0Cr18Ni9奥氏体不锈钢管破裂的原因

某公司输气管项目使用的0Cr18Ni9奥氏体不锈钢管,采用焊接方式连接,焊接工艺为手工电弧焊,钢管内输送介质为含硫化氢等腐蚀介质的富氨液,管内介质压力0.5MPa,介质温度35~45℃,运行半年后停产半年,复产时即在钢管焊接接头附近发现横向裂纹。通过宏观低倍、微观金相、化学成分分析以及扫描电镜分析等一系列方法,对该0Cr18Ni9奥氏体不锈钢裂纹形成原因进行分析。结果表明:该0Cr18Ni9奥氏体不锈钢管的破裂原因为连多硫酸应力腐蚀破裂,通过向该0Cr18Ni9奥氏体不锈钢管内吹扫氩气,密封两端口,可避免连多硫酸应力腐蚀破裂。焊接时降低焊接电流,加快焊接速率,减小焊接热影响区的范围,也可降低连多硫酸应力腐蚀破裂的可能性。     

1Cr18Ni9Ti薄壁不锈钢管断裂失效分析

对1Cr18Ni9Ti奥氏体不锈钢焊接接头进行SEM、显微组织观察分析和晶间腐蚀倾向分析,研究焊接工艺对奥氏体不锈钢的影响及其发生腐蚀的原因.试验结果表明:断口为脆性断口,主要由"氢脆"和 "疲劳"引起;焊接过程中1Cr18Ni9Ti奥氏体不锈钢由于经受高温,在晶界组织中形成了贫铬区,使得焊接接头的耐蚀性大大下降,产生晶间腐蚀.     

马氏体和奥氏体不锈钢TIG焊端接接头失效分析

针对船舶设备采用的马氏体和奥氏体不锈钢钨极氩弧焊焊接接头的泄漏问题,采用光学显微镜和扫描电镜观察、显微硬度测定等方法,分析了1Cr17Ni2马氏体不锈钢和1Cr18Ni9Ti奥氏体不锈钢焊接接头各个区域的组织变化和硬度分布.结果表明,在1Cr17Ni2一侧的热影响区紧邻焊缝部位,铁素体受热作用明显长大,显微硬度较低,在热影响区的较高温度区,快冷得到高硬度马氏体,该区断口呈典型的解理与准解理脆性断口,成为焊接接头的薄弱地带,容易产生裂纹导致泄漏.还分析了接头失效的其它原因并提出了改进措施.     

不锈钢波纹管膨胀节早期断裂原因分析

采用化学成分分析、断口宏观检查、金相检验、扫描电镜观察及能谱分析等方法对0Cr18Ni9不锈钢波纹管膨胀节早期断裂的失效原因进行了检验和分析。结果表明:该不锈钢波纹管膨胀节的断裂属脆性断裂,其早期断裂的主要原因是波纹管材料固溶处理不当,晶界存在大量网状碳化物导致其塑性降低,从而使得材料在较大变形时容易产生早期断裂。     

换热设备用不锈钢材料腐蚀失效分析

用能量散射能谱(EDS)、金相分析和化学分析等手段，对换热器用的1Cr18Ni9Ti不锈钢材料的腐蚀失效行为进行了分析.结果表明，换热器用1Cr18Ni9Ti不锈钢的腐蚀失效主要由不锈钢晶间的碳化物析出、环境介质中氯离子含量过高及残余应力所引起.     

