Novel coated graphite electrode for the selective determination of Gd(III) in rocks and waste water samples

A novel gadolinium selective coated graphite electrode based on 2,6-bis-[1-{N-cyanopropyl,N-(2-methylpridyl)}aminoethyl]pyridine [P] is described. The best performance was exhibited by the electrode having membrane composition P:NaTPB:PVC:NPOE as 8:4:30:58 (%, w/w). The electrode demonstrates excellent potentiometric characteristics towards gadolinium ion over several interfering ions. The electrode exhibited a Nernstian response to Gd³⁺ ion over a wide concentration range 2.8 × 10⁻⁷ to 5.0 × 10⁻² M with a detection limit (6.3 ± 0.1) × 10⁻⁸ M and slope 19.6 ± 0.1 mV decade⁻¹ of a_Gd³⁺. Furthermore, it showed a fast response time (12 s) and can be used for 2.5 months without significant divergence in its characteristics. Noticeably, the electrode can tolerate the concentration of different surfactants up to 1.0 × 10⁻⁴ M and can be used successfully in 30% (v/v) ethanol media and 10% (v/v) methanol and acetonitrile water mixture. The useful pH range of this sensor is 2.0 to 8.0. It is sufficiently selective and can be used for the determination of Gd³⁺ ions in waste water and rock samples. It also serves as a good indicator in the potentiometric titration of GdCl₃ with EDTA.     

Thermal and chemical stability of Cu–Zn–Cr-LDHs prepared by accelerated carbonation

Layered double hydroxides Cu_xZn_6 − xCr₂(OH)₁₆(CO₃)·4H₂O with different molar ratios of Cu/Zn/Cr were synthesized by accelerated carbonation. The products were characterized by XRD, SEM, FT-IR and TG-DTG-DSC-MS. The chemical stability was tested by the modified Toxicity Characteristic Leaching Procedure (TCLP). The results showed that the products were the mixture of Cu_xZn_6 − xCr₂(OH)₁₆(CO₃)·4H₂O and (CuZn)₂(CO₃)(OH)₂, with similar thermal behavior. All products were chemically stable with reduced leaching at pH > 6 (Cu²⁺, Zn²⁺) or > 5 (Cr³⁺).     

Electrochemistry of thulium on inert electrodes and electrochemical formation of a Tm–Al alloy from molten chlorides

The electrochemical behaviour of TmCl₃ solutions was studied in the eutectic LiCl–KCl in the temperature range 673–823 K using inert and reactive electrodes, i.e. W and Al, respectively.On an inert electrode, Tm(III) ions are reduced to metallic thulium through two consecutive steps:

Tm(III) + 1e ↔ Tm(II) and Tm(II) + 2e ↔ Tm(0)

The electroreduction of Tm(III) to Tm(II) was found to be quasi-reversible. The intrinsic rate constant of charge transfer, k⁰, as well as of the charge transfer coefficient, α, have been calculated by simulation of the cyclic voltammograms and logarithmic analysis of the convoluted curves. Electrocrystallization of thulium plays an important role in the electrodeposition process, being the nucleation mode affected by temperature.The diffusion coefficients of Tm(III) and Tm(II) ions have been found to be equal. The validity of the Arrhenius law was verified by plotting the variation of the logarithm of the diffusion coefficients vs. 1/T.The electrode reactions of Tm(III) solutions at an Al electrode were also investigated. The results showed that for the extraction of thulium from molten chlorides, the use of a reactive electrode made of aluminium leading to Al–Tm alloys seems to be a pertinent route.Potentiometric titrations of Tm(III) solutions with oxide donors, using a ytria stabilized zirconia electrode “YSZE” as a pO²⁻ indicator electrode, have shown the formation of thulium oxychloride and thulium oxide and their corresponding solubility products have been determined at 723 K (pk_s(TmOCl) = 8.0 ± 0.3 pk_s(Tm₂O₃) = 18.8 ± 0.7).     

