Electrical Instability of RF Sputter Amorphous In-Ga-Zn-O Thin-Film Transistors

Bias-temperature-stress (BTS) induced electrical instability of the RF sputter amorphous In-Ga-Zn-O (a-IGZO) thin-film transistors (TFTs) was investigated. Both positive and negative BTS were applied and found to primarily cause a positive and negative voltage shift in transfer $(I _{rm DS} -V _{rm GS})$ characteristics, respectively. The time evolution of bulk-state density $(N _{rm BS})$ and characteristic temperature of the conduction-band-tail-states $(T _{G})$ are extracted. Since both values showed only minor changes after BTS, the results imply that observed shift in TFT $I _{rm DS} -V _{rm GS}$ curves were primarily due to channel charge injection/trapping rather than defect states creation. We also demonstrated the validity of using stretch-exponential equation to model both positive and negative BTS induced threshold voltage shift $(Delta V _{rm th})$ of the a-IGZO TFTs. Stress voltage and temperature dependence of $Delta V _{rm th}$ evolution are described.      

Q-Band pHEMT and mHEMT Subharmonic Gilbert Upconversion Mixers

This letter makes a comparison between Q-band 0.15 $mu{rm m}$ pseudomorphic high electron mobility transistor (pHEMT) and metamorphic high electron mobility transistor (mHEMT) stacked-LO subharmonic upconversion mixers in terms of gain, isolation and linearity. In general, a 0.15 $mu{rm m}$ mHEMT device has a higher transconductance and cutoff frequency than a 0.15 $mu{rm m}$ pHEMT does. Thus, the conversion gain of the mHEMT is higher than that of the pHEMT in the active Gilbert mixer design. The Q-band stacked-LO subharmonic upconversion mixers using the pHEMT and mHEMT technologies have conversion gain of $-$7.1 dB and $-$0.2 dB, respectively. The pHEMT upconversion mixer has an ${rm OIP}_{3}$ of $-$12 dBm and an ${rm OP}_{1 {rm dB}}$ of $-$24 dBm, while the mHEMT one shows a 4 dB improvement on linearity for the difference between the ${rm OIP}_{3}$ and ${rm OP}_{1 {rm dB}}$. Both the chip sizes are the same at 1.3 mm $times$ 0.9 mm.      

$hbox{TiN/ZrO}_{2}$/Ti/Al Metal–Insulator–Metal Capacitors With Subnanometer CET Using ALD-Deposited $hbox{ZrO}_{2}$ for DRAM Applications

We provide the first report of the structural and electrical properties of $hbox{TiN/ZrO}_{2}$/Ti/Al metal–insulator–metal capacitor structures, where the $hbox{ZrO}_{2}$ thin film (7–8 nm) is deposited by ALD using the new zirconium precursor ZrD-04, also known as Bis(methylcyclopentadienyl) methoxymethyl. Measured capacitance–voltage ($C$– $V$) and current–voltage ( $I$–$V$) characteristics are reported for premetallization rapid thermal annealing (RTP) in $hbox{N}_{2}$ for 60 s at 400 $^{circ}hbox{C}$, 500 $^{circ}hbox{C}$, or 600 $^{ circ}hbox{C}$. For the RTP at 400 $^{circ}hbox{C}$ , we find very low leakage current densities on the order of nanoamperes per square centimeter at a gate voltage of 1 V and low capacitance equivalent thickness values of $sim$ 0.9 nm at a gate voltage of 0 V. The dielectric constant of $ hbox{ZrO}_{2}$ is 31 $pm$ 2 after RTP treatment at 400 $^{circ}hbox{C}$.      

Operation of Pt/AlGaN/GaN-Heterojunction Field-Effect-Transistor Hydrogen Sensors With Low Detection Limit and High Sensitivity

To enhance the device sensitivity and detection limit, a gate bias is applied to the catalytic metal of AlGaN/GaN-heterojunction field-effect-transistor (HFET) hydrogen sensors to control the carrier concentration in the channel at operation. The sensors exhibit a good sensitivity at temperatures up to 800 $^{circ}hbox{C}$ and a detection limit of 10-ppb $ hbox{H}_{2}$ in $hbox{N}_{2}$. The dependence of the device sensitivity on gate and drain biases has been investigated. The sensitivity peaks at the gate bias of threshold voltage and the drain bias of knee voltage in sensing gas. At high temperatures and $hbox{H}_{2}$ concentrations, specifically from 300 $^{circ}hbox{C}$ and 1000-ppm $hbox{H}_{2}/hbox{N}_{2}$, respectively, the sensitivity of HFETs at $V_{rm gs} = -hbox{3.5} hbox{V}$ and $V_{rm ds} = hbox{1} hbox{V}$ is more than three orders higher than their sensitivity at $V_{rm gs} = hbox{0} hbox{V}$ and the sensitivity of Schottky diodes.      

