Study on the rapid synthesis of LiNi1−xCoxO2 cathode material for lithium secondary battery

LiNi_1−xCo_xO₂ (x = 0, 0.1, 0.2) cathode materials were successfully synthesized by a rheological phase reaction method with calcination time of 0.5 h at 800 °C. All obtained powders are pure phase with α-NaFeO₂ structure (R-3m space group). The samples deliver an initial discharge capacity of 182, 199 and 189 mAh g⁻¹ (25 mA g⁻¹, 4.35-3.0 V), respectively. The reaction mechanism was also discussed, which consists of a series of defect reactions. As a result of these defect reactions, the reaction of forming LiNi_1−xCo_xO₂ takes place in high speed.     

Comparison of AlPO4- and Co3(PO4)2-coated LiNi0.8Co0.2O2 cathode materials for Li-ion battery

Electrochemical and thermal properties of Co₃(PO₄)₂- and AlPO₄-coated LiNi_0.8Co_0.2O₂ cathode materials were compared. AlPO₄-coated LiNi_0.8Co_0.2O₂ cathodes exhibited an original specific capacity of 170.8 mAh g⁻¹ and had a capacity retention (89.1% of its initial capacity) between 4.35 and 3.0 V after 60 cycles at 150 mA g⁻¹. Co₃(PO₄)₂-coated LiNi_0.8Co_0.2O₂ cathodes exhibited an original specific capacity of 177.6 mAh g⁻¹ and excellent capacity retention (91.8% of its initial capacity), which was attributed to a lithium-reactive Co₃(PO₄)₂ coating. The Co₃(PO₄)₂ coating material could react with LiOH and Li₂CO₃ impurities during annealing to form an olivine Li_xCoPO₄ phase on the bulk surface, which minimized any side reactions with electrolytes and the dissolution of Ni⁴⁺ ions compared to the AlPO₄-coated cathode. Differential scanning calorimetry results showed Co₃(PO₄)₂-coated LiNi_0.8Co_0.2O₂ cathode material had a much improved onset temperature of the oxygen evolution of about 218 °C, and a much lower amount of exothermic-heat release compared to the AlPO₄-coated sample.     

LiNi0.1Mn0.1Co0.8O2 electrode material: Structural changes upon lithium electrochemical extraction

We reported here on the synthesis, the crystal structure and the study of the structural changes during the electrochemical cycling of layered LiNi_0.1Mn_0.1Co_0.8O₂ positive electrode material. Rietveld refinement analysis shows that this material exhibits almost an ideal α-NaFeO₂ structure with practically no lithium-nickel disorder. The SQUID measurements confirm this structural result and evidenced that this material consists of Ni²⁺, Mn⁴⁺ and Co³⁺ ions.Unlike LiNiO₂ and LiCoO₂ conventional electrode materials, there was no structural modification upon lithium removal in the whole 0.42 ≤ x ≤1.0 studied composition range. The peaks revealed in the incremental capacity curve were attributed to the successive oxidation of Ni²⁺ and Co³⁺ while Mn⁴⁺ remains electrochemically inactive.     

Synthesis of LiNi1/3Co1/3Mn1/3O2 cathode materials by using a supercritical water method in a batch reactor

