戊二醛交联对CCMC/PVA复合膜性能的影响

采用流延成膜工艺制备了CCMC/PVA共混复合膜,研究了戊二醛交联剂对复合膜的透光性能和力学性能的影响。结果表明:交联处理膜的致密性和机械性能显著提高;当戊二醛添加量为2%(质量分数),体系的pH为10,交联反应温度为85℃,交联时间为35 min时,复合膜的拉伸强度可达18.91 MPa,断裂伸长率为226%,透光率为75%。     

乙二醛交联对明胶/PVA可生物降解复合膜性能的影响

采用流延成型法制备明胶/聚乙烯醇(Gel/PVA)复合膜,并以乙二醛为交联剂通过溶液交联法制备乙二醛交联的Gel/PVA复合膜,采用红外光谱(FTIR)、X-射线衍射(XRD)、差示扫描量热(DSC)、热重(TG)等表征交联前后复合膜的结构与性能,研究了交联剂用量对Gel/PVA复合膜力学性能及溶解性能的影响。结果表明,随着乙二醛用量的增加,Gel/PVA复合膜的拉伸强度呈先增加后逐渐降低的趋势,而断裂伸长率和溶解率则逐渐降低;乙二醛交联可提高复合膜的熔融温度及热稳定性;乙二醛交联显著影响Gel/PVA复合膜中分子间的氢键和化学结构。     

纳米蒙脱土负载茶多酚改性聚乙烯醇膜的制备及性能表征

目的 利用负载有茶多酚（TP）的蒙脱土（MMT）对聚乙烯醇（PVA）改性制备出PVA复合膜,以期改善纯PVA膜的综合性能,从而替代传统包装膜。方法 利用溶液流延法制备不同茶多酚（TP）质量分数的PVA/MMT复合膜（MMT添加量为PVA质量的3.0%）,测试其耐水性能、力学性能、水蒸气阻隔性能及抗氧化性能等。结果 当茶多酚质量分数为3.0%时,其溶胀率、溶解质量损失率分别约为532%和12.3%,水蒸气透过率系数约为1.0×10?10 g?m/(m2?Pa?s);抗张强度相对于PVA/MMT复合膜增强了约26%,断裂伸长率下降明显;PVA/MMT/TP复合膜的DPPH自由基清除率达到了65.5%。结论 采用蒙脱土负载茶多酚可有效改性PVA基复合膜。     

聚乙烯醇/合成硅酸镁锂纳米复合膜的制备研究

以聚乙烯醇(PVA)和合成硅酸镁锂为原料,采用溶液插层-流延成膜法制备了不同合成硅酸镁锂含量的PVA/合成硅酸镁锂纳米复合膜,并对PVA/合成硅酸镁锂纳米复合膜进行了表征。研究结果表明:6%(wt,质量分数)合成硅酸镁锂含量制得的PVA/合成硅酸镁锂纳米复合膜,结晶熔融温度达到253.1℃,平衡溶胀比为2.6,拉伸强度最大达到78MPa、断裂伸长率达到100%,耐水性、热性能和力学性能都得到明显改善。     

PVA-壳聚糖/有机累托石复合膜的结构与性能

目的将聚乙烯醇(PVA)引入壳聚糖(CS)/有机累托石(OREC)复合体系制备插层效果、力学性能、抗紫外老化及阻隔性能良好的插层纳米复合膜。方法利用溶液流延法制备PVA-CS/OREC系列复合膜,以XRD及SEM研究复合膜的插层结构及OREC在基体中的分散性,研究复合膜的力学性能、抗紫外辐射性及水蒸气透过性。结果 OREC及PVA添加量较少时可与CS形成良好的插层结构。当OREC质量分数为2%,PVA质量分数为10%时的复合膜(标记为PVA10-CS/OREC2)插层结构最好,OREC在CS及PVA基体中分散性最好,与OREC质量分数为2%且不含PVA的复合膜(标记为CS/OREC2)相比,拉伸强度提高42.2%,断裂伸长率提高30%,水蒸气透过量降低10.2%,复合膜经紫外辐射后拉伸强度保持率、断裂伸长保持率仍达82.5%及68.2%。结论 PVA10-CS/OREC2膜可作为医用膜和药品、食品等的包装材料。     

