Synthesis of spherical Li[Ni(1/3−z)Co(1/3−z)Mn(1/3−z)Mgz]O2 as positive electrode material for lithium-ion battery

Li[Ni_(1/3−z)Co_(1/3−z)Mn_(1/3−z)Mg_z]O₂ (z = 0, 0.04) positive electrode materials were synthesized via a co-precipitation method. These materials have α-NaFeO₂ () structure, as confirmed by X-ray diffraction (XRD) studies. Cation mixing in Li layer seemed to be decreased by Mg substitution as examined by Rietveld refinements of XRD data. Spherical morphologies were observed for the as-synthesized final products by scanning electron microscopy. Their electrochemical properties during charge and discharge were discussed. When magnesium ions are substituted, the initial reversible capacity reduced. However, the substitution for Mn sites in Li[Ni_1/3Co_1/3Mn_1/3]O₂ did not decrease the capacity because Mn sites substitution did not result in loss of electroactive elements in the compound. Differential scanning calorimetric studies showed the exothermic peaks of the charged electrode Li[Ni_(1/3−z)Co_(1/3−z)Mn_(1/3−z)Mg_z]O₂ (z = 0.04) were significantly smaller than that of Li[Ni_1/3Co_1/3Mn_1/3]O₂, which means that thermal stability was greatly improved by Mg substitution even at highly delithiated state.     

Synthesis of LiNi1/3Co1/3Mn1/3O2 cathode materials by using a supercritical water method in a batch reactor

LiNi_1/3Co_1/3Mn_1/3O₂ and LiCoO₂ cathode materials were synthesized by using a supercritical water (SCW) method with a metal salt solution in a batch reactor. Stoichiometric LiNi_1/3Co_1/3Mn_1/3O₂ was successfully synthesized in a 10-min reaction without calcination, while overlithiated LiCoO₂ (Li_1.15CoO₂) was synthesized using the batch SCW method. The physical properties and electrochemical performances of LiNi_1/3Co_1/3Mn_1/3O₂ were compared to those of Li_1.15CoO₂ by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), and charge/discharge cycling tests. The XRD pattern of LiNi_1/3Co_1/3Mn_1/3O₂ was found to be similar to that of Li_1.15CoO₂, showing clear splitting of the (0 0 6)/(1 0 2) and (1 0 8)/(1 1 0) peak pairs as particular characteristics of the layered structure. In addition, both cathode powders showed good crystallinity and phase purity, even though a short reaction time without calcination was applied to the SCW method. The initial specific discharge capacities of the Li_1.15CoO₂ and LiNi_1/3Co_1/3Mn_1/3O₂ powders at a current density of 0.24 mA/cm² in 2.5-4.5 V were 149 and 180 mAh/g, and their irreversible capacity loss was 20 and 17 mAh/g, respectively. The discharge capacities of the Li_1.15CoO₂ and LiNi_1/3Co_1/3Mn_1/3O₂ powders decreased with cycling and remained at 108 and 154 mAh/g after 30 cycles, which are 79% and 89% of the initial capacities. Compared to the overlithiated LiCoO₂ cathode powders, the LiNi_1/3Co_1/3Mn_1/3O₂ cathode powders synthesized by SCW method had better electrochemical performances.     

Synthetic optimization of spherical Li[Ni1/3Mn1/3Co1/3]O2 prepared by a carbonate co-precipitation method

A carbonate co-precipitation method was employed to prepare spherical Li[Ni_1/3Co_1/3Mn_1/3]O₂ cathode material. The precursor, [Ni_1/3Co_1/3Mn_1/3]CO₃, was prepared using ammonia as chelating agent under CO₂ atmosphere. The spherical Li[Ni_1/3Co_1/3Mn_1/3]O₂ was prepared by mixing the precalcined [Ni_1/3Co_1/3Mn_1/3]CO₃ with LiOH followed by high temperature calcination. The preparation conditions such as ammonia concentration, co-precipitation temperature, calcination temperature and Li/[Ni_1/3Co_1/3Mn_1/3] ratio were varied to optimize the physical and electrochemical properties of the prepared Li[Ni_1/3Co_1/3Mn_1/3]O₂. The structural, morphological, and electrochemical properties of the prepared LiNi_1/3Co_1/3Mn_1/3O₂ were characterized by XRD, SEM, and galvanostatic charge-discharge cycling. The optimized material has a spherical particle shape and a well ordered layered structure, and it also has an initial discharge capacity of 162.7 mAh g^− 1 in a voltage range of 2.8-4.3 V and a capacity retention of 94.8% after a hundred cycles. The optimized ammonia concentration, co-precipitation temperature, calcination temperature, and Li/[Ni_1/3Co_1/3Mn_1/3] ratio are 0.3 mol L^− 1, 60 °C, 850 °C, and 1.10, respectively.     

