[目的]研究壳聚糖微球的制备以及其对动物皮内的刺激影响,为壳聚糖微球进一步临床应用提供依据.[方法]以壳聚糖(CS)为原料,通过乳化交联法制备CS微球,显微镜观察壳聚糖微球微观形态,研究微球理化特性受壳聚糖脱乙酰度、壳聚糖醋酸溶液浓度、交联剂用量等工艺条件影响,并将壳聚糖微球进行兔子皮内刺激试验.[结果]优化得出壳聚糖微球制备工艺为壳聚糖醋酸质量浓度0.3g/L,Span80为油相体积的8%,油水相体积比3:1,交联时间1 h.该壳聚糖微球不会对兔子产生损害.[结论]壳聚糖微球符合医疗器械生物学评价要求,为壳聚糖微球进一步临床应用奠定了基础.     

玉米交联淀粉的制备研究

[目的]探讨甲醛用量、pH值、反应温度、反应时间对玉米交联淀粉交联度(即沉降积)的影响.[方法]以玉米淀粉为原料,甲醛为交联剂,制备玉米交联淀粉.[结果]确定最佳工艺条件为:甲醛与淀粉的质量比为0.020、反应时间为1 h、反应pH值为9.0、反应温度为42.5 ℃,所制备的交联淀粉沉降积为2.7 ml.[结论]该试验筛选出了制备玉米交联淀粉的最佳工艺条件,该法具有工艺简单、快速、高效等特点.     

氧化淀粉的制备

[目的]对影响氧化淀粉羧基含量的各个因素进行系统考察.[方法]以马铃薯淀粉为原料,次氯酸钠作氧化剂制备氧化淀粉.并对最佳工艺条件下制备的最终产品的羟基含量、白度、透明度及黏度进行测定.[结果]制备马铃薯淀粉的最佳工艺条件为:pH值为8.0,温度为40 ℃,次氯酸钠用量(有效氯用量)为2%,反应时间为8 h.[结论]试验得到的氧化淀粉具有羧基含量低,白度较好,透明度较高,黏度较低的特点.     

牛白蛋白包裹复合磁性微球的制备及性能表征

[目的]研究制备的牛白蛋白包裹复合磁性微球的性能.[方法]在反相(W/O)微乳液体系中制备出Fe3O4/PAM(聚丙烯酰胺)磁性微球;然后在蛋白质的磷酸氢二钠-柠檬酸缓冲溶液中,以戊二醛为交联剂,加入Fe3O4/PAM微球,使蛋白质特异性吸附在微球上.采用电子衍射、透射电镜、差热、热重等方法对复合微球的粒径、结构等性质进行了表征与分析;并考察了温度、溶液离子强度对微球吸附蛋白量的影响.[结果]微球粒径20 nm左右,且粒径均匀、细小,微球具有较大吸附量;反应温度在37℃时,微球对蛋白的吸附达到最大值,离子强度越小越有利于微球对蛋白的吸附.[结论]该研究可为进一步制备高磁响应性、高吸附量的靶向药物奠定基础.     

替米考星β-环糊精聚合物微球的制备与表征

[目的]优化替米考星β-环糊精聚合物(β-CDP)微球的制备工艺.[方法]采用共沉淀法制备替米考星β-CDP微球,以包封率和产率的回归分析综合得分为指标,通过L9(34)正交试验设计对制备工艺进行优化;采用扫描电镜、激光粒度分布仪、红外光谱仪和综合热分析仪对替米考星β-CDP微球进行表征.[结果]最佳工艺条件为:β-CDP微球3 g、替米考星 0.25 g、反应温度50 ℃、反应时间1 h、搅拌速度600 r/min;在最佳工艺条件下:产率为83.32%,包封率为67.61%.以优化工艺制备的载药微球形态良好,平均粒径为 161.35 μm;替米考星进入到β-CDP微球中的内部,且以无定形的状态分散在聚合物载体中,具有较好的热稳定性.[结论]替米考星β-CDP微球制备方法合理可行.     

