核壳型碳铁纳米粉体的制备及磁性能研究

采用直流碳弧法制备碳包铁纳米粒子,用透射电子显微镜(TEM)、X射线衍射仪(XRD)对产物的形貌和尺寸、物相结构组成进行分析,并在真空和氮气气氛下在200～800℃对制备的碳包铁纳米粒子进行热处理,用振动样品磁强计测量处理前后的碳包铁纳米粒子的剩磁强度、矫顽力和饱和磁化强度.结果表明,碳包铁纳米粒子的磁滞回线显示出较好的超顺磁特性;剩磁强度、矫顽力和饱和磁化强度随着粉体中铁含量的增加而增大.对碳包铁纳米粒子进行热处理,其磁性能随温度的升高首先改善,温度进一步升高又逐步劣化.在450℃退火,粉体磁性能最佳.     

纳米碳包铁磁性颗粒的制备及表征

采用激光感应复合加热蒸发合成法,以CH4为碳源,制备了大量具有壳核结构的纳米碳包铁颗粒,通过透射电子显微镜(TEM)、X射线衍射分析仪(XRD)、能量弥散X射线分析(EDX)等对颗粒进行了表征,并利用动态磁滞回线测定仪测定了纳米颗粒的磁化强度等磁性能.结果表明,利用该方法制备的碳包铁纳米颗粒的平均粒径为25nm,表面碳层厚度为5nm左右,具有铁磁性能.纳米碳包铁颗粒将作为磁性载体在医学细胞分离、细胞染色、靶向用药、定向治疗、肿瘤热疗等方面具有广阔的应用前景.     

碳包铜纳米颗粒的制备及其性能研究

采用碳弧法制备出碳包铜纳米粒子,并用透射电子显微镜(TEM)、X射线衍射仪(XRD)和DSC对产物的形貌、尺寸、物相结构组成以及抗氧化性能进行了表征分析,同时对碳包铜纳米粒子的导电性能进行了测量.测试结果表明碳包铜纳米粒子为核壳型结构,内部为金属铜核,外部为碳层.在铜核的周围碳以类石墨状形式存在,离铜核较远处碳以非晶态...     

直流碳弧法制备碳包覆铁纳米颗粒机理研究

采用直流碳弧等离子体法成功制备了碳包覆铁纳米颗粒,利用透射电子显微镜和高分辨透射电子显微镜、X射线衍射、X射线能谱仪对样品的形貌、物相结构、化学成分和粒度进行表征分析,并对碳包覆纳米金属颗粒的形成机理进行初步探讨。结果表明:直流碳弧等离子体技术制备的碳包覆纳米金属颗粒具有明显的铁核(bcc-Fe)/碳壳(石墨层片)包覆结构,颗粒大多呈球形和椭球形,粒径分布在20~60nm范围,平均粒径为44nm,铁粒子外碳层的厚度为5~8nm。碳包覆铁纳米铁颗粒是通过颗粒内部固态形式的碳自行扩散至颗粒表面和颗粒外部气态形式的碳沉积到颗粒表面形成的。     

石墨包覆铁纳米粒子的结构及生长机制

用金属钾还原2阶FeCl3石墨层间化合物(FeCl3-GICs)前驱体制备了石墨包覆纳米α-Fe.X射线衍射(XRD)、X射线能量色散谱(EDX)分析表明所制备样品由石墨、α-Fe和少量KCl组成,透射电镜(TEM)观察发现样品中的α-Fe为纳米粒子,嵌入在石墨结构层间,含量丰富.高分辨透射电镜(HRTEM)观察证实α-Fe纳米粒子由多晶组成,呈二维或准二维形态,α-Fe纳米晶的空间取向严格受石墨结构层控制.在实验基础上提出了一种石墨包覆纳米α-Fe的可能生长机制.     

氧化硅包覆铁“壳/核”型纳米复合粒子的制备及其吸波特性研究

采用非平衡物理气相蒸发法在氢气氩气混合气氛下制备了氧化硅包覆铁“壳/核”型纳米复合粒子. 通过X射线衍射(XRD)、透射电子显微镜(TEM)和能谱分析(EDS)等方法表征了纳米复合粒子的相组分、结构以及颗粒形貌. 结果表明,制备的氧化硅包覆铁纳米复合粒子的尺寸在50nm左右,在铁纳米粒子的表面还出现了非晶态的氧化硅纳米棒,长度为150~200nm. 利用电磁参数模拟微波吸收特性得出,涂层厚度为1.79mm时,在15.4GHz频率处达到最小反射损耗值为-14.5dB,反射损耗在8~18GHz的频段低于-10dB,且损耗机制为自然共振.     

