纳米二氧化钛的光催化性能研究

采用TiOSO4常温水解法制备纳米二氧化钛，以甲基橙溶液做光催化降解实验，考察各种因素对光催化降解效果的影响。结果表明：加入表面活性剂方式制备的纳米TiO2具有更大的比表面积,光催化降解效果明显；甲基橙溶液的初始浓度越低,光催化降解效果越好；锐钛晶型96．5％、金红石晶型3．5％(质量比)的混晶型纳米TiO2具有更高的光催化活性；进行过多次光催化实验的纳米TiO2经再生后仍然可保持较高的光催化活性。     

陶瓷表面TiO_2薄膜的制备及光催化性能研究

采用化学溶胶-凝胶法制备TiO2溶胶,用浸渍-提拉方式在陶瓷表面制成锐钛矿相TiO2薄膜。用X射线衍射法(XRD)确定了晶型及晶粒的大小;用光电子能谱测定了其微观成分及其含量;考察了7种过渡金属离子掺杂后对甲基橙降解的光催化性能的影响及其变化规律,并对陶瓷和玻璃的光催化活性进行了比较。实验结果表明:掺杂Mn及Ni离子对于提高TiO2薄膜的光催化活性有明显的促进作用,降解30min后,降解率分别达到79.7%,80.8%。瓷片和玻璃的光催化活性要视掺杂的金属离子而定,不同的掺杂离子对瓷片和玻璃的光催化活性有不同的作用效果。     

纳米二氧化钛光催化活性影响因素的研究

以苯酚为模拟污染物,考察了不同晶型、溶液初始pH值、反应物初始浓度、氧气的协同作用对TiO2悬浮体系光催化活性的影响;并将TiO2负载到活性炭纤维上,制备了固定体系的TiO2/ACF复合催化剂.结果表明,具有混晶结构的P25降解速率比纯锐钛矿TiO2快;溶液pH=6及苯酚初始浓度为150 mg/L时,降解速度最快;通入氧气,可以提高催化剂活性;光催化降解苯酚表明,TiO2/ACF复合催化剂具有较好的光催化活性.     

不同气氛下TiO2纳米晶的光催化性能研究

以甲基橙的光催化降解为探针反应,从表观降解率和TOC去除率两个指标评价了纳米TiO2样品在不同焙烧温度和反应气氛下的光催化活性.结果表明,400℃焙烧的锐钛矿型TiO2纳米粒子的晶粒尺寸为11.69nm,在光催化降解甲基橙的实验中表现出最佳的光催化活性.光催化反应进行20min后对甲基橙的表现降解率达98.99%,反应进行30min后对甲基橙水溶液TOC的去除率为79.36%,TOC的去除效果滞后于色度的去除.不通空气时,样品对甲基橙的降解率最差,降解速率明显滞后于通空气和O2的情况,且通O2的降解效果更好.     

低温制备锐钛矿型TiO2溶胶的性能研究

采用溶胶-凝胶法,以水为溶剂,在低于70℃下直接合成纳米锐钛矿型TiO2溶胶,研究了反应温度、pH值对溶胶晶型、晶粒大小和稳定性的影响.以不同光照下对亚甲基蓝的降解,评价了溶胶的光催化活性.结果表明:较低pH值下溶胶中的TiO2出现了金红石相与锐钛矿相组成的混晶相,而pH值相对较高时则得到纯锐钛矿相TiO2;在紫外光、日光灯和太阳光下,与P25对亚甲基蓝的降解相比,同等条件下所制备的TiO2溶胶显示出更好的光催化活性;混晶相TiO2溶胶的光催化性优于纯锐钛矿相TiO2溶胶.     

Ce4+/TiO2溶胶对酸性藏青GGR的光催化降解

以钛酸四正丁酯为前驱体,采用溶胶-凝胶法常温制备稀土离子Ce4+掺杂的TiO2溶胶,用以光催化降解酸性藏青GGR,探究掺杂对TiO2溶胶光催化活性的影响.研究Ce4+掺杂量、pH、溶胶浓度和染料初始浓度对溶胶光催化活性的影响.结果表明:未掺杂TiO2溶胶粒径为29.7nm,随Ce4+掺杂量增加粒径逐渐降低至22.4nm,粒径的减小使得TiO2粒子比表面积加大,光催化活性提高.染料降解率随掺杂量增加而提高,当Ce4+的掺杂量超过1.0％时,降解率下降,说明过量的掺杂会抑制TiO2的光催化活性.溶胶pH会影响溶胶中TiO2晶型和带电情况,pH为1-2时溶胶光催化活性最高.溶胶浓度低光催化反应体系中TiO2受激发产生的电子和空穴少,染料降解率低.染料初始浓度高紫外光透过率小,光能利用率低,染料降解速度慢.当溶胶pH为1-2,溶胶浓度0.2mol·L-1,染料初始浓度59mg· L-1时,未掺杂TiO2溶胶对酸性藏青GGR的降解率为64.5％,摩尔掺杂比1.0％的Ce4+/TiO2对染料的降解率达90.2％.掺杂使TiO2的光催化活性提高了25.7％.     