La(1−x)SrxCo1−yFeyO3 perovskites prepared by sol–gel method: Characterization and relationships with catalytic properties for total oxidation of toluene

La_(1−x)Sr_xCo_(1−y)Fe_yO₃ samples have been prepared by sol–gel method using EDTA and citric acid as complexing agents. For the first time, Raman mappings were achieved on this type of samples especially to look for traces of Co₃O₄ that can be present as additional phase and not detect by XRD. The prepared samples were pure perovskites with good structural homogeneity. All these perovskites were very active for total oxidation of toluene above 200 °C. The ageing procedure used indicated good thermal stability of the samples. A strong improvement of catalytic properties was obtained substituting 30% of La³⁺ by Sr²⁺ cations and a slight additional improvement was observed substituting 20% of cobalt by iron. Hence, the optimized composition was La_0.7Sr_0.3Co_0.8Fe_0.2O₃. The samples were also characterized by BET measurements, SEM and XRD techniques. Iron oxidation states were determined by Mössbauer spectroscopy. Cobalt oxidation states and the amount of O⁻ electrophilic species were analyzed from XPS achieved after treatment without re-exposition to ambient air. Textural characterization revealed a strong increase in the specific surface area and a complete change of the shape of primary particles substituting La³⁺ by Sr²⁺. The strong lowering of the temperature at conversion 20% for the La_0.7Sr_0.3Co_(1−y)Fe_yO₃ samples can be explained by these changes. X photoelectron spectra obtained with our procedure evidenced very high amount of O⁻ electrophilic species for the La_0.7Sr_0.3Co_(1−y)Fe_yO₃ samples. These species able to activate hydrocarbons could be the active sites. The partial substitution of cobalt by iron has only a limited effect on the textural properties and the amount of O⁻ species. However, Raman spectroscopy revealed a strong dynamic structural distortion by Jahn–Teller effect and Mössbauer spectroscopy evidenced the presence of Fe⁴⁺ cations in the iron containing samples. These structural modifications could improve the reactivity of the active sites explaining the better specific activity rate of the La_0.7Sr_0.3Co_0.8Fe_0.2O₃ sample. Finally, an additional improvement of catalytic properties was obtained by the addition of 5% of cobalt cations in the solution of preparation. As evidenced by Raman mappings and TEM images, this method of preparation allowed to well-dispersed small Co₃O₄ particles that are very efficient for total oxidation of toluene with good thermal stability contrary to bulk Co₃O₄.     

Synthesis of onion-like mesoporous silica from sodium silicate in the presence of α,ω-diamine surfactant

Mesoporous silicas with vesicular and onion-like morphologies were assembled through hydrogen-bonding pathway from sodium silicate as silica source and electrically neutral α,ω-diamine, Jeffamine D2000 surfactant (H₂NCH(CH₃)CH₂[OCH₂CH(CH₃)]₃₃NH₂) as template in aqueous media at different synthesis temperatures (25, 60 and 100 °C). Assembling the material at 100 °C afforded onion-like core shell mesoporous silica, while at relatively lower temperature, e.g. 25 and 60 °C, multilamellar vesicles were obtained. Mesoporous silica with onion-like morphology was also obtained by a two-step synthesis involving an aging period of 20 h at room temperature followed by a hydrothermal stage (1–12 h) at 100 °C. The heavily cross-linked (Q⁴/Q³ ratio of 4.43) onion-like mesophase silica exhibited high hydrothermal stability. The BET surface area, pore volume and KJS (Kruk-Jaroniec-Sayari) pore diameter of the onion-like mesoporous silica were found to be 464 m² g⁻¹, 1.16 m³ g⁻¹ and 7.2 nm, respectively.     

