Synthesis of nitrogen incorporated diamond-like carbon thin films using microwave surface-wave plasma CVD

Nitrogenated diamond-like (DLC:N) carbon thin films have been deposited by microwave surface wave plasma chemical vapor deposition on silicon and quartz substrates, using argon gas, camphor dissolved in ethyl alcohol composition and nitrogen as plasma source. The deposited DLC:N films were characterized for their chemical, optical, structural and electrical properties through X-ray photoelectron spectroscopy, UV/VIS/NIR spectroscopy, Raman spectroscopy, atomic force microscope and current–voltage characteristics. Optical band gap decreased (2.7 to 2.4 eV) with increasing Ar gas flow rate. The photovoltaic measurements of DLC:N / p-Si structure show that the open-circuit voltage (V_oc) of 168.8 mV and a short-circuit current density (J_sc) of 8.4 μA/cm² under light illumination (AM 1.5 100 mW/cm²). The energy conversion efficiency and fill factor were found to be 3.4 × 10^{− 4}% and 0.238 respectively.     

Characteristics of nitrogen doped diamond-like carbon thin films grown by microwave surface-wave plasma CVD

Nitrogen doped diamond-like carbon (DLC:N) thin films were deposited on p-type silicon (p-Si) and quartz substrates by microwave (MW) surface-wave plasma (SWP) chemical vapor deposition (CVD) at low temperature (< 100 °C). For films deposition, argon (Ar: 200 sccm), acetylene (C₂H₂:10 sccm) and nitrogen (N: 5 sccm) were used as carrier, source and doping gases respectively. DLC:N thin films were deposited at 1000 W microwave power where as gas composition pressures were ranged from 110 Pa to 50 Pa. Analytical methods such as X-ray photoelectron spectroscopy (XPS), UV-visible spectroscopy, FTIR and Raman spectroscopy were employed to investigate the chemical, optical and structural properties of the DLC:N films respectively. The lowest optical gap of the film was found to be 1.6 eV at 50 Pa gas composition pressure.     

Diamond-like carbon thin films by microwave surface-wave plasma CVD aimed for the application of photovoltaic solar cells

The nitrogen doped diamond-like carbon (DLC) thin films were deposited on quartz and silicon substrates by a newly developed microwave surface-wave plasma chemical vapor deposition, aiming the application of the films for photovoltaic solar cells. For film deposition, we used argon as carrier gas, nitrogen as dopant and hydrocarbon source gases, such as camphor (C₁₀H₁₆O) dissolved with ethyl alcohol (C₂H₅OH), methane (CH₄), ethylene (C₂H₄) and acetylene (C₂H₂). The optical and electrical properties of the films were studied using X-ray photoelectron spectroscopy, Nanopics 2100/NPX200 surface profiler, UV/VIS/NIR spectroscopy, atomic force microscope, electrical conductivity and solar simulator measurements. The optical band gap of the films has been lowered from 3.1 to 2.4 eV by nitrogen doping, and from 2.65 to 1.9 eV by experimenting with different hydrocarbon source gases. The nitrogen doped (flow rate: 5 sccm; atomic fraction: 5.16%) film shows semiconducting properties in dark (i.e. 8.1 × 10^{− 4} Ω^{− 1} cm^{− 1}) and under the light illumination (i.e. 9.9 × 10^{− 4} Ω^{− 1} cm^{− 1}). The surface morphology of the both undoped and nitrogen doped films are found to be very smooth (RMS roughness ≤ 0.5 nm). The preliminary investigation on photovoltaic properties of DLC (nitrogen doped)/p-Si structure show that open-circuit voltage of 223 mV and short-circuit current density of 8.3 × 10^{− 3} mA/cm². The power conversion efficiency and fill factor of this structure were found to be 3.6 × 10^{− 4}% and 17.9%, respectively. The use of DLC in photovoltaic solar cells is still in its infancy due to the complicated microstructure of carbon bondings, high defect density, low photoconductivity and difficulties in controlling conduction type. Our research work is in progress to realize cheap, reasonably high efficiency and environmental friendly DLC-based photovoltaic solar cells in the future.     