TiO_2/HZSM-5的制备及光催化性能的表征

以钛酸四丁酯为钛源,采用溶胶-凝胶法在HZSM-5分子筛表面合成TiO2前驱体,程序升温处理制得TiO2/HZSM-5负载型光催化剂。采用X射线衍射、扫描电镜、傅里叶变换红外光谱、X射线光电子能谱对光催化剂晶相结构、表面形貌及化学组成进行了表征。结果表明,HZSM-5可提高TiO2分散性能,降低TiO2晶粒的尺寸。TiO2/HZSM-5中的Ti都以TiO2形式存在,没有Ti—O—Si键生成。甲基橙溶液的光催化降解结果表明,负载后提高了TiO2对甲基橙溶液的光催化降解活性。TiO2的质量分数为30%,400℃下煅烧2h时的催化剂光催化性能最好。     

陶瓷表面 TiO2薄膜的制备及光催化性能研究

采用化学溶胶-凝胶法制备TiO2溶胶，用浸渍-提拉方式在陶瓷表面制成锐钛矿相TiO2薄膜。用X射线衍射法(XRD)确定了晶型及晶粒的大小；用光电子能谱测定了其微观成分及其含量；考察了7种过渡金属离子掺杂后对甲基橙降解的光催化性能的影响及其变化规律，并对陶瓷和玻璃的光催化活性进行了比较。实验结果表明：掺杂Mn及Ni离子对于提高TiO2薄膜的光催化活性有明显的促进作用，降解30min后，降解率分别达到79．7％，80.8％。瓷片和玻璃的光催化活性要视掺杂的金属离子而定，不同的掺杂离子对瓷片和玻璃的光催化活性有不同的作用效果。     

热处理工艺对多孔TiO2薄膜光催化性能的影响

以十八胺为模板剂,采用溶胶-凝胶法在玻璃基体上制备了多孔TiO2薄膜,研究了热处理工艺对薄膜理化性质及光催化性能的影响。随煅烧温度和煅烧时间的增加,TiO2薄膜表面逐渐形成清晰的孔结构,晶粒尺寸增大。薄膜由锐钛矿型TiO2组成,Ti以Ti 4+的形式存在。制备的TiO2薄膜厚度在200nm左右,薄膜的UV-Vis透射率随煅烧温度的升高呈下降趋势,随煅烧时间的延长先下降而后又上升。多孔TiO2薄膜光催化降解甲基橙结果表明,随煅烧温度升高薄膜的光催化活性增加,在500℃煅烧2h制备的薄膜具有最佳的光催化活性。     

镧掺杂TiO2/膨润土复合光催化材料的制备及性能

以钠基膨润土为载体,钛酸丁酯和硝酸镧为原料,采用溶胶-凝胶法制备镧掺杂TiO2/膨润土复合光催化剂,采用X射线衍射(XRD)和红外光谱(IR)对复合催化剂进行了表征,在紫外光照射下,通过对TNT废水的光催化降解,考察其光催化活性。实验结果表明,掺杂镧与未掺杂镧的TiO2/膨润土复合光催化剂中TiO2主要以锐钛矿型存在;掺杂镧的TiO2/膨润土复合光催化剂的光催化性能明显优于未掺杂镧的TiO2/膨润土复合光催化剂,当镧的掺杂量为1%(原子分数),焙烧温度为500℃时,其光催化活性达到最佳效果。     

Ce-TiO2光催化剂的制备与性能研究

采用溶胶-凝胶法制备了稀土Ce离子掺杂的纳米TiO2光催化剂(Ce-TiO2),通过XRD、FT-IR、UV-Vis、PL、Nano-sizer纳米粒度分析仪等对Ce-TiO2样品进行了表征和分析,并以亚甲基蓝(MB)作为目标降解物,考察了不同掺杂浓度及经不同温度热处理后的Ce-TiO2样品对MB的光催化降解效果,结果表明所制备样品的晶型均为锐钛矿相和金红石相的混晶相,Ce离子的掺杂拓展了TiO2在可见光区的光谱响应范围,提高了TiO2光催化活性。当pH值为1.5,Ce的掺杂量为n(Ce)∶n(TiO2)=1∶300,热处理温度为600℃条件下制备的样品其催化活性显著高于Degussa P25。     