聚乙烯醇/磺化聚醚醚酮/对氨基二苯胺电活性复合膜的制备与性能

以聚乙烯醇(PVA)、磺化聚醚醚酮(SPEEK)和对氨基二苯胺(p-ADA)为原料,通过水溶液流延成膜法制备了PVA/SPEEK/p-ADA电活性复合膜。借助核磁共振谱(1 H-NMR)、红外光谱(FTIR)和X射线光电子能谱(XPS)分别对SPEEK和复合膜的化学结构进行了表征。采用万能材料试验机和电化学综合站分别对复合膜的力学性能和电性能进行分析测试。结果表明,当PVA含量为60%(质量分数)、SPEEK含量为35%(质量分数)、p-ADA含量为5%(质量分数)时复合膜的力学性能最佳,拉伸强度和弹性模量分别达到64 MPa和2 538 MPa,较纯PVA分别提高了52%和122%。电压窗口为-0.8~0.8 V时,PVA-60%/SPEEK-35%/p-ADA-5%复合膜具有明显的电活性,并且该电活性复合膜在外界酸碱环境发生改变时具有变色性。     

交联羧甲基玉米淀粉／PVA复合膜制备工艺的研究

以玉米淀粉为原料,采用先醚化后交联改性工艺合成了交联羧甲基玉米淀粉(CCMS).通过改性淀粉与聚乙烯醇(PVA)溶液共混反应,并辅以增塑剂、增强荆、交联剂及疏水化改性剂等加工助荆制备了性能优异的CCMS/PvA复合膜.研究了复合膜制备过程中的影响因素及其对薄膜耐水性能、透光性能和力学性能的影响.结果表明,当交联羧甲基玉米淀粉与PVA的质量比为7:3,甘油用量为10%(质量分数),复合交联剂用量3.3%(质量分数),疏水化改性荆聚酰胺多胺环氧氯丙烷树脂(PPE)用量为1.5%(质量分数),溶液pH为10,反应温度88℃,反应时间35min时,淀粉膜的拉伸强度为40.5MPa,断裂伸长率为311%,透光率为82%,吸水率最小为3.6%(质量分数).     

可降解抑菌功能薄膜的制备及性能研究

目的研究可降解抑菌功能薄膜的制备及性能。方法将具有抗菌性能的丝瓜络纤维浸提液(LF)、微晶棉纤维素(MCC)粉末、聚乙烯醇(PVA)和乙烯醋酸乙烯酯共聚物(EVA)乳液进行不同比例的共混,采用水溶液流延成膜的方法制备出可控制释放LF抗菌剂的可降解薄膜,并研究薄膜的抗菌性能和生物降解性能。结果流延膜中LF的浓度越大,薄膜缓释出的鞣质及甙类物质的浓度越高,对微生物的抑制作用也越强,但当LF的质量分数高于25%时,薄膜的基本性能会受到影响。当LF/MCC添加量(质量分数)为20%时,与对照组相比,流延薄膜的抗菌性相对提高61.5%,堆肥条件下20 d后有44.8%的成分可发生降解。结论该包装薄膜属于较理想的生物降解材料。     

高直链玉米淀粉基复合膜的制备

以高直链玉米淀粉为原料,选用甘油为增塑剂,乙二醛为交联剂,采用流延法制备淀粉/聚乙烯醇(PVA)复合膜。研究不同直链淀粉含量、增塑剂种类和用量、交联剂种类和用量、烘干温度等因素对复合膜性能的影响,并使用扫描电镜(SEM)观察膜的微观形态。结果表明,高直链淀粉复合膜的性能明显优于普通淀粉复合膜。当聚乙烯醇、甘油、乙二醛用量分别为40%、16%和12%,反应温度和烘干温度分别为90℃、70℃时,复合膜性能最佳。     

