Mechanical and unlubricated tribological properties of titanium-containing diamond-like carbon coatings

Titanium-containing diamond-like carbon (Ti-DLC) coatings were deposited on steel with a close-field unbalanced magnetron sputtering in a mixed argon/acetylene atmosphere. The morphology and structure of Ti-DLC coatings were investigated by scanning electron microscopy, transmission electron microscopy, atomic force microscopy and Raman spectroscopy. Nanoindentation, nanoscratch and unlubricated wear tests were carried out to evaluate the hardness, adhesive and tribological properties of Ti-DLC coatings. Electron microscopic observations demonstrated the presence of titanium-rich nanoscale regions surrounded by amorphous carbon structures in Ti-DLC coating. The Ti-DLC coatings exhibit friction coefficients of 0.12–0.25 and wear rates of 1.82 × 10^?9 to 4.29 × 10^?8 mm³/Nm, depending on the counterfaces, sliding speed and temperature. The Ti-DLC/alumina tribo-pair shows a lower friction coefficient than the Ti-DLC/steel tribo-pair under the identical wear conditions. Increasing the test temperature from room temperature to 200 °C reduces the coefficient of friction and, however, clearly increases the wear rate of Ti-DLC coatings. Different wear mechanisms, such as surface polishing, delamination and tribo-chemical reactions, were found in the tribo-contact areas, depending on different wear conditions.     

Erosion wear and mechanical properties of plasma-sprayed nickel- and iron-based coatings subjected to service conditions in boilers

The erosion wear and mechanical properties after exposure to simulated industrial service conditions in boilers of nickel-based, iron-based and chromium–nickel plasma-sprayed coatings on carbon steel and stainless steel have been obtained. These types of coatings are used as heat transfer and structural elements in boilers. Different tests simulating boiler service conditions under standard and extreme situations were carried out at 400, 600 and 800°C in a laboratory combustion unit. The influence of high temperature oxidation processes on the adherence, microhardness, microstructure, and wear erosion behaviour of both base materials and coatings have been evaluated.     

Analysis of the friction and wear mechanisms of multilayered plasma-sprayed ceramic coatings

Wear tests were conducted on a rotor-vane-disk adaptor where three rotating vanes were pressed against a disk. Vanes were coated by WC and used as the upper specimen while the disk was coated by Cr₂O₃ and used as the lower specimen. A buffer layer of various thicknesses and contents was placed between the top coating and the bulk steel of the disk to alleviate the effects of the large difference in thermal properties of the two materials. The experimental results reveal that correct placement of a buffer layer can indeed improve the wear resistance. Factors such as the temperature to which the specimen was heated before testing, the proportion by weight of each individual constituent in the buffer layer, and the thickness of each coating layer, were also important for the volume of wear of the lower specimen. As the specimens were heated to higher temperatures, the wear volume decreased with increasing proportions of Cr₂O₃ in the buffer layer. Elevating the preheating temperature of the specimens can diminish the wear volume but increases the friction coefficient. The steady-state wear rate is not much influenced by the constituents of the buffer layer and the coating thickness. Brittle fracture, abrasion, adhesion and oxidation were found to be the primary wear mechanisms in the tests.     

Evaluation of wear and tribological properties of coatings rubbing against copper

A new crossed-cylinders tribo-tester is proposed. This tribo-tester can decrease the tendency of the chatter vibration. The tribological properties of coatings against copper is evaluated with this tribo-tester. The wear rate of TiN, TiC and TiCN rubbing against copper is higher than the substrate high speed tool steel: SKH51 (JIS). The catalytic action of copper for oxidation of Ti-based coatings is a main reason of this high wear rate of TiN, TiC and TiCN rubbing against copper. The wear rate of CrN rubbing against copper is in a very low level because CrN shows the excellent oxidation resistance and Cr₂O₃ film formation decreases the wear loss of CrN coating.     

Three body abrasive wear characteristics of plasma sprayed conventional and nanostructured Al2O3-13%TiO2 coatings

In this paper, the conventional Metco130 coatings, and two kinds of nanostructured coatings (NP and NS coatings) were fabricated by plasma spray with different feed powders. The coatings were evaluated by indentation, scratch and three body abrasive wear tests. The NP coating sprayed with plasma densified feed powder had the highest hardness, crack growth resistance and scratch resistance. Test results exhibited that the nanostructured coatings had greatly improved three body abrasive wear resistance compared with conventional coatings. The three body abrasive wear resistance of NP coatings was about three times that of conventional coatings. The failure mode in scratch tests and wear mechanism of three coatings were also discussed.     