Electrical properties of V2O5–WO3/TiO2 EUROCAT catalysts evidence for redox process in selective catalytic reduction (SCR) deNOx reaction

Electrical conductivity measurements on EUROCAT V₂O₅–WO₃/TiO₂ catalyst and on its precursor without vanadia were performed at 300°C under pure oxygen to characterize the samples, under NO and under NH₃ to determine the mode of reactivity of these reactants and under two reaction mixtures ((i) 2000 ppm NO + 2000 ppm NH₃ without O₂, and (ii) 2000 ppm NO + 2000 ppm NH₃ + 500 ppm O₂) to put in evidence redox processes in SCR deNO_x reaction.It was first demonstrated that titania support contains certain amounts of dissolved W⁶⁺ and V⁵⁺ ions, whose dissolution in the lattice of titania creates an n-type doping effect. Electrical conductivity revealed that the so-called reference pure titania monolith was highly doped by heterovalent cations whose valency was higher than +4. Subsequent chemical analyses revealed that so-called pure titania reference catalyst was actually the WO₃/TiO₂ precursor of V₂O₅–WO₃/TiO₂ EUROCAT catalyst. It contained an average amount of 0.37 at.% W⁶⁺dissolved in titania, i.e. 1.07 × 10²⁰ W⁶⁺ cations dissolved/cm³ of titania. For the fresh catalyst, the mean amounts of W⁶⁺ and V⁵⁺ ions dissolved in titania were found to be equal to 1.07 × 10²⁰ and 4.47 × 10²⁰ cm⁻³, respectively. For the used catalyst, the mean amounts of W⁶⁺ and V⁵⁺ ions dissolved were found to be equal to 1.07 × 10²⁰ and 7.42 × 10²⁰ cm⁻³, respectively. Since fresh and used catalysts have similar compositions and similar catalytic behaviours, the only manifestation of ageing was a supplementary progressive dissolution of 2.9 × 10²⁰ additional V⁵⁺ cations in titania.After a prompt removal of oxygen, it appeared that NO alone has an electron acceptor character, linked to its possible ionosorption as NO⁻ and to the filling of anionic vacancies, mostly present on vanadia. Ammonia had a strong reducing behaviour with the formation of singly ionized vacancies. A subsequent introduction of NO indicated a donor character of this molecule, in opposition to its first adsorption. This was ascribed to its reaction with previously adsorbed ammonia strongly bound to acidic sites. Under NO + NH₃ reaction mixture in the absence of oxygen, the increase of electrical conductivity was ascribed to the formation of anionic vacancies, mainly on vanadia, created by dehydroxylation and dehydration of the surface. These anionic vacancies were initially subsequently filled by the oxygen atom of NO. N^o atoms, resulting from the dissociation of NO and from ammonia dehydrogenation, recombined into dinitrogen molecules. The reaction corresponded to

Full-size image

. In the presence of oxygen, NO did not exhibit anymore its electron acceptor character, since the filling of anionic vacancies was performed by oxygen from the gas phase. NO reacted directly with ammonia strongly bound on acidic sites. A tentative redox mechanism was proposed for both cases.     

Phase separation temperatures in the polystyrene—poly(α-methyl styrene)—methylcyclohexane system

The phase separation temperatures (PST) in the ternary system polystyrene (PS) (M_w = 1.75 × 10⁴ g mol⁻¹ — poly(α-methyl styrene) (PαMS) (M_w = 6.0 × 10⁴) — methylcyclohexane (MCH) and the binary systems PS-MCH and PαMS-MCH have been determined by using a He---Ne laser light-scattering apparatus over the total polymer weight fraction (W_{PS + PαMS}) range of 0.018 to 0.80 and various polymer blend ratios. The PST determined at a scattering angle of 0° agreed with those at 90° for the binary systems over polymer concentrations of 0.1 to 0.7 and for the ternary over W_{PS + PαMS} of higher than 0.3. Deviations of the PST determined at an angle of 90° from those at 0° were observed in the ternary system when W_{PS + PαMS} was lower than 0.3. Two phase separation temperatures, at which the intensity scattered from zero angle changed discontinuously, are observed at concentrations lower than W_{PS + PαMS} = 0.042 in the ternary system. The PST in the ternary system decreases monotonically with increasing W_{PS + PαMS} over 0.3 to 0.7. The phase diagram for the PS-PαMS-MCH system at W_{PS + PαMS} = 0.8 is characterized by a maximum PST around − 14°C.     

