Study on the hydrogen storage properties and reaction mechanism of NaAlH4–MgH2–LiBH4 ternary-hydride system

In this paper, we report the hydrogen storage properties and reaction mechanism of NaAlH₄–MgH₂–LiBH₄ (1:1:1) ternary-hydride system prepared by ball milling. It was found that during ball milling, the NaAlH₄/MgH₂/LiBH₄ combination converted readily to the mixture of LiAlH₄/MgH₂/NaBH₄ and there is a mutual destabilization among the hydrides. Three major dehydrogenation steps were observed in the system, which corresponds to the decomposition of LiAlH₄, MgH₂, and NaBH₄, respectively. The onset dehydrogenation temperature of MgH₂ in this system is observed at around 275 °C, which is over 55 °C lower from that of as-milled MgH₂. Meanwhile, NaBH₄-relevant decomposition showed significant improvement, starts to release hydrogen at 370 °C, which is reduced by about 110 °C compared to the as-milled NaBH₄. The second and third steps decomposition enthalpy of the system were determined by differential scanning calorimetry measurements and the enthalpies were changed to be 61 and 100 kJ mol⁻¹ H₂ respectively, which are smaller than that of MgH₂ and NaBH₄ alone. From the Kissinger plot, the apparent activation energy, E_A, for the decomposition of MgH₂ and NaBH₄ in the composite was reduced to 96.85 and 111.74 kJ mol⁻¹ respectively. It is believed that the enhancement of the dehydrogenation properties was attributed to the formation of intermediate compounds, including Li–Mg, Mg–Al, and Mg–Al–B alloys, upon dehydrogenation, which change the thermodynamics of the reactions through altering the de/rehydrogenation pathway.     

Processing analysis of the ternary LiNH2–MgH2–LiBH4 system for hydrogen storage

In this article, we investigate the ternary LiNH₂–MgH₂–LiBH₄ hydrogen storage system by adopting various processing reaction pathways. The stoichiometric ratio of LiNH₂:MgH₂:LiBH₄ is kept constant with a 2:1:1 molar ratio. All samples are prepared using solid-state mechano-chemical synthesis with a constant rotational speed, but with varying milling duration. Furthermore, the order of addition of parent compounds as well as the crystallite size of MgH₂ are varied before milling. All samples are intimate mixtures of Li–B–N–H quaternary hydride phase with MgH₂, as evidenced by XRD and FTIR measurements. It is found that the samples with MgH₂ crystallite sizes of approximately 10 nm exhibit lower initial hydrogen release at a temperature of 150 °C. Furthermore, it is observed that the crystallite size of Li–B–N–H has a significant effect on the amount of hydrogen release with an optimum size of 28 nm. The as-synthesized hydrides exhibit two main hydrogen release temperatures, one around 160 °C and the other around 300 °C. The main hydrogen release temperature is reduced from 310 °C to 270 °C, while hydrogen is first reversibly released at temperatures as low as 150 °C with a total hydrogen capacity of ∼6 wt.%. Detailed thermal, capacity, structural and microstructural properties are discussed and correlated with the activation energies of these materials.     

Combined effects of hydrogen back-pressure and NbF5 addition on the dehydrogenation and rehydrogenation kinetics of the LiBH4–MgH2 composite system

It is well known that the dehydrogenation pathway of the LiBH₄–MgH₂ composite system is highly reliant on whether decomposition is performed under vacuum or a hydrogen back-pressure. In this work, the effects of hydrogen back-pressure and NbF₅ addition on the dehydrogenation kinetics of the LiBH₄–MgH₂ system are studied under either vacuum or hydrogen back-pressure, as well as the subsequent rehydrogenation and cycling. For the pristine sample, faster desorption kinetics was obtained under vacuum, but the performance is compromised by slow absorption kinetics. In contrast, hydrogen back-pressure remarkably promotes the absorption kinetics and increases the reversible hydrogen storage capacity, but with the penalty of much slower desorption kinetics. These drawbacks were overcome after doping with NbF₅, with which the dehydrogenation and rehydrogenation kinetics was significantly improved. In particular, the enhanced kinetics was observed to persist well, even after 9 cycles, in the case of the NbF₅ doped sample under hydrogen back-pressure, as well as the suppression of forming Li₂B₁₂H₁₂. Furthermore, the mechanism that is behind these effects of NbF₅ additive on the reversible dehydrogenation reaction of the LiBH₄–MgH₂ system is discussed.     