A study on electrochemical characteristics of LiCoO2/LiNi1/3Mn1/3Co1/3O2 mixed cathode for Li secondary battery

In this study, the LiCoO₂/LiNi_1/3Mn_1/3Co_1/3O₂ mixed cathode electrodes were prepared and their electrochemical performances were measured in a high cut-off voltage. As the contents of LiNi_1/3Mn_1/3Co_1/3O₂ in the mixed cathode increases, the reversible specific capacity and cycleability of the electrode enhanced, but the rate capability deteriorated. On the contrary, the rate capability of the cathode enhanced but the reversible specific capacity and cycleability deteriorated, according to increasing the contents of LiCoO₂ in the mixed cathode. The cell of LiCoO₂/LiNi_1/3Mn_1/3Co_1/3O₂ (50:50, wt.%) mixed cathode delivers a discharge capacity of ca. 168 mAh/g at a 0.2 C rate. The capacity of the cell decreased with the current rate and a useful capacity of ca. 152 mAh/g was obtained at a 2.0 C rate. However, the cell shows very stable cycleability: the discharge capacity of the cell after 20th charge/discharge cycling maintains ca. 163 mAh/g.     

Effect of fluorine in the preparation of Li(Ni1/3Co1/3Mn1/3)O2 via hydroxide co-precipitation

Uniform and spherical Li(Ni_1/3Co_1/3Mn_1/3)O_(2−δ)F_δ powders were synthesized via NH₃ and F⁻ coordination hydroxide co-precipitation. The effect of F⁻ coordination agent on the morphology, structure and electrochemical properties of the Li(Ni_1/3Co_1/3Mn_1/3)O_(2−δ)F_δ were studied. The morphology, size, and distribution of (Ni_1/3Co_1/3Mn_1/3)(OH)_(2−δ)F_δ particle diameter were improved in a shorter reaction time through the addition of F⁻. The study suggested that the added F improves the layered characteristics of the lattice and the cyclic performance of Li(Ni_1/3Co_1/3Mn_1/3)O₂ in the voltage range of 2.8-4.6 V. The initial capacity of the Li(Ni_1/3Co_1/3Mn_1/3)O_1.96F_0.04 was 178 mAh g⁻¹, the maximum capacity was 186 mAh g⁻¹ and the capacity after 50 cycles was 179 mAh g⁻¹ in the voltage range of 2.8-4.6 V.     

Synthesis and electrochemical characteristics of Al2O3-coated LiNi1/3Co1/3Mn1/3O2 cathode materials for lithium ion batteries

LiNi_1/3Co_1/3Mn_1/3O₂ cathode materials have been coated with Al₂O₃ nano-particles using sol-gel processing to improve its electrochemical properties. The X-ray diffraction (XRD) pattern of the as-prepared Al₂O₃ nano-particles was indexed to the cubic structure of the γ-Al₂O₃ phase and had an average size of ∼4 nm. The XRD showed that the structure of LiNi_1/3Co_1/3Mn_1/3O₂ was not affected by the Al₂O₃ coating. However, the Al₂O₃ coatings on LiNi_1/3Co_1/3Mn_1/3O₂ improved the cyclic life performance and rate capability without decreasing its initial discharge capacity. These electrochemical properties were also compared with those of LiAlO₂-coated LiNi_1/3Co_1/3Mn_1/3O₂ cathode material. The electrochemical impedance spectroscopy (EIS) was studied to understand the enhanced electrochemical properties of the Al₂O₃-coated LiNi_1/3Co_1/3Mn_1/3O₂ compared to uncoated LiNi_1/3Co_1/3Mn_1/3O₂.     

