肉豆蔻酸/改性粉煤灰复合相变储能材料的制备及性能研究

以肉豆蔻酸(MA)为相变储能基材、改性粉煤灰为复合基底,采用熔融混合法制备了肉豆蔻酸/改性粉煤灰复合相变储能材料。利用TG/DTA与IR分析研究了复合相变储能材料的热性能与结构。结果表明:MA可均匀地嵌入改性粉煤灰的多孔结构中。经过400次储放热循环后,其相变温度和相变焓变化都不大,表现出较好的储热稳定性,有望在储能方面得到实际的应用。     

十六醇-癸酸/粉煤灰定形相变材料的制备及热性能分析

基于节能减排的重要性,采用实验的方法制备了1种十六醇与癸酸的低共熔相变材料,该材料的融化温度为25.5℃,潜热为203J·g-1,通过与作为封装基质的粉煤灰进行熔融,得到另一种相变储能材料,测得其熔点为22.7℃,潜热为70.51J·g-1,相变材料在粉煤灰中的质量分数为48%。SEM和比热分析表明,相变材料与粉煤灰有很好的相容性,复合后的相变材料比纯粉煤灰的比热高出1.07倍;经过500次凝固融化循环,其稳定性较好。添加质量分数为6%的石墨后,相变材料的冷凝与融化时间分别减少20%和15%,传热性能得到提高。实际应用测试表明,这种材料能起到很好的隔热保温作用。     

癸酸/膨胀珍珠岩复合相变储能材料的制备及性能研究

以癸酸为相变材料、膨胀珍珠岩为载体,采用真空吸附法将相变材料吸附到膨胀珍珠岩孔隙内,制备出癸酸/膨胀珍珠岩复合相变储能材料。采用SEM、FT-IR及DSC分别对复合相变储能材料的形貌、结构、相变温度和相变潜热进行表征。结果表明:癸酸能很好地吸附到膨胀珍珠岩的孔隙内,当癸酸的质量分数达到70%时,吸附量达到最大,起始相变温度为30.91℃,相变潜热达109.74J/g;癸酸与膨胀珍珠岩的复合为物理复合,没有改变癸酸的相变储能特性。     

硅藻土基定形相变复合材料的制备与热性能研究

以硅藻土为基材,在高温条件下物理吸附相变材料A,再经冷却、粉碎及真空干燥后制得硅藻土基定形相变复合材料,并对制得的硅藻土基定形相变复合材料的结构形貌、化学组成、热性能、粒径变化进行了测试。研究结果表明,相变材料A被成功吸附至硅藻土孔隙中,且没有发生其他化学变化,硅藻土基定形相变复合材料的熔融温度为143.53℃,熔融焓55.26kJ/kg,储热效率为55.08%,硅藻土对相变材料A的实际吸附率为91.67%;原硅藻土的平均粒径为1316nm,硅藻土基定形相变复合材料的平均粒径为971nm,具有良好的定形效果,在加热至相变材料熔融温度以上仍未发生渗漏。     

癸酸／膨胀珍珠岩复合相变储能材料的制备及性能研究

以癸酸为相变材料、膨胀珍珠岩为载体,采用真空吸附法将相变材料吸附到膨胀珍珠岩孔隙内,制备出癸酸／膨胀珍珠岩复合相变储能材料。采用SEM、FT-IR及DSC分别对复合相变储能材料的形貌、结构、相变温度和相变潜热进行表征。结果表明：癸酸能很好地吸附到膨胀珍珠岩的孔隙内,当癸酸的质量分数达到70％时,吸附量达到最大,起始相变...     

定形相变储能建筑材料的制备与热性能研究

采用真空浸渗的方法,将棕榈酸和十六醇的低共熔物(PA-HD)与膨胀珍珠岩(EP)结合,制备一种新型定形相变材料(PA-HD/EP).环境扫描电子显微镜测试显示相变材料PA-HD进入到珍珠岩的孔道结构中.棕榈酸和十六醇的低共熔物在膨胀珍珠岩的最佳浸渗量为58.0%(质量分数,下同),在此浸渗量下,即使是没有进行包覆,PA-HD也不会在发生相变时从EP中渗漏.差示扫描量热仪测试获得PA-HD/EP的熔点为41.49℃,相变焓值为122.9J/g.通过在PA-HD/EP中添加10%石墨,改善材料的导热性能.该复合相变材料可以很好地与普通建筑材料进行结合,进一步制备成具有温度调节功能的建筑材料.     

