输电杆塔用复合材料性能研究——树脂体系对复合材料性能的影响

针对电力电网行业对输电杆塔用复合材料的性能要求,开展了两种聚氨酯树脂(聚氨酯改性乙烯基树脂,VPU;双组份聚氨酯,TPU)制备的复合材料的多项性能研究,并与高性能环氧树脂(EP)复合材料进行了性能对比(采用拉挤成型方式制备)。性能评估包括力学性能、电气绝缘性能、耐腐蚀及老化性能以及表面性能等。研究测试结果表明,EP复合材料具有最优的力学、电气性能,但在耐紫外老化和耐烧蚀方面较差,不适合直接作为户外用绝缘材料;而VPU复合材料具有较好的绝缘、防腐、耐老化性能,同时其表面疏水性最好,但其横向性能有待完善;TPU复合材料的综合性能相对较好,是制备输、配电杆塔或横担的理想材料。     

SCRIMP用原位分相增韧中温环氧树脂体系制备及复合材料性能

针对复合材料真空辅助树脂浸渍模塑技术(SCRIMP)对树脂体系要求进行配方设计及性能测试。采用动态差示扫描量热(DSC)法,运用Kissinger动力学方程研究了基础树脂的固化反应动力学。通过添加QS-VA-3型原位分相型增韧剂,改善了基础树脂脆性,依据力学性能测试结果确定最佳添加量。对增韧环氧树脂体系进行等温/非等温黏度特性研究,确定了SCRIM P灌注成型过程的适用期,并使用该技术成型了增韧环氧树脂体系/单向玻璃纤维布复合材料试样,发现与玻璃纤维复合后具有强度高、界面性能好及低电压绝缘性能良好特点,但牺牲了高电压环境下绝缘性能。     

聚砜改性环氧树脂复合材料热老化性能研究

以聚砜(PSF)改性环氧树脂(EP)为基体树脂,玻璃纤维为增强材料,采用高温模压成型法制备出PSF改性EP/玻璃纤维复合材料。结果表明:PSF能有效提高EP基体的热稳定性能;经200℃热老化72 h后,PSF改性EP/玻璃纤维复合材料的热失重率<1%,其冲击强度和弯曲强度呈先升后降态势,电绝缘性能仍然较好(其体积电阻率和表面电阻率的数量级仍保持在1012左右);该复合材料在高温绝缘场合中具有良好的应用前景。     

POSS改性邻苯二甲腈树脂制备及性能

为探究不同结构笼型聚倍半硅氧烷(POSS)对邻苯二甲腈(PN)树脂综合性能的影响，以PN树脂为基体，分别添加了三硅烷醇苯基POSS、氨基丙基异丁基POSS、缩水甘油基异丁基POSS、三硅醇异丁基POSS及环氧环己基异丁基POSS 5种POSS，利用溶液共混法制备了改性PN浇铸体试样，并制备了PN/石英布复合材料。开展了热重分析、动态热机械分析、透波率测试、介电性能测试等多种试验，研究了不同结构POSS对PN树脂热稳定性以及复合材料透波性能和介电性能的影响。结果表明，POSS的引入提升了PN树脂的耐热性能及热分解起始温度，同时，POSS的引入提高了PN树脂的玻璃化转变温度，提高了材料的可用温度范围，也提升了PN复合材料在12～18 GHz及26.5～40GHz两个波段下的透波性能。除环氧环己基异丁基POSS使PN复合材料的介电损耗有所增大外，其余4种POSS对复合材料的介电性能影响较小。综合分析5种改性后的试样表明，使用三硅醇异丁基POSS改性的PN树脂及复合材料具有最优的综合性能。该改性PN复合材料在12～18 GHZ频率下的平均透波率可达74.21%，在26.5～40 GHz频率下的...     