氧化石墨烯/聚乙烯醇复合膜的性能研究

通过化学氧化法制备了氧化石墨烯(GO),采用溶液共混法和流延成膜法制备了氧化石墨烯/聚乙烯醇(GO/PVA)复合膜。采用红外光谱、X射线衍射、水蒸汽透过仪和高阻计研究了复合膜的结构、水蒸汽透过性和电性能,并对复合膜的溶解性进行了研究。结果表明:当GO在PVA中的固含量达到4%(质量分数)时,GO/PVA复合膜的结晶度最高,水蒸汽透过率达到最低值,耐溶解性最好。     

多糖类天然高分子/PVA可生物降解共混膜的研究进展

目的综述天然高分子(淀粉、羧甲基纤维素、壳聚糖、海藻酸钠和木质素)与聚乙烯醇(PVA)复合制备可生物降解共混膜的方法及性能的研究进展。方法分类讨论淀粉、羧甲基纤维素、壳聚糖、海藻酸钠、木质素分别与PVA进行共混制备共混膜的方法及应用。结果总结了多糖类天然高分子/PVA共混膜的研究与应用进展,并指出了该类共混膜今后发展的方向。结论多糖类天然高分子/PVA可生物降解共混膜的研究是目前科研的热点之一,该共混膜对降低环境污染和节约能源具有重要的意义,具有广阔的应用前景。     

海藻酸钠/聚乙烯醇共混膜的制备及表征

用溶液共混法制备海藻酸钠/聚乙烯醇(SA/PVA)共混膜,并对其进行了IR、DSC表征和吸水率、透气率、力学性能等测定.结果表明,在这种由两种可生物降解的高聚物共混而成的共混膜中,PVA与SA分子链间有一定的相互作用,相容性好;共混膜有较高的抗水性和较好的综合力学性能.     

高速搅拌对淀粉／聚乙烯醇共混物薄膜性能的影响

通过高速搅拌，将淀粉与聚乙烯醇进行溶液共混，制备了淀粉／ＰＶＡ共混薄膜。测定了高速搅拌前后共混薄膜的力学性能。透明性，耐水性及生物降解性。结果表明，高速搅拌改善了淀粉／ＰＶＡ薄膜的力学性能，透明性与耐水性，并可提高共混膜的全用稳定性。     

Investigation of a novel freeze-thaw process for the production of drug delivery hydrogels

Poly(vinyl alcohol) (PVA) is a water-soluble, biocompatible and biodegradable polymer, which has been widely applied in biomedical fields. In this paper, novel physically cross-linked hydrogels composed of PVA and comprising a blend of poly(vinyl alcohol) (PVA) with different concentrations of HCl, NaOH and NaCl are prepared by a freezing/thawing treatment of aqueous solutions. The structure and complexation of the electrolytes were studied by Fourier transform infrared (FTIR) spectroscopy. The mechanical properties were investigated using rheometery and the thermal transitions of the hydrogels were examined by modulated differential scanning calorimetry (MDSC). Freeze/thawed PVA gels containing NaOH showed overall enhanced swelling with increased mechanical strength over traditional gels prepared by chemical or irradiative crosslinking techniques. These novel physically cross-linked hydrogels show promise for a variety of biomedical and drug delivery applications.     

Polysaccharide nanofibrous scaffolds as a model for in vitro skin tissue regeneration

Tissue engineering and nanotechnology have advanced a general strategy combining the cellular elements of living tissue with sophisticated functional biocomposites to produce living structures of sufficient size and function at a low cost for clinical relevance. Xylan, a natural polysaccharide was electrospun along with polyvinyl alcohol (PVA) to produce Xylan/PVA nanofibers for skin tissue engineering. The Xylan/PVA glutaraldehyde (Glu) vapor cross-linked nanofibers were characterized by SEM, FT-IR, tensile testing and water contact angle measurements to analyze the morphology, functional groups, mechanical properties and wettability of the fibers for skin tissue regeneration. The cell-biomaterial interactions were studied by culturing human foreskin fibroblasts on Xylan/PVA Glu vapor cross-linked and Xylan/PVA/Glu blend nanofibrous scaffolds. The observed results showed that the mechanical properties (72 %) and fibroblast proliferation significantly increased up to 23 % (P < 0.05) in 48 h Glu vapor cross-linked nanofibers compared to 24 h Glu vapor cross-linked Xylan/PVA nanofibers. The present study may prove that the natural biodegradable Xylan/PVA nanofibrous scaffolds have good potential for fibroblast adhesion, proliferation and cell matrix interactions relevant for skin tissue regeneration.     