Effect of SWNTs on the reversible hydrogen storage properties of LiBH4–MgH2 composite

Single-walled carbon nanotubes (SWNTs) were mechanically milled with LiBH₄/MgH₂ mixture, and examined with respect to its effect on the reversible dehydrogenation properties of the Li–Mg–B–H system. Experimental results show that the addition of SWNTs results in an enhanced dehydriding rate and improved cyclic stability of the LiBH₄/MgH₂ composite. For example, the LiBH₄/MgH₂ composite with 10 wt% purified SWNTs additive can release nearly 10 wt% hydrogen within 20 min at 450 °C, with an average dehydriding rate over 2 times faster than that of the neat LiBH₄/MgH₂ sample. Based on the results of phase analysis and a series of designed experiments, the mechanism underlying the observed property improvement was discussed.     

Effects of MoS2 addition on the hydrogen storage properties of 2LiBH4–MgH2 systems

A 2LiBH₄–MgH₂–MoS₂ composite was prepared by solid-state ball milling, and the effects of MoS₂ as an additive on the hydrogen storage properties of 2LiBH₄–MgH₂ system together with the corresponding mechanism were investigated. As shown in the TG–DSC and MS results, with the addition of 20 wt.% of MoS₂, the onset dehydrogenation temperature is reduced to 206 °C, which is 113 °C lower than that of the pristine 2LiBH₄–MgH₂ system. Meanwhile, the total dehydrogenation amount can be increased from 9.26 wt.% to 10.47 wt.%, and no gas impurities such as B₂H₆ and H₂S are released. Furthermore, MoS₂ improves the dehydrogenation kinetics, and lowers the activation energy (E_a) 34.49 kJ mol⁻¹ of the dehydrogenation reaction between Mg and LiBH₄ to a value lower than that of the pristine 2LiBH₄–MgH₂ sample. According to the XRD test, Li₂S and MoB₂ are formed by the reaction between LiBH₄ and MoS₂, which act as catalysts and are responsible for the improved hydrogen storage properties of the 2LiBH₄–MgH₂ system.     

Improved hydrogen storage performance of the LiNH2–MgH2–LiBH4 system by addition of ZrCo hydride

Significant improvements in the hydrogen absorption/desorption properties of the 2LiNH₂–1.1MgH₂–0.1LiBH₄ composite have been achieved by adding 3wt% ZrCo hydride. The composite can absorb 5.3wt% hydrogen under 7.0 MPa hydrogen pressure in 10 min and desorb 3.75wt% hydrogen under 0.1 MPa H₂ pressure in 60 min at 150 °C, compared with 2.75wt% and 1.67wt% hydrogen under the same hydrogenation/dehydrogenation conditions without the ZrCo hydride addition, respectively. TPD measurements showed that the dehydrogenation temperature of the ZrCo hydride-doped sample was decreased about 10 °C compared to that of the pristine sample. It is concluded that both the homogeneous distribution of ZrCo particles in the matrix observed by SEM and EDS and the destabilized N–H bonds detected by IR spectrum are the main reasons for the improvement of H-cycling kinetics of the 2LiNH₂–1.1MgH₂–0.1LiBH₄ system.     

Compaction pressure influence on material properties and sorption behaviour of LiBH4–MgH2 composite

Among different Reactive Hydride Composites (RHCs), the combination of LiBH₄ and MgH₂ is a promising one for hydrogen storage, providing a high reversible storage capacity. During desorption of both LiBH₄ and MgH₂, the formation of MgB₂ lowers the overall reaction enthalpy. In this work, the material was compacted to pellets for further improvement of the volumetric hydrogen capacity. The influence of compaction pressure on the apparent density, thermal conductivity and sorption behaviour for the Li-based RHC during cycling was investigated for the first time. Although LiBH₄ melts during cycling, decrepitation or disaggregation of the pellets is not observed for any of the investigated compaction pressures. However, a strong influence of the compaction pressure on the apparent hydrogen storage capacity is detected. The influence on the reaction kinetics is rather low. To provide explanations for the observed correlations, SEM analysis before and after each sorption step was performed for different compaction pressures. Thus, the low hydrogen sorption in the first cycles and the continuously improving sorption for low pressure compacted pellets with cycling may be explained by some surface observations, along with the form stability of the pellets.     