Highly oriented diamond growth on SixGe1−x (100) thin films

Highly oriented (100) diamond films have been successfully grown on Si_xGe_1−x (100) thin films by bias enhanced nucleation (BEN) in microwave plasma chemical vapor deposition (MPCVD) system. Raman spectra show the 1332 cm⁻¹ peak which proves the formation of diamond. Diamond nucleation density on Si_xGe_1−x substrate estimated by scanning electron microscopy is higher than 10⁹ cm⁻². The interface between diamond and Si_xGe_1−x substrate was characterized by transmission electron microscopy (TEM). About 20 nm decrease in thickness of the Si_xGe_1−x film was observed after bias enhanced nucleation step. TEM shows the existence of silicon carbide and heteroepitaxial diamond grains grown on Si_xGe_1−x substrate. Characterization from high-resolution TEM on the specimen of short time deposition reveals that a number of epitaxial diamond grains were directly nucleated on Si_xGe_1−x with {111} interplanar spacing ratio of diamond and Si_xGe_1−x of 2:3. The diamond nucleation is found to be preferred on the ridge position of the rough substrate surface. Diamond {100} facets were quickly developed in the early stage of growth.     

气溶胶溶剂萃取技术制备β-谷甾醇亚微粒

The submicroparticles of β-sitosterol were produced by using an aerosol solvent extraction system (ASES) and characterized by scanning electronic microscope (SEM), X-ray diffraction (XRD), and Fourier transform infrared (FT-IR) analysis. The effects of operational parameters including pressure, temperature, solution concentration, and ratio of flow rate (CO2/solution, r) on particle size (PS), yield, and morphology were investigated. The results showed that microparticles of β-sitosterol (less than 1000 nm size and larger than 70% yield) could be obtained at 10-15 MPa, 35-50°C, 15 mg•ml－1, 10/1(r); β-sitosterol particles were found to occur as three mophologies: flakes, rods, and spheres by varying ratio of flow rate or solution concentration. In contrast, the crystallinity of β-sitosterol decreased, whereas its molecular structure remained almost unchanged after being ASES-treated. Therefore, ASES was an effective method to produce submicroparticles of β-sitosterol.     

Catalytic reduction of NH4NO3 by NO: Effects of solid acids and implications for low temperature DeNOx processes

Ammonium nitrate is thermally stable below 250 °C and could potentially deactivate low temperature NO_x reduction catalysts by blocking active sites. It is shown that NO reduces neat NH₄NO₃ above its 170 °C melting point, while acidic solids catalyze this reaction even at temperatures below 100 °C. NO₂, a product of the reduction, can dimerize and then dissociate in molten NH₄NO₃ to NO⁺ + NO₃⁻, and may be stabilized within the melt as either an adduct or as HNO₂ formed from the hydrolysis of NO⁺ or N₂O₄. The other product of reduction, NH₄NO₂, readily decomposes at ≤100 °C to N₂ and H₂O, the desired end products of DeNO_x catalysis. A mechanism for the acid catalyzed reduction of NH₄NO₃ by NO is proposed, with HNO₃ as an intermediate. These findings indicate that the use of acidic catalysts or promoters in DeNO_x systems could help mitigate catalyst deactivation at low operating temperatures (<150 °C).     

