Synthesis of BaCu(B2O5) Ceramics and their Effect on the Sintering Temperature and Microwave Dielectric Properties of Ba(Zn1/3Nb2/3)O3 Ceramics

BaCu(B₂O₅) ceramics were synthesized and their microwave dielectric properties were investigated. BaCu(B₂O₅) phase was formed at 700°C and melted above 850°C. The BaCu(B₂O₅) ceramic sintered at 810°C had a dielectric constant (ɛ_r) of 7.4, a quality factor ( Q × f ) of 50 000 GHz and a temperature coefficient of resonance frequency (τ_f) of −32 ppm/°C. As the BaCu(B₂O₅) ceramic had a low melting temperature and good microwave dielectric properties, it can be used as a low-temperature sintering aid for microwave dielectric materials for low temperature co-fired ceramic application. When BaCu(B₂O₅) was added to the Ba(Zn_1/3Nb_2/3)O₃ (BZN) ceramic, BZN ceramics were well sintered even at 850°C. BaCu(B₂O₅) existed as a liquid phase during the sintering and assisted the densification of the BZN ceramic. Good microwave dielectric properties of Q × f =16 000 GHz, ɛ_r=35, and τ_f=22.1 ppm/°C were obtained for the BZN+6.0 mol% BaCu(B₂O₅) ceramic sintered at 875°C for 2 h.     

Effects of B2O3 Addition on the Dielectric and Ferroelectric Properties of Ba0.7Sr0.3TiO3 Ceramics

The effects of B₂O₃ addition on the sintering behavior and the dielectric and ferroelectric properties of Ba_0.7Sr_0.3TiO₃ (BST) ceramics were investigated. The dielectric and ferroelectric properties of a BST sample with 0.5 wt% B₂O₃ sintered at <1150°C were as good as those of undoped BST sintered at 1350°C, and the dielectric loss was better. When >1.0 wt% B₂O₃ was added to BST, the overdoped B₂O₃ did not form a liquid phase or volatilize; it remained in the samples and formed a secondary phase that lowered the sintering behavior and the dielectric and ferroelectric properties of the BST.     

Microwave Dielectric Properties of Li2TiO3 Ceramics Doped with ZnO–B2O3 Frit

A type of new low sintering temperature ceramic, Li₂TiO₃ ceramic, has been found. Although it is difficult for the Li₂TiO₃ compound to be sintered compactly at temperatures above 1000°C for the volatilization of Li₂O, dense Li₂TiO₃ ceramics were obtained by conventional solid-state reaction method at the sintering temperature of 900°C with the addition of ZnO–B₂O₃ frit. The sintering behavior and microwave dielectric properties of Li₂TiO₃ ceramics with less ZnO–B₂O₃ frit (≤3.0 wt%) doping were investigated. The addition of ZnO–B₂O₃ frit can lower the sintering temperature of the Li₂TiO₃ ceramics, but it does not apparently degrade the microwave dielectric properties of the Li₂TiO₃ ceramics. Typically, the good microwave dielectric properties of ɛ_r=23.06, Q × f =32 275 GHz, τ_f = 35.79 ppm/°C were obtained for 2.5 wt% ZnO–B₂O₃ frit-doped Li₂TiO₃ ceramics sintered at 900°C for 2 h. The porosity was 0.08%. The Li₂TiO₃ ceramic system may be a promising candidate for low-temperature cofired ceramics applications.     

Low-Temperature Sintering and Microwave Dielectric Properties of the Zn2SiO4 Ceramics

B₂O₃ was added to nominal composition Zn_1.8SiO_3.8 (ZS) ceramics to decrease their sintering temperature for application to low-temperature cofired ceramic (LTCC) devices. B₂O₃ reacted with SiO₂ to form a liquid phase containing SiO₂ and B₂O₃. The composition and melting temperature of the liquid phase depended on the sintering temperature and the B₂O₃ content. The specimen containing 20.0 mol% of B₂O₃ sintered at 900°C exhibited high microwave dielectric properties of Q × f =53 000 GHz, ɛ _r=5.7, and τ_f=−16 ppm/°C, confirming the promising potential of the B₂O₃-added ZS ceramics as candidate materials for the LTCC devices.     