Comprehensive hydrogen storage properties and catalytic mechanism studies of 2LiBH4–MgH2 system with NbF5 in various addition amounts

In the present work, the role of NbF₅ addition amount in affecting the comprehensive hydrogen storage properties (dehydrogenation, rehydrogenation, cycling performance, hydrogen capacity) of 2LiBH₄–MgH₂ system as well as the catalytic mechanism of NbF₅ have been systematically studied. It is found that increasing the addition amount of NbF₅ to the 2LiBH₄–MgH₂ system not only results in dehydrogenation temperature reduction and hydriding–dehydriding kinetics enhancement but also leads to the de/rehydrogenation capacity loss. Compared with other samples, 2LiBH₄–MgH₂ doping with NbF₅ in weight ratios of 40:4 exhibits superior comprehensive hydrogen storage properties, which can stably release ∼8.31 wt.% hydrogen within 2.5 h under 4 bar H₂ and absorb ∼8.79 wt.% hydrogen within 10 min under 65 bar H₂ at 400 °C even up to 20 cycling. As far as we know, this is the first time that excellent reversibility as high as 20 cycles without obvious degradation tendency in both of hydrogen capacity and reaction rate has been achieved in the 2LiBH₄–MgH₂ system. The further experimental study reveals that the highly catalytic effects of NbF₅ on the 2LiBH₄–MgH₂ system are derived from the reaction between NbF₅ and LiBH₄, which provides a fundamental insight into the catalytic mechanism of NbF₅.     

Effective nanoconfinement of 2LiBH4–MgH2 via simply MgH2 premilling for reversible hydrogen storages

To improve nanoconfinement of LiBH₄ and MgH₂ in carbon aerogel scaffold (CAS), particle size reduction of MgH₂ by premilling technique before melt infiltration is proposed. MgH₂ is premilled for 5 h prior to milling with LiBH₄ and nanoconfinement in CAS to obtained nanoconfined 2LiBH₄–premilled MgH₂. Significant confinement of both LiBH₄ and MgH₂ in CAS, confirmed by SEM–EDS–mapping results, is achieved due to MgH₂ premilling. Due to effective nanoconfinement, enhancement of CAS:hydride composite weight ratio to 1:1, resulting in increase of hydrogen storage capacity, is possible. Nanoconfined 2LiBH₄–premilled MgH₂ reveals a single–step dehydrogenation at 345 °C with no B₂H₆ release, while dehydrogenation of nanoconfined sample without MgH₂ premilling performs in multiple steps at elevated temperatures (up to 430 °C) together with considerable amount of B₂H₆ release. Activation energy (E_A) for the main dehydrogenation of nanoconfined 2LiBH₄–premilled MgH₂ is considerably lower than those of LiBH₄ and MgH₂ of bulk 2LiBH₄–MgH₂ (ΔE_A = 31.9 and 55.8 kJ/mol with respect to LiBH₄ and MgH₂, respectively). Approximately twice faster dehydrogenation rate are accomplished after MgH₂ premilling. Three hydrogen release (T = 320 °C, P(H₂) = 3–4 bar) and uptake (T = 320–325 °C, P(H₂) = 84 bar) cycles of nanoconfined 2LiBH₄–premilled MgH₂ reveal up to 4.96 wt. % H₂ (10 wt. % H₂ with respect to hydride composite content), while the 1st desorption of nanoconfined sample without MgH₂ premilling gives 4.30 wt. % of combined B₂H₆ and H₂ gases. It should be remarked that not only kinetic improvement and B₂H₆ suppression are obtained by MgH₂ premilling, but also the lowest dehydrogenation temperature (T = 320 °C) among other modified 2LiBH₄–MgH₂ systems is acquired.     

