Effects of Cooling Rate on Thermoelectric Properties of <Emphasis Type="Italic">n</Emphasis>-Type Bi<Subscript>2</Subscript>(Se<Subscript>0.4</Subscript>Te<Subscript>0.6</Subscript>)<Subscript>3</Subscript> Compounds

A series of Bi₂(Se_0.4Te_0.6)₃ compounds were synthesized by a rapid route of melt spinning (MS) combined with a subsequent spark plasma sintering (SPS) process. Measurements of the Seebeck coefficient, electrical conductivity, and thermal conductivity were performed over the temperature range from 300 K to 520 K. The measurement results showed that the cooling rate of melt spinning had a significant impact on the transport properties of electrons and phonons, effectively enhancing the thermoelectric properties of the compounds. The maximum ZT value reached 0.93 at 460 K for the sample prepared with the highest cooling rate, and infrared spectrum measurement results showed that the compound with lower tellurium content, Bi₂(Se_0.4Te_0.6)₃, possesses a larger optical forbidden gap (E _g) compared with the traditional n-type zone-melted material with formula Bi₂(Se_0.07Te_0.93)₃. Our work provides a new approach to develop low-tellurium-bearing Bi₂Te₃-based compounds with good thermoelectric performance.     

Effects of SiC Nanodispersion on the Thermoelectric Properties of <Emphasis Type="Italic">p</Emphasis>-Type and <Emphasis Type="Italic">n</Emphasis>-Type Bi<Subscript>2</Subscript>Te<Subscript>3</Subscript>-Based Alloys

Polycrystalline p-type Bi_0.5Sb_1.5Te₃ and n-type Bi₂Te_2.7Se_0.3 thermoelectric (TE) alloys containing a small amount (vol.% ≤5) of SiC nanoparticles were fabricated by mechanical alloying and spark plasma sintering. It was revealed that the effects of SiC addition on TE properties can be different between p-type and n-type Bi₂Te₃-based alloys. SiC addition slightly increased the power factor of the p-type materials by decreasing both the electrical resistivity (ρ) and Seebeck coefficient (α), but decreased the power factor of n-type materials by increasing both ρ and α. Regardless of the conductivity type, the thermal conductivity was reduced by dispersing SiC nanoparticles in the Bi₂Te₃-based alloy matrix. As a result, a small amount (0.1 vol.%) of SiC addition increased the maximum dimensionless figure of merit (ZT _max) of the p-type Bi_0.5Sb_1.5Te₃ alloys from 0.88 for the SiC-free sample to 0.97 at 323 K, though no improvement in TE performance was obtained in the case of n-type Bi₂Te_2.7Se_0.3 alloys. Importantly, the SiC-dispersed alloys showed better mechanical properties, which can improve material machinability and device reliability.     

Bi<Subscript>2</Subscript>Te<Subscript>3</Subscript>-Sb<Subscript>2</Subscript>Te<Subscript>3</Subscript> Superlattices Grown by Nanoalloying

In this work, Bi₂Te₃-Sb₂Te₃ superlattices were prepared by the nanoalloying approach. Very thin layers of Bi, Sb, and Te were deposited on cold substrates, rebuilding the crystal structure of V₂VI₃ compounds. Nanoalloyed super- lattices consisting of alternating Bi₂Te₃ and Sb₂Te₃ layers were grown with a thickness of 9 nm for the individual layers. The as-grown layers were annealed under different conditions to optimize the thermoelectric parameters. The obtained layers were investigated in their as-grown and annealed states using x-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive x-ray (EDX) spectroscopy, transmission electron microscopy (TEM), and electrical measurements. A lower limit of the elemental layer thickness was found to have c-orientation. Pure nanoalloyed Sb₂Te₃ layers were p-type as expected; however, it was impossible to synthesize p-type Bi₂Te₃ layers. Hence the Bi₂Te₃-Sb₂Te₃ superlattices consisting of alternating n- and p-type layers showed poor thermoelectric properties.     

