回火温度对COST-FB2转子钢析出相与力学性能的影响

 为了调整COST-FB2转子钢的强韧性,采用OM、SEM和TEM等手段研究了回火温度对COST-FB2转子钢的析出相类型与力学性能的影响。结果表明,随着回火温度由350 ℃升高到750 ℃,试验钢的强度、硬度不断下降,塑性和冲击功上升;试验钢350 ℃和570 ℃回火后的高强低韧性可通过再次在700 ℃回火改善。淬火后COST-FB2转子钢中的残余奥氏体,可通过在570 ℃回火消除;在350 ℃和570 ℃回火后马氏体板条内部有大量针状的M₃C,700 ℃回火后的显微组织中M₃C消失,M₂₃C₆在原奥氏体晶界和马氏体板条界上析出,750 ℃回火后晶界上的M₂₃C₆有聚集粗化的现象,部分马氏体板条存在回复现象。     

临界区高温侧正火对COST-FB2钢组织与性能的影响

采用扫描电镜、光学显微镜、力学性能测试等手段研究了临界区高温侧正火工艺对COST-FB2钢的显微组织与力学性能的影响.结果表明：临界区高温侧正火促进了COST-FB2钢中的球状奥氏体增加,同时抑制了针状奥氏体的发展,三次临界区高温侧正火能达到消除组织遗传的目的;最终热处理后的显微组织表明,临界区高温侧正火处理能够优化COST-FB2钢中的析出相,使M₂₃C₆析出相呈细小状弥散分布;临界区高温侧正火处理明显提高了COST-FB2钢的强度和韧性,其中三次临界区高温侧正火后钢的抗拉强度和屈服强度都提高了12%左右,但随着临界区高温侧正火次数的增加,组织中开始出现粗化的M₂₃C₆相,使钢的冲击韧性稍有下降.     

回火工艺对COST-FB2转子钢组织与性能的影响

利用OM、SEM和TEM等手段研究了回火工艺对COST-FB2转子钢的显微组织与力学性能的影响,结果表明:570℃一次回火后,马氏体板条内有杆状Fe_3C和细小颗粒状的MX,板条界有少量颗粒状碳化物析出;700℃二次回火后,板条内杆状Fe_3C和板条界上颗粒状碳化物消失或转变成M_(23)C_6型碳化物。经570℃一次回火,COST-FB2转子钢试样的强度较高,冲击功较低,再经700℃回火强度略有降低,冲击功增加。经不同温度的2次回火的调整,COST-FB2转子钢试样获得了较好的强韧性配合。     

淬火及回火处理对新型槽帮钢30MnSiCrMo组织性能的影响

采用光学显微镜、扫描电镜、拉伸冲击试验机及布氏硬度计等研究了新型槽帮钢30MnSiCrMo经900～920℃30 min淬火,350～550℃2h回火的组织性能变化。结果表明,350～550℃不同回火过程中,试验钢出现马氏体分解、碳化物转变、聚集长大及α相回复再结晶等转变,室温组织由回火马氏体向回火屈氏体和回火索氏体过渡。随着回火温度的上升,基体固溶强化与碳化物析出强化减弱,试验钢的强度与硬度连续降低,而塑性与韧性不断提高,试验钢在900和920℃30 min水淬后450～520℃2 h回火时获得良好的强韧性匹配,即抗拉强度1159～1008 MPa,屈服强度1107～944 MPa,断后伸长率11.8%～15.0%,室温硬度336～293HBW,V型缺口冲击吸收功45.5～67.5 J,能够满足中部槽材料的强韧性要求。     

回火温度对30CrMnSiNi2A钢组织和性能的影响

在200-300℃温度范围内30CrMnSiNi2A钢ε-碳化物稳定性和残余奥氏体的热稳定性较好。因此200-300℃回火均可保持稳定力学性能，并随回火温度的提高钢的屈服强度σ0.2提高。30CrMnSiNi2A钢在400-550℃回火时出现了明显的回火脆性。     

