Synthesis of a novel nanostructured zinc oxide/baghdadite coating on Mg alloy for biomedical application: In-vitro degradation behavior and antibacterial activities

In this research, zinc oxide (ZnO) and zinc oxide/baghdadite (ZnO/Ca₃ZrSi₂O₉) were prepared on the surface of Mg alloy using physical vapor deposition (PVD) coupled with electrophoretic deposition (EPD). For this purpose, the nanostructured ZnO was prepared with a thickness of 900 nm and crystallite sizes of 64 nm as under layer while nanostructured baghdadite with a thickness of 10 µm was deposited on the Mg alloy substrate as an over-layer. Electrochemical measurement exhibited that the ZnO/Ca₃ZrSi₂O₉-coated specimen has a higher corrosion resistance and superior stability in simulated body fluid (SBF) solution in comparison with the ZnO-coated and bare Mg alloy samples. Antibacterial activities of the uncoated and coated specimens were evaluated against various pathogenic species (Escherichia coli, Klebsiella pneumoniae, and Shigella dysenteriae) via disc diffusion method. The obtained results showed that ZnO and ZnO/Ca₃ZrSi₂O₉ coatings have great zones of inhibition (ZOI) against E. coli, Klebsiella, and Shigella. However, less ZOI was found around the bare Mg alloy. Therefore, ZnO/Ca₃ZrSi₂O₉ is a promising coating for orthopedic applications of biodegradable Mg alloys considering its excellent antibacterial activities and high corrosion resistance.     

In vitro biocompatibility of a nanocrystalline β-Ta2O5 coating for orthopaedic implants

To improve the durability and bioactivity of Ti–6Al–4V alloy used for medical implants, the β-Ta₂O₅ nano-crystalline coatings were introduced using double cathode glow discharge technique. The coating microstructure was characterized using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HRTEM). The coating exhibits an assembly of near-equiaxed grains, locally aligned normal to the coating surface. The β-Ta₂O₅ coating exhibits strong adhesion to substrate and a strong resistance to deformation and cracking under applied loads. Cells culture tests showed that the coating is more beneficial to the adhesion and proliferation of NIH-3T3 cells as compared to the uncoated alloy. In-vitro bioactivity was evaluated by immersion of the coating in simulated body fluids (SBF) for different periods up to 14 days at 37 °C. The results indicated that bioactivity of Ti–6Al–4V was dramatically improved after the deposition of β-Ta₂O₅, since the coating has a higher apatite forming ability than the Ti–6Al–4V substrate. Finally, the electrochemical behavior of the β-Ta₂O₅ coating after soaking in SBF at 37 °C for 0, 3, 7, and 14 days was studied through potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). EIS measurements also confirm that the presence of a hydroxyapatite layer on the coating becomes thicker and denser during soaking in SBF. Moreover, the coating exhibits better corrosion resistance than the bare alloy. Hence, the β-Ta₂O₅ coating is a promising candidate coating for protection of orthopedic implants with enhanced bioactivity and corrosion resistance.     

Fabrication and characterization of hybrid coating on Mg–Zn–Ca Mg alloy for enhanced corrosion and degradation resistance as medical implant

Magnesium (Mg)-based alloys have appealing properties as promising implants for medical applications. However, their clinical applications are hindered due to the rapid corrosion and degradation rate in the physiological environment. In this investigation, we reported a novel interfacial engineering approach for the fabrication of polymer/ceramic hybrid coating on Mg–Zn–Ca Mg alloy. Firstly, hydroxyapatite (HA) coating was fabricated on the Mg–Zn–Ca sample followed by an alkali treatment that was performed in 1 M NaOH solution at 60 °C. Finally, polycaprolactone (PCL) coating was synthesized using a dip-coating approach on the top of the HA-coated Mg–Zn–Ca specimen. Microhardness test and adhesion test revealed that PCL/HA hybrid coating significantly improved mechanical properties and enhanced biointerface property between the substrate and coating. The immersion tests showed that the hybrid coating considerably slowed down the degradation in the simulated body fluid (SBF) solution. In addition, in vitro electrochemical investigations confirmed that PCL/HA coating significantly improved corrosion resistance and greatly reduced corrosion rate by about 10 times compared to HA coating and about 900 times to untreated Mg–Zn–Ca sample. Moreover, cytotoxicity assessment exhibited PCL/HA hybrid coating enhanced biocompatibility and bioactivity due to adopting a suitable interfacial engineering approach.     