A study on erosive wear behavior of HVOF sprayed nanostructured WC-CoCr coatings

WC-CoCr cermet coatings were deposited on stainless steel substrate using high-velocity oxy-fuel (HVOF) thermal spray process. The coatings were developed with two different thermal spray powders: one has WC grains of conventional micron size and the other is composed of nanosized (near-nanostructured) grains. HVOF spraying was assisted with in-flight particle temperature and velocity measurement system to control the process parameters that have resulted in quality coatings. Cavitation erosion testing was performed using a vibratory test apparatus based on ASTM standard G32-98. Surface morphology of powders and coatings was examined using the FESEM images, and phase identification was performed by XRD analysis. The erosion behavior of coatings and mechanism of material removal was discussed by examining the microstructure images of worn-out surfaces. WC-CoCr cermet coating deposited with nanosized WC grains exhibited higher cavitation erosion resistance as compared to conventional coating.     

Improvement in wear resistance of plasma sprayed yttria stabilized zirconia coating using nanostructured powder

Plasma sprayed yttria stabilized zirconia coatings were prepared using nanostructured and conventional powders with optimized process parameters for the highest deposition efficiency, the smallest porosity and the highest microhardness. The tribological properties of these coatings against 100C6 steel were then tested with a ball-on-disc arrangement. Results showed that although the friction coefficients of the coatings sprayed using the nanostructured powder were slightly different from those of the coatings sprayed using the conventional powder, the former coatings were more wear resistant than the latter coatings. The wear mechanisms of all the coatings were explained in terms of adhesion-induced spallation and micro-fracturing of lamellae. The improvement in wear resistance of the coatings sprayed using the nanostructured powder could be mainly ascribed to the decrease of micrometer-sized defects such as pores and interlamellar and intralamellar cracks in the coatings.     

Friction and wear behaviour of low-friction coatings in conventional and alternative fuels

Today low-friction PVD coatings are used regularly in combustion engines to reduce wear and energy loss due to friction. Three coatings based on transition-metal dichalcogenides and three DLC coatings were tested with respect to tribological behaviour in non-conformal sliding contact, in five conventional and alternative fuels and fuel blending components. The friction and wear proved to vary substantially between the different tested systems. The DLC coatings exhibited extremely good wear properties, but also higher friction. Contrastingly the TMD coatings showed promising friction results, but in their present forms they do not offer sufficient wear resistance in the tested severe contact situation.     

Tribological properties of nanostructured DLC coatings deposited by C60 ion beam

The frictional and wear characteristics of nanostructured DLC films were investigated. The coatings were deposited on silicon substrates by irradiation of a mass-separated C₆₀ ion beam with 5 keV of energy and a deposition temperature ranging from 100 to 450 °C. The effects of deposition temperature on the surface morphology, nano-structure, mechanical properties and tribological characteristics of the coatings were assessed. Results showed that deposition temperature strongly affects the nanostructure and surface morphology of the coatings. Coatings deposited at temperatures exceeding 350–400 °C exhibited an increase in surface roughness as well as compressive stress due to the formation of graphite, which led to a significant increase in the friction coefficient and wear rate. Coatings deposited at 300 °C showed the best tribological properties.     

Study of tribological properties of detonation nanostructured WC-Co-based coatings

The study deals with tribological properties of the nanostructured WC-12%Co coatings deposited by the detonation method. It is found experimentally that their wear resistance depends on the concentration of monocarbide WC. The dependence of the WC concentration in the coating on deposition conditions is obtained. The microstructure of the coatings, their physical-mechanical properties, phase composition, porosity, hardness, and modulus of elasticity are studied. The advantage of the nanostructured coatings over the coatings deposited from micropowders is shown.     

