A study on tribological behaviour of transfer films of PTFE/bronze composites

Transfer films of PTFE/bronze composites with 5–30% volume content of bronze were prepared using a RFT friction and wear tester on surface of AISI-1045 steel bar by different sliding time (5–60 min). Tribological properties of these transfer films were studied using a DFPM reciprocating tribometer in a point contacting configuration under normal loads of 0.5, 1.0, 2.0 and 3.0 N. Thickness and surface morphology of the transfer films were investigated. It was found thickness of the transfer films slightly increased along with the increase of bronze content of corresponding composites. Increased sliding time of transfer film preparation is helpful to form transfer film with better ductibility and continuity, but sliding time almost has no effect on tribological properties of the transfer film. Higher bronze content in the composite improved tribological properties of the corresponding transfer film, i.e., reduced friction coefficient and prolonged wear life. All these transfer films are sensitive to load change. Their wear life becomes shorter along with the increase of load. SEM image of the worn surface show fatigue wear and adhesion wear have happened on the transfer film during the friction process. The author believe bronze in the transfer film effectively partaked in shear force applied on the transfer film and its good ductibility helped to improve tribological properties of the transfer films.     

Tribological properties of ultra-thin ionic liquid films on single-crystal silicon wafers with functionalized surfaces

Two kinds of room temperature ionic liquid (RTIL) films carrying vinyl and hydroxyl functional groups were prepared on single-crystal Si wafers by spin coating. The tribological properties of the RTIL films sliding against AISI-52100 steel ball and Si₃N₄ ball in a ball-on-plate configuration were investigated on a dynamic–static friction coefficient measurement apparatus, using perfluoropolyether (PFPE) film as a comparison. The tribological behaviors of the ionic liquid films sliding against the same counterparts at extended test durations were also evaluated using a universal UMT-2MT test rig. The morphologies of the wear tracks of the RTIL films and the counterparts were examined using a scanning electron microscope equipped with an energy-dispersive X-ray analyzer attachment. It was found that the tribological performances of the ionic liquid films were closely related to the chemical structures of the RTILs and the chemical characteristics of the substrate surfaces. The films of vinyl group functionalized ionic liquids on hydroxylated substrate and vinyl group modified substrate exhibited very good friction-reduction and wear-resistant properties. It was assumed that there were enough strong forces between the films and substrate in these cases, and the ionic liquid molecules maintained good flexibility simultaneously. The films on hydrogen-terminated and methyl-terminated substrate showed poor tribological performance, which could be related to the relatively weak forces between the films and substrates. Moreover, the films on hydroxylated substrate showed lower friction at higher sliding velocities, which was assumed to be governed by the more rapid adsorption of the ionic liquid molecules on the steel ball at a higher sliding velocity. In addition, the ionic liquid films also had excellent tribological properties as they slid against silicon nitride ball. Therefore, it was supposed that the ionic liquid films could be used as a kind of universal lubricant for various combinations of the frictional pair.     

Characterization and tribological investigation of sol–gel ceramic films on Ti–6Al–4V

SiO₂, TiO₂, and hydroxyapatite (HA) thin films with good biocompatibility were grown on Ti–6Al–4V (coded as TC4) substrate by sol–gel and dip-coating processes from specially formulated sols, followed by annealing at 500 °C The chemical states of some typical elements in the target films were detected by means of X-ray photoelectron spectroscopy (XPS). Atomic force microscopy (AFM) and high-resolution scanning electron microscopy (SEM) are applied to characterize the original unworn films. The tribological properties of thin films sliding against an AISI52100 steel ball were evaluated on a reciprocating friction and wear tester. As the result, the target films composed of nano-particles ranging from 30 nm to 100 nm around were obtained. All the sol–gel ceramic films are superior in resisting wear compared with the TC4 substrate. Among all, HA film shows the best resistance while SiO₂ film shows the worst wear resistance both under higher (3 N) and lower load (1 N). TiO₂ shows good wear resistance under lower load (1 N). SEM observation of the morphologies of worn surfaces indicates that the wear of TC4 is characteristic of abrasive wear. Differently, abrasion, plastic deformation and micro-fracture dominate the wear of ceramic films. The superior friction reduction and wear resistance of HA film is greatly due to the slight plastic deformation of the film. It is supposed that the deformation of the HA film is closely related to the special arrangement of the nano-particles and microstructure. HA film is recommended for clinical application from the point of wear resistance view.     