The first cycle characteristics of Li[Ni1/3Co1/3Mn1/3]O2 charged up to 4.7 V

In this research, we studied the first cycle characteristics of Li[Ni_1/3Co_1/3Mn_1/3]O₂ charged up to 4.7 V. Properties, such as valence state of the transition metals and crystallographic features, were analyzed by X-ray absorption spectroscopy and X-ray and neutron diffractions. Especially, two plateaus observed around 3.75 and 4.54 V were investigated by ex situ X-ray absorption spectroscopy. XANES studies showed that the oxidation states of transition metals in Li[Ni_1/3Co_1/3Mn_1/3]O₂ are mostly Ni²⁺, Co³⁺ and Mn⁴⁺. Based on neutron diffraction Rietveld analysis, there is about 6% of all nickel divalent (Ni²⁺) ions mixed with lithium ions (cation mixing). Meanwhile, it was found that the oxidation reaction of Ni²⁺/Ni⁴⁺ is related to the lower plateau around 3.75 V, but that of Co³⁺/Co⁴⁺ seems to occur entire range of x in Li_1−x[Ni_1/3Co_1/3Mn_1/3]O₂. Small volume change during cycling was attributed to the opposite variation of lattice parameter “c” and “a” with charging-discharging.     

Molten salt synthesis of LiNi0.5Mn1.5O4 spinel for 5 V class cathode material of Li-ion secondary battery

Well-ordered high crystalline LiNi_0.5Mn_1.5O₄ spinel has been readily synthesized by a molten salt method using a mixture of LiCl and LiOH salts. Synthetic variables on the synthesis of LiNi_0.5Mn_1.5O₄, such as synthetic atmosphere, LiCl salt amount, synthetic temperature, and synthetic time, were intensively investigated. X-ray diffraction (XRD) patterns and scanning electron microscopic (SEM) images showed that LiNi_0.5Mn_1.5O₄ synthesized at 900 and 950 °C have cubic spinel structure () with clear octahedral dimension. LiNi_0.5Mn_1.5O₄ spinel phase began to decompose at around 1000 °C accompanied with structural and morphological degradation. LiNi_0.5Mn_1.5O₄ powders synthesized at 900 °C for 3 h delivered an initial discharge capacity of 139 mAh/g with excellent capacity retention rate more than 99% after 50 cycles.     

Preparation, morphology and electrochemical characteristics of LiNi1/3Mn1/3Co1/3O2 with LiF addition

LiNi_1/3Mn_1/3Co_1/3O₂ with LiF additives was prepared by a spray dry process, and characterized by XRD, SEM, TEM, ICP, XPS, EIS and charge-discharge testing. Although some of the LiF was lost during the preparation, the remaining LiF existed on the surface of the LiNi_1/3Mn_1/3Co_1/3O₂ particles and had little influence on its structure. The LiF addition could not only promote the combine of the particles and increase the tap density of the material, but also effectively improve the cyclic performance of LiNi_1/3Mn_1/3Co_1/3O₂ at high cutoff voltages (up to 4.7 V) and at a high current density. The EIS results suggest that the LiF presence could significantly suppress the increase in the charge transfer resistance that occurred during the charged storage state or after long cycling, which should be related to the improvement on the electrochemical properties.     

Evolution of the local structure and electrochemical properties of spinel LiNixMn2−xO4 (0 ≤ x ≤ 0.5)

