High-Temperature Oxidation Behavior of 5Cr21Mn9Ni4N Steel Micro-Alloyed by Rare Earth

The oxidation resistance of 5Cr21Mn9Ni4N steel micro-alloying by RE at 700 - 900 ℃ was investigated. The results indicate that oxidation exponent n and oxidation activation energy are increased, and oxidation velocity constant kp is decreased when 0.2% RE is added in 5Cr21Mn9Ni4N steel. The addition of RE elements does not alter phase constitution of oxidation scale, however it improves the configuration of oxidation scale, and increases thermal stability and adhesivity of oxidation scale, which results in the raise of oxidation resistance of 5Cr21Mn9Ni4N steel at high temperature. The oxidation scale constitutes of refractory steel transfer from manganic oxide mostly to ferric oxide mostly with the increase of temperature, which leads to descend of compactness and desquamation resistance of oxidation scale. The mass increase of ferric oxide in the oxidation scale and the looseness of oxidation scale are the main reason to descend the oxidation resistance of refractory steel.     

节镍型奥氏体不锈钢1Cr17Mn9Ni4N的组织和力学性能

从热处理工艺对室温拉伸性能的影响和试验温度对拉伸性能的影响两个方面分析了1Cr17Mn9Ni4N钢组织和力学性能之间的关系。试验结果表明：随着固溶处理温度(950～1075℃)的提高,强度降低、塑性提高;水冷或空冷对力学性能的影响不大;材料的锻比对力学性能具有一定的影响;与同类钢相比,1Cr17Mn9Ni4N钢具有优异的室温和低温力学性能。该钢在低温变形时的TRIP效应是低温综合力学性能良好的根本原因。     

工艺参数对5Cr21Mn9Ni4N钢塑性的影响

本文讨论了热变形和冷变形工艺参数对５Ｃｒ２１Ｍｎ９Ｎｉ４Ｎ钢塑性的影响，提出大断面钢坯锻轧温度为１１００℃，小断面钢坯开轧温度为１１８０℃，并用冷轧代替冷拔成材的工艺流程。     

0Cr21Ni6Mn9N奥氏体不锈钢的应变强化行为

研究了不同氮含量的0Cr21Ni6Mn9N奥氏体不锈钢的塑性流变行为。结果表明,其形变强化特性可用Ludwigson模型来表示。钢在不同的应变下表现出不同的塑性流变行为,存在一个瞬变应变。当应变量低于它时,流变行为与Ludwik方程存在一个正偏差;而应变量高于它时,则符合Ludwik模型。造成这一差异的主要原因是位错滑移模式发生了改变,低于瞬变应变时为单系滑移,高于瞬变应变时为多系滑移。氮对位错滑移模式的影响主要表现为对瞬变应变的影响。随氮含量的增加,瞬变应变被推向更高的水平,这意味着氮原子使位错在更大的应变下才产生多系滑移和交滑移。     

5Cr21Mn9Ni4N阀门钢冷拉材半径裂的形成和扩展

覆盖在裂纹分裂面上的氧化物，裂面上的断裂源和放射扩展共清晰可见，表面平坦裂纹有冷拉前形成和过程中生成的两种形式，与冷拉过程相关的半径裂，大都起始于钢材表皮下０．０７～０．５ｍｍ皮下夹杂处，并沿富Ｃｒ相与基体的界面进行扩展。     

节镍型双相不锈钢00Cr21Mn5Ni1N的热加工性能

 采用热压缩和热拉伸试验方法,对节镍型双相不锈钢00Cr21Mn5Ni1N的高温变形抗力、高温塑性及高温变形时奥氏体相的数量进行了研究。结果表明,00Cr21Mn5Ni1N双相不锈钢在950~1 200 ℃之间变形时,具有良好的热加工性能,钢中奥氏体相量可以控制在适合热加工的范围。     

长期时效对GH4199合金组织和性能的影响

 采用金相和电镜微观组织观察、室温和高温拉伸试验、物理化学相分析等综合试验方法，对经600、700、800、900 ℃和100、200、500、1 000 h长期时效处理的GH4199合金进行测试和研究。结果表明，GH4199合金经长期时效后，其室温和高温力学性能仍保持在较高水平；合金的组织稳定性良好，析出相主要为γ′相和碳化物。据相分析结果可知，在700~900 ℃时效1 000 h左右，合金组织中存在极微量的脆性(TCP)相——μ相和σ相，它们对合金的力学性能基本无影响，组织中虽然存在微量TCP相，但合金的室温和高温塑性不发生“脆化”。     

Grain Growth Behavior of 5Cr21Mn9Ni4N Steel Micro-Alloyed by Rare Earth

Grain growth behavior of 5Cr21Mn9Ni4NRE steel was experimentally studied at various solid solution treatment temperatures and holding for different times. The experimental results show that the 5Cr21Mn9Ni4NRE steel has the feature of sharp austenite grain coarsening after solid solution treatment at the temperature above 1150 ℃. RE added in the steel has the benefit to restrain grain growth and increase grain growth activation energy.     