Beneficial Effect of S-Filling on Thermoelectric Properties of S<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>Co<Subscript>4</Subscript>Sb<Subscript>11.2</Subscript>Te<Subscript>0.8</Subscript> Skutterudite

In this work, Te-doped and S-filled S _x Co₄Sb_11.2Te_0.8 (x = 0.1, 0.15, 0.2, 0.25, 0.3, 0.4) skutterudite compounds have been prepared using solid state reaction and spark plasma sintering. Thermoelectric measurements of the consolidated samples were examined in a temperature range of 300–850 K, and the influences of S-addition on the thermoelectric properties of S _x Co₄Sb_11.2Te_0.8 skutterudites are systematically investigated. The results indicate that the addition of sulfur and tellurium is effective in reducing lattice thermal conductivity due to the point-defect scattering caused by tellurium substitutions and the cluster vibration brought by S-filling. The solubility of tellurium in skutterudites is enhanced with sulfur addition via charge compensation. The thermal conductivity decreases with increasing sulfur content. The highest figure of merit, ZT = 1.5, was obtained at 850 K for S_0.3Co₄Sb_11.2Te_0.8 sample, because of the low lattice thermal conductivity.     

Preparation and Thermoelectric Properties of Nanoporous Bi<Subscript>2</Subscript>Te<Subscript>3</Subscript>-Based Alloys

n-Type nanoporous Bi₂Te₃-based thermoelectric materials with different porosity ratios have been prepared by spark plasma sintering (SPS). The microstructure and phase morphology have been analyzed by x-ray diffraction (XRD) and field-emission scanning electron microscopy (FESEM), and the thermoelectric properties of the SPS samples have been measured. Experimental results show that the nanoporous structures lying in the sheet layers and among the plate grains of the Bi₂Te₃ bulk material can lead to an increase in the Seebeck coefficient and a decrease in the thermal conductivity, thus leading to an enhanced figure of merit.     

Improvement of Thermoelectric Power Factor of Hydrothermally Prepared Bi<Subscript>0.5</Subscript>Sb<Subscript>1.5</Subscript>Te<Subscript>3</Subscript> Compared with its Solvothermally Prepared Counterpart

We report on the successful hydrothermal synthesis of Bi_0.5Sb_1.5Te₃, using water as the solvent. The products of the hydrothermally prepared Bi_0.5 Sb_1.5Te₃ were hexagonal platelets with edges of 200–1500 nm and thicknesses of 30–50 nm. Both the Seebeck coefficient and electrical conductivity of the hydrothermally prepared Bi_0.5Sb_1.5Te₃ were larger than those of the solvothermally prepared counterpart. Hall measurements of Bi_0.5Sb_1.5Te₃ at room temperature indicated that the charge carrier was p-type, with a carrier concentration of 9.47 × 10¹⁸ cm⁻³ and 1.42 × 10¹⁹ cm⁻³ for the hydrothermally prepared Bi_0.5Sb_1.5Te₃ and solvothermally prepared sample, respectively. The thermoelectric power factor at 290 K was 10.4 μW/cm K² and 2.9 μW/cm K² for the hydrothermally prepared Bi_0.5Sb_1.5Te₃ and solvothermally prepared sample, respectively.     

Influence of Nanoinclusions on Thermoelectric Properties of <Emphasis Type="Italic">n</Emphasis>-Type Bi<Subscript>2</Subscript>Te<Subscript>3</Subscript> Nanocomposites

n-Type Bi₂Te₃ nanocomposites with enhanced figure of merit, ZT, were fabricated by a simple, high-throughput method of mixing nanostructured Bi₂Te₃ particles obtained through melt spinning with micron-sized particles. Moderately high power factors were retained, while the thermal conductivity of the nanocomposites was found to decrease with increasing weight percent of nanoinclusions. The peak ZT values for all the nanocomposites were above 1.1, and the maximum shifted to higher temperature with increasing amount of nanoinclusions. A maximum ZT of 1.18 at 42°C was obtained for the 10 wt.% nanocomposite, which is a 43% increase over the bulk sample at the same temperature. This is the highest ZT reported for n-type Bi₂Te₃ binary material, and higher ZT values are expected if state-of-the-art Bi₂Te_3−x Se _x materials are used.     

