复掺矿物掺合料对C50海工混凝土性能影响

研究了复掺技术对C50海工混凝土力学性能、工作性能和耐久性能的影响规律。试验结果表明,粉煤灰和矿粉复掺能增强混凝土的抗压和抗折强度,改善新拌浆体的工作性能,硅灰尽管降低了混凝土工作性,却极大提高了它的强度和耐久性。     

Recycling of industrial waste and performance of steel slag green concrete

Workability and mechanical properties of steel slag green concrete with different types of steel slag and different dosages of admixtures were investigated. The effectiveness of steel slag powder on suppressing alkali aggregate reaction (AAR) expansion was assessed using the method of ASTM C441 and accelerated test method. Experimental results show that mechanical properties can be improved further due to the synergistic effect and mutual activation when compound mineral admixtures with steel slag powder and blast-furnace slag powder are mixed into concrete. In addition, about 50% decrease in expansion rate of mortar bars with mineral admixtures can be achieved in AAR tests. Mineral admixtures with steel slag powder as partial replacement for Portland cement in concrete is an effective means for controlling expansion due to AAR.     

高强轻集料混凝土分层离析控制技术的研究

针对轻集料混凝土易分层离析的特点 ,采用掺加高效减水剂、矿物掺和料、调整砂率、掺入有机纤维和控制轻集料粒径等技术措施有效防止了轻集料混凝土的分层离析 ,建立了高强轻集料混凝土的工作性能评价体系 ,配制出工作性能好 ,易泵送的CL4 0 -CL6 0高强轻集料混凝土     

矿物掺合料对大流动性轻混凝土拌和物性能的影响

针对轻混凝土拌和物在大流动性条件下,易于分层而导致工作性不良的现象,采用L-800混凝土拌和物流动性能测定仪,结合混凝土拌和物性能测定方法,研究了粉煤灰和硅灰等矿物掺合料对大流动性轻混凝土(HFLC)拌和物在不同时间间隔时流过40 cm距离的流动时间t(40,T)、坍落度和扩展度等工作性能的影响.结果表明,掺加矿物掺合料是保证HFLC拌和物具有较好性能的关键因素,Ⅰ级粉煤灰和硅灰的最佳掺量分别为水泥总用量的30%和2%.     

双高混凝土优化配制试验研究

混凝土高性能化是保障混凝土结构质量的基本措施。通过系列试验,优化了双高(高工作性能、高强)混凝土配合比,研究了其基本力学性能,确定了C50~C80混凝土的施工配合比。结果表明:采用P·O 42.5R普通硅酸盐水泥,掺加优质矿粉和高性能聚羧酸减水剂,可配制拌合物工作性能良好的C70、C75和C80混凝土,其基本力学性能满足现行结构设计规范要求。基于试验结果,建议了考虑胶结材料强度和密度、水胶比的双高混凝土立方体抗压强度计算公式,并分别分析了轴心抗压强度、抗压弹性模量、劈裂抗拉强度和抗折强度与立方体抗压强度的关系。     

掺矿粉混凝土在黑糜峰工程的应用

黑糜峰工程地下厂房和洞室群为大体积混凝土结构,为使其混凝土耐久性达到较高要求,通过配制掺矿粉混凝土和不掺矿粉混凝土进行力学性能及耐久性能试验对比,结果表明选用掺矿粉混凝土,既可减少水泥用量、降低混凝土成本,又可改善混凝土的和易性和可泵性,提高混凝土耐久性能,并达到工程设计和规范要求.     

多元外加剂复掺对混凝土抗渗性的研究

为了改善混凝土抗渗性,采用多元矿物外加剂、聚丙烯纤维与引气剂组合复掺配制混凝土,并进行了混凝土渗透性试验．结果表明：多元矿物外加剂复掺,可有效提高混凝土的抗渗性;而多元矿物外加剂分别与一定量聚丙烯纤维和引气剂复掺,可使混凝土抗渗性得到进一步改善,且随着聚丙烯纤维和引气剂掺量在一定范围内的增加,混凝土抗渗性的改善程度愈加明显．     