基于氩弧焊的0Cr18Ni9Ti不锈钢焊缝成形行为分析

以0Cr18Ni9Ti奥氏体不锈钢作为实验研究对象,采用直流钨极氩弧焊的焊接方式对0Cr18Ni9Ti奥氏体不锈钢进行焊缝熔透性实验,分析超高频脉冲电流、占空比和弧长等因素对0Cr18Ni9Ti奥氏体不锈钢焊缝熔透率的影响。结果表明,0Cr18Ni9Ti奥氏体不锈钢焊缝的熔透率是随着脉冲频率的升高而不断的增大,占空比较小时熔透性对脉冲频率会更敏感,而弧长的变化对其没有显著影响。     

1Cr18Ni9Ti不锈钢管的泄漏及控制方案

1Cr18Ni9Ti是一种应用广泛的奥氏体不锈钢。焊接后,会使接头耐蚀性明显下降,会产生晶间腐蚀和应力腐蚀开裂。分析1Cr18Ni9Ti的焊接性、食品回收管发生泄漏的原因,针对材料特点,采用焊条电弧焊补焊,通过选用合理的焊接材料、焊前准备、焊接工艺来保证焊接质量。     

再生器中奥氏体不锈钢取热盘管失效原因分析

分析表明炼油厂催化裂化装置再生器取热盘管失效的主要原因是腐蚀疲劳。本文就该实际工程条件下,对1Cr18Ni9Ti及1Cr25Ni20两类奥氏体不锈钢在高温含微量氯离子水中的腐蚀疲劳现象及成因进行了讨论。改善汽水流动条件可显著延长盘管的使用寿命。     

废气处理燃烧炉壳裂纹原因及焊接修复

针对材质为0Cr18Ni9的奥氏体不锈钢燃烧炉,分析高温环境使用产生裂纹的原因及焊接性能,通过选择合适的焊接材料和制定合理的工艺措施,成功修复裂纹缺陷,保证0Cr18Ni9奥氏体不锈钢的高温使用性能和要求。     

用扫描电镜研究双相不锈钢应力腐蚀开裂

奥氏体不锈钢由于其综合性能较好,得到了广泛的应用;但在含Cl的介质中,却容易产生应力腐蚀,导致很多重大工程部件发生了应力腐蚀破裂事故,引起各国高度重视。在开拓新的耐应力腐蚀破裂材料中,瑞典人首先提出了铁素体—奥氏体双相不锈钢。我们在实验室用高温高压水和NaCl水溶液对单相奥氏体不锈钢0Cr18Ni9Ti和铁素体-奥氏体双相不锈钢00Cr18Ni5Si2Mo3Nb进行了耐应力腐蚀性能对比实验,在高     

20/0Cr18Ni9复合管焊接工艺和接头的抗腐蚀性能

研究了薄不锈钢内衬复合管的焊接工艺和焊接接头的抗腐蚀性能。采用背部充氩保护的钨极氩弧焊(TIG)和超低碳奥氏体不锈钢焊丝TGS—309L焊接20／0Crl8Ni9复合管的第1层焊缝，焊后利用金相显微镜、扫描电子显微镜和电化学分析方法对焊接接头的化学成分、金相组织、显微硬度以及抗腐蚀性能进行了研究。结果表明：焊缝成形良好焊缝成分和金相组织能保证复合管使用过程中的强度和抗腐蚀性能要求。     

1Cr18Mn14N双相不锈钢在腐蚀介质中的抗空蚀性能

利用磁致伸缩空蚀实验机研究了1Cr18Mn14N双相不锈钢在3%NaCl和05 mol/L HCl溶液中的空蚀行为.结果表明：在3%NaCl溶液中，低硬度的Cr18Mn14N双相不锈钢的抗空蚀性能优于高硬度的水轮机常规用材0Cr13Ni5Mo.1Cr18Mn14N双相不锈钢的空蚀破坏首先在铁素体相发生，铁素体相的失效方式为脆性失效，而奥氏体相是延性失效.奥氏体相区由滑移和孪生引起的塑性变形耗散了空泡溃灭产生的冲击能量，从而提高1Cr18Mn14N双相不锈钢的抗空蚀性能.在05 mol/L HCl溶液中，1Cr18Mn14N的抗空蚀性能不如0Cr13Ni5Mo，结果与3%NaCl溶液中的正好相反，这是由于阳极溶解和氢共同作用的结果.     