Point Defect Engineering of High‐Performance Bismuth‐Telluride‐Based Thermoelectric Materials

Developing high‐performance thermoelectric materials is one of the crucial aspects for direct thermal‐to‐electric energy conversion. Herein, atomic scale point defect engineering is introduced as a new strategy to simultaneously optimize the electrical properties and lattice thermal conductivity of thermoelectric materials, and (Bi,Sb)₂(Te,Se)₃ thermoelectric solid solutions are selected as a paradigm to demonstrate the applicability of this new approach. Intrinsic point defects play an important role in enhancing the thermoelectric properties. Antisite defects and donor‐like effects are engineered in this system by tuning the formation energy of point defects and hot deformation. As a result, a record value of the figure of merit ZT of ≈1.2 at 445 K is obtained for n‐type polycrystalline Bi₂Te_2.3Se_0.7 alloys, and a high ZT value of ≈1.3 at 380 K is achieved for p‐type polycrystalline Bi_0.3Sb_1.7Te₃ alloys, both values being higher than those of commercial zone‐melted ingots. These results demonstrate the promise of point defect engineering as a new strategy to optimize thermoelectric properties.     

Effect of Deformation Temperature on Texture and Thermoelectric Properties of Bi<Subscript>0.5</Subscript>Sb<Subscript>1.5</Subscript>Te<Subscript>3</Subscript> Prepared by Hot-Press Deformation

The effects of deformation temperature on texture and thermoelectric properties of p-type Bi_0.5Sb_1.5Te₃ sintered materials were investigated. The sintered materials were prepared by mechanical alloying and hot-press sintering. The hot-press deformation was performed at 723 K and 823 K by applying mechanical pressure in a graphite die. Then, the materials were extruded in the direction opposite to the direction of applied pressure. X-ray diffraction and electron backscattered diffraction patterns showed that the hexagonal c-plane tended to align along the extruded direction when the samples were deformed at high temperatures. The thermoelectric power factor was increased by high-temperature hot-press deformation because of the low electrical resistivity that originated from the c-plane orientation.     

Low-Temperature Thermoelectric Properties of Co<Subscript>0.9</Subscript>Fe<Subscript>0.1</Subscript>Sb<Subscript>3</Subscript>-Based Skutterudite Nanocomposites with FeSb<Subscript>2</Subscript> Nanoinclusions

Bulk thermoelectric nanocomposite materials have great potential to exhibit higher ZT due to effects arising from their nanostructure. Herein, we report low-temperature thermoelectric properties of Co_0.9Fe_0.1Sb₃-based skutterudite nanocomposites containing FeSb₂ nanoinclusions. These nanocomposites can be easily synthesized by melting and rapid water quenching. The nanoscale FeSb₂ precipitates are well dispersed in the skutterudite matrix and reduce the lattice thermal conductivity due to additional phonon scattering from nanoscopic interfaces. Moreover, the nanocomposite samples also exhibit enhanced Seebeck coefficients relative to regular iron-substituted skutterudite samples. As a result, our best nanocomposite sample boasts a ZT = 0.041 at 300 K, which is nearly three times as large as that for Co_0.9Fe_0.1Sb₃ previously reported.     

Electrical and Thermal Conductivity and Conduction Mechanism of Ge<Subscript>2</Subscript>Sb<Subscript>2</Subscript>Te<Subscript>5</Subscript> Alloy

Ge₂Sb₂Te₅ alloy has drawn much attention due to its application in phase-change random-access memory and potential as a thermoelectric material. Electrical and thermal conductivity are important material properties in both applications. The aim of this work is to investigate the temperature dependence of the electrical and thermal conductivity of Ge₂Sb₂Te₅ alloy and discuss the thermal conduction mechanism. The electrical resistivity and thermal conductivity of Ge₂Sb₂Te₅ alloy were measured from room temperature to 823 K by four-terminal and hot-strip method, respectively. With increasing temperature, the electrical resistivity increased while the thermal conductivity first decreased up to about 600 K then increased. The electronic component of the thermal conductivity was calculated from the Wiedemann–Franz law using the resistivity results. At room temperature, Ge₂Sb₂Te₅ alloy has large electronic thermal conductivity and low lattice thermal conductivity. Bipolar diffusion contributes more to the thermal conductivity with increasing temperature. The special crystallographic structure of Ge₂Sb₂Te₅ alloy accounts for the thermal conduction mechanism.     

