纤维长度和体积分数对Al2O3-SiO2 / Al2Si微屈服行为的影响

以通过浸渗挤压工艺制备的Al₂O₃-SiO₂ / Al₂Si 复合材料为研究对象, 使用配备有精度达10 - 7位移测量装置的Inst ron5569 电子拉伸试验机, 并采用连续加载法, 详细研究了晶化硅酸铝短纤维的体积分数和短纤维长度对铝硅基复合材料微屈服行为的影响规律, 并定性分析了原因。结果表明: 随着晶化硅酸铝短纤维体积分数的逐渐增大, 铝硅基复合材料的微屈服强度逐渐减小, 但其宏观屈服强度和弹性模量却逐渐增大; 随着晶化硅酸铝短纤维长度的逐渐增加, 铝硅基复合材料的微屈服强度逐渐减小, 但其宏观屈服强度却逐渐增大。      

三维网络Al2O3增强球墨铸铁基复合材料摩擦磨损性能

采用SRV摩擦磨损试验机研究了球墨铸铁及三维网络Al₂O₃增强球墨铸铁基复合材料的干摩擦磨损性能, 测量了球墨铸铁和复合材料在不同摩擦频率及载荷下的摩擦系数和磨损率; 用扫描电镜观察磨损表面形貌, 并分析了三维网络Al₂O₃对复合材料磨损机制的影响。结果表明: 陶瓷与金属基体之间具有良好界面结合的三维网络Al₂O₃/球墨鋳铁复合材料, 其摩擦系数随载荷和摩擦频率的变化保持稳定; 复合材料的耐磨性能远优于球墨铸铁, 而且随着摩擦频率和载荷的增加, 复合材料的抗磨损性能明显提高。这是由于复合材料中陶瓷与金属相之间三维空间结构和良好的界面结合有利于摩擦载荷的传递; 金属基体中的石墨减摩作用保持摩擦系数的稳定; 三维陶瓷骨架在磨损表面形成硬的微突体并起承载作用, 制约了基体的塑性变形和高温软化, 有利于磨损表面氧化膜的留存。     

Fracture toughness of microsphere Al2O3–Al particulate metal matrix composites

The fracture toughness and behaviour of COMRAL-85^TM, a 6061 aluminium–magnesium–silicon alloy reinforced with 20 vol% Al₂O₃-based polycrystalline ceramic microspheres, and manufactured by a liquid metallurgy route, have been investigated. Fracture toughness tests were performed using short rod and short bar (chevron-notch) specimens machined from extruded 19 mm diameter rod, heat treated to the T6 condition. The fracture toughness in the R–L orientation was found to be lower than in the C–R or L–R orientations owing to the presence of particle-free bands in the extrusion direction. Short rod tests were also conducted for the R–L orientation on six powder metallurgy composites with particle volume fractions ranging between 5% and 30%. It was found that the fracture toughness decreased progressively with particle volume fraction, but at a decreasing rate. A detailed examination of the fracture behaviour was made for both the liquid metallurgy and powder metallurgy processed composites.     

Effect of Al2O3 particle size on vacuum breakdown behavior of Al2O3/Cu composite

In order to clarify the effect of Al₂O₃ particle size on the arc erosion behavior of the ceramic-reinforced Al₂O₃/Cu composite, Al₂O₃/Cu composites with different sizes of Al₂O₃ particles were prepared by powder metallurgy, the effect of Al₂O₃ particle size on the characteristics of arc motion was studied, and the mechanism of arc erosion of Al₂O₃/Cu composites was discussed as well. The results show that with decrease in the size of Al₂O₃ particles, the erosion area increases significantly and the erosion pits become shallower. The vacuum breakdown is preferred to appear in the area between Al₂O₃ particle and the copper matrix. Based on the experimental results and theoretical analysis, a particle partition arc model is proposed.     