复合相变储能材料的制备及热性能研究

基于建筑节能的重要性,采用实验的方法制备了一种癸酸与月桂酸的低共熔复合相变材料,这种相变材料的峰值融化温度是22.2℃,潜热是126.7℃,经过200次的循环以及释热特性测试发现这种复合相变材料的稳定性很好,再加入4%的石墨之后,导热性能有较大的提高。选用多孔建筑材料膨胀珍珠岩作为基质,用与相变材料直接浸泡的方式制得复合建筑材料,经过24h的浸泡,相变材料的质量分数达到了60%,用DSC测试出,复合材料的开始融化的温度17.9℃,潜热74.41J/g,做为一种新型的材料可以在节能建筑上使用。     

硬脂酸/改性硅藻土复合相变储能材料的制备及性能研究

以硬脂酸为相变储能材料,改性硅藻土为载体,无水乙醇为溶剂,采用溶液插层法制备了硬脂酸/改性硅藻土复合相变储能材料.利用综合热分析仪(TG-DSC)测定了复合材料的相变温度、相变潜热及复合材料的热稳定性,通过FT-IR对复合材料的兼容性进行了表征.结果表明,复合相变储能材料中硬脂酸的适宜含量为65%(质量分数),相变温度为61.6℃,相变潜热为142.87J/g,复合材料具有良好的热稳定性和兼容性.     

石蜡/改性硅藻土复合相变储能材料的制备及性能研究

以石蜡为相变储能材料,改性硅藻土为载体,无水乙醇为溶剂采用溶液插层法制备了石蜡/改性硅藻土复合相变储能材料,利用综合热分析仪(TG-DSC)测定了复合材料的相变温度、相变潜热及复合材料的热稳定性,通过扫描电镜(SEM)、FT-IR分别对复合材料的微观结构及兼容性进行了表征,结果表明:复合相变储能材料中石蜡的适宜含量为65%,此时相变温度为53.7℃,相变潜热为147.93J/g,复合材料具有良好的热稳定性和兼容性。     

癸酸-月桂酸/膨胀石墨相变储能材料的制备及性能研究

以癸酸-月桂酸低共熔物为相变材料,多孔石墨为基体,利用多孔石墨的吸附特性,制备出癸酸-月桂酸/膨胀石墨定形相变储能材料。采用DSC、ESEM、融化凝固过程分析对定形相变储能材料进行了结构和热性能研究。结果表明,癸酸-月桂酸被有效地包封在多孔石墨孔内,并且在定形相变材料中占80.47%(质量比);定形相变材料的相变温度为19.50℃,相变焓为93.18J/g;与癸酸-月桂酸相比,定形相变材料的导热性能有一定程度的提高。     

二元脂肪酸/硅藻土助滤剂定形相变复合材料的制备及性能

采用真空浸渗法制备了癸酸-月桂酸（CA-LA）/硅藻土助滤剂定形相变储热复合材料,对样品进行扩散-渗出圈测试、FTIR、SEM、BET、DSC和TG等表征分析,研究了硅藻土助滤剂对CA-LA二元低共熔脂肪酸的定形性能和吸附容量及CA-LA/硅藻土助滤剂定形相变复合材料的热物性、热稳定性和蓄放热性能。结果表明：无渗出圈产生的CA-LA/硅藻土助滤剂定形相变复合材料中,硅藻土助滤剂对CA-LA的吸附量约为49.88wt%,CA-LA/硅藻土助滤剂定形相变复合材料的相变温度和相变潜热分别为21.8℃和75.45 J/g;TG和热循环试验结果表明,CA-LA/硅藻土助滤剂定形相变复合材料具有良好的热稳定性,经历100次热循环后相变温度和相变潜热的变化量较小;蓄放热性能测试结果证明CA-LA/硅藻土助滤剂定形相变复合材料能够进行蓄热和释热,起到明显的调节和控制环境温度的作用,可应用在建筑节能和储热领域。     

储能相变材料制备方法研究进展

潜热储能是充分利用太阳能等洁净能源的一种有效方法,储能相变材料具有潜热存储密度高、相变时保持温度基本不变等特点,在清洁能源应用领域表现出广阔应用前景。从机械法、物理法和化学法等几方面总结了储能相变材料制备方法,同时分析了各种方法的特点。     

Preparation and thermal properties of form-stable palmitic acid/active aluminum oxide composites as phase change materials for latent heat storage

Form-stable palmitic acid (PA)/active aluminum oxide composites as phase change materials were prepared by adsorbing liquid palmitic acid into active aluminum oxide. In the composites, the palmitic acid was used as latent heat storage materials, and the active aluminum oxide was used as supporting material. Fourier transformation infrared spectroscope (FT-IR), X-ray diffractometer (XRD) and scanning electronic microscope (SEM) were used to determine the chemical structure, crystalloid phase and microstructure of the composites, respectively. The thermal properties and thermal stability were investigated by a differential scanning calorimeter (DSC) and a thermogravimetry analyzer (TGA). The FT-IR analyses results indicated that there is no chemical interaction between the palmitic acid and active aluminum oxide. The SEM results showed that the palmitic acid was well adsorbed into porous network of the active aluminum oxide. The DSC results indicated that the composites melt at 60.25 °C with a latent heat of 84.48 kJ kg⁻¹ and solidify at 56.86 °C with a latent heat of 78.79 kJ kg⁻¹ when the mass ratio of the PA to active aluminum oxide is 0.9:1. Compared with that of the PA, the melting and solidifying time of the composites CPCM5 was reduced by 20.6% and 21.4% because of the increased heat transfer rate through EG addition. The TGA results showed that the active aluminum oxide can improve the thermal stability of the composites.     

