Direct synthesis of syndiotactic-rich poly(N-isopropylacrylamide) via radical polymerization of hydrogen-bond-complexed monomer

Radical polymerization of N-isopropylacrylamide (NIPAAm) in toluene was investigated in the presence of hexamethylphosphoramide (HMPA). We succeeded in directly preparing syndiotactic-rich poly(NIPAAm), the syndiotacticity of which (r=70%) is the highest among those of radically-prepared poly(NIPAAm)s so far reported, by lowering polymerization temperature to −60 °C in the presence of a two-fold amount of HMPA. The NMR analysis revealed that the induced syndiotactic-specificity was ascribed to 1:1 complex formation between NIPAAm and HMPA. Furthermore, thermodynamic analysis described that the induced syndiotactic-specificity was enthalpically achieved.     

Heterotactic poly(N-isopropylacrylamide) prepared via radical polymerization in the presence of fluorinated alcohols

Radical polymerization of N-isopropylacrylamide in toluene at −40 °C in the presence of fourfold amounts of fluorinated alcohols was investigated. The ¹³C NMR analysis of the obtained polymers suggested that the addition of fluorinated alcohols induced heterotactic specificity in radical polymerization of NIPAAm, although syndiotactic poly(NIPAAm)s were obtained by adding alkyl alcohols as we have previously reported. To the best of our knowledge, this is the first synthesis of heterotactic poly(NIPAAm).     

Effect of a combination of hexamethylphosphoramide and alkyl alcohol on the stereospecificity of radical polymerization of N-isopropylacrylamide

Radical polymerization of N-isopropylacrylamide (NIPAAm) was investigated at low temperatures in the presence of both hexamethylphosphoramide (HMPA) and alkyl alcohols. Although HMPA and alkyl alcohols separately induced syndiotactic specificity in NIPAAm polymerization in toluene at low temperatures, a combination of HMPA and less bulky alkyl alcohols, such as methanol and ethanol, was found to induce isotactic specificity at −80 °C. NMR analysis of mixtures of NIPAAm, ethanol and HMPA suggested the formation of a 1:1:1 complex through O-H•••O=C and N-H•••O=P hydrogen bonding. It is believed that the steric effect of HMPA enhanced by cooperative hydrogen bonding was responsible for the combined effect of HMPA and alkyl alcohols in inducing isotactic specificity.     

Hydrogen-bond-assisted isotactic-specific radical polymerization of N-isopropylacrylamide with pyridine N-oxide

Radical polymerization of N-isopropylacrylamide (NIPAAm) in CHCl₃ at low temperatures in the presence of pyridine N-oxide (PNO) was investigated. An isotactic poly(NIPAAm) with meso diad content of 61% was successfully prepared at −60 °C in the presence of a two-fold amount of PNO. Thermodynamic analysis suggested that the isotactic-specificity was entropically induced, probably due to conformational fixation near the propagating chain-end through coordination by PNO.     

Metal-free isotactic-specific radical polymerization of N-alkylacrylamides with 3,5-dimethylpyridine N-oxide: The effect of the N-substituent and solvent on the isotactic specificity

Radical polymerization of N-methylacrylamide (NMAAm), N-n-propylacrylamide, N-isopropylacrylamide (NIPAAm) and N-benzylacrylamide was investigated in CHCl₃, CH₂Cl₂ and CH₃CN, in the presence of 3,5-dimethylpyridine N-oxide (35DMPNO) to examine the effects of the N-substituent and the solvent on the isotactic specificity induced by 35DMPNO. With addition of 35DMPNO to radical polymerization of N-alkylacrylamides in CHCl₃, isotactic specificity was significantly induced in NIPAAm polymerization but only slightly induced in NMAAm polymerization. Furthermore, mixed solvents of CH₃CN and halomethanes such as CHCl₃ and CH₂Cl₂ enhanced the ability of 35DMPNO to induce isotactic specificity, and poly(NIPAAm) with 74% meso dyad was obtained.     

Hydrogen-bond-assisted stereocontrol in the radical polymerization of N-isopropylacrylamide with bidentate Lewis base

Radical polymerization of N-isopropylacrylamide (NIPAAm) in toluene was investigated in the presence of bidentate Lewis base such as diphosphonates. Isotacticity of the obtained poly(NIPAAm)s slightly increased at −80 °C, whereas syndiotactic-rich poly(NIPAAm)s were obtained at −40-0 °C. This result corresponded to the results observed in the presence of primary alkyl phosphates. NMR analysis revealed that NIPAAm monomer and tetraisopropyl methylenebisphosphonate formed mono-binding hydrogen-bond-assisted complex at 0 °C, but a chelate complex at −80 °C. Thus, it was concluded that the stereospecificity in NIPAAm polymerization strongly depended on the complexation mode of the added bidentate Lewis base.     

