Improving the rate performance of LiFePO4 by Fe-site doping

LiFePO₄ doped by bivalent cation in Fe-sites show improved rate performance and cyclic stability. Under 10 C rate at room temperature, the capacities of LiFe_0.9M_0.1PO₄ (M = Ni, Co, Mg) maintain at 81.7, 90.4 and 88.7 mAh/g, respectively, in comparison with 53.7 mAh/g for undoped LiFePO₄ and 54.8 mAh/g for carbon-coated LiFePO₄ (LiFePO₄/C). The capacity retention is 95% after 100 cycles for doped samples while this value is only 70% for LiFePO₄ and LiFePO₄/C. Such a significant improvement in electrochemical performance should be partially related to the enhanced electronic conductivities (from 2.2 × 10⁻⁹ to <2.5 × 10⁻⁷ S cm⁻¹) and probably the mobility of Li⁺ ions in the doped samples.     

Synthesis and electrochemical properties of LiFe0.95VxNi0.05−xPO4/C cathode material for lithium-ion battery

In this study, crystalline LiFe_0.95V_xNi_0.05−xPO₄/C powders are successfully synthesized using the hydrothermal method. Materials characterization and the electrochemical performance of LiFe_0.95V_xNi_0.05−xPO₄/C are investigated. The structure, morphology, and electrochemical performances of the prepared samples are investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), cyclic voltammetry, and AC impedance. The XRD pattern indicates that the LiFe_0.95V_xNi_0.05−xPO₄/C powders are single-phased with an orthorhombic olivine structure. The LiFe_0.95V_0.05PO₄ sample has the highest capacity of 141 mAh g⁻¹, which is 6% higher than that of pure LiFePO₄ at 0.1 C. As the discharge rate increases to 10 C, the LiFe_0.95V_0.04Ni_0.01PO₄ sample has the highest capacity of 100 mAh g⁻¹, which is 18% higher than that of pure LiFePO₄. The CV results prove that the LiFe_0.95V_0.04Ni_0.01PO₄ cathode has high capacity and good cyclic performance caused by the high lithium-ion diffusion transport, which is improved by Ni and V doping.     

Direct-hydrothermal synthesis of LiFe<Subscript>1−<Emphasis Type="Italic">x</Emphasis></Subscript>Mn<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>PO<Subscript>4</Subscript> cathode materials

Carbon free LiFe_1−x Mn _x PO₄ (x = 0, 0.05, 0.1, 0.2, 0.4) cathode materials were prepared by a direct-hydrothermal process at 170 °C for 10 h. The structural and electrochemical properties of the samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), charge–discharge experiments, cyclic voltammetry (CV) and alternating current (AC) impedance spectroscopy. The electrochemical performance of LiFePO₄ prepared in this manner showed to be positively affected by Mn²⁺-substitution. Among the Mn²⁺-substitution samples, the LiFe_0.9Mn_0.1PO₄ exhibited an initial discharge capacity of 141.4 mA h g⁻¹ at 0.1 C, and the capacity fading is only 2.7% after 50 cycles.     

Yellowish green-emitting KSrPO4:Tb phosphors with various doping concentrations prepared by using microwave assisted sintering

KSr_1−xPO₄:xTb³⁺ phosphors with various concentrations (x = 0.05, 0.06, 0.07, 0.08) of Tb³⁺ ions were synthesized in succession by using microwave assisted sintering. The sintering condition was set at 1200 °C for 1 h in air. The microstructural and luminescent characteristics of KSrPO₄:Tb³⁺ phosphors were investigated and are discussed here. The XRD result shows that the prepared KSr_1−xPO₄:xTb³⁺ phosphors would have an impure phase as the Tb³⁺ ion increases to more than x = 0.06. The photoluminescence measurement shows that the series of the emission-state ⁵D₄ → ⁷F₆, ⁵D₄ → ⁷F₄, and ⁵D₄ → ⁷F₃, corresponding to the typical 4f → 4f intra-configuration forbidden transitions of Tb³⁺, are appeared and the major emission peak is around at 542 nm. Moreover, the maximum photoluminescence intensity is appeared when the molar concentration of Tb³⁺ is 0.06. The decay time value of the KSr_1−xPO₄:xTb³⁺ phosphors with x = 0.06 is about 0.27 ms.     

