3.
4.
《金属功能材料》2006,13(1):46-47
低弹性模量高强度β型TiNbSn合金采用高纯钛、铌和锡金属原料在氩气氛中电弧熔炼,制备了成分为Ti-35%(质量)Nb-4%(质量)Sn和Ti-35%(质量)Nb-7·9%(质量)Sn的两个Ti-Nb-Sn合金。铸成钮扣状合金锭,经过固溶热处理后冰水淬火,冷轧成1·0mm厚的板状试样。用差示扫描量热器测定马氏体转变温度,用X射线衍射和光学显微镜观察显微组织。使用X射线织构测角器检验试样的织构。用尺寸为10×50×1mm的试样主要运用自由谐振法测量了室温下的动态杨氏模量;运用拉伸试验于不同温度(233~423K)下测量静态杨氏模量。研究结果表明:(1)Ti-35Nb-4Sn合金冷… 相似文献
5.
研究了铝合金回炉料和废料经电渣重熔与精炼后合金的性能。回炉料和废料分别在熔渣中熔化和在煤气火焰炉中熔化。用获得的合金在金属型中浇注光谱分析的专门试样。用φ60,长150毫米的工艺试样测定化学成分,氧化铝含量、含氢量,进行铸造与形变金属的断口宏观组织分析,以及测定未经热处理试样的机械性能。选择电渣重熔的熔剂应避免和合金产生相互作用而导致合金中任一组元的烧损。因 相似文献
6.
容量法测定金合金中的金 总被引:4,自引:0,他引:4
对重铬酸钾滴定过量硫酸亚铁返滴定法测定金合金中金的主要问题做了探讨和实验.拟定了简便、准确的测定方法,方法的重现性好,金含量为60%~99%时的相对标准偏差<0.2%. 相似文献
7.
用PHILIPS-XL30型扫描电子显微镜(SEM)观察了不同Sn含量对易切削Bi黄铜组织的影响,采用HY-1080型电子拉伸试验机测试了试样的力学性能,使用C6136卧式普通机床检测合金切削性能.结果表明,Sn能改变Bi的分布状态,使Bi从相界向α相迁移,从而有效改善材料性能;但Sn的含量超过2.0%时,合金中生成CuZnSn脆性电子化合物,使材料力学性能指标降低;合金的切削性能随着Sn含量的增加而提高. 相似文献
8.
9.
通过建立以纯铁助熔剂和钨锡助熔剂与试样钴铬钨系合金粉末共熔融体系,于高频感应燃烧红外吸收碳硫联测仪测得钴铬钨系合金粉末中碳的含量。实验测定结果表明,以0.30 g纯铁和1.20 g钨锡粒混合助熔,测得三个不同梯度钴铬钨系合金粉末中碳的含量结果准确。该方法熔样过程中无试样飞溅、熔体块状散开的现象,出峰峰形释放曲线流畅不拖尾。方法中碳的检出限(3 s)为0.000 34%,测定下限(10 s)为0.001 1%。采用所建立的方法测定待测元素碳的结果 RSD(n=11)在0.33%~1.98%之间,加标回收率为97.37%~103.52%,表明该方法对于钴铬钨系合金粉末中碳含量的测定结果具有准确性好、精密度高等特点,能够满足企业在工业生产过程中的质量控制分析要求,可应用于第三方实验室的日常分析检测工作。 相似文献
10.
11.
12.
采用高能球磨机械合金化法制备了Au-20%Sn合金,分析了合金物相、组织和硬度随球磨时间的变化规律,探讨了合金塑性与合金组织及制备工艺的关系。结果表明:采用高能球磨机械合金化法可以制备Au-20%Sn合金;随球磨时间的增加,Au-20%Sn的合金化程度增加,组织中的金属间化合物逐渐增多,最终基本上为δ相和ζ′相;合金的硬度随球磨时间的延长逐渐升高,并在球磨60min后获得最高硬度104.2HV,然后开始下降;球磨后的合金粉末在190℃×2h的烧结过程中发生了不同程度的再结晶和晶粒长大,再结晶程度随球磨时间的延长而增加,导致烧结后合金硬度在球磨时间超过60min后反而下降。 相似文献
13.
Yong MAO Dan-li ZHU Jun-jie HE Chao DENG Ying-jie SUN Guang-jie XUE Heng-fei YU Chen WANG 《中国有色金属学会会刊》2021,31(6):1700-1716
Hot compression was performed on a multilayered Au?20Sn eutectic alloy to investigate the deformation behavior and microstructure evolution. During hot compression, microstructural spheroidization was initiated from plastic instability regions, and it was preferentially activated in vertical lamellae with a growth direction parallel to the compressive direction. Continuous dynamic recrystallization associated with lattice dislocations was the mechanism in both AuSn and Au5Sn multilayers. After spheroidization, strain accumulations were weakened in both of the equiaxed phases, and the deformation mechanism was substantially replaced by grain boundary sliding and migration. Based on these findings, hot rolling was conducted on an as-cast Au?20Sn alloy and a foil with a thickness of ~50 μm was successfully prepared. The present study can promote the development of Au?20Sn foils, and provide insights into the deformation behavior and microstructure evolution of multilayered eutectic alloys. 相似文献
14.