LiNi_1/3Co_1/3Mn_1/3O₂ and LiCoO₂ cathode materials were synthesized by using a supercritical water (SCW) method with a metal salt solution in a batch reactor. Stoichiometric LiNi_1/3Co_1/3Mn_1/3O₂ was successfully synthesized in a 10-min reaction without calcination, while overlithiated LiCoO₂ (Li_1.15CoO₂) was synthesized using the batch SCW method. The physical properties and electrochemical performances of LiNi_1/3Co_1/3Mn_1/3O₂ were compared to those of Li_1.15CoO₂ by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), and charge/discharge cycling tests. The XRD pattern of LiNi_1/3Co_1/3Mn_1/3O₂ was found to be similar to that of Li_1.15CoO₂, showing clear splitting of the (0 0 6)/(1 0 2) and (1 0 8)/(1 1 0) peak pairs as particular characteristics of the layered structure. In addition, both cathode powders showed good crystallinity and phase purity, even though a short reaction time without calcination was applied to the SCW method. The initial specific discharge capacities of the Li_1.15CoO₂ and LiNi_1/3Co_1/3Mn_1/3O₂ powders at a current density of 0.24 mA/cm² in 2.5-4.5 V were 149 and 180 mAh/g, and their irreversible capacity loss was 20 and 17 mAh/g, respectively. The discharge capacities of the Li_1.15CoO₂ and LiNi_1/3Co_1/3Mn_1/3O₂ powders decreased with cycling and remained at 108 and 154 mAh/g after 30 cycles, which are 79% and 89% of the initial capacities. Compared to the overlithiated LiCoO₂ cathode powders, the LiNi_1/3Co_1/3Mn_1/3O₂ cathode powders synthesized by SCW method had better electrochemical performances.     

A delithiated LiNi0.65Co0.25Mn0.10O2 electrode material: A structural, magnetic and electrochemical study

A crystalline LiNi_0.65Co_0.25Mn_0.10O₂ electrode material was synthesized by the combustion method at 900 °C for 1 h. Rietveld refinement shows less than 3% of Li/Ni disorder in the structure. Lithium extraction involves only the Ni²⁺/Ni⁴⁺ redox couple while Co³⁺ and Mn⁴⁺ remain electrochemically inactive. No structural transition was detected during cycling in the whole composition range 0 < x < 1.0. Furthermore, the hexagonal cell volume changes by only 3% when all lithium was removed indicating a good mechanical stability of the studied compound. LiNi_0.65Co_0.25Mn_0.10O₂ has a discharge capacity of 150 mAh/g in the voltage range 2.5-4.5 V, but the best electrochemical performance was obtained with an upper cut-off potential of 4.3 V. Magnetic measurements reveal competing antiferromagnetic and ferromagnetic interactions - varying in strength as a function of lithium content - yielding a low temperature magnetically frustrated state. The evolution of the magnetic properties with lithium content confirms the preferential oxidation of Ni ions compared to Co³⁺ and Mn⁴⁺ during the delithiation process.     

Hydrothermal synthesis of LiNixCo1−xO2 cathode materials

Ultrafine powders of LiCoO₂, nonstoichiometric LiNiO₂ and LiNi_0.9Co_0.1O₂ were prepared under mild hydrothermal conditions. The influence of the molar ratio of Li/Co, Li/Ni and Li/(Ni + Co) was studied. The final products were investigated by XRD, TEM and EDS. To synthesize a stoichiometric LiNiO₂ under mild hydrothermal conditions was found to be a big challenge. Transmission electron microscopies (TEM) revealed the formation of well-crystallized LiCoO₂ and LiNi_0.9Co_0.1O₂ with average size of 100 nm and 10 nm, respectively.     

Electrochemical characteristics of cobalt-substituted lithium nickel oxides synthesized from lithium hydro-oxide and nickel and cobalt oxides

LiNi_1−yCo_yO₂ (y=0.1, 0.3 and 0.5) were synthesized by solid state reaction method at 800 °C and 850 °C from LiOH·H₂O, NiO and Co₃O₄ as starting materials. The electrochemical properties of the synthesized LiNi_1−yCo_yO₂ were investigated. As the content of Co decreases, particle size decreases rapidly and particle size distribution gets more homogeneous. When the particle size is compared at the same composition, the particles synthesized at 850 °C are larger than those synthesized at 800 °C. LiNi_0.7Co_0.3O₂ synthesized at 850 °C has the largest intercalated and deintercalated Li quantity Δx among LiNi_1−yCo_yO₂ (y=0.1, 0.3 and 0.5). LiNi_0.7Co_0.3O₂ synthesized at 850 °C has the largest first discharge capacity (178 mAh/g), followed by LiNi_0.7Co_0.3O₂ (162 mAh/g) synthesized at 800 °C. LiNi_0.7Co_0.3O₂ synthesized at 800 °C has discharge capacities of 162 and 125 mAh/g at n=1 and n=5, respectively.     