Nano/Microtribological Properties of Ultrathin Functionalized Imidazolium Wear-Resistant Ionic Liquid Films on Single Crystal Silicon

Ionic liquids (ILs) are considered as a new kind of lubricant for micro/nanoelectromechanical system (M/NEMS) due to their excellent thermal and electrical conductivity. However, so far, only few reports have investigated the tribological behavior of molecular thin films of various ILs. Evaluating the nanoscale tribological performance of ILs when applied as a few nanometers-thick film on a substrate is a critical step for their application in MEMS/NEMS devices. To this end, four kinds of ionic liquid carrying methyl, hydroxyl, nitrile, and carboxyl group were synthesized and these molecular thin films were prepared on single crystal silicon wafer by dip-coating method. Film thickness was determined by ellipsometric method. The chemical composition and morphology were characterized by the means of multi-technique X-ray photoelectron spectrometric analysis, and atomic force microscopic (AFM) analysis, respectively. The nano- and microtribological properties of the ionic liquid films were investigated. The morphologies of wear tracks of IL films were examined using a 3D non-contact interferometric microscope. The influence of temperature on friction and adhesion behavior at nanoscale, and the effect of sliding frequency and load on friction coefficient, load bearing capacity, and anti-wear durability at microscale were studied. Corresponding tribological mechanisms of IL films were investigated by AFM and ball-on-plane microtribotester. Friction reduction, adhesion resistance, and durability of IL films were dependent on their cation chemical structures, wettability, and ambient environment.     

Tribological properties of anatase TiO<Subscript>2</Subscript> sol–gel films controlled by mutually soluble dopants

Tribological properties of TiO2 sol–gel thin films with mutually soluble dopants were studied on a glass substrate. The results showed that the formation of mutually soluble solid solution played a very important role in the growth of titania grains. The fine-grained TiO₂ films controlled by SiO₂ dopant were superior to pure TiO₂ film in wear resistance and endurance life, although both films greatly improve the surface characteristics of glass substrate, enhancing its tribological characteristics. High resistance to microfracture because of the very small grain size as well as a good adhesion of the film to the substrate is believed to be the determining factors influencing the tribological properties of SiO₂ doped TiO₂ films. However, excessive SiO₂ seriously deteriorates wear resistance of film due to phase separation. The wear mechanisms were also discussed based on the observation of the surface morphologies by scanning electron microscope (SEM).     

Carbon Nanotube Reinforced Polyimide Thin-film for High Wear Durability

In this paper, the influence of single walled carbon nano tubes (SWCNTs) addition on the tribological properties of the polyimide (PI) films on silicon substrate was studied. PI films, with and without SWCNTs, were spin coated onto the Si surface. Coefficient of friction and wear durability were characterized using a ball-on-disk tribometer by employing a 4 mm diameter Si₃N₄ ball sliding against the film, at a contact pressure of ∼370 MPa, and a sliding velocity of 0.042 ms⁻¹. Water contact angle, AFM topography, and nano-indentation tests were conducted to study the physical and mechanical properties of the films. SWCNTs marginally increased the water contact angle of PI film. The addition of SWCNTs to PI has increased the hardness and elastic modulus of pristine PI films by 60–70%. The coefficient of friction of PI films increased slightly (∼20%) after the addition of SWCNTs, whereas, there was at least two-fold increase in the wear life of the film based on the film failure condition of coefficient of friction higher than 0.3. However, the film did not show any sign of wear even after 100,000 cycles of rotation indicating its robustness. This increase in the wear durability due to the addition of the SWCNTs is believed to be because of the improvement in the load-bearing capacity of the composite film and sliding induced microstructural changes of the composite film.     

A study of the friction and wear performance of MoSx thin films produced by ion beam enhanced deposition and magnetron sputtering

MoS_x thin films were deposited by ion beam enhanced deposition (IBED) and magnetron sputtering (MS) onto the surface of IBEN Si₃N₄ and TiN thin films. The friction and wear performances of thin films and 52100 steel were compared using an SRV model reciprocating testing machine. The results showed that all MoS_x films exhibit good tribological behavior. The MS MoS_x thin film has better wear resistance and the IBED MoS_x film has a longer wear life. The wear resistance of IBED Si₃N₄ and TiN thin film plus MoS_x film is 3–4 times and 8–20 times that of single IBED Si₃N₄ and TiN thin films and 52100 steel respectively. The analyses indicate that the difference in friction and wear performance between the two kinds of MoS_x thin film is determined by the x value of MoS_x, its microstructure and the atom mixing effect at the interface.     