Electrochemical and structural evaluation of functionally graded bioglass-apatite composites electrophoretically deposited onto Ti6Al4V alloy

Titanium and its alloys are widely used as materials for implants, owing to their corrosion resistance, mechanical properties and excellent biocompatibility. However, clinical experience has shown that they are susceptible to localised corrosion in the human body causing the release of metal ions into the tissues surrounding the implants. Several incidences of clinical failures of such devices have demanded the application of biocompatible and corrosion resistant coatings and surface modification of the alloys. Coating metallic implants with bioactive materials is necessary to establish good interfacial bonds between the metal substrate and the bone. Hence, this work aimed at developing a bioglass-apatite (BG-HAP) graded coating on Ti6Al4V titanium alloy through electrophoretic deposition (EPD) technique. The coatings were characterized for their properties such as structural, electrochemical and mechanical stability. The electrochemical corrosion parameters such as corrosion potential (E_corr) (open circuit potential) and corrosion current density (I_corr) evaluated in simulated body fluid (SBF) have shown significant shifts towards noble direction for the graded bioglass-apatite coated specimens in comparison with uncoated Ti6Al4V alloy. Electrochemical impedance spectroscopic investigations revealed higher polarisation resistance and lower capacitance values for the coated specimens, evidencing the stable nature of the formed coatings. The results obtained in the present work demonstrate the suitability of the electrophoretic technique for the preparation of graded coating on Ti6Al4V substrates.     

Biopolymeric coatings for delivery of antibiotic and controlled degradation of bioresorbable Mg AZ31 alloys

Magnesium and magnesium alloys are attracting considerable interest as biodegradable materials with high potential for application as temporary implants. The high corrosion rate of Mg-based implants is considered a serious drawback, and it is crucial to design novel surface protection strategies that minimize the detrimental effects of corrosion, while contributing for introducing additional functionalities on the material surface. In this work, a layer-by-layer coating architecture composed of an inner poly(lactic-co-glycolic) acid layer, working as adhesion promoter, and additional polycaprolactone (PCL) layers working as reservoirs for antibiotic (levofloxacin) and for nanohydroxyapatite (nanoHA) particles was applied on the Mg alloy AZ31. The results demonstrate that the composition and number of PCL layers can tailor the biodegradation of the bare magnesium alloy, surface wettability, and the kinetics of release of antibiotic (levofloxacin). The distribution of nanoHA in the coating architecture plays a crucial role on tailoring the desired biocompatible functionalities and corrosion protection of the bare alloy.     

Novel bi-layered nanostructured SiO2/Ag-FHAp coating on biodegradable magnesium alloy for biomedical applications

In this study, a novel bi-layered nanostructured silica (SiO₂)/ silver-doped fluorohydroxyapatite (Ag-FHAp) coating was deposited on biodegradable Mg-1.2Ca-4.5Zn alloy via physical vapor deposition (PVD) combined with electrodeposition (ED). The nano-SiO₂ underlayer had a compact columnar microstructure with thickness of around 1 µm while the Ag-FHAp overlayer presented large plate-like crystals accompanied with small rounded particles with thickness about 10 µm. Potentiodynamic polarization test exhibited that the double layer SiO₂/Ag-FHAp coated Mg alloy has superior corrosion resistance compared to uncoated and single layer SiO₂ coated samples. Contact angle measurement showed that Ag-FHAp coating over nano-SiO₂ layers significantly increased surface wettability which is favorable for the attachment of cells. Cytotoxicity tests indicated that the nanostructured SiO₂/Ag-FHAp coating enabled higher cell viability compared to nano-SiO₂ coating and uncoated samples. In addition, bi-layer and single-layer coatings considerably improved the ability of cell attachment than that of the uncoated samples. The cell viability of coated and uncoated samples increased with increasing incubation time. The double layer SiO₂/Ag-FHAp coated biodegradable Mg alloy possessed high corrosion resistance and cytocompatibility and can be considered as a promising material for implant applications.     