洛伐他汀聚乳酸缓释微球的制备及其体外释药

采用油/水型乳化溶剂挥发法制备了洛伐他汀聚乳酸缓释微球,通过正交试验筛选最优制备工艺;考察了微球的粒径,形态,及载药量、包封率等特征,采用透析法进行微球体外释药研究.结果表明由最佳工艺制备的洛伐他汀聚乳酸微球形态圆整,粒径分布较为均匀.分子量5万聚乳酸制备的微球,载药量32.28%,包封率81.81%,平均粒径65.8μm;分子量3万聚乳酸制备的微球,载药量27.66%,包封率60.84%,平均粒径63.3μm.二者在10d内体外累积释放率分别为34.81%和40.96%,释药动力学符合Higuchi方程.     

壳聚糖/明胶复合微球的制备

采用乳化-凝聚法,在油包水(W/O)体系中制备壳聚糖/明胶(Cs/Gel)复合微球,研究乳化剂用量、搅拌速率和水油比等因素对微球粒径以及脱水过程中的丙酮浓度对Cs/Gel复合微球形貌的影响.研究结果表明:乳化剂浓度较低时,微球的粒径随乳化剂浓度的增加呈降低趋势,当乳化剂浓度高于0.012 g·mL-1时微球粒径不再发生...     

玉米淀粉基缓释膜的制备及表征

[目的]研究玉米淀粉基缓释膜的制备条件及特征.[方法]以玉米淀粉与聚乙烯醇为原料,在交联剂的作用下,制得包膜料液,用此料液给尿素涂膜,制得包膜尿素.通过红外光谱时膜的结构进行表征和分析,研究改性淀粉膜的形成条件和影响因素.[结果]制备玉米淀粉基缓释膜的最佳反应条件是淀粉和PVA的质量比为1:1,PVA的含量为15%,吐温0.2 ml,尿素0.5 g,丙三醇1.5 g,甲醛2ml,硼砂0.2 g,引发剂用量0.5%,反应30 min,反应温度控制在80℃.[结论]制备得到的包膜材料具有成本低、可生物降解、无环境污染等特点.     

啶虫脒/羧甲基壳聚糖缓释微球性能研究

[目的]探索啶虫脒/羧甲基壳聚糖缓释微球的最佳制备条件.[方法]以啶虫脒为囊心药物,以羧甲基壳聚糖-阿拉伯胶-明胶作为载体材料,采用锐孔法制备啶虫脒缓释凝胶微球,以包封率为参考指标,通过正交试验探究啶虫脒缓释微球的最佳制备条件,并探讨壳聚糖缓释微球对啶虫脒的缓释性能.[结果]啶虫脒缓释微球的最佳制备条件为:25 g/L羧甲基壳聚糖、羧甲基壳聚糖-啶虫脒的浓度比为2:1、1.5%氯化钙、戊二醛浓度为5%.所制备的啶虫脒/羧甲基壳聚糖-阿拉伯胶-明胶缓释凝胶微球的包封率达48.56%,并具有很好的缓释性能,缓释时间达60 h以上.[结论]制得的羧甲基壳聚糖-阿拉伯胶-明胶微球对啶虫脒有控制释放的作用.     

新型环保木薯淀粉改性聚氨酯硬质泡沫塑料的制备及性能研究

[目的]以木薯淀粉和蔗糖为起始原料制备淀粉改性聚氨酯泡沫塑料,研究反应条件对产品性能的影响.[方法]用FT-IR、SEM、DSC和TG分析产品的结构及热稳定性,通过土埋试验考察产品的降解性能.[结果]淀粉在聚氨酯的制备过程中参与交联反应,随着淀粉含量的增加,产品的降解速度有所加快,且降解的程度也越大.[结论]淀粉改性聚氨酯泡沫具有良好的热稳定性、较低的导热系数和优异的生物降解性能,可以作为环保的保温材料使用.     

UASB Treatment of Tapioca Starch Wastewater

Feasibility of the upflow anaerobic sludge blanket (UASB) process was investigated for the treatment of tapioca starch industry wastewater. After removal of suspended solids by simple gravity settling, starch wastewater was used as a feed. Start-up of a 21.5-L reactor with diluted feed of approximately 3,000 mg∕L chemical oxygen demand (COD) was accomplished in about 6 weeks using seed sludge from an anaerobic pond treating tapioca starch wastewater. By the end of the start-up period, gas productivity of 4–5 m3/m3r?day was obtained. Undiluted supernatant wastewater with a COD concentration of 12,000–24,000 mg∕L was fed during steady-state reactor operation at an organic loading rate of 10–16 kg COD/m3r?day. The upflow velocity was maintained at 0.5 m∕h with a recirculation ratio of 4:1. COD conversion efficiencies >95% and gas productivity of 5–8 m3/m3r?day were obtained. These results indicated that removal of starch solids from wastewater by simple gravity settling was sufficient to obtain satisfactory performance of the UASB process.     