Catalytic effect of MgFe2O4 on the hydrogen storage properties of Na3AlH6–LiBH4 composite system

The effect of MgFe₂O₄ on the hydrogen storage properties of the composite Na₃AlH₆4LiBH₄ was studied for the first time, where it was found that MgFe₂O₄ addition decreased the onset desorption temperature of Na₃AlH₆4LiBH₄. Hydrogen (～9.5 wt%) was released in three stages and the dehydrogenation temperatures were reduced to 80 °C, 350 °C, and 430 °C for the first, second, and third stage, respectively. The absorption kinetics of Na₃AlH₆4LiBH₄ was also significantly improved due to the catalytic effect of MgFe₂O₄. Using Kissinger analysis, the apparent activation energies of decomposition of the Li₃AlH₆ and NaBH₄ stages in Na₃AlH₆4LiBH₄-10 wt% MgFe₂O₄ were calculated to be 72 and 141 kJ/mol, respectively. These values were considerably lower than the corresponding values for the undoped composite. X-ray diffraction analysis revealed the formation of new products such as MgO and Fe during the heating process. Our results suggest that MgFe₂O₄ enhanced the hydrogen storage properties of Na₃AlH₆4LiBH₄ through the formation of active species, such as MgO and Fe.     

Nanoconfined 2LiBH4–MgH2–TiCl3 in carbon aerogel scaffold for reversible hydrogen storage

Nanoconfinement of 2LiBH₄–MgH₂–TiCl₃ in resorcinol–formaldehyde carbon aerogel scaffold (RF–CAS) for reversible hydrogen storage applications is proposed. RF–CAS is encapsulated with approximately 1.6 wt. % TiCl₃ by solution impregnation technique, and it is further nanoconfined with bulk 2LiBH₄–MgH₂ via melt infiltration. Faster dehydrogenation kinetics is obtained after TiCl₃ impregnation, for example, nanoconfined 2LiBH₄–MgH₂–TiCl₃ requires ∼1 and 4.5 h, respectively, to release 95% of the total hydrogen content during the 1st and 2nd cycles, while nanoconfined 2LiBH₄–MgH₂ (∼2.5 and 7 h, respectively) and bulk material (∼23 and 22 h, respectively) take considerably longer. Moreover, 95–98.6% of the theoretical H₂ storage capacity (3.6–3.75 wt. % H₂) is reproduced after four hydrogen release and uptake cycles of the nanoconfined 2LiBH₄–MgH₂–TiCl₃. The reversibility of this hydrogen storage material is confirmed by the formation of LiBH₄ and MgH₂ after rehydrogenation using FTIR and SR-PXD techniques, respectively.     

Catalytic effect of carbon nanostructures on the hydrogen storage properties of MgH2–NaAlH4 composite

The present investigation describes the hydrogen storage properties of 2:1 molar ratio of MgH₂–NaAlH₄ composite. De/rehydrogenation study reveals that MgH₂–NaAlH₄ composite offers beneficial hydrogen storage characteristics as compared to pristine NaAlH₄ and MgH₂. To investigate the effect of carbon nanostructures (CNS) on the de/rehydrogenation behavior of MgH₂–NaAlH₄ composite, we have employed 2 wt.% CNS namely, single wall carbon nanotubes (SWCNT) and graphene nano sheets (GNS). It is found that the hydrogen storage behavior of composite gets improved by the addition of 2 wt.% CNS. In particular, catalytic effect of GNS + SWCNT improves the hydrogen storage behavior and cyclability of the composite. De/rehydrogenation experiments performed up to six cycles show loss of 1.50 wt.% and 0.84 wt.% hydrogen capacity in MgH₂–NaAlH₄ catalyzed with 2 wt.% SWCNT and 2 wt.% GNS respectively. On the other hand, the loss of hydrogen capacity after six rehydrogenation cycles in GNS + SWCNT (1.5 + 0.5) wt.% catalyzed MgH₂–NaAlH₄ is diminished to 0.45 wt.%.     

