硅酸盐细菌JXF菌株浸矿脱硅条件研究

采用单独摇瓶浸出方法研究了影响硅酸盐细菌浸矿脱硅的各种条件,摇瓶试验表明,pH值、温度、摇瓶转速、装液量、接种量、浸矿时间、矿物种类、菌种特性均对硅酸盐细菌的脱硅效果有重要影响。在pH7.2、温度28℃、摇床转速200 r/min、500 mL锥型瓶的装液量100 mL、接种量3.8×106个/mL,浸出时间5~7 d情况下,JXF菌种浸矿脱硅效果最好。硅酸盐细菌JXF菌株对供试矿物的分解能力依次为绿泥石、高岭石、长石、石英。其中JXF-1菌株脱硅效果最好,可以浸出铝土矿原矿、绿泥石人工混合矿样中50.4%与65.3%的硅,而B.C菌株对该两种矿样的脱硅率仅分别为35.3%,48.2%。     

胶质芽孢杆菌JXF释硅特性研究

摇瓶单因素条件试验与正交试验结果表明,在pH7.2、矿浆浓度20%、温度30℃和细菌接种量15%的条件下,JXF菌种脱硅效果最好。细菌浸矿过程中,应尽量接种芽孢生成率较低时的细菌,试验表明细菌在培养的前4天,芽孢产生率低,活性高。单独摇瓶浸矿试验采用了四种不同的浸出方式,其中利用预先在含被浸矿样和蔗糖的培养基中培养的菌种,然后在有糖的培养基质中对矿样进行浸出,硅的浸出率最高,从各种矿样中浸出硅的范围为25.7%￣65.3%,比其它浸出方式高10%以上。而连续浸出工艺表明,JXF菌株的脱硅率在34.8%￣86.3%,且浸矿时间由7d缩短到5d。     

硅酸盐矿物的硅酸盐细菌浸出工艺研究

采用5种硅酸盐细菌,对含不同硅酸盐矿物的5种矿样（包括铝土矿原矿和人工混合矿）进行细菌浸矿脱硅摇瓶试验和工艺试验。摇瓶试验表明：5种细菌均能较好地浸出矿样中的硅,但其中JXF-1菌的脱硅效果最好;细菌存活环境和硅酸盐矿物的晶格结构影响浸硅效果。工艺试验表明：连续浸出工艺的细菌浸硅效果明显优于摇瓶试验和半连续浸出工艺,并可将浸出时间缩短4 d;以JXF-F菌为浸矿细菌,以含2%蔗糖的阿什比基质矿物盐培养基为细菌培养液和浸出液,采用连续浸出工艺可从铝土矿原矿和含绿泥石人工混合矿获得铝硅比分别为12.53和17.74的精矿,硅浸出率分别达70.1%和83.6%。     

用细菌从铝硅酸盐矿物中浸出硅的工艺研究

采用单独摇瓶浸出、半连续浸出和连续浸出工艺的方式对硅酸盐细菌的浸矿能力作了一个较全面的对比试验.不同来源的硅酸盐菌株均能较好的从铝硅酸盐矿物中浸出硅,但它们的浸出能力存在较明显的差异,微生物浸出工艺表明,采用连续浸出工艺,细菌浸出矿样中硅的效果明显比单独摇瓶浸出与半连续浸出效果要好,且浸矿时间也大幅度的缩短.5种矿样在连续浸出工艺中硅的浸出率比单独摇瓶浸出平均高10个百分点左右,对矿物中的铝也有一定的活化作用,可以浸出供试矿样中6.5%～14.9%的铝,但远低于浸出的硅,可除去铝土矿中的硅,为该菌种在矿物加工和土壤微生物硅肥中的应用提供理论依据.     