Temperature-sensitive hydrogel prepared by graft polymerization of N-isopropylacrylamide onto macroradical Pluronic

A new series of thermo-responsive graft copolymers were prepared via consecutive Pluronic backbone-initiated by t-butylperoxybenzoate with N-isopropylacrylamide (NIPAAm) onto Pluronic by a radical-induced graft polymerization technique. The thermal characterizations of the graft copolymers were investigated by differential scanning calorimetry (DSC). The Pluronic-g-poly(NIPAAm) copolymers exhibited sol-to-gel transitions depending on chain length of the grafted poly(NIPAAm) onto Pluronic. The graft copolymers indicated that the hydrophobic–hydrophilic balance achieved by varying contents of NIPAAm was an important parameter in controlling the transition temperature of the graft copolymers in solution and stability of the resultant gels. The data suggest that graft copolymers may be attractive substrates for tissue engineering and drug delivery applications as the combination of mechanistically independent gelation techniques with regard to gelation kinetics.     

Considerations of polymerization method and molecular weight for proton-conducting poly(p-phenylene) derivatives

Ni(0)-catalyzed coupling polymerization of 2,5-dichloro-4′-phenoxybenzophenone was investigated by varying the ligand and coligand, temperature, reaction time, and solvent. The weight-average molecular weight (M_w) of poly(4-phenoxybenzoyl-1,4-phenylene)s (PPBPs) could be controlled by the polymerization conditions and reached a maximum of 4.4 × 10⁵ g mol⁻¹. Sulfonated PPBPs (S-PPBPs) with various M_ws were prepared with sulfuric acid to study the effect of molecular weight on the chemical and electrical properties of PPBP-based electrolytes. The strong molecular interactions in S-PPBP provided an ion exchange capacity of 2.9 meq g⁻¹ without loss of high mechanical properties. High molecular weight S-PPBPs had more desirable properties for fuel cell applications. While the swelling ratios and hydration numbers of S-PPBPs decreased with increasing molecular weight, the mechanical strength, proton conductivity, and fuel cell performance increased. S-PPBP also showed anisotropic behavior in the swelling and proton conductivity; such behavior is caused by the rigid-rod nature and the liquid-crystal structure.     

Metal-free isotactic-specific radical polymerization of N-isopropylacrylamide with pyridine N-oxide derivatives: The effect of methyl substituents of pyridine N-oxide on the isotactic specificity and the proposed mechanism for the isotactic-specific radical polymerization

The radical polymerizations of N-isopropylacrylamide (NIPAAm) in chloroform at low temperatures in the presence of pyridine N-oxide (PNO) derivatives were investigated. It was found that the methylation at meta-positions of PNO improved the isotactic specificity induced by PNO, whereas the methylation at ortho-positions prevented the induction of the isotactic specificity. NMR analysis revealed that NIPAAm and PNO derivatives formed predominantly 2:1 complex through a hydrogen-bonding interaction. Furthermore, the induction of the isotactic specificity was attributed to the conformationally limited propagating radicals. Based on these findings, the mechanism of the isotactic-specific radical polymerization was discussed.     

Ultra high molar mass poly[2-(dimethylamino)ethyl methacrylate] via atom transfer radical polymerization

Well-defined high molecular weight poly[2-(dimethylamino)ethyl methacrylates] [poly(DMAEMA)s] with molar masses up to ∼1×10⁶ g/mol were successfully synthesized via atom transfer radical polymerization (ATRP). This was achieved by using p-toluenesulfonyl chloride(p-TsCl)/CuCl/1,1,4,7,10,10-hexamethyl-triethylenetetramine(HMTETA) initiator/catalyst complex in methanol/water mixture. Well-controlled/‘living’ behavior was demonstrated throughout the reaction, up to high monomer conversion. The PDI value remained low at 1.26 even for a polymer with very high molecular weight at 1.1×10⁶ g/mol. We believe this is the first successful case where controlled ATRP produces a polymer with molar mass exceeding a million!     