尾矿砂商品混凝土的试验研究与工程应用

用细度模数为1.8的铁矿尾矿砂,分别以30%,40%,50%和60%的比率取代天然砂,配制C20,C30和C40商品混凝土。通过与基准混凝土的对比试验,研究了不同取代率时,尾矿砂混凝土的和易性、抗压强度等性能以及50%取代率时,尾矿砂混凝土抗氯离子渗透性能。结果表明：尾矿砂取代率为30%,40%和50%时,各强度等级的尾矿砂混凝土的和易性、抗压强度均能满足要求;当取代率达到60%时,混凝土和易性较差,但抗压强度仍能满足要求;当取代率为50%时,尾矿砂混凝土抗氯离子渗透能力与基准混凝土相当。将尾矿砂取代率为40%和50%的混凝土应用于相关工程,经持续质量跟踪,未发现任何问题,且经济和社会效益显著。     

C80机制砂泵送混凝土的配制及其影响因素

以机制砂为细骨料，对C80泵送混凝土的配合比和掺合料进行了优化、着重对机制砂的石粉含量和砂率等因素对混凝土工作性和强度的影响规律进行了探讨：结果表明：机制砂混凝土合理砂率应略大于相应的河砂混凝土，且存在最佳砂率（45％）；机制砂中一定量的石粉对混凝土强度和工作性有促进作用，在7％石粉含量情况下，C80机制砂混凝土强度和工作性均达到最佳。     

大跨度细管径薄壁钢管拱桥混凝土配合比设计与施工

浙江南浦大桥为典型的大跨度、细管径薄壁钢管混凝土拱桥,其钢管混凝土施工采用泵送顶升法,施工难度大,对混凝土性能要求高.经混凝土配合比设计与优化,制备出满足设计要求的C50微膨胀钢管混凝土,并进行混凝土的拌合物性能、物理力学性能及微观结构分析研究.结果表明,所配制的混凝土不离析、不泌水,初始坍落度23 cm,扩展度不小于60 cm,混凝土拌和物3 h后的坍落度不小于18 cm,混凝土具有早强、高弹性模量和补偿收缩等性能,完全满足浙江南浦钢管混凝土拱桥的工程设计及施工要求.     

矿物掺合料对混凝土抗氯离子渗透性影响研究

氯离子渗透腐蚀是引起钢筋混凝土腐蚀的主要原因,然而氯离子渗透性和矿物掺合料有直接关联。主要通过实验研究了掺入矿物掺合料后混凝土中孔结构的特征,进而分析了矿物掺合料对混凝土抗氯离子渗透性的影响。     

高强页岩轻集料混凝土的力学性能

目的探索影响高强页岩轻集料混凝土力学性能的主要因素,为制备高强页岩轻集料混凝土提供依据.方法配制高强度页岩轻集料混凝土,并利用微观手段观察页岩轻集料混凝土微观结构特征.选择水胶质量比0.34～0.38、砂率38%和粉煤灰掺入量10%,提前预湿轻集料和选用高强度等级的页岩轻集料.结果配制出28 d抗压强度为55～60 MPa的页岩轻集料混凝土.水胶质量比、砂率、粉煤灰掺入量对轻集料混凝土的抗压强度有着不同程度地影响.页岩轻集料混凝土抗压强度随着水胶质量比减少而增大;合理砂率为38%和最佳的粉煤灰掺量10%.结论轻集料本身的强度对配制高强度等级轻集料混凝土起到非常重要的作用,同时通过预湿轻集料可以有效提高轻集料混凝土的后期强度.     

Determination of the Thermal Expansion Coefficient of Concrete at Early Ages by Using Temperature-stress Testing Machine

By using the uptodate temperatuer-stress testing machine, the thermal expansion coefficient of concrete at early ages was studied and indicative conclusions were achieved ： temperature rising due to hydration heat is not directly correlated with cracking, but the temperature and stress evolation process should be taken into consideration in the same time. Proper chemical admixtures and mineral cornpasitions can improve the mechanical properties of concrete such as thermal expansion coefficient, which is very indicative in practice.     