A series of Ni substituted spinel LiNi_xMn_2−xO₄ (0 ≤ x ≤ 0.5) have been synthesized to study the evolution of the local structure and their electrochemical properties. X-ray diffraction showed a few Ni cations moved to the 8a sites in heavily substituted LiNi_xMn_2−xO₄ (x ≥ 0.3). X-ray photoelectron spectroscopy confirmed Ni²⁺ cations were partially oxidized to Ni³⁺. The local structures of LiNi_xMn_2−xO₄ were studied by analyzing the and A_1g Raman bands. The most compact [Mn(Ni)O₆] octahedron with the highest bond energy of Mn(Ni)O was found for LiNi_0.2Mn_1.8O₄, which showed a Mn(Ni)O average bond length of 1.790 Å, and a force constant of 2.966 N cm⁻¹. Electrolyte decomposition during the electrochemical charging processes increased with Ni substitution. The discharge capacities at the 4.1 and 4.7 V plateaus obeyed the linear relationships with respect to the Ni substitution with the slopes of −1.9 and +1.9, which were smaller than the theoretical values of −2 and +2, respectively. The smaller slopes could be attributed to the electrochemical hysteresis and the presence of Ni³⁺ in the materials.     

Synthesis and characterization of high-density non-spherical Li(Ni1/3Co1/3Mn1/3)O2 cathode material for lithium ion batteries by two-step drying method

Non-spherical Li(Ni_1/3Co_1/3Mn_1/3)O₂ powders have been synthesized using a two-step drying method with 5% excess LiOH at 800 °C for 20 h. The tap-density of the powder obtained is 2.95 g cm⁻³. This value is remarkably higher than that of the Li(Ni_1/3Co_1/3Mn_1/3)O₂ powders obtained by other methods, which range from 1.50 g cm⁻³ to 2.40 g cm⁻³. The precursor and Li(Ni_1/3Co_1/3Mn_1/3)O₂ are characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and scanning electron microscope (SEM). XPS studies show that the predominant oxidation states of Ni, Co and Mn in the precursor are 2⁺, 3⁺ and 4⁺, respectively. XRD results show that the Li(Ni_1/3Co_1/3Mn_1/3)O₂ material obtained by the two-step drying method has a well-layered structure with a small amount of cation mixing. SEM confirms that the Li(Ni_1/3Co_1/3Mn_1/3)O₂ particles obtained by this method are uniform. The initial discharge capacity of 167 mAh g⁻¹ is obtained between 3 V and 4.3 V at a current of 0.2 C rate. The capacity of 159 mAh g⁻¹ is retained at the end of 30 charge-discharge cycle with a capacity retention of 95%.     

Characterization of high tap density Li[Ni1/3Co1/3Mn1/3]O2 cathode material synthesized via hydroxide co-precipitation

Li[Ni_1/3Co_1/3Mn_1/3]O₂ cathode material for lithium ion batteries was prepared by mixing metal hydroxide, (Ni_1/3Co_1/3Mn_1/3)(OH)₂, with 6% excess LiOH followed by calcinations. The (Ni_1/3Co_1/3Mn_1/3)(OH)₂ with secondary particle of about 12 μm was prepared by hydroxide co-precipitation. The tap density of the obtained Li[Ni_1/3Co_1/3Mn_1/3]O₂ powder was 2.56 ± 0.21 g cm⁻³. The powder was characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), particle size distribution (PSD) and galvanostatic charge-discharge cycling. The XRD pattern of Li[Ni_1/3Co_1/3Mn_1/3]O₂ revealed a well ordered hexagonal layered structure with low cation mixing. Secondary particles with size of 13-14 μm and primary particles with size of about 1 μm can be identified from the SEM observations. In the voltage range of 2.8-4.3 V, the initial discharge capacity of the Li[Ni_1/3Co_1/3Mn_1/3]O₂ electrode was 166.6 mAh g⁻¹, and 96.5% of the initial capacity was retained after 50 charge-discharge cycling.     

Effect of synthesis condition on the structural and electrochemical properties of Li[Ni1/3Mn1/3Co1/3]O2 prepared by the metal acetates decomposition method

In order to get homogeneous layered oxide Li[Ni_1/3Mn_1/3Co_1/3]O₂ as a lithium insertion positive electrode material, we applied the metal acetates decomposition method. The oxide compounds were calcined at various temperatures, which results in greater difference in morphological (shape, particle size and specific surface area) and the electrochemical (first charge profile, reversible capacity and rate capability) differences. The Li[Ni_1/3Mn_1/3Co_1/3]O₂ powders were characterized by means of X-ray diffraction (XRD), charge/discharge cycling, cyclic voltammetry and SEM. XRD experiment revealed that the layered Li[Ni_1/3Mn_1/3Co_1/3]O₂ material can be best synthesized at temperature of 800 °C. In that synthesized temperature, the sample showed high discharge capacity of 190 mAh g⁻¹ as well as stable cycling performance at a current density of 0.2 mA cm⁻² in the voltage range 2.3-4.6 V. The reversible capacity after 100 cycles is more than 190 mAh g⁻¹ at room temperature.     