Hydrothermal synthesis of LiNi0.9Co0.1O2 cathode materials

Ultrafine powders of LiNi_0.9Co_0.1O₂ were prepared under mild hydrothermal conditions. The product was characterized by XRD, TEM and EDS tests, which indicated that the obtained products were pure and well-crystallized LiNi_0.9Co_0.1O₂. The ICP-AES results indicated the products were lithium-deficient compounds. The addition of KOH hardly effected the crystallinity of the product but gave larger crystals.     

Electrochemical and thermal studies of Li[NixLi(1/3−2x/3)Mn(2/3−x/3)]O2 (x = 1/12, 1/4, 5/12, and 1/2)

Samples of the layered cathode materials, Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ (x = 1/12, 1/4, 5/12, and 1/2), were synthesized at 900 °C. Electrodes of these samples were charged in Li-ion coin cells to remove lithium. The charged electrode materials were rinsed to remove the electrolyte salt and then added, along with EC/DEC solvent or 1 M LiPF₆ EC/DEC, to stainless steel accelerating rate calorimetry (ARC) sample holders that were then welded closed. The reactivity of the samples with electrolyte was probed at two states of charge. First, for samples charged to near 4.45 V and second, for samples charged to 4.8 V, corresponding to removal of all mobile lithium from the samples and also concomitant release of oxygen in a plateau near 4.5 V. Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ samples with x = 1/4, 5/12 and 1/2 charged to 4.45 V do not react appreciably till 190 °C in EC/DEC. Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ samples charged to 4.8 V versus Li, across the oxygen release plateau, start to significantly react with EC/DEC at about 130 °C. However, their high reactivity is similar to that of Li_0.5CoO₂ (4.2 V) with 1 μm particle size. Therefore, Li[Ni_xLi_(1/3−2x/3)Mn_(2/3−x/3)]O₂ samples showing specific capacity of up to 225 mAh/g may be acceptable for replacing LiCoO₂ (145 mAh/g to 4.2 V) from a safety point of view, if their particle size is increased.     

A study on electrochemical characteristics of LiCoO2/LiNi1/3Mn1/3Co1/3O2 mixed cathode for Li secondary battery

In this study, the LiCoO₂/LiNi_1/3Mn_1/3Co_1/3O₂ mixed cathode electrodes were prepared and their electrochemical performances were measured in a high cut-off voltage. As the contents of LiNi_1/3Mn_1/3Co_1/3O₂ in the mixed cathode increases, the reversible specific capacity and cycleability of the electrode enhanced, but the rate capability deteriorated. On the contrary, the rate capability of the cathode enhanced but the reversible specific capacity and cycleability deteriorated, according to increasing the contents of LiCoO₂ in the mixed cathode. The cell of LiCoO₂/LiNi_1/3Mn_1/3Co_1/3O₂ (50:50, wt.%) mixed cathode delivers a discharge capacity of ca. 168 mAh/g at a 0.2 C rate. The capacity of the cell decreased with the current rate and a useful capacity of ca. 152 mAh/g was obtained at a 2.0 C rate. However, the cell shows very stable cycleability: the discharge capacity of the cell after 20th charge/discharge cycling maintains ca. 163 mAh/g.     

Spray-drying synthesized LiNi0.6Co0.2Mn0.2O2 and its electrochemical performance as cathode materials for lithium ion batteries

Layered LiNi_0.6Co_0.2Mn_0.2O₂ materials were synthesized at different sintering temperatures using spray-drying precursor with molar ratio of Li/Me = 1.04 (Me = transition metals). The influences of sintering temperature on crystal structure, morphology and electrochemical performance of LiNi_0.6Co_0.2Mn_0.2O₂ materials have been characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and charge-discharge test. As a result, material synthesized at 850 °C has excellent electrochemical performance, delivering an initial discharge capacity of 173.1 mAh g^− 1 between 2.8 and 4.3 V at a current density of 16 mA g^− 1 and exhibiting good cycling performance.     