Thermoelectric Properties of Cu-doped Bi<Subscript>0.4</Subscript>Sb<Subscript>1.6</Subscript>Te<Subscript>3</Subscript> Prepared by Hot Extrusion

Cu_0.003Bi_0.4Sb_1.6Te₃ alloys were prepared by using encapsulated melting and hot extrusion (HE). The hot-extruded specimens had the relative average density of 98%. The (00l) planes were preferentially oriented parallel to the extrusion direction, but the specimens showed low crystallographic anisotropy with low orientation factors. The specimens were hot-extruded at 698 K, and they showed excellent mechanical properties with a Vickers hardness of 76 Hv and a bending strength of 59 MPa. However, as the HE temperature increased, the mechanical properties degraded due to grain growth. The hot-extruded specimens showed positive Seebeck coefficients, indicating that the specimens have p-type conduction. These specimens exhibited negative temperature dependences of electrical conductivity, and thus behaved as degenerate semiconductors. The Seebeck coefficient reached the maximum value at 373 K and then decreased with increasing temperature due to intrinsic conduction. Cu-doped specimens exhibited high power factors due to relatively higher electrical conductivities and Seebeck coefficients than those of undoped specimens. A thermal conductivity of 1.00 Wm^?1 K^?1 was obtained at 373 K for Cu_0.003Bi_0.4Sb_1.6Te₃ hot-extruded at 723 K. A maximum dimensionless figure of merit, ZT _max = 1.05, and an average dimensionless figure of merit, ZT _ave = 0.98, were achieved at 373 K.     

Thermoelectric Properties of Mo<Subscript>3</Subscript>Sb<Subscript>5.4</Subscript>Te<Subscript>1.6</Subscript> and Ni<Subscript>0.06</Subscript>Mo<Subscript>3</Subscript>Sb<Subscript>5.4</Subscript>Te<Subscript>1.6</Subscript>

Mo₃Sb₇, crystallizing in the Ir₃Ge₇ type structure, has poor thermoelectric (TE) properties due to its metallic behavior. However, by a partial Sb-Te exchange, it becomes semiconducting without noticeable structure changes and so achieves a significant enhancement in the thermopower with the composition of Mo₃Sb₅Te₂. Meanwhile, large cubic voids in the Mo₃Sb₅Te₂ crystal structure provide the possibility of filling the voids with small cations to decrease the thermal conductivity by the so-called rattling effect. As part of the effort to verify this idea, we report herein the growth as well as measurements of the thermal and electrical transport properties of Mo₃Sb_5.4Te_1.6 and Ni_0.06Mo₃Sb_5.4Te_1.6.     

Thermoelectric Properties of the Pseudobinary Alloy (Ag<Subscript>0.365</Subscript>Sb<Subscript>0.558</Subscript>Te)<Subscript>0.975</Subscript>(GeTe)<Subscript>0.025</Subscript> Prepared by Spark Plasma Sintering

Ag-Sb-Te-Ge-based alloys have received great attention in recent years. In the present work we prepared the pseudobinary alloy (Ag_0.365Sb_0.558Te)_0.975 (GeTe)_0.025 using spark plasma sintering and evaluated its thermoelectric (TE) properties over the temperature range from 318 K to 551 K. Rietveld analysis revealed that about 1.3 at.% Ge atoms occupy the Sb sites and that the alloy exhibits the same crystal structure as AgSbTe₂. By using back-scattered electron imaging, we observed two instead of one phase in the sample. The small white AgSbTe₂ chunks embedded in the matrix can substantially scatter phonons. Compared with the transport properties of Ag_0.365Sb_0.558Te, we obtained a slightly increased Seebeck coefficient and reduced thermal conductivity without sacrificing electrical conductivity. The highest TE figure of merit, ZT, was 0.69 at 551 K, whereas that of the ternary alloy Ag_0.365Sb_0.558Te was 0.61 at the corresponding temperature, suggesting that (Ag_0.365Sb_0.558Te)_0.975(GeTe)_0.025 has the potential to improve TE performance with optimization of its chemical composition.     