20/0Cr18Ni9复合管手工电弧焊工艺研究

研究了薄不锈钢内衬20／0Cr18Ni9复合管的焊接工艺和焊接接头性能。通过光学金相、能谱（EDS）成分及线扫描、扫描电镜（SEM）以及力学性能试验等分析方法对焊接接头进行了分析研究，结果表明：采用手弧焊和超低碳CHS062奥氏体不锈钢焊条焊接20／0Cr18Ni9复合管的过渡层焊缝，能保证复合管使用过程中对焊接接头强度和抗腐蚀性能的要求。     

1Cr18Ni9Ti与1Cr13不锈钢的焊接试验

通过钨极氩弧焊方法,对 1Cr18Ni9Ti 与 1Cr13 实施焊接.采用光学显微镜、扫描电镜对 1Cr13 马氏体型与 1Cr18Ni9Ti 奥氏体型不锈钢焊接接头进行金相组织、断口形貌观察及分析;利用显微硬度计、电子万能拉伸机测量焊接接头的力学性能;并通过海水模拟溶液浸泡试验,测量焊接接头极化曲线和交流阻抗谱.结果表明,通过手工钨极氩弧焊,采用直流正接接法,在合适的工艺下(焊接电流为 80 A,焊接速度为 110 mm/min),能够获得外观平整、组织均匀,力学性能与电化学性能符合要求的焊接接头.

Abstract：

The stainless steels of 1Cr18Ni9Ti and 1Cr13 were welded through deterministic craft by tungsten inert-gas (TIG) welding. The microstructure and fracture pattern of weld joints of 1Cr13martensite and 1Cr18Ni9Ti austenite stainless steels were observed and analyzed by means of LOM and SEM, the mechanical properties of the weld joints were measured with micro-hardness tester and electronic universal stretcher, and the polarization curves and AC impedance spectroscopy of weld joints were tested by seawater immersion test of simulation solution. The results show that adopting manual TIG welding through electrode negative to direct current soldering machine to weld 1Cr18Ni9Ti austenite stainless steel and 1Cr13 martensite stainless steel is feasible; under suitable process (welding current is 80 A, welding speed is 110 mm/min), weld joints can obtain good appearance and uniform structure; mechanical properties and galvano-chemistry properties can meet use requirements.     

HIP diffusion bonding of P/M titanium alloy Ti-6Al-4V and stainless steel 1Cr18Ni9Ti

The HIP diffusion bonding of P/M titanium alloy Ti-6A1-4V and stainless steel 1Cr18Ni9Ti using pure Ni as intermediate layer was studied. Bonding joint with complex bonding interface was obtained by HIPing pre-alloyed Ti-6Al-4V powders and stainless steel 1Crl 8Ni9Ti in a vacuum canning. The joint strengths were examined and the characteristics of bonding joint were observed. The result shows that the maximized strength of HIP diffusion bonding between P/M titanium alloy Ti-6Al-4V and stainless steel 1Cr18Ni9Ti can be up to 388 MPa and the microstructure of bonding joint is acceptable.     

5A02/0Cr18Ni9异种金属电子束焊接接头组织与性能

对5A02防锈铝与不锈钢0Cr18Ni9进行了电子束焊接,分析了接头成形、显微组织、力学性能与断口特征.结果表明,铝、钢的对中焊接头中生成了大量的脆性Fe-Al金属间化合物,未能实现有效连接.偏束焊接头成形总体较好,两母材实质为熔—钎连接,铝—钢界面上生成了一层厚度为1.5μm的化合物层,X射线衍射分析结果显示化合物层由FeAl,FeAl3与FeAl6等相混合组成.熔—钎焊接头最高抗拉强度达136MPa,为铝母材强度的62.7%,断口呈现出脆性断裂与韧性断裂的混合特征,接头的断裂发生在化合物层及其附近的铝焊缝区域.     