Sintering and Microwave Dielectric Properties of the LiNb0.63Ti0.4625O3 Ceramics with the B2O3–SiO2 Liquid-Phase Additives

The effect of B₂O₃–SiO₂ liquid-phase additives on the sintering, microstructure, and microwave dielectric properties of LiNb_0.63Ti_0.4625O₃ ceramics was investigated. It was found that the sintering temperature could be lowered easily, and the densification and dielectric properties of LiNb_0.63Ti_0.4625O₃ ceramics could be greatly improved by adding a small amount of B₂O₃–SiO₂ solution additives. No secondary phase was observed for the ceramics with B₂O₃–SiO₂ additives. With the addition of 0.10 wt% B₂O₃–SiO₂, the ceramics sintered at 900°C showed favorable microwave dielectric properties with ɛ_r=71.7, Q × f =4950 GHz, and τ_f=−2.1 ppm/°C. The energy dispersive spectra analysis showed an excellent co-firing interfacial behavior between the LiNb_0.63Ti_0.4625O₃ ceramic and the Ag electrode. It indicated that LiNb_0.63Ti_0.4625O₃ ceramics with B₂O₃–SiO₂ solution additives have a number of potential applications on passive integrated devices based on the low-temperature co-fired ceramics technology.     

Effect of Glass Additions on BaO–TiO2–WO3 Microwave Ceramics

The effect of glass addition on the properties of BaO–TiO₂-WO₃ microwave dielectric material N-35, which has Q = 5900 and K = 35 at 7.2 GHz for samples sintered at 1360°C, was investigated. Several glasses including B₂O₃, SiO₂, 5ZnO–2B₂O₃, and nine other commercial glasses were selected for this study. Among these glasses, one with a 5 wt% addition of B₂O₃ to N-35, when sintered at 1200°C, had the best dielectric properties: Q = 8300 and K = 34 at 8.5 GHz. Both Q and K increased with firing temperature as well as with density. The Q of N-35, when sintered with a ZnO–B₂O₃ glass system, showed a sudden drop in the sintering temperature to about 1000°C. The results of XRD, thermal analysis, and scanning electron microscopy indicated that the chemical reaction between the dielectric ceramics and glass had a greater effect on Q than on the density. The effects of the glass content and the mixing process on the densification and microwave dielectric properties are also presented. Ball milling improved the densification and dielectric properties of the N-35 sintered with ZnO–B₂O₃.     

Electrical Properties of Sr0.7Ba0.3TiO3 Ceramics Doped with Nb2O5, 3Li2O · 2SiO2, and Bi2O3

The electrical properties of Sr_0.5Ba_0.3TiO₃ in the presence of Nb₂O₅ as a donor, 3Li₂O · 2SiO₂ as a sintering agent, and Bi₂O₃ as a dopant have been studied. When the compositions of the ceramics were 1 mol Sr_0.7Ba_0.3TiO₃+ 0.5 mol% Nb₂O₅+ 2 mol% 3Li₂O · 2SiO₂+ 0.2 mol% Bi₂O₃, the ceramics were sintered at 1100°C and exhibited the following characteristics: apparent dielectric constant ɛ, 25000; loss factor tan δ, 2%; insulating resistivity ρ_j, 10¹⁰Ω· cm; variation of dielectric constant with temperature Δɛ/ɛ (−25° to +85°C), +10%, −14%. ɛ and tan δ show only small changes with frequency. The study shows this ceramic can be used in multilayer technology.     

Microwave Dielectric Properties of Low-Fired Ba5Nb4O15

The effect of B₂O₃ on the sintering temperature and microwave dielectric properties of Ba₅Nb₄O₁₅ has been investigated using X-ray powder diffraction, scanning electron microscopy, and a network analyzer. Interactions between Ba₅Nb₄O₁₅ and B₂O₃ led to formation of second phases, BaNb₂O₆ and BaB₂O₄. The addition of B₂O₃ to Ba₅Nb₄O₁₅ resulted in lowering the sintering temperature from 1400° to 925°C. Low-fired Ba₅Nb₄O₁₅ could be interpreted by measuring changes in the quality factor ( Q × f ), the relative dielectric constant (ɛ_r), and the temperature coefficient of resonant frequency (τ_f) as a function of B₂O₃ additions. More importantly, the formation of BaNb₂O₆ provided temperature compensation. The microwave dielectric properties of low-fired Ba₅Nb₄O₁₅ had good dielectric properties: Q × f = 18700 GHz, ɛ_r= 39, and τ_f= 0 ppm/°C.     