1Cr21Ni5Ti钢管冷弯脆性问题研究

论文研究了热处理工艺对1Cr21Ni5Ti钢组织与性能’的影响,找到了材料冷弯脆性的原因,得到了如下结论：（1）材料产生脆性的原因是敏化处理时。相的析出,材料固溶后在650℃。900℃敏化处理时析出。相,导致塑性和韧性降低,并且在700℃敏化口相的析出量最大;（2）材料经固溶处理后在700℃保温10分钟时就有口相析出,20分钟达到最大析出量,导致塑性和韧性降低;（3）σ相在900℃～950℃之间开始溶解。已经产生。相的材料可以通过重新加热到950℃以上然后快速冷却来消除因σ相的析出而产生的脆性。     

Effect of Rare Earth Elements on Austenite Growth Dynamics of Steel 9Cr2Mo

ＥｆｆｅｃｔｏｆＲａｒｅＥａｒｔｈＥｌｅｍｅｎｔｓｏｎＡｕｓｔｅｎｉｔｅＧｒｏｗｔｈＤｙｎａｍｉｃｓｏｆＳｔｅｅｌ９Ｃｒ２ＭｏＹａｎｇＱｉｎｇｘｉａｎｇ；ＷａｎｇＡｉｒｏｎｇ；ＧａｏＭｉｎｇ；ＷｕＨａｏｑｕａｎ；ＧｕｏＴｉｅｂｏＧａｏＭｉing;Ａｂｓｔ...     

稀土Ce对1Cr18Mn8Ni5N不锈钢耐均匀腐蚀性能影响

利用电化学的极化曲线及交流阻抗技术研究了不同稀土含量的1Cr18Mn8Ni5N不锈钢在硫酸介质中的腐蚀行为。应用扫描电镜对试样的腐蚀形貌及夹杂物形态进行了观察,利用EDS对夹杂物成分进行了分析。结果表明:钢中加入稀土Ce可改变夹杂物形态,并使其交流阻抗的极化电阻增大,极化曲线的腐蚀电位正移,降低了腐蚀电流密度,抵制了均匀腐蚀,改善了1Cr18Mn8Ni5N不锈钢的耐蚀性。当钢中稀土Ce质量分数为0.022%时,1Cr18Mn8Ni5N不锈钢可获得最好的耐均匀腐蚀性能。     

00Cr25Ni7Mo4N双相不锈钢的热轧组织与织构

观察了00cr25Ni7M04N双相不锈钢在不同轧制温度和不同压下率下的组织形貌和晶粒取向,结果表明,在相同压下量下,奥氏体相形变程度随轧制温度上升而减弱;铁素体相织构复杂,织构强度远大于奥氏体相.轧制过程中的相变、形变和动态再结晶是产生上述这些现象的原因.     

喂稀土丝处理16Mn钢的试验研究

在实验室内模拟生产在结晶器丝的工艺，对１６ｎｍ钢进行稀土处理试验研究。检验了稀土加入量对钢中氧含量、钢的晶粒度、钢中夹杂物状况以及对钢材冲击韧性的影响。提出在结晶器内喂稀土丝的工艺及稀土的合适加入量为０．１０％、１．１２％。     

稀土对16Mn钢等温相变及显微组织的影响

采用金相观察与硬度测量相结合的方法测定了不同稀土含量16Mn钢的TTT曲线,并研究了稀土含量对其等温相变及显微组织的影响.研究表明,随稀土含量的增加,先共析铁素体的晶粒大小及其析出的孕育期减小,完成珠光体相变所需时间和组织中铁素体含量增大;贝氏体形态逐渐由羽毛状向粒状转变.含稀土钢组织中的碳化物具有明显的偏聚现象.本文对这些结果产生的原因进行了讨论.     

Effects of Rare Earth Elements on Corrosive Wear Behaviour of Cast Cr-Mn-N Stainless Steel in Dilute Sulphuric Acid

ＥｆｅｃｔｓｏｆＲａｒｅＥａｒｔｈＥｌｅｍｅｎｔｓｏｎＣｏｒｒｏｓｉｖｅＷｅａｒＢｅｈａｖｉｏｕｒｏｆＣａｓｔＣｒＭｎＮＳｔａｉｎｌｅｓＳｔｅｌｉｎＤｉｌｕｔｅＳｕｌｐｈｕｒｉｃＡｃｉｄＤｉｎｇＨｕｉ（丁晖），ＹｕａｎＧｕａｎｇｙｉｎ（袁广银），...     

