研究了控制熔体结晶法制备的半固态ZL101合金的压缩变形行为以及显微组织的变化.结果表明:在液固相区二次加热并保温足够时间后,该合金的球状固相仍保持半固态加工要求的适当尺寸,575℃和582℃压缩变形时,半固态浆料具有稳定触变流动变形特征,即应力随应变增大而缓慢下降,其应力水平较接近固相线的高温(550℃)塑性变形应力低得多;枝晶组织和高变形速率提高半固态合金的变形应力,并使应力随应变增大而单调提高;大变形后,圆柱试样中心和边缘区域存在球状初生α相变形程度的不同.半固态变形中,变形机理从以阻尼液相流动为主变为以固相颗粒塑性变形为主.     

Al-4Cu-Mg合金半固态压缩过程中的微观组织演变

研究了SIMA法制备的半固态Al-4Cu-Mg合金在不同变形温度、变形程度和应变速率下压缩变形时的微观组织演变．并研究了半固态Al-4Cu-Mg合金在高温变形条件下的微观组织形态。研究结果表明，在半固态条件下，品粒平均尺寸随变形温度的升高而增大：从540℃到560℃，品粒平均尺寸增大了2％～9％，而从560℃到580℃，晶粒平均尺寸增大了3％～16％，后者的增幅比前者大、变形程度增大，晶粒平均尺寸减小．同一试样大变形区的晶粒平均尺寸比小变形区的晶粒平均尺寸小4％～15％。应变速率减小，晶粒平均尺寸增大．晶粒变得圆整。     

铝合金半固态变形时的微观组织特征

文章在铝合金半固态压缩实验的基础上,深入研究了不同工艺参数下Al-4Cu-Mg合金半固态压缩时的微观组织形貌及参数变化。研究结果表明,半固态压缩时的微观组织特征受变形工艺参数的影响较大。变形程度越大,晶粒尺寸越小,晶粒圆整度越差。变形程度超过40%,晶粒尺寸急剧减小,变形机制发生了显著变化。随着应变速率的减小,晶粒尺寸增大,晶粒逐渐趋于圆整。在较高的变形温度下,晶粒发生了合并长大。但过高的变形温度引起晶粒尺寸的急剧增大,对变形不利。     

Ti14合金半固态变形的组织演变特征

以新型阻燃合金Ti14合金(α+Ti2Cu)为对象,研究了Ti合金在固态和半固态变形的组织演变过程,分析了温度和变形量对合金晶粒形态和晶界特征的影响,结果表明:半固态条件下未发生动态再结晶,使得晶粒粗大,温度影响了液相的析出,随着温度的升高,液相析出量增加,并集中在晶界处,使得晶界宽化,由不连续转变为连续分布;变形量改变了晶界的界面能,促使晶界发生迁移和转动,导致弯曲的晶界向其曲率中心方向移动,三叉晶的交角向120°趋近。     

Al-Zn-Mg-Cu合金热压缩流变应力行为及组织演变

采用Gleeble-1500D热力模拟试验机进行了Al-Zn-Mg-Cu合金的等温压缩实验,变形温度为250～450℃,应变速率为0.001～0.1 s-1,变形量为10%～50%,获得了热压缩变形的真应力-真应变曲线.应力-应变曲线基本呈现回复型曲线特征,计算得出其应力指数为4.60,热变形激活能为186.70 kJ·mol-1;综合分析了变形温度、应变速率和变形量对组织演变的影响规律,确定了Al-Zn-Mg-Cu合金的锻造工艺参数为:锻造温度区间420350℃,应变速率0.01～0.1 s-1,变形量>30%.     