高性能芳纶绝缘拉杆用树脂配方及性能研究

本文研究了双酚A、双酚F环氧树脂配方体系基础性能,对比分析了两种树脂配方浇注体的力学性能、电气性能和耐热性能,从试验数据得出双酚F配方体系改善了树脂配方耐热性能,却没有降低树脂工艺性能;并使用显微镜和SEM电镜观察绝缘拉杆复合材料结构,并其进行了各种性能测试。     

金红石型纳米TiO_2改性纳米复合氟碳涂层的制备与性能研究

采用氟硅烷偶联剂改性金红石R型纳米TiO_2,并用作常温固化氟碳树脂FEVE的填料,制备了疏水性金红石型纳米TiO_2改性纳米复合氟碳涂层。以红外光谱(FT-IR)、扫描电镜(SEM)、X射线光电子能谱(XPS)等表征了其微观结构,以接触角测量仪测定了其疏水性、计算了其表面能,按国家及电力行业标准测定了其理化与电气性能。结果表明,制备的纳米复合氟碳涂层对水静态接触角为121°,具备良好的疏水性。理化及电气绝缘性能测试结果表明,其体积电阻率为2.5×10~(10)Ω·m,击穿场强为21.1 kV/mm,符合绝缘子国家标准,制备的涂层具有优良的防污闪性能。     

耐（150～500）kV电压绝缘支撑杆复合材料研制

介绍了一种新型耐（150～500）kVg压绝缘支撑杆复合材料的研制情况。这种绝缘支撑杆复合材料的树脂基体具有良好的工艺性能,其力学性能与进口树脂相当．采用合适的成型工艺,制成的复合材料具有优异的电气绝缘性能和力学性能,并能取代进口产品。     

改性酚醛树脂对石墨电刷性能的影响

采用原位聚合法合成改性酚醛树脂,并用其制作成树脂石墨电刷.测试电刷试样的烧结收缩率、电阻率、肖氏硬度等性能,研究酚醛树脂改性对电刷性能的影响.结果表明:硼改性酚醛树脂中的B会吸收树脂热分解产生的氧,形成的B2O3能促进制品的烧结,产生收缩,获得密度较高、硬度较大的电刷制品.邻甲酚醛环氧树脂和环氧氯丙烷热分解时会产生比普通酚醛树脂更多的小分子气体,导致试样膨胀更大,甚至开裂,烧结后密度、硬度提高较小;硼酸的加入量对试样的电阻率影响较小,随硼酸含量的增加密度先增加后减小,当硼/酚比为0.35时,密度达到了最大.     

铁道车辆抗侧滚扭杆用耐磨绝缘涂料的研究

以聚酰胺酰亚胺（PAI）树脂为基料,制得了一种铁道车辆抗侧滚扭杆用耐磨绝缘涂料,研究了不同树脂基料对绝缘涂层的电气绝缘性能和耐磨性能的影响,并使用SEM、IR、TG对耐磨绝缘涂层进行了性能表征。结果表明：当选用某聚酰胺酰亚胺树脂,采用聚四氟乙烯和二硫化钼润滑剂时,耐磨绝缘涂层的电气强度达到57.2 kV/mm,体积电阻率达到3.2×1014Ω·m,动态摩擦系数低至0.078,经过300万次疲劳试验涂层完好无损。     

改性氰酸酯基复合材料力学和透波性能研究

利用低介电改性剂对氰酸酯树脂进行改性,制备了石英纤维/改性氰酸酯树脂复合材料,利用SEM表征了树脂及其复合材料的断面,并对改性氰酸酯树脂的耐热性能、力学性能、复合材料的力学性能及透波性能进行了研究。结果表明,改性氰酸酯树脂的玻璃化转变温度达到200℃以上,树脂拉伸破坏表现为韧性断裂,拉伸强度、弯曲强度和压缩强度分别在27MPa、69MPa和148MPa以上;改性氰酸酯树脂和纤维的界面结合良好,复合材料的拉伸强度、弯曲强度和压缩强度分别达到447MPa、461MPa和259MPa以上;在0.5~18GHz范围内,介电常数为3.1~3.3,4mm试样的S21小于-1.6d B。     

烧蚀复合材料用酚醛树脂的结构表征及性能

采用FTIR、GPC、DSC及TG等方法对4种烧蚀复合材料用酚醛树脂(钨酚醛树脂(WPR)、硼酚醛树脂(BPR)、高残炭酚醛树脂(HCYPR)、S-157酚醛树脂)固化前的结构、分子质量及其分布、固化历程、热失重特性进行了表征和对比,以便为烧蚀复合材料基体的筛选提供理论依据。研究结果发现,S-157PR的分子质量最小,分布最窄,浸润性最好;4种酚醛树脂的固化峰温依次为HCYPR>BPR>WPR>S-157PR;800℃残炭率依次为BPR>HCYPR>WPR>S-157PR。     

