二次冷轧压下率对镀锡板组织性能的影响

 为了开发高硬度二次冷轧镀锡板,采用硬度计、拉伸试验机、光学显微镜和X射线衍射仪研究了二次冷轧压下率对氮强化镀锡板组织性能的影响规律。结果表明,随着二次冷轧压下率提高,试验钢的硬度和强度提高,各向异性增加,伸长率降低,当二次冷轧压下率为44%时可达到DR-9M的技术要求。同时采用高碳和氮强化成分体系配合低温退火不利于有利织构{111}的形成,织构取向密度的峰值出现在{001}<110>~{114}<110>、{223}<110>~{445}<110>和{554}<225>,冲压成形时易在45°方向上产生制耳。     

冷轧压下率对无抑制剂取向硅钢初次再结晶退火的影响

对无抑制剂取向硅钢不同压下率下初次再结晶退火后的显微组织、宏观织构和微观织构进行了研究.结果表明,冷轧板织构主要为α取向线{001}＜110＞、{112}＜110＞和{111}＜110＞织构以及γ取向线{111}＜110＞织构.初次再结晶退火后,α取向线织构减弱,织构主要为γ取向线{111}＜112＞织构.随冷轧压下率的增加,冷轧和初次再结晶织构强度增加.当压下率为88％时,初次再结晶退火后 Goss 织构和{111}＜112＞织构强度最高,最有利于发生二次再结晶.EBSD 分析显示,Goss 取向晶粒大多与{111}＜112＞取向晶粒相邻.提高冷轧压下率,Goss取向晶粒和{111}＜112＞取向晶粒都增加,Goss 取向晶粒偏离理想取向角度减少.     

退火工艺及压下率对超低碳CSP冷轧薄板织构的影响

在实验室用电阻炉模拟了包钢CSP工艺生产的以62.0%和71.4%压下率冷轧的1.9 mm和1.0 mmCD01钢(0.047%C)和SPCC钢(0.041%C)冷轧板的700℃罩式退火工艺。结果表明,冷轧板退火后主要以{111}〈110〉和{111}〈112〉织构为主;71.4%压下率冷轧板快速升温退火后{112}〈110〉取向密度最大,且大角度晶界所占比例较大,织构密度较大,织构主要集中在γ取向线附近。     

冷轧压下率对连续退火Ti-IF钢组织和织构的影响

以工业生产的Ti-IF钢热轧板为研究材料,结合连续热镀锌线的工艺特点,采用实验室冷轧、盐浴退火方法和金相、X射线织构测试等分析手段,研究了冷轧压下率对组织和织构的影响规律。试验结果表明,随着冷轧压下率从60%提高到90%,冷轧态α取向线上的取向密度不断增强,而且主要形成了{223}110和{114}110织构,γ线上的{111}110和{111}112织构亦有所增强;退火后铁素体晶粒尺寸从9.0级细化到10.5级;试验钢退火后仍具有较强的{223}110和{114}110织构,且随着冷轧压下率的提高,{111}织构有增强的趋势。要获得强的{111}织构,冷轧压下率需在80%以上。     

冷轧压下率对IF钢组织织构和性能的影响

以工业生产的热轧板为原料,研究了冷轧压下率对罩式退火后的Ti-IF钢和Ti＋Nb-IF钢组织织构和性能的影响。研究结果表明,经罩式退火后,两种IF钢再结晶基本完成,晶粒呈饼状;随着压下率的增加,晶粒尺寸变小;应变硬化指数n90&#176;值逐渐降低。Ti＋Nb-IF钢塑性应变比r90&#176;值在碳含量较高、压下率为70%,或碳含量较低、压下率为80%时,达到最大值;Ti-IF钢塑性应变比r90&#176;值在压下率70%时,达到最大值。随着冷轧压下率的加大,IF钢的织构也越强,并且织构从较低冷轧压下率时的{223}〈110〉、{114}〈110〉和{111}织构变为较高压下率时的{223}〈110〉、{111}〈110〉和{114}〈110〉织构,织构类型有向{111}织构靠拢的趋势。     

冷轧过程中IF钢的织构演变

以铁素体区热轧低温卷取的Ti-IF钢为研究对象,选择13%~75%的冷轧压下率,观察在冷轧过程中织构的演变。研究表明,压下率为46%是一个转折点,冷轧压下率较小(13%~35%)时,表面上取向变化为{110}001→{554}225→{111}112→{111}110→{223}110,{114}110转向{001}110;压下率达到46%时,{111}织构消失;继续增加压下率,{111}织构再次出现,并随压下率增加而增强。随着冷轧压下率的增加,中心面上的{111}织构强度先增加,压下率达到46%后又降低,最强组分先由{001}110向{223}110转动;压下率达46%时,又向反方向转动。     

二次冷轧压下率对无取向电工钢薄带磁性能和织构的影响

研究了二次冷轧压下率对无取向硅钢薄带磁性能和织构的影响,结果表明:采用二次冷轧工艺时,55%左右的二次冷轧压下率能够获得磁性能优良的0.2 mm厚无取向硅钢薄带.当二次冷轧压下率高于55%后,成品钢带中对磁性能不利的r织构组分比例逐渐增强,特别是{111}<112>、{111)<110>织构.采用55%左右的二次冷轧压下率制造能获得{100}面织构和高斯织构比例都较高的产品,其铁损P1.0/400能够降低到10.6 W/kg,同时磁感B50能达到1.68T.     

