氧压碱浸-水洗分离高砷锑烟尘中砷锑的研究

以铅阳极泥火法处理过程产出的高砷锑烟尘为处理对象，结合氧压碱浸试验和XRD、ICP-OES等表征方法，探究氧分压、液固比、氢氧化钠浓度、浸出温度、浸出时间对砷、锑、铅分配行为的影响。结果表明，以氧分压2.0 MPa、液固比10 mL/g、氢氧化钠浓度2 mol/L、浸出温度200℃、浸出时间2 h的条件对高砷锑烟尘进行氧压碱浸，浸出渣再经水洗处理，可使烟尘中99.5%以上的砷进入溶液，锑、铅、铋进入浸出渣，水洗渣中砷含量小于0.5%,可制备高品质锑白产品，实现了砷和锑的深度分离。     

高砷锡烟尘碱性浸出脱砷试验研究

采用氢氧化钠浸出高砷锡烟尘进行脱砷试验研究,在氢氧化钠浓度150 g/L、双氧水与烟尘质量比0.15、液固体积质量比5:1、反应时间4 h、反应温度90℃的条件下,砷浸出率92.5%,浸出渣含砷1.5%。浸出渣回收锡、铟,碱浸液冷却结晶回收砷酸钠,实现高砷锡烟尘中砷与锡、铟的有效分离。     

高砷氯氧锑碱浸脱砷试验研究

采用常温碱浸脱砷方法处理高砷氯氧锑,就水洗、液固比、终点pH值等因素对脱砷效果的影响进行了研究。结果表明:浸出前调浆水洗可降酸除铜,浸出时液固比选择12∶1、终点pH值控制在10.0左右可脱除氯氧锑渣中90%以上的砷。含砷浸出液经石灰乳沉砷后可返回浸出工序重复使用。     

白烟尘两段逆流浸出工艺研究

针对白烟尘既富含铜、铅、锌、铋等多种有价金属，又含有砷、镉等有害元素的特点，提出一种两段逆流浸出工艺。采用该工艺进行实验处理某铜冶炼厂生产的白烟尘，分别考察了酸浸方式、初始硫酸质量浓度、酸浸液固比、酸浸温度、酸浸时间对铜砷浸出的影响。探索出最佳工艺条件液固比为4∶1，初始硫酸质量浓度80g/L，反应温度为80℃，反应时间为2 h。二次浸出液返回继续浸出白烟尘，此时白烟尘铜、锌、砷浸出率分别为95.7%、98.5%、92.2%，而浸出渣中铜、锌、砷品位降至0.42%、0.50%、1.28%。铅、铋的品位实现有效富集，二次酸浸渣中品位分别为47.73%和9.72%，相比原料分别富集约2.6倍和4.5倍。     

铜冶炼烟尘选择性湿法脱砷及有价元素的同步回收

针对铜冶炼系统含砷烟尘中砷难以高效富集和脱除的问题,采用水浸-碱浸两步浸出工艺进行脱砷研究。结果表明：含砷烟尘先在液固比1∶1的条件下常温水浸,然后在NaOH浓度2 mol/L、Na₂S浓度0.2 mol/L、温度70℃、液固比4∶1的条件下碱浸,最终砷的平均浸出率为96.27%,浸出渣含砷量小于0.5%,铜、铁、锌、铅的平均浸出率分别为0.01%、0.01%、4.72%和11.17%。     

铜电解黑铜渣处理工艺应用研究

正本研究采用加碱湿磨后固砷焙烧,使铜精炼生产电铜过程中产生的大量含砷锑铋的黑铜渣中的砷与碱生成易溶于水的砷酸钠,在水浸脱砷工序中进入溶液;水浸液中的砷加石灰生成砷酸钙沉淀填埋;脱砷后滤液含碱高、含砷极低,可部分返回循环使用;其它返铜盐厂沉镍工序替代一部分纯碱使用;滤渣进行硫酸浸出,酸浸液可用作生产铜盐产品;硫酸浸渣用于提取锑、铋、银,取得了很好的经济技术指标。现有铜精炼系统电解液净化过程中,砷、锑、铋与铜一起在阴极上析出,产出成分复杂含砷较高的黑铜渣。其数量通常为电铜量的1.0%~1.5%,渣中含铜     