Highly efficient complete oxidation of dilute benzene over ultrafine Cu0.1Ce0.5Zr0.4O2−δ catalyst in a fluidized bed reactor

Ultrafine Cu_0.1Ce_0.5Zr_0.4O_2−δ catalyst operated in a fluidized bed reactor was found to be very effective for complete oxidation of dilute benzene in air. The complete conversion of benzene could be achieved at reaction temperature as low as 220 °C. The mechanism of benzene oxidation over the Cu_0.1Ce_0.5Zr_0.4O_2−δ catalyst was investigated by conducting pulse reaction of pure benzene in the absence of O₂ over the catalyst and the results indicated the involvement of lattice oxygen from the catalyst in benzene oxidation.     

High temperature SrCe0.9Eu0.1O3−δ proton conducting membrane reactor for H2 production using the water–gas shift reaction

The water–gas shift (WGS) reaction is used to shift the CO/H₂ ratio prior to Fischer–Tropsch synthesis and/or to increase H₂ yield. A WGS membrane reactor was developed using a mixed protonic–electronic conducting SrCe_0.9Eu_0.1O_3−δ membrane coated on a Ni–SrCeO_3−δ support. The membrane reactor overcomes the thermodynamic equilibrium limitations. A 46% increase in CO conversion and total H₂ yield was achieved at 900 °C under 3% CO and 6% H₂O, resulting in a 92% single pass H₂ production yield and 32% single pass yield of pure permeated H₂.     

Structure and magnetic properties of Fe1−xCox nanowires in self-assembled arrays

Fe_1−xCo_x nanowires in self-assembled arrays with varying compositions were produced by the template-assisted pulsed electrochemical deposition method. The structural and magnetic properties of the arrays were investigated using several experimental techniques. TEM analyses indicated that the nanowires were regular, uniform, 8 μm in length and 50 nm in diameter. The results of X-ray diffraction indicated that the body-centered-cubic (bcc) (α), face-centered-cubic (fcc) (γ), and hexagonal-close-packed (hcp) () Fe–Co phases appeared in different compositions. Magnetic measurements showed that the coercivity and squareness of the hysteresis loops of the Fe_1−xCo_x changed with their compositions, which may be attributable to shape anisotropy. The room temperature ⁵⁷Fe Mössbauer spectra of the arrays of the Fe_1−xCo_x nanowires revealed strong shape anisotropy.     

Thermal properties of the nitrogen-rich Ca-α-Sialons

Nitrogen-rich Ca-α-Sialon (Ca_xSi_12−2xAl_2xN₁₆ with x = 0.2, 0.4, and 0.8, 1.2 and 1.6) ceramics were prepared from the mixtures of Si₃N₄, AlN and CaH₂ powders in a hot press at 1800 °C using a pressure of 35 MPa and a holding time of 4 h, and then were investigated with respect to reaction mechanism, phase stability and oxidation resistance. In addition the sample with x = 1.6 was prepared in the temperature range 600–1800 °C using a pressure of 35 MPa and a holding time of 2 h. The α-Sialon phase was first observed at 1400 °C but the α-Si₃N₄ and AlN phases were still present at 1700 °C. Phase pure Ca-α-Sialon ceramics could not be obtained until the sintering temperature reached 1800 °C. The phase pure nitrogen-rich Ca-α-Sialon exhibited no phase transformation in the temperature range 1400–1600 °C. In general, mixed α/β-Sialon showed better oxidation resistance than pure α-Sialon in the low temperature range (1250–1325 °C), while α-Sialons with compositions located at α/β-Sialon border-line showed significant weight gains over the entire temperature range tested (1250–1400 °C). The phases formed upon oxidation were characterized by X-ray, SEM and TEM studies.     

