HVOF喷涂WC-10Co-4Cr涂层的砂浆冲蚀行为

以2种不同的HVOF喷涂系统和3种商用粉末在0Cr13Ni5Mo基材上喷涂6种WC-10Co-4Cr涂层,用自行研制的料浆罐冲蚀设备对涂层和基材的砂浆冲蚀行为进行了研究,分析了显微结构和显微硬度对涂层冲蚀性能的影响及涂层冲蚀后的表面形貌.结果表明,在文中试验范围内涂层和基材的冲蚀失重均随冲蚀时间线性增加;各攻角下,WC-10Co-4Cr涂层的耐冲蚀性远远优于0Cr13Ni5Mo不锈钢;除了分层和裂纹明显的涂层,HVOF热喷WC-10Co-4Cr涂层的冲蚀失重表现出对攻角不敏感的特征.涂层的冲蚀机制为粘结相的微切削和涂层片状剥落,低攻角下的剥落坑面积大而浅,高攻角时面积小而深,片状剥落的程度随涂层气孔率的增加而增加.     

含MoS2的超音速喷涂WC-10Co-4Cr复合涂层摩擦性能研究

利用超音速火焰喷涂方法,以WC-10Co-4Cr为基体,添加MoS2以制备WC- 10Co-4Cr/MoS2自润滑复合涂层;对比分析了添加不同含量MoS2涂层的微观组织结构和物相;重点进行了摩擦磨损试验,研究润滑相MoS2对超音速喷涂WC涂层摩擦学特性的影响机理.研究结果表明:引入的MoS2一少部分转化成新态,其余则进入WC涂层空隙中,在摩擦过程中形成润滑膜起到润滑作用,并有效地降低了摩擦因数,使摩擦磨损过程中温升降低,有效减少热损伤,提高了涂层的耐磨性能;WC-10Co-4Cr/MoS2复合涂层具有很好的自润滑性,w(MoS2)15％时WC-10Co-4Cr/MoS2复合涂层的摩擦磨损性能最佳.     

启闭机活塞杆表面超音速火焰喷涂WC-10Co-4Cr涂层的性能

采用超音速火焰热喷涂技术在启闭机活塞杆材料40Cr钢表面制备WC-10Co-4Cr涂层,通过扫描电镜、X射线衍射仪、显微硬度计、摩擦磨损试验机、电化学工作站等手段对涂层的基本性能进行了研究并与基材的性能进行了对比分析。结果表明:涂层的显微硬度为1 330HV0.3是基体的3.9倍,摩擦因数小于基体,其耐磨性能达到基体的145倍,涂层的耐腐蚀性能较基体也有大幅提高,并且涂层致密度高孔隙率低于0.45%,与基体之间的结合强度高于70.37MPa。将涂层应用于活塞杆表面可以大幅提高其表面性能,特别是耐磨性能及耐腐蚀性能,使得活塞杆的使用寿命提高为常用电镀铬的3倍以上。     

HVOF/AC-HVAF热喷WC-10Co-4Cr涂层的耐冲蚀性能

采用高速火焰热喷涂系统（HVOF/AC-HVAF）在0Cr13Ni5Mo不锈钢表面制备了三种组织结构不同的WC-10Co-4Cr涂层,通过料浆罐冲蚀试验机对三种涂层和0Cr13Ni5Mo基材的冲蚀行为和冲蚀机制进行了研究,重点分析涂层组织与耐冲蚀性能的关系. 结果表明,三种涂层的耐冲蚀性能均优于0Cr13Ni5Mo基材,冲蚀失重仅为基材的6% ~ 35%,组织越均匀、致密的涂层耐冲蚀性能越优. 低攻角冲击时,涂层冲蚀机制以粘结相去除,WC颗粒剥落为主,基材冲蚀机制主要为微切削;高攻角冲击时,涂层冲蚀机制以涂层剥落为主,基材的冲蚀机制主要为变形磨损. 涂层的组织决定了不同试验条件下涂层的冲蚀行为和冲蚀机制.     