用细菌从铝硅酸盐矿物中浸出硅的工艺研究

采用单独摇瓶浸出、半连续浸出和连续浸出工艺的方式对硅酸盐细菌的浸矿能力作了一个较全面的对比试验。不同来源的硅酸盐菌株均能较好的从铝硅酸盐矿物中浸出硅,但它们的浸出能力存在较明显的差异,微生物浸出工艺表明,采用连续浸出工艺,细菌浸出矿样中硅的效果明显比单独摇瓶浸出与半连续浸出效果要好,且浸矿时间也大幅度的缩短。5种矿样在连续浸出工艺中硅的浸出率比单独摇瓶浸出平均高10个百分点左右,对矿物中的铝也有一定的活化作用,可以浸出供试矿样中6.5%～14.9%的铝,但远低于浸出的硅,可除去铝土矿中的硅,为该菌种在矿物加工和土壤微生物硅肥中的应用提供理论依据。     

硅酸盐细菌代谢产物对硅酸盐矿物的浸溶作用研究

研究发现,硅酸盐细菌JXF菌株在含有石英粉的培养基中能合成有机酸、氨基酸、多糖等各种代谢产物并分泌释放到发酵液中。随着发酵时间的延长,发酵液中4种有机酸（草酸、柠檬酸、酒石酸、苹果酸）含量逐渐降低,说明细菌又以它们为营养物质进行生长繁殖;在菌种的不同发酵期,合成氨基酸的种类不同,在无氮或含石英粉的培养基中,有利于细菌大量合成多糖类物质。摇瓶试验表明,有机酸、氨基酸、多糖均具有破坏高岭石晶格结构的能力而释放出其中的铝、硅,原因是这些有机物具有络合矿物中各种金属离子的有机基团并有一定的酸溶作用。试验还表明,各种代谢产物在浸出硅酸盐矿物中具有协同作用,三者的混合物的浸矿效果明显好于它们各自对矿物的作用效果。     

胶质芽孢杆菌JXF菌株代谢产物与脱硅作用研究

采用摇瓶振荡培养和电镜分析, 研究了胶质芽孢杆菌JXF菌株在发酵培养过程中产生代谢产物的种类、能力及其对钾长石中硅的浸出效果。结果表明, 在含有石英粉的培养基中, JXF菌株可合成有机酸、氨基酸、多糖等代谢产物并析释于发酵液中。发酵液中4种有机酸(草酸、柠檬酸、酒石酸、苹果酸)的含量随发酵时间延长逐渐降低, 说明细菌又以它们为营养物进行生长繁殖; 在不同发酵期JXF合成的氨基酸种类不同, 而无氮或含石英粉的培养基有利于细菌大量合成多糖类物质。代谢产物摇瓶浸矿试验表明, 有机酸、氨基酸、多糖等均具有配合矿物中各种金属离子的有机基团并有一定的酸溶作用, 均可破坏钾长石晶格结构, 并释放出其中的铝、硅。在浸出硅酸盐矿物时, 代谢产物具有协同作用, 三者的混合物的浸矿效果明显优于它们单独作用时的效果。     

硅酸盐细菌代谢产物对不同结构硅酸盐矿物风化作用的影响

选用一株硅酸盐细菌,采用摇瓶发酵培养,对比分析不同结构硅酸盐矿物刺激与促进细菌产代谢产物的差异;采用摇瓶浸矿试验,研究细菌代谢产物及细菌对石英、斜长石与高岭石的风化分解作用。结果表明,硅酸盐矿物可促进细菌产草酸、酒石酸、苹果酸等有机酸、氨基酸与多糖,同时可刺激细菌代谢产生特定的柠檬酸与氨基酸,高岭石对细菌代谢产有机酸与多糖促进作用最强,斜长石对细菌代谢产生氨基酸促进作用最明显;各代谢产物均对硅酸盐矿物具有一定的风化分解作用,其中多糖对矿物分解作用最强,混合代谢产物对矿物具有更强的风化作用;具层状结构的高岭石较架状结构的斜长石更易被细菌及代谢产物所风化分解;3种代谢产物的混合物在风化矿物过程中具有明显协同作用;细菌对矿物分解作用明显较混合代谢产物强,表明细菌对矿物风化分解作用是生物物理及化学等多种因素共同作用的结果。     