PDDA/PSS分子沉积膜的摩擦学行为研究

以聚对苯乙烯磺酸钠为聚阴离子,聚二烯丙基二甲基胺盐酸盐为聚阳离子在基底上交替沉积制备分子沉积膜。用紫外-可见吸收光谱仪、接触角测量仪、原子力显微镜对所制备的有序薄膜进行了表征。用UMT-2摩擦仪考察了超薄膜的摩擦学行为,结果表明,所制备的超薄膜具有良好的减摩抗磨性能,薄膜的表面电荷及亲水、疏水性对其摩擦学行为有较大影响,负电荷表面、亲水性强的表面在较高湿度下,耐磨寿命较长。     

碳靶电流对磁控溅射GLC/Ti薄膜结构及摩擦学性能的影响*

为改善掺杂Ti的GLC/Ti薄膜的摩擦学性能,采用非平衡磁控溅射技术在不同C靶电流下制备了类石墨碳基薄膜。利用扫描电子显微镜(SEM)、拉曼光谱仪(Raman)对薄膜结构进行表征;采用纳米压痕仪测量薄膜的硬度及弹性模量;利用HSR-2M型高速往复试验机测试薄膜在干摩擦条件下的摩擦磨损性能,并用白光干涉仪观察磨痕表面形貌。结果表明:随着C靶电流的增大,薄膜的柱状生长趋势日趋明显,其致密性降低,sp~2键含量减小,石墨化程度和结合力降低,而硬度和弹性模量略增;随着C靶电流的增大,摩擦因数和磨损率均增大。因此,适当降低C靶电流可以提高磁控溅射GLC/Ti薄膜干摩擦条件下的减摩耐磨性能。     

Effect of Water Swelling on the Tribological Properties of PMMA Spin-Cast Film and Brush in Aqueous Environment

Due to their light weight, low corrosion and good tribological properties, polymer films have been widely studied in dry condition as well as recently in aqueous environment. Though the presence of water can further reduce the friction, it promotes the wear rate of the polymer films. As a remedy to decrease the wear rate of polymer films under aqueous condition, in this study, we used PMMA brush which is chemically anchored to a substrate and compared its friction and wear properties with those of conventional PMMA spin-cast film. Ellipsometry, contact angle measurements and atomic force microscopy are used to study the surface properties, e.g., wear mechanisms and wear depths of PMMA films. Under different sliding speeds and applied loads, PMMA brush showed lower friction than PMMA spin-cast film in aqueous. Moreover, it was shown that the swelling of water molecules is a dominant factor in determining the wear durability of PMMA films in which PMMA brush showed better wear performance than PMMA spin-cast film.     

Measurements of tribological properties of poly(pyrrole) thin film bearings

We report the results of a recent study on the tribological properties of electropolymerised thin films at light loads and low speeds. Poly(pyrrole) films incorporating different counter-ions have been electrochemically deposited onto gold electrodes on the plano-convex glass substrates and studied extensively. The measuring apparatus has been greatly improved from that reported earlier and now provides simultaneous monitoring of frictional force and wear. High precision capacitive gauging is employed to provide high resolutions of frictional force of better than 100 μN and height variation (wear) of 2 nm. A large number of specimens of poly(pyrrole) grown from five different counter-ions were prepared and their performances evaluated. The film morphology of each type of film was examined by atomic force microscopy (AFM) for control of the variability of film formation. Results are presented for the friction coefficients and wear rates observed for the films typically at a load of 2 N and a sliding speed of 5 mm s⁻¹. The effects of normal loading force and sliding speed on the friction coefficient are also discussed with a load range of 0.2–5 N and a sliding speed up to 30 mm s⁻¹.     

Tribological Performance of UHMWPE and PFPE Coated Films on Aluminium Surface

A thin layer of Ultra High Molecular Weight Polyethylene (UHMWPE) or UHMWPE + PFPE is coated onto cylindrical aluminium (Al) pin (4.6 mm diametre) surface with the aim of providing wear resistant coating on this soft and tribologically poor metal. The coefficient of friction and wear life of the coated samples are investigated on a pin-on-disk tribometre under different normal loads (394–622 g) and two sliding speeds (0.1 and 0.31 m/s) against uncoated Al disk as the counterface. Both coatings provide coefficient of friction values in the range of 0.02–0.2 as compared to 0.4–1.0 for uncoated Al. There is tremendous improvement in the wear life of the pin, with UHMWPE + PFPE film giving wear life approximately twice to thrice higher than that with only UHMWPE film. A thin polymer film is transferred to the disk surface during sliding providing very long-term wear life (continuous low coefficient of friction) despite visual removal of the film from the pin surface. The present films will have applications in gears and bearings as solid or boundary lubricants for automotive and aerospace component.     