减少高强混凝土中未水化水泥的方法研究

双掺、三掺方式可以保证混凝土在大掺量矿物掺合料条件下仍具有良好的工作性、较高的强度 ,同时还可以显著提高硬化混凝土密实性 ,有效改善水泥石 集料界面区结构 ,从而减少了硬化混凝土中未水化水泥数量 ,抑制了外界水分的渗入 ,最终消除了未水化水泥日后的水化对混凝土的危害     

新型混凝土减缩剂的研究(Ⅱ)--混凝土试验

将能够显著降低水泥胶砂自收缩率的减缩剂应用于高强混凝土，考察其对混凝土工作性、强度和自收缩率等性能的影响，结果证实该种减水剂同样能够有效地改善高强混凝土的自收缩率，显著提高抗开裂能力，对混凝土早期强度无不良影响，但会轻微降低混凝土28d抗压强度，综合考虑各项因素，认为该种减缩剂适用于实际工程应用。     

公路面层脱硫石膏—粉煤灰混凝土试验研究与应用

脱硫石膏和粉煤灰按比例混合后,掺入适量改性剂复合而成一种新型活性矿物掺合料,并制备C30～C40脱硫石膏-粉煤灰混凝土,试验研究其主要技术性能。结果表明,脱硫石膏-粉煤灰按质量比例掺入30%以上,混凝土不离析、不泌水,施工和易性优于普通混凝土;力学性能满足公路面层设计要求;180d干缩率小于450×10-6、磨耗量仅为标准限值的60%左右,抗冻等级大于D300。脱硫石膏-粉煤灰混凝土成功应用于常德桃花源-花岩溪旅游公路路面试验段施工,社会经济和环保效益显著。     

Experimental investigation on dynamic mechanical characteristics and microstructure of steam-cured concrete

Steam-cured concrete is widely used to manufacture prefabricated units of high-speed railway foundation structure such as girder and track slab. The dynamic mechanical property of steam-cured concrete is one of the key properties affecting service performance of high-speed railway foundation structure. In the present paper, serial macro/micro-experiments were carried out to investigate the dynamic elastic modulus, shear modulus, damping ratio, and microstructure of steam-cured concrete. The relationships between compositions, curing regime, microstructure, and dynamic properties of steam-cured concrete as well as the corresponding mechanisms were discussed. The results indicate that steam-cured concrete in early age has a larger dynamic elastic modulus and shear modulus as well as a smaller damping ratio compared with standard-cured concrete. On the contrary, at a later age a slightly smaller dynamic elastic modulus and a larger damping ratio of steam-cured concrete are observed. Addition of mineral admixture results in a bit lower dynamic elastic modulus and damping ratio of concrete than that of the control specimen without mineral admixtures. The achievements can provide some fundamental suggestions for materials parameters selection during structural design of steam-cured concrete precast element.     

自密实混凝土配合比优化研究

自密实混凝土是一种具有高工作性能的高性能混凝土。本文探讨了自密实混凝土工作性能的评定方法,并对掺加磨细矿渣的自密实混凝土进行了研究。通过分析磨细矿渣含量、胶凝材料总量、砂率、减水剂掺量对自密实混凝土流动性和强度的影响,配制了高工作性能和力学性能的自密实混凝土,为掺加磨细矿渣的高强自密实混凝土配合比设计提供了依据。     

混凝土矿物复合掺合料应用技术规范的探讨

目前,混凝土矿物掺合料应用技术规范多数是对单一矿物掺合料做出了规定,缺乏对复合混凝土矿物掺合料的应用技术标准.鉴于混凝土掺合料应用技术水平还相当粗犷,为提高其应用技术水平,提出了混凝土矿物掺合料必须走专业化生产的道路;为适应和指导混凝土矿物复合掺合料的工程应用,提出了其必须走功能化生产的道路,建议复合混凝土掺合料应按混凝土的性能进行配制和使用,并推荐了复合混凝土掺合料规范的部分技术指标.     

桥梁清水混凝土设计方法与匀质性控制

根据桥梁工程结构特点,提出了桥梁清水混凝土的配合比优化设计方法,制备出粘聚性与包裹性好、流动度佳,且具有优良力学性能的C30~C50高性能清水混凝土。通过对混凝土拌合物含气量、硬化试件不同部位显微硬度与微观结构的测试,分析了增粘剂对其匀质性的影响规律。试验表明：对于C30桥梁清水混凝土,掺5×10 -5的纤维素醚或掺6%的硅灰时,混凝土的含气量不超过2%,浆体旋转粘度值在1 900~2 000 MPa·s之间,试件不同部位显微硬度值接近,匀质性好,结构密实。