梳形共聚物侧链长度对水泥浆体早期性能的影响

研究了梳形共聚物侧链长度对水泥浆体的凝结、水化热效应和增强性能的影响。结果表明,随共聚物侧链长度增加,水泥浆凝结时间缩短,早期强度提高。而且梳形共聚物侧链对水泥水化放热性能影响也很显著,添加长侧链梳形共聚物可使水泥水化热平缓释放,放热速率和最高温峰大大降低,但水化热峰值出现的时间提前。     

矿物掺合料对PVA-ECC性能的影响

研究了单掺粉煤灰和复掺粉煤灰与硅灰代替部分水泥对PVA-ECC试件力学性能、裂缝宽度及抗渗性能的影响。结果表明,单掺粉煤灰会导致PVA-ECC试件强度下降,但可显著增加其韧性。复掺粉煤灰与硅灰时,PVA-ECC试件表现出优异的应变硬化特性以及多缝开裂现象,力学性能得到提升,基体均匀性增加,抗渗性能得到改善,最大提升了约33%。试验得到了具有良好性能的粉煤灰-硅灰-水泥三元体系PVA-ECC试件,其极限拉伸应变达到2.07%,抗压强度达到42.6 MPa,裂缝宽度较小且分布均匀,渗透系数仅为2.136×10-~(11)m/s,抗渗性能较优。     

矿物掺合料对透水混凝土性能的影响研究进展

透水混凝土作为一种环境友好型建筑材料,研究外掺材料对提高其工作性能和效益成为热点。论文概述了矿物掺合料对透水混凝土力学性能、透水性能、耐久性能的影响,总结了不同矿物掺合料改性透水混凝土的作用效果和影响规律。得出矿物掺合料对透水混凝土的力学性能、耐久性能通常是有利影响,对透水性能是不利影响。     

矿物掺合料对聚合物改性多孔水泥混凝土的性能影响研究

为有效改善聚合物改性多孔水泥混凝土(PMPC)的力学性能,在混合料中加入粉煤灰、硅灰等矿物掺和料。优化了PMPC中矿物掺和料的掺量,研究了矿物掺和料对其强度性能、透水性能、表面功能性的影响,并提出了PMPC的结构模型,揭示了PMPC的强度形成机理。试验结果表明:在混合料中加入10%掺量的粉煤灰或6%掺量的硅灰,其28 d抗压强度分别达到23、47 MPa,28 d抗折强度分别达到5.2、5.9 MPa,透水系数分别达到0.36、0.34 cm/s,其表面构造深度可达到1 mm以上,表面抗滑摆值可达到40 BPN以上。     

梳形共聚物分散剂羧基与聚醚侧链比例对水泥浆体流变性能的影响

本文系统研究了梳形共聚物分散剂羧基和聚醚侧链比例对水泥浆流变和分散性能的影响。结果表明：随共聚物主链中羧酸基团比例的提高,分散剂在水泥颗粒界面上吸附作用增强,分散性能提高,黏度下降,流变性能改善。但当羧基比例超过一定范围时,吸附能力反而下降,导致分散性能下降。同时,所有添加梳形共聚物的水泥浆体流动曲线方程都符合H—B方程,且具有良好的相关性。     

矿物掺合料对混凝土性能的影响

随着我国工程建设事业的不断发展,高性能混凝土的应用越来越广泛,我国学者对其进行了长达十多年的研究。矿物掺合料是混凝土中的一个重要组成部分,其直接影响到混凝土的施工性能。本文笔者通过试验分析不同种类的矿物掺合料对混凝土的力学性能和抗氯离子渗透性能的影响。希望能对读者起到借鉴作用。     

不同掺合料对硫铝酸盐水泥性能影响的研究进展

因硫铝酸盐水泥后期强度有不同程度的倒缩、凝结时间过短等缺陷,使其在某些工程中的应用受到限制。为了解决硫铝酸盐水泥后期强度问题,使其满足工程和建筑强度的要求,论述了不同掺合料不同含量对硫铝酸盐强度的影响,改善硫铝酸盐水泥性能,以期增加其后期强度。     