Dispersion polymerization in supercritical carbon dioxide using comb-like fluorinated polymer surfactants having different backbone structures

Comb-like fluorinated polymers with different backbone structures, poly(heptadecafluorodecyl acrylate) (PA-R_f), poly[oxy[(2-perfluorooctylethylene)thiomethyl]ethylene] (PEO-R_f), and poly[p-[[(perfluorooctylethylene)thio]methyl]styrene] (PS-R_f), were used as surfactants in dispersion polymerization to examine the effect of backbone structure on the formation of polymer particles. Dispersion polymerization of monomers with different polarities using these comb-like fluorinated polymer surfactants in CO₂ showed that PEO-R_f containing a polar oxyethylene backbone was an effective surfactant for the dispersion polymerization of a polar monomer, such as N-vinyl-2-pyrrolidone, whereas PA-R_f was effective for less polar monomers, such as methyl methacrylate and N-vinyl caprolactam.     

Effects of molecular weight on liquid-crystalline behavior of a mesogen-jacketed liquid crystal polymer synthesized by atom transfer radical polymerization

The synthesis of poly{2,5-bis[(4-methoxyphenyl)oxycarbonyl]styrene} (PMPCS) with different molecular weight and low polydispersity was achieved by atom transfer radical polymerization in methoxybenzene solution using 1-bromoethylbenzene as an initiator and CuBr/sparteine complex as a catalyst. The concentration of the living centers throughout the polymerization was found to be constant. The liquid-crystalline behavior of the polymers with M_n ranging from 3800 to 17,400 g/mol was studied using DSC and POM. Only the polymers with M_n beyond 10,200 g/mol formed a liquid-crystalline phase, which was quite stable with a high clearing point (higher than the decomposition temperature of the polymer).     

Synthesis of polyvinyl alcohol stereoblock copolymer via the combination of living cationic polymerization and RAFT/MADIX polymerization using xanthate with vinyl ether moiety

Different types of novel xanthates containing a vinyl ether moiety, S-benzyl O-2-(vinyloxy)ethyl carbonodithioate (Xanthate 1) and S-1-(ethoxycarbonyl)ethyl O-2-(vinyloxy)ethyl carbonodithioate (Xanthate 2) were synthesized. In particular, the Xanthate 2 enabled to design polyvinyl alcohol (PVA) stereoblock copolymer via the combination of living cationic vinyl polymerization and RAFT/MADIX polymerization. For cationic polymerization of isobutyl vinyl ether (IBVE) and tert-butyl vinyl ether (TBVE), the polymerizations were conducted under Xanthate 1-HCl adduct/SnCl₄ and Xanthate 1 or 2-CF₃COOH adduct/EtAlCl₂ initiating system in the presence of ethyl acetate. Both systems proceeded in living polymerization fashion because the calculated M_n of both poly(IBVE) and poly(TBVE) matches with the M_n polymerized assuming that one polymer chain is formed per one molecule of the Xanthate 1 or 2. The resulting poly(TBVE) had a high number average α-end functionality as determined by MALDI-TOF-MS spectrometry. Xanthate 2 is more efficient for the following RAFT/MADIX polymerization of vinyl acetate (VAc). The RAFT/MADIX polymerization of vinyl acetate (VAc) using azobis(isobutyronitrile) (AIBN) at 60 °C was conducted using either poly(IBVE) or poly(TBVE) macro-CTA. The poly(TBVE) macro-CTAs synthesized from the Xanthate 2 were able to polymerize VAc smoothly via RAFT/MADIX polymerization, to prepare well-defined diblock copolymer, poly(TBVE)-b-poly(VAc). The resulting block copolymer was then hydrolyzed using KOH in methanol and followed by acid hydrolysis using HBr gas bubbling. The resulting polymer is inherently stereoblock like copolymer, isotactic rich PVA-b-atactic PVA (iPVA-b-aPVA). From the DSC measurement, the iPVA-b-aPVA has one glass transition at 69.5 °C and two melting points according to iPVA and aPVA at 237.9 and 198.1 °C, respectively. Thus, it can be suggested that the obtained PVA has two different geometries by the combination of living cationic polymerization and RAFT/MADIX polymerization.     