超音速火焰喷涂WC-10Co-4Cr涂层的摩擦腐蚀性能研究

目的研究不同喷涂距离下WC-10Co-4Cr涂层的摩擦腐蚀性能,探究其机理并优化工艺参数,以提高涂层性能。方法通过超音速火焰喷涂技术在304不锈钢基体上制备WC-10Co-4Cr防护涂层,通过扫描电子显微镜和X射线衍射仪研究涂层的微观结构及相组成,采用维氏显微硬度计测量涂层的显微硬度。采用装配有电化学工作站的摩擦磨损测试仪,对浸没于3.5%NaCl盐溶液中的涂层进行摩擦腐蚀实验,测量涂层在静态及滑动条件下的磨损率、摩擦系数和极化曲线。结果喷涂距离提高时,涂层孔隙率降低,硬度提高,达到1100～1400 HV。在腐蚀介质中滑动摩擦时,WC-10Co-4Cr涂层的磨损率较304不锈钢低2个数量级,磨损率为1.7×10~(-7)mm~3/(N·m),而304不锈钢的磨损率为2.6×10~(-5)mm~3/(N·m)。结论 WC-10Co-4Cr涂层良好的摩擦腐蚀性能归因于承受负载的WC相与产生钝化的金属粘结相之间的协同作用,其抵抗涂层受摩擦腐蚀破坏。     

不同颗粒致密度WC-10Co-4Cr涂层的耐腐蚀性能

在300 M钢表面上,利用超音速火焰喷涂技术将两种不同颗粒致密度的WC-10Co-4Cr粉末制成涂层.利用扫描电镜、X射线衍射仪、显微硬度计分析涂层的微观组织,通过极化试验和浸泡试验分析涂层的耐腐蚀性能.结果表明,高颗粒致密度粉末制备的WC-10Co-4Cr涂层孔隙率为1.52％,是低颗粒致密度粉末制备涂层的1.95倍;在3.5％ NaCl溶液中,高颗粒致密度粉末制备涂层的耐蚀性较差,腐蚀电流密度是低颗粒致密度粉末制备涂层的2.67倍.低颗粒致密度粉末制备的涂层孔隙率低,对基体的保护性较好.     

超音速火焰喷涂微、纳米结构WC-10Co4Cr涂层及其性能

采用超音速火焰喷涂技术（HVOF）在06Cr13Ni4Mo不锈钢基体上分别制备了微米结构、纳米结构WC-10Co4Cr涂层。通过X射线衍射仪（XRD）和扫描电子显微镜（SEM）表征和分析了不同结构WC-10Co4Cr涂层的物相组成、微观组织结构,并对涂层的显微硬度、孔隙率、结合强度、抗冲蚀性能进行了对比,探讨了涂层泥沙冲蚀机理。结果表明：HVOF制备的纳米结构 WC-10Co4Cr涂层组织致密,孔隙率更低,涂层的显微硬度、结合强度高于微米涂层,冲蚀质量损失量也小于微米涂层;纳米结构细化了涂层晶粒,增强了涂层的显微硬度和韧性,提高了涂层的抗微切削和抗疲劳剥落性能,有利于涂层的抗泥沙冲蚀性能。     

Fatigue and corrosion fatigue behavior of an AA6063-T6 aluminum alloy coated with a WC-10Co-4Cr alloy deposited by HVOF thermal spraying

The present investigation has been conducted in order to study the fatigue and corrosion fatigue behavior of an AA6063-T6 aluminum alloy substrate coated with a WC-10Co-4Cr deposited by HVOF thermal spraying. It has been determined that the deposition of such a coating on the aluminum substrate gives rise to significant gains in fatigue life in comparison with the uncoated substrate, when testing is carried out both in air and in a 3 wt.% NaCl solution. It has been shown that during testing in air, the fatigue gain ranges between ~ 540 and 4300%, depending on the maximum alternating stress applied to the material. Larger fatigue gains are associated with low alternating stresses. Also, when fatigue testing is conducted in the NaCl solution, the gain in fatigue resistance varies between ~ 620 and 1460%. Fatigue cracks have been observed to initiate at the coating surface and then grow towards the substrate after propagating through the entire coating thickness. Crack growth along the coating has been observed to occur mainly along the regions formed by the agglomeration of W and W-Co-Cr-rich particles, flanking the tougher Co-Cr-rich areas. Although in the present work residual stresses were not measured, it is believed that the gain in fatigue life of the coating-substrate system is due to the presence of compressive residual stresses within the coating which hinder fatigue crack propagation. The deposition of the coating does not give rise to significant changes in the static mechanical properties and hardness of the aluminum alloy substrate. It has been observed that the WC-10Co-4Cr coating displays a significant indentation size effect and has a mean hardness of ~ 9.4 GPa.     