Optoelectronic properties of nitrogenated amorphous carbon films synthesized by microwave surface wave plasma chemical vapor deposition system

The n-type nitrogen doped amorphous carbon (a-C:N) thin films have been grown by microwave (MW) surface wave plasma (SWP) chemical vapor deposition (CVD) system on silicon, quartz and ITO substrates at different nitrogen flow rates (1 to 4 sccm). The effects of nitrogen doping on chemical, optical, structural and electrical properties were studied through X-ray photoelectron spectroscopy, Nanopics 2100/NPX200 surface profiler, UV/VIS/NIR spectroscopy, Raman spectroscopy and solar simulator measurements. Argon, acetylene and nitrogen are used as plasma sources. Optical band gap decreased and nitrogen atomic concentration (%) increased with increasing nitrogen flow rate as a dopant. The a-C:N/p-Si based device exhibits photovoltaic behavior under illumination (AM 1.5, 100 mW/cm²), with a maximum open-circuit voltage (V_oc), short-circuit current (J_sc) and fill factor of 4.2 mV, 7.4 μA/cm² and 0.25 respectively.     

Iodine doping of amorphous diamond-like carbon films

Amorphous diamond-like carbon (a:DLC) films have been doped by incorporation of iodine during the films deposition. XPS and AES analysis shows the existence of iodine atoms with constant concentration of 0.9% along the iodine doped DLC film (a:I-DLC). The optical and electronic properties of the doped films were studied. Optical measurements in the visible light show that iodine affects the interband absorption of the a:DLC films. Iodine causes decreasing of the optical energy gap, from 1.07 to 0.78 eV and affects the density of states at the conducting band. Like the optical measurements, electrical measurements show that iodine also decreases the activation energy of the films from 0.34 to 0.22 eV. This shows that although both gaps decrease, the optical energy gap remains different from that of electrical gap, also after doping.     

Preparation of diamond like carbon thin films above room temperature and their properties

Diamond like carbon (DLC) thin films were deposited on p-type silicon (p-Si), quartz and ITO substrates by microwave (MW) surface-wave plasma (SWP) chemical vapor deposition (CVD) at different substrate temperatures (RT ∼ 300 °C). Argon (Ar: 200 sccm) was used as carrier gas while acetylene (C₂H₂: 20 sccm) and nitrogen (N: 5 sccm) were used as plasma source. Analytical methods such as X-ray photoelectron spectroscopy (XPS), FT-IR and UV–visible spectroscopy were employed to investigate the structural and optical properties of the DLC thin films respectively. FT-IR spectra show the structural modification of the DLC thin films with substrate temperatures showing the distinct peak around 3350 cm^− 1 wave number; which may corresponds to the sp² C–H bond. Tauc optical gap and film thickness both decreased with increasing substrate temperature. The peaks of XPS core level C 1 s spectra of the DLC thin films shifted towards lower binding energy with substrate temperature. We also got the small photoconductivity action of the film deposited at 300 °C on ITO substrate.     

Tribological properties of DLC films with different hydrogen contents in water environment

Diamond-like carbon (DLC) films were deposited on silicon wafers by thermal electron excited chemical vapor deposition (CVD). To change the hydrogen content in film, we used three types of carbon source gas (C₇H₈, CH₄, and a CH₄+H₂) and two substrate bias voltages. The hydrogen content in DLC films was analyzed using elastic recoil detection analysis (ERDA). Tribological tests were conducted using a ball-on-plate reciprocating friction tester. The friction surface morphology of DLC films and mating balls was observed using optical microscopy and laser Raman spectroscopy.Hydrogen content in DLC films ranged from 25 to 45 at.%. In a water environment, the friction coefficient and specific wear rate of DLC films were 0.07 and in the range of 10⁻⁸–10⁻⁹ mm³/Nm, respectively. The friction coefficient and specific wear rate of DLC film in water were hardly affected by hydrogen content. The specific wear rate of DLC film with higher hardness was lower than that of film with low hardness. Mating ball wear was negligible and the friction surface features on the mating ball differed clearly between water and air environments, i.e., the friction surface on mating balls in water was covered with more transferred material than that in air.     

The role of pressure on thin amorphous carbon films deposited using microwave surface wave plasma CVD

We report the effects of gas composition pressure (GCP) on the optical, structural and electrical properties of thin amorphous carbon (a-C) films grown on p-type silicon and quartz substrates by microwave surface wave plasma chemical vapor deposition (MW SWP CVD). The films, deposited at various GCPs ranging from 50 to 110 Pa, were studied by UV/VIS/NIR spectroscopy, atomic force microscopy, Raman spectroscopy, X-ray photoelectron spectroscopy and current–voltage characteristics. The optical band gap of the a-C film was tailored to a relatively high range, 2.3–2.6 eV by manipulating GCPs from 50 to 110 Pa. Also, spin density strongly depended on the band gap of the a-C films. Raman spectra showed qualitative structured changes due to sp³/sp² carbon bonding network. The surfaces of the films are found to be very smooth and uniform (RMS roughness < 0.5 nm). The photovoltaic measurements under light illumination (AM 1.5, 100 mW/cm²) show that short-circuit current density, open-circuit voltage, fill factor and photo-conversion efficiency of the film deposited at 50 Pa were 6.4 μA/cm², 126 mV, 0.164 and 1.4 × 10^− 4% respectively.     