回火温度对淬火后30MnB5热成形钢组织与性能影响

将30MnB5热成形钢进行淬火和回火处理,利用扫描电镜、透射电镜、能谱仪和拉伸性能检测等方法研究了不同回火温度后的显微组织和力学性能变化.经200℃保温2 min回火后热成形钢的综合力学性能最佳,抗拉强度为1774 MPa,总伸长率为8%,强塑积达14 GPa·%以上,该性能满足热成形后作为汽车结构件的使用要求;并且随着回火温度的升高,力学性能呈非单调性变化.200℃低温回火后,主要为板条马氏体和ε碳化物,位错密度略有降低,析出的ε碳化物粒子呈针状分布在马氏体板条内,长度方向大小为100 nm左右,并与位错发生钉扎作用.随着回火温度的升高,板条马氏体发生回复和再结晶,板条边界逐渐模糊,并向等轴状铁素体转变,位错密度显著降低,ε碳化物逐渐向低能态的近球形渗碳体转变并粗化至200 nm左右,对位错的钉扎作用也随之减弱.     

回火温度对Mo-V-Ti钢组织与性能的影响

为了研究回火温度、析出相对含Mo-V-Ti钢组织与性能的影响,试验采用550 mm轧机对含Mo-V-Ti钢轧制后进行完全淬火,然后在630~710℃不同的温度下进行回火。结果表明,高温回火后,钢的组织由回火索氏体和少量贝氏体组成,组织中发生回复和再结晶,钢的强韧性匹配发生变化。在670℃以下回火时产生的析出相主要为Ti、V和Mo复合的碳氮化合物和V、Mo复合的碳氮化合物,随着回火温度的提高,产生了新的析出相Fe、Mn和Mo及V合金渗碳体,析出相对钢的强韧性有重要影响。     

回火对C-Si-Mn系双相钢组织与性能的影响

在实验室研究了回火温度对C-Si-Mn双相钢力学性能与显微组织的影响.力学性能测定结果表明,250℃以下的低温回火,对改善双相钢的伸长率具有良好作用,但是其它力学性能的变化不明显.高于300℃的高温回火对改善双相钢的延性作用不大,但会引起双相钢的屈服强度升高,抗拉强度、加工硬化与烘烤硬化值降低,使双相钢性能恶化.扫描电镜与透射电镜的观察结果表明,低温回火双相钢的显微组织变化不明显,马氏体为板条状,马氏体前沿的铁素体基体中分布着大量的可动位错,高温回火双相钢的显微组织则有较大变化,马氏体分解,边界变得模糊,岛内出现碳化物颗粒,铁素体中的位错密度减小,位错线附近出现粗大的析出物.高温回火后,马氏体的分解软化以及铁素体中位错密度减小是导致双相钢性能恶化的主要原因.     

回火工艺对热轧低碳贝氏体高强钢组织和性能的影响

通过大量的试验检验数据,研究了回火热处理工艺对550 MPa级低碳贝氏体高强钢显微组织和力学性能的影响.结果 表明:经650℃高温回火热处理后,试验钢主要组织为粒状贝氏体和准多边形铁素体的混合组织,准多边形铁素体组织占比有所增加;回火热处理后钢板屈服强度、延伸率得到明显提高,但抗拉强度受到的影响相对较小,屈强比呈上升趋...     

