热冲压成形SAF2507 SDSS在不同溶液中耐点蚀性能

 为了研究SAF2507 SDSS热冲压成形后在不同服役环境中阴离子对耐点蚀性能的影响,对SAF2507 SDSS板材进行1 050 ℃热冲压成形,使用ZEISS-SUPRA55型扫描电镜观察微观组织并测定相组织能谱,运用动电位极化曲线、开路电位和交流阻抗谱手段研究SAF2507 SDSS在3.5%质量浓度的NaClO和卤化钠NaX(X=Cl、Br、I)溶液中的耐点蚀性能。结果表明,SAF2507 SDSS在1 050 ℃热冲压成形后微观组织良好,α/γ体积比约为1∶1,α相富铬、钼贫镍电极电位低,为阳极,γ相富镍贫铬、钼电极电位高,为阴极;在4种溶液中,耐点蚀性能从高到低为NaClO、NaCl、NaBr和NaI,NaClO溶液中点蚀坑数量最少,蚀坑小而浅,NaI溶液中点蚀坑数量最多,蚀坑大而深;ClO-对点蚀形核和生长阶段起到抑制作用,Cl-、Br-和I-只在点蚀形核阶段起到促进作用,促进作用从大到小为I-、Br-和Cl-。     

00Cr24Ni6M02N双相不锈钢优良的耐腐蚀性能

00Er24Ni6M02N双相不锈钢是具有优良的耐腐蚀性能的钢种，在正常情况下组织中有α铁奥体相和γ奥氏体相，并各占约50％。它的击破电位(Eb为+1050my)和保护电位(Ep为+950mv)都很高，使得它很难产生点蚀，即使存在点蚀坑也会被重新钝化，这在室内加速腐蚀试验和海港挂片试验中，都得到证实。它同时具有良好的耐应力腐蚀和冲涮腐蚀能力。00Cr24Ni6M02N双相不锈钢具有广泛应用前景。     

304L不锈钢焊缝在混凝土模拟孔隙液中的点蚀行为

采用动电位极化曲线、电化学阻抗谱、Mott-Schottky曲线等电化学方法研究了以308 L为焊丝的304 L不锈钢焊接接头在不同氯离子含量的混凝土模拟孔隙液中腐蚀行为和电化学规律.随Cl-增加,304 L不锈钢焊接接头的三个区域(母材、焊缝和热影响区)在混凝土模拟孔隙液中的自腐蚀电位、点蚀电位及电荷转移电阻降低,钝化膜中载流子密度和焊接接头的点蚀坑数量增加.在同浓度的腐蚀溶液中,308 L的焊缝区域耐蚀性最佳,热影响区次之,304 L基体表现出低的电荷转移电阻和高的掺杂浓度使得母材的耐蚀性最差.      

σ相对S32760超级双相不锈钢组织和性能的影响

通过对含W的S32760超级双相不锈钢不同温度时效热处理研究σ相的析出行为.用扫描电镜和透射电镜分析σ相的形貌和化学组成,并研究σ相对力学性能和耐腐蚀性能的影响.在850~1000℃之间,实验钢析出大量由Fe-Cr-Mo-W组成的具有正方结构的σ相,钢板强度和硬度高,塑性差,延伸率低于4%;1050℃时仍存在少量析出,虽然延伸率大幅度提高至31.1%,但冲击韧性离散度高,冲击功偏低;直至1080℃,σ相才能完全溶解至基体中,抗拉强度为640MPa,延伸率为35.5%,纵、横向冲击功平均值分别达到217J和110J.随时效热处理温度升高,点蚀电位提高,点蚀失重率不断下降,1080℃热处理的试样点蚀电位高达1246mV.该试样在50℃的3.5% NaCl溶液中腐蚀失重率也仅为0.005~0.007g·m-2·h-1.      

低温盐浴渗氮对Custom 465钢耐蚀及耐磨性的影响

为了提高Custom 465马氏体沉淀硬化不锈钢的耐磨性,分别在440、480和520℃对580℃时效后的样品进行了2 h的盐浴渗氮,使用显微硬度计、X射线衍射仪、电化学工作站、球盘式摩擦磨损仪、表面轮廓仪、扫描电镜等设备,研究渗氮温度对Custom 465钢表面物相、硬度、渗层显微形貌、耐蚀性及耐磨性的影响.随着渗氮温度升高,耐蚀性逐渐降低,但表面硬度增加,520℃处理后表面硬度增大到1240 HV,较未处理试样的400 HV明显上升,渗层厚度达到22μm.440℃渗氮后表面物相为氮在马氏体基体中过饱和的α'_N,点蚀电位降低约60 m V;480℃时有少量CrN相析出,引起点蚀电位降低约180 mV,同时磨损体积下降约43%;520℃时CrN相的含量明显升高,自腐蚀电位降低约70 mV,无明显的稳态钝化区,磨损体积降低82%,减磨效果明显.      

镍含量对2205双相不锈钢焊接接头的影响

采用光学显微镜观察了不同镍含量下2205双相不锈钢焊接接头的金相组织,通过点腐蚀试验测量腐蚀速率,并采用电化学工作站对焊接接头的点蚀电位进行测量.结果表明,1.2 m m厚度规格2205双相不锈钢焊接接头为铁素体加奥氏体的两相组织,点蚀坑主要出现在热影响区和焊缝.镍含量高的样品金相组织中奥氏体含量高,对应点蚀电位也要高...     

交流电流密度对X65钢在碳酸盐/碳酸氢盐溶液中腐蚀行为的影响

通过极化曲线测试、浸泡实验和表面分析技术研究了不同交流电流密度对X65钢在碳酸盐/碳酸氢盐溶液中腐蚀行为的影响.随交流电流密度的增加,钝化区宽度明显变