Spray pyrolysis synthesis of nanostructured LiFexMn2−xO4 cathode materials for lithium-ion batteries

A series of partially Fe-substituted lithium manganese oxides LiFe_xMn_2−xO₄ (0 ≦ x ≦ 0.3) was successfully synthesized by an ultrasonic spray pyrolysis technique. The resulting powders were spherical nanostructured particles which comprised the primary particles with a few tens of nanometer in size, while the morphology changed from spherical and porous to spherical and dense with increasing Fe substitution. The densification of particles progressed with the amount of Fe substitution. All the samples exhibited a pure cubic spinel structure without any impurities in the XRD patterns.The as-prepared powders were then sintered at 750 °C for 4 h in air. However, the particles morphology and pure spinel phase of LiFe_xMn_2−xO₄ powders did not change after sintering. The as-sintered powders were used as cathode active materials for lithium-ion batteries, and cycle performance of the materials was investigated using half-cells Li/LiFe_xMn_2−xO₄. The first discharge capacity of Li/LiFe_xMn_2−xO₄ cell in a voltage 3.5-4.4 V decreased as the value x increased, however these cells exhibited stable cycling performance at wide ranges of charge-discharge rates.     

Synthesis and electrochemical properties of Co-doped Li3V2(PO4)3 cathode materials for lithium-ion batteries

Co-doped Li₃V_2−xCo_x(PO₄)₃/C (x = 0.00, 0.03, 0.05, 0.10, 0.13 or 0.15) compounds were prepared via a solid-state reaction. The Rietveld refinement results indicated that single-phase Li₃V_2−xCo_x(PO₄)₃/C (0 ≤ x ≤ 0.15) with a monoclinic structure was obtained. The X-ray photoelectron spectroscopy (XPS) analysis revealed that the cobalt is present in the +2 oxidation state in Li₃V_2−xCo_x(PO₄)₃. XPS studies also revealed that V⁴⁺ and V³⁺ ions were present in the Co²⁺-doped system. The initial specific capacity decreased as the Co-doping content increased, increasing monotonically with Co content for x > 0.10. Differential capacity curves of Li₃V_2−xCo_x(PO₄)₃/C compounds showed that the voltage peaks associated with the extraction of three Li⁺ ions shifted to higher voltages with an increase in Co content, and when the Co²⁺-doping content reached 0.15, the peak positions returned to those of the unsubstituted Li₃V₂(PO₄)₃ phase. For the Li₃V_1.85Co_0.15(PO₄)₃/C compound, the initial capacity was 163.3 mAh/g (109.4% of the initial capacity of the undoped Li₃V₂(PO₄)₃) and 73.4% capacity retention was observed after 50 cycles at a 0.1 C charge/discharge rate. The doping of Co²⁺into V sites should be favorable for the structural stability of Li₃V_2−xCo_x(PO₄)₃/C compounds and so moderate the volume changes (expansion/contraction) seen during the reversible Li⁺ extraction/insertion, thus resulting in the improvement of cell cycling ability.     

Development of blue ceramic dyes from cobalt phosphates

In this study the development of blue ceramic dyes from compositions based on phosphate structures have been investigated. The replacement of cobalt by copper or iron to minimize the Co content have been considered. MFeO(PO₄) (M = Co, Cu) solid solutions have been obtained with Co_1−xCu_xFeOPO₄ (0 ≤ x ≤ 1) compositions prepared from gels and fired at 1000 °C/2 h. Co_1−xCu_xFeOPO₄ compositions are not indicated to minimize the Co content in ceramic dyes because they decompose in glazed samples and pinhole defect is obtained. From FeCoOPO₄–2FePO₄ compositions, Co₃Fe₄(PO₄)₆ structure introduces the Co²⁺ ions into glassy matrix and suitable blue materials are obtained. In the conditions of this study, optimal cobalt amount is about 10 wt% Co from Co_1−xFe_1+xO_1−x(PO₄)_1+x (x ≈ 0.6) compositions.     