Effect of synthesis condition on the structural and electrochemical properties of Li[Ni1/3Mn1/3Co1/3]O2 prepared by the metal acetates decomposition method

In order to get homogeneous layered oxide Li[Ni_1/3Mn_1/3Co_1/3]O₂ as a lithium insertion positive electrode material, we applied the metal acetates decomposition method. The oxide compounds were calcined at various temperatures, which results in greater difference in morphological (shape, particle size and specific surface area) and the electrochemical (first charge profile, reversible capacity and rate capability) differences. The Li[Ni_1/3Mn_1/3Co_1/3]O₂ powders were characterized by means of X-ray diffraction (XRD), charge/discharge cycling, cyclic voltammetry and SEM. XRD experiment revealed that the layered Li[Ni_1/3Mn_1/3Co_1/3]O₂ material can be best synthesized at temperature of 800 °C. In that synthesized temperature, the sample showed high discharge capacity of 190 mAh g⁻¹ as well as stable cycling performance at a current density of 0.2 mA cm⁻² in the voltage range 2.3-4.6 V. The reversible capacity after 100 cycles is more than 190 mAh g⁻¹ at room temperature.     

Preparation and characterization of ramsdellite Li2Ti3O7 as an anode material for asymmetric supercapacitors

Ramsdellite Li₂Ti₃O₇ was first synthesized via sol-gel process with good crystallity of an average particle size of 0.175 μm. The product was thoroughly investigated as a lithium intercalation compound, and as an active anode material in asymmetric supercapacitors coupling with activated carbon as cathode. Lithium intercalation reactions were found occurring at 1.32 and 1.62 V versus Li/Li⁺, respectively. A reversible specific capacity of 150 mA h g⁻¹ at 1C was obtained on Li₂Ti₃O₇ electrode in a nonaqueous electrolyte. The charge current was found to strongly influence the anodic discharge capacity in the asymmetric cell. The capacity retention at 10C charge-discharge rate was found to be 75.9% in comparison with that at 1C.     

Structural and electrochemical behaviors of metastable Li2/3[Ni1/3Mn2/3]O2 modified by metal element substitution

Layered metastable lithium manganese oxides, Li_2/3[Ni_1/3−xMn_2/3−yM_x+y]O₂ (x = y = 1/36 for M = Al, Co, and Fe and x = 2/36, y = 0 for M = Mg) were prepared by the ion exchange of Li for Na in P2-Na_2/3[Ni_1/3−xMn_2/3−yM_x+y]O₂ precursors. The Al and Co doping produced the T^#2 structure with the space group Cmca. On the other hand, the Fe and Mg doped samples had the O6 structure with space group R-3m. Electron diffraction revealed the 1:2 type ordering within the Ni_1/3−xMn_2/3−yM_x+yO₂ slab. It was found that the stacking sequence and electrochemical performance of the Li cells containing T^#2-Li_2/3[Ni_1/3Mn_2/3]O₂ were affected by the doping with small amounts of Al, Co, Fe, and Mg. The discharge capacity of the Al doped sample was around 200 mAh g⁻¹ in the voltage range between 2.0 and 4.7 V at the current density of 14.4 mA g⁻¹ along with a good capacity retention. Moreover, for the Al and Co doped and undoped oxides, the irreversible phase transition of the T^#2 into the O2 structure was observed during the initial lithium deintercalation.     

Zr-doped Li[Ni0.5−xMn0.5−xZr2x]O2 (x = 0, 0.025) as cathode material for lithium ion batteries

Layered Li[Ni_0.5−xMn_0.5−xZr_2x]O₂ (x = 0, 0.025) have been prepared by the mixed hydroxide and molten-salt synthesis method. The individual particles of synthesized materials have a sub-microsize range of 200-500 nm, and LiNi_0.475Mn_0.475Zr_0.05O₂ has a rougher surface than that of LiNi_0.5Mn_0.5O₂. The Li/Li[Ni_0.5−xMn_0.5−xZr_2x]O₂ (x = 0, 0.025) electrodes were cycled between 4.5 and 2.0 V at a current density of 15 mA/g, the discharge capacity of both cells increased during the first ten cycles. The discharge capacity of the Li/LiNi_0.475Mn_0.475Zr_0.05O₂ cell increased from 150 to 220 mAh/g, which is 50 mAh/g larger than that of the Li/LiNi_0.5Mn_0.5O₂ cell. We found that the oxidation of oxygen and the Mn³⁺ ion concerned this phenomenon from the cyclic voltammetry (CV). Thermal stability of the charged Li[Ni_0.5−xMn_0.5−xZr_2x]O₂ (x = 0, 0.025) cathode was improved by Zr doping.     

