Hot compression deformation behavior of the Mg-AI-Y-Zn magnesium alloy

The hot deformation behavior of a Mg-Al-Y-Zn magnesium alloy was investigated by hot compressive testing on a Gleeble-1500 thermal simulator at the temperanging from 523 to 673 K with the swain rate varying from 0.001 to 1s-1.The relationships among flow stress,swain rate,and deformation temperature were analyzed,and the deformation activation energy and stress exponent were calculated.Microstructure evolution of the alloy under different conditions was examined.The results indicated that the maximum value of the flow stress increased with the decrease of deformation temperature or the increase of swain rate.Under the present deformation conditions,dynamic recrystallization (DRX) oeettrred in the alloy,which was the main softening mechanism during deformation at elevated temperature.The deformation temperature and strain had significant effects on the microstructure of the alloy.     

AZ70镁合金热压缩变形特性

在温度为300℃～420℃、应变速率为0.001s-1～1s-1的变形条件下,采用Gleeble-1500热模拟机对AZ70镁合金热压缩变形特性进行了研究。结果表明,合金的流变应力随应变速率的增大而增大,随温度的升高而降低;在给定的变形条件下,计算出合金的变形激活能为132kJ/mol,应力指数为6.2;建立了合金高温变形的本构方程;降低变形温度和提高应变速率可使再结晶晶粒平均尺寸减小。根据实验分析得出,材料的最佳热加工工艺条件为变形温度340℃～400℃,应变速率0.001s-1～0.1s-1,并提出以低速为宜。     

AZ31镁合金高温热压缩变形特性

在应变速率为0.005～5 s-1、变形温度为250～450℃条件下,在Gleeble-1500热模拟机上对AZ31镁合金的高温热压缩变形特性进行了研究.结果表明:材料流变应力行为和显微组织强烈受到变形温度的影响;变形温度低于350℃时,流变应力呈现幂指数关系;变形温度高于350℃时,流变应力呈现指数关系;变形过程中发生了动态再结晶且晶粒平均尺寸随变形参数的不同而改变,其自然对数与Zener-Hollomon(Z)参数的自然对数成线性关系;材料动态再结晶机制受变形机制的影响,随温度的不同而改变;低温下基面滑移和机械孪晶协调变形导致动态再结晶晶粒的产生;中温时Friedel-Escaig机理下位错的交滑移控制动态再结晶形核;高温时位错攀移控制整个动态再结晶过程.在本实验下,材料的最佳工艺条件是:变形温度350～400℃,应变速率为0.5～5 s-1.     

Mg-6.3Zn-0.7Zr-0.9Y-0.3Nd镁合金的高温塑性变形行为的热压缩模拟

采用Gleeble-1500热压缩模拟试验机进行压缩实验,研究ZK60(0.9Y+0.3Nd)镁合金在变形温度623～773K、应变速率0.001～1s-1的范围内的变形行为,计算应力指数和变形激活能,并采用Zener-Hollomon参数法构建合金高温塑性变形的本构关系。结果表明:在实验变形条件下,合金的真应力—真应变曲线为动态再结晶型;在实验温度范围内,应力指数随着变形温度的升高而增大,变形激活能随着变形温度和应变速率的增加而增大。对比ZK60合金,ZK60(0.9Y+0.3Nd)合金的变形激活能提高38%。     

Hot compression deformation behavior of MB26 magnesium alloy

The flow stress features of MB26 magnesium alloy were studied by isothermal compression at 300-450 ℃ and strain rate of 0.001^-1 s J with Gleeble 1500 thermal simulator. In addition, the deformation activation energy Q was calculated. The results show that the strain rate and deformation temperature have obvious effect on the true stress. The peak value of flow stress becomes larger with increasing strain rate at the same temperature, and gets smaller with the increasing deformation temperature at the same strain rate. The alloy shows partial dynamic recrystallization. The flow stress of MB26 magnesium alloy during high temperature deformation can be represented by Zener-Hollomon parameter including the Arrhemius term. The temperatt, re range of 350-400℃ is suggested for hot-forming of this alloy.     

Cu-Ni-Si-Cr合金高温热压缩变形行为

采用Gleeble-1500D热模拟试验机,对Cu-Ni-Si-Cr合金在变形温度为600～800℃、应变速率为0.01～5 s-1条件下的动态再结晶行为以及组织转变进行了研究,分析了实验合金在高温变形时的流变应力和应变速率及变形温度之间的关系,并研究了在热压缩过程中组织的变化.结果表明:应变速率和变形温度的变化强烈地影响合金流变应力的大小,流变应力随变形温度升高而降低,随应变速率提高而增大,材料显微组织强烈受到变形温度的影响.     