回火处理对一种低碳贝氏体钢组织及低温韧性的影响

对一种含硼的低碳贝氏体钢进行了不同工艺的回火处理,并通过室温拉伸、摆锤冲击实验和扫描电镜研究了回火处理对实验钢的晶粒尺寸、晶界比例、贝氏体板条块的演变及强韧性的影响。结果表明,回火处理可使实验钢屈服强度升高,低温韧性显著改善,高温回火后塑性提高。300T实验钢-20℃下断口为韧窝断裂和准解理组成的混合型断裂,而500T和650T实验钢断口为韧窝断裂,600℃出现回火脆性区间,韧性恶化,属混合型断裂。650T钢的低温韧性最优,较高的回火温度促进了小角度晶界的迁移、亚晶合并过程,亚板条块数量减少,大角度晶界的比例、数量提高,晶粒尺寸有效细化,同时单位面积内板条块数目显著增加,有效地钝化了裂纹,提高了低温韧性。     

回火温度对Cu-Cr-Ti马氏体耐磨钢组织及强韧性的影响

摘要：矿山机械用耐磨钢构件服役环境恶劣而常常出现磨损失效,研究适用于复杂工况下的高耐磨钢成分、工艺与组织性能的关系,有利于提高耐磨构件的服役寿命并降低经济损失。利用SEM、TEM、洛氏硬度计、万能拉伸试验机及冲击试验机等,研究了160～400℃不同回火温度下Cu-Cr-Ti马氏体耐磨钢的组织形貌、强度硬度及-20℃冲击韧性的变化。结果表明,试验钢淬火态组织主要为板条马氏体,当回火温度为160℃时,马氏体板条依然清晰,但随回火温度升高到400℃,马氏体板条界渐渐消失,基体中出现大量片状或粒状渗碳体。EDS分析发现样品钢基体中含有纳米级Ti、Nb的碳氮化物。随回火温度升高,基体组织演变导致强化机制发生变化,回火温度为300℃,综合力学性能最佳,其抗拉强度为1500MPa,屈服强度1100MPa,伸长率为15.5%。随回火温度升高,-20℃冲击韧性由60J/cm2逐渐降低到36.3J/cm2。     

Variation microstructure and properties of X80 pipeline steel in the rapid induction tempering process

A self-developed electromagnetic induction-heating device was used to investigate the variation in the microstructure and properties of X80 pipeline steel in the rapid induction tempering process at different process parameters. The effects of the tempering condition on toughness,microstructure,size and distribution of precipitates of X80 pipeline steel were observed using a metallographic microscopy and scanning electron microscopy.Compared with the samples prepared via traditional tempering techniques,results showthat the samples prepared via rapid induction tempering had improved performances. When the heating temperature is 590 ℃,at a holding time of90 s,it was found that acicular ferrite was refined,carbonite precipitation was small,and precipitates were evenly distributed in the matrix. The low-temperature impact energy,also known as the impact absorption energy,at- 40 ℃ was found to be 430. 5 J for the rapid induction tempering samples and 323. 2 J for the traditionally tempered sample. The low-temperature impact energy at- 60 ℃ was found to be 351. 3 J for the rapid induction tempered sample and 312. 1 J for the tradition tempering sample.     

终冷温度对风电用S460级钢组织性能的影响

在S460铁素体钢的控轧控冷实验中,采用纯净冶炼,控制轧制和加速冷却相结合的方法,研究了不同终冷温度对钢板显微组织和力学性能的影响.不同终冷温度下显微组织均由多边形铁素体和珠光体组成.终冷温度为570℃时,较细的显微组织导致了较高的-80和-110℃冲击功.终冷温度为630℃时,较多的析出粒子导致了较高的屈服强度以及-...     

回火温度对Ti-V-Mo复合微合金钢组织及硬度的影响

利用OM、SEM、TEM、EBSD和维氏硬度计等手段研究了回火温度对Ti-V-Mo复合微合金钢组织转变及硬度的影响,探讨了(Ti,V,Mo)C在不同回火温度下的析出规律及其对硬度的作用机制。结果表明,在450～600℃回火时,随着回火温度的升高,硬度呈直线上升趋势,在600℃回火时硬度具有最大值450HV。随着回火温度的升高,试验钢马氏体板条块宽度由7.3μm增大至9.9μm,600℃回火时析出相粒子的平均尺寸为5 nm,10 nm以下的(Ti,V,Mo)C粒子可高达90%,理论计算沉淀强化增量导致硬度上升90.7HV,远高于基体软化造成的硬度损失,因而析出强化是影响Ti-V-Mo复合微合金钢硬度的主要因素。在600～650℃回火,大小角度晶界分布比例基本相同,马氏体板条块的平均尺寸变化不大,但是析出相的平均尺寸由5 nm提高到5.6 nm,尺寸小于5 nm的(Ti,V,Mo)C粒子所占比例逐渐下降,导致硬度下降。     