Characterization of the hydrothermally synthesized nano-TiO2 crystallite and the photocatalytic degradation of Rhodamine B

Pure anatase-TiO2 nanoparticles with 8 nm average crystallite size was synthesized hydrothermally at 200 degrees C in 2 h. The structural and physico-chemical properties of nano-TiO2 were determined by powder XRD, FT-IR, BET and SEM analyses. The behavior of anatase nano-TiO2 in catalytic degradation of Rhodamine B (RB) dye in transparent nano-TiO2 sol under UV-light was examined as a function of irradiation power of UV-light, irradiation time, amount of nano-TiO2 and initial RB concentration in the sol. Rhodamine B was fully degraded with the catalysis of the nano-TiO2 in a short time as low as 60 min. Photocatalytic activity of the nano-TiO2 for degradation of RB was compared with Degussa P-25 at optimum catalysis conditions determined for the nano-TiO2. It was found that, when compared to Degussa P-25, the nano-TiO2 could be repeatedly used with increasing photocatalytic activity. It was found that the photodegradation obeys the pseudo first-order reaction kinetics with the rate constant of 0.0658 min(-1), and the half period t1/2 was 10.53 min.     

PEO改性纳米TiO2/LDPE复合薄膜的光降解性能

以聚氧乙烯(PEO)改性纳米TiO2颗粒作为光催化剂,与低密度聚乙烯(LDPE)树脂复合制备了一种新型可光催化降解的TiO2/LDPE纳米复合薄膜,进行了该薄膜在空气中紫外光照下的光催化降解实验。通过表面接触角、失重率、红外光谱(FT-IR)和扫描电镜(SEM)等分析技术系统地研究了该复合薄膜的降解性能。结果表明,PEO的加入能提高薄膜的亲水性和TiO2的分散性,提高TiO2的光催化活性,有利于促进LDPE薄膜的降解。TiO2/PEO/LDPE复合薄膜在0.8mW/cm2紫外光强下照射425h,失重率达到15.2%;在4mW/cm2紫外光强下照射500h,失重率达到38.1%。光照后薄膜的拉伸强度和断裂伸长率显著降低,羰基指数升高。     

掺铁二氧化钛薄膜的自组装制备和光催化性能研究

以TiCl4为钛源,SAMs为模板,Fe（NO3）3·9H2O为铁源,采用自组装方法于低温液相反应体系中分别成功地制备出大面积二维结构纳米的纯净和掺铁Ⅱ0：薄膜,通过拉曼光谱、高分辨透射电镜、荧光发射光谱等方法对样品进行表征,研究紫外光和可见光下纳米薄膜对甲基橙溶液的光催化降解过程以及紫外光下对甲苯的降解效率,探讨了掺铁后对TiO2：的光催化活性的影响,结果表明,此方法不需要高温煅烧即可得到高催化活性的以金红石为主的掺铁二氧化钛纳米薄膜。     

Preparation of re-usable photocatalytic filter for degradation of Malachite Green dye under UV and vis-irradiation

Sn(4+) doped and undoped nano-TiO(2) particles easily dispersed in water were synthesized without using organic solvent by hydrothermal process. Nanostructure-TiO(2) based thin films were prepared on flyswatter substrate, made with stainless steel, by dip-coating technique. The structure, surface and optical properties of the particles and thin films were characterized by element analysis and XRD, BET, SEM and UV/vis/NIR techniques. The photocatalytic performance of the films were tested for degradation of Malachite Green dye in solution under UV and vis-lights. The results showed that the coated flyswatter has a very high photocatalytic performance for the photodegradation of Malachite Green irradiated with UV and vis-lights. The results also proved that the hydrothermally synthesized nano-TiO(2) particles are fully anatase crystalline form and are easily dispersed in water, the coated surfaces are hydrophilic, and the doping of transition metal ion efficiently improved the degradation performance of TiO(2)-coated flyswatter. The photocatalytic performances determined at both irradiation conditions were very good and were almost similar to each other for Sn(4+) doped TiO(2)-coated flyswatter and it can be repeatedly used with increasing photocatalytic activity compared to undoped TiO(2)-coated flyswatter.     

Effect of deposition of Ag on TiO2 nanoparticles on the photodegradation of Reactive Yellow-17

Nanoparticles of TiO(2) were synthesized by sol-gel technique and the photodeposition of about 1% Ag on TiO(2) particles was carried out. Ag-deposited TiO(2) catalyst was characterised by XRD, TEM and UV-vis spectroscopy. The Ag-TiO(2) catalyst was evaluated for their photocatalytic activity towards the degradation of Reactive Yellow-17 (RY-17) under UV and visible light irradiations. Then the results were compared with synthesized nano-TiO(2) sol and P-25 Degussa and the enhanced degradation was obtained with Ag-deposited TiO(2). This enhanced activity of Ag-TiO(2) may be attributed to the trapping of conduction band electrons. The effect of initial dye concentration, pH and electron acceptors such as H(2)O(2), K(2)S(2)O(8) on the photocatalytic activity were studied and the results obtained were fitted with Langmuir-Hinshelwood model to study the degradation kinetics and discussed in detail.     