Comparative study of different crystallographic structure of LiNi0.5Mn1.5O4−δ cathodes with wide operation voltage (2.0-5.0 V)

LiNi_0.5Mn_1.5O_4−δ cathode materials with two different structures ( and P4₃32) were synthesized by ultrasonic spray pyrolysis method. The X-ray diffraction (XRD) data was confirmed that face-centered spinel () transformed into primitive simple cubic (P4₃32) structure by annealing process at 700 °C. In spite of two electrons operated cut-off voltage range between 2.0 and 5.0 V, LiNi_0.5Mn_1.5O₄ with P4₃32 structure has better electrochemical behaviors than the cathode with simple cubic structure. Ex situ XRD study of the electrode revealed that LiNi_0.5Mn_1.5O₄ (P4₃32) has reversible crystal transformation between fully lithiated state (2.0 V) and delithiated state (5.0 V) whereas LiNi_0.5Mn_1.5O_4−δ () showed irreversible phase transformed at two voltage region. The LiNi_0.5Mn_1.5O_4−δ () has voltage drop was occurred after 20th cycled compared without any voltage drop of the P4₃32 structure.     

One-step synthesis and improved electrochemical performance of Li(Ni1/3Co1/3Mn1/3)O2 by a modified radiated polymer gel method

We present the mechanism for the synthesis of a layered Li(Ni_1/3Co_1/3Mn_1/3)O₂ compound by a modified radiated gel method. Pure-phase Li(Ni_1/3Co_1/3Mn_1/3)O₂ material was achieved when the polymer gel was calcined at 900 °C between 15 and 30 h. The unit cell parameter c decreased, and a varied slightly with increased sintering time. Electrochemical characterization revealed that the optimized sample (25 h) had a high initial discharge capacity of 188 mAh/g (2.8-4.5 V, 20 mA/g), an excellent capacity retention of 90.1% after 30 cycles and a good rate performance.     

Hydrothermal synthesis of Li(Ni1/3Co1/3Mn1/3)O2 for lithium rechargeable batteries

Ultrafine powders of Li(Ni_1/3Co_1/3Mn_1/3)O₂ cathode materials for lithium-ion secondary batteries were prepared under mild hydrothermal conditions. The influence of the molar ratio of Li/(Ni + Co + Mn) was studied. The products were investigated by XRD, TEM and EDS. The final products were found to be well crystallized Li(Ni_1/3Co_1/3Mn_1/3)O₂ with an average particle size of about 10 nm.     

A delithiated LiNi0.65Co0.25Mn0.10O2 electrode material: A structural, magnetic and electrochemical study

A crystalline LiNi_0.65Co_0.25Mn_0.10O₂ electrode material was synthesized by the combustion method at 900 °C for 1 h. Rietveld refinement shows less than 3% of Li/Ni disorder in the structure. Lithium extraction involves only the Ni²⁺/Ni⁴⁺ redox couple while Co³⁺ and Mn⁴⁺ remain electrochemically inactive. No structural transition was detected during cycling in the whole composition range 0 < x < 1.0. Furthermore, the hexagonal cell volume changes by only 3% when all lithium was removed indicating a good mechanical stability of the studied compound. LiNi_0.65Co_0.25Mn_0.10O₂ has a discharge capacity of 150 mAh/g in the voltage range 2.5-4.5 V, but the best electrochemical performance was obtained with an upper cut-off potential of 4.3 V. Magnetic measurements reveal competing antiferromagnetic and ferromagnetic interactions - varying in strength as a function of lithium content - yielding a low temperature magnetically frustrated state. The evolution of the magnetic properties with lithium content confirms the preferential oxidation of Ni ions compared to Co³⁺ and Mn⁴⁺ during the delithiation process.