High-Performance Poly-Silicon TFTs Using a High-$k$ $hbox{PrTiO}_{3}$ Gate Dielectric

In this letter, a polycrystalline-silicon thin-film transistor (poly-Si TFT) with a high- $k$ $hbox{PrTiO}_{3}$ gate dielectric is proposed for the first time. Compared to TFTs with a $hbox{Pr}_{2}hbox{O}_{3}$ gate dielectric, the electrical characteristics of poly-Si TFTs with a $hbox{PrTiO}_{3}$ gate dielectric can be significantly improved, such as lower threshold voltage, smaller subthreshold swing, higher $I_{rm on}/I_{rm off}$ current ratio, and larger field-effect mobility, even without any hydrogenation treatment. These improvements can be attributed to the high gate capacitance density and low grain-boundary trap state. All of these results suggest that the poly-Si TFT with a high- $k$ $hbox{PrTiO}_{3}$ gate dielectric is a good candidate for high-speed and low-power display driving circuit applications in flat-panel displays.      

0.8-V Supply Voltage Deep-Submicrometer Inversion-Mode $hbox{In}_{0.75}hbox{Ga}_{0.25}hbox{As}$ MOSFET

We report the experimental demonstration of deep-submicrometer inversion-mode $hbox{In}_{0.75}hbox{Ga}_{0.25}hbox{As}$ MOSFETs with ALD high- $k$ $hbox{Al}_{2}hbox{O}_{3}$ as gate dielectric. In this letter, n-channel MOSFETs with 100–200-nm-long gates have been fabricated. At a supply voltage of 0.8 V, the fabricated devices with 200–130-nm-long gates exhibit drain currents of 232–440 $muhbox{A}/muhbox{m}$ and transconductances of 538–705 $muhbox{S}/muhbox{m}$. The 100-nm device has a drain current of 801 $muhbox{A}/muhbox{m}$ and a transconductance of 940 $muhbox{S}/muhbox{m}$. However, the device cannot be pinched off due to severe short-channel effect. Important scaling metrics, such as on/off current ratio, subthreshold swing, and drain-induced barrier lowering, are presented, and their relations to the short-channel effect are discussed.      

A 67 dBm $OIP_{3}$ Multistacked Junction Varactor

A multistacked varactor is presented for ultra-linear tunable radio frequency applications. The varactor elements are applied in anti-series configuration and are characterized by an “exponential” $C$- $V _{R}$ relationship. Third-order intermodulation ($IM_{3}$) is cancelled through proper harmonic loading of the terminals of the anti-series configuration. Multiple stacking is used to further increase the power handling and to minimize the remaining fifth-order distortion. The measured output intercept point ($OIP_{3}$ ) at 2 GHz is $ > 67~{rm dBm}$ for modulated signals up to 10 MHz bandwidth, while providing a capacitance tuning ratio of 3:1 with an average quality factor of 40 and maximum control voltage of 10 V.      

W-Band Active Down-Conversion Mixer in Bulk CMOS

A W-band (76–77 GHz) active down-conversion mixer has been demonstrated using low leakage (higher ${rm V}_{{rm T}}$) NMOS transistors of a 65-nm digital CMOS process with 6 metal levels. It achieves conversion gain of ${-}8$ dB at 76 GHz with a local oscillation power of 4 dBm (${sim-}2$ dBm after de-embedding the on-chip balun loss), and 3 dB bandwidth of 3 GHz. The SSB noise figures are 17.8–20 dB (11.3–13.5 dB after de-embedding on-chip input balun loss) between 76 and 77 GHz. ${rm IP}_{1{rm dB}}$ is ${-}6.5$ dBm and IIP3 is 2.5 dBm (${sim-}13$ and ${sim}-4$ dBm after de-embedding the on-chip balun loss). The mixer consumes 5 mA from a 1.2 V supply.      