Pt／TiO2纳米粒子的制备及其光催化性能研究

采用溶胶-凝胶法制备了掺杂Pt的TiO2粉末，利用紫外可见光谱对粉末的光吸收性能进行了表征，并分别在模拟日光和可见光下考察了其光催化氧化对．硝基苯酚的活性。结果表明，掺杂Pt以后TiO2粉末的光谱吸收范围被拓展至可见光，光催化活性也明显提高。在模拟日光照射下，以光催化活性较好的Pt／TiO2粉末为催化剂降解对．硝基苯酚，4h后对-硝基苯酚的转化率为93．7％，其反应是一级反应。     

微波辅助制备掺铁纳米TiO2溶胶及其性能研究

为了进一步提高纳米二氧化钛溶胶的光催化活性,采用微波辅助胶溶的方法制备了不同铁掺杂量的纳米二氧化钛(Fe-TiO2)溶胶,并以偶氮染料活性艳红X-3B为目标物,分别考察不同铁掺杂量对纳米Fe-TiO2溶胶光催化活性的影响,研究表明原子数分数为0.05%的Fe3+掺杂量最佳;对Fe-TiO2溶胶、TiO2溶胶及P25(Degussa纳米TiO2)悬浮液的光催化活性进行对比,结果表明:TiO2溶胶与P25悬浮液光催化活性相当,而Fe-TiO2溶胶较前两者具有更高的光催化活性.采用XRD、DLS、AFM和DRS的分析方法对溶胶进行表征,结果表明:微量铁掺杂对纳米TiO2的晶型及粒径分布无显著影响;但铁掺杂可以使纳米TiO2对紫外光的吸收有较大程度的增强,同时吸收边带发生了较明显的红移.铁掺杂对于提高纳米TiO2溶胶的光催化活性和拓展其光吸收范围均具有显著的积极的作用.     

TiO2/活性炭复合体超临界沉淀法制备及其光催化性能

以活性炭为载体、超临界二氧化碳为流体、钛酸丁酯为前驱体,用超临界流体沉积法制备TiO2/活性炭（TiO2/AC）复合体。用X射线衍射（XRD）、扫描电镜（SEM）、比表面积分析（BET）、热重-差热（TG-DTA）对TiO2/AC进行表征。以紫外灯为光源,偶氮类染料亚甲基蓝为标准降解物,考察TiO2/AC复合体的光催化...     

Photocatalytic degradation of azo dyes using Au:TiO2, gamma-Fe2O3:TiO2 functional nanosystems

We report photocatalytic degradation studies on Navy Blue HE2R (NB) dye on significant details as a representative from the class of azo dyes using functional nanosystems specifically designed to allow a strong photocatalytic activity. A modified sol-gel route was employed to synthesize Au and gamma-Fe2O3 modified TiO2 nanoparticles (NPs) at low temperature. The attachment strategy is better because it allows clear surface of TiO2 to remain open for photo-catalysis. X-ray diffraction, Raman and UV-VIS spectroscopy studies showed the presence of gold and iron oxide phases along-with the anatase TiO2 phase. TEM studies showed TiO2 nanocomposite particles of size approximately 10-12 nm. A detailed investigation on heterogeneous photocatalytic performance for Navy Blue HE2R dye was done using the as-synthesized catalysts Au:TiO2 and gamma-Fe2O3:TiO2 in aqueous suspension under 8 W low-pressure mercury vapour lamp irradiation. Also, the photocatalytic degradation of Amranth and Orange G azo dyes were studied. The surface modified TiO2 NPs showed significantly improved photocatalytic activity as compared to pure TiO2. Exposure of the dye to the UV light in the presence of pure and gold NPs attached TiO2 catalysts caused dye degradation of about approximately 20% and approximately 80%, respectively, in the first couple of hours. In the presence of gamma-Fe2O3 NPs attached TiO2, a remarkable approximately 95% degradation of the azo dye was observed only in the first 15 min of UV exposure. The process parameters for the optimum catalytic activity are established which lead to a complete decoloration and substantial dye degradation, supported by the values of the Chemical Oxygen Demand (COD) approximately 93% and Total Organic Carbon (TOC) approximately 65% of the treated dye solution after 5 hours on the employment of the UV/Au:TiO2/H2O2 photocatalytic process.