Study on Microstructure Refinement of Vanadium and Nitrogen Microalloyed Low Carbon Bainitic Steel

The effect of relaxation treatment after finish rolling on microstructure and mechanical properties has been investigated for a vanadium and nitrogen microalloyed low carbon bainitic steel.Finer lath bainite microstructure can be obtained in the plate with relaxation.The results of quantitative statistics show that in the plate without relaxation,80% of the total bainite lath bundles are in the range 5-15μm in length and 3-13μm in width,while in the plate with relaxation 80% of the total bundles are in the range 3-9μm in length and 1-7μm in width.The mechanical properties show that the plate with relaxation has higher impact energy,yield strength and hardness than the plate without relaxation,also the comprehensive performance after tempered at 650℃ is superior to the plate without relaxation.     

氮对钒微合金化钢筋组织与性能的影响

通过生产试验及现有的大量研究成果研究了不同氮含量钒微合金化钢筋的组织与性能。研究结果表明,随着氮含量的增加,钢筋的组织晶粒度无明显变化,但钢筋的屈服强度增加,其原因是氮促进了V（C,N）的析出,有效地细化了析出物的颗粒尺寸,从而大大增强了钒的沉淀强化效果。     

钒,氮含量对耐磨钢NM400组织及性能的影响

在普通Cr-Mo-B系低合金耐磨钢成分基础上,通过添加适量的钒、氮元素,研究钒氮微合金化对轧后直接淬火(DQ)+低温回火耐磨钢板组织及性能的影响。结果表明:无钒氮钢板的微观组织为板条马氏体组织,-20℃冲击功为15 J,布氏硬度为443HBW。分别添加质量分数0.088%V-0.013%N和0.089%V-0.029%N的2种钒氮微合金化的钢板,板条马氏体组织明显细化,在组织中发现存在少量针状铁素体组织。2种钢板的-20℃冲击功分别提高至30和42 J,质量分数0.089%V-0.029%N的钢板强度、硬度与无钒氮钢板基本一致。低温轧制过程中析出的V(C,N)颗粒起到定扎奥氏体晶界、抑制晶粒长大作用。在860℃温度终轧及轧后弛豫过程中析出的V(N,C)粒子可以促进针状铁素体形成,它们起到分割奥氏体晶粒、细化马氏体板条束的作用。含质量分数0.089%V-0.029%N的耐磨钢板的综合性能最好。     

钒对耐火耐候钢组织与性能的影响

为了探索V对耐火耐候钢组织和性能的影响,采用相变仪、电子显微镜、相分析和拉伸等方法,研究了V对CCT曲线、不同热轧工艺条件下显微组织及室温和600℃拉伸性能的影响,探讨了微观组织与力学性能之间的关系.结果表明向钢中添加V可以提高相变温度,而0.20%V促进铁素体的形成;V在钢中的作用取决于其析出相,随钢中V含量增加,析出V量增加,析出物数量相应增加并细化;对于0.60%Mo耐火耐候钢,要得到高的高温屈服强度和YS比,组织中必须引入适当比例的贝氏体.     

V-N微合金化Q460GJC钢板的研发

 为降低传统的Nb-V复合微合金化Q460建筑用钢板中的合金含量及生产成本,利用第3代TMCP技术和V-N微合金化技术,研制出单独V-N微合金化(wV=0.06%~0.08%)、不含铌的合金设计,并通过合理地控轧控冷工艺,在中厚板轧机上成功地生产出厚度40和50mm的V-N微合金化Q460GJC钢板。产品具有良好的综合性能,屈服强度大于470MPa,0℃冲击功超过150J,屈强比仅为80%。分析表明,细晶及析出强化对强度的贡献比例达到66%。     

HRB400螺纹钢筋产品的开发

论述了萍钢公司开发HRB400螺纹钢筋产品的工艺技术过程。     

三级钢筋钒合金化的实践与研究

承钢冶炼三级钢试验了钒铁、氮化钒和氮化钒铁3种不同的钒合金,钢筋性能均满足用户要求。通过对比分析其成分控制,认为对于钒吸收率,氮化钒铁最高、氮化钒次之、钒铁最低。对比其钢筋性能,在碳当量相同时,认为加氮化钒的钢筋其屈服强度和抗拉强度最高,氮化钒铁次之,钒铁最低,对低成本冶炼三级钢具有指导意义。     

VN12合金在钒氮微合金化钢中的应用研究

本文主要介绍了在济钢２０ＭｎＳｉＶ、１６ＭｎＶ钢中,加入钒铁合金ＶＦｅ（５１．６％Ｖ）及美国钒公司提供的专利产品富氮钒合金ＶＮ１２（８０％Ｖ,１２％Ｎ）的对比试验,研究了钒、氮复合微合金化对钢的力学性能的影响,分析了采用钒铁及富氮钒合金微合金化时,钢中钒含量的差别及其经济性。     

带肋钢筋套筒挤压连接技术简介

介绍了带肋钢筋套筒挤压连接技术的定义、适用范围、主要优点、施工中的主要注意事项、质量检查要求。     

钢筋下料优化设计

通过钢筋下料长度设计,探讨了优化设计的必要性、可行性,并通过实例来说明线性规划法在钢筋下料方案设计中的运用。     

Effects of RE and Vanadium on Microalloyed Steel

The effects of RE were studied by TEM, SEM, ICP and thermal simulation methods in vanadium microalloyed steel. The content.of RE in the solid solution can reach the order of 10^-5 --10^-4 in steel. The solid solution of RE was found to reduce the stability of precipitated V (C, N ), impede the precipitation of V (C, N ) in austenite, and accelerate and refine the precipitation of V (C, N) in ferrite. The combined effect of RE and V is to delay the dynamic recrystaUization, refine the grains and second phase particles, and to promote the precipitation of V (C, N) obviously. Thus the microalloying with RE and V leads to raising the strength and toughness of steel.     