Low-Voltage Organic Field-Effect Transistor With PMMA/$ hbox{ZrO}_{2}$ Bilayer Dielectric

This paper reports on the application of a bilayer polymethylmethacrylate (PMMA)/ $hbox{ZrO}_{2}$ dielectric in copper phthalocyanine (CuPc) organic field-effect transistors (OFETs). By depositing a PMMA layer on $hbox{ZrO}_{2}$, the leakage of the dielectric is reduced by one order of magnitude compared to single-layer $hbox{ZrO}_{2}$. A high-quality interface is obtained between the organic semiconductor and the combined insulators. By integrating the advantages of polymer and high- $k$ dielectrics, the device achieves both high mobility and low threshold voltage. The typical field-effect mobility, threshold voltage, on/off current ratio, and subthreshold slope of OFETs with bilayer dielectric are $hbox{5.6}timeshbox{10}^{-2} hbox{cm}^{2}/hbox{V} cdot hbox{s}$, 0.8 V, $hbox{1.2} times hbox{10}^{3}$, and 2.1 V/dec, respectively. By using the bilayer dielectrics, the hysteresis observed in the devices with single-layer $hbox{ZrO}_{2}$ is no longer present.      

Extended Fault-Tolerant Cycle Embedding in Faulty Hypercubes

We consider fault-tolerant embedding, where an $n$-dimensional faulty hypercube, denoted by $Q_{n}$, acts as the host graph, and the longest fault-free cycle represents the guest graph. Let $F_{v}$ be a set of faulty nodes in $Q_{n}$. Also, let $F_{e}$ be a set of faulty edges in which at least one end-node of each edge is faulty, and let ${cal F}_{e}$ be a set of faulty edges in which the end-nodes of each edge are both fault-free. An edge in $Q_{n}$ is said to be critical if it is either fault-free or in $F_{e}$. In this paper, we prove that there exists a fault-free cycle of length at least $2^{n}-2vert F_{v}vert$ in $Q_{n} (ngeq 3)$ with $vert{cal F}_{e}vertleq 2n-5$, and $vert F_{v}vert+vert{cal F}_{e}vertleq 2n-4$ , in which each node is incident to at least two critical edges. Our result improves on the previously best known results reported in the literature, where only faulty nodes or faulty edges are considered.      

2 MHz AO $Q$ -switched ${rm TEM}_{00}$ Grazing Incidence Laser With 3 at.% Neodymium Doped Nd:YVO$_{4}$

We present a detailed experimental and theoretical study of the ultrahigh repetition rate AO $Q$ -switched ${rm TEM}_{00}$ grazing incidence laser. Up to 2.1 MHz $Q$-switching with ${rm TEM}_{00}$ output of 8.6 W and 2.2 MHz $Q$ -switching with multimode output of 10 W were achieved by using an acousto-optics $Q$ -switched grazing-incidence laser with optimum grazing-incidence angle and cavity configuration. The crystal was 3 at.% neodymium doped Nd:YVO$_{4}$ slab. The pulse duration at 2 MHz repetition rate was about 31 ns. The instabilities of pulse energy at 2 MHz repetition rate were less than ${pm}6.7hbox{%}$ with ${rm TEM}_{00}$ operation and ${pm}3.3hbox{%}$ with multimode operation respectively. The modeling of high repetition rate $Q$-switched operation is presented based on the rate equation, and with the solution of the modeling, higher pump power, smaller section area of laser mode, and larger stimulated emission cross section of the gain medium are beneficial to the $Q$-switched operation with ultrahigh repetition rate, which is in consistent with the experimental results.      

The Electrical and Interfacial Properties of Metal-High-$kappa$ Oxide-Semiconductor Field-Effect Transistors With $hbox{LaAlO}_{3}$ Gate Dielectric

$hbox{LaAlO}_{3}$ is a promising candidate for gate dielectric of future VLSI devices. In this letter, n-channel metal–oxide–semiconductor field-effect transistors with $hbox{LaAlO}_{3}$ gate dielectric were fabricated, and the electron mobility degradation mechanisms were studied. The leakage current density is $hbox{7.6} times hbox{10}^{-5} hbox{A/cm}^{2}$ at $-!$ 1 V. The dielectric constant is 17.5. The surface-recombination velocity, the minority-carrier lifetime, and the effective capture cross section of surface states were extracted from gated-diode measurement. The rate of threshold voltage change with temperature $(Delta V_{T} / Delta T)$ from 11 K to 400 K is $-!$ 1.51 mV/K, and the electron mobility limited by surface roughness is proportional to $E_{rm eff}^{-0.66}$.      