冷却速率对奥氏体型FeMnAlC钢组织和性能的影响

利用SEM、TEM、XRD、EPMA等手段,研究了水冷、空冷和炉冷对奥氏体基FeMnAlC钢微观组织和力学性能的影响.研究结果表明,3种冷却工艺都获得了以奥氏体为基体的微观组织,均含有大量孪晶,随冷却速度的降低,沿晶界析出的铁素体和κ碳化物逐渐增多,微观结构呈现出从以位错为主到调制结构再到矩形畴界的转变过程,组织演变受...     

淬火工艺对高速列车车轴用DZ2钢组织性能的影响

摘要：采用OM、SEM、EBSD、室温拉伸试验和低温冲击试验,揭示了淬火工艺对高速列车车轴用DZ2钢组织和性能的影响。研究结果表明,经850℃两次淬火和650℃回火后,DZ2钢获得了最佳的力学性能。抗拉强度、屈服强度、断后伸长率和-40℃冲击吸收能量分别为874MPa、773MPa、24%和222J。该工艺条件下原始奥氏体晶粒、马氏体板条束和板条块最为细小,其尺寸分别为14.9、6.9和1.32μm,较经950℃淬火和650℃回火后的分别细化了14.3、5.2和0.35μm,可有效抑制裂纹的扩展,提高低温韧性,韧脆转变温度由-103℃显著降低至-136℃。     

LNG用7％Ni钢快速回火工艺模拟

摘要：采用淬火膨胀仪模拟研究了LNG用7%Ni钢淬火后快速加热回火工艺,结合显微组织观察以及对回火冷却过程中膨胀曲线的分析,讨论了该工艺对钢中逆转变奥氏体含量及其稳定性的影响。结果表明,提高淬火终冷温度能显著增加组织中逆转变奥氏体的含量,且其在基体上的分布也更为均匀,但当淬火终冷温度提高至300℃时,淬火组织中残留了大量的残余奥氏体,经快速加热回火后虽然保留在组织中,但其稳定性较差,导致冷却后的最终组织中出现大量的岛状M/A。回火前的快速加热一方面抑制了残余奥氏体在加热过程中发生分解,同时也有利于碳原子在较短的时间内扩散至其中,因此不但能促进钢中逆转变奥氏体含量的增加,也有利于其稳定性的提高。     

Effect of quenching process on microstructure and properties of DZ2 steel for high speed train axle

The effect of quenching process on the microstructure and properties of DZ2 steel used for high speed train axles is revealed by means of OM, SEM, EBSD, room temperature tensile test and low temperature impact test. The results show that after twice quenching at 850℃ and tempering at 650℃, the optimum mechanical properties of DZ2 steel were obtained. The tensile strength, yield strength, elongation after fracture and impact energy absorption at -40℃ of DZ2 steel are 874MPa, 773MPa, 24% and 222J, respectively. Moreover, the prior austenite grain, martensite packet and block are the finest, with the size of 14.9, 6.9 and 1.32μm, respectively, which are 14.3, 5.2 and 0.35μm finer than those after quenching at 950℃ and tempering at 650℃, respectively. And it is found that finer prior austenite grain boundaries, packet boundaries and block boundaries can effectively inhibit the crack propagation and improve the low temperature toughness, resulting in the ductile brittle transition temperature of DZ2 steel significantly reduced from -103℃ to -136℃.