High cycle fatigue behaviour of microsphere Al2O3–Al particulate metal matrix composites

The high-cycle stress-life (S–N) curve and fatigue crack growth threshold (ΔK_th) behaviour of COMRAL-85^TM, a 6061 aluminium–magnesium–silicon alloy reinforced with 20 vol.% Al₂O₃-based polycrystalline ceramic microspheres, and manufactured by a liquid metallurgy route, have been investigated for a stress ratio of R = −1 (fully reversed loading). Fatigue testing was conducted on both smooth round bar (S–N) specimens and notched round bar (fatigue threshold) specimens. Unreinforced Al 6061-T6 also processed by a liquid metallurgy route and six powder metallurgy processed composites with particle volume fractions ranging between 5% and 30% were also studied. S–N data revealed that the powder metallurgy processed composites generally gave longer fatigue lives than the matrix alloy, whereas COMRAL-85^TM exhibited a reduced fatigue life. The fatigue threshold results were very similar for all the composites, being lower than for Al 6061-T6. Fatigue failure mechanisms were determined from examination of the fracture surfaces and the crack profiles.     

Effects of Al2O3 particle reinforcement on the lubricated sliding wear behavior of ZA-27 alloy composites

The present investigation deals with the effect of Al₂O₃ particle reinforcement on the lubricated sliding behavior of ZA-27 alloy. The composites with 3, 5, and 10 wt% of Al₂O₃ particles were produced by the compocasting procedure. Tribological properties of alloy and composites were studied, using block-on-disk tribometer at different specific loads and sliding speeds. The test results revealed that composite specimens exhibited significantly lower wear rate, but higher coefficient of friction than the matrix alloy specimens in all the combinations of applied loads and sliding speeds. The improved antiwear characteristics of the composites were influenced by positive effects of higher frictional heating on compatibility of the composite phases and suppressing micro-cracking tendency. Due to that, effects of reinforcing hard particles were manifested through the reduced wear rate of composites, especially in conditions of higher load, lower sliding speeds and higher Al₂O₃ particle content. In present wear tests, the significant forming of mechanically mixed layers was not noticed, what is confirmed by the SEM microphotographs.     

Bi2O3助熔剂对CaO-B2O3-SiO2/Al2O3玻璃陶瓷复合材料性能的影响

以CaO-B₂O₃-SiO₂(CBS)玻璃粉体和Al₂O₃陶瓷粉体为原料,通过在CBS与Al₂O₃的质量比固定为50:50的玻璃-陶瓷复合材料中添加适量的Bi₂O₃作为烧结助熔剂,探讨了Bi₂O₃助熔剂对CBS/Al₂O₃复合材料的烧结性能、介电性能、抗弯强度和热膨胀系数的影响规律.研究表明:Bi₂O₃助熔剂能通过降低CBS玻璃的转变温度和黏度促进CBS/Al₂O₃复合材料的致密化进程,于880 ℃下烧结即能获得结构较致密、气孔较少的CBS/Al₂O₃复合材料.然而,过量添加Bi₂O₃将使玻璃的黏度过低,从而恶化CBS/Al₂O₃复合材料的烧结性能、介电性能及抗弯强度.当Bi₂O₃的添加量为CBS/Al₂O₃复合材料的1.5wt%时,于880 ℃下烧结即能获得最为致密的CBS/Al₂O₃复合材料,密度为2.82 g·cm^-3,这一材料具有良好的介电性能(介电常数为7.21,介电损耗为1.06×10^-3),抗弯强度为190.34 MPa,0~300 ℃的热膨胀系数为3.52×10^-6 K^-1.     

Al2O3颗粒形貌对注凝成型ZrO2/Al2O3陶瓷性能的影响

采用3种不同形貌的Al₂O₃原料对注凝成型制备ZrO₂/Al₂O₃（ZTA）陶瓷工艺中悬浮体的流变性能进行了研究。以低毒的单体N,N-二甲基丙烯酰胺（DMAA）制备了ZrO₂/Al₂O₃坯体和陶瓷。讨论了3种不同形貌的Al₂O₃原浆料的分散剂用量、球磨时间和固含量对浆料流变性的影响。Al₂O₃粉体呈扁平状有利于降低浆料的黏度,Al₂O₃粉体呈棒状对生坯强度的提高有利。制得的3种ZrO₂/Al₂O₃坯体颗粒间结合紧密,抗弯强度分别达到21.45,19.87,25.90 MPa。Al₂O₃粉体呈颗粒状有利于最终陶瓷力学性能的提高,陶瓷的抗弯强度及断裂韧性分别为680 MPa和7.49 MPa·m^1/2,453.1 MPa和6.8 MPa·m^1/2,549.4 MPa和6.34 MPa·m^1/2。     