交联剂对玉米淀粉醋酸酯/PVA可降解复合膜性能的影响

制备了低酯化度玉米淀粉醋酸酯(SA)(DS<0.2)/聚乙烯醇(PVA)可降解复合膜,重点讨论了交联剂的种类、用量、交联反应温度及时间对复合膜力学性能和耐水性的影响。并利用扫描电镜(SEM)X射线衍射(XRD)、热重分析(TG),对复合膜的形貌、结晶度、热稳定性进行表征。结果表明:经过交联后的复合膜,致密性提高,结晶度降低,热稳定性有所增强,表现出更好的力学性能和耐水性。     

纳米纤维素晶体和柠檬酸改性聚乙烯醇薄膜的制备及性能

以球形纳米纤维素晶体(NCC)作增强相、柠檬酸作交联剂对聚乙烯醇(PVA)进行改性,制备了PVA/NCC纳米复合薄膜和柠檬酸交联PVA/NCC纳米复合薄膜。通过热重分析、差热分析、吸水实验和拉伸实验考察了NCC的添加和柠檬酸的交联对薄膜热性能、耐水性和力学性能的影响。结果表明,与纯PVA薄膜相比,改性PVA薄膜的起始分解温度升高、熔融/结晶峰向高温方向移动、吸水率降低;只用NCC或柠檬酸对PVA改性时,所得PVA/NCC纳米复合薄膜、柠檬酸交联PVA薄膜的力学性能均对环境湿度敏感;同时用NCC(m(NCC)/m(PVA)=6/100)和柠檬酸(m(柠檬酸)/m(PVA)=3/100或m(柠檬酸)/m(PVA)=4.5/100)对PVA改性时,所得柠檬酸交联PVA/NCC纳米复合薄膜的力学性能不随环境湿度变化。     

聚乳酸/酯化纤维素纳米晶体共混膜性能研究

以聚乳酸(PLA)为基体,酯化纤维素纳米晶体(ECNC)为添加剂,制备了PLA/ ECNC共混膜。探讨了原始纤维素纳米晶体(CNC)与ECNC对PLA膜的透光率、表面形貌、热稳定性、亲疏水性及力学性能的影响。结果表明,与CNC相比,ECNC与PLA的相容性提高,透光率、热稳定性及力学性能也显著增强;经酯化的纤维素纳米晶体能降低CNC的亲水性,从而增强与PLA的界面黏合力,使CNC在PLA共混膜中的质量分数由小于1%提高到5%。该PLA/ECNC共混膜在包装塑料领域具有潜力,为制备出性能更加优良的可降解包装用塑料提供了一种简单可行的方法。     

茯苓–聚乙烯醇抑菌膜的制备及生物可降解动力学评价

目的 以可降解材料聚乙烯醇为基材,通过添加茯苓溶液,制备出复合抑菌薄膜,研究不同浓度茯苓对共混膜理化性能和功能性能的影响。方法 采用溶剂浇铸法制备茯苓/PVA共混膜。对共混膜的物理力学性能,以及溶解度、透光率、抑菌性、可降解性进行检测。利用红外光谱、扫描电镜对其结构进行分析表征。结果 茯苓的添加削弱了PVA分子间作用力,显著提高了断裂伸长率,由202.77%增加到398.82%,降低了拉伸强度,并且茯苓与PVA之间形成氢键,减少了水分对薄膜的溶解,薄膜溶解度由100%降到38.21%。随着茯苓质量分数的增加,薄膜的透光率下降,抑菌性得到增强。土壤降解实验表明茯苓/PVA共混膜具有良好的生物降解性。结论 制备的茯苓/PVA共混膜的力学性能和耐水性均得到提高,并且复合膜具有一定的抑菌性和可降解性。文中制备的复合膜为食品包装提供了理想选择。