Effect of particle size,heating rate and CNT addition on densification,microstructure and mechanical properties of B4C ceramics

Monolithic B₄C ceramics and B₄C–CNT composites were prepared by spark plasma sintering (SPS). The influence of particle size, heating rate, and CNT addition on sintering behavior, microstructure and mechanical properties were studied. Two different B₄C powders were used to examine the effect of particle size. The effect of heating rate on monolithic B₄C was investigated by applying three different heating rates (75, 150 and 225 °C/min). Moreover, in order to evaluate the effect of CNT addition, B₄C–CNT (0.5–3 mass%) composites were also produced. Fully dense monolithic B₄C ceramics were obtained by using heating rate of 75 °C/min. Vickers hardness value increased with increasing CNT content, and B₄C–CNT composite with 3 mass% CNTs had the highest hardness value of 32.8 GPa. Addition of CNTs and increase in heating rate had a positive effect on the fracture toughness and the highest fracture toughness value, 5.9 MPa m^1/2, was achieved in composite with 3 mass% CNTs.     

Aqueous tape casting of B4C ceramics

B₄C green tapes are prepared by aqueous tape casting and a spark plasma sintering (SPS) process using polyethylenimine (PEI) as dispersant, hydroxypropyl methyl cellulose (HPMC) as binder and polyethylene glycol (PEG) as plasticiser. The influences of solid content, dispersant content, mass ratio of plasticiser to binder (R value) and milling time on the slurry viscosity are studied. The samples are characterised by means of hardness tester, universal testing machine and scanning electron microscopy. The results indicate that the solid content of B₄C slurry achieves 47.5?wt-% with milling time of 12?h when the content of PEI, HPMC and PEG is 1.5, 5 and 5?wt-%, respectively. The relative density of B₄C ceramics subject to SPS at 1600°C and 50?MPa for 8?min is up to 97.2%. The Vickers hardness, flexural strength and fracture toughness of B₄C ceramics reach 36.5?±?0.7?GPa, 510.3?±?19.4?MPa and 5.04?±?0.29?MPa?m^?1/2, respectively.     

In situ toughened two-phase B12(C,Si, B)3–SiC ceramics fabricated via liquid silicon infiltration

In situ toughened B₁₂(C, Si, B)₃–SiC ceramics were successfully fabricated via the liquid silicon infiltration process. Two types of B₁₂(C, Si, B)₃ phases, with high and low Si contents, respectively, and plate-like SiC particles were formed by the reaction between B₄C and Si. The in situ toughening mechanism involved two effects: the multiple crack deflections caused by the increased grain boundaries, and the pullout and rupture of a significant amount of plate-like SiC particles. Block ceramics with a high fracture toughness of 6.5 ± 0.5 MPa·m^1/2 were fabricated via the in situ toughening mechanism. A strong interface bond was present between the high- and low-B₄C-content layers in the laminated ceramics, which led to residual compressive stress inside the materials. As a result, the laminated structural design enhanced the fracture toughness to 7.5 ± 0.5 MPa·m^1/2.     

Spark plasma sintering of boron nitride micron tubes reinforced boron carbide ceramics with excellent mechanical property

In this paper, the novel boron nitride micron tubes (BNMTs) were used to reinforce commercial boron carbide (B₄C) ceramics prepared via spark plasma sintering technology. The effects of the sintering parameters, sintering temperature, the holding time, and the BNMTs content on the microstructure and mechanical properties of B₄C/BNMTs composite ceramics were studied. The results indicated that adding a proper amount of BNMTs could inhibit the grain growth of B₄C and improve the fracture toughness of the B₄C/BNMTs composite ceramics. The prepared composite ceramic sample with 5 wt% BNMTs at 1850°C, 8 min and 30 MPa displayed the best mechanical properties. The relative density, hardness, fracture toughness, and bending strength of the samples were 99.7% ± .1%, 35.62 ± .43 GPa, 6.23 ± .2 MPa m^1/2, and 517 ± 7.8 MPa, respectively. Therein, the corresponding value of hardness, fracture toughness, and bending strength was increased by 10.3%, 43.59%, and 61.5%, respectively, than that of the B₄C/BNMTs composite ceramic without BNMTs. It was proved that the high interface binding energy and bridging effect between boron carbide and BNMTs were the toughening principle of BNMTs.     

