Synthesis and electrochemical properties of Co-doped Li3V2(PO4)3 cathode materials for lithium-ion batteries

Co-doped Li₃V_2−xCo_x(PO₄)₃/C (x = 0.00, 0.03, 0.05, 0.10, 0.13 or 0.15) compounds were prepared via a solid-state reaction. The Rietveld refinement results indicated that single-phase Li₃V_2−xCo_x(PO₄)₃/C (0 ≤ x ≤ 0.15) with a monoclinic structure was obtained. The X-ray photoelectron spectroscopy (XPS) analysis revealed that the cobalt is present in the +2 oxidation state in Li₃V_2−xCo_x(PO₄)₃. XPS studies also revealed that V⁴⁺ and V³⁺ ions were present in the Co²⁺-doped system. The initial specific capacity decreased as the Co-doping content increased, increasing monotonically with Co content for x > 0.10. Differential capacity curves of Li₃V_2−xCo_x(PO₄)₃/C compounds showed that the voltage peaks associated with the extraction of three Li⁺ ions shifted to higher voltages with an increase in Co content, and when the Co²⁺-doping content reached 0.15, the peak positions returned to those of the unsubstituted Li₃V₂(PO₄)₃ phase. For the Li₃V_1.85Co_0.15(PO₄)₃/C compound, the initial capacity was 163.3 mAh/g (109.4% of the initial capacity of the undoped Li₃V₂(PO₄)₃) and 73.4% capacity retention was observed after 50 cycles at a 0.1 C charge/discharge rate. The doping of Co²⁺into V sites should be favorable for the structural stability of Li₃V_2−xCo_x(PO₄)₃/C compounds and so moderate the volume changes (expansion/contraction) seen during the reversible Li⁺ extraction/insertion, thus resulting in the improvement of cell cycling ability.     

Preparation and electrochemical performance studies on Cr-doped Li3V2(PO4)3 as cathode materials for lithium-ion batteries

Cr-doped Li₃V_2−xCr_x(PO₄)₃/C (x = 0, 0.05, 0.1, 0.2, 0.5, 1) compounds have been prepared using sol–gel method. The Rietveld refinement results indicate that single-phase Li₃V_2−xCr_x(PO₄)₃/C with monoclinic structure can be obtained. Although the initial specific capacity decreased with Cr content at a lower current rate, both cycle performance and rate capability have excited improvement with moderate Cr-doping content in Li₃V_2−xCr_x(PO₄)₃/C. Li₃V_1.9Cr_0.1(PO₄)₃/C compound presents an initial capacity of 171.4 mAh g⁻¹ and 78.6% capacity retention after 100 cycles at 0.2C rate. At 4C rate, the Li₃V_1.9Cr_0.1(PO₄)₃/C can give an initial capacity of 130.2 mAh g⁻¹ and 10.8% capacity loss after 100 cycles where the Li₃V₂(PO₄)₃/C presents the initial capacity of 127.4 mAh g⁻¹ and capacity loss of 14.9%. Enhanced rate and cyclic capability may be attributed to the optimizing particle size, carbon coating quality, and structural stability during the proper amount of Cr-doping (x = 0.1) in V sites.     

Mn influence on the electrochemical behaviour of Li3V2(PO4)3 cathode material

The role played by the substitution of Mn on the electrochemical behaviour of Li₃V₂(PO₄)₃ has been investigated. Independently of the synthesis route, the Mn doping improves the electrochemical features with respect to the undoped samples. Different reasons can be taken into consideration to explain the electrochemical enhancement. In the sol–gel synthesis the capacity slightly enhances due to the Mn substitution on both the V sites, within the solubility limit x = 0.124 in Li₃V_2−xMn_x(PO₄)₃. In the solid state synthesis the significant capacity enhancement is preferentially due to the microstructural features of the crystallites and to the LiMnPO₄ phase formation.     

Carbon coated Li3V2(PO4)3 cathode material prepared by a PVA assisted sol-gel method

Carbon coated Li₃V₂(PO₄)₃ cathode material was prepared by a poly(vinyl alcohol) (PVA) assisted sol-gel method. PVA was used both as the gelating agent and the carbon source. XRD analysis showed that the material was well crystallized. The particle size of the material was ranged between 200 and 500 nm. HRTEM revealed that the material was covered by a uniform surface carbon layer with a thickness of 80 Å. The existence of surface carbon layer was further confirmed by Raman scattering. The electrochemical properties of the material were investigated by charge-discharge cycling, CV and EIS techniques. The material showed good cycling performance, which had a reversible discharge capacity of 100 mAh g⁻¹ when cycled at 1 C rate. The apparent Li⁺ diffusion coefficients of the material ranged between 9.5 × 10⁻¹⁰ and 0.9 × 10⁻¹⁰ cm² s⁻¹, which were larger than those of olivine LiFePO₄. The large lithium diffusion coefficient of Li₃V₂(PO₄)₃ has been attributed to its special NASICON-type structure.     