2019~2020年世界塑料工业进展(Ⅰ):通用塑料

收集了2019年7月~2020年6月世界塑料工业的相关资料,介绍了2019~2020年世界塑料工业的发展情况,提供了世界塑料产量、消费量及全球各类树脂的需求量及产能情况。按通用热塑性树脂(聚乙烯、聚丙烯、聚氯乙烯、聚苯乙烯及苯乙烯系共聚物)的顺序,对树脂的产量、消费量、供需状况及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等技术作了详细介绍。     

改性沥青树脂及其复合材料的制备及相关性能

以煤沥青为原料、三聚甲醛为交联剂,在对甲苯磺酸的催化作用下合成了沥青树脂（COPNA树脂）,通过添加酚醛树脂对其进行了改性;分别以沥青树脂和改性树脂为原料,与石墨混合制备了复合材料。考察了酚醛树脂含量对改性树脂的残炭率、甲苯不溶物含量、喹啉不溶物含量、p树脂含量的影响,以及树脂含量对复合材料的电阻率,肖氏硬度的影响;采用FT—IR和H—NMR研究其反应机理;采用TG研究了沥青树脂和改性树脂的热行为。研究表明,酚醛树脂与沥青树脂可以在一定比例范围内进行复配,在加热混合过程中酚醛树脂与沥青树脂发生化学反应,提高了沥青树脂的耐热性。经酚醛树脂改性的沥青树脂具有更高残炭率、更高β树脂含量和更好耐热性。改性后的树脂复合材料具有更高的电阻率、更高的肖氏硬度和更高的耐磨性。     

对苯二甲醛酚醛树脂的制备及其固化动力学研究

基于酚醛树脂原料中甲醛的危害性与不可再生性,使用安全、可再生的对苯二甲醛代替甲醛,合成了一种新型的酚醛树脂——对苯二甲醛酚醛树脂。采用核磁、红外、GPC和流变仪等分析手段对此类树脂的结构与性能进行了表征。为了进一步提高该树脂的热性能,使用二茂铁甲醛对其进行改性。采用Kissinger方程、等转换法及双参数自催化模型对改性前后树脂的固化动力学进行了研究,明确了二茂铁甲醛在树脂固化中的作用机理。最后通过MDSC和TG研究了改性前后树脂固化物的热性能,结果表明：在加入15%的二茂铁甲醛后,改性树脂呈现出优异的热性能,其玻璃化转变温度为319.3℃,起始分解温度为397.7℃,在800℃氮气气氛下质量保持率高达76.07%。     

Micromorphology of resin–dentin interfaces using self-adhesive and conventional resin cements: A confocal laser and scanning electron microscope analysis

Purpose: The aim of this study was to evaluate the resin–dentin morphology created by four dual-cured resin cements. Materials and Methods: Two self-adhesive resin cements (RelyX Unicem, 3 M ESPE and Clearfil SA Luting, Kuraray Med.) and two conventional resin cementing systems (RelyX ARC, 3 M ESPE and Clearfil Esthetic Cement, Kuraray Med.) were evaluated. Occlusal dentin surfaces of 32 extracted human third molars were flattened to expose coronal dentin. Teeth were assigned to 8 groups (n=4), according to resin cement products and microscope analysis (SEM: scanning electron microscope or CLSM: confocal laser scanning microscopy). For CLSM, two different fluorescent dyes, fluorescein isothiocyanate–dextran and rhodamine B, were incorporated into the adhesive system and resin cement, respectively. The resin cements were applied to indirect composite resin disks, which were cemented to dentin surface according to manufacturer's instructions. After 24 h, all restored teeth were vertically sectioned into 1-mm-thick slabs for SEM or CLSM analyses. Results: Scotchbond Multi-Purpose Plus/RelyX ARC cementing system formed a thin hybrid layer and resin tags penetration into the dentin tubules. Clearfil DC Bond/Clearfil Esthetic Cement showed only short resin tags. Neither hybrid layer nor resin tags were detected for self-adhesive resin cements. Conclusion: Representative SEM and CLSM images provided resin–dentin interfaces variability among resin cements studied.     