氧化锌烟尘中铟锗的分离回收工艺

采用火法烟化挥发法处理湿法炼锌、火法炼铅渣后产生的氧化锌烟尘主要含锌、铁,还含有铟、锗等一种或多种稀有金属,具有较高的回收价值。常规处理氧化锌烟尘采用两段酸浸工艺处理,通常只能针对其中一种稀有金属进行单一回收,不能满足目前企业的原料变化和冶炼要求。以含铟、锗的氧化锌烟尘为原料,利用铟、锗浸出特性的不同,通过调控反应过程的酸度,分步浸出铟、锗,并通过铟、锗萃取特性的不同,进一步分离回收铟、锗,从而实现氧化锌烟尘中铟、锗的分离提取。结果表明,经三段中浸—低酸浸—高酸浸强化浸出,中浸液中铟含量在2 mg/L左右,锗含量在60 mg/L左右,可用于后续的沉淀回收锗;低酸浸出液的铟含量在280 mg/L左右,锗含量在70 mg/L左右,经过后续的中和沉淀,铟富集到10 075 g/t左右,中和渣进行浸出—萃取—电积得到精铟产品和含锗萃余液,萃余液返回中浸,达到了铟锗分离提取的目的,实现了对资源的综合利用。     

二次净化渣中锑回收工艺研究

通过二次净化渣中回收锑方法研究,试验表明:对二次净化渣采用"盐酸浸铋—碱浸除砷"工艺,能使二次净化渣中锑与铋、铜有效分离、富集,且工艺简单,生产成本低。盐酸浸铋工序铋浸出率97.65%,铜浸出率97.21,锑基本残留在渣相中,通过碱浸脱砷,实现了锑的较好富集,可作为优质锑原料进入锑酸钠生产线进一步回收锑。     

综合回收含砷碱液与二氧化硫烟气的工艺探讨

利用锑冶炼过程中产生的含砷碱液吸收低浓度二氧化硫烟气,然后,通过过滤干燥、煅烧挥发、炭还原等过程后,含砷碱液中的锑富集为锑渣,砷化合物富集在氧化砷烟尘中,碱转化为硫化钠产品。处理过程中,锑的回收率达到了95％,砷超过94％进入氧化砷烟尘中,副产品硫化钠达到了工业级。锑冶炼过程中的含砷碱液和二氧化硫烟气得到了综合回收。     

用黑铜泥制备砷酸钠和焦锑酸钠

采用Na2S作浸出剂,在强碱性介质中浸出黑铜泥中的砷和锑,继续保持强碱性条件,用H2O2氧化浸出液,使砷、锑分离,分别制备砷酸钠和焦锑酸钠。浸出渣可以返回熔炼主流程。     

铜精矿湿法除砷试验研究

研究了铜精矿湿法除砷、除砷浸出液循环利用和浸出液固砷。结果表明:采用湿法工艺可以较好地脱除铜精矿中的砷,砷脱除率达97.51%;只要浸出液中S2-浓度保持足够高,除砷浸出液循环利用就不影响砷的脱除,浸出渣中的砷质量分数可降低到0.50%以下,但是硫化钠耗量较大;除砷浸出液采用常压氧化—铁盐固砷工艺,固砷率为30.80%。     

砷碱渣浸出液氧化脱锑试验

考察了双氧水的加入方式和加入量、反应温度、氧化时间等对砷碱渣浸出液氧化脱锑效果的影响,以及电位与脱锑率的关系。结果表明,最佳工艺参数为:常温、反应时间60min、双氧水加入量为原液体积的0.6%(等价于每克锑17.65 mL)、双氧水进料时间控制在反应的前1/3时间段、反应终点电位-550~-450mV。脱锑率可达到95%以上,氧化后得到的锑酸钠纯度可达到91.83%,达到市售普通锑酸钠的品质要求。该技术突破了价态调控还原浸出液中锑的关键技术。     

Recovery of metal values from copper smelter flue dust

A hydrometallurgical process has been developed for the recovery of valuable metals from the flue dust of a copper smelter. The dust containing various metals, such as lead, zinc, copper, bismuth, indium, cadmium, iron, arsenic etc., was treated using this hydrometallurgical process to recover all these metals and also to solve environmental pollution problems. Leachings were carried out under atmospheric and elevated pressure utilizing sulfuric acid. Sulfuric acid pressure leaching in the absence of oxygen provided the best separation of copper and arsenic. About 80% of arsenic went into solution during leaching, and more than 90% of copper remained in the residue as cupric sulfide. Zinc, cadmium and indium from the solution and bismuth, copper and lead from the residue were recovered by various well-known processes. Arsenic and iron were removed from the solution by oxidation and precipitation as ferric arsenate. Both laboratory and bench-scale experiments were carried out with satisfactory results.     