A promising sol-gel route based on citric acid to synthesize Li3V2(PO4)3/carbon composite material for lithium ion batteries

Li₃V₂(PO₄)₃/carbon composite material was synthesized by a promising sol-gel route based on citric acid using V₂O₅ powder as a vanadium source. Citric acid acts not only as a chelating reagent but also as a carbon source, which enhance the conductivity of the composite material and hinder the growth of Li₃V₂(PO₄)₃ particles. The structure and morphology of the sample were characterized by TG, XRD and TEM measurements. XRD results reveal that Li₃V₂(PO₄)₃/carbon was successfully synthesized and has a monoclinic structure with space group P2₁/n. TEM images show Li₃V₂(PO₄)₃ particles are about 45 nm in diameter embeded in carbon networks. Galvanostatic charge/discharge and cyclic voltammetry measurements were used to study its electrochemical behaviors which indicate the reversibility of the lithium extraction/insertion processes. Li₃V₂(PO₄)₃/carbon performed in a voltage window (3.0-4.8 V) exhibits higher discharge capacity, better cycling stability and its discharge capacity maintains about 167.6 mAh/g at a current density of 28 mA/g after 50 cycles.     

Electrochemical performance of Li3V2(PO4)3/C cathode material using a novel carbon source

Polyethylene glycol (PEG, mean molecular weight of 10,000) has been used to prepare a Li₃V₂(PO₄)₃/C cathode material by a simple solid-state reaction. The Raman spectra shows that the coating carbon has a good structure with a low I_D/I_G ratio. The images of SEM and TEM show that the carbon is dispersed between the Li₃V₂(PO₄)₃ particles, which improves the electrical contact between the corresponding particles. The electronic conductivity of Li₃V₂(PO₄)₃/C composite is 7.0 × 10⁻¹ S/cm, increased by seven orders of magnitude compared with the pristine Li₃V₂(PO₄)₃ (2.3 × 10⁻⁸ S/cm). At a low discharge rate of 0.28C, the sample presents a high discharge capacity of 131.2 mAh/g, almost achieving the theoretical capacity (132 mAh/g) for the reversible cycling of two lithium. After 500 cycles, the discharge capacity is 123.9 mAh/g with only 5.6% fading of the initial specific capacity. The Li₃V₂(PO₄)₃/C material also exhibits an excellent rate capability with high discharge capacities of 115.2 mAh/g at 1C and 106.4 mAh/g at 5C.     

Structure and electrochemical properties of nanocarbon-coated Li3V2(PO4)3 prepared by sol-gel method

A liquid-based sol-gel method was developed to synthesize nanocarbon-coated Li₃V₂(PO₄)₃. The products were characterized by XRD, SEM and electrochemical measurements. The results of Rietveld refinement analysis indicate that single-phase Li₃V₂(PO₄)₃ with monoclinic structure can be obtained in our experimental process. The discharge capacity of carbon-coated Li₃V₂(PO₄)₃ was 152.6 mAh/g at the 50th cycle under 1C rate, with 95.4% retention rate of initial capacity. A high discharge capacity of 184.1 mAh/g can be obtained under 0.12C rate, and a capacity of 140.0 mAh/g can still be held at 3C rate. The cyclic voltammetric measurements indicate that the electrode reaction reversibility is enhanced due to the carbon-coating. SEM images show that the reduced particle size and well-dispersed carbon-coating can be responsible for the good electrochemical performance obtained in our experiments.     

Electrochemical performance of the carbon coated Li3V2(PO4)3 cathode material synthesized by a sol-gel method