Activated treatment of magnesite for preparing size-controlled Mg2B2O5 whiskers and their microwave dielectric properties

In this study, magnesite was activated through hydration and balling treatment, and the received MgO with high activity and H₃BO₃ were used as raw materials for synthesizing Mg₂B₂O₅ whiskers with the aid of KCl salt. Attention was paid to the effects of B/Mg ratio and reaction temperature on the phase transformation and morphology evolution of the produced whiskers, and their growth mechanism was proposed as well. The Mg₂B₂O₅ ceramics were prepared based on the whiskers with different diameters via traditional pressing-sintering. Their physical properties, such as bulk density, apparent porosity and Vickers hardness (Hv), were studied. Particular emphasis was placed on the relationship between microstructure and microwave dielectric properties (ε, Q × f, and τ_f) of the Mg₂B₂O₅ ceramics. According to the results, the higher B/Mg ratio and the lower reaction temperature were more suitable for the growth of Mg₂B₂O₅ whiskers with high aspect ratio conforming to the liquid-solid (LS) mechanism. In particular, the Mg₂B₂O₅ ceramics based on the whiskers with average diameter (AD) = 198 nm and sintered at 1250 °C exhibited good microwave dielectric properties (ε = 6.18, Q × f = 18,597 GHz, and τ_f = −82 ppm/°C). This new design principle provides a guidance for fabricating high value-added magnesia-based ceramics from magnesite.     

Processing and mechanical properties of B4C-SiCw ceramics densified by spark plasma sintering

Homogenous distribution of whiskers in the ceramic matrix is difficult to be achieved. To solve this problem, B₄C-SiC_w powder mixtures were freeze dried from a slurry dispersed by cellulose nanofibrils (CellNF) in this work. Dense B₄C ceramics reinforced with various amounts of SiC_w up to 12 wt% were consolidated by spark plasma sintering (SPS) at 1800 °C for 10 min under 50 MPa. During this process, CellNF was converted into carbon nanostructures. As iron impurities exist in the starting B₄C and SiC_w powders, both thermodynamic calculations and microstructure observations suggest the dissolution and precipitation of SiC_w in the liquids composed of Fe-Si-B-C occurred during sintering. Although not all the SiC_w grains were kept in the final ceramics, B₄C-9 wt% SiC_w ceramics sintered at 1800 °C still exhibit excellent Vickers hardness (35.5 ± 0.8 GPa), flexural strength (560 ± 9 MPa) and fracture toughness (5.1 ± 0.2 MPa·m^1/2), possibly contributed by the high-density stacking faults and twins in their SiC grains, no matter in whisker or particulate forms.     

Improving specific stiffness of silicon carbide ceramics by adding boron carbide

A strategy for improving the specific stiffness of silicon carbide (SiC) ceramics by adding B₄C was developed. The addition of B₄C is effective because (1) the mass density of B₄C is lower than that of SiC, (2) its Young’s modulus is higher than that of SiC, and (3) B₄C is an effective additive for sintering SiC ceramics. Specifically, the specific stiffness of SiC ceramics increased from ~142 × 10⁶ m²?s^?2 to ~153 × 10⁶ m²?s^?2 when the B₄C content was increased from 0.7 wt% to 25 wt%. The strength of the SiC ceramics was maximal with the incorporation of 10 wt% B₄C (755 MPa), and the thermal conductivity decreased linearly from ~183 to ~81 W?m^?1?K^?1 when the B₄C content was increased from 0.7 to 30 wt%. The flexural strength and thermal conductivity of the developed SiC ceramic containing 25 wt% B₄C were ~690 MPa and ~95 W?m^?1?K^?1, respectively.     

Pressureless sintering of SiC ceramics with improved specific stiffness

The effects of B₄C content on the specific stiffness and mechanical and thermal properties of pressureless-sintered SiC ceramics were investigated. SiC ceramics containing 2.5 wt% C and 0.7–20 wt% B₄C as sintering aids could be sintered to ≥ 99.4% of the theoretical density at 2150 °C for 1 h in Ar. The specific stiffness of SiC ceramics increased from 136.1 × 10⁶ to 144.4 × 10⁶ m²‧s⁻² when the B₄C content was increased from 0.7 to 20 wt%. The flexural strength and fracture toughness of the SiC ceramics were maximal with the incorporation of 10 wt% B₄C (558 MPa and 3.69 MPa‧m^1/2, respectively), while the thermal conductivity decreased from ∼154 to ∼83 W‧m⁻¹‧K⁻¹ when the B₄C content was increased from 0.7 to 30 wt%. The flexural strength and thermal conductivity of the developed SiC ceramic containing 20 wt% B₄C were ∼346 MPa and ∼105 W‧m⁻¹‧K⁻¹, respectively.     