Effects of CuO Doping on the Microstructural and Dielectric Properties of Ba0.6Sr0.4TiO3 Ceramics

This study investigates the effect of CuO on the sintering behavior, dielectric properties, and microstructures of Ba_0.6Sr_0.4TiO₃ (BST) ceramics. The ceramics were sintered in air at temperatures ranging from 1000° to 1230°C. It is found that a small amount of added CuO (0.6 mol%) can significantly increase the density and improve the dielectric properties of BST ceramics. Doped BST ceramics can be sintered to a density >95% of the theoretical density at 1150°C. scanning electron microscopic observations show that the BST grain sizes increase with increasing amounts of CuO. No secondary phases in the BST ceramics are observed using X-ray diffraction pattern for CuO additions up to 0.9 mol%. However, compositional analysis using transmission electron microscopy-EDX for the BST ceramics with 0.9 mol% CuO sintered at 1150°C showed that a small level of secondary phase formation is present. On the other hand, large dislocations are observed for BST with 0.6 mol% CuO addition as a result of lattice distortion, which creates the vacancy condensation because of the atomic mismatch in the solid solutions. Optimal CuO doping concentrations can reduce the loss tangents of BST that can also ensure a high dielectric constant. When the doping concentration of CuO is 0.6 mol% and the ceramic is sintered at 1150°C, the BST ceramic has the following properties at 1 MHz: dielectric constant=4094, tan δ=0.55%.     

Effect of Bi2O3 Addition on the Sintering Temperature and Microwave Dielectric Properties of Zn2SiO4 Ceramics

Bi₂O₃ was added to a nominal composition of Zn_1.8SiO_3.8 (ZS) ceramics to decrease their sintering temperature. When the Bi₂O₃ content was <8.0 mol%, a porous microstructure with Bi₄(SiO₄)₃ and SiO₂ second phases was developed in the specimen sintered at 885°C. However, when the Bi₂O₃ content exceeded 8.0 mol%, a liquid phase, which formed during sintering at temperatures below 900°C, assisted the densification of the ZS ceramics. Good microwave dielectric properties of Q × f =12,600 GHz, ɛ_r=7.6, and τ_f=−22 ppm/°C were obtained from the specimen with 8.0 mol% Bi₂O₃ sintered at 885°C for 2 h.     

Microwave Dielectric Properties of 5Li2O–0.583Nb2O5–3.248TiO2 Ceramics with V2O5

The effects of V₂O₅ addition on the sintering behavior, microstructure, and the microwave dielectric properties of 5Li₂O–0.583Nb₂O₅–3.248TiO₂ (LNT) ceramics have been investigated. With addition of low-level doping of V₂O₅ (≤2 wt%), the sintering temperature of the LNT ceramics could be lowered down to around 920°C due to the liquid phase effect. A secondary phase was observed at the level of 2 wt% V₂O₅ addition. The addition of V₂O₅ does not induce much degradation in the microwave dielectric properties but lowers the τ_f value to near zero. Typically, the excellent microwave dielectric properties of ɛ_r=21.5, Q × f =32 938 GHz, and τ_f=6.1 ppm/°C could be obtained for the 1 wt% V₂O₅-doped sample sintered at 920°C, which is promising for application of the multilayer microwave devices using Ag as an internal electrode.     

Influence of V2O5 Additions to 5Li2O–1Nb2O5–5TiO2 Ceramics on Sintering Temperature and Microwave Dielectric Properties

The effects of the addition of V₂O₅ on the sintering behavior, microstructure, and microwave dielectric properties of 5Li₂O–1Nb₂O₅–5TiO₂ (LNT) ceramics have been investigated. With low-level doping of V₂O₅ (≤3 wt%), the microstructure of the LNT ceramic changed from a special two-level intergrowth structure into a two-phase composite structure with separate grains. And the sintering temperature of the LNT ceramics could be lowered to around 900°C by adding a small amount of V₂O₅ without much degradation in microwave dielectric properties. Typically, better microwave dielectric properties of ɛ_r=41.7, Q × f =7820 GHz, and τ _f =45 ppm/°C could be obtained for the 1 wt% V₂O₅-doped ceramics sintered at 900°C.     