Phase equilibria of the Au–Sn–Zn ternary system and interfacial reactions between Sn–Zn alloys and Au were experimentally investigated at 160 °C. Experimental results reveal that no equilibrium-stated ternary phases were found and the ternary element solubility in the binary phase is insignificant. When the Zn content was less than 3 wt% in the Sn–Zn alloy, only the Au–Sn binary intermetallic compounds (IMCs), such as AuSn, AuSn2 and AuSn4 phases, were formed at the Sn–Zn/Au interface. When the Zn content in Sn–Zn alloys was greater than 7 wt%, the AuZn, AuZn2 and Au3Zn7 phases were formed in the Sn–Zn/Au couples at 160 °C. However, both Sn–Zn and Au–Zn IMCs, and the Au–Zn–Sn ternary IMC (T phase) were observed between Au and the Sn–Zn alloys with 3–5 wt% added Zn. This T phase might be the metastable phase. The evolution of IMCs in the Sn–Zn/Au couples is very sensitive to the Zn content in Sn–Zn alloys. 相似文献
15.
16.
采用光学显微镜(OM)、维氏硬度计、热动态分析仪、X射线衍射(XRD)、多功能内耗仪等,研究了Sn含量对Mg-xSn-1Mn合金显微组织、阻尼性能和力学性能的影响。结果表明:当Sn含量从2%增加到8%时,Mg-xSn-1Mn合金的枝晶间隙呈现细化的趋势,硬度从43.84 HV0.1增加至54.00 HV0.1,呈单调增加的趋势。应变无关阻尼随着Sn含量的增加呈现先增后减的趋势,在Sn含量为4%时达到最大,应变相关阻尼则随着Sn含量的增加呈现逐渐减小的趋势。在低温阶段,相同Sn含量的合金的阻尼随着频率的增大呈现增加的趋势;但在高温下,阻尼值在低频时的上升速率比高频时快,并随着温度的升高,低频阻尼和高频阻尼趋向于相等。当Sn含量不同时,随着温度的升高,Sn含量较高的合金的阻尼值上升速率变快。 相似文献
17.
HSn70-1B铜管在中性NaCl溶液中的腐蚀行为 总被引:2,自引:0,他引:2
利用原子吸收光谱、电子衍射、电子显微镜等测试技 术,对在不同含量的NaCl中性水溶液中HSn70-1B铜管的腐蚀行为进行研究.在中性NaC l溶液中HSn70-1B铜管的腐蚀行为主要受表面膜的形成过程和组成所控制,可分为2个 阶段:氯离子含量在0 mol/L~0.02 mol/L时,合金表面逐渐形成较完整的Cu2O表面膜, 保护性增 强;氯离子含量在0.02 mol/L~0.05 mol/L时,Cu2O膜减薄而变得不完整,合金逐渐进入 均匀腐蚀状态. 相似文献
18.
19.
研究了添加不同含量的Sn(3%,6%,9%,质量分数)对铸态、固溶态及时效态Mg-Sn二元合金导热性能的影响。结果表明,铸态及固溶处理态Mg-Sn合金的热导率均随着Sn元素含量的增加不断降低,其中Sn含量最多的固溶态Mg-10Sn合金所对应的热导率降低至52.6 W/(m·K);同固溶态合金相比,相同溶质含量的铸态合金的热导率更高。Mg-Sn合金的热导率随时效的进行逐渐升高,Mg-3Sn、Mg-6Sn及Mg-10Sn合金的热导率分别最终可达到125、120及110 W/(m·K)。分析表明,镁合金热导率的不断升高可以归结于基体的纯化效应,Sn元素的原子大小、核外电子分布以及化合价等均会对Mg-Sn合金的导热性能产生影响。 相似文献
20.
Sn对ZM61合金组织与性能的影响 总被引:1,自引:0,他引:1
通过光学金相(OM),扫描电镜(SEM),X射线衍射(XRD)等分析方法,研究不同Sn含量对Mg-6Zn-1Mn(ZM61)合金显微组织和力学性能的影响,并初步探讨Sn元素在镁合金中的存在形式和作用机理。结果表明:Sn元素在ZM61合金中主要以Mg2Sn相存在;Sn元素不仅可以改善合金的铸造性能,所形成弥散的Mg2Sn相颗粒还可以明显的细化晶粒改善组织,提高合金的力学性能,其中经440℃,2h+90℃,24h+180℃,8h双级时效处理的ZM61-4Sn合金具有最佳的综合力学性能,其屈服强度、抗拉强度和延伸率分别为358MPa、374MPa和4.6%;Sn的加入不会改变合金的断裂机制,但是粗大的Mg2Sn粒子会成为裂纹源,从而降低合金的塑性,所以Sn含量不宜过高,不大于4%较为合适。 相似文献