半固态5083铝合金压缩变形行为及组织特性

采用Gleeble 3500热模拟试验机,分别对铸态和SIMA法制备的半固态5083铝合金压缩变形行为进行了研究,并结合压缩后的宏观形貌和显微组织对液相的流动规律进行了分析。结果表明,变形温度和应变速率是影响5083铝合金半固态坯料热压缩变形的两个重要参数;在半固态温度区间压缩变形时,铸态坯料整体应力水平明显高于SIMA法制备的半固态坯料;而在固态温度区间内高温压缩变形时,二者流变应力曲线特征相似,半固态坯料没有明显优势;两种不同状态5083铝合金固液两相区压缩变形时,存在3个典型变形区域,半固态组织中液相均匀分布于晶粒晶界处,而铸态组织中液相分布位置极不均匀,半固态5083铝合金压缩变形后试样的致密度和均匀性优于铸态材料。     

半固态LY11合金的压缩变形

研究了变形温度和应变速率对半固态LY11合金变形行为和微观组织的影响.研究结果表明:在液固温度区间变形时,变形温度、应变速率对半固态LY11合金的流变应力峰值影响显著,对稳态流变应力影响较小.对微观组织的影响是:随着变形温度的升高和应变速率的降低,固相晶粒尺寸增大,但仍保持初始的近球状.在半固态合金的压缩过程中,随着工艺参数的变化,占主导地位的变形机制也随之变化.     

铝铁合金的研究进展与应用状况

综述了Al-Fe合金的国内外研究现状，阐述了共晶、过共晶铝铁合金及其在快速凝固条件下的凝固特点，概述了添加Ca、Mg、Mn、RE等微量元素及采用热速处理、电流处理、交变磁场、超声振动等工艺条件对Al-Fe合金微观组织的影响规律，叙述了目前Al-Fe合金的应用状况，并对铝铁合金的研究及应用前景进行了展望。     

半固态7050铝合金热压缩变形行为

在Gleeble-3500热模拟机上对半固态7050铝合金进行了高温热压缩试验,研究了该合金在变形温度为420～465℃、应变速率为0.001～0.100s-1条件下的流变应力行为以及变形过程中的显微组织。结果表明,流变应力在变形初期随着应变的增大迅速增大,出现峰值应力后逐渐平稳,流变应力随着应变速率的增大而增大,随着变形温度的升高而下降;流变应力可以用双曲线正弦形式的关系来描述,通过线性拟合计算出该材料的形变激活能等参数,获得流变应力的本构方程。随着变形温度升高和应变速率降低,合金中拉长的晶粒变大,合金热压缩变形的主要软化机制为动态再结晶。     

半固态成形Al-Fe基合金组织与性能

设计了一种Al-Fe合金的化学成分,采用半固态技术进行了成形,分析了合金铸态、电磁搅拌态、挤压态的组织,检测了合金铸态、半固态成形态的力学性能。试验结果表明:合金元素的加入和凝固过程中外加电磁搅拌以后,合金组织明显细化;经过半固态成形后,合金组织进一步细化,第二相长度和厚度减小,同时尖角发生钝化,且分布较均匀,力学性能比铸态提高了79.7%。     

铝铁合金热压缩流变行为

采用Gleeble-1500模拟实验机研究铝铁合金在783K~693K,应变速率为0.01s-1~10 s-1条件下的热变形行为。结果表明,铝铁合金高温变形时存在明显的稳态流变特征,流动应力对应变速率和温度敏感。实验得出真应力应变曲线分析峰值的应力与变形温度、应变速率之间的关系,用包含Arrhenius项的Zener-Hollomon参数描述铝铁合金高温塑性变形时的流变行为;计算得出材料的真应力-应变方程。     

Microstructure and mechanical properties of hypereutectic Al-Fe alloys prepared by semi-solid formation

The effects of alloying elements, electromagnetic stirring, reheating and semi-solid formation on the microstructure and mechanical properties of Al-Fe alloys prepared by semi-solid formation were studied. It was found that alloying elements and electromagnetic stirring can alter the morphology and growth mode of the iron-rich phase in Al-Fe alloys; and effectively refine the primary Al3Fe phase. In contrast to the microstructure obtained in conventional casting, the Al3Fe phase becomes thin short rod-like instead of thick needle-like; and the dendritic grain structure almost disappears in the semi-solid formation. The Al3Fe phase can be further refined through being dissolved or fused during subsequent reheating. It was also found that the larger extrusion ratio of semi-solid formation causes a greater crushing effect and therefore the Al3Fe phase is more refined and has more uniform distribution. Moreover, Al-Fe alloys prepared by semi-solid formation exhibit excellent mechanical properties at both room and high temperatures.     