A 0.55 V 60 dB-DR Fourth-Order Analog Baseband Filter

A 0.55 V supply voltage fourth-order low-pass continuous-time filter is presented. The low-voltage operating point is achieved by an improved bias circuit that uses different opamp input and output common-mode voltages. The fourth-order filter architecture is composed by two Active- ${rm G}_{rm m}{-}{rm RC}$ biquadratic cells, which use a single opamp per-cell with a unity-gain-bandwidth comparable to the filter cut-off frequency. The $-$ 3 dB filter frequency is 12 MHz and this is higher than any other low-voltage continuous-time filter cut-off frequency. The $-$3 dB frequency can be adjusted by means of a digitally-controlled capacitance array. In a standard 0.13 $mu{rm m}$ CMOS technology with ${V}_{THN}approx 0.25 {rm V}$ and ${V}_{THP}approx 0.3 {rm V}$, the filter operates with a supply voltage as low as 0.55 V. The filter $({rm total} {rm area}=0.47 {rm mm}^{2})$ consumes 3.4 mW. A 8 dBm-in-band IIP3 and a 13.3 dBm-out-of-band IIP3 demonstrate the validity of the proposal.      

Work-Function Engineering for 32-nm-Node pMOS Devices: High-Performance TaCNO-Gated Films

We have demonstrated p-type field effect transistors (p-FETs) devices using a TaCNO metal gate for the first time. These p-FETs have threshold voltage values of $-$ 0.4 and $-$ 0.25 V for HfSiON and HfSiO gate dielectrics, respectively, with equivalent oxide thickness of 1.6–1.7 nm. The TaCNO metal shows a high effective work function (eWF) of 4.89 eV on thick $hbox{SiO}_{2}$ interface layer, although the eWF rolls off with reducing EOT. Excellent transistor characteristics are achieved, with $I_{rm on}$ of $hbox{375} muhbox{A}/muhbox{m}$ at $I_{rm off} = hbox{60 nA}$, for $V_{rm dd} = hbox{1.1} hbox{V}$ .      

The Impact of Oxide Traps Induced by SOI Thickness on Reliability of Fully Silicide Metal-Gate Strained SOI MOSFET

In this letter, we investigate the effects of oxide traps induced by various silicon-on-insulator (SOI) thicknesses $({T}_{rm SOI})$ on the performance and reliability of a strained SOI MOSFET with SiN-capped contact etch stop layer (CESL). Compared to the thicker ${T}_{rm SOI}$ device, the thinner ${T}_{rm SOI}$ device with high-strain CESL possesses a higher interface trap $({N}_{rm it})$ density, leading to degradation in the device performance. On the other hand, however, the thicker ${T}_{rm SOI}$ device reveals inferior gate oxide reliability. From low-frequency noise analysis, we found that thicker ${T}_{rm SOI}$ has a higher bulk oxide trap $({N}_{rm BOT})$ density, which is induced by larger strain in the gate oxide film and is mainly responsible for the inferior TDDB reliability. Presumably, the gate oxide film is bended up and down for the p- and nMOSFETs, respectively, by the net stress in thicker ${T}_{rm SOI}$ devices in this strain technology.      

Electrical Properties of Amorphous $hbox{Bi}_{5} hbox{Nb}_{3}hbox{O}_{15}$ Thin Film for RF MIM Capacitors

Amorphous $hbox{Bi}_{5}hbox{Nb}_{3}hbox{O}_{15}(hbox{B}_{5} hbox{N}_{3})$ film grown at 300 $^{circ}hbox{C}$ showed a high-$k$ value of 71 at 100 kHz, and similar $k$ value was observed at 0.5–5.0 GHz. The 80-nm-thick film exhibited a high capacitance density of 7.8 fF/$muhbox{m}^{2}$ and a low dissipation factor of 0.95% at 100 kHz with a low leakage-current density of 1.23 nA/ $hbox{cm}^{2}$ at 1 V. The quadratic and linear voltage coefficient of capacitances of the $hbox{B}_{5}hbox{N}_{3}$ film were 438 ppm/$hbox{V}^{2}$ and 456 ppm/V, respectively, with a low temperature coefficient of capacitance of 309 ppm/$^{circ}hbox{C}$ at 100 kHz. These results confirmed the potential of the amorphous $hbox{B}_{5}hbox{N}_{3}$ film as a good candidate material for a high-performance metal–insulator–metal capacitors.      