PMMA基复合定形相变储热材料的制备与性能研究

以聚甲基丙烯酸甲酯(PMMA)为支撑材料,石蜡(PA)、聚乙二醇(PEG 6000)和硬脂酸(SA)为相变材料(PCM),采用本体聚合法制备3种不同体系的复合定形相变储热材料,综合评价各复合体系的结构、热性能以及储/放热循环稳定性。结果表明:PMMA的交联网络结构使PCM在高于其熔化融温度时不发生泄漏;支撑材料与3种PCM均没有发生显著的化学反应;相同质量百分比的三类复合体系中,PMMA与PEG的界面相容性最好,SA/PMMA体系的储热能力最强,而PEG/PMMA体系的热稳定性最佳。     

相变储能材料的研究与发展

储能技术是通过物理或化学变化将某种能量存储,然后在后续过程中释放利用的技术,现多用于电力系统、交通运输、太阳能利用和移动电子等设备中,能够有效节约能源和提高能源利用率。相变储能材料是相变储能技术的关键载体,对其应用起着重要作用。本文对相变储能材料的基本特征、应用领域、储能原理以及分类等方面作了简要的介绍。并依据成分分类,对目前国内外研究的无机类、有机类、金属基及复合类相变储能材料进行了综述。详细介绍了不同材料的种类、性质、优缺点、适用范围等。最后指出了当前相变储能材料存在的不足,并展望了相变储能材料未来的发展方向和应用前景。     

静电纺PA-SA/PET/MWNTs复合相变纤维的制备及储热性能研究

以聚对苯二甲酸乙二酯(PET)、棕榈酸和硬脂酸二元低共熔物(PA-SA)和多壁碳纳米管(MWNTs)为原料,通过静电纺丝的方法制备了新型的PA-SA/PET/MWNTs定形相变复合纤维。研究了强酸处理后的MWNTs对静电纺PA-SA/PET/MWNTs复合相变纤维的形貌结构和储热性能的影响。FT-IR光谱分析表明,强酸处理后在MWNTs的表面成功的引入了羧基(-COOH)官能团。SEM观察表明,随着MWNTs的加入,复合相变纤维表面沟槽变得更加明显且纤维直径明显增大。DSC分析表明了MWNTs的含量对复合相变纤维的熔化焓值和结晶焓值有一定的影响,对熔化温度和结晶温度没有显著性的影响。     

二元脂肪酸/SiO2复合相变储能材料的制备与表征

针对适用于建筑领域的相变储能材料,选用癸酸(CA)分别与月桂酸(LA)、肉豆蔻酸(MA)和棕榈酸(PA)复合制备了二元低共熔脂肪酸作为储能材料。通过施罗德公式计算得到二元低共熔脂肪酸的混合比例和理论相变温度。基于CA-MA优异的性能,采用溶胶-凝胶法制备CA-MA/SiO2定形相变储能材料。采用FT-IR、SEM、DSC、TG对CA-MA/SiO2的结构、形貌、热性能和热稳定性进行了分析。结果表明,制备的3种二元低共熔脂肪酸适合于建筑领域。CA-MA较好地被固定在SiO2多孔网络中,储能材料和SiO2之间仅为物理结合,没有新物质的生成。定形相变储能材料的相变温度为20.96℃,相变焓为70.17J/g,相变温度适中,相变焓高,热稳定性好。     

有机/复合相变储能材料研究进展

相变储能材料在相变过程中实现能量的储存或释放,这种材料因具有优良的性能而成为近年来研究的热点.主要介绍了相变材料的分类、性质以及评价标准,着重讨论了有机/复合相变材料的一些常见的制备方法,如原位聚合法、界面聚合法、喷雾干燥法、多孔材料吸附法和溶胶-凝胶法等.概括了相变材料在太阳能利用、建筑材料、空调蓄冷、工业余热回收和军事伪装隐身等方面的应用研究,并提出了相变材料研究的未来发展趋势.     

凹凸棒土吸附相变储能复合材料制备及其热物理性能表征

基于凹凸棒土对有机物的良好吸附性能,以凹凸棒土为吸附介质、石蜡为吸附对象,制备有机/无机复合相变材料。由于有机相变材料被吸附到微孔中,使其相变在固定的空间内进行,从而避免了材料在液相状态下的流动和渗漏问题。试验结果显示,坡缕石占80%的凹凸棒土吸附石蜡的最优质量比为2∶1。DSC的测试显示,复合相变材料的焓变值与凹凸棒土和石蜡的吸附比例相关,凹凸棒土中坡缕石的含量越高,凹凸棒土的吸附能力就越强,复合相变材料的焓变值也就越大。温度循环试验的结果显示,复合相变材料具有良好的储(放)热性能,在环境温度上升和下降的过程中,能够储存和释放热量,这不仅增加了环境温度的惰性,也使能量能够在不同的时间和空间进行迁移,从而达到一定的节能效果。