Microstructure evolution of casting Mg alloy AM60B subjected to compression deformation

In order to research the microstructure evolution of casting Mg alloy AM60B after compression,the isothermally compressive deformation of different compression ratios followed by metallographic observation was performed.The influence of grain boundaries and second phases on the deformation and recrystallization behavior of the alloy was investigated with optical microscopy,followed by transmission electron microscopy(TEM) to gain an insight into the interplay between the dislocations and microstructure f...     

小热变形半固态A2017合金的二次加热组织与半固态轧制

对单辊搅拌技术制得的A2017半固态材料小热变形后二次加热时的组织演化进行了研究。小热变形后的半固态材料加热到半固态区后可获得细小的球形组织；在加热过程中，由于位错能与界面能的存在以及溶质的扩散使合金发生块状化、再结晶、熔断球化3阶段变化；小变形促进该过程的进行；由于细小球形组织成形性能好、半固态轧材的断裂强度提高了75MPa，延伸率提高了16％。     

Al-Mn-Mg-Cu-Ni合金热压缩变形的流变行为和组织

在Gleeble-1500热模拟机上对Al-Mn-Mg-Cu-Ni合金进行热压缩试验,分析合金的流变应力与应变速率和变形温度之间的关系,计算高温变形时的变形激活能,并研究合金在变形过程中的显微组织。结果表明:Al-Mn-Mg-Cu-Ni合金在本实验条件下具有正的应变速率敏感性;流变应力随应变速率的增大而增大,随变形温度的升高而减小。该合金热压缩变形的流变应力行为可用双曲正弦形式的本构方程来描述,也可用Zener-Hollomon参数来描述,其变形激活能为209.84kJ/mol。随着热变形温度的升高和应变速率的减小,合金中的主要软化机制逐步由动态回复转变为动态再结晶。     

6063铝合金双道次热变形微观组织演变

采用Gleeble-1500热模拟试验机对6063铝合金进行双道次热轧试验,分析了合金在变形温度为300~500 ℃,应变速率为0.001~0.1 s^-1,道次间停留时间10~90 s时的流变应力和微观组织。结果表明:随着道次间停留时间增长,第二道次屈服应力减小;温度与道次间停留时间对合金的静态软化率有较大的影响。低温大应变速率短道次间停留时间下试样的强化相较多,其形貌为长条状与圆形;高温低应变速率长道次间停留时间下试样的强化相数量有所减少,其形貌以圆形为主。通过能谱分析可知,试样中的强化相以AlFeSi为主,长条状强化相为6 μm左右,圆形强化相尺寸约2 μm。     

Microstructure evolution of semi-solid 2024 alloy during two-step reheating process

A two-step reheating process was proposed and applied to perform reheating experiments on the semi-solid 2024 alloy billet. In this process, the semi-solid billet was firstly heated over liquidus temperature and then isothermally held at solid-liquid zone temperature. Microstructure evolution of the semi-solid billet during two-step reheating was studied by optical microscope and compared with that during isothermal reheating. The results show that the remelting rate of the semi-solid billet during two-step reheating is faster than that during isothermal reheating. Under the same reheating time, the grains of the semi-solid billet reheated by two-step reheating process are finer and rounder than those by isothermal reheating process. The present experimental results indicate that accelerating the formation of liquid phase during the two-step reheating process can restrain the coalescence of grains to a certain extent, and thus refine the grain size and promote the grain spheroidization.     

Al-6.2Zn-2.3Mg-2.3Cu合金热压缩变形的流变应力与组织演变

利用GPL-1500热模拟试验机对Al-6.2Zn-2.3Mg-2.3Cu合金在不同温度和不同应变速率条件下进行高温压缩试验,得到压缩真应力-应变曲线,并得出该合金的变形激活能和流变应力-应变方程。结果表明,变形温度和应变速率的变化对流变应力的影响明显,流变应力随变形温度的提高而显著降低,随应变速率的提高而增加。该合金高温变形过程的流变应力可用Zener-Hollomon参数(Z)描述;用双曲正弦函数修正的Arrhenius关系表示的流变应力方程为.ε·=1.282×100[sin(0.010σ)]4.9145exp(-134157/RT)。