Bonding defects and optical band gaps of DLC films deposited by microwave surface-wave plasma CVD

The effects of CH₄ / C₂H₄ flow ratio and annealing temperature on the defect states and optical properties of diamond-like carbon (DLC) films deposited by novel microwave surface-wave plasma chemical vapour deposition (MW SWP CVD) are studied through UV/VIS/NIR measurements, atomic force microscopy, Raman spectroscopy and electron spin resonance analysis. The optical band gap of DLC has been tailored between a relatively narrow range, 2.65–2.5 eV by manipulating CH₄ / C₂H₄ flow ratio and a wide range, 2.5–0.95 by thermal annealing. The ESR spin density varied between 10¹⁹ to 10¹⁷ spins/cm³ depending on the CH₄ / C₂H₄ flow ratio (1 : 3 to 3 : 1). The defect density increased with increasing annealing temperature. Also, there is a strong dependence of spin density on the optical band gap of the annealed-DLC films, and this dependency has been qualitatively understood from Raman spectra of the films as a result of structural changes due to sp³/sp² carbon bonding network. The surfaces of the films are found to be very smooth and uniform (RMS roughness < 0.5 nm).     

Effects of post-deposition annealing on different DLC films

Amorphous hydrogenated carbon films have been deposited by plasma-enhanced chemical vapour deposition at different process pressures and substrate temperatures, resulting in film properties ranging from polymer-like to diamond-like. The deposition parameter combinations were chosen by experimental design to enable the determination of both deposition pressure and deposition temperature effects on the annealing behaviour. The deposited films have then been annealed in vacuum at successively higher temperatures. Changes in optical band gap, internal stress, film thickness and infrared (IR) absorption spectra have been recorded to assess the influence of deposition parameters on the thermal stability of diamond-like carbon (DLC) and to identify temperature-induced modifications in the bonding structure. The results show a large variation in thermal stability between the different DLC films; samples deposited at low pressure display the greatest stability. The internal stress of the films starts decreasing at very low annealing temperature (<100 °C for the majority of samples), in most cases long before any decrease in the optical band gap can be detected. This is explained by a movement of hydrogen from sp² to sp³ sites as detected by IR measurements.     

Microstructure and optical band gap control of DLC film deposited by pulsed discharge plasma CVD

DLC films were deposited on silicon and quartz glass substrates by pulsed discharge plasma chemical vapor deposition (CVD), where the plasma was generated by pulsed DC discharge in H₂–CH₄ gas mixture at about 90 Torr in pressure, and the substrates were located near the plasma. The repetition frequency and duty ratio of the pulse were 800 Hz and 20%, respectively. When CH₄ / (CH₄ + H₂) ratio, i.e. methane concentration (Cm), increased from 3 to 40%, C₂ species in the plasma was increased, and corresponding to the increase of C₂, deposition rate of the film was increased from about 0.2 to 2.4 μm/h. The absorption peaks of sp³C–H and sp²C–H structures were observed in the FT-IR spectra, and the peak of sp²C–H structure was increased with increasing Cm, showing that sp² to sp³ bonding ratio was increased when Cm was increased. Corresponding to these structural changes due to the increase of Cm, optical band gap (Eg) was decreased from 3 to 0.5 eV continuously when Cm was increased from 3 to 40%.     

Electrochemical properties of N-doped hydrogenated amorphous carbon films fabricated by plasma-enhanced chemical vapor deposition methods