Unlubricated gross slip fretting wear of metallic plasma-sprayed coatings for Ti6Al4V surfaces

Plasma-sprayed Al–bronze or CuNiIn coatings are often applied to protect against fretting wear and extend the operational life of Ti-alloy compressor blades in turbine engines. In order to develop a fundamental understanding of how these coating systems perform under gross slip fretting conditions, bench level fretting wear tests were conducted at room temperature to simulate cold engine startup. Alternative coatings such as plasma-sprayed molybdenum and nickel were also evaluated because of their potential for reducing fretting wear under certain simulated engine conditions. The combination of scanning electron microscopy (SEM), surface profilometry, surface chemistry (EDS), and friction analysis were used to study coating performance and evaluate the interfacial wear mechanisms. In this study, it was determined that all coatings caused significant damage to the mating Ti6Al4V surfaces and that the wear mechanisms were all similar to those of the uncoated baseline case.     

Mechanical and tribological properties of nanostructured coatings based on multicomponent oxides

The mechanical and tribological properties of thin (up to 300 nm) oxide coatings that are produced by the carboxylate method and have various chemical compositions and thicknesses and are deposited on substrates from different materials (steel or quartz glass) have been assessed. The study involves the surface examination and the determination of the surface roughness of specimens using optical and atomic force microscopes, the determination of the elastic properties of the coatings based on indentation results, as well as the study of their tribological behavior during dry and lubricated sliding.     

Friction coefficient and wear rate of sputter-deposited thin films and plasma-sprayed thick coatings at high temperatures in room air

Silver, calcium fluoride (CaF_x with x = 1.85) and chromium-carbon (Cr₃C₂) thin films were deposited onto various tribological test specimens by sputtering. The friction properties of sputter-deposited Ag and CaF_x single layers as well as Ag/CaF_x multilayer films were determined by ball-on-disk tribological tests conducted in room air under various experimental conditions. The tribological properties (friction coefficient and wear rate) of sputter-deposited CaF_x films were also determined at 500°C by pin-on-disk tribological tests performed with pin specimens made of cobalt-based alloy (alacrite). Chromium-carbon films sputter-deposited onto alacrite disk and counterfaces were found to be of interest for reducing the formation of alacrite wear debris in the wear tracks; thus reduced friction coefficient and wear rate values were obtained. The friction behavior of sputter-deposited CaF_x/Cr₃C₂ thin bilayer structures and plasma-sprayed (PS) chromium carbide/Ag/BaF₂-CaF₂ eutectic composite coatings (PS-212 type coatings) was investigated by plane-on-plane tribological tests conducted in room air at 500°C and 700°C. The friction performance of solid lubricant thin bilayer films was compared with that of thick PS-212 type coatings similar to coatings developed by NASA.     

Development of a new type micro slurry‐jet erosion (MSE) tester for evaluation of wear properties of hard thin coatings

Versatile and reliable techniques for evaluation of hard thin coatings are necessary for the development and tribological assessment of new coatings. We have proposed a new type of micro slurry‐jet erosion (MSE) test, i.e. a solid particle impact erosion test for swift evaluation of wear properties of hard thin coatings. We are using a new type of MSE test apparatus (pot type tester) that makes it possible to obtain the wear loss per unit mass of erodent, which in this test was alumina particles with an average size of 1.2 µm. Its performance was evaluated by using a Si wafer plate under various test condition. In addition, the MSE tester was demonstrated by evaluating the wear resistance of TiN on high‐speed steel substrate. The new MSE test generates highly reproducible results and is very sensitive to the quality of the coatings. Copyright © 2009 John Wiley & Sons, Ltd.     

Sliding wear of an unlubricated frictional combination of ductile metal and brittle abrasive

The concept of determining wear from hypotheses concerning shear effects in metal surface regions was applied to the sliding wear of a smooth elastoplastically deformable metal substance and a rough brittle abrasive. Interfacial layers or lubricating depositions on either surface were neglected. The form of the contact was modelled using random fields for the roughness profiles. The resulting intensities of wear may be compared with published experimental results. The wear intensity level was quantitatively determined. Dependence on the nominal pressure and properties of the rough abrasive is thus explained. Instead of hardness the compressive strength of abrasive peaks is the dominant characteristic parameter.     