A 36–80 GHz High Gain Millimeter-Wave Double-Balanced Active Frequency Doubler in SiGe BiCMOS

This letter presents a high conversion gain double-balanced active frequency doubler operating from 36 to 80 GHz. The circuit was fabricated in a 200 GHz ${rm f}_{rm T}$ and ${rm f}_{max}$ 0.18 $mu$m SiGe BiCMOS process. The frequency doubler achieves a peak conversion gain of 10.2 dB at 66 GHz. The maximum output power is 1.7 dBm at 66 GHz and ${-}3.9$ dBm at 80 GHz. The maximum fundamental suppression of 36 dB is observed at 60 GHz and is better than 20 dB from 36 to 80 GHz. The frequency doubler draws 41.6 mA from a nominal 3.3 V supply. The chip area of the active frequency doubler is 640 $mu$m $,times,$424 $mu$m (0.272 mm $^{2}$) including the pads. To the best of authors' knowledge, this active frequency doubler has demonstrated the highest operating frequency with highest conversion gain and output power among all other silicon-based active frequency doublers reported to date.      

An Analytical Method to Extract the Physical Parameters of a Solar Cell From Four Points on the Illuminated $J{-}V$ Curve

For a variety of solar cells, it is shown that the single exponential $J{-}V$ model parameters, namely—ideality factor $eta$ , parasitic series resistance $R_{s}$, parasitic shunt resistance $R_{rm sh}$, dark current $J_{0}$, and photogenerated current $J_{rm ph}$ can be extracted simultaneously from just four simple measurements of the bias points corresponding to $V_{rm oc}$, $sim!hbox{0.6}V_{rm oc}$, $J_{rm sc}$, and $sim! hbox{0.6}J_{rm sc}$ on the illuminated $J{-}V$ curve, using closed-form expressions. The extraction method avoids the measurements of the peak power point and any $dJ/dV$ (i.e., slope). The method is based on the power law $J{-}V$ model proposed recently by us.      

Linear Systems, Sparse Solutions, and Sudoku

In this paper, we show that Sudoku puzzles can be formulated and solved as a sparse linear system of equations. We begin by showing that the Sudoku ruleset can be expressed as an underdetermined linear system: ${mmb{Ax}}={mmb b}$, where ${mmb A}$ is of size $mtimes n$ and $n>m$. We then prove that the Sudoku solution is the sparsest solution of ${mmb{Ax}}={mmb b}$, which can be obtained by $l_{0}$ norm minimization, i.e. $minlimits_{mmb x}Vert{mmb x}Vert_{0}$ s.t. ${mmb{Ax}}={mmb b}$. Instead of this minimization problem, inspired by the sparse representation literature, we solve the much simpler linear programming problem of minimizing the $l_{1}$ norm of ${mmb x}$, i.e. $minlimits_{mmb x}Vert{mmb x}Vert_{1}$ s.t. ${mmb{Ax}}={mmb b}$, and show numerically that this approach solves representative Sudoku puzzles.      

Comparative Study of the Low-Frequency-Noise Behaviors in a-IGZO Thin-Film Transistors With $hbox{Al}_{2}hbox{O}_{3}$ and $hbox{Al}_{2}hbox{O}_{3}/hbox{SiN}_{x}$ Gate Dielectrics

A comparative study is made of the low-frequency noise (LFN) in amorphous indium–gallium–zinc oxide (a-IGZO) thin-film transistors (TFTs) with $hbox{Al}_{2}hbox{O}_{3}$ and $hbox{Al}_{2}hbox{O}_{3}/hbox{SiN}_{x}$ gate dielectrics. The LFN is proportional to $hbox{1}/f^{gamma}$, with $gamma sim hbox{1}$ for both devices, but the normalized noise for the $hbox{Al}_{2}hbox{O}_{3}/hbox{SiN}_{x}$ device is two to three orders of magnitude lower than that for the $hbox{Al}_{2} hbox{O}_{3}$ device. The mobility fluctuation is the dominant LFN mechanism in both devices, but the noise from the source/drain contacts becomes comparable to the intrinsic channel noise as the gate overdrive voltage increases in $hbox{Al}_{2}hbox{O}_{3}/hbox{SiN}_{x}$ devices. The $hbox{SiN}_{x}$ interfacial layer is considered to be very effective in reducing LFN by suppressing the remote phonon scattering from the $hbox{Al}_{2}hbox{O}_{3}$ dielectric. Hooge's parameter is extracted to $sim !!hbox{6.0} times hbox{10}^{-3}$ in $hbox{Al}_{2}hbox{O}_{3}/hbox{SiN}_{x}$ devices.