Corrosion Resistance of MgZn Alloy Covered by Chitosan-Based Coatings

Chitosan coatings are deposited on the surface of Mg20Zn magnesium alloy by means of the spin coating technique. Their structure was investigated using Fourier Transform Infrared Spectroscopy (FTIR) an X-ray photoelectron spectroscopy (XPS). The surface morphology of the magnesium alloy substrate and chitosan coatings was determined using Scanning Electron Microscope (FE-SEM) analysis. Corrosion tests (linear sweep voltamperometry and chronoamperometry) were performed on uncoated and coated magnesium alloy in the Hank’s solution. In both cases, the hydrogen evolution method was used to calculate the corrosion rate after 7-days immersion in the Hank’s solution at 37 °C. It was found that the corrosion rate is 3.2 mm/year and 1.2 mm/year for uncoated and coated substrates, respectively. High corrosion resistance of Mg20Zn alloy covered by multilayer coating (CaP coating + chitosan water glass) is caused by formation of CaSiO₃ and Ca₃(PO₄)₂ compounds on its surface.     

Study on properties of Hf6Ta2O17/Ta2O5 system: A potential candidate for environmental barrier coating (EBC)

Ta₂O₅ doped Hf₆Ta₂O₁₇ system (Hf₆Ta₂O₁₇/Ta₂O₅) is considered to have potential application prospect in the field of aero-engine. We herein focus on the thermo-physical, mechanical properties and CMAS corrosion resistance of Hf₆Ta₂O₁₇/Ta₂O₅ to systematically evaluate the possibility for the application of environmental barrier coating (EBC). By changing the content of Ta₂O₅, the gradient adjustment of thermal expansion coefficient can be realized while maintaining low thermal conductivity (1.5–2.2 W/(m·K)). The introduction of Ta₂O₅ significantly reduces the modulus and improves the fracture toughness. Single-phase Hf₆Ta₂O₁₇ shows excellent corrosion resistance against molten calcium-magnesium-alumina-silicate (CMAS). The crystallization of CaTa₂O₆ and HfSiO₄ is the important factor to prevent further corrosion. The introduction of Ta₂O₅ weakens the ability to prevent Si penetration and greatly increases the thickness of the corrosion layer. The results highlight the merit of Hf₆Ta₂O₁₇/Ta₂O₅ system as potential candidate for multi-layer gradient coating on the surface of ceramic matrix composites.     

Evaluation of the corrosion resistance of Ni-Co-B coatings in simulated PEMFC environment

The corrosion resistance behavior of Ni-Co-B coated carbon steel, Al 6061 alloy and 304 stainless steel was evaluated in simulated proton exchange membrane fuel cell (PEMFC) environment. The phase structure of the NiCoB based alloy was determined by Rietveld analysis. The PEMFC environment was constituted of 0.5 M H₂SO₄ at 60 °C and the evaluation techniques employed included potentiodynamic polarization, linear polarization resistance, open circuit potential measurements and electrochemical impedance spectroscopy. The results showed that in all cases the corrosion resistance of the Ni-Co-B coating was higher than that of the uncoated alloys; about two orders of magnitude with respect to carbon steel and an order of magnitude compared to 304 stainless steel. Except for the uncoated 304 type stainless steel, the polarization curves for the coated specimens did not exhibit a passive region but only anodic dissolution. The corrosion potential value, E_corr, was always nobler for the coated samples than for the uncoated specimens. This was true for the stainless steel in the passive region, but in the active state for the carbon steel and Al 6061 alloy. The corrosion of the underlying alloy occurred due to filtering of the solution through coating defects like microcracks, pinholes, etc. During the filtering process the E_corr value of the coating decreased slowly until it reached a steady state value, close to the E_corr value of the underlying alloy.     