A carbon coated Li₃V₂(PO₄)₃ cathode material for lithium ion batteries was synthesized by a sol-gel method using V₂O₅, H₂O₂, NH₄H₂PO₄, LiOH and citric acid as starting materials, and its physicochemical properties were investigated using X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) spectroscopy, scanning electron microscopy (SEM), energy dispersive analysis of X-ray (EDAX), transmission electron microscope (TEM), and electrochemical methods. The sample prepared displays a monoclinic structure with a space group of P2₁/n, and its surface is covered with a rough and porous carbon layer. In the voltage range of 3.0-4.3 V, the Li₃V₂(PO₄)₃ electrode displays a large reversible capacity, good rate capability and excellent cyclic stability at both 25 and 55 °C. The largest reversible capacity of 130 mAh g⁻¹ was obtained at 0.1C and 55 °C, nearly equivalent to the reversible cycling of two lithium ions per Li₃V₂(PO₄)₃ formula unit (133 mAh g⁻¹). It was found that the increase in total carbon content can improve the discharge performance of the Li₃V₂(PO₄)₃ electrode. In the voltage range of 3.0-4.8 V, the extraction and reinsertion of the third lithium ion in the carbon coated Li₃V₂(PO₄)₃ host are almost reversible, exhibiting a reversible capacity of 177 mAh g⁻¹ and good cyclic performance. The reasons for the excellent electrochemical performance of the carbon coated Li₃V₂(PO₄)₃ cathode material were also discussed.     

Study on synthesis routes and their influences on chemical and electrochemical performances of Li3V2(PO4)3/carbon

In this study, Li₃V₂(PO₄)₃/carbon samples were synthesized by two different synthesis routes. Their influence on chemical and electrochemical performances of Li₃V₂(PO₄)₃/carbon as cathode materials for lithium-ion batteries was investigated. The structure and morphology of Li₃V₂(PO₄)₃/carbon were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscope (TEM) measurements. TEM revealed that the Li₃V₂(PO₄)₃ grains synthesized through the sol-gel route had a depressed grain size. Electrochemical behaviors were characterized by galvanostatic charge/discharge, cyclic voltammetry and AC impedance measurements. Li₃V₂(PO₄)₃/carbon with smaller grain size showed better performances in terms of the discharge capacity and cycle stability. The improved electrochemical properties of the Li₃V₂(PO₄)₃/carbon were attributed to the depressed grain size and enhanced electrical contacts produced via the sol-gel route. AC impedance measurements also showed that the sol-gel route significantly decreased the charge-transfer resistance and shortened the migration distance of lithium ion.     

Low temperature solid-state synthesis routine and mechanism for Li3V2(PO4)3 using LiF as lithium precursor

Monoclinic lithium vanadium phosphate, Li₃V₂(PO₄)₃, has been successfully synthesized using LiF as lithium source. The one-step reaction with stoichiometric composition and relative lower sintering temperature (700 °C) has been used in our experimental processes. The solid-state reaction mechanism using LiF as lithium precursor has been studied by X-ray diffraction and Fourier transform infrared spectra. The Rietveld refinement results show that in our product sintered at 700 °C no impurity phases of VPO₄, Li₅V(PO₄)₂F₂, or LiVPO₄F can be detected. The solid-state reaction using Li₂CO₃ as Li-precursor has also been carried out for comparison. X-ray diffraction patterns indicate that impurities as Li₃PO₄ can be found in the product using Li₂CO₃ as Li-precursor unless the sintering temperatures are higher than 850 °C. An abrupt particle growth (about 2 μm) has also been observed by scanning electron microscope for the samples sintered at higher temperatures, which can result in a poor cycle performance. The product obtained using LiF as Li-precursor with the uniform flake-like particles and smaller particle size (about 300 nm) exhibits the better performance. At the 50th cycle, the reversible specific capacities for Li₃V₂(PO₄)₃ measured between 3 and 4.8 V at 1C rate are found to approach 147.1 mAh/g (93.8% of initial capacity). The specific capacity of 123.6 mAh/g can even be hold between 3 and 4.8 V at 5C rate.     

Long-term cyclability and high-rate capability of Li3V2(PO4)3/C cathode material using PVA as carbon source

The Li₃V₂(PO₄)₃/C composite cathode material is synthesized via a simple carbothermal reduction reaction route using polyvinyl alcohol (PVA) as both reduction agent and carbon source. The XRD pattern shows that the as-prepared Li₃V₂(PO₄)₃/C composite has a monoclinic structure with space group P2₁/n. The result of XPS shows the oxidation state of V in the Li₃V₂(PO₄)₃/C composite is +3. The Raman spectrum reveals that the coating carbon has a good structure with a low I_D/I_G ratio. The high-quality carbon can not only enhance the electronic conductivity of the Li₃V₂(PO₄)₃/C composite but also prevent the growth of the particle size. The electrochemical performance, which is especially notable for its high-rate performance, is excellent. It delivers an initial discharge capacity of 105.3 mAh/g at 5 C, which is retained as high as 90% after 2000 cycles. No capacity loss can be observed up to 300 cycles under 20 C rate condition. Our experimental results suggest that this compound can be a candidate as cathode materials for the power batteries of hybrid electric vehicles (HEVs) and electric vehicles (EVs) in the future.     