纤维长度和体积分数对Al2O3-SiO2/Al-Si微屈服行为的影响

以通过浸渗挤压工艺制备的Al2O3-SiO2/Al-Si复合材料为研究对象,使用配备有精度达10-7位移测量装置的Instron5569电子拉伸试验机,并采用连续加载法,详细研究了晶化硅酸铝短纤维的体积分数和短纤维长度对铝硅基复合材料微屈服行为的影响规律,并定性分析了原因.结果表明: 随着晶化硅酸铝短纤维体积分数的逐渐增大,铝硅基复合材料的微屈服强度逐渐减小,但其宏观屈服强度和弹性模量却逐渐增大; 随着晶化硅酸铝短纤维长度的逐渐增加,铝硅基复合材料的微屈服强度逐渐减小,但其宏观屈服强度却逐渐增大.     

Optimization of cold-sprayed AA2024/Al2O3 metal matrix composites via friction stir processing: Effect of rotation speeds

In this study, friction stir processing (FSP) was employed to modify cold-sprayed (CSed) AA2024/Al₂O₃ metal matrix composites (MMCs). Three different rotation speeds with a constant traverse speed were used for FSP. Microstructural analysis of the FSPed specimens reveals significant Al₂O₃ particle refinement and improved particle distribution over the as-sprayed deposits. After FSP, a microstructural and mechanical gradient MMC through the thickness direction was obtained. Therefore, a hybrid technique combining these two solid-state processes, i.e. CS and FSP, was proposed to produce functionally gradient deposits. The Guinier-Preston-Bagaryatskii zone was dissolved during FSP, while the amounts at different rotation speeds were approximately the same, which is possibly due to the excellent thermal conductivity of the used Cu substrate. Mechanical property tests confirm that FSP can effectively improve the tensile performance and Vickers hardness of CSed AA2024/Al₂O₃ MMCs. The properties can be further enhanced with a larger rotation speed with a maximum increase of 25.9% in ultimate tensile strength and 27.4% in elongation at 1500 rpm. Friction tests show that FSP decreases the wear resistance of CSed MMCs deposits due to the breakup of Al₂O₃ particles. The average values and fluctuations of friction coefficients at different rotation speeds vary significantly.     

Study on the yield behavior of Al2O3–SiO2(sf)/Al–Si metal matrix composites

As the yield behavior of Al₂O₃–SiO₂(sf)/Al–Si MMCS is concerned, effects of heat treatment and parameters of short fiber, including volume fraction, size, distribution mode, were investigated. Dislocation configurations adjacent to interface between matrix and fiber were observed by TEM. Macro-yield stress (σ_0.2) and micro-yield stress (σ_MYS) vary with parameters of short fiber, and effects of these parameters on σ_0.2 appear to be opposite to those on σ_MYS. This phenomenon was interpreted by thermal residual stress in matrix and dislocation configuration. Suitable quenching followed aging treatment is an effective method to enhance the σ_MYS and the σ_0.2 simultaneously. For the specimen with heat treatment of 550 °C/1 h WQ + 170 °C/6 h (T6) AC, σ_0.2 and σ_MYS reach 200 and 58 MPa, respectively, and they are almost as twice as those as-cast.     

Al2O3-TiC/Al2O3-TiC-CaF2复合叠层陶瓷材料摩擦磨损性能

将Al₂O₃-TiC陶瓷材料与具有固体润滑特性的Al₂O₃-TiC-CaF₂陶瓷材料进行叠层, 通过真空热压烧结制备Al₂O₃-TiC/Al₂O₃-TiC-CaF₂复合叠层陶瓷材料。在环盘式摩擦磨损试验机上进行摩擦磨损实验, 研究该材料在不同载荷、 转速条件下的摩擦系数和磨损率, 分别用SEM及EDS观察材料磨损前后的微观形貌和分析其成分组成, 研究其磨损机制。结果表明: 在相同载荷条件下, Al₂O₃-TiC/Al₂O₃-TiC-CaF₂复合叠层陶瓷材料的摩擦系数和磨损率随着转速的升高而下降, 在相同转速条件下, 其摩擦系数和磨损率随着载荷的增加而下降; Al₂O₃-TiC/Al₂O₃-TiC-CaF₂复合叠层陶瓷材料的磨损机制主要是磨粒磨损和黏着磨损。     

