镁锌铁氧体粉末的水热法合成及其矫顽力机理

采用水热法合成名义成分为Mg1-xZnxFe2O4(x=0,0.2,0.4,0.6和0.8)的铁氧体粉末样品,采用X射线衍射仪、扫描电镜和振动样品磁强计等对其结构和矫顽力机理进行研究。结果表明:Zn含量增加有利于(Mg,Zn)Fe2O4铁氧体的成相,晶格常数也随着x的增加而增加;与x=0的样品相比,普通软磁材料矫顽力较大,其他样品的矫顽力呈现典型的软磁铁氧体值,且随着x的增大矫顽力呈逐渐减小的趋势,这与晶粒大小有密切关系;样品中微米级的大颗粒是纳米级小晶粒的聚集体。     

Gd含量对烧结NdFeB永磁体热稳定性的影响

选择不同Gd含量制备了永磁材料,使用磁性能测量设备NIM-200C和环境扫面电子显微镜FEI QUAN-TA400研究了(GdxPrNd1-x)33.2 Fe65.25Al0.5B105(x=1.5,3,4.5,6,7.5,9)的温度稳定性和显微结构.结果表明,在(GdxPrNd1-x)33.2Fe65.25Al0.5B1.05中,当Gd的质量分数为3％时,样品具有最高矫顽力1 015 kA/m,较好的剩磁1.203 T,以及最好的温度稳定性.在200℃时的剩磁温度系数为-0.001 27％/℃,矫顽力温度系数为-0.004 94％/℃.Gd的添加在一定程度上减少了α-Fe相,并使富稀土相均匀化分布,从而提高了铸锭的破碎性能和磁体的致密程度.     

快速热处理的[Fe/Pt]n薄膜的结构和磁性

采用直流磁控溅射方法在Si基片上制备[Fe/Pt]_n薄膜,利用X射线荧光光谱仪(XRF)、X射线衍射仪(XRD)和振动样品磁强计(VSM)分析薄膜的组分、结构和磁性。研究结果表明：[Fe/Pt]_n薄膜经过600 ℃快速热处理,得到了L1₀-FePt薄膜。对于[Fe (x nm)/Pt (0.5 nm)]_n薄膜,当Fe层厚度为0.7 nm时,薄膜的有序度最大,平行膜面和垂直膜面的矫顽力均最高;对于不同调制周期的[Fe/Pt]_n薄膜,有序度随调制周期先增大后减小,平行膜面的矫顽力均高于垂直膜面的矫顽力,当调制周期为2.4 nm时,薄膜平行膜面的矫顽力最大。     

Sm-Cu离子取代锶铁氧体制备与磁性能研究

采用固相法制备了Sm-Cu联合取代的锶铁氧体Sr_(1-x)Sm_xFe_(12-x)Cu_xO_(19)(x=0. 00-0. 20)。利用XRD、SEM及VSM对锶铁氧体的晶相组成、微观形貌及磁学性能进行了研究。结果表明:随着掺杂量x的增加饱和磁化强度Ms,矫顽力Hc以及剩磁Mr均出现先增大后减小的趋势;当Sm-Cu掺杂量x=0. 05时,剩磁Mr达到最大值Mr=24. 173 emu/g;当掺杂量x=0. 10时,饱和磁化强度达到最大值Ms=51. 757 emu/g,同时矫顽力也出现最大值Hc=809. 904 Oe。     

Sm-Mn离子取代锶铁氧体的制备及其表征

采用高温固相法制备了Sr_(1-x)Sm_xFe_(12-x)Mn_xO_(19)(x=0~0.4)。利用XRD、SEM、VSM等表征手段对锶铁氧体的晶相、形貌和磁性能进行了表征。通过XRD分析发现当掺杂量0≤x0.2时衍射峰基本没有出现杂峰,衍射峰的强度比较高,粉体为结晶度比较高的单一六方相锶铁氧体。通过SEM发现随着掺杂量的增加晶体的晶粒尺寸逐渐增大;通过VSM分析发现:随着掺杂量的增大矫顽力Hc出现先增大后减小的趋势。测试结果表明:当掺杂量在x=0.2时Sm-Mn联合取代锶铁氧体的结晶度最好,矫顽力最大Hc=33.417 emu/g。     