电纺Co掺杂碳纳米纤维的制备及其吸波性能

采用静电纺丝法和后续的热处理工艺制备不同浓度Co纳米粒子掺杂的碳纳米纤维。通过差热-热重(DSC-TGA)仪、X射线衍射仪(XRD)、扫描电子显微镜(SEM)、矢量网络分析仪(VNA)对复合碳纳米纤维的热稳定性、物相、微观结构、电磁参数进行表征,并对其微波吸收性能进行研究。结果表明:当炭化温度为800℃时,复合纳米纤维结晶度适中,无定形碳部分转化为石墨相碳,CoAc_2全部被炭化还原为面心立方结构的金属Co纳米粒子,且纤维形貌完整,有串珠状结构存在于纤维网络之间;掺杂后碳纤维电磁性能得到明显改善,当掺杂量为7%(质量分数),涂层厚度为1.5mm时,有效吸收带宽达到最大,为4.5GHz,相比于纯碳纳米纤维,吸波性能得到显著提升。     

化学处理法制备碳包铜导热纳米流体及其性能表征

氩电弧等离子体法制备碳包铜纳米粒子,采用双氧水化学处理和添加十二烷基苯磺酸钠两种方法制备碳包铜-水纳米流体,探讨了不同分散方法对碳包铜纳米流体导热性能的影响.结果表明,双氧水化学处理碳包铜纳米粒子制备水介质分散体系具有比添加分散剂制备分散体系更高的导热性能.采用化学处理法,添加质量分数为2.0%的碳包铜-水纳米流体导热...     

单分散Fe纳米粒子的合成与性能表征

以液态五羰基铁(Fe(CO)5)为原料,通过表面活性剂控制合成得到了粒径小于20nm的α-Fe纳米粒子。用透射电镜、X射线衍射、红外光谱、矢量网络分析仪研究了液相热分解制备Fe纳米粒子的形貌和性能随表面活性剂用量的变化情况。当表面活性剂用量分别为0.4g和1.0g时,制备的Fe纳米粒子平均粒径分别为3.1、12.5nm,统计方差分别为0.03、3.42。对微波电磁参数的初步研究表明,Fe纳米粒子随粒径的变化表现出丰富的铁磁共振现象,并可以用静磁模式和交换模式的共振模型进行解释。     

电弧法制备碳包覆铁纳米微粒的纯化研究

利用钨电极电弧法制备了碳包覆铁纳米微粒,采用酸洗加磁选的方法对初产物进行了纯化.用透射电子显微镜、X射线衍射仪和振动样品磁强计对产物的形貌结构、物相组成以及磁性能进行了表征分析.结果表明:该纯化方法可以有效地去除产物中未被包覆或碳包覆不完整的铁颗粒及各类碳杂质,纯化后的产物以包覆多层碳膜的铁纳米颗粒为主;粉体的磁滞回线也表明经纯化后产物的磁性能得到了明显提高.     

Insertion of triangulated surfaces into a meccano tetrahedral discretization by means of mesh refinement and optimization procedures

In this paper, we present a new method for inserting several triangulated surfaces into an existing tetrahedral mesh generated by the meccano method. The result is a conformal mesh where each inserted surface is approximated by a set of faces of the final tetrahedral mesh. First, the tetrahedral mesh is refined around the inserted surfaces to capture their geometric features. Second, each immersed surface is approximated by a set of faces from the tetrahedral mesh. Third, following a novel approach, the nodes of the approximated surfaces are mapped to the corresponding immersed surface. Fourth, we untangle and smooth the mesh by optimizing a regularized shape distortion measure for tetrahedral elements in which we move all the nodes of the mesh, restricting the movement of the edge and surface nodes along the corresponding entity they belong to. The refining process allows approximating the immersed surface for any initial meccano tetrahedral mesh. Moreover, the proposed projection method avoids computational expensive geometric projections. Finally, the applied simultaneous untangling and smoothing process delivers a high‐quality mesh and ensures that the immersed surfaces are interpolated. Several examples are presented to assess the properties of the proposed method.     