酸洗对薄壁0Cr18Ni9不锈钢腐蚀的试验研究

0Cr18Ni9不锈钢薄壁产品在酸洗过程中易发生过腐蚀。本研究采用0.1 mm厚度0Cr18Ni9不锈钢带,对酸洗的各影响因素进行试验研究,结果表明:材料状态不同,耐腐蚀能力不同,退火态更易出现过腐蚀;酸液温度、浓度及酸洗的时间均对不锈钢带腐蚀程度和力学性能有较大影响;在含HF的腐蚀剂中酸洗容易使薄壁不锈钢带力学性能降低,造成材料脆化,且HF含量越高对薄壁不锈钢力学性能影响越大。     

焊后热处理对1Cr18Ni9Ti与2Cr13钢焊接接头组织和性能的影响

通过钨极氩弧焊方法,对1Cr18Ni9Ti与2Cr13钢实施焊接,并对焊接接头整体进行焊后热处理。采用OM、SEM对2Cr13与1Cr18Ni9Ti钢热处理前后的焊接接头组织进行分析,利用显微硬度计、电子万能拉伸机测量了焊接接头的力学性能。结果表明,1Cr18Ni9Ti和2Cr13钢焊接接头热处理前焊缝组织为典型的柱状晶,组织为板条马氏体+残留奥氏体+碳化物;热处理后焊缝组织为回火索氏体,而且碳化物析出量也明显增多。拉伸时,热处理前后焊接接头断裂的部位都发生在奥氏体不锈钢热影响区一侧,热处理前后焊接接头的抗拉强度分别约为635.56、649.44 MPa;焊缝区的显微硬度分别约为276、222 HV0.5,热处理后焊接接头的整体显微硬度比热处理前的明显降低。     

奥氏体不锈钢储能焊接头组织形成规律

采用微型储能焊机对厚度为 0.2mm 的 0Cr18Ni9 奥氏体不锈钢薄板进行了点焊连接研究,理论分析了微型熔核的温度场和冷却速率.结果表明,微型接头由熔核区和熔合区组成.极短的焊接时间,高的冷却速率 5.1×106 K/s,使得熔核中奥氏体组织来不及长大,熔核凝固组织得到显著细化,具有快速凝固特征;同时,熔核中奥氏体组织在敏化温度区停留时间很短,抑制了铬在奥氏体晶界上的析出.当储能焊接电压为 80V、电容为 6600μF、电极力为 18N 时,可获得综合性能优良的高质量点焊接头.

Abstract：

The 0Cr18Ni9 austenitic stainless steel sheet with 0.2 mm thickness was welded in capacitor discharge spot welding.The temperature field and cooling rate of nugget was calculated. The results show that the joint microstructure consists of nugget zone and semi-melt zone. Due to very short time in welding, the cooling rate of the joint reaches to 5.1×106 K/s, the growth of austenite microstructure is impeded, and the microstructure of the nugget is refined,which has rapidly solidified characteristics. As the austenite microstructure of the nugget stays in temperature province of activation with very short time, the chrome of austenite grain boundary precipitations is checked. To obtain the high quality spot-weld joint, the welding parameters are determined as: welding voltage 80 V, capacitor 6 600μF and electrode pressure 18 N.     

1Cr18Ni9Ti不锈钢超窄间隙焊接接头组织与性能分析

采用超细颗粒焊剂约束电弧超窄间隙焊接方法进行了1Cr18Ni9Ti奥氏体不锈钢的超窄间隙焊接试验,并对所得超窄间隙焊接接头的组织及性能进行了测试和分析。结果表明,1Cr18Ni9Ti奥氏体不锈钢超窄间隙焊接接头的根焊焊缝区晶粒为等轴晶,而填充焊和盖面焊的焊缝区晶粒则为粗大的柱状晶。等轴晶和柱状晶的基体均为奥氏体,晶粒内部均分布有少量板条状铁素体。超窄间隙焊接接头的填充焊缝和根焊焊缝具有与母材相当的硬度,而盖面焊缝的硬度则略低于母材。超窄间隙焊接接头除了收缩率和冲击功比母材的略低外,抗拉强度、屈服强度及伸长率明显高于母材所对应性能的最低值。此外,试验还测得超窄间隙焊接接头的腐蚀速率为0.417 g/(m2·h),该值明显低于母材的腐蚀速率。