Fe_(71-x)Nb_9B_(20)W_x磁性非晶合金玻璃形成能力及热稳定性研究

为了研究W元素部分替代Fe元素对Fe基非晶合金热稳定性和软磁性能的影响规律,文中采用单辊旋淬法制备了Fe_(71-x)Nb_9B_(20)W_x(x=1,3,5)非晶合金带材,利用X射线衍射仪(XRD)、差示扫描量热仪(DSC)及振动样品磁强计(VSM)等手段测试Fe_(71-x)Nb_9B_(20)W_x非晶合金的热学性能和软磁性能。研究结果表明:Fe基非晶的晶化过程与W含量密切相关,随着W含量的增加,合金由两次晶化过程转变为一次晶化过程。添加W元素能够有效提高Fe基非晶合金的玻璃形成能力,改善合金的热稳定性。Fe_(66)Nb_9B_(20)W_5非晶合金具有优异的热稳定性和较高的非晶形成能力,过冷液相区宽度T_x和晶化起始温度T_(x1)分别高达58 K和928 K。合金的饱和磁感应强度M_s和矫顽力H_c分别为42～90 emu·g~(-1)和0.61～6.59 Oe,其中M_s随着W含量的增加而降低。     

脉冲磁场处理工艺对非晶合金磁致伸缩系数的影响

低频脉冲磁场处理工艺,可以使非晶薄带(Fe1-xCox) 86Hf7B6Cu1(x=0.4)产生纳米晶化α- Fe,(Fe1-x Cox) 86Hf7B6Cu1(x=0.4)表现为正磁致伸缩,α- Fe表现为负磁致伸缩。提高磁场强度、处理时间可以调整晶化量的大 小,使λSA和λSB之间体积分数比达到最佳,样品的磁致伸缩系数λS 最小。     

LaZn掺杂锶铁氧体纳米颗粒的制备与磁性研究

利用化学共沉淀法制备出化学组成为Sr1-xLaxFe12-xZnxO19(x=0~0.4)的掺杂锶铁氧体纳米颗粒,研究了不同的掺杂量对铁氧体结构和磁学性能的影响.结果显示,γ-Fe2O3的是M型锶铁氧体相形成的前驱体,随退火温度的升高,γ-Fe2O3衍射峰强度逐渐减弱直至消失,850℃时已形成单一的M型铁氧体相;随着代换量x的增大,样品的比饱和磁化强度σS先增大后下降,而矫顽力HC的值则单调减小,这些非常适合用于高密度磁记录材料.     

天然气膜基吸收脱硫研究

在膜接触器天然气脱硫实验平台上以N-甲基二乙醇胺(MDEA)水溶液为吸收剂,采用疏水性聚丙烯中空纤维膜(HFPPM)作为膜接触器,利用膜基吸收技术对天然气中的H2S进行脱除实验研究.实验结果表明:膜基吸收技术可以有效的达到天然气脱硫的目的,调节操作参数,可以使脱硫率达到99%以上;提高吸收液的浓度和流量可以同时增加H2S的脱除率η和H2S总传质系数K;进气流量的增大降低了η,K反而增大;进气压力的增大可以提高η,同时提高了K;原料气中H2S浓度增加导致η下降,同时降低了K;吸收液循环利用次数的增加降低了H2S的脱除率.为膜基吸收技术在脱除天然气中的H2S的应用提供了依据.     

Pr_2(Co_(1-x)Mn_x)_(14)B和Pr_2(Fe_(1-x)Mn_x)_(14)B的结构和低温磁性

本文研究了Pr_2(Co_(1-x)Mn_x)_(14)B 和 Pr_2(Fe_(1-x)Mn_x)14B 化合物的晶体结构和低温内禀磁性.在 x≤0.5时,可以形成2-14-1四方晶体结构.当 x 分别大于0.3和0.2时,Pr_2(Co_(1-x)Mn_x)_(14)B 和 Pr_2(Fe_(1-x)Mn_x)_(14)B 的居里温度 T_c 和饱和磁化强度σ_s 急剧减小.这两种化合物块状样品在1.5 K 的内禀矫顽力分别达到16 kOe 和22 kOe.内禀矫顽力既随成分变化,也随温度改变.低温特大矫顽力来源于窄畴壁能的涨落.     

Nd2Fe17 nanograins effect on the coercivity of HDDR NdFeB magnets with low boron content

Relationships between the coercivity of hydrogenation disproportionation desorption recombination(HDDR) Nd12.5Fe81.5-xCo6Bx bonded magnets and boron content were investigated.Nd2Fe17 phase with planar magnetic anisotropy is present in the microstructure when x= 4at%-5.88at%,which does not reduce the coercivity of the bonded magnets.High-resolution transmission electron microscopy(TEM) images show that Nd2Fe17 phase exists in the form of nanocrystals in the Nd2Fe14B matrix.There is an exchange-coupling interaction between the two phases so that the coercivity of HDDR Nd12.5Fe81.5-xCo6Bx bonded magnets is hardly reduced with a decrease in boron content.     