Preparation and electrochemical properties of spherical LiFePO<Subscript>4</Subscript> and LiFe<Subscript>0.9</Subscript>Mg<Subscript>0.1</Subscript>PO<Subscript>4</Subscript> cathode materials for lithium rechargeable batteries

The spherical LiFePO₄/C and LiFe_0.9Mg_0.1PO₄/C powders were successfully prepared from spherical FePO₄ via a simple uniform-phase precipitation method at normal pressure, using FeCl₃ and H₃PO₄ as the reactants. The FePO₄, LiFePO₄/C, and LiFe_0.9Mg_0.1PO₄/C powders were characterized by scanning electron microscopies (SEM), powder X-ray diffraction (XRD), X-ray photoelectron spectrometer (XPS), and tap-density testing. The uniform spherical particles produced are amorphous, but they were crystallized to FePO₄ after calcining above 400 °C. Due to the homogeneity of the basic FePO₄, the final products, LiFePO₄/C and LiFe_0.9Mg_0.1PO₄/C, are also significantly uniform and the particle size is of about 1 μm in diameter. The tap-density of the spherical LiFePO₄/C and LiFe_0.9Mg_0.1PO₄/C are 1.75 and 1.77 g cm⁻³, respectively, which are remarkably higher than the non-spherical LiFePO₄ powders (the tap-density is 1.0–1.3 g cm⁻³). The excellent specific capacities of 148 and 157 mAh g⁻¹ with a rate of 0.1 C are achieved for the LiFePO₄/C and LiFe_0.9Mg_0.1PO₄/C, respectively. Comparison of the cyclic voltammograms of LiFePO₄/C and LiFe_0.9Mg_0.1PO₄/C shows enhanced redox current and reversibility for the sample substituting Mg on the Fe site. LiFe_0.9Mg_0.1PO₄/C exhibits better high-rate and cycle performances than the un-substituted LiFePO₄/C.     

In situ X-ray absorption spectroscopic study for the electrochemical delithiation of a cathode LiFe0.4Mn0.6PO4 material

The electronic and local atomic structural characterization of a promising cathode material, LiFe_0.4Mn_0.6PO₄, for a lithium rechargeable battery was performed by in situ X-ray absorption fine structure (XAFS) on both Mn and Fe K-edges. Upon delithiation, the X-ray absorption near edge structure (XANES) spectra analysis showed that the Fe²⁺/Fe³⁺ electrochemical reaction was two times faster than that of Mn²⁺/Mn³⁺. The Fe and Mn K-edge extended X-ray absorption fine structure (EXAFS) spectra were effectively altered with different spectral behaviors for the local atomic structure near Fe and Mn during delithiation. Alternatively, the EXAFS spectra of LiFePO₄ changed significantly and those of LiMnPO₄ were constant through all delithiations for the corresponding reference materials of LiFePO₄ and LiMnPO₄. The present study with XAFS characterization demonstrates that initially delithiated Fe-rich domains at 3.5 V can promote more effective local structural change of the neighboring Mn-rich domains during the next second plateau at 4.1 V, which can ease delithiation in the Mn-rich domains through more flexible reaction of the local structure in the Mn octahedra.     

Preparation and characterization of nano-particle LiFePO4 and LiFePO4/C by spray-drying and post-annealing method

Pure, nano-sized LiFePO₄ and LiFePO₄/C cathode materials are synthesized by spray-drying and post-annealing method. The influence of the sintering temperature and carbon coating on the structure, particle size, morphology and electrochemical performance of LiFePO₄ cathode material is investigated. The optimum processing conditions are found to be thermal treatment for 10 h at 600 °C. Compared with LiFePO₄, LiFePO₄/C particles are smaller in size due to the inhibition of crystal growth to a great extent by the presence of carbon in the reaction mixture. And that the LiFePO₄/C composite coated with 3.81 wt.% carbon exhibits the best electrode properties with discharge capacities of 139.4, 137.2, 133.5 and 127.3 mAh g⁻¹ at C/5, 1C, 5C and 10C rates, respectively. In addition, it shows excellent cycle stability at different current densities. Even after 50 cycles at the high current density of 10C, a discharge capacity of 117.7 mAh g⁻¹ is obtained (92.4% of its initial value) with only a low capacity fading of 0.15% per cycle.     