Effect of Li2CO3 Addition on the Sintering Temperature and Microwave Dielectric Properties of Mg2V2O7 Ceramics

Li₂CO₃ was added to Mg₂V₂O₇ ceramics in order to reduce the sintering temperature to below 900°C. At temperatures below 900°C, a liquid phase was formed during sintering, which assisted the densification of the specimens. The addition of Li₂CO₃ changed the crystal structure of Mg₂V₂O₇ ceramics from triclinic to monoclinic. The 6.0 mol% Li₂CO₃-added Mg₂V₂O₇ ceramic was well sintered at 800°C with a high density and good microwave dielectric properties of ɛ _r=8.2, Q × f =70 621 GHz, and τ_f=−35.2 ppm/°C. Silver did not react with the 6.0 mol% Li₂CO₃-added Mg₂V₂O₇ ceramic at 800°C. Therefore, this ceramic is a good candidate material in low-temperature co-fired ceramic multilayer devices.     

Effects of B2O3 on the Phase Stability of Ba2Ti9O20 Microwave Ceramic

Preparation of dense and phase-pure Ba₂Ti₉O₂₀ is generally difficult using solid-state reaction, since there are several thermodynamically stable compounds in the vicinity of the desired composition and a curvature of Ba₂Ti₉O₂₀ equilibrium phase boundary in the BaO–TiO₂ system at high temperatures. In this study, the effects of B₂O₃ on the densification, microstructural evolution, and phase stability of Ba₂Ti₉O₂₀ were investigated. It was found that the densification of Ba₂Ti₉O₂₀ sintered with B₂O₃ was promoted by the transient liquid phase formed at 840°C. At sintering temperatures higher than 1100°C, the solid-state sintering became dominant because of the evaporation of B₂O₃. With the addition of 5 wt% B₂O₃, the ceramic yielded a pure Ba₂Ti₉O₂₀ phase at sintering temperatures as low as 900°C, without any solid solution additive such as SnO₂ or ZrO₂. The facilities of B₂O₃ addition to the stability of Ba₂Ti₉O₂₀ are apparently due to the eutectic liquid phase which accelerates the migration of reactant species.     

Effect of Nb2O5/ZnO Addition on Microwave Properties of (Zr0.8Sn0.2)TiO4 Ceramics

The effects of Nb₂O₅ and ZnO addition on the dielectric properties, especially the quality factor, of (Zr_0.8Sn_0.2)TiO₄ (ZST) ceramics were investigated in terms of the sintered density acquired by the zinc. For ZST ceramics with 2 mol% added ZnO, the relative density of the samples decreased with >0.5 mol% addition of Nb₂O₅. On the other hand, for samples with 6 mol% added ZnO, the relative density remained >97%, even when the amount of Nb₂O₅ was increased to 2.0 mol%. When >0.5 mol% Nb₂O₅ was added, both the quality factor and the dielectric constant exhibited similar trends with sintered density. The ZST ceramics with 6 mol% added ZnO, especially, still manifested a quality factor >40 000 and a dielectric constant of 37, even when the amount of Nb₂O₅ was increased, values that are not explainable by the previously suggested electronic defect model.     

Effect of Alkali Metal Oxide Addition on the Sinterability of MgO–B2O3–Al2O3 Glass–Al2O3 Filler Composites

The sintering of a composite of MgO–B₂O₃–Al₂O₃ glass and Al₂O₃ filler is terminated due to the crystallization of Al₄B₂O₉ in the glass. The densification of a composite of MgO–B₂O₃–Al₂O₃ glass and Al₂O₃ filler using pressureless sintering was accomplished by lowering the sintering temperature of the composite. The sintering temperature was lowered by the addition of small amounts of alkali metal oxides to the MgO–B₂O₃–Al₂O₃ glass system. The resultant composite has a four-point bending strength of 280 MPa, a coefficient of thermal expansion (RT—200°C) of 4.4 × 10⁻⁶ K⁻¹, a dielectric constant of 6.0 at 1 MHz, porosity of approximately 1%, and moisture resistance.     