Effects of surface modification on the cycling stability of LiNi0.8Co0.2O2 electrodes by CeO2 coating

A high-performance LiNi_0.8Co_0.2O₂ cathode was successfully fabricated by a sol-gel coating of CeO₂ to the surface of the LiNi_0.8Co_0.2O₂ powder and subsequent heat treatment at 700 °C for 5 h. The surface-modified and pristine LiNi_0.8Co_0.2O₂ powders were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), slow rate cyclic voltammogram (CV), and differential scanning calorimetry (DSC). Unlike pristine LiNi_0.8Co_0.2O₂, the CeO₂-coated LiNi_0.8Co_0.2O₂ cathode exhibits no decrease in its original specific capacity of 182 mAh/g (versus lithium metal) and excellent capacity retention (95% of its initial capacity) between 4.5 and 2.8 V after 55 cycles. The results indicate that the surface treatment should be an effective way to improve the comprehensive properties of the cathode materials for lithium ion batteries.     

Improved electrochemical properties of Li1+x(Ni0.3Co0.4Mn0.3)O2−δ (x = 0, 0.03 and 0.06) with lithium excess composition prepared by a spray drying method

Layered Li_1+x(Ni_0.3Co_0.4Mn_0.3)O_2−δ (x = 0, 0.03 and 0.06) materials were synthesized through the different calcination times using the spray-dried precursor with the molar ratio of Li/Me = 1.25 (Me = transition metals). The physical and electrochemical properties of the lithium excess and the stoichiometric materials were examined using XRD, AAS, BET and galvanostatic electrochemical method. As results, the lithium excess Li_1.06(Ni_0.3Co_0.4Mn_0.3)O_2−δ could show better electrochemical properties, such as discharge capacity, capacity retention and C rate ability, than those of the stoichiometric Li_1.00(Ni_0.3Co_0.4Mn_0.3)O_2−δ. In this paper, the effect of excess lithium on the electrochemical properties of Li_1+x(Ni_0.3Co_0.4Mn_0.3)O_2−δ materials will be discussed based on the experimental results of ex situ X-ray diffraction, transmission electron microscopy (TEM) and galvanostatic intermittent titration technique (GITT)     

The first cycle characteristics of Li[Ni1/3Co1/3Mn1/3]O2 charged up to 4.7 V

In this research, we studied the first cycle characteristics of Li[Ni_1/3Co_1/3Mn_1/3]O₂ charged up to 4.7 V. Properties, such as valence state of the transition metals and crystallographic features, were analyzed by X-ray absorption spectroscopy and X-ray and neutron diffractions. Especially, two plateaus observed around 3.75 and 4.54 V were investigated by ex situ X-ray absorption spectroscopy. XANES studies showed that the oxidation states of transition metals in Li[Ni_1/3Co_1/3Mn_1/3]O₂ are mostly Ni²⁺, Co³⁺ and Mn⁴⁺. Based on neutron diffraction Rietveld analysis, there is about 6% of all nickel divalent (Ni²⁺) ions mixed with lithium ions (cation mixing). Meanwhile, it was found that the oxidation reaction of Ni²⁺/Ni⁴⁺ is related to the lower plateau around 3.75 V, but that of Co³⁺/Co⁴⁺ seems to occur entire range of x in Li_1−x[Ni_1/3Co_1/3Mn_1/3]O₂. Small volume change during cycling was attributed to the opposite variation of lattice parameter “c” and “a” with charging-discharging.