碱溶性聚丙烯酸酯乳液增韧水溶性酚醛树脂的研究

制备碱溶性聚丙烯酸酯乳液用于增韧水溶性酚醛树脂,研究不同用量的碱溶性聚丙烯酸酯乳液对共混树脂体系性能的影响,通过傅立叶变换红外光谱(FTIR)和扫描电子显微镜(SEM)表征共混树脂体系间的相互作用和树脂断裂面的微观形貌,采用万能试验机测试共混树脂体系的力学性能。结果表明,碱溶性聚丙烯酸酯乳液的添加量在20%以内,聚丙烯酸酯乳液的分子链段能够充分展开,共混树脂体系为完全均相体系。FTIR分析说明,聚丙烯酸酯树脂与酚醛树脂之间形成化学键合作用,SEM微观形貌分析表明,随着聚丙烯酸酯乳液用量的添加,纯酚醛树脂的典型脆性断裂逐渐转变为韧性断裂,起到良好的增韧作用。当酚醛树脂与聚丙烯酸酯乳液的质量比为8∶2时,共混树脂体系的力学性能达到最佳,冲击强度为10.7 k J/m2,拉伸强度达12.3 MPa,压缩强度为21.2 MPa。     

用石油树脂代替古马隆树脂作橡胶软化剂的研究

将等量的石油树脂和古马隆树脂分别配制成橡胶胶料，在同等条件下炼胶、硫化，按照橡胶软化剂的性能采用古马隆树脂胶的分析标准进行检测。经实验数据的对比分析，证实了石油树脂作为橡胶软化剂，完全可以代替古马隆树脂，而且优于古马隆树脂。     

Curing characteristics of epoxy resin systems that include a biphenyl moiety

The curing characteristics of epoxy resin systems that include a biphenyl moiety were investigated according to the change of curing agents. Their curing kinetics mainly depend on the type of hardener. An autocatalytic kinetic reaction occurs in epoxy resin systems with phenol novolac hardener, regardless of the kinds of epoxy resin and the epoxy resin systems using Xylok and DCPDP (dicyclopentadiene‐type phenol resin) curing agents following an nth‐order kinetic mechanism. The kinetic parameters of all epoxy resin systems were reported in terms of a generalized kinetic equation that considered the diffusion term. The fastest reaction conversion rate among the epoxy resin systems with a phenol novolac curing agent was obtained in the EOCN‐C epoxy resin system, and for systems with Xylok and DCPDP hardeners, the highest reaction rate values were obtained in NC‐3000P and EOCN‐C epoxy resin systems, respectively. The system constants in DiBenedetto's equation of each epoxy resin system with different curing agents were obtained, and their curing characteristics can be interpreted by the curing model using a curing agent as a spacer. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 86: 1942–1952, 2002     

The electrodeposition properties of coemulsion-contained quaternary ammonium/tertiary amine salt epoxy–amine adducts and the composition analysis of its electrodeposited film

Two-component electrodepositable coemulsion-contained quaternary ammonium resin Q , as a pigment grinding vehicle, and DGEBA–N-methylethanolamine (MEA) tertiary amine salt resin T , as the principal resin, were obtained and then deposited to form a resinous film on the cathode during electrodeposition. The resin composition of this deposited film was determined by the quantitative analysis of FTIR and it was found different from the resin composition of the original coemulsion. The electrodeposition behaviors of the coemulsion were deeply affected by the quaternary ammonium resin. In addition, the electrodeposition properties of emulsions dispersed by quaternary ammonium resin and tertiary amine salt resin were also studied for comparison. © 1994 John Wiley & Sons, Inc.     

ABS树脂国内市场回顾与展望

ABS树脂是一种综合性能优异的热塑性树脂。本文对2000年-2005年我国ABS树脂国内市场供需状况、消费状况和市场价格进行了回顾,并对2006年-2010年国内ABS市场供需状况和市场竞争情况进行了展望。