Preparation and electrochemical properties of Cr-doped Li9V3(P2O7)3(PO4)2 as cathode materials for lithium-ion batteries

Cr-doped Li₉V_3−xCr_x(P₂O₇)₃(PO₄)₂ (x = 0.0–0.5) compounds have been prepared using sol–gel method. The Rietveld refinement results indicate that single-phase Li₉V_3−xCr_x(P₂O₇)₃(PO₄)₂ (x = 0.0–0.5) with trigonal structure can be obtained. Although the initial specific capacity decreased with Cr content at a lower current rate, both cycle performance and rate capability have excited improvement with moderate Cr-doping content. Li₉V_2.8Cr_0.2(P₂O₇)₃(PO₄)₂ compound presents the good electrochemical rate and cyclic ability. The enhancement of rate and cyclic capability may be attributed to the optimizing particle size, morphologies, and structural stability during the proper amount of Cr-doping (x = 0.2) in V sites.     

A novel method for preparing LiFePO4 nanorods as a cathode material for lithium-ion power batteries

An effective method for synthesizing a one-dimensional nanostructure to improve the rate performance of LiFePO₄ as the cathode material for Li-ion power batteries is described. The crystal structure, composition, and morphology of the prepared LiFePO₄ were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM), respectively. The reaction mechanism of the LiFePO₄ nanorods is discussed herein. Electrodes consisting of the LiFePO₄ nanorods have better rate discharge capacities over a potential range of 2.5-4.2 V (vs. Li⁺/Li). These results are attributed to the shorter distance of electron transport and the fact that ion diffusion in the electrode material is limited by the nanorod radius. Our results indicate that the prepared LiFePO₄ nanorods are promising cathode materials for Li-ion power batteries. This new process for synthesizing nanorod products from nanorod raw material can be extended to the preparation of other one-dimensional materials.     

Layered monodiphosphate Li9V3(P2O7)3(PO4)2: A novel cathode material for lithium-ion batteries

Single phase Li₉V₃(P₂O₇)₃(PO₄)₂ is synthesized at 750 °C via solid-state reaction method for the first time. The Rietveld refinement results show that the trigonal system (space group: ) with the lattice parameters a = 0.9724 nm, c = 1.3596 nm are obtained. Its intrinsic electrical conductivity of 1.43 × 10⁻⁸ S cm⁻¹ is higher than that of LiFePO₄ and as the same order of Li₃V₂(PO₃)₄. The electrochemical measurement results show that there are two plateaus (3.77 V and 4.51 V) and three plateaus (3.77 V, 4.51 V and 4.75 V) in the potential ranges of 2.0–4.6 V and 2.0–4.8 V, respectively. In the range of 2.0–4.6 V, two discharge plateaus (4.46 V and 3.74 V) can be observed and 110 mAh g⁻¹ of discharge capacity is achieved. The Rietveld refinement result of the X-ray diffraction (XRD) data at the end of discharge after the first cycle suggests that the structural reversibility can be retained during electrochemical reactions in Li₉V₃(P₂O₇)₃(PO₄)_2. In the range of 2.0–4.8 V, almost six lithium ions are extracted and the trigonal structure is still recovered after 30 cycles. Therefore, this novel layered vanadium monodiphosphate offers a promising candidate as cathode material for lithium-ion batteries.     

Comparison of AlPO4- and Co3(PO4)2-coated LiNi0.8Co0.2O2 cathode materials for Li-ion battery

Electrochemical and thermal properties of Co₃(PO₄)₂- and AlPO₄-coated LiNi_0.8Co_0.2O₂ cathode materials were compared. AlPO₄-coated LiNi_0.8Co_0.2O₂ cathodes exhibited an original specific capacity of 170.8 mAh g⁻¹ and had a capacity retention (89.1% of its initial capacity) between 4.35 and 3.0 V after 60 cycles at 150 mA g⁻¹. Co₃(PO₄)₂-coated LiNi_0.8Co_0.2O₂ cathodes exhibited an original specific capacity of 177.6 mAh g⁻¹ and excellent capacity retention (91.8% of its initial capacity), which was attributed to a lithium-reactive Co₃(PO₄)₂ coating. The Co₃(PO₄)₂ coating material could react with LiOH and Li₂CO₃ impurities during annealing to form an olivine Li_xCoPO₄ phase on the bulk surface, which minimized any side reactions with electrolytes and the dissolution of Ni⁴⁺ ions compared to the AlPO₄-coated cathode. Differential scanning calorimetry results showed Co₃(PO₄)₂-coated LiNi_0.8Co_0.2O₂ cathode material had a much improved onset temperature of the oxygen evolution of about 218 °C, and a much lower amount of exothermic-heat release compared to the AlPO₄-coated sample.     