Hot deformation behavior and processing map of squeeze cast ZK60 magnesium alloy

The deformation behavior of squeeze cast ZK60 magnesium alloy was investigated by compressive tests conducted at temperatures of 250-450 ℃ and strain rates of 0.001-10 s^-1 with Gleeble--1500D thermal simulator system. The hot deformation behavior of squeeze cast ZK60 magnesium alloy was characterized using processing map developed on the basis of the dynamic materials model. The processing map gives safe ＂processing windows＂ in which the processes of dynamic recovery and dynamic recrystallization occur. It reveals that the dynamic recrystallization domain occurs at 375 ℃ and strain rate of 0.001 s^-1, and its power dissipation efficiency approximately corresponds to 36%, which should be considered the optimum parameters for hot working of squeeze cast ZK60 magnesium alloy. The variation of the instability parameter ξ（ε） with temperature and strain rate constitutes an instability map, which is used for delineating the region of flow instability. The material exhibits flow instability which should be avoided in mechanical processing.     

铸态AZ61镁合金热压缩变形组织变化

利用Gleeble-1500对铸态AZ61镁合金在变形温度200~500℃,应变速率0.001~1s-1的条件下进行压缩变形;利用显微结构分析和硬度测试等研究不同变形条件下AZ61镁合金的组织和性能,引用Z值(Zener-Hollomon系数)研究温度和应变速率对AZ61镁合金组织的影响,建立再结晶晶粒尺寸与Z值之间的关系。结果表明:铸态AZ61镁合金在热变形时表现出动态再结晶特征,随温度上升,再结晶容易发生且峰值应力降低,再结晶晶粒尺寸随温度升高而增大;随应变速率上升,峰值应力增大且峰值应力对应的应变量增大,再结晶晶粒尺寸减小;硬度大小的变化也与动态再结晶密切相关。     

Mg-Nd-Zn-Zr稀土镁合金的热变形行为

采用GLEEBLE-1500热模拟机对Mg-Nd-Zn-Zr稀土镁合金在温度为250～450.℃、应变速率为0.002～0.100.s-1、最大变形程度为60%的条件下, 进行高温压缩模拟实验研究. 分析了实验合金在高温变形时的流变应力和应变速率及变形温度之间的关系, 计算了变形激活能和应力指数, 并研究了在热压缩过程中组织的变化, 为确定该稀土镁合金的挤压温度提供了实验依据. 结果表明: 合金的峰值流变应力随应变速率的增大而增加, 随温度的升高而降低; 合金的变形激活能在300～400.℃内变化不大, 而在400～450.℃时增加很大; 根据实验分析认为该稀土镁合金挤压温度定在350～400.℃左右为宜; 在350.℃左右顺利挤出的实验合金有很好的力学性能: σb=275.5.MPa, δ=13.5%.     

CuZn(Cr，Zr)合金的热变形行为

制备了ＣｕＺｎ和ＣｕＺｎＣｒＺｒ两种合金，用Ｇｌｅｅｂｌｅ－１５００测定它们在恒温和恒速下的稳态变形抗力绘制成ｌｎσ－１／Ｔ关系曲线，从而确定合金的变形激话能Ｑ和应力指数ｎ，并观察了热变形组织。结果表明；在Ｃｕ１３Ｚｎ合金中加入０．１％Ｚｒ和０．１％Ｃｒ，对合金的动态再结晶有强烈抑制作用，合金在６５０～８２０℃之间热变表为不完全动态再结晶组织，而Ｃｕ１３Ｚｎ合金在７５０～８２０℃之间为完全动态再结     

Hot deformation behavior of KFC copper alloy during compression at elevated temperatures

1 Introduction Along with the recent development in the semiconductor industries, precipitation-hardenable alloy copper strips with high electrical conductivity and strength, as well as excellent heat resistance, were commonly used as a leadframe materia…     

Mg-6Zn-1Al-0.3Mn 镁合金的热压缩变形行为及变形组织

采用Gleeble热模拟方法研究Mg?6Zn?1Al?0.3Mn 变形镁合金在温度为200~400°C,应变速率为0.01~7 s?1条件下的热压缩变形行为。结果表明,变形温度和应变速率显著影响其热变形行为。通过计算获得了热变形激活能及应力指数分别为Q=166 kJ/mol,n=5.99,且其本构方程为ε&=3.16×1013[sinh(0.010σ)]5.99exp [?1.66×105/(RT)]。热压缩显微组织观察表明：在应变速率为0.01~1 s?1的条件下,在250°C热压缩变形时初始晶粒晶界及孪晶处发生了部分动态再结晶,而在高温(350~400°C)条件下,发生了完全动态再结晶且再结晶晶粒尺寸随着应变速率的增加而减小。获得的较优的变形条件为温度330~400°C、应变速率为0.01~0.03 s?1以及350°C、应变速率为1 s?1。     

基于人工神经网络的ZK60镁合金热压缩变形行为

在变形温度为200～400℃、应变速率为0.001～1s-1条件下,对ZK60镁合金进行热压缩实验,建立一个单隐层前馈误差反向传播人工神经网络模型,研究该镁合金的流变行为。模型的输入参数分别为变形温度、应变速率和应变,输出为流变应力,中间隐含层包含23个神经元,并采用Levenberg-Marquardt算法对此网络模型进行训练。结果表明:ZK60镁合金的流变应力随变形温度升高和应变速率降低而减小;其高温压缩流变应力曲线可描述为加工硬化、过渡、软化和稳态流变4个阶段,但在较高温度和较低应变速率时,过渡阶段不很明显;所建神经网络模型可以很好地描述ZK60镁合金的流变应力,其预测值与实验值吻合很好;利用该模型预测的变形温度和应变速率对流变应力的影响结果与一般热加工理论所得结果一致。     