微钛处理对钒微合金钢组织与力学性能的影响

在承钢1780热连轧生产线上,轧制了钒微合金钢及钒钛复合微合金化钢,研究了微钛处理对钒微合金化钢微观组织与力学性能的影响.试验结果表明,钒微合金钢经微钛处理后生成了少量TiN析出物,其数量较少,晶粒细化效果有限;由于钛与氮的优先结合,减少了与钒结合的氮含量,降低了钒的析出量,导致微钛处理的钒微合金钢抗拉强度降低约54 ...     

Research, Development, and Production of V-N Microalloyed High Strength Rebars for Building in China

The research,production,and application of V-N microalloyed high strength rebars in China were reviewed.Enhanced nitrogen in vanadium-containing rebars promotes the precipitation of fine V（C,N）particles,and markedly improves the precipitation strengthening effectiveness of vanadium.Therefore,vanadium added to V-N microalloyed rebars can be reduced by 40% compared to the same strength level of vanadium-containing rebars.     

HRB400Ⅲ钢筋抗震性能研究

从强度与塑性的配合、应变时效敏感性、低温脆性、可焊性等方面对Ф20mm牌号为20MnSiV HRB400Ⅲ钢筋的抗震性能进行了系统的测试和研究。结果表明,钢筋应变时效后韧脆转变温度较高,低温抗震性能差;钢筋碳当量高,焊接性能有待改善;微观分析和成分分析结果表明,为加强钢筋的抗震性能,微合金元素应当适当调整。     

氮含量对正火型钒微合金化钢强化效果和显微组织的影响

 利用V-N微合金化技术,在Q345钢基础上进行V-N微合金化,将通用型正火容器用钢的强度水平由345 MPa升级至400 MPa。考察了不同N含量对正火型V-N钢组织和强化效果的影响。结果表明,随着N含量增加,正火态V微合金化试验钢的屈服强度明显提高;每加入50×10-6的N,屈服强度提高18 MPa左右,同时屈强比上升。随着N含量提高,V微合金化钢产生明显的晶粒细化效果,试验钢的铁素体晶粒尺寸由13.36 μm逐渐细化至7.89 μm。对比热轧态试验钢和正火态试验钢的强化效果,发现正火态试验钢的析出强化作用相对较弱,而细晶强化作用相对显著。     

稀土微合金化钢稀土加入工艺的选择

总结了稀土在钢中的作用,提出了稀土微合金化钢的定义,对比研究了不同稀土加入工艺,研究表明结晶器喂丝是当前稀土微合金化钢生产的最为合理的稀土加入工艺。     

气体增氮法冶炼钒氮微合金钢

从理论上分析了钢液增氮的热力学、动力学影响因素,进行了BOF＋RH双联吹氮冶炼钒氮钢试验。结果表明,转炉底吹、RH喷吹均能有效增加钢液氮含量。RH真空度两段式控制既能满足控氢要求又能实现钢液搬出时较高的氮含量。BOF＋RH双联吹氮气工艺可以不加含氮合金冶炼钒氮微合金钢。     

氮对高强度耐候钢钒析出行为的影响

在普通耐候钢的基础上采用单独添加或复合添加微合金元素的方法生产高强度耐候钢,并结合攀枝花现有资源特点,针对性地进行了不同氮含量含钒高强度耐候钢的研究。采用Glbeele-3500热模拟试验机、相分析等方法,研究了含钒高强度耐候钢在不同变形程度及变形温度条件下的钒析出-温度-时间关系(PTT曲线),探讨了氮含量、变形量对钒析出行为的影响。试验表明,试验钢的PTT曲线为典型的C曲线形状,在一定的奥氏体化条件下,钒析出过程存在所需时间最短的析出温度;增加氮含量会使PTT曲线明显向左移动;增加变形量可以加快V(C,N)在奥氏体中的析出过程,使PTT曲线向左移动;变形量越大,析出开始时间越短。通过研究,为进一步产品开发提供了技术支持。     

高韧性锚杆钢筋的开发

为解决树脂锚杆钢筋在应用中杆体加工端发生脆断问题,提出将韧性指标作为锚杆钢筋的质量控制指标之一,并确定了400 MPa级以上的产品20℃冲击功(Akv)不小于30 J的领先指标.为此,结合装备水平采用了“低温开轧、快速冷却为主,优化成分、进一步提高钢的洁净度为辅”的先进生产工艺,成功开发出了冲击韧性指标突出、综合性能优良的低成本高安全性的高级锚杆钢筋.     

铝对微合金钢奥氏体分解动力学的影响

通过实验室热模拟和轧制实验研究了添加0.21%Al对成分为0.05%C-1.7%Mn-0.4%Si-0.05%Nb-0.03%Ti(质量分数)的微合金钢奥氏体分解动力学的影响.结果表明:加入0.21%Al在冷速为10℃/s范围内明显抑制奥氏体向先共析铁素体的转变,提高了贝氏体的淬透性;对于780℃终轧后在600℃等温20min的钢板,Al通过提高碳的活度减轻或避免了带状组织的形成,明显提高了轧制钢板的力学性能.