High-strength TiB2-B4C composite ceramics sintered by spark plasma sintering

Spark plasma sintering (SPS) is an advanced sintering technique because of its fast sintering speed and short dwelling time. In this study, TiB₂, Y₂O₃, Al₂O₃, and different contents of B₄C were used as the raw materials to synthesize TiB₂-B₄C composites ceramics at 1850°C under a uniaxial loading of 48 MPa for 10 min via SPS in vacuum. The influence of different B₄C content on the microstructure and mechanical properties of TiB₂-B₄C composites ceramics are explored. The experimental results show that TiB₂-B₄C composite ceramic achieves relatively good comprehensive properties and exceptionally excellent flexural strength when the addition amount of B₄C reaches 10 wt.%. Its relative density, Vickers hardness, fracture toughness, and flexural strength reach to 99.20%, 24.65 ± .66 GPa, 3.16 MPa·m^1/2, 730.65 ± 74.11 MPa, respectively.     

Microstructure and mechanical properties of TiB2–B4C ceramics fabricated by hot-pressing

In this study, TiB₂–B₄C composite ceramics were prepared using Y₂O₃ and Al₂O₃ as the sintering aids. Different contents of B₄C were added to seek promoted comprehensive mechanical properties of the composites. The mixed powders were sintered at 1850 °C under a uniaxial loading of 30 MPa for 2 h via hot-pressing. Through the measurement of XRD, SEM and related mechanical properties, the influence of B₄C content on the microstructure and mechanical properties of TiB₂–B₄C composites ceramics was discussed. The experimental results show that TiB₂–B₄C composite ceramics exhibit excellent mechanical properties, which can be attributed to the dense microstructure and fine grain size. In addition, TiB₂–B₄C composite ceramic shows a relatively high comprehensive properties when the addition amount of B₄C is 20 wt%. The relative density, Vickers hardness, fracture toughness and flexural strength are measured to be 99.61%, 27.63 ± 1.73 GPa, 4.77 ± 0.06 MPa m^1/2, 612.5 ± 28.78 MPa, respectively.     

Mechanical properties and pre-oxidation behavior of spark plasma sintered B4C ceramics using (Ti3SiC2+CeO2/La2O3) as sintering aid

B₄C ceramic with the addition of 5 wt % (Ti₃SiC₂+ CeO₂/La₂O₃) as sintering aids was fabricated by spark plasma sintering at a relatively low temperature of 1650 °C for 5 min at 80 MPa. The phase composition, microstructures, and comprehensive mechanical properties of the ceramics were studied in detail. The existence of reinforced second phase particles, the refinement of the matrix grains, the formation of residual stress along the grain boundaries and the appearance of the mixed fracture mode had a synergetic strengthening effect on the mechanical properties. The flexural strength, fracture toughness and Vickers hardness of B₄C ceramics reached 565.2 ± 21.8/551.0 ± 25.2 MPa, 6.28 ± 0.01/6.41 ± 0.12 MPa·m^0.5, and 28.51 ± 0.86/27.23 ± 1.08 GPa, respectively. In addition, to reduce the crack sensitivity of the ceramic, the ceramics were pre-oxidized at 800 °C for different durations. The flexural strength was increased by approximately 13.4% after the ceramic was oxidized at 800 °C for 45 min due to the crack-healing effect induced by the oxide glass B₂O₃ on the ceramic surface.     

Microstructure,mechanical and thermal properties of in situ toughened boron carbide-based ceramic composites co-doped with tungsten carbide and pyrolytic carbon

Boron carbide (B₄C)-based ceramics were pressureless sintered to a relative density of 96.1% at 2150 °C, with the co-incorporation of tungsten carbide and pyrolytic carbon. The as-batched boron carbide power was 7.89 m² g^?1 in surface area. A level of fracture toughness as high as 5.80 ± 0.12 MPa m^1/2 was achieved in the BW-6C composite. Sintering aids of carbon and tungsten boride were formed by an in situ reaction. The toughness improvement was attributed to the presence of thermal residual stress as well as the W₂B₅ platelets. The thermal conductivity and thermal expansivity of the BW-6C composite as a function of temperature are also reported in this work. Our current study demonstrated that the B₄C–W₂B₅ composites could be potential candidate materials for structural applications.     