工业态AZ31镁合金的超塑性变形行为

研究了工业态AZ31镁合金在温度 6 2 3～ 72 3K和应变速率 1× 10 -5～ 1× 10 -3 s-1范围内的超塑性变形行为。结果表明 ,工业态AZ31镁合金表现出良好的超塑性 ,其最高断裂延伸率达到 314%,应变速率敏感指数达 0 .4。显微组织观察和断口分析表明 ,工业态AZ31镁合金超塑变形主要由晶界滑动机制所控制 ,同时 ,动态再结晶也是合金超塑变形的一种协同机制。     

Hot deformation behavior of a spray-deposited AZ31 magnesium alloy

The flow stress behavior of an as-spray-deposited AZ31 magnesium alloy with fine grains was investigated by means of compression tests with a Gleeble 1500 thermal mechanical simulator at isothermal constant strain rates of 0.01, 0.1, 1.0, and 10 s-1; the testing temperatures ranged from 623 to 723 K. It is demonstrated that a linear equation can be fitted between the Zemer-Hollomon parameter Z and stress in a double-log scale. The effect of deformation parameters on the behavior of recrystallization was analyzed. Dynamic recrystallization (DRX) generally occurs at a higher temperature and at a lower strain rate. The constitutive equation of the spray-deposited AZ31 magnesium alloy is elevated temperatures due to the fine grain, which provides a large amount of nucleation sites and a high-diffnsivity path for the atom.     

流变铸造镁合金AZ31B的热/力模拟

采用双螺旋流变铸造工艺制备了镁合金AZ31B的棒坯,利用Gleeble-3000型热/力模拟机研究了流变铸造和普通连铸棒坯在变形温度为250～400℃,变形速率为0.001～5 s-1,最大变形量为60%时的热压缩变形行为.分析了材料流变应力与变形量、变形温度和应变速率之间的关系,比较了两种不同铸造工艺对热塑性变形行为的影响.结果表明:流变铸造坯料在变形过程中的形变均匀性明显优于普通铸造的,因此不需预处理即可直接进行塑性成型;350℃以上热变形流变铸造坯料的变形抗力明显小于普通铸造坯料的;流变铸造使AZ31B合金的塑性加工性能得到改善;产生这种差别的主要原因是普通铸造坯料组织为粗大树枝晶,而流变铸造坯料组织为细小等轴晶.     

压下量对WE43镁合金变形机理和孪生行为的影响（英文）

研究最后一道次压下量对铸态WE43镁合金在480℃直接热轧过程中位错滑移和孪生行为的影响。结果表明,在480℃轧制时柱面滑移始终是主要的滑移模式。另外,不同压下量下激活的孪生类型不同。较小的压下量(2%)下激活的主要是{■}拉伸孪生,而在较大的压下量(12%和20%)下激活的主要是{■}压缩孪生和■二次孪生。Schmid因子计算表明,{■}孪晶变体选择遵循Schmid定律,而{■}孪晶变体选择不遵循Schmid定律。即使单道次压下量达到20%也几乎没有发现动态再结晶晶粒,这可能是因为没有达到动态再结晶所需要的变形量。     

MoNb合金热变形行为及本构关系

采用Gleeble-3800型热模拟试验机对MoNb合金进行等温恒应变速率压缩试验,研究该合金在变形温度900~1200℃和应变速率0.01~10 s^-1条件下的热变形行为,计算其热变形激活能。结果表明:变形温度和应变速率对流动应力具有显著影响,流动应力随变形温度的升高和应变速率的降低而减小。误差分析表明,采用多元线性回归法建立的MoNb合金本构关系模型具有较高的精度,该模型的预测值误差小于10%的数据点占总数的92.86%,相关系数和平均相对误差分别为0.976和4.08%,能较为准确的预测合金的高温流动应力。     

7150铝合金高温热压缩变形流变应力行为

在Gleeble-1500热模拟机上对7150铝合金进行高温热压缩实验,研究该合金在变形温度为300~450 ℃和应变速率为0.01～10 s~(-1) 条件下的流变应力行为.结果表明:流变应力在变形初期随着应变的增加而增大,出现峰值后逐渐趋于平稳;峰值应力随着温度的升高而减小,随着应变速率的增大而增大;可用包含Zener-Hollomon参数的Arrhenius双曲正弦关系来描述合金的热流变行为,其变形激活能为226.698 8 kJ/mol;随着温度的升高和应变速率的降低,合金中拉长的晶粒发生粗化,亚晶尺寸增大,再结晶晶粒在晶界交叉处出现并且晶粒数量逐渐增加;合金热压缩变形的主要软化机制由动态回复逐步转变为动态再结晶.