Certification Institutions Expected to Update and Transfer Information on Present Standards

Standards are the basis for production enterprises to organize production, ex-factory inspection, trade (delivery) and technical exchanges, product certification, quality arbitration and supervision.……     

Flow calorimeter for enthalpy increment measurements on condensed gases

A flow calorimeter for enthalpy increment measurements on condensed gases is presented. A better knowledge of the properties of the liquefied natural gas is needed, and therefore a liquid loop has been designed for our flow calorimeter. The fluid loop in the calorimeter is designed in order to avoid the two-phase region, since two phases would give compositional disturbances in the measurements. The avoidance of the two-phase region is made possible by increasing the pressure of the test fluid after the measurement section, then heating the fluid at super-critical pressure past the critical point. Finally, the fluid is throttled to the low-pressure gas state at the inlet condition of the compressor that circulates the fluid. To perform the pressure increase, a new cryogenic pump has been designed. To evaluate the new equipment, measurements were taken on liquid ethane over the temperature range 146–256 K at pressure between 0.9 and 5.1 MPa.     

Refrigerators Enter a New Era of Health Preservation Frestech initiates the establishment of China's first standard for household sterilization refrigerators

On November 30, 2007, the China Association for Standardization (CAS) held a press conference at Beijing Diaoyutai State Guest House. Leaders from the China Household Electric Appliance Research Institute, the China Household Electric Appliance Association, and the China Consumers' Association attended and made speeches.……     

Optimum-Simulation von Ernteprozessen

Zusammenfassung Bei der Gestaltung von Ernteprozessen — beispielsweise des Prozesses Mähdrusch, Körnertransport und -abnahme — als transportverbundene Fließarbeitsverfahren mit mindestens zwei verschiedenen Arbeitsmitteln gibt es einen großen Optimierungsspielraum. Solche Prozesse sind mehrstufige Bedienungsprozesse mit gemischter Anordnung der Bedienungseinrichtungen. Außerdem besitzen sie stark ausgeprägte räumliche Aspekte. Es wird vor allem gezeigt, welche Merkmale solcher Prozesse in Simulationsmodellen abgebildet sein müssen, welche Zielgrößen in Abhängigkeit von welchen Einflußgrößen unter Berücksichtigung welcher Prozeßbedingungen ermittelt werden sollten und wie der Bewertungsprozeß zur Ermittlung der gewünschten Informationen gestaltet werden muß.     

A study of centrifugal cast high boron high speed steel

In the present study a high‐boron high speed steel (HSS) roll material was designed. Many expensive alloy elements have been substituted by cheap boron alloy, and high‐boron high speed steel roll has been manufactured by centrifugal casting method. The microstructures, mechanical properties and wear resistance of centrifugal casting high‐boron high speed steel roll have been investigated by optical microscopy (OM), scanning electron microscopy (SEM), and X‐ray diffraction (XRD) analysis, hardness test, impact test and wear test. The results indicated that the solidification microstructures of high‐boron high speed steel roll consisted of M₂(B,C), (W,Mo)₂(B,C), M₃(B,C), M₂₃(B,C)₆ type borocarbides and martensite, a small amount of retained austenite. Borocarbides were continuously distributed over the grain boundary. After quenching from 1050 °C, local broken network appeared in partial borocarbides, and fine secondary borocarbide precipitated from the matrix. After tempering from 525 °C, the amount of precipitated borocarbide increased significantly. After heat treatment, the hardness of high‐boron high speed steel roll excelled 60 HRC, and its impact toughness excelled 8.0 J/cm². The single groove steel rolling amount of high‐boron high speed steel rolls increases by 500% than that of bainite cast iron roll, when the rolls are used in K₁ mill housing of bar mill.     

Thixotropy of Systems with Shear Thinning and Plastic Flow Behavior

The definition of the thixotropy is a decrease in viscosity with time in shear and a subsequent recovery of viscosity after the shear deformation is removed.We ...     

Brainstorming for ISO Strategy 2016-2020

正Responding to ISO’s appeal for survey for the to-be-developed ISO Strategy Plan for 2016-2020,SAC hosted a special workshop over the needs and comments of various fi elds on June 8 in Beijing.The workshop was attended by ISO President-elect and Ansteel General Manager Zhang Xiaogang,SAC Vice-Administrator Yu Xinli,and 30 experts from     

CNAS Passes APLAC's PTP Review

正The review group of Asia Pacific Laboratory Accreditation Cooperation(APLAC)carried out a 4-day peer review of the proficiency testing provider(PTP)for China National Accreditation Service for Conformity Assessment(CNAS)from July 28 to 31,2014.CNAS passed the PTP review with excellent performance.Two senior peer reviewers of APLAC made a comprehensive,rigorous and detailed review of CNAS’s PTP accreditation activities,and made the on-spot inspection of the review groups in Shanghai and Shenzhen respectively.