Tribological properties of self-assembled monolayers on Au,SiOx and Si surfaces

Using interfacial force microscopy (IFM), the tribological properties of self-assembled monolayers (SAM) on Si surfaces produced by a new chemical strategy are investigated and compared to those of “classical” SAM systems, which include alkanethiols on Au and alkylsilanes on SiO_x. The new SAM films are prepared by depositing n-alkyl chains with OH-terminations onto Cl-terminated Si substrates. The chemical nature of the actual lubricating molecules, n-dodecyl, is kept constant in all three thin film systems for direct comparison and similarities and differences in tribological properties are observed. The adhesion strength is virtually identical for all three systems; however, frictional properties differ due to differences in film packing. Differences in the chemical bonds that attach the lubricant molecules to the substrate are also discussed as they influence variations in film wear and durability. It is demonstrated that the new SAM films are capable of controlling the friction and adhesion of Si surfaces equally well as the classical SAMs and are potentially more reproducible and more durable.     

Cr12MoV钢表面磁控溅射TiB2-TiN薄膜的摩擦磨损性能

采用磁控溅射技术在淬火态Cr12MoV表面制备SiC/TiN、SiC/TiB2-TiN薄膜(SiC为中间层),研究TiN、TiB2-TiN薄膜的组织结构和摩擦磨损性能。结果表明,SiC薄膜与基材和TiN、TiB2-TiN薄膜间都具有明显的且呈梯度的元素扩散,界面结合良好。在水润滑条件下与钢球对摩时(载荷0.5 N,时间0.5 h),TiN薄膜、TiB2-TiN薄膜具有良好摩擦磨损性能,其平均摩擦因数分别为0.33、0.31,低于淬火态Cr12MoV的0.45,磨损速率分别为2.0×10-8和1.5×10-8mm3/(N.m),低于淬火态Cr12MoV的8.66×10-7mm3/(N.m),其中在水润滑条件下TiB2-TiN薄膜比TiN薄膜具有更好的摩擦磨损性能。     

Effect of Molecular Structure on Friction and Wear of Polymer Thin Films Deposited on Si Surface

In this study, the influence of the molecular structure (linear or with bulky side groups) of polymer films covalently attached to Si surface on tribological properties is investigated. Two polymers, PE (polyethylene) and PS (polystyrene), are selected where PE has simple linear molecular structure whereas PS has linear molecular structure but contains bulky benzene groups located at the sides of the linear chain. PE and PS molecules, both with reactive maleic anhydride groups, are chemisorbed onto Si via an intermediate APTMS SAM (3-aminopropyltrimethoxysilane self-assembled monolayer). Water contact angle measurements, AFM (atomic force microscopy), ellipsometry, and XPS (X-ray photoelectron spectroscopy) are used to identify and characterize the polymer films. Tribological properties are studied using a microtribometer where a 4 mm diameter Si₃N₄ ball is used as the counterface. Among the two polymer films investigated, Si/APTMS/PE has shown very low coefficient of friction (0.08) and high wear life (∼4,400 cycles) than those of Si/APTMS/PS. Surprisingly, Si/APTMS/PS did not show any improvement in tribological properties when compared to that of bare Si. The present study proves that the polymer with linear molecular structure without the bulky side groups show good tribological properties even when it is coated as a thin film and hence such polymers can be used as thin-films for reducing friction and wear of substrates such as Si or other materials.     

Investigation of the Tribological Behaviors of Polymer Molecular Deposition Films by Tribometer Based on Interferometer

The polymer molecular deposition films including polyelectrolyte molecular deposition (PEMD) film and nanoparticles composite molecular deposition (NPs/MD) film have been prepared using the molecular deposition method and the in situ synthesize method. The polymer molecular deposition films were characterized by atomic force microscope (AFM) and X-ray photoelectron spectroscopy (XPS). The tribological behaviors of the substrate and polymer molecular deposition films were investigated by a tribometer based on interferometer. It is found that the NPs/MD film has a lower friction force and a better anti-wear property than the PEMD film under the dry friction. The poly alpha olefin (PAO2) and water films confined between samples and steel ball surfaces have been investigated using thin film interferometry. The friction force of substrate was lower than the polymer molecular deposition films under PAO2 lubrication. The friction forces alteration of PEMD film and NPs/MD film were similar and consistent, and lower than that for substrate under water lubrication.     