Polymer pendant ligand chemistry, 4. Recovery of precious metal ions from strongly acidic solution with a polymer-supported o-phenylenediamine hydrochloride ligand

We report on the synthesis and reactivity of a polymer-supported o-phenylenediamine hydrochloride ligand, PS-PDHC, using macroporous 6% crosslinked polystyrene-divinylbenzene beads. The PS-PDHC ligand was found to be highly selective to AuCl₄⁻ ions in strongly acidic solutions in the presence of other precious metal ions, PdCl₄²⁻, PtCl₄²⁻, RhCl₆³⁻, and RuCl₅²⁻ (selectivity values: 2.5, Au/Pd; 7.5, Au/Pt; 7, Au/Rh; 2.2, Au/Ru) as well as other transition metal ions, Fe ³⁺, Cr³⁺, CU²⁺, Nit+, and Mn²⁺. The sorption capacity, selectivity, kinetics of removal and recovery, and solution isotherms have been determined for AuCl₄⁻ ions in competition with the above-mentioned metal ions. The relative ease of formation of the anionic complex in 0.5 M HCI, AuCl₄⁻ was thought to be the primary reason for its selective ability to bind to the PS-PDHC ligand by an anion-exchange mechanism. Therefore, the effect of the HCI concentration on the kinetics of AuCl₄⁻ ion removal from solution was also investigated to clearly show that raising the pH from 0 to 5 caused a dramatic decrease in rate. The AuCl₄⁻ ion can be recovered quantitatively from the PS-PDHC beads using a 5% thiourea solution in 0.1 M HCl, allowing the polymer-supported ligand to be reused.     

Solvothermal synthesis of a novel mixed valence Cu(I)/Cu(II) complex containing sulphate, malate and 4,4-bipyridine, [CuCu2(mal)(SO4)(bpy)2 · H2O]n. Unique binding mode of the malate anion

The reaction of CuSO₄ · 5H₂O with 4,4^′-bipyridine and malic acid at 140 °C under solvothermal conditions afforded a mixed valence three-dimensional coordination polymer [Cu^ICu^II₂(mal)(SO₄)(bpy)₂ · H₂O]_n, (1). The building unit consists of a Cu²⁺-dimer in which copper centers are bridged by malate and sulphate anions. SO₄²⁻ anion further connects dimeric unit with the Cu¹⁺ center. Building units are linked by 4,4^′-bipyridine ligands to form double chains, that are interconnected into 3D network through additional sulphate bridge.     

Origins of the Rio Capim kaolinites (northern Brazil) revealed by δO and δD analyses

Deuterium (δD) and oxygen (δ¹⁸O) isotope data from the Rio Capim kaolin, northern Brazil, were combined with optical studies in order to better understand the genesis and evolution of the kaolinites. The results show that δ¹⁸O values from a lower soft kaolin unit range from 6.0‰ to 19.2‰ for Ka (size ranging from 1 to 3 μm) and Kb (size ranging from 10 to 30 μm) kaolinites, and from 15.4‰ to 24.9‰ for Kc (size < 200 nm) kaolinites. The δD values range from − 63.1‰ to 79.5‰ for the Ka + Kb kaolinites, and from − 68.8‰ to − 244.35‰ for the Kc kaolinites. An upper semi flint kaolin unit, dominated by Kc kaolinites, displays δ¹⁸O and δD values ranging from 15.1‰ to 21.8‰, and − 71.3‰ to − 87.4‰, respectively. Based on these data, and on the δ¹⁸O and δD values obtained for the surface meteoric water and groundwater, it can be concluded that the kaolinites are not in equilibrium with the modern weathering environment, but they reflect isotopic compositions of the formation time, probably due to the interaction with fossil groundwater. However, mineralogical contaminations derived from replacements of framework grains also had great influence in the isotopic composition of these kaolinites. In addition, the isotope values of the Kc kaolinites from the semi-flint kaolin unit is variable, which is due to the presence of Kc kaolinites of different origins, including kaolinites derived from the underlying soft kaolin unit, kaolinites formed during different phases of paleoweathering, as well as later phases of coarse-grained kaolinites formed along fractures. Due to these complexities, binary diagrams contrasting δ¹⁸O and δD values, worldwide applied for distinguishing supergenic from hypogenic kaolinites, as well as those formed under weathering conditions, can not be applied to interpret the origin of the kaolinites in the Rio Capim Kaolin.     