Effects of Heating Rate on the Sintering Behavior and the Dielectric Properties of Ba0.7Sr0.3TiO3 Ceramics Prepared by Boron-Containing Liquid-Phase Sintering

The effects of heating rate on the sintering behavior and the dielectric properties of Ba_0.7Sr_0.3TiO₃ ceramics prepared by boron-containing liquid-phase sintering were investigated. When 0.5 wt% B₂O₃ was added to Ba_0.7Sr_0.3TiO₃, sintering was achieved at ∼1150°C, and the overdoped B₂O₃ did not form an adequate amount of liquid phase or volatilize; it remained in the samples and formed a secondary phase. A transition broadening was observed as the heating rate increased. As the heating rate increased, the Curie temperature increased and the maximum dielectric constant ( k _max) at the Curie temperature decreased. This result is attributable to a decrease in the diffuseness parameter (δ) and the tetragonality ( c / a ).     

Effect of V2O5 Doping on the Sintering and Dielectric Properties of M-Phase Li1+x−yNb1−x−3yTix+4yO3 Ceramics

The effect of the addition of V₂O₅ on the structure, sintering and dielectric properties of M -phase (Li_{1+ x − y} Nb_{1− x −3 y} Ti _x +4 _y )O₃ ceramics has been investigated. Homogeneous substitution of V⁵⁺ for Nb⁵⁺ was obtained in LiNb_{0.6(1− x )}V_{0.6 x} Ti_0.5O₃ for x ≤ 0.02. The addition of V₂O₅ led to a large reduction in the sintering temperature and samples with x = 0.02 could be fully densified at 900°C. The substitution of vanadia had a relatively minor adverse effect on the microwave dielectric properties of the M -phase system and the x = 0.02 ceramics had [alt epsilon]_r= 66, Q × f = 3800 at 5.6 GHz, and τ_f= 11 ppm/°C. Preliminary investigations suggest that silver metallization does not diffuse into the V₂O₅-doped M -phase ceramics at 900°C, making these materials potential candidates for low-temperature cofired ceramic (LTCC) applications.     

Low-Temperature Sintering Barium Titanate-Based X8R Ceramics with Nd2O3 Dopant and ZnO–B2O3 Flux Agent

To demonstrate that barium titanate-based ceramics could be sintered at a low temperature thus reducing the cost of capacitor production, systematic investigation has been made on the structure and dielectric properties of barium titanate-based X8R ceramics, doped with various Nd₂O₃ content and different ZnO–B₂O₃ solution as the sintering aids. The dielectric ceramic powder with good permittivity and low dielectric loss were obtained at a sintering temperature of 900°C, meeting X8R specifications. Transmission electron microscopy and EDS analysis shows a high concentration of Nd element in the boundary regions, which verifies the beneficial role of Nd in facilitating the formation of core-shell structure. The results also suggest that the developed BaTiO₃-based ceramics may serve as a promising candidate for fabricating cheap multilayer capacitors with pure Ag as inner electrode.     

High-Q Microwave Dielectric Materials Based on the Spinel Mg2TiO4

Composite ceramics based on the spinel Mg₂TiO₄ were prepared by a conventional mixed-oxide route. To achieve the temperature stabilization of the dielectric constant, each of the composites was added with 7 mol% CaTiO₃. The effect of the substitution of isovalent Co for Mg on the microstructure and the microwave dielectric properties of the composite ceramics was also investigated. A maximum Q × f value of around 150–160 THz was obtained for the undoped Mg₂TiO₄, whereas a reduced Q × f value was observed for an increase in the Co concentration in the system (1− x )Mg₂TiO₄− x Co₂TiO₄. Upon doping with 7 mol% CaTiO₃, the Q × f value passed through a maximum with increasing Co concentration. Adding ZnO–B₂O₃ to the composite system based on Co-doped Mg₂TiO₄ resulted in a reduction of the sintering temperature by 150°–200°C without any significant degradation in the Q × f value.