Synthesis of thermoresponsive block and graft copolymers via the combination of living cationic polymerization and RAFT polymerization using a vinyl ether-type RAFT agent

A novel vinyl ether-type RAFT agent, benzyl 2-(vinyloxy)ethyl carbonotrithioate (BVCT) was synthesized for various block copolymers via the combination of living cationic polymerization of vinyl ethers and reversible addition−fragmentation chain transfer (RAFT) polymerization. The novel BVCT–trifluoroacetic acid adduct play an important role to produce well-defined block copolymers, which is both as a cationogen under EtAlCl₂ initiation system in the presence of ethyl acetate for living cationic polymerization and a RAFT agent for blocks by RAFT polymerization. The resulting polymer, poly(vinyl ether)s, by living cationic polymerization had a high number average α-end functionality (≥0.9) as determined by both ¹H NMR and MALDI-TOF-MS spectrometry. In addition, this poly(vinyl ether)s worked well as a macromolecular chain transfer agent for RAFT polymerization. The RAFT polymerization of radically polymerizable monomers was conducted in toluene using 2,2′-azobis(isobutyronitrile) at 70 °C. For example, a double thermoresponsive block copolymer (MOVE₆₁-b-NIPAM₁₅₀) consisting of 2-methoxyethyl vinyl ether (MOVE) and N-isopropylacrylamide (NIPAM) was prepared via the combination of living cationic polymerization and RAFT polymerization. The block copolymer reversibly formed and deformed micellar assemblies above the phase separation temperature (T_ps) of poly(NIPAM) block in water. This BVCT is not only functioned as an initiator, but also acted as a monomer. When BVCT was copolymerized with MOVE by living cationic polymerization, followed by graft copolymerization with NIPAM via RAFT polymerization, well-defined graft copolymers (MOVE_n-co-BVCT_m)-g-NIPAM_x (n = 62–73, m = 1–9, x = 19–214) were successfully obtained. However, no micelle formed in water above T_ps of poly(NIPAM) graft chain unlike the case of block copolymers.     

Superparamagnetic thermoresponsive composite latex via W/O miniemulsion polymerization

In this research, the thermoresponsive composite latex particles were prepared via W/O miniemulsion polymerization. Fe₃O₄ nanoparticles were homogeneously dispersed inside the poly(NIPAAm‐co‐MAA) latex particles. In the first step, PAA oligomers were used as stabilizers to produce a stable water‐based Fe₃O₄ ferrofluid, which could mix well with the water‐soluble monomers. In the second step, the Fe₃O₄/poly(NIPAAm‐co‐MAA) composite latex particles were synthesized via W/O miniemulsion polymerization. This polymerization proceeded in cyclohexane at room temperature, with Span80 as the emulsifier, NIPAAm as the thermoresponsive monomer, MAA as a comonomer with ? COOH functional groups, and APS/SMBS as the redox initiator system. The distribution of Fe₃O₄ nanoparticles inside the composite latex particles was expected to be homogeneous. The nucleation and morphology of the composite latex particles were mainly controlled by the concentration of the surfactant, Span80, in cyclohexane. The properties of the composite latex were examined with several instruments such as DSC and TGA. Finally, the superparamagnetic and thermoresponsive characteristics of this functional composite latex were also investigated. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 3987–3996, 2006     

pH-responsive micelles based on (PCL)2(PDEA-b-PPEGMA)2 miktoarm polymer: controlled synthesis,characterization, and application as anticancer drug carrier

Amphiphilic A₂(BC)₂ miktoarm star polymers [poly(ϵ-caprolactone)]₂-[poly(2-(diethylamino)ethyl methacrylate)-b- poly(poly(ethylene glycol) methyl ether methacrylate)]₂ [(PCL)₂(PDEA-b-PPEGMA)₂] were developed by a combination of ring opening polymerization (ROP) and continuous activators regenerated by electron transfer atom transfer radical polymerization (ARGET ATRP). The critical micelle concentration (CMC) values were extremely low (0.0024 to 0.0043 mg/mL), depending on the architecture of the polymers. The self-assembled empty and doxorubicin (DOX)-loaded micelles were spherical in morphologies, and the average sizes were about 63 and 110 nm. The release of DOX at pH 5.0 was much faster than that at pH 6.5 and pH 7.4. Moreover, DOX-loaded micelles could effectively inhibit the growth of cancer cells HepG2 with IC₅₀ of 2.0 μg/mL. Intracellular uptake demonstrated that DOX was delivered into the cells effectively after the cells were incubated with DOX-loaded micelles. Therefore, the pH-sensitive (PCL)₂(PDEA-b-PPEGMA)₂ micelles could be a prospective candidate as anticancer drug carrier for hydrophobic drugs with sustained release behavior.     