Influence of Element Substitution on Corrosion Behavior of Bi<Subscript>2</Subscript>Te<Subscript>3</Subscript>-Based Compounds

Atmospheric water may condense on the surface of Bi₂Te₃-based compounds constituting the Peltier module, depending on the operating environment used. In the stage of disposal, Bi₂Te₃-based compounds may come into contact with water in waste disposal sites. There are very few publications about the influence of condensed water on Peltier modules. Bi₂Te₃-Sb₂Te₃ or Bi₂Te₃-Bi₂Se₃ pseudo binary system compounds are used as p-type material or n-type material, respectively. The lattice distortion will be induced in the crystal of Bi₂Te₃-based compounds by element substitution due to the reduction in their thermal conductivity. However, the influence of element substitution on the corrosion behavior of Bi₂Te₃-based compounds remains unclear. In this study, the influence of element substitution on the corrosion behavior of Bi₂Te₃-based compounds with practical compositions has been investigated. Bi_0.5Sb_1.5Te₃ or Bi₂Te_2.85Se_0.15 was prepared by the vertical Bridgman method. The electrochemical properties at room temperature were evaluated by cyclic voltammetry in a standard three-electrode cell. The working electrolyte was a naturally aerated 0.6 or 3.0 mass% NaCl solution. From the tendency for corrosion potential for all the samples, the corrosion sensitivity of ternary compounds was slightly higher than that of binary compounds. From the trend of current density, it was found that Bi_0.5Sb_1.5Te₃ had a corrosion resistance intermediate between Bi₂Te₃ and Sb₂Te₃. On the other hand, corrosion resistance was affected despite a small amount of Se substitution, and the corrosion resistance of Bi₂Te_2.85Se_0.15 was close to or lower than that of Bi₂Se₃. From the observation results of the corrosion products, the trends of morphology and composition of corrosion products for Bi_0.5Sb_1.5Te₃ or Bi₂Te_2.85Se_0.15 were consistent with those of Sb₂Te₃ or Bi₂Se₃, respectively. From the results of x-ray photoelectron spectroscopy for the electrolyte after testing, the possibility that a corrosion product diffuses to the environment including the salt was suggested in Bi_0.5Sb_1.5Te₃. However, the amount of dissolved corrosion product was very low, and the chemical stability of the corrosion product was not changed or improved by element substitution.     

Synthesis and Thermoelectric Properties of the Double-Filled Skutterudite Yb<Subscript>0.2</Subscript>In<Subscript><Emphasis Type="Italic">y</Emphasis></Subscript>Co<Subscript>4</Subscript>Sb<Subscript>12</Subscript>

Filled skutterudites have long been singled out as one of the prime examples of phonon glass electron crystal materials. Recently the double-filling approach in these materials has been attracting increased attention. In this study, Yb_0.2In _y Co₄Sb₁₂ (y = 0.0 to 0.2) samples have been prepared by a simple melting method and their thermoelectric properties have been investigated. The power factor is increased dramatically when increasing the In content, while the lattice thermal conductivity is lowered considerably, leading to a large increase of the ZT value. A state-of-the-art ZT value of 1.0 is attained in Yb_0.2In_0.2Co₄Sb₁₂ at 750 K.     