The role of particle size on the electrochemical properties at 25 and at 55 °C of the LiCr0.2Ni0.4Mn1.4O4 spinel as 5 V-cathode materials for lithium-ion batteries

The role of the particle size on the electrochemical properties at 25 and at 55 °C of the LiCr_0.2Ni_0.4Mn_1.4O₄ spinel synthesized by combustion method has been determined. Samples with different particle size were obtained by heating the raw spinel from 700 to 1100 °C, for 1 h in air. X-ray diffraction patterns revealed that all the prepared materials are single-phase spinels. The main effect of the thermal treatment is the remarkable increase of the particles size from 60 to 3000 nm as determined by transmission electron microscopy. The electrochemical properties were determined at high discharge currents (1C rate) in two-electrode Li-cells. At 25 and at 55 °C, in spite of the great differences in particle size, the discharge capacity drained by all samples is similar (Q_dch ≈ 135 mAh g⁻¹). Instead, the cycling performances strongly change with the particle size. The spinels with Φ > 500 nm show better cycling stability at 25 and at 55 °C than those with Φ < 500 nm. The samples heated at 1000 and 1100 °C, with high potential (E ≈ 4.7 V), elevate capacity (Q ≈ 135 mAh g⁻¹), and remarkable cycling performances (capacity retention after 250 cycles >96%) are very attractive materials as 5V-cathodes for high-energy Li-ion batteries.     

Study of IrxRu1−xO2 oxides as anodic electrocatalysts for solid polymer electrolyte water electrolysis

Electrocatalysts of the general formula Ir_xRu_1−xO₂ were prepared using Adams’ fusion method. The crystallite characterization was examined via XRD, and the electrochemical properties were examined via cyclic voltammetry (CV) in, linear sweep voltammetry (LSV) and chronopotentiometry measurements in 0.5 M H₂SO₄. The electrocatalysts were applied to a membrane electrode assembly (MEA) and studied in situ in an electrolysis cell through electrochemical impedance spectroscopy (EIS) and stationary current density–potential relations were investigated. The Ir_xRu_1−xO₂ (x = 0.2, 0.4, 0.6) compounds were found to be more active than pure IrO₂ and more stable than pure RuO₂. The most active electrocatalyst obtained had a composition of Ir_0.2Ru_0.8O₂. With an Ir_0.2Ru_0.8O₂ anode, a 28.4% Pt/C cathode and the total noble metal loading of 1.7 mg cm⁻², the potential of water electrolysis was 1.622 V at 1 A cm⁻² and 80 °C.     

Effect of sintering temperature on varistor properties and aging characteristics of ZnO–V2O5–MnO2 ceramics

The microstructure, electrical properties, dielectric characteristics, and DC accelerated aging behavior of the ZVM-based varistors were investigated for different sintering temperatures of 800–950 °C. The microstructure of the ZVM-based ceramics consisted of mainly ZnO grain and secondary phase Zn₃(VO₄)₂, which acts as liquid-phase sintering aid. The Zn₃(VO₄)₂ has a significant effect on the sintered density, in the light of an experimental fact, which the decreases of the Zn₃(VO₄)₂ distribution with increasing sintering temperature resulted in the low sintered density. The breakdown field exhibited the highest value (17,640 V/cm) at 800 °C in the sintering temperature and the lowest value (992 V/cm) at 900 °C in the sintering temperature. The nonlinear coefficient exhibited the highest value, reaching 38 at 800 °C and the lowest value, reaching 17 at 850 °C. The varistor sintered at 900 °C exhibited not only high nonlinearity with 27.2 in nonlinear coefficient, but also the highest stability, in which %ΔE_1 mA = −0.6%, %Δα = −26.1%, and %Δ tan δ = +21.8% for DC accelerated aging stress of 0.85 E_1 mA/85 °C/24 h.