新型羧酸类梳型接枝共聚物超塑化剂的应用性能研究

本文应用高分子材料分子设计原理,构筑了一种被用作混凝土超塑化剂的羧酸系低分子量梳型接枝共聚物,采用一种高活性的改性剂对工业聚乙二醇进行改性,然后采用高效催化剂在无溶剂方式下进行接枝,合成出具有聚合活性的功能性大单体,后通过高效、经济的水相自由基聚合法来制备梳型接枝共聚物超塑化剂,并讨论了该聚合物在混凝土中的应用性能。     

矿物掺合料对机制砂浆性能影响

研究了磨细石灰石粉、粉煤灰和矿渣掺合料对机制砂砂浆物理力学性能的影响。当矿物掺量由10%向40%递增,结果表明:矿渣试件7d强度下降,28d强度高于基准试件;砂浆流动性提高但保水性降低。粉煤灰试件、石灰石粉试件的7d和28d强度低于基准试件,石灰石粉试件强度降低尤甚;粉煤灰砂浆流动性先升高而后降低,以20%或者30%为拐点,石灰石粉会显著提高砂浆的保水性,但对砂浆强度有不利影响。矿渣与石灰石粉复合制备的砂浆,其稠度、保水性和强度满足工程实际对砂浆的要求,且优于粉煤灰与石灰石粉复合制备的砂浆。     

不同掺合料对透水混凝土性能的影响

利用正交试验方法研究了硅灰掺量(3％、5％、7％)、偏高岭土掺量(8％、10％、12％)与聚丙烯纤维体积掺量(1％、2％、3％)对透水混凝土力学性能、渗透性能和耐久性能的影响.正交试验结果表明:硅灰对透水混凝土力学性能的影响较为显著,纤维对透水混凝土连续孔隙率的影响较为显著;得出推荐掺量为:硅灰掺量为7％、偏高岭土掺量...     

MPEG侧链长度对聚羧酸超塑化剂吸附分散性能的影响

通过自由基聚合反应,本文制备了一系列具有不同侧链长度的梳型共聚物。研究了MPEG侧链长度对梳型共聚物分子构象的影响,并通过总有机碳分析(TOC)和净浆流动度测试对制得的不同侧链长度的聚羧酸梳型共聚物在水泥颗粒上的吸附分散性能进行了表征。结果表明:随着侧链MPEG长度的增加,共聚物在水泥颗粒上的吸附量会急剧降低;在MPEG-MAA与甲基丙烯酸(MAA)共聚体系中,按一定比例同时接人不同长度的MPEG侧链时,共聚物会表现出特殊的吸附规律;并且当侧链聚合度n_(EO)=22和n_(EO)=43按摩尔比1:2在共聚体系中进行接枝时,共聚物表现出最佳的分散性能。     

Effect of nonionic side chain length of polycarboxylate-ether-based high-range water-reducing admixture on properties of cementitious systems

Despite the large variations in the behaviors of water-reducing admixtures upon changes in their structures, most previous reports on the cement-admixture compatibility did not provide sufficient information on the structure of the admixture. Hence, the evaluation and generalization of the reports on the cement-admixture compatibility are challenging. In this study, three different polycarboxylate-ether-based water-reducing admixtures with the same free nonionic content, anionic/nonionic molar ratio, and main chain length and different side chain lengths were produced. The compatibility of these admixtures with a CEM I 42.5R-type cement was investigated. In addition, an analysis of variance was performed on the experiment results to evaluate the contributions of the admixture type, admixture/cement ratio, and elapsing time to the Marsh funnel flow time, mini-slump, slump flow, and compressive strength. The water-reducing admixtures having long or short side chains reduced the initial flow characteristics of the cementitious systems. However, the admixture having the shortest side chain was better with regard to flow retention. The side chain length of the admixture did not have significant effects on the compressive strength and water absorption capacity of the mortar mixtures and mini-slump performances of the cement paste mixtures. Regarding the behaviors of the admixtures in the cementitious systems, an optimal admixture side chain molecular weight is proposed.     