Physico-chemical and antimicrobial properties of Ag/Ta2O5 nanocomposite coatings

Surface modification of surgical instruments is carried out in order to improve the antibacterial performance against the surgical site infections. Healthcare acquired infections (HAI) and Nosocomial infections are one of the leading causes of complications/deaths after surgery. There is an increasing trend of antibiotic resistance in bacteria such as, vancomycin-resistant Enterococcus (VRE), carbapenem-resistant Enterobacteriaceae (CRE), multi-drug-resistant Mycobacterium tuberculosis (MDR-TB), methicillin-resistant Staphylococcus aureus (MRSA), and Neisseria gonorrhoeae. Thus, surfaces that counteract the adherence and growth of bacteria are employed to avoid the infections. In present study, stainless steel 316 L (SS 316 L) was coated with Silver/Tantalum oxide (Ag/Ta₂O₅) nanocomposite using reactive magnetron sputtering. The as-sputtered Ag/Ta₂O₅ nanocomposite (a-Ag/Ta₂O₅) film was crystallized via thermal treatment at 400 °C. Due to the annealing, the AgNPs migrated to the surface through the columnar paths of the a-Ag/Ta₂O₅. Thus, the crystallized layer (c-Ag/Ta₂O₅) exhibited 302% improvement in adhesion strength and enhanced hydrophopibicity. The c-Ag/Ta₂O₅ also demonstrated excellent antibacterial performance against Staphylococcus aureus (NCTC 6571) (gram-positive bacteria) and Escherichia coli (ATCC 15597) (gram-negative bacteria) according to the inhibition zone measurements. These results suggest that c-Ag/Ta₂O₅ deposition on SS 316 L substrate has a high potential to serve as an adherent, antibacterial layer on the surgical tools, in order to resist surgical site infections.     

Effects of pH value and temperature on the corrosion behavior of a Ta2N nanoceramic coating in simulated polymer electrolyte membrane fuel cell environment

To improve the corrosion resistance and electrical conductivity of Ti-6Al-4V bipolar plates used in polymer electrolyte membrane fuel cells (PEMFCs), a novel electro-conductive Ta₂N nanoceramic coating was developed by reactive sputter-deposition using a double cathode glow discharge plasma technique. The microstructure of the coating consisted of fine equiaxed Ta₂N grains with an average grain size of ∼13 nm, which exhibited a strong (101) preferred orientation. To explore the influence of both pH values and temperatures on the corrosion resistance of the coating, the electrochemical behaviors and electronic properties of passive films grown on the Ta₂N coating were systematically investigated using different electrochemical techniques in simulated PEMFC operating environment. It was shown that either increasing the acidity or the temperatures of the solution, the corrosion potential (E_corr) decreased and the corrosion current density (i_corr) increased. At a given temperature or pH value, the Ta₂N coating had a higher E_corr and lower i_corr as compared with uncoated Ti-6Al-4V. The results of EIS measurements showed that with increasing temperature or acidity of the solution, the resistance of the passive film (R_p) formed on the Ta₂N coating decreased slightly, being of the order of magnitude of 10⁷ Ω cm², which was an order of magnitude higher than that of uncoated Ti-6Al-4V. The interfacial contact resistance (ICR) values were found to increase with increasing pH value or decreasing solution temperature, and the ICR values of the Ta₂N coating were markedly lower than that of uncoated Ti-6Al-4V, due to the thinner thickness of passive films. Furthermore, the Ta₂N-coated Ti-6Al-4V is more hydrophobic than bare Ti-6A1-4V, which was favorable for both the simplification of water management and improving corrosion resistance in PEMFC operating environment.     