Magneto-optical,thermal, and mechanical properties of polycrystalline Tb3Al5O12 transparent ceramics

Terbium aluminum garnet (Tb₃Al₅O₁₂, TAG) ceramics have become a promising magneto-optical material owing to the outstanding comprehensive performance, including the magneto-optical, thermal, and mechanical properties. Fine-grained TAG ceramics with high optical quality and mechanical properties have attracted much attention. In this study, TAG ceramics with fine grains and high optical quality are fabricated successfully by a two-step sintering method from co-precipitated nano-powders. After pre-sintered at 1525°C in vacuum and hot isostatic pressed at 1600°C, the in-line transmittance of TAG ceramics reaches 81.8% at 1064 nm, and the average grain size is 7.1 μm. The Verdet constant of TAG ceramics is −179.6 ± 4.8 rad T⁻¹ m⁻¹ at 633 nm and −52.1 ± 1.9 rad T⁻¹ m⁻¹ at 1064 nm, higher than that of commercial Tb₃Ga₅O₁₂ crystals. The thermal conductivity of TAG ceramics is determined from 25 to 450°C, and the result is 5.12 W m⁻¹ K⁻¹ at 25°C and 3.61 W m⁻¹ K⁻¹ at 450°C. A comparison of mechanical properties between large- and fine-grained TAG ceramics fabricated under different conditions is conducted. The fine-grained TAG ceramics possess a bending strength of 226.3 ± 16.4 MPa, which is 9.7% higher than that of the large-grained ceramics. These results indicate that reducing the grain size on the premise of high optical quality helps improve the comprehensive performance of TAG ceramics.     

Aqueous Gelcasting and Pressureless Sintering of Zirconium Diboride Ceramics

Dense (97.3%) zirconium diboride (ZrB₂) ceramics were obtained via gelcasting and pressureless sintering. Four wt% B₄C was used as sintering aid. ZrB₂, SiC, and B₄C can codisperse well in the alkaline region, using a polyacrylate dispersant. Compared with monolithic ZrB₂ (Z), the mechanical properties of ZrB₂‐SiC (ZS) were enhanced. The Vickers hardness and fracture toughness of ZS were (13.1 ± 0.6) GPa and (2.5 ± 0.4) MPa m^1/2, respectively.     

The new complex high-entropy metal boron carbonitride: Microstructure and mechanical properties

In this contribution, the ternary BCN anion systems of high-entropy ceramics (HEC) are consolidated by hot-pressing sintering and the impacts of sintering temperature and the content of amorphous BCN addition on microstructural evolution and mechanical performance were evaluated. Results confirmed that high-entropy, oxide, and BN(C) phases were precipitated for (Ta_0.2Nb_0.2Zr_0.2Hf_0.2Ti_0.2)(B, C, N) ceramics after sintering at 1900°C. With the decrease of BCN addition, a new phase of MiB₂ (Mi representing the metal atoms) occurred. The Vickers hardness, bending strength, elastic modulus, and fracture toughness of the optimized bulk HECs were investigated, obtained at 24.5 ± 2.3 GPa, 522.0 ± 2.6 MPa, 478.9 ± 11.1 GPa, and 5.36 ± 0.56 MPa m^1/2, respectively.     

Synthesis and properties of conductive B4C ceramic composites with TiB2 grain network

High electrical resistance and low fracture toughness of B₄C ceramics are 2 of the primary challenges for further machining of B₄C ceramics. This report illustrates that these 2 challenges can be overcome simultaneously using core‐shell B₄C‐TiB₂&TiC powder composites, which were prepared by molten‐salt method using B₄C (10 ± 0.6 μm) and Ti powders as raw materials without co‐ball milling. Finally, the near completely dense (98%) B₄C‐TiB₂ interlayer ceramic composites were successfully fabricated by subsequent pulsed electric current sintering (PECS). The uniform conductive coating on the surface of B₄C particles improved the mass transport by electro‐migration in PECS and thus enhanced the sinterability of the composites at a comparatively low temperature of 1700°C. The mechanical, electrical and thermal properties of the ceramic composites were investigated. The interconnected conductive TiB₂ phase at the grain boundary of B₄C significantly improved the properties of B₄C‐TiB₂ ceramic composites: in the case of B₄C‐29.8 vol% TiB₂ composite, the fracture toughness of 4.38 MPa·m^1/2, the electrical conductivity of 4.06 × 10⁵ S/m, and a high thermal conductivity of 33 W/mK were achieved.     