Deformation and damage in Al/Al2O3

Al/Al₂O₃-composites as an example of light weight materials are very interesting for many industrial applications because of a favourable combination of low density and improved mechanical properties. The prediction of the macroscopic mechanical behaviour of these materials related to their microstructure requires the knowledge of damage initiation and crack development under external loading conditions and, if present, residual stresses have to be taken into consideration. Different types of material degradation like particle/matrix-debonding, particle failure and matrix cracking can be observed in these types of metal matrix composites. The aim of the present work is to introduce damage criteria into a FE-microstructural model in order to foresee the degradation process in an Al₂O₃-particle reinforced Al(6061) composite during mechanical loading. Presently, the conventional fabrication route of the Al/Al₂O₃-composite is a metallurgical method with extrusion for homogenisation of the microstructure and final heat treatment to achieve a defined precipitation state. The influence of thermal residual stresses due to cooling down from annealing temperature on the deformation and damage initiation of Al(6061)/10vol%Al₂O₃-composites is investigated through finite element analyses using the experimentally mapped real microstructure as binary data. Especially, the stresses in the ceramic particles which are responsible for particle cracking and the hydrostatic stresses in the Al-matrix making the particle–matrix interface prone to debonding were analysed. The results show the importance of the thermal residual stresses with respect to damage criteria as obtained by micromechanical FE-calculations.     

Al2O3纤维对SiO2基陶瓷型芯的烧缩阻滞

向SiO₂基体粉料中添加Al₂O₃纤维,采用热压注法制备Al₂O₃/SiO₂陶瓷型芯。分析Al₂O₃纤维含量对陶瓷型芯性能的影响。研究结果表明：Al₂O₃纤维含量对Al₂O₃/SiO₂陶瓷型芯的线收缩率、体积密度和抗弯强度均有较大的影响。当Al₂O₃纤维含量大于1wt%时,Al₂O₃/SiO₂陶瓷型芯的线收缩率大幅度降低,稳定在0.335%左右,体积密度随之降低,稳定在1.790 g · cm^-3左右;当Al₂O₃纤维含量为1wt%时,陶瓷型芯抗弯强度达最大值20.48 MPa。分析了Al₂O₃纤维对Al₂O₃/SiO₂陶瓷型芯烧结收缩的阻滞作用机制。     

Processing, microstructure and properties of C40 Mo(Si,Al)2/Al2O3 composites

The C40 Mo(Si_0.75Al_0.25)₂/Al₂O₃ composites were prepared by spark plasma sintering (SPS) of mechanically alloyed (MA) powders. The Mo(Si_0.75Al_0.25)₂/0–20 vol.% Al₂O₃ materials, showing micron and submicron composite structure, possess a hardness of 13.9–14.6 GPa but a poor toughness of 1.78–1.80 MPa m^1/2. The addition of 30 vol.% Al₂O₃ leads to the formation of the micron C40 Mo(Si_0.75Al_0.25)₂/Al₂O₃ composite with an intergranular distribution of Al₂O₃, that results in a drop of the hardness to 10.2 GPa and an improvement of the toughness to 3.67 MPa m^1/2. The transition of the cleavage facets to the intergranular fracture with the addition of Al₂O₃ is assumed as the main toughening mechanism.     

Ti/Al2O3复合材料制备及其力学性能

利用放电等离子烧结(SPS)制备了性能优异的40%(体积分数)Ti/Al2O3复合材料,其弯曲强度、断裂韧性、显微硬度和相对密度分别为897.29MPa、17.38MPa·m1/2、17.13GPa和99.24%.SEM和HREM对复合材料的微观结构分析发现,晶粒细化、位错环强化等是材料强度提高的主要原因;裂纹的偏转和桥联是材料韧性提高的关键所在.     