Microwave solid-state synthesis and electrochemical properties of carbon-free Li3V2(PO4)3 as cathode materials for lithium batteries

Monoclinic Li₃V₂(PO₄)₃ can be rapidly synthesized at 750 °C for 5 min (MW5m) by using microwave solid-state synthesis method. The refined cell parameters and atomic coordination of the sample MW5m show some deviations compared with those of the sample synthesized in conventional solid-state synthesis method, especially the coordinate of Li atoms. Compared with the electrochemical properties of the carbon-coating sample Li₃V₂(PO₄)₃, the carbon-free sample MW5m presents well electrochemical properties. In the cut-off voltage of 3.0-4.3 V, MW5m sample presents a specific charge capacity of 132 mAh g⁻¹, almost equivalent to the reversible cycling of two lithium ions per Li₃V₂(PO₄)₃ formula unit (133 mAh g⁻¹), and specific discharge capacity of 126.4 mAh g⁻¹. In the cut-off voltage of 3.0-4.8 V, MW5m shows an initial specific discharge capacity of 183.4 mAh g⁻¹ at 0.1 C, near the theoretical discharge capacity. In the cycle performance, the capacity fade of Li₃V₂(PO₄)₃ is dependent on the cut-off voltage and the preparation method, more capacity lost at relatively higher charge/discharge voltage. The reasons for the excellent electrochemical properties of Li₃V₂(PO₄)₃ rapidly synthesized in microwave field are discussed in detail.     

Hydrothermal synthesis of LiMn2O4/C composite as a cathode for rechargeable lithium-ion battery with excellent rate capability

A spinel LiMn₂O₄/C composite was synthesized by hydrothermally treating a precursor of manganese oxide/carbon (MO/C) composite in 0.1 M LiOH solution at 180 °C for 24 h, where the precursor was prepared by reducing potassium permanganate with acetylene black (AB). The AB in the precursor serves as the reducing agent to synthesize the LiMn₂O₄ during the hydrothermal process; the excess of AB remains in the hydrothermal product, forming the LiMn₂O₄/C composite, where the remaining AB helps to improve the electronic conductivity of the composite. The contact between LiMn₂O₄ and C in our composite is better than that in the physically mixed LiMn₂O₄/C material. The electrochemical performance of the LiMn₂O₄/C composite was investigated; the material delivered a high capacity of 83 mAh g⁻¹ and remained 92% of its initial capacity after 200 cycles at a current density of 2 A g⁻¹, indicating its excellent rate capability as well as good cyclic performance.     

Optimum synthesis of Li2Fe1−xMnxSiO4/C cathode for lithium ion batteries

Li₂Fe_1−xMn_xSi0₄/C cathode materials were synthesized by mechanical activation-solid-state reaction. The effects of Mn-doping content, roasting temperature, soaking time and Li/Si molar ratio on the physical properties and electrochemical performance of the Li₂Fe_1−xMn_xSi0₄/C composites were investigated. The materials were characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM), charge-discharge tests and AC impedance measurements. SEM images suggest that the morphology of the Li₂Fe_1−xMn_xSi0₄/C composite is sensitive to the reaction temperature. Samples synthesized at different temperatures have different extent of agglomeration. Being charged-discharged at C/32 between 1.5 and 4.8 V, the Li₂Fe_0.9Mn_0.1Si0₄/C synthesized at the optimum conditions shows good electrochemical performances with an initial discharge capacity of 158.1 mAh g⁻¹ and a capacity retention ratio of 94.3% after 30 cycles. AC impendence investigation shows Li₂Fe_0.9Mn_0.1SiO₄/C have much lower resistance of electrode/electrolyte interface than Li₂FeSiO₄/C.     

Synthesis and electrochemical properties of monoclinic Li3V2(PO4)3/C composite cathode material prepared from a sucrose-containing precursor

Monoclinic structure Li₃V₂(PO₄)₃/C composite powders are synthesized via a novel homogeneous mixing route followed by a one-step heat treatment. The composites were characterized by X-ray diffraction (XRD) and galvanostatic charge/discharge, CV measurements. The influence of the heat treatment on the electrochemical properties of Li₃V₂(PO₄)₃/C composites was investigated. To examine the effect of residual carbon content on the properties of the composites, six samples with 1.2, 2.3, 3.4, 4.4, 5.8, and 7.0 wt% carbon were prepared. The sample with 4.4 wt% carbon exhibited good cycling performance and rate capability in the range of 3.0–4.8 V.