Nitrogen-doped hydrogenated amorphous carbon thin films (a-C:N:H, N-doped DLC) were synthesized with microwave-assisted plasma-enhanced chemical vapor deposition widely used for DLC coating such as the inner surface of PET bottles. The electrochemical properties of N-doped DLC surfaces that can be useful in the application as an electrochemical sensor were investigated. N-doped DLC was easily fabricated using the vapor of nitrogen contained hydrocarbon as carbon and nitrogen source. A N/C ratio of resulting N-doped DLC films was 0.08 and atomic ratio of sp³/sp²-bonded carbons was 25/75. The electrical resistivity and optical gap were 0.695 Ω cm and 0.38 eV, respectively. N-doped DLC thin film was found to be an ideal polarizable electrode material with physical stability and chemical inertness. The film has a wide working potential range over 3 V, low double-layer capacitance, and high resistance to electrochemically induced corrosion in strong acid media, which were the same level as those for boron-doped diamond (BDD). The charge transfer rates for the inorganic redox species, Fe^2+/3+ and Fe(CN)₆^4−/3− at N-doped DLC were sufficiently high. The redox reaction of Ce^2+/3+ with standard potential higher than H₂O/O₂ were observed due to the wider potential window. At N-doped DLC, the change of the kinetics of Fe(CN)₆^3−/4− by surface oxidation is different from that at BDD. The rate of Fe(CN)₆^3−/4− was not varied before and after oxidative treatment on N-doped DLC includes sp² carbons, which indicates high durability of the electrochemical activity against surface oxidation.     

Study on metal-doped diamond-like carbon films synthesized by cathodic arc evaporation

In this study, we developed a novel method of synthesizing metal-doped diamond-like carbon films (DLC) using the cathodic arc evaporation (CAE) process. Intense Cr plasma energy activated the decomposition of hydrocarbon source gas C₂H₂ to form a metal-doped amorphous carbon film on steel substrates. We deposited a Cr interlayer to prevent interdiffusion between DLC and the steel substrates. When the C₂H₂ partial pressure is higher than 1.3 Pa, the deposition reaction switched from Cr₃C₂ to DLC formation. The result is a hydrogenated DLC thin film possessing excellent microhardness as high as 3824 Hv(25g), and for which the incorporation of a Cr interface and Cr doping in the DLC matrix ensure film ductility and sufficient film adhesion. We employed Raman spectroscopy to evaluate the influences of reactive gas flow and substrate bias on the DLC composition; we carried out the microstructure and mechanical property measurements by scanning electron microscopy (SEM), X-ray diffraction (XRD), glow discharge optical spectroscopy (GDS) and wear tests.     

The mechanical and biocompatibility properties of DLC-Si films prepared by pulsed DC plasma activated chemical vapor deposition

Films of diamond-like carbon containing up to 22 at.% silicon (DLC-Si) were deposited on to silicon substrates by low-frequency pulsed DC plasma activated chemical vapor deposition (PACVD). The influence of silicon doping on deposition rate, composition, bonding structure, hardness, stress, surface roughness and biocompatibility was investigated and correlated with silicon content. A mixture of methane and tetramethylsilane (TMS) was used for the deposition of DLC-Si films at a pressure of 200 Pa. The deposition rate increased with increasing TMS flow. The addition of silicon into the DLC film leads to an increase of sp³ bonding, as measured by Raman spectroscopy, and also resulted in lower stress and hardness values. The RMS surface roughness of the films was measured by atomic force microscopy and increased from 0.35 nm for DLC to 6.7 nm for DLC-Si (14 at.% Si) due to the surface etching by the H atoms. Biocompatibility tests were performed using MG-63 osteoblast-like cell cultures that were left to grow for 3 days and their proliferations were assessed by scanning electron microscopy. The results indicated a homogeneous and optimal tissue integration for both the DLC and the DLC-Si surfaces. This pulsed PACVD technique has been shown to produce biocompatible DLC and DLC-Si coating with potential for large area applications.     

Electrical and optical properties of diamond-like carbon films deposited by pulsed laser ablation

Pulsed laser ablation of a graphite target was carried out by ArF excimer laser deposition at a laser wavelength of 193 nm and fluences of 10 and 20 J/cm² to produce diamond-like carbon (DLC) films. DLC films were deposited on silicon and quartz substrates under 1 × 10^? 6 Torr pressure at different temperatures from room temperature to 250 °C. The effect of temperature on the electrical and optical properties of the DLC films was studied. Laser Raman Spectroscopy (LRS) showed that the DLC band showed a slight increase to higher frequency with increasing film deposition temperature. Spectroscopic ellipsometry (SE) and ultraviolet–visible absorption spectroscopy showed that the optical band gap of the DLC films was 0.8–2 eV and decreased with increasing substrate temperature. These results were consistent with the electrical resistivity results, which gave values for the films in the range 1.0 × 10⁴–2.8 × 10⁵ Ω cm and which also decreased with deposition temperature. We conclude that at higher substrate deposition temperatures, DLC films show increasing graphitic characteristics yielding lower electrical resistivity and a smaller optical band gap.     