Evolution of the local structure and electrochemical properties of spinel LiNixMn2−xO4 (0 ≤ x ≤ 0.5)

A series of Ni substituted spinel LiNi_xMn_2−xO₄ (0 ≤ x ≤ 0.5) have been synthesized to study the evolution of the local structure and their electrochemical properties. X-ray diffraction showed a few Ni cations moved to the 8a sites in heavily substituted LiNi_xMn_2−xO₄ (x ≥ 0.3). X-ray photoelectron spectroscopy confirmed Ni²⁺ cations were partially oxidized to Ni³⁺. The local structures of LiNi_xMn_2−xO₄ were studied by analyzing the and A_1g Raman bands. The most compact [Mn(Ni)O₆] octahedron with the highest bond energy of Mn(Ni)O was found for LiNi_0.2Mn_1.8O₄, which showed a Mn(Ni)O average bond length of 1.790 Å, and a force constant of 2.966 N cm⁻¹. Electrolyte decomposition during the electrochemical charging processes increased with Ni substitution. The discharge capacities at the 4.1 and 4.7 V plateaus obeyed the linear relationships with respect to the Ni substitution with the slopes of −1.9 and +1.9, which were smaller than the theoretical values of −2 and +2, respectively. The smaller slopes could be attributed to the electrochemical hysteresis and the presence of Ni³⁺ in the materials.     

Effect of surface modified porous inorganic-organic hybrid polyphosphazene nanotubes on the properties of polyethylene oxide based solid polymer electrolytes

2-(2-methyloxyethoxy)ethanol modified poly (cyclotriphosphazene-co-4,4′-sufonyldiphenol) (PZS) nanotubes were synthesized and solid composite polymer electrolytes based on the surface modified polyphosphazene nanotubes added to PEO/LiClO₄ model system were prepared. Differential Scanning Calorimetry (DSC) and Scanning Electron Microscopy (SEM) were used to investigate the characteristics of the composite polymer electrolytes (CPE). The ionic conductivity, lithium ion transference number and electrochemical stability window can be enhanced after the addition of surface modified PZS nanotubes. The electrochemical investigation shows that the solid composite polymer electrolytes incorporated with PZS nanotubes have higher ionic conductivity and lithium ion transference number than the filler SiO₂. Maximum ionic conductivity values of 4.95 × 10⁻⁵ S cm⁻¹ at ambient temperature and 1.64 × 10⁻³ S cm⁻¹ at 80 °C with 10 wt % content of surface modified PZS nanotubes were obtained and the lithium ion transference number was 0.41. The good chemical properties of the solid state composite polymer electrolytes suggested that the inorganic-organic hybrid polyphosphazene nanotubes had a promising use as fillers in solid composite polymer electrolytes and the PEO₁₀-LiClO₄-PZS nanotubes solid composite polymer electrolyte can be used as a candidate material for lithium polymer batteries.     

One-step microwave synthesis and characterization of carbon-modified nanocrystalline LiFePO4

The precursors of LiFePO₄ were prepared by a sol-gel method using lithium acetate dihydrate, ferrous sulfate, phosphoric acid, citric acid and polyethylene glycol as raw materials, and then the carbon-modified nanocrystalline LiFePO₄ (LiFePO₄/C) cathode material was synthesized by a one-step microwave method with the domestic microwave oven. The effect of microwave time and carbon content on the performance of the resulting LiFePO₄/C material was investigated. Structural characterization by X-ray diffraction and scanning electron microscopy proved that the olivine phase LiFePO₄ was synthesized and the grain size of the samples was several hundred nanometers. Under the optimal conditions of microwave time and carbon content, the charge-discharge performance indicated that the nanosized LiFePO₄/C had a high electrochemical capacity at 0.2 C (152 mAh g⁻¹) and improved capacity retention; the exchange current density was 1.6977 mA cm⁻². Furthermore, the rate capability was improved effectively after LiFePO₄ was modified with carbon, with 59 mAh g⁻¹ being obtained at 20 C.     