Controlling the degradation rate of bioactive magnesium implants by electrophoretic deposition of akermanite coating

In order to improve the corrosion resistance and the surface bioactivity of biodegradable magnesium alloys, a nanostructured akermanite (Ca₂MgSi₂O₇) coating was grown on AZ91 magnesium alloy through electrophoretic deposition (EPD) assisted with micro arc oxidation (MAO) method. The crystalline structures, morphologies and compositions of samples were characterized by X–ray diffraction, scanning electron microscopy and energy dispersive spectroscopy. The in vitro bio–corrosion (biodegradability) and bioactivity behaviors of samples were investigated by electrochemical and immersion tests. The experimental results indicated that the nanostructured akermanite coating could slow down the corrosion rate and improve the in vitro bioactivity of biodegradable magnesium alloy. Thus, magnesium alloy coated with nanostructured akermanite may be a promising candidate to be used as biodegradable bone implants.     

The Potential of Calcium/Phosphate Containing MAO Implanted in Bone Tissue Regeneration and Biological Characteristics

Micro arc oxidation (MAO) is a prominent surface treatment to form bioceramic coating layers with beneficial physical, chemical, and biological properties on the metal substrates for biomaterial applications. In this study, MAO treatment has been performed to modify the surface characteristics of AZ31 Mg alloy to enhance the biocompatibility and corrosion resistance for implant applications by using an electrolytic mixture of Ca₃(PO₄)₂ and C₁₀H₁₆N₂O₈ (EDTA) in the solutions. For this purpose, the calcium phosphate (Ca-P) containing thin film was successfully fabricated on the surface of the implant material. After in-vivo implantation into the rabbit bone for four weeks, the apparent growth of soft tissues and bone healing effects have been documented. The morphology, microstructure, chemical composition, and phase structures of the coating were identified by SEM, XPS, and XRD. The corrosion resistance of the coating was analyzed by polarization and salt spray test. The coatings consist of Ca-P compounds continuously have proliferation activity and show better corrosion resistance and lower roughness in comparison to mere MAO coated AZ31. The corrosion current density decreased to approximately 2.81 × 10⁻⁷ A/cm² and roughness was reduced to 0.622 μm. Thus, based on the results, it was anticipated that the development of degradable materials and implants would be feasible using this method. This study aims to fabricate MAO coatings for orthopedic magnesium implants that can enhance bioactivity, biocompatibility, and prevent additional surgery and implant-related infections to be used in clinical applications.     

In Vitro Macrophage Immunomodulation by Poly(ε-caprolactone) Based-Coated AZ31 Mg Alloy

Due to its excellent bone-like mechanical properties and non-toxicity, magnesium (Mg) and its alloys have attracted great interest as biomaterials for orthopaedic applications. However, their fast degradation rate in physiological environments leads to an acute inflammatory response, restricting their use as biodegradable metallic implants. Endowing Mg-based biomaterials with immunomodulatory properties can help trigger a desired immune response capable of supporting a favorable healing process. In this study, electrospun poly(ε-caprolactone) (PCL) fibers loaded with coumarin (CM) and/or zinc oxide nanoparticles (ZnO) were used to coat the commercial AZ31 Mg alloy as single and combined formulas, and their effects on the macrophage inflammatory response and osteoclastogenic process were investigated by indirect contact studies. Likewise, the capacity of the analyzed samples to generate reactive oxygen species (ROS) has been investigated. The data obtained by attenuated total reflection Fourier-transform infrared (FTIR-ATR) and X-ray photoelectron spectroscopy (XPS) analyses indicate that AZ31 alloy was perfectly coated with the PCL fibers loaded with CM and ZnO, which had an important influence on tuning the release of the active ingredient. Furthermore, in terms of degradation in phosphate-buffered saline (PBS) solution, the PCL-ZnO- and secondary PCL-CM-ZnO-coated samples exhibited the best corrosion behaviour. The in vitro results showed the PCL-CM-ZnO and, to a lower extent, PCL-ZnO coated sample exhibited the best behaviour in terms of inflammatory response and receptor activator of nuclear factor kappa-B ligand (RANKL)-mediated differentiation of RAW 264.7 macrophages into osteoclasts. Altogether, the results obtained suggest that the coating of Mg alloys with fibrous PCL containing CM and/or ZnO can constitute a feasible strategy for biomedical applications.     