Electrical conduction mechanisms of metal nanoclusters embedded in an amorphous Al2O3 matrix

We present the synthesis and electrical characterization of amorphous nanocomposite layers made of metallic nanoclusters embedded in an alumina matrix (nc-Co:Al₂O₃). The nanostructured materials were fabricated using a pulsed laser deposition (PLD)-derived method based on a nano-cluster generator coupled with a conventional PLD system for host medium co-deposition. The films were subjected to a detailed structural study carried out using high-resolution transmission electron microscopy and atomic force microscopy. The clusters inserted in the alumina matrix are metallic, well crystallized and possess an fcc structure with an average diameter centered at ∼ 2 nm. Dielectric constant and electrical conduction mechanisms of nc-Co:Al₂O₃ layers integrated in metal-insulator-metal capacitive structures were studied for different doping levels and for a broad temperature range (303-473 K). It was concluded that the dielectric constant in the films depends on the doping levels while the major electrical conduction mechanisms are best described by the space charge limited currents formalism, in which the current density J on an applied voltage V follow a power-law dependence (J ∼ Vⁿ) at applied voltages higher than ∼ 2 V. Such composite may find immediate applications as dielectric layers with controlled discharging conduction paths in Radio Frequency-Micro-Electro-Mechanical Systems capacitive structures.     

三维网络结构Al2O3陶瓷/高铬铸铁复合材料干摩擦磨损性能

采用往复式滑动摩擦磨损（SRV）试验机研究了高铬铸铁及三维网络结构Al₂O₃陶瓷增强高铬铸铁复合材料的干摩擦磨损性能,测量了高铬铸铁和Al₂O₃陶瓷/高铬铸铁复合材料在不同摩擦频率及载荷下的摩擦系数和磨损率;用扫描电镜观察磨损表面形貌,并分析了三维网络Al₂O₃陶瓷对复合材料磨损机制的影响。结果表明：陶瓷Al₂O₃与高铬铸铁基体之间具有良好的界面结合,复合材料的摩擦系数随摩擦频率和载荷的变化保持稳定,耐磨性远优于高铬铸铁,而且随着摩擦频率和载荷的增加,Al₂O₃陶瓷/高铬铸铁复合材料的抗磨损性能明显提高,这是由于复合材料中Al₂O₃与高铬铸铁相之间三维空间结构和良好的界面结合有利于摩擦载荷的传递;三维Al₂O₃陶瓷骨架在磨损表面形成硬的网络突体并起承载作用,能有效保护金属基体;磨损机制为氧化磨损及磨粒磨损共同作用。     

Mechanical and machining properties of X38CrMoV5-1/Al2O3 metal matrix composites and components

Large plates and discs of X38CrMoV5-1/Al₂O₃ metal matrix composites (MMCs) were produced via Ti-activated pressureless melt infiltration. After machining the plates were characterised using non-destructive testing methods (X-ray and ultrasonic C-scans) in order to investigate the quality of infiltration before preparing bars for four-point-bending tests. Subsequently, parts of the plates were used for machining tests, including sawing, welding and spark erosion. Furthermore, MMC discs were prepared for wear tests. The as-infiltrated MMC discs show a low wear rate of 1.6 × 10⁻¹⁰–2.2 × 10⁻¹⁰ m/s, which is 2–3 times better than the hardened steel itself, or 12–17 times better compared to X38CrMoV5-1 in the annealed state. As a first component a wire-drawing die was fabricated and successfully tested for drawing Al alloy AA6082 and steel 16MnCr5.     

In situ Al3Ti and Al2O3 nanoparticles reinforced Al composites produced by friction stir processing in an Al-TiO2 system

Al and TiO₂ powders were selected to fabricate in situ Al composites via multiple pass friction stir processing (FSP) based on the thermodynamic analysis. The microstructural investigations indicated FSP would induce reaction between Al and TiO₂. Al₃Ti and Al₂O₃ particles were formed after 4 pass FSP with 100% overlapping. The in situ particles were about 80 nm in size at various FSP conditions, and ultrafine matrix grains 602 nm in size were obtained when water cooling was applied during FSP. Tensile tests indicated that the in situ nanocomposites exhibited pronounced work hardening behavior and a good combination of strength and ductility.