Improved hydrogen storage properties of LiBH4 doped Li–N–H system

Remarkable improvement of hydrogen sorption properties of Li–N–H system has been obtained by doping with a small amount of LiBH₄. The starting and ending temperatures of hydrogen desorption shift to lower temperatures and the release of NH₃ is obviously restrained by 10 mol% LiBH₄ doping. The kinetics of hydrogen desorption and absorption of Li–N–H system became faster by the addition of LiBH₄. About 4 wt.% H₂ can be released within 30 min and ∼4.8 wt.% H₂ can be reabsorbed within 2 min by LiBH₄ doped sample at 250 °C, while only 1.44 wt.% H₂ is released and 2.1 wt.% is reabsorbed for pure Li–N–H system. The quaternary hydride (LiNH₂)_x(LiBH₄)_(1−x) formed by the reaction between LiBH₄ and LiNH₂ may contribute to the enhancement of the hydrogen sorption performances by yielding a ionic liquid phase and transferring LiNH₂ from solid state to molten state with a weakened N–H bond.     

Improved reversible dehydrogenation of LiBH4–MgH2 composite by the synergistic effects of Al and MgO

In this paper, we report a novel method of improving the reversible dehydrogenation properties of the 2LiBH₄–MgH₂ composite. Our study found that mechanically milling with small amount of Al powder can markedly shorten or even eliminate the problematic incubation period that interrupts the dehydrogenation steps of the 2LiBH₄–MgH₂ composite. But the resulting composite showed serious kinetics degradation upon cycling. In an effort to solve this problem, we found that combined usage of small amounts of Al and MgO enabled the 2LiBH₄–MgH₂ composite to rapidly and reversibly deliver around 9 wt% hydrogen at 400 °C under 0.3 MPa H₂, which compares favorably with the dehydrogenation performance of the composites with transition-metal additives. A combination of phase/microstructural analyses and series of control experiments has been conducted to gain insight into the promoting effects of Al and MgO. It was found that Al and MgO additives act as precursor and promoter for the formation of AlB₂ heterogeneous nucleation sites, respectively.     

Morphological effects of Nb2O5 on Mg–MgH2 system for thermal energy storage application

The solar thermal energy could be stored and reused at the desired locations and conditions. The requirement is to develop a suitable medium which could be able to store the solar thermal energy reversibly. Metal-metal hydride system may be one of the options. The high hydrogen storage capacity and fast hydrogenation-dehydrogenation kinetics are the desirable conditions for the practical applications. In this regard, magnesium – magnesium hydride (Mg-MgH₂) system has been considered as a potential candidate. The prerequisite is to fine tune the hydrogenation-dehydrogenation kinetics by a suitable additive. Niobium pentoxide (Nb₂O₅) has been recognized as a suitable additive to improve the hydrogenation-dehydrogenation kinetics. The Nb₂O₅ is found in various morphological forms, however; all of them are not suitable to enhance the hydrogenation-dehydrogenation kinetics of Mg-MgH₂ system. In the current study, it has been found that the mesoporous amorphous Nb₂O₅ has shown remarkable catalytic property on the Mg-MgH₂ system as compared to crystalline Nb₂O₅ under the similar experimental conditions.     

Enhanced hydrogen storage properties of TiN–LiAlH4 composite

The hydrogen storage properties of LiAlH₄ doped efficient TiN catalyst were systematically investigated. We observe that TiN catalyst enhances the dehydrogenation kinetics and decreases the dehydrogenation temperature of LiAlH₄. The dehydrogenation behaviors of 2%TiN–LiAlH₄ are investigated using temperature programmed desorption (TPD), differential scanning calorimetry (DSC) and fourier transform infrared spectroscopy (FTIR). Interestingly, the onset hydrogen desorption temperature of 2%TiN–LiAlH₄ sample gets lowered from 151.0 °C to 90.0 °C with a faster kinetics, and the dehydrogenation rate reached a maximum value at 137.2 °C. By adding a small amount of as-prepared TiN, approximately 7.1 wt% of hydrogen can be released from the LiAlH₄ at 130 °C. Interestingly, the result of the FTIR indicates that the 2%TiN–LiAlH₄ maybe restore hydrogen under 5.5 MPa hydrogen. Moreover, 2%TiN–LiAlH₄ displayed a substantially reduced activation energy for LiAlH₄ dehydrogenation.     