Strontium and copper co-substituted hydroxyapatite-based coatings with improved antibacterial activity and cytocompatibility fabricated by electrodeposition

Bacterial infection are serious complications for biomedical implants in the orthopedic and dental fields, and the ideal implants should combine good antibacterial ability and bioactivity. In this paper, we have fabricated the strontium/copper substituted hydroxyapatite (SrCuHA) coating on the commercially pure titanium (CP-Ti) and studied their effect on antibacterial and in vitro cytocompatible properties. Cu was incorporated into HA in order to improve its antimicrobial properties. Sr was added as a second binary element to improve the biocompatibility. The structural and morphological characteristics of the SrCuHA coatings were investigated using various analytical techniques. The presence of Sr²⁺ and Cu²⁺ in solution led to reduced roughness of the coating and finer nucleus size formed. The results highlight that Sr²⁺ and Cu²⁺ were homogenously incorporated into HA lattice to form SrCuHA coatings. Inductively coupled plasma mass spectrometry (ICP-MS) was used for the leach out analysis of the samples. A low contact angle value revealed the hydrophilic nature. In vitro electrochemical corrosion studies indicated that the SrCuHA coating sustain in the stimulated body-fluid (SBF), exhibiting superior corrosion resistance with a lower corrosion penetration rate than the bare CP-Ti substrate. The SrCuHA coatings can kill Escherichia coli to a certain extent during the first few days, which might be due to the Cu substitution in the coating. An enhancement of in vitro osteoblast adhesion, proliferation, and alkaline phosphatase activity was observed, which could lead to the optimistic orthopedic and dental applications.     

Structure and surface properties of Al2O3–TiO2 ceramic coated AZ31 magnesium alloy

Magnesium and its alloys are the engineering materials which have the potential ability to be able to used widely particularly in the automotive, aerospace and in the biomedical sectors, especially thanks to their features such as lightness, specific strength that they have and biocompatibility. However, due to their poor wear resistance and corrosion resistance, the areas of usage are being restricted. This situation prevents Mg alloys to be used without any surface protection despite their good mechanical properties such as high strength/weight ratio. In this study, plasma spraying method is used to improve the poor corrosion resistance of AZ31 Mg alloy. Al₂O₃–13 wt% TiO₂ (AT13) and Al₂O₃–40 wt% TiO₂ (AT40) composite ceramic coatings were coated successfully on the surfaces of AZ31 Mg samples. The wear properties of the AT13 and AT40 coated samples were investigated for tribological applications. Surface morphology and microstructure of the duplex treated samples were analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The microhardness value of the uncoated AZ31 Mg alloy is 40±3 HV_0.1, while the microhardness values of the AT40 and AT13 coatings are enhanced to 800±39 HV_0.1 and 1500±35 HV_0.1, respectively.     

In-vitro corrosion inhibition mechanism of fluorine-doped hydroxyapatite and brushite coated Mg–Ca alloys for biomedical applications

Magnesium alloys have received great attention as a new kind of biodegradable metallic biomaterials. However, they suffer from poor corrosion resistance. In this study, Mg–Ca alloy was coated with nano-fluorine-doped hydroxyapatite (FHA), and brushite (DCPD); via electrochemical deposition (ED). Coatings were characterized by X-ray diffraction (XRD), Fourier-transformed infrared spectroscopy (FTIR), transmission electron microscopy (TEM), scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). The results revealed that nano-fluorine-doped hydroxyapatite coating produced more dense and uniform coating layer, compared to the brushite coating. The compression tests of the ED-coated Mg alloy samples immersed in simulated body fluid for different time periods showed higher yield strength (YS) and ultimate tensile strength (UTS), compared to those of the uncoated samples. The degradation behavior and corrosion properties of the ED-coated Mg alloy samples were examined via electrochemical measurements and immersion tests. The results showed that FHA coating could effectively induce the precipitation of more Ca²⁺ and PO₄³⁻ ions than DCPD coating, because the nanophase can provide higher specific surface area. It was also found that FHA and DCPD coatings can significantly decline the initial degradation rate of the alloy. A corrosion mechanism of the ED-coated alloy is proposed and discussed in this paper.     