掺矿物掺合料混凝土抗氯离子渗透性龄期研究

采用ASTM C1202标准测试了分别掺有粉煤灰、矿渣、硅灰的混凝土28 d和91 d的6 h电通量并测试了7 d,28 d,91 d抗压强度,分析了矿物掺合料对6 h电通量的影响规律以及强度增进率和电通量变化率之间的关系,为合理确定矿物掺合料混凝土抗氯离子渗透性能测试龄期提供了依据。     

掺合料对高性能混凝土早期自收缩的影响

本文采用自制的混凝土自收缩测定仪测定了高性能混凝土早期的自收缩，研究了硅灰、磨细矿渣、磨细粉煤灰三种掺合料对高性能混凝土自收缩的影响。研究结果表明：硅灰和磨细矿渣增大了高性能混凝土3d前的自收缩值，而磨细粉煤灰降低了高性能混凝土3d前的自收缩值。     

大掺量矿物掺合料自密实混凝土工作性能研究

分别采用粉煤灰单掺(0～40%)、矿粉单掺(0～40%)及二者复掺(总掺量40%)作为矿物掺合料等量替代水泥,研究大掺量矿物掺合料对自密实混凝土工作性能的影响。结果表明,当粉煤灰掺量为30%时,浆体的流动度最大;当矿粉掺量为10%时,浆体的流动度最大;粉煤灰和矿粉的掺入都会使自密实混凝土浆体包裹性能更好,同时浆体稠度提高,增加流动的阻力,单掺粉煤灰30%,单掺矿粉10%分别能达到自密实混凝土流动性能最佳状态;30%粉煤灰+10%矿粉复掺时,自密实混凝土的流动性能达到最佳状态。     

石灰石粉作为矿物掺合料对水泥胶砂性能的影响研究

本文以石灰石粉等量替代水泥、等量替代粉煤灰或矿渣粉,试验研究了石灰石粉对水泥胶砂流动度和强度的影响。试验结果表明:作为掺合料在砂浆中掺入10%~30%数量的石灰石粉是完全可行的,与单掺粉煤灰相比,石灰石粉与粉煤灰复掺作为掺合料的效果较好;而与矿渣粉相比,石灰石粉与矿渣粉复掺作为掺合料的效果较差。     

矿物掺合料对高性能混凝土断裂性能影响的试验研究

通过带缺口高性能混凝土小梁的三点弯曲断裂试验,研究了不同掺量的矿物掺合料粉煤灰、硅粉对高性能混凝土断裂性能的影响。根据试验得到的荷载-挠度曲线和荷载-裂缝嘴张开位移曲线,运用虚拟裂缝模型并结合线弹性断裂力学理论,计算了起裂韧度、失稳韧度、断裂能等断裂性能评价指标。试验表明:高性能混凝土断裂性能随活性矿物掺合料掺量的逐渐增大呈先增大后减小的趋势。     

偏高岭土作混凝土掺和料的应用性能研究

高岭土在经700℃~800℃热处理得到新型高活性混凝土偏高岭土(Metakaolin)矿物掺和料,所配制的混凝土具有良好的力学性能和耐久性能。本文详细介绍了MK掺和料的火山灰特征及在混凝土中的应用机理,以及国内外偏高岭土的研究现状和应用前景。     

高效活性矿物掺料与混凝土的高性能化(续)

笔者论述了高效活性矿物掺料在混凝土高性能化进程中的重大意义 ,阐明了高效活性矿物掺料对混凝土的增强效应、填充效应、增塑效应、削减温峰效应、改善耐久性效应的机理 ,说明了活性矿物掺料的分类以及其质量的影响因素 ,阐述了活性矿物掺料的掺入方式 ,比较了活性的各种评定方法 ,介绍了蒲心诚提出的活性矿物掺料在混凝土中的火山灰效应数值分析新方法