Stereochemistry of the radical polymerization of vinyl pentafluorobenzoate

The free-radical polymerization of vinyl pentafluorobenzoate (VPBz) was carried out under various conditions in order to compare its stereochemistry to that of the vinyl benzoate (VBz) polymerization using similar conditions. Contrary to the stereochemistry of the radical polymerization of VBz, VPBz favors syndiotactic propagation. The poly(VPBz) obtained in hexafluoroisopropanol (HFIP) with nBu₃B-air at −30 °C has a triad syndiotacticity (rr) of 52% which achieved the highest syndiotacticity reported for the radical polymerization of vinyl esters. The stereochemistry difference for the VPBz polymerization was ascribed to the electron-withdrawing effect of the fluorine on the aromatic ring. The solvent effect of enhancing the rr specificity in HFIP may be related to the hydrogen-bonding between HFIP and VPBz or the growing species. It was also found that the glass transition temperatures (T_g) of the VPBz polymers apparently increased with an increase in their diad syndiotacticities (r): the T_g of poly(VPBz) with r=72% was 79 °C, which was 25 °C higher than that of poly(VPBz) with r=56% obtained in toluene.     

Adsorption of block copolymers at latex surface and their utilization in emulsion polymerization

Amphiphilic block copolymers have been investigated for their utilization in emulsion polymerization of butyl methacrylate. Special attention has been paid to the adsorption mechanism of the block copolymers from systematic measurements of equilibrium adsorption isotherms. A series of well-defined water-soluble amphiphilic block copolymers, composed of poly(butyl methacrylate) and poly(sodium methacrylate) blocks, were synthesized by anionic polymerization of butyl methacrylate and tert-butyl methacrylate followed by the thermal deprotection of the tert-butyl ester groups and final hydrolysis. The number density of emulsion polymer particles N_P varied as [copolymer]^α, α lying between 0.44 and 0.73 according to the hydrophilic content of the copolymers. In contrast with SDS taken as a reference emulsifier, the adsorption of the copolymers was very strong and this provided quite an efficient stabilization of the polymer particles during emulsion polymerization, even at low concentrations (<10⁻⁴ mol L⁻¹) and low coverages (<10% of the interfacial area).     

A new polymerization method and kinetics for acrylamide: Aqueous two‐phase polymerization

The concept of aqueous two‐phase polymerization and a new polymerization method for the preparation of water‐soluble polymers are presented. The phase diagram of poly(acrylamide) (PAAm)‐poly (ethylene glycol) (PEG)‐water two‐phase system was measured by the gel permeation chromatography (GPC). The aqueous two‐phase of PAAm‐PEG‐water system can be easily formed. The critical concentration of phase separation was affected by the molecular weight of PEG. The aqueous two‐phase polymerization of acrylamide (AAm) has been successfully carried out in the presence of PEG by using ammonium persulfate (APS) as the initiator. The polymerization behaviors with varying concentration of AAm, initiator and PEG, the polymerization temperature, the molecular weight of PEG, and emulsifier types were investigated. The activation energy of aqueous two‐phase polymerization of AAm was 132.3 kJ/mol. The relationship of initial polymerization rate (R_p0) with APS and AAm concentrations was R_p0 ∝ [APS]^0.72 [AAm]^1.28. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2009     

Highly isotactic poly(vinyl alcohol). III: Heterogeneous cationic polymerization of tert-butyl vinyl ether

We studied the polymerization of tert-butyl vinyl ether (tBVE) and benzyl vinyl ether with heterogeneous catalysts, that is, modified Ziegler type (Vandenberg type) catalysts and metal sulfate-sulfuric acid complexes.Vandenberg type catalysts gave high molecular weight and highly isotactic poly(tBVE)s with relatively narrow molecular weight distribution at high temperature, and then the resultant poly(tBVE)s were converted into the stereoregular poly(vinyl alcohol)s (PVAs). With titanium based Vandenberg type catalyst, a relative high isotactic PVA, which has 52% triad isotacticity, was obtained from the poly(tBVE) polymerized at 30 °C. It was found from NMR study that the content of the triad tacticity of PVAs derived from poly(tBVE) catalyzed by titanium based catalysts agreed with the value calculated from the chain-end control model (Bovey's model). This fact suggests that the steric structure of the adding monomer in this system is determined by same mechanism to homogeneous BF₃ complexes catalysts system. On contrast to that, the metal sulfate-sulfuric acid complexes show significantly low activity to tBVE polymerization.