Microstructure and properties of Nb2O5/Mg gradient coating on AZ31 magnesium alloy by magnetron sputtering

A Nb₂O₅/Mg gradient coating was synthesized on AZ31 magnesium alloy through the magnetron sputtering technique. The microstructure and properties of the coating were investigated by SEM, AFM, EDS and XPS, scratch tester, nanoindenter, friction tester, and electrochemical workstation, with a Nb₂O₅ monolayer coating as a control. The results show that all the as-disposed films have an amorphous columnar structure, and can improve the mechanical, anti-wear and anti-corrosion properties of AZ31 magnesium alloy. The Nb₂O₅/Mg gradient coating shows a gradual change in chemical composition through its depth, decreasing the residual stress of the coating/substrate system, thus reducing the risk of film cracking, and increasing compactness of the coating. Compared with a Nb₂O₅ single-layer film of the same thickness, the gradient coating exhibits increased adhesion, H/E and H³/E² increased by about 16 times, 7.8% and 100% respectively, and a wear rate reduced by more than an order of magnitude. In addition, the gradient coating has better corrosion resistance, having a two orders of magnitude lower current density and one order of magnitude higher polarization resistance. This study provides a workable strategy for improving the performance of ceramic coatings on magnesium alloy, for medical applications.     

Improving the adhesive,mechanical, tribological properties and corrosion resistance of reactive sputtered tantalum oxide coating on Ti6Al4V alloy via introducing multiple interlayers

Tantalum oxide film has become an investigation focus for surface modification materials in the biomedical field owing to its outstanding biocompatibility, anti-corrosion, and anti-wear performances. However, tantalum oxide films exhibit poor adhesion because of the mismatch between the properties of the film and the substrate. In this study, a novel multilayer tantalum oxide coating of Ta_mO_n/Ta_mO_n-TiO₂/TiO₂/Ti (code M-Ta_mO_n) was deposited on Ti6Al4V by magnetron sputtering with Ta_mO_n single-layer coating as control. The purpose of this work is to evaluate the influence of the introduced Ta_mO_n-TiO₂/TiO₂/Ti multi-interlayer on the microstructure, adhesive, mechanical, and anti-corrosion properties of reactive sputtered tantalum oxide coatings. The outcomes show that the Ta_mO_n-TiO₂/TiO₂/Ti intermediate layer improves the bonding strength between the Ta_mO_n layer and Ti6Al4V matrix from 17.83 N to over 50 N and enables the Ta_mO_n coating to have an increased H/E and H³/E² ratio, decreased friction coefficient and wear rate, raised potential, and reduced corrosion current density. The improved properties of the multilayer system are attributed to the positive effects of the inserted multiple interlayers in reducing the residual stress in the coating, coupling the mechanical performance between the layer and the substrate, blocking the continuous growth of penetrating defects in a film with columnar structure. These experimental results provide a workable route for improving the properties of the tantalum oxide coating on Ti6Al4V alloy for medical applications.     

Black plasma-sprayed Ta2O5 coatings with photothermal effect for bone tumor therapy

In this work, a black vacuum-plasma-sprayed Ta₂O₅ coating (VTO) was fabricated using white Ta₂O₅ powder as a raw material. Interestingly, a gray Ta₂O₅ coating was obtained by heat treatment of VTO coating (HVTO). The morphology, phase composition, photothermal conversion and cancer therapy effect in vitro of VTO and HVTO were comprehensively evaluated. Experimental results showed that VTO exhibited higher photothermal conversion effect and had an efficiency of 30.8% with high photostability. It has been proved that the VTO coating could be used in potential applications for bone tumor therapy.