Deposition of diamond film on silicon and quartz substrates located near DC plasma

Deposition of diamond films on to both Si and quartz substrates was succeeded by means of locating the substrate near plasma, and their microstructures were investigated by using SEM and Raman spectroscopy. The plasma was generated by intermittent DC discharge in H₂–CH₄ gas mixture at high gas pressure. The deposition rate of the film was remarkably increased when distance (D) between the substrate and the plasma (discharge electrodes) decreased. When the gas pressure (P_g) was increased from 100 to 250 Torr, the deposition rate was extremely increased and the crystalline quality of the film was improved. The deposition rate, when P_g = 200 Torr and D = 5 mm, was about 2.1 and 1.7 μm/h for Si and quartz substrate, respectively.     

Influence of technological conditions on mechanical stresses inside diamond-like carbon films

In this paper the influences of the technological conditions, i.e. the influences of the hydrogen flow rate and deposition time, on the values of the intrinsic mechanical stresses inside the diamond-like carbon (DLC) thin films prepared by plasma enhanced chemical vapor deposition onto silicon substrates are studied. These stresses are measured by two-beam interferometry and optical profilometry based on chromatic aberration through the measurements of deformations of the silicon substrates originating in consequence of the film stresses. It is shown that the influence of the deposition time (i.e. film thickness) on the film stress is relatively slight in contrast to the influence of the hydrogen flow rate on this quantity. It is namely shown that the film stresses are influenced by the hydrogen flow rate values in a pronounced way within the interval of interest, i.e. within the interval 1–7 sccm. Moreover, it is shown that the method of optical profilometry used can be competitive to the method of two-beam interferometry from the practical point of view.     

Effect of substrate bias voltage on the properties of diamond-like carbon thin films deposited by microwave surface wave plasma CVD

Diamond-like carbon (DLC) thin films were deposited on silicon and ITO substrates with applying different negative bias voltage by microwave surface wave plasma chemical vapor deposition (MW SWP-CVD) system. The influence of negative bias voltage on optical and structural properties of the DLC film were investigated using X-ray photoelectron spectroscopy, UV/VIS/NIR spectroscopy, Fourier transform infrared spectroscopy and Raman spectroscopy. Optical band gap of the films decreased from 2.4 to 1.7 with increasing negative bias voltage (0 to − 200 V). The absorption peaks of sp³ CH and sp² CH bonding structure were observed in FT-IR spectra, showing that the sp²/sp³ ration increases with increasing negative bias voltage. The analysis of Raman spectra corresponds that the films were DLC in nature.     

Polymeric semiconducting carbon from fullerene by pulsed laser ablation

The polymeric semiconducting carbon films are grown on silicon and quartz substrates by excimer (XeCl) pulsed laser deposition (PLD) technique using fullerene C₆₀ precursor. The substrate temperature is varied up to 300 °C. The structure and optical properties of the films strongly depend on the substrate temperature. The grain size is increased and uniform polymeric film with improved morphology at higher temperature is observed. The Tauc gap is about 1.35 eV for the film deposited at 100°C and with temperature the gap is decreased upto 1.1 eV for the film deposited at 250 °C and increased to about 1.4 eV for the film deposited at 300 °C. The optical absorption properties are improved with substrate temperature. Raman spectra show the presence of both G peak and D peak and are peaked at about 1590 cm^− 1 and 1360 cm^− 1, respectively for the film deposited at 100 °C. The G peak position remains almost unchanged while D peak has changed only a little with temperature might be due to its better crystalline structure compared to the typical amorphous carbon films and might show interesting in device such as, optoelectronic applications.     

Effect of microwave power on diamond-like carbon films deposited using electron cyclotron resonance chemical vapor deposition

Diamond-like carbon (DLC) films have been deposited using electron cyclotron resonance chemical vapor deposition (ECR-CVD) under various microwave power conditions. Langmuir probe measurement and optical emission spectroscopy (OES) were used to characterize the ECR plasma, while the films were characterized using Raman and infrared (IR) spectroscopies, hardness and optical gap measurements. It was found that the ion density and all signal peaks in the optical emission (OE) spectra increased monotonously following the increase in microwave power. Raman spectra and optical gap measurements indicate that the films become more graphitic with lower content of sp³-hybridized carbon atoms as the microwave power was increased. IR and hardness measurements indicate a reduction in hydrogen content and decrease in hardness for the film produced at relatively high microwave powers. A deposition mechanism is described which involved the ion bombardment of film surfaces and hydrogen–surface interactions. The deposition rate of DLC film is correlated to the ion density and CH₃ density.