冷轧压下率对薄规格取向硅钢冷轧和退火织构的影响

实验采用不同厚度的低温取向硅钢热轧板冷轧至0.18 mm。通过XRD分析冷轧板表面和中心层的织构,通过EBSD分析了脱碳板截面的织构。结果表明,冷轧样品表层和中心层,随着压下率增大,{111}面织构总含量有所减少,{100}面织构总含量有所增多;脱碳样品中{111}面织构明显增多,尤其是{111}〈112〉织构组分,{100}面织构明显减少,尤其是{100}〈011〉织构组分,{411}〈148〉织构组分也明显增多;脱碳样品中,随着压下率增大,晶粒尺寸逐渐减小。不利于二次再结晶发展的织构随着压下率的增大明显增加,同时有利的CSL晶界随着压下率的增加会稍有减少。     

冷轧Ti-IF超深冲钢罩式退火机理及织构变化规律的研究

在480~750℃条件下,模拟罩式退火,利用光学显微镜、X射线衍射和金相显微硬度计研究了冷轧Ti-IF超深冲钢晶粒结构的变化,通过取向密度函数分析了再结晶过程织构演变规律。研究表明:冷轧Ti-IF超深冲钢的再结晶温度约为630℃,再结晶过程能够在660℃条件下2 h之内完成;冷轧后该钢主要有4种织构,分别是{001}〈110〉、{111}〈110〉、{111}〈112〉和{112}〈110〉;在退火再结晶过程中,{111}逐渐转变为γ-{111},当退火温度升至720℃时,{001}〈110〉和{112}〈110〉转变为纤维织构γ-{111},最终{111}〈110〉和{111}〈112〉成为主要织构类型。     

热轧工艺对TSCR流程生产取向硅钢组织和性能的影响

取向硅钢热轧板中组织、织构梯度对发展完善的二次再结晶十分关键,通过对2种不同热轧工艺生产取向硅钢的组织、织构进行研究,结果表明:采用后道次大压下热轧工艺时热轧板表层再结区晶粒平均尺寸增加,再结晶区厚度增加,高温退火后二次晶粒尺寸减小;采用后道次大压下热轧工艺热轧时,热轧板中平均等效应变高,热轧板厚度心部{100}〈011〉和{100}〈001〉位向取向强度降低,({111}～{113})〈110〉位向取向强度提高,高温退火后{110}〈001〉位向偏离角降低,磁性能提高。     

JSP-双机可逆冷轧条件下IF钢织构研究

针对济钢现场工艺条件下生产的Ti-IF钢,利用X’Pert ProxX射线衍射宏观织构分析方法,研究了中薄板坯热连轧轧制及随后的冷轧、退火工艺过程中织构的变化规律。IF钢冷硬板主要织构类型为{111}〈110〉、{111}〈112〉和{001}〈110〉,其中{111}〈110〉织构强度达到12;再结晶退火后的IF钢退火板,主要织构类型为{111}〈110〉和{111}〈112〉,{111}〈110〉织构强度提高到15.37。济钢生产的Ti-IF钢获得了对板材成形最有利的{111}//ND织构。     

Effect of Cold Rolling Reduction Rate on Secondary Recrystallized Texture in 3 Pct Si-Fe Steel

The phenomenon of secondary recrystallization in 3 pct Si-Fe electrical steel subjected to relatively high cold rolling reduction rates has been investigated. The texture of the secondary recrystallized sample that has a cold rolling reduction rate of 97.2 pct consists mainly of {110}〈112〉 component, which is quite different from the ideal Goss ({110}〈001〉) texture obtained after lower cold rolling reduction rates. The grain boundary character distribution (GBCD) analysis on the primary recrystallized sample with a cold rolling reduction rate of 97.2 pct indicates that the {110}〈112〉 component has the highest frequency of high energy (HE) boundary with a misorientation angle between 20 and 45 deg, whereas the Goss component in the sample subjected to lower cold rolling reduction rates has the highest frequency of HE boundary. These results indicate that the component with the highest frequency of HE boundary surrounding it after primary recrystallization has the privilege to outgrow other components during secondary recrystallization. However, the GBCD analysis for coincidence site lattice (CSL) boundary points out that the Goss component has the highest frequency of CSL boundaries in the primary recrystallized texture irrespective of the cold rolling reduction applied. These results suggest that the HE model can predict the orientation relationship between the primary and secondary recrystallized textures better than the CSL model.     