Amorphous hydrogenated carbon films for tribological applications I. Development of moisture insensitive films having reduced compressive stress

Although earlier investigations on the tribological behaviour of amcrphous hydrogenated carbon (AHC) films in sliding contact with steel showed encouraging results, four open issues were identified. They were: (a) dependence of friction and wear on humidity (i.e., the friction coefficient and the wear increased with humidity), (b) limitations on film thickness (i.e., films greater than 2 μm thick delaminated due to large compressive stress), (c) deposition of films on substrates other than silicon and (d) lubricant compatibility (i.e., formation of lubricant-derived antiwear films on AHC film surfaces). Steps were taken to address some of these open issues by incorporating silicon in AHC films. Friction and wear tests were conducted on AHC films containing various amounts of silicon. Incorporation of silicon in AHC films rendered the friction coefficients and the wear of a steel counterface insensitive to moisture. Silicon incorporation in AHC films also significantly reduced compressive stress. This allowed deposition of 10 μm thick films. These effects were achieved without any compromise with the friction coefficient and the film wear if the amount of silicon in the film was kept within a certain concentration range. In addition, silicon-containing AHC films were thermally more stable than silicon-free films. Experiments conducted with two lubricants resulted in significantly lower wear of the silicon-free AHC films than that obtained for unlubricated sliding. Similar friction coefficients were obtained for AHC film/steel and steel/steel combinations in lubricated sliding.     

A comparative study on the microstructure and tribological properties of Si3N4 and TiN films produced by the IBED method

The tribological properties of Si₃N₄ and TiN thin films produced by ion beam enhanced deposition (IBED) were compared on a SRV friction and wear testing machine. The friction coefficient of all thin films shows a descending tendency with increase in load, and is lower than that of 52100 steel. All the IBED films show a much better wear resistance than 52100 steel, especially in the higher load and frequency ranges; it can reach six times that of the latter. In order to understand the reasons for their excellent properties, the microstructure, microhardness and bonding strength with the substrate were analysed by SEM, X-ray diffraction, Knoop hardness and scratching test methods separately. The results show that the TiN(1) film exhibits the best tribological properties, which are closely related with its greater hardness and bonding strength.     

Preparation of functional ionic liquids and tribological investigation of their ultra-thin films

Novel ionic liquid materials based on 1-alkyl-4-[5-(alkylsulfanyl)-1,3,4-oxadiazol-2-yl] pyridinium tetrafluoroborate derivatives were synthesized. Ultra-thin ionic liquid films were prepared on silicon wafers by means of spin-coating and their tribological properties were investigated. The wear life increases when the chain length decreases. Under low load, they show good tribological properties which are closely related to the interaction between ionic liquid and substrate surface, especially the film of 1-ethyl-4-[5-(ethylsulfanyl)-1,3,4-oxadiazol-2-yl] pyridinium tetrafluoroborate, it has low friction coefficient and long wear life. So, this kind of ionic liquid can be potentially applied as ultra-thin lubricating coating.     

Friction and Wear Properties of Graphite-Like Carbon Films Deposited on Different Substrates with a Different Interlayer Under High Hertzian Contact Stress

Four types of graphite-like carbon (GLC) films were deposited on different substrates (Ti6Al4V, WC-27CrNi) with a different interlayer (TiC/Ti, TiC/Ti/TiN) using an unbalanced magnetron sputtering system. The effect of substrate and interlayer on the microstructure and properties of the studied GLC films was then investigated using different characterization techniques. The results show that both the substrate and interlayer had an obvious influence on the tribological properties of the studied GLC films even though there was no significant structural difference between these films. Specifically, a substrate with a high hardness was propitious to achieving superior tribological behaviors for carbon film even with a different interlayer. However, the interlayer had a distinct influence on the tribological properties of the carbon film deposited on different substrates, and this effect varied with the hardness property of the substrate. For a hard substrate, the wear rate and wear life were similar irrespective of the interlayer. For a soft substrate, the addition of a TiN interlayer improved the wear life sevenfold compared to the film with only a TiC/Ti interlayer, but the wear rate for a film with and without a TiN interlayer was approximately the same. The obvious discrepancy between wear life and wear rate for a carbon film deposited on soft substrate was closely related with the film adhesion strength and plastic deformation of the substrate materials. Based on these results, it can be concluded that the wear life is a better parameter than wear rate in terms of characterization of the wear resistance of carbon film once the applied load causes the plastic deformation of the substrate.