硅酸盐细菌生长及对硅酸盐矿物中硅铝的浸溶

为了找到能从高硅含量的硅酸盐矿物中脱硅的细菌,利用常规微生物筛选技术,从硅酸盐肥料中筛选到1株编号为JXF菌株,通过形态学研究,并与标准的胶质芽孢杆菌等硅酸盐细菌的生化特征比较,表明JXF细菌为胶质芽孢杆菌。摇瓶浸矿试验表明,硅酸盐细菌具有较强的活化、吸持硅酸盐矿物中硅、铝的能力,以高岭石为底物,培养2~6d,接灭活菌上清液中硅的含量均高于接菌组中硅的含量,细菌吸持的硅含量占解硅量的90%左右,细菌数越多,细胞吸持的硅也多。通过对浸渣主要矿物物相分析,表明层状结构的硅酸盐矿物如高岭石、伊利石等较易被细菌作用而释放出其中的硅、铝、钾等元素。     

铝土矿的微生物选矿

利用野生和实验室繁殖的环状芽胞杆菌和粘液芽胞杆菌的突变体菌种,从五种不同的铝土矿中浸出硅。矿石中硅是主要杂质,它与铝结合形成铝硅酸盐。在连续浸出条件下,五天内从不同矿石中浸出了12.5%到73.6%的硅。浸出后的固体浸渣,具有更高的铝含量和硅模数(即 Al_2O_3/SiO_2的比值)。     

The use of collectors mixture in the reverse cationic flotation of magnetite ore: The role of Fe-bearing silicates

The paper describes effective reagent combinations for removal of silicates by reverse cationic flotation from magnetic concentrate in magnetite ores processing. This work is based on a hypothesis that a further development in reverse cationic flotation of iron ores implies, a more detailed consideration of the nature of the Fe-bearing gangue minerals. Thus, the choice of reagent regime has been determined by the similar physicochemical properties of iron oxides and silicates such as amphiboles due to inclusion of iron into their crystal lattice. Zeta-potential studies of Fe-oxides, quartz and Fe-bearing amphibole samples have shown that amines of different molecular structure are equally well adsorbed both on the surface of Fe-oxides and on the surface of silicates within рН range of 4–10. Flotation studies of quartz and Fe-bearing amphibole samples have revealed that the use of starch as a depressant of Fe-oxides has a hydrophilic effect on the surface of Fe-bearing silicates and significantly decreases their flotation by ether amines. Flotation of these minerals is not possible by primary monoamines in the presence of starch due to the adsorption layer formation.The experimentally selected mixtures of ether amines with primary monoamines or with alcohols provide formation of a hydrophobic adsorption layer on the surface of amphiboles and magnetite–silicate aggregates, even in the presence of starch in the system. A total hydrophobic effect is sufficient for an effective flotation of the entire silicate complex and producing of magnetite concentrates with SiO₂ content <1.0% and Fe content up to 70.3% from magnetic concentrate with SiO₂ content ～3%.     

激发剂的性质对页岩提钒尾渣基地聚物性能的影响

为研究地聚物的弱碱性激发技术,以湖北某地的页岩提钒尾渣为原料,进行了地聚物碱激发研究。主要研究了不同偏高岭土掺量、激发剂模数和激发剂用量对地聚物抗压强度的影响。最终确定在m（提钒尾渣）:m（偏高岭土）=9:1,弱碱性激发剂Na₂SiO₃的模数为3.0,Na₂SiO₃的掺量为14%的激发制度下,地聚物试样3 d的抗压强度即可达到27.55 MPa,极大地提高了地聚物的抗压性能。对不同模数的硅酸钠下制备的地聚物进行物相转变、化学键变化和微观形貌分析,发现在液体硅酸钠的作用下,页岩提钒尾渣中的石英被进一步溶解;溶解的无定形硅铝物质与液体硅酸钠中的硅酸根反应逐渐生成硅铝凝胶相;液体硅酸钠中的硅酸根起一个诱导作用,液体硅酸钠的模数越高,其硅酸根含量越高,与页岩提钒尾渣中的无定形硅铝物质反应也越迅速,从而生成更多的硅铝凝胶相,促进了地聚物抗压强度的提高,实现了地聚物的安全制备。      