基于CSP工艺稀土冷轧板罩式退火中组织织构演变

 采用金相显微镜和X射线衍射仪对CSP(Compact Strip Production)稀土板热轧、冷轧及退火3个阶段的组织和织构进行了检测和分析,并结合文献讨论了稀土板组织织构的演变规律。结果表明：稀土冷轧板以{223}<110>、{001}<110>、{112}<110>为主要织构,退火后形成了以{223}<110>和{111}<110>为主的再结晶织构,织构密度均达8. 5以上,{223}<110>和{111}<110>取向差为10°。稀土板开始再结晶需要的温度较高,并且再结晶完成需要的时间较长。再结晶初期织构变化比后期小。试验稀土板退火后{111}/{001}值极大,{111}<011>织构与{111}<211>织构密度差约为6。     

Ti-26Nb-4Zr合金冷轧板材的织构和力学性能

采用X射线衍射和室温拉伸方法研究了冷轧变形和固溶处理对Ti-26Nb-4Zr合金板材的织构和力学性能的影响.研究发现,50%冷轧时形成了{001}〈uvw〉织构,随着冷变形量的增加,逐渐形成了{121}〈111〉和{001}〈110〉混合织构,〈110〉方向由与轧制方向垂直转到与轧制方向平行.800℃固溶处理后,随着变形量的增加,{111}〈110〉再结晶织构形成并逐渐增强,但〈110〉方向始终保持与轧制方向平行.由于加工硬化及晶粒细化的作用,导致随着变形量增加,冷轧板材的强度逐渐提高,塑性降低.固溶处理后,由于发生再结晶,使得板材的塑性相比冷轧态明显提高.      

Effects of Rolling Parameters on Texture and Formability of High Strength Ultra-Low Carbon BH Steel

 The effects of hot rolling and cold rolling parameters on texture and r (plastic strain ratio) value of high strength ultra low carbon bake hardening (ULC-BH) steels are studied with orientation distribution function (ODF) structural analysis method. After hot rolling, the high strength ULC-BH steel sheet has weak γ-fiber with uniform orientation distributions, and weak α-fiber, of which {445}<110> component forms a high intensity peak at coiling temperature of 750 ℃. After cold rolling, both {111}<110>-{111}<112> intensity on the γ-fiber and {111}-{112}<110> intensity on the α-fiber enhanced. As a result of substitutional solute elements Mn and P being added to the steel, strong {112}<110> deformation texture component is observed on α-fiber, especially at 80% cold rolling reduction, and this leads to the strong {111}<112> recrystallization texture after annealing. The increase of cold rolling reduction shifts the maximum intensity on the γ-fiber from {111}<112> to {111}<113>. After annealing, a very strong γ-fiber is obtained, with intensity peak at {111}<112> component when cold rolling reduction reaches 80%. Increasing coiling temperature and cold rolling reduction improve γ-fiber intensity and r value, resulting in good deep drawability.     

冷轧厚度对3.0 %Si无取向硅钢组织及磁性能的影响

研究了冷轧厚度对3.0 %Si的无取向硅钢组织和磁性能的影响规律。结果表明：当冷轧厚度由0.35 mm减薄至0.27 mm时,平均晶粒尺寸由104 μm降低至89 μm ,P1.5/50由2.186 W/kg降低至2.139 W/kg,P1.0/400由16.978 W/kg降低至13.978 W/kg,涡流损耗占比随之降低,{112}〈110〉取向强度减弱而{111}〈110〉取向强度增加,B50由1.684 T降低至1.662 T。     

一次再结晶法取向硅钢超薄带的冷轧塑性变形行为北大核心CSCD

以市场上购买的取向硅钢成品板为原料,经不同压下率冷轧至0.23~0.08 mm不等。借助X射线衍射仪(XRD)检测了冷轧后样品中的织构组分及其含量,利用电子背散射技术(EBSD)测量了试样的取向因子分布情况。观察了孪晶的形貌与晶体学特征,分析了硅钢超薄带的塑性变形行为。结果发现,在平面压缩应力下,{112}<111>滑移系的取向因子较大。随冷轧压下率的增加,Goss织构的含量逐渐减少,{212}<141>织构组分的含量先增加后减少,{111}<112>织构组分的含量逐渐增加,织构组分以{110}<001>→{212}<141>→{111}<112>顺序演变。冷轧后样品中出现了孪晶,其晶体取向为{001}<110>,冷轧过程中孪晶取向没有发生变化。     

CSP流程DC04汽车板研制

 酒钢利用CSP流程与冷轧生产线匹配进行汽车板DC04的研制,采用提高钢质纯净度和优化热轧工艺及控制冷轧压下量等措施,研制的DC04汽车板碳含量可控制在50×10-6以下,罩式退火后为等轴铁素体组织,成品板晶粒度在ASTM7.5~8,获得了较强的{111}〈110〉{111}〈112〉织构,力学性能均达到IF钢标准。