马铃薯氧化淀粉胶粘剂制备研究

[目的]研究制备马铃薯氧化淀粉胶粘剂最合适的氧化剂.[方法]选用马铃薯淀粉为原料,以高锰酸钾、双氧水、次氯酸钠为氧化剂,先对马铃薯淀粉进行氧化,然后制备马铃薯氧化淀粉胶粘剂.对不同氧化剂制备的马铃薯氧化淀粉的羰基含量、羧基含量进行测定,并对马铃薯氧化淀粉胶粘剂的粘度、失水率、初粘性、流动性、贮存期等性能进行测试.[结果]在相同条件下,用双氧水制备的马铃薯淀粉胶粘剂的各个性能都明显优于其他氧化剂制备的胶粘荆.[结论]双氧水是制备马铃薯氧化淀粉胶粘剂最合适的氧化剂.     

Starch granulomas after transurethral resection of bladder tumors

Cerebrovascular reactivity to CO2 inhalation and voluntary hyperventilation was studied in seven normotensive subjects and nine hypertensive patients without clinical or angiographical signs of arteriosclerosis. Cerebral blood flow (CBF) was measured by the intracarotid 133Xe clearance method and calculated as the initial slope index. Three to five CBF measurements were made in each patient in the PaCO2 range of 20 to 55 mm Hg. No difference was observed in reactivity between hypertensive and normotensive patients, either during CO2 inhalation or during hyperventilation. The shape of the CBF:PaCO2 curve suggested a decrease in reactivity below a PaCO2 of 30 to 35 mm Hg in both groups. Above a PaCO2 of 35 mm Hg, exponential regression analysis yielded a mean reactivity of 6 +/- 2%, whereas below a PaCO2 of 30 mm Hg it was about 2%. The rise in CBF during CO2 inhalation was not influenced by the intravenous infusion of a small dose of trimethaphan which blocked the concomitant rise in blood pressure.     

木薯淀粉补强天然胶乳的研究

[目的]研究木薯淀粉用于补强天然胶乳的可行性.[方法]将木薯淀粉糊化后加入天然胶乳中,对天然胶乳进行补强,考察淀粉用量及偶联剂KH-551用量对天然胶乳胶体性质及硫化胶膜物理机械性能的影响.[结果]经KH-551处理后的木薯淀粉对天然胶乳有明显的补强作用,天然胶乳硫化胶膜的物理机械性能得到显著提高,同时对天然胶乳的胶体性质影响不大.[结论]采用廉价的木薯淀粉进行天然胶乳的补强,为该工艺的广泛应用奠定了基础.     

Waxy蛋白缺失对小麦淀粉性状的影响

综述了国内外关于Waxy蛋白缺失对小麦淀粉性状影响的研究进展.在普通小麦中存在3个Waxy蛋白亚基,它们的缺失会对小麦籽粒中直链淀粉的含量产生重要影响,使小麦淀粉的理化特性发生显著变化,进而影响到小麦面粉的加工品质.同时,对糯小麦的潜在应用价值进行了探讨.     

淀粉塑化改性的机理及研究进展

综述了淀粉塑化改性的主要方法和研究进展,并对改性方法进行分析,展望了淀粉塑化改性的发展趋势.     

淀粉接枝丙烯酸超强吸水剂研究

本文采用正交实验讨论了淀粉接枝丙烯酸合成树脂过程中,引发剂、交联剂、丙烯酸的中和度、单体的用量等因素的影响,同时讨论了产品的耐盐性和受热保水性。     

淀粉废水资源化工程改造技术

针对河北省某玉米淀粉生产企业产生的玉米浸泡废水,研究了采用离子交换法从玉米浸泡水中提取菲叮,使玉米浸泡水回用率达到100%。在原污水处理工艺基础上增加絮凝沉淀和气浮工序,可大大减少污染物,使处理后污水水质达到《污水综合排放标准》(GB8978—1996)—级排放标准。