硅钙渣复合地聚物水化机理研究

为实现硅钙渣、粉煤灰及矿渣三种固废的协同利用,本文通过开展不同粉煤灰、矿渣比(灰渣比)下的硅钙渣复合地聚物制备实验,对硅钙渣复合地聚物的水化机理进行了研究。结果表明,硅钙渣复合地聚物是由β-硅酸二钙自身水化和碱激发水化共同形成的一种以C—S—H和C(N)—A—S—H为主的二元复合胶凝材料;相较于晶相矿物,玻璃相矿物更易发生碱激发水化反应,导致灰渣比在0.5以上时7 d水化物中残存大量未反应的莫来石,但随养护时间的延长莫来石会继续进行水化,并在28 d时生成蠕虫状四方钠沸石和条状贝德石。同时在灰渣比为1.0时,硅钙渣地聚物微观形貌最均匀致密,28 d抗压强度最高,达到37.9 MPa,说明此时能够发挥出粉煤灰、矿渣、硅钙渣之间最佳的协同效应。     

Bioleaching of six nickel sulphide ores with differing mineralogies in stirred-tank reactors at 30 °C

A bioleaching study was conducted with six nickel sulphide ores from different geographical locations across Canada. Mineralogical and chemical examination revealed considerable variability between the samples, particularly in the silicate phases. The ores contain 0.3–1% nickel, primarily in pentlandite and secondarily in pyrrhotite. Copper is present primarily in chalcopyrite, and cobalt in pentlandite. The ores were subjected to the same crushing and grinding procedure, and bioleached under the same conditions for 3 weeks with a mixed culture of iron- and sulphur-oxidizing bacteria. Stirred-tank experiments with finely ground ore (−147 μm) at 30 °C were conducted to assess the effect of pH (2–5) and the impact of the bacteria. Nickel extraction from pentlandite and pyrrhotite during bioleaching at pH 2 and 3 was generally good (49–86% after 3 weeks), and cobalt extraction tracked nickel extraction over most conditions. All six ores showed a similar response to a change in pH; an increase in pH from 2 to 3 resulted in approximately the same nickel and cobalt extraction (within statistical error), and a statistically significant reduction in sulphuric acid consumption, dissolved iron, and magnesium extraction.     

赤铁矿与锥辉石浮选分离捕收剂的研究

以最具代表性的白云鄂博矿床原生赤铁矿和含铁硅酸盐矿物锥辉石(Acmite)为研究对象,在纯矿物浮选试验的基础上,结合吸附量、ζ-电位测定结果,对各类捕收剂的选择性及其与矿物表面作用机理进行了讨论,提出了研制新型高效硅铁分离捕收剂的有效途径。     

硅酸盐杆菌的紫外诱变育种与脱硅应用研究

将一株从矿坑水中筛选到的硅酸盐杆菌YK-1进行紫外诱变,选育出突变菌株YK-4。对YK-1和YK-4进行铝土矿脱硅能力对比试验和YK-4突变株遗传稳定性试验,结果表明,紫外诱变的最佳照射时间为20 s,YK-4菌株对SiO2的脱除率比原菌株YK-1提高了29.51%,并且其遗传性能稳定。应用YK-4进行了铝土矿脱硅的单槽放大试验,结果表明,单槽放大后,突变菌株的脱硅效果仍然比较显著,能将铝土矿铝硅比从4.02的提高到8.05,硅浸出率达到45.53%。     

铜捕收剂EP浮选永平铜矿石的工业应用

永平铜矿矿石经过一段磨矿,铜矿物单体解离度可达到80％-85％,以高效选择性铜捕收剂EP对已单体解离的粗粒铜矿物进行选择性捕收,并采用开路优先浮选流程结构,避免了在中矿循环中使硫受到抑制,从而也提高硫的回收率。试验室多次试验获得较好试验结果,在现场完成了适应性验证试验的基础上,工业试验达到预期效果,铜精矿品位提高1．11％,铜回收率提高1．58％,硫回收率提高10．86％。