Evaluation of erosive wear resistance of TiN coatings by a slurry jet impact test

In this paper, it is proposed to use a new type of solid particle impact test (slurry jet) to swiftly evaluate wear properties of thin, single layered or multilayered coatings. By the slurry jet, 1.2 μm alumina particles were impacted at high velocity perpendicular to thin PVD coatings of TiN deposited on high speed steel substrate materials under various substrate temperatures. Since the coatings have a much higher wear resistance than the substrate material, the wear rate increases significantly to the higher level of the HSS material when the coatings are penetrated. This is utilized in the quantification of the assessment of coating wear. A ranking of wear resistance and correlations to the coating surface hardness measured by nano-indentation tests, and coating morphology and structures are given and discussed. The TiN deposited under the highest substrate temperature proved to have the highest wear resistance although it had a relatively low hardness. The wear rate of the TiN coatings varies with the orientation of grains, that is, the {1 1 1} orientation that dominates for the high temperature deposition shows a higher wear resistance than the {1 0 0} orientation, which corresponds with the cleavage fracture behavior. Thus, it can be recommended as a screening test when evaluating coatings and coated materials.     

The repeatability of friction and wear results obtained from unlubricated reciprocating sliding tests

Laboratory tests can help in the analysis of tribological failures of elements, and improve tribo‐systems by choosing appropriate materials. In order to characterise the friction and wear behaviour of candidate materials, various different test methods have been developed in the past and are still in use. One such method is the reciprocating sliding of a ball against a disc. In the work reported here, the repeatability of friction and wear results was evaluated with ten tests under identical conditions with a steel (100Cr6) or alumina (Al₂O₃) ball against a steel (100Cr6) disc under unlubricated conditions at room temperature. The influence of ambient humidity on friction and wear behaviour was determined in three additional tests in dry and in moist air, respectively. The repeatability of friction coefficient in normal air was better than 5% for alumina/100Cr6 and 12% for 100Cr6/100Cr6, while the repeatability of volumetric wear was slightly better than 10% for alumina/steel, and slightly worse than 10% for steel/steel. For both couples the coefficient of friction is lowest in moist air and about 50% higher in dry air. The coefficient of wear is also least in moist air and higher by a factor of 3(5) in dry air for tests with a 100Cr6 (alumina) ball.     

An experimental investigation into the friction and wear characteristics of unlubricated roller bearings

Lubricated rolling element bearings usually fail by fatigue. In the case of unlubricated rolling element bearings failure is due to wear of the rolling elements and cage. As the amount of wear increases so the friction torque of the bearing increases until catastrophic failure occurs and the bearing seizes.     

A comparative study of high-temperature erosion wear of plasma-sprayed NiCrBSiFe and WC–NiCrBSiFe coatings under simulated coal-fired boiler conditions

A comparative study was carried out of the behaviour of plasma sprayed NiCrBSiFe and WC–NiCrBSiFe alloys subjected to conditions which simulate a post-combustion gas atmosphere from a coal-fired boiler combustor. The study first evaluates the effects of thermal exposure at high temperatures on the microstructure of the coatings and on the adherence between substrate (austenitic stainless steel) and coatings. The oxidation rates of these coatings in atmospheres with 3–3.5% of free oxygen at 773 and 1073 K were then evaluated. The effect of WC on the low-velocity corrosion–erosion behaviour produced by the impact of fly ashes in the gas stream at high temperatures (773 and 1073 K) was assessed under impact angles of 30° and 90°. Finally, the eroded surfaces were analysed using scanning electron microscopy in order to characterize the ash embedment phenomena and the operating erosive micromechanisms.     

Comparison of wear behaviour of plasma-sprayed Al2O3 coatings with and without laser treatment

This paper studies experimentally the effects of CO₂ laser-treatment on the wear behaviour of plasma-sprayed Al₂O₃ coatings, in linear contact sliding (dry, abrasive and lubricated) against SAE 4620 steel. Tests were carried out using a block-on-ring friction and wear tester, under different loads at different speeds. The wear mechanism and the changes in adherence, porosity and microstructure by laser treatment were also investigated. Results show a better wear behaviour for both laser-treated ceramic coating and its paired steel under dry and abrasive conditions, compared with the case without laser treatment. The lubricated wear behaviour of the laser-treated ceramic coating, however, is not improved. The changes in microhardness, porosity and adherence caused by the laser treatment are responsible for the change in wear behaviour of the ceramic coating.