析氧电位、寿命等方面均明显优于三元涂层，而且更适合在高电流密度下运行。     

钛基锡锰钌氧化物阳极的电化学性能

通过热分解法制备不同钌含量的钛基锡锰氧化物阳极。X射线衍射谱图显示所制备的电极的主要相态为金红石型β—MnO2;循环伏安曲线与稳态极化曲线测试表明随着钌含量的增加,电极上的氧化电流也快速上升,析氯的选择性提高;适量掺混钌可以增加涂层表面析氯反应活性点的数目,当钌的质量分数为2％时,反应活性点的数目达到最大;电化学阻抗谱研究表明掺杂钌明显减小电极氧化物涂层的膜电阻R和析氯反应的电荷传递电阻Rct。有效地提高电极的电催化效果。钛基锡锰钌涂层电极可用于制备次氯酸钠,NaClO的生成速率为34．8mg／（L·min）。     

电极对PTCR热敏电阻常温断续负荷的影响

本文研究了在彩电消磁用PTCR热敏电阻分别烧渗Ag-Zn电极和AI电极，研究了两种电极对PTCR元件常温断续负荷的影响，分析了失效机理，根据结果我们选取合适的电极作为实际生产中的电极。     

电化学法处理废水的研究进展

介绍了近年来二维电极及三维电极电化学法处理废水研究进展及应用,并对各种方法进行了阐述,对其前景进行展望,提出了今后的重点研究方向.     

电熔窑寿命的探讨

从电熔窑结构、耐火材料质量、熔化工艺控制、保温节能等几个方面简要阐述了影响电熔窑寿命的因素,指出耐火材料的侵蚀是主要原因,提出了解决的方法和应注意的事项。     

离子选择电极法测定水质氟化物

在水样中加入总离子强度调节缓冲溶液,由离子选择电极法测定标准溶液剂水样的电动势,由标准溶液的标准曲线求得水样的氟离子含量。     

Development of a Ag/Ag micro-reference electrode for electrochemical measurements in ionic liquids

We report on a novel miniaturized Ag/Ag⁺ reference electrode (RE) design suitable for electrochemical measurements in room temperature ionic liquids (RTILs). The electrode is based on capillaries with an outer diameter of 365 μm and contains a 10 mmol/l solution of a silver salt in a RTIL. The silver salt bears the same type of anion as the RTIL. While potential shifts of several hundred millivolts have been observed for common platinum or silver pseudo-reference electrodes, our Ag/Ag⁺ micro electrode provides a stable and reliable reference potential over a period of more than two weeks, if protected from light and stored in a nitrogen atmosphere. Due to the small dimensions of the RE, it can be placed close to the working electrode (WE) and it is well-suited for application in electrochemical micro cells as well as for potential-controlled in situ AFM, STM or electrochemical impedance measurements. The electrode characteristics were determined by voltammetric measurements on ferrocene and cobaltocenium hexafluorophosphate dissolved in a RTIL. The highest expected contamination of the sample with Ag⁺ ions was calculated and found to be below 4 ppm.     

不同电极方式交变脉冲电絮凝法处理废水的比较研究

以酸性蓝模拟废水为受试溶液,考察交变脉冲电絮凝法采用不同电极形式的效果。通过对模拟废水的处理实验,得到用单一铁电极、单一铝电极以及铁铝混合电极等3种电极方式处理酸性蓝废水的最佳条件,并进行对比,得出使用铁铝混合电极处理废水兼具单一铝电极和单一铁电级的优点。     

电位滴定法检测有机热载体时电极选用的研究

通过三电极体系和非水相电极两组试验数据的对比,对电位滴定法测定有机热载体酸值时电极配置的选用进行了比较,两组电极的标定试验和空白试验曲线突跃大,平行性好;但是样品试验的平行性非水相电极优于三电极体系。最后得出用电位滴定法检测有机热载体酸值时非水相电极优于三电极体系的结论。     

“原电池电动势的测定”实验的几点改进

电动势的测定是物理化学实验教学中的重要内容,大多数国内高校都开展了关于电动势测定及其应用的实验。但在多年实验管理和教学中发现,实验存在如汞污染严重、甘汞电极损耗较多及实验数据时有不稳定等问题,该文针对上述问题对原电池电动势的测定实验做出几点改进,改进后实验数据更加稳定可靠,同时提高了实验室管理人员的工作效率,节省了实验经费。     

Electrochemical characterization of screen-printed and conventional carbon paste electrodes

This work compares the electroactivity of a conventional carbon paste electrode and non-pretreated commercially available screen-printed carbon electrodes (from Alderon Biosciences, University of Florence and DropSens) towards some benchmark redox couples like hexaammineruthenium (III), ferricyanide, p-aminophenol and hydroquinone. While cyclic voltammograms of Ru³⁺ did not show significative electron transfer reactivity differences between the electrodes tested, the other redox systems exhibited higher reversible behaviours on DropSens electrodes. Scanning electron microscopy and roughness analysis with a profilometer were applied to detect the surface morphology of the working electrodes. The roughness evaluated of the screen-printed carbon working electrodes increased in this order Alderon < University of Florence < DropSens. Finally, the most electrochemically active and rough unpretreated electrode (DropSens commercial screen-printed electrode) was used to study the electrochemical-chemical reaction mechanism of indigo carmine oxidation in 0.1 M sulphuric acid. This study showed that the adsorption of the oxidation product of indigo carmine is stabilized when it is adsorbed on the surface of the electrode.     

Pt/PbO_2电极在COD测定中的初探

选用铅基二氧化铅膜作为电极材料 ,研究了用Pt为基体PbO2 膜电极的制备。以此新型电极作为工作电极组成三电极工作系统 ,并通过增大电位气泡更新法对电极再生 ,来阻止电极表面被污染。应用恒电位伏安法的原理测定电流值 ,保证了测量的重现性。通过对试液COD值的测定 ,表明此法有好的应用价值