Influence of the tetravalent cation on the high-voltage electrochemical activity of LiNi0.5M1.5O4 spinel cathode materials

The electrochemical properties of substituted LiNi_0.5Mn_1.5−xM_xO₄ spinels at high potential (>4 V vs Li⁺/Li) have been investigated for M = Ti and Ru, in order to determine the role of the tetravalent cation in such systems where nickel is a priori the only electroactive species. These systems are found to form extended solid solutions (up to x = 1.3 and x = 1.0 for Ti and Ru, respectively) that were characterized by X-ray diffraction and Raman spectroscopy. Titanium substitution induces a drastic decrease in high potential electrochemical capacity, whereas the capacity is maintained and the kinetics are even improved in the presence of ruthenium. These results are completed by new results on the Li_4−2xNi_3xTi_5−xO₁₂ spinel system, which shows not any high potential activity in spite of the presence of up to 0.5 Ni²⁺ per spinel formula unit on the octahedral site. Taking into account previous data on LiNi_0.5Ge_1.5O₄, we clearly show that even if the tetravalent cation does not participate in the overall redox reaction, electrochemical activity is only possible when nickel is surrounded by tetravalent cations able to accept a local variation of valence (Mn, Ru), whereas full-shell cations such as Ti⁴⁺ and Ge⁴⁺ block the necessary electron transfer pathways in the spinel oxide electrode.     

Synthesis and characterization of Pt-doped LiFePO4/C composites using the sol–gel method as the cathode material in lithium-ion batteries

LiFePO₄/C and LiFe_0.96Pt_0.04PO₄/C nanocomposite cathode materials were synthesized using the sol–gel method in a nitrogen atmosphere. The samples were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). Their electrochemical properties were investigated using galvanostatic charge/discharge tests, cyclic voltammetry (CV), and electrochemical impedance spectroscopy (EIS). The XRD results indicate that substituting iron with platinum does not destroy the structure of LiFePO₄, but expands the lattice parameters and enlarges the cell volume. The electrochemical results show that platinum doping improves the electrochemical performance of LiFePO₄/C particles owing to the expansion of the lattice structure, which provides more space for Li ion diffusion. The, larger lattice structure parameters of the LiFe_0.96Pt_0.04PO₄/C material result in a high discharge capacity of 166, 156, 142 and 140 mAh g^?1 at rates of 0.2, 1, 5, and 10 C, respectively, as compared to 164, 150, 120, and 105 mAh g^?1 for undoped LiFePO₄/C.     

Influence of carbon sources on LiFePO4/C composites synthesized by the high-temperature high-energy ball milling method

Carbon-coated LiFePO₄ composites were synthesized by a new method of high-temperature high-energy ball milling (HTHEBM). Fe₂O₃ and LiH₂PO₄ were used as raw materials. Glucose, sucrose, citric acid and active carbon were used as reducing agents and carbon sources, respectively. In this method, high-energy ball milling and carbon coating worked together and, therefore, fine and homogeneous LiFePO₄/C particles with excellent properties were obtained in a relatively short synthesis time of 9 h. Moreover, the synthesis process could be completely finished at a relatively lower temperature of 600 °C for high-energy ball milling transforming mechanical energy into thermal energy. The results of X-ray diffraction (XRD) analysis, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and electrochemical performance tests indicated that carbon source had an important influence on the properties of LiFePO₄/C composites synthesized by the HTHEBM method. It was proved that the LiFePO₄ composites coated with glucose had the best properties with 1 μm geometric mean diameter and 150.3 mA h g⁻¹ initial discharge capacity at a current rate of 0.1 C. After the 20th cycle test, the reversible capacity was 148 mA h g⁻¹ at 0.1 C, showing a retention ratio to the initial capacity of 98.5%.     