Interface chemical states of NiO/NiFe films and their effects on magnetic properties

Ta/NiOx/Ni81Fe19/Ta multilayers were prepared by rf reactive and dc magnetron sputtering. The exchange coupling field ( Hex) and the coercivity ( Hc) of NiOx/Ni81Fe19 as a function of the ratio of Ar to O2 during the deposition process were studied. The composition and chemical states at the interface region of NiOx/NiFe were also investigated using the X-ray photoelectron spectroscopy (XPS) and peak decomposition technique. The results show that the ratio of Ar to O2 has great effect on the nickel chemical states in NiOx film. When the ratio of Ar to O2 is equal to 7 and the argon sputtering pressure is 0.57 Pa, the x value is approximately 1 and the valence of nickel is + 2. At this point, NiOx is antiferromagnetic NiO and the corresponding Hex is the largest. As the ratio of Ar/O2 deviates from 7, the exchange coupling field ( Hex) will decrease due to the presence of magnetic impurities such as Ni +3 or metallic Ni at the interface region of NiOx/NiFe, while the coercivity ( Hc) will increase due to     

低浓度H_2S在Fe（OH）_3表面的吸附反应研究

以活性硫H2S为例,研究低浓度时与炼油装置内表面腐蚀产物Fe（OH）3的表面吸附反应过程,考察温度、反应气体相对湿度、Fe（OH）3含水率对吸附反应的影响,旨在为炼油厂抑制因活性硫腐蚀产物引发的自燃事故提供依据。研究结果表明,温度升高,有利于吸附反应,反应气体相对湿度及Fe（OH）3含水率的增加均促进吸附反应。     

Fe/Al2O3纳米复合材料的结构和磁性

采用溶胶-凝胶法制备了复合材料Fe2O3/Al2O3,将其在氢气中还原得到了纳米复合材料Fe/Al2O3。利用X-ray衍射、Mssbauer效应和振动样品磁强计对样品的结构和性质进行了研究,结果表明,Fe2O3含量对样品的还原过程及结构和性质有明显的影响。随Fe2O3含量的增加,还原后样品中α-Fe的晶粒尺寸变大,样品的比饱和磁化强度增加,矫顽力减小。Mssbauer效应结果显示,在一些样品中存在超顺磁现象和FeAl2O4相。     

Giant magnetoimpedance effect in as quenched Fe89—xZr7B4Cux（x=1.0—2.5） ribbons

The giant magnetoimpedance (GMI) effect in as-quenched Fe_(89) _xZr_7B_4Cu_x (x= 1.0-2.5) ribbons is reported. The as-quenched Fe_(89-x)Zr_7B_4Cu_x(x=1.0-2.5) ribbons were prepared by the vacuum melt-spun processes with the quenching speed of 37m/s. The magnetoimpedance measurement were performed at room temperature, where the current flows through the length of the ribbons in the direction parallel to the dc fields. Results show that values Z (impedance), R (resistance) and X (reactance) for both H=0 A/m and H=5 127 A/m increases with increasing ac frequency. This can be explained by the skin effect mechanism. The GMI effect almost can not be found in the Cu content (mass fraction) range x ≤ 1.5%. With increasing Cu content x > 1.5%, the GMI effect become evident for as-quenched Fe_(89-x)Zr_7B_4Cu_x (x=1.0-2.5) ribbons. GMI ratio (Z(0)-Z(H)/Z(0)) in as quenched Fe_(86.5)Zr_7B_4Cu_(2.5) with melt-spun quenching speed of 37 m/s can reaches 33.69% atH=5 127 A/m. This indicated that good GMI properties can     

FePt/Ag薄膜的结构和磁性

采用直流磁控溅射在SiO2〈0001〉基片上制备了FeAg和FePt/Ag薄膜,将其在不同温度下进行真空热处理,得到具有高矫顽力的L10-FePt颗粒膜。利用X射线衍射、振动样品磁强计、扫描探针显微镜对样品的结构、磁性、形貌进行了研究。结果表明:Ag元素的添加有效地降低了FePt薄膜的有序化温度,样品在300℃热处理时即发生有序化转变。随着热处理温度的升高,样品的有序化程度提高,矫顽力变大,样品表面粗糙度减小,形成了均匀的颗粒薄膜。     

快速循环热处理对(Co0.35Fe0.65)99O1薄膜磁性能的影响

针对(Co0.35Fe0.65)99O1薄膜,研究了两种不同热处理工艺对其磁性能的影响。结果表明:快速循环热处理可以改善高磁矩(Co0.35Fe0.65)99O1薄膜磁性能,在450℃几个快速循环热处理后,沉积薄膜的矫顽力从105下降到3 Oe,电阻率下降到70%,a-Fe (Co)相晶粒尺寸可以减小到15~35 nm,该处理方法较以往的热处理更能改善软磁薄膜的性能。