冶炼方法对0Cr12Mn5Ni4Mo3Al高强不锈钢棒材力学性能和组织的影响

 研究了使用真空感应炉+电渣重熔工艺代替原有的电炉+炉外精炼（LF）+电渣重熔工艺对0Cr12Mn5Ni4Mo3Al高强度不锈钢不同规格棒材的力学性能和组织的影响。结果表明,使用新工艺得到的钢材更为洁净,组织中保留有适量的残余奥氏体;与旧工艺小规格棒材相比,新工艺得到的大规格棒材在保持或提高抗拉强度的同时,优化了屈强比,提高了塑韧性,冲击吸收功提高了40~60J;适当调节w(Cr)eq/w(Ni)eq比以及采用合理的锻造、轧制工艺,可以消除棒材组织中δ-铁素体的不利影响,更大限度地发挥材料潜力。     

Effect of Rare Earth on Thermal Shock Resistance of Steel 9Cr2Mo

Ｒａｒｅｅａｒｔｈｅｌｅｍｅｎｔｓｈａｖｅｂｅｅｎａｄｄｅｄｉｎｔｏｈｏｔｒｏｌｌｅｒｓｔｅｅｌ.ＲＥｅｌｅｍｅｎｔｓｃａｎｉｍｐｒｏｖｅｔｈｅｒ ｍａｌｆａｔｉｇｕｅ[1] ,ｌｏｗｆｒｅｑｕｅｎｃｙｆａｔｉｇｕｅ[2 ] ,ｐｌａｓ ｔｉｃｉｔｙａｎｄｔｏｕｇｈｎｅｓｓ[3] ,ｒｅｆｉｎｅａｕｓｔｅｎｉｔｉｃｇｒａｉｎｓｉｚｅ[4] ａｎｄｍｏｄｉｆｙｉｎｃｌｕｓｉｏｎｓ[5 ] ｏｆｈｏｔｒｏｌｌｅｒｓｔｅｅｌ 6 0ＣｒＭｎＭｏ .Ｓｔｅｅｌ 9Ｃｒ2Ｍｏｉｓａｔｒａｄｉｔｉｏｎａｌｃｏｌｄｒｏｌｌｅｒｓｔｅｅｌ.Ｗｈｅｎ…     

双相不锈钢1Cr21Ni5Ti脆化研究

主要研究了1Cr21Ni5Ti双相不锈钢400℃～600℃之间不同温度的脆化倾向，结果表明：400℃～500℃之间时效脆化速度明显高于550℃和600℃时效，脆化原因主要是铁素体钢具有的475℃脆性。     

扩渗稀土对1Cr18Ni9钢耐腐蚀性能的影响

研究了通过化学气相扩渗稀土方法提高1Cr18Ni9钢表面耐腐蚀性能的作用.结果表明,经过65%硝酸腐蚀三个周期试验,扩渗稀土试样质量损失腐蚀速率明显减小;阳极极化曲线的测定结果证明了扩渗稀土后的试样临界钝化电流密度和稳定钝态下溶解电流密度降低,钝态电位区间加宽.经扩渗稀土处理的1Cr18Ni9钢晶界和晶内元素铬含量趋于一致,不存在贫铬区,耐腐蚀性能显著提高.     

Effect of Rare Earth Elements on Quenching Crack Resistance of Steel 9Cr2Mo

Ｒｏｌｌｅｒｆｏｒｃｏｌｄｒｏｌｌｉｎｇｉｓａｋｅｙｆｏｒｇｉｎｇｐａｒｔ,ｗｈｉｃｈｅｘｐｅｒｉｅｎｃｅｓｃｏｎｔａｃｔｓｔｒｅｓｓ ,ａｌｔｅｒ ｎａｔｉｎｇｓｔｒｅｓｓａｎｄｆｒｉｃｔｉｏｎａｌｓｔｒｅｓｓｄｕｒｉｎｇｒｏｌｌｉｎｇ .Ｔｈｅｒｅｆｏｒｅ ,ｈｉｇｈｅｒｓｔｒｅｎｇｔｈ ,ｓｕｒｆａｃｅｈａｒｄｎｅｓｓ,ｗｅａｒｒｅｓｉｓｔａｎｃｅａｎｄｅｎｏｕｇｈｔｏｕｇｈ ｎｅｓｓｓｈｏｕｌｄｂｅｃｏｎｓｉｄｅｒｅｄｆｏｒｍａｎｕｆａｃｔｕｒｉｎｇｔｈｉｓｃｏｌｄｒｏｌｌｅｒ[1] .Ｓｉｎｃｅｔｈｅ…