Preparation and cycling performance of Aland F co-substituted compounds Li4AlxTi5−xFyO12−y

Li₄Al_xTi_5−xF_yO_12−y compounds were prepared by a solid-state reaction method. Phase analyses demonstrated that both Al³⁺ and F⁻ ions entered the structure of spinel-type Li₄Ti₅O₁₂. Charge-discharge cycling results at a constant current density of 0.15 mA cm⁻² between the cut-off voltages of 2.5 and 0.5 V showed that the Al³⁺ and F⁻ substitutions improved the first total discharge capacity of Li₄Ti₅O₁₂. However, Al³⁺ substitution greatly increased the reversible capacity and cycling stability of Li₄Ti₅O₁₂ while F⁻ substitution decreased its reversible capacity and cycling stability slightly. The electrochemical performance of the Al³⁺-F⁻-co-substituted specimen was better than the F⁻-substituted one but worse than the Al³⁺-substituted one.     

Spray-drying synthesized lithium-excess Li4+xTi5−xO12−δ and its electrochemical property as negative electrode material for Li-ion batteries

Li₄Ti₅O₁₂ (Fd-3m space group) materials were synthesized by controlling the lithium and titanium ratios (Li/Ti) in the range of 0.800-0.900 by using a spray-drying method, followed by calcination at several temperatures between 700 and 900 °C for large-scale production. Chemical and structure studies of the final products were done by X-ray diffraction (XRD), neutron diffraction (ND), X-ray photon electron spectroscopy (XPS), scanning electron microscopy (SEM) and inductively coupled plasma mass spectrometry (ICP-MS). The optimum synthesis condition was examined in relation to the electrochemical characteristics including charge-discharge cycling and ac impedance spectroscopy. It was found that when the spray-drying precursors at the Li/Ti ratio of 0.860 were calcined at 700-900 °C for 12 h in air, a pure Li_4+xTi_5−xO_12−δ (x = 0.06-0.08) phase with a lithium-excess composition was obtained. Based on the structural studies, it was found that the excess lithium is located at the lithium and titanium layer of the 16d site in the spinel structure (Fd-3m). These pure Li_4+xTi_5−xO_12−δ (x = 0.06-0.08) phase materials showed a higher discharge capacity of ∼164 mAh g⁻¹ at 1.55 V (vs. Li/Li⁺), between the cut-off voltage of 1.2-3.0, with an excellent cyclability and superior rate performance in comparison with the Li₄Ti₅O₁₂ phase containing impurity phases.     

Enhanced electrochemical stability of Al-doped LiMn2O4 synthesized by a polymer-pyrolysis method

LiAl_xMn_2−xO₄ samples (x = 0, 0.02, 0.05, 0.08) were synthesized by a polymer-pyrolysis method. The structure and morphology of the LiAl_xMn_2−xO₄ samples calcined at 800 °C for 6 h were investigated by powder X-ray diffraction and scanning electron microscopy. The results show that all samples have high crystallinity, regular octahedral morphology and uniform particle size of 100-300 nm. The electrochemical performances were tested by galvanostatic charge-discharge and cyclic voltammetry. The results demonstrate that the Al-doped LiMn₂O₄ can be very well cycled at an elevated temperature of 55 °C without severe capacity degradation. In particular, the LiAl_0.08Mn_1.92O₄ sample demonstrates excellent capacity retention of 99.3% after 50 cycles at 55 °C, confirming the greatly enhanced electrochemical stability of LiMn₂O₄ by a small quantity of Al-doping.     

Optimization of electrochemical properties of LiFePO4/C prepared by an aqueous solution method using sucrose

LiFePO₄ can be used as a positive electrode material for lithium-ion batteries by making composite with electrical conductive carbonaceous materials. In this study, LiFePO₄/C (carbon) composite was prepared by a soft chemistry route, in which sucrose was used as a carbon source of a low price. We tried to optimize a Li/(LiFePO₄/C) cell performance through changing synthetic conditions and discussed the factors affecting the electrochemical performances of the cell, such as the amount of the carbon source, synthetic temperature, gas flow rate of pyrolysis and the formation of secondary phases. It was found that the connection of the residual carbon and Fe₂P to LiFePO₄ particles and the amount of these two phases were important factors. In our experimental conditions, LiFePO₄/C including 9.72 wt.% of residual carbon, prepared at 800 °C for 12 h showed the highest reversible capacity and the best C rate performance among the synthesized materials; 130 mAh g⁻¹ at 10C rate and 50 °C.