HVOF喷涂WC-10Co4Cr涂层的性能及滑动磨损机理

目的研究WC-10Co4Cr涂层的耐滑动磨损性能及机理。方法在0Cr13Ni5Mo不锈钢基体上,采用超音速火焰喷涂(HVOF)制备了WC-10Co4Cr金属陶瓷涂层。分析了WC-10Co4Cr涂层的物相组成、显微组织,并测试了其硬度、结合强度、孔隙率及在560 r/min和1120 r/min转速下的滑动磨损性能。结果涂层的显微硬度为1325HV0.2,结合强度为72 MPa。涂层组织致密,孔隙率为0.76%。在560 r/min下磨损10h,涂层与基体的磨损失重比为1:138.36;在1120 r/min下磨损10 h,涂层与基体的磨损失重比为1:127.44。结论在滑动摩擦磨损的初期,涂层的磨损失效机制主要表现为磨粒磨损。随着滑动速度的增大,涂层的磨损失效机制主要表现为疲劳磨损。     

超音速火焰喷涂WC-10Co4Cr涂层的耐滑动磨损行为

采用超音速火焰喷涂(HVOF)工艺制备微米结构WC-10Co4Cr涂层,分别采用金相显微镜、扫描电镜(SEM)、X射线衍射(XRD)和滑动磨损设备分析涂层的微观结构和滑动磨损行为。结果表明:采用液体煤油燃料HVOF喷涂的微米结构WC-10Co4Cr涂层的脱碳程度较低,涂层中仅出现WC和W2C相,而无η相(Co3W3C、Co6W6C)以及软相W。涂层微观结构致密,孔隙率约为1%,平均显微硬度为1 322HV0.3;在相同试验条件下,WC-10Co4Cr涂层的摩擦因数(约0.8)高于不锈钢(1Cr18Ni9Ti)的摩擦因数(约0.5),其滑动体积损失量仅为不锈钢涂层的1/146,具有优异的抗滑动磨损性能。涂层在滑动磨损过程中首先是粘结相的脱落,然后是WC颗粒的磨损。     

超细/纳米结构WC-10Co-4Cr涂层的透射电镜表征与性能分析

利用真空原位还原碳化反应合成超细/纳米WC-Co复合粉末,通过添加一定量Cr获得WC-10Co-4Cr复合粉末,经团聚造粒获得喷涂用复合粉末喂料,采用超音速火焰(HVOF)喷涂系统制备出超细/纳米结构的WC-10Co-4Cr涂层。利用X射线衍射仪,扫描电子显微镜和透射电子显微镜对涂层的物相、显微组织结构、元素分布特征等进行了系统表征,并对涂层耐磨性、耐蚀性进行了测试分析。结果表明:基于原位反应合成WC-Co复合粉制备的超细/纳米结构WC-10Co-4Cr涂层具有较好的耐磨性和耐腐蚀性。涂层以WC为主相,含有非晶结构的粘结相Co(Cr),同时存在少量六方晶体结构的W_2C相和非晶复相W_2C+Co(Cr)。对涂层中元素Co和Cr的分布进行了量化分析,得到其从WC晶粒到相界到共晶区再到Co区的变化规律。结合WC-10Co-4Cr复合粉末和超音速火焰喷涂工艺的特点,阐释了Cr在WC-10Co-4Cr涂层分布状态的形成原因,并讨论了对涂层性能的影响。     

300M钢基体上高速火焰喷涂WC-17Co和WC-10Co4Cr涂层的疲劳和抗盐雾腐蚀性能

以涂层在飞机起落架的应用作为研究背景,在300M超高强钢基体上对替代电镀硬铬的两种高速火焰喷涂WC-17Co和WC-10Co4Cr涂层的疲劳和抗中性盐雾腐蚀性能进行了研究.结果表明,两种有涂层的300M钢的疲劳寿命均高于无涂层300M钢,如考虑扣除涂层承受载荷,有涂层的300M钢与无涂层300M钢的疲劳寿命相当.喷砂镶嵌在基体表面的刚玉砂粒导致有WC-10Co4Cr涂层的疲劳寿命低于有WC-17Co涂层的300M钢.两种涂层对基体的疲劳性能都没有负面影响;两种涂层都提高了300M钢的抗盐雾腐蚀性能,但有WC-10Co4Cr涂层的300M钢表现出更好的抗盐雾腐蚀性能.综合比较两种涂层的性能,高速火焰喷涂WC-10Co4Cr涂层是更好的电镀铬替代涂层.