Reversible hydrogen storage in the Li–Mg–N–H system – The effects of Ru doped single walled carbon nanotubes on NH3 emission and kinetics

In this study, the LiNH₂–MgH₂ (2:1.1) complex hydride system (Li–Mg–N–H is investigated in terms of hydrogen ab/desorption kinetics and the concomitant NH₃ emission levels. By selecting more intense ball milling parameters, the hydrogen ab/desorption kinetics were improved and the NH₃ emission reduced. However, it is shown that NH₃ emission cannot be completely eliminated during ball milling. Single walled carbon nanotubes (SWCNTs) and 20 wt.% Ru doped SWCNTs are utilized as catalysts to study their effects on NH₃ emission and kinetics characteristics of the Li–Mg–N–H system. The SWCNT doped sample did not show any kinetics improvement, whereas the SWCNT-20Ru doped sample showed similar kinetics performance as that of the base sample. More importantly, the presence of SWCNT increased the NH₃ emission as compared to the base sample. On the other hand, SWCNT-20Ru doping reduced the NH₃ emission compared to the SWCNT doping, but did not eliminate it completely. As revealed from the mass spectrometry signals, the SWCNT-20Ru catalyst starts to decompose NH₃ at a temperature as low as 200 °C.     

Enhanced hydrogen reversibility of nanoconfined LiBH4–Mg(BH4)2

This study shows the hydrogen desorption kinetics and reversible hydrogen storage properties of 0.55LiBH₄–0.45Mg(BH₄)₂ melt-infiltrated in different nanoporous carbon aerogels with different BET surface areas of 689 or 2660 m²/g and pore volumes of 1.21 or 3.13 mL/g. These investigations clearly show a significantly improved hydrogen storage capacity after four cycles of hydrogen release and uptake for bulk 0.55LiBH₄–0.45Mg(BH₄)₂ and infiltrated in carbon aerogel and the high surface area scaffold, where 22, 36 and 58% of the initial hydrogen content remain after four cycles of hydrogen release and uptake, respectively. Nanoconfinement in high surface area carbon aerogel appears to facilitate hydrogen release illustrated by release of 13.3 wt% H₂ (93%) and only 8.4 wt% H₂ (58%) from bulk hydride in the first cycle using the same physical condition. Notably, nanoconfinement also appear to have a beneficial effect on hydrogen uptake, since 8.3 wt% H₂ (58%) is released from the high surface area scaffold and only 3.1 wt% H₂ (22%) from the bulk sample during the fourth hydrogen release.     

The hydrogen storage properties and reaction mechanism of the NaAlH4 + Ca(BH4)2 composite system

The hydrogen storage properties and reaction mechanism of the combined NaAlH₄ + Ca(BH₄)₂ (2:1) composite system was investigated in the present study. Analyses show that after 6 h of milling, the NaAlH₄ + Ca(BH₄)₂ combination fully converted to the mixture of Ca(AlH₄)₂ + NaBH₄, and a metathesis reaction occurred between the hydrides. Four major dehydrogenation stages were observed in the system, which corresponds to the decomposition of Ca(AlH₄)₂, CaAlH₅, CaH₂ and NaBH₄, respectively. The onset desorption temperature of the composite system is reduced to 125 °C, which is much lower than a unary component of NaAlH₄ and Ca(BH₄)₂. The de/rehydrogenation kinetics of the composite system had improve at a higher temperature. From the Kissinger plot, the apparent activation energies for the decomposition of CaAlH₅ and NaBH₄ in the composite system were reduced to 142.9 and 146.5 kJ/mol, respectively. It is believed that the formation of AlCa, AlB and CaB alloys during the dehydrogenation process is responsible for the distinct reduction in the onset desorption temperature and kinetics enhancement of the 2NaAlH₄ + Ca(BH₄)₂ composite system.