Microstructure and mechanical properties of fine-grained boron carbide ceramics fabricated by high-pressure hot pressing combined with high-energy ball milling

Dense and fine-grained boron carbide (B₄C) ceramics were fabricated via high-pressure hot pressing (100?MPa) using powders, which are prepared by high-energy ball milling. These powders were sintered at a low temperature (1800?°C) without any sintering aid. The dense and fine-grained B₄C ceramics demonstrate super high hardness, outstanding fracture toughness and modern flexure strength. The milled powders were characterised by disordered crystal structure and ultrafine particle size that ranges from a few nanometres to a few hundred nanometres. The combined contributions of high pressure and the characteristic of the milled powders guaranteed that the dense fine-grained microstructure was achieved at only 1800?°C. The grain size distribution of the ceramics was inhomogeneous and ranged from 70?nm to 1.6?µm. However, the average grain size was fine at only 430?nm, which partially contributed to the super high hardness of the B₄C ceramics. The locally concentrated areas of the small grains changed the fracture mode of the B₄C ceramics from the complete transgranular fracture to a mixture of transgranular and intergranular fractures, thereby enhancing the toughness of the B₄C ceramics. The relative density, Vickers hardness, flexure strength and fracture toughness of the obtained B₄C ceramics reached up to 99.5%, 41.3?GPa, 564?MPa and 4.41?MPa?m^1/2, respectively.     

Room-temperature mechanical properties of a high-entropy diboride

The mechanical properties of a (Hf,Mo,Nb,Ta,W,Zr)B₂ high-entropy ceramic were measured at room temperature. A two-step synthesis process was utilized to produce the (Hf,Mo,Nb,Ta,W,Zr)B₂ ceramics. The process consisted of a boro/carbothermal reduction reaction followed by solid solution formation and densification through spark plasma sintering. Nominally, phase pure (Hf,Mo,Nb,Ta,W,Zr)B₂ was sintered to near full density (8.98 g/cm³) at 2000°C. The mean grain size was 6 ± 2 µm with a maximum grain size of 17 µm. Flexural strength was 528 ± 53 MPa, Young's modulus was 520 ± 12 GPa, fracture toughness was 3.9 ± 1.2 MPa·m^1/2, and hardness (HV_0.2) was 33.1 ± 1.1 GPa. A Griffith-type analysis determined the strength limiting flaw to be the largest grains in the microstructure. This is one of the first reports of a variety of mechanical properties of a six-component high-entropy diboride.     

First-principles prediction,fabrication and characterization of (Hf0.2Nb0.2Ta0.2Ti0.2Zr0.2)B2 high-entropy borides

The microstructure and mechanical properties of (Hf_0.2Nb_0.2Ta_0.2Ti_0.2Zr_0.2)B₂ high-entropy boride (HEB) were first predicted by first-principles calculations combined with virtual crystal approximation (VCA). The results verified the suitability of VCA scheme in HEB studying. Besides, single-phase (Hf_0.2Nb_0.2Ta_0.2Ti_0.2Zr_0.2)B₂ ceramics were successfully fabricated using boro/carbothermal reduction (BCTR) method and subsequent spark plasma sintering (SPS); furthermore, the effects of different amounts of B₄C on microstructure and mechanical properties were evaluated. Due to the addition of B₄C and C, all samples formed single-phase solid solutions after SPS. When the excess amount of B₄C increased to 5 wt%, the sample with fine grains exhibited superior comprehensive properties with the hardness of 18.1 ± 1.0 GPa, flexural strength of 376 ± 25 MPa, and fracture toughness of 4.70 ± 0.27 MPa m^1/2. Nonetheless, 10 wt% excess of B₄C coarsened the grains and decreased the strength of the ceramic. Moreover, the nanohardness (34.5–36.9 GPa) and Young's modulus (519–571 GPa) values with different B₄C contents just showed a slight difference and were within ranges commonly observed in high-entropy diboride ceramics.     

The effect of carbon nanotubes introduction on the mechanical properties of reaction bonded boron carbide ceramics

The influence of carbon nanotubes (CNTs) on the mechanical properties and structure formation during reactive sintering of B₄C materials with Si addition was studied. Upon infiltrating the B₄C structure with molten silicon, a non-porous composite was formed with a density of 2.45-2.55 g/cm³ and a hardness of 22-27 GPa. The formation of highly dispersed B-C-Si phases was observed in the interphase of adjacent B₄C particles due to the incorporation of Si into B₄C structures. These phases increase the bonding strength between B₄C particles. In spite of the fact that the addition of 1-5 wt% Multi-Walled Carbon Nanotubes decreases the green density of the compacts, the flexural strength of the infiltrated material significantly increased. The improvement of the strength of ceramics modified with MWCNTs was interpreted in terms of the formation of thin flattened SiC crystals at the interfaces between B₄C and B-C-Si particles, which strengthen the interfaces between ceramic particles.