Thermoelectric properties of Bi<Subscript>0.5</Subscript>Sb<Subscript>1.5</Subscript>Te<Subscript>3</Subscript> ribbons prepared by melt spinning

The results of studying the thermoelectric properties of p-type Bi_0.5Sb_1.5Te₃ alloy samples prepared by melt spinning quenching are presented. The material after melt spinning is shaped as thin ribbons and has a quasi-amorphous structure. The thermoelectric properties (thermoelectric power and electrical resistance) and crystallization processes of as-prepared melt-spun ribbons are studied at 300–800 K for the first time. The stability range of the initial state, the crystallization-onset temperature, and the effect of thermal annealing on the thermoelectric-power factor of the alloy are determined.     

Crystal Structure and High-Temperature Thermoelectric Properties of the Mo<Subscript>3−<Emphasis Type="Italic">x</Emphasis></Subscript>Ru<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>Sb<Subscript>7</Subscript> Compounds

Zintl phases are currently receiving great attention for their thermoelectric potential typified by the discovery of a high ZT value in Yb₁₄MnSb₁₁-based compounds. Herein, we report on the crystallographic characterization via neutron and x-ray diffraction experiments, and on the thermoelectric properties measured in the 300 K to 1000 K temperature range, of Mo₃Sb₇ and its isostructural compounds Mo_3−x Ru _x Sb₇. Even though Mo₃Sb₇ displays rather high ZT values given its metallic character, the partial substitution of Mo by Ru substantially improves its thermoelectric properties, resulting in a ZT value of ∼0.45 at 1000 K for x = 0.8.     

Enhancing the Thermoelectric Properties of p-Type Bulk Bi-Sb-Te Nanocomposites via Solution-Based Metal Nanoparticle Decoration

Embedding nanosized particles in bulk thermoelectric materials is expected to lower the lattice thermal conductivity by enhancing the degree of interface phonon scattering, thus improving their thermoelectric figure of merit ZT. We have developed a wet chemical process to fabricate Bi_0.5Sb_1.5Te₃-based thermoelectric nanocomposites which include nanometer-sized metal particles. By simple solution mixing of metal acetate precursors and Bi_0.5Sb_1.5Te₃ powders in ethyl acetate as a medium for homogeneous incorporation, it is possible to apply various types of metal nanoparticles onto the surfaces of the thermoelectric powders. Next, bulk Bi_0.5Sb_1.5Te₃ nanocomposites with homogeneously dispersed metal nanoparticles were fabricated using a spark plasma sintering technique. The lattice thermal conductivities were reduced by increasing the long-wavelength phonon scattering in the presence of metal nanoparticles, while the Seebeck coefficients increased for a few selected metal-decorated nanocomposites, possibly due to the carrier-energy-filtering effect. Finally, the figure of merit ZT was enhanced to 1.4 near room temperature. This approach highlights the feasibility of incorporating various types of nanoparticles into an alloy matrix starting by wet chemical routes, which is an effective means of improving the thermoelectric performance of Bi-Te-based alloys.     

Microstructures and Thermoelectric Properties of an Annealed Ti<Subscript>0.5</Subscript>(Hf<Subscript>0.5</Subscript>Zr<Subscript>0.5</Subscript>)<Subscript>0.5</Subscript>NiSn<Subscript>0.998</Subscript>Sb<Subscript>0.002</Subscript> Ribbon

The thermoelectric half-Heusler compound Ti_0.5(Hf_0.5Zr_0.5)_0.5NiSn_0.998Sb_0.002 was fabricated by spin-casting and subsequent annealing. ZT at room temperature increased with annealing time through an increase in absolute Seebeck coefficients despite a decrease in electrical conductivity. ZT reached 0.10 after annealing at 1050 K for 48 h. In powder x-ray diffraction analysis, each half-Heusler peak was accompanied by a bump at the high-angle side, corresponding to a minor Ti-rich half-Heusler phase. The quantity and Ti composition of the minor phase increased with annealing time, although those of the major half-Heusler phase were almost constant. In transmission electron microscopic analysis, granular domains, several nanometers in size, with atomic ordering or disordering were observed. Thermoelectric properties were␣improved by annealing through the growth of heterogeneous microstructures of the Ti-rich and Ti-poor half-Heusler grains and of the granular domains.