锑冶炼中砷碱渣与二氧化硫烟气综合回收清洁工艺探讨

通过将炼锑中产生的含砷碱渣经过浸出、含砷碱溶液吸收废气二氧化硫、硫化钠等硫化剂脱砷、硫酸铁深度除砷以及净化浓缩干燥等过程后,难以处理的砷碱渣和废气低含量的二氧化硫得到彻底处理。整个处理过程,锑回收率达到99%,砷开路率超过90%,二氧化硫经吸收超过95%,使气体达到排放标准,碱转化为亚硫酸钠,达到了以废治废的目的,是一种清洁炼锑的工艺。     

含砷金精矿催化压力氧化—氰化提金试验研究

针对某含砷金精矿,进行了催化压力氧化—氰化提金工艺研究,考察了亚硝酸钠用量、氧化温度、硫酸用量、氧分压等对催化压力氧化效果的影响。结果表明:在亚硝酸钠用量50 kg/t,硫酸用量135 kg/t,氧化温度200℃,氧分压0.6 MPa,氧化时间2.0 h的最佳条件下,金浸出率为97.65%;催化压力氧化过程中金溶解率为24.25%;酸性氧化液采用活性炭吸附,金吸附率达到99.51%。该工艺可有效处理含砷金精矿,指标较好。     

锑冶炼中砷碱渣与二氧化硫烟气综合回收清洁工艺探讨

通过将炼锑中产生的含砷碱渣经过浸出、含砷碱溶液吸收废气二氧化硫、硫化钠等硫化剂脱砷、硫酸铁深度除砷以及净化浓缩干燥等过程后,难以处理的砷碱渣和废气低含量的二氧化硫得到彻底处理．整个处理过程,锑回收率达到99％,砷开路率超过90％,二氧化硫吸收率超过95％,使烟气达到排放标准,碱转化为亚硫酸钠,达到了以废治废的目的,是一种清洁炼锑的工艺．     

碱浸预处理提高某含砷锑难处理金精矿回收率的试验研究

内蒙古某黄金矿山金精矿中,金主要包裹在黄铁矿及砷黄铁矿中,同时还有锑金属硫化物的存在。氰化浸出生产工艺中金的回收率比较低,只有76.63%。通过常规氰化工艺条件优化试验,金的回收率最高可达到80.15%。对该低品位含砷、锑难处理金精矿进行碱浸预处理,优先除砷、锑,以提高金氰化浸出率。确定了生产操作的最佳工艺条件,金的氰化回收率由原来的76.63%提高到92%,试验获得了较好技术指标和经济效益。     

复杂高含铟物料铟浸出工艺研究

某铅冶炼厂的复杂高含铟物料为冶炼的中间产物,此物料采用常规酸浸工艺铟的浸出率较低.针对此问题,本文采用盐酸-硫酸混酸浸出、加压酸浸法、硫酸化焙烧-低酸浸出等3种工艺对此复杂高含铟物料进行了试验,在各试验的较佳工艺条件下,试验结果为:采用盐酸-硫酸混酸浸出工艺,铟的浸出率可以达到75.87％,浸出渣铟含量可以降低至0.3...     

某含砷铅矿石抑砷浮铅试验研究

针对某含砷铅矿石性质,进行了抑砷浮铅工艺探讨,考察了铅捕收剂、砷抑制剂等因素对铅砷分离指标的影响,并通过正交试验研究了药剂之间的协同作用。结果表明:在最佳条件下,采用石灰、硫代硫酸钠、硫酸铵组合作为砷抑制剂,丁铵黑药、乙硫氮组合作为铅捕收剂,对矿石进行抑砷浮铅选别,闭路流程获得的铅精矿铅品位46.00%、铅回收率83.26%,银品位1 190.00 g/t、银回收率79.77%,含砷0.58%;砷精矿砷品位8.81%、砷回收率74.58%。     

锌加压酸浸渣中硫磺的回收方法研究

对比分析了浮选法、热过滤法和硫化铵法回收锌加压酸浸渣中硫磺的优缺点。考察了硫化铵溶液浸出浮选硫精矿、硫化物滤饼和多硫化铵母液热分解过程的影响因素。结果表明,液固比和硫化铵浓度对硫磺浸出效果影响较为明显,在最佳试验条件下硫化物滤饼中硫的浸出率约为95%,浮选硫精矿中硫的浸出率和回收率均达到98%,多硫化铵母液热分解后获得的硫磺产品纯度高达99.57%。硫化铵浸出渣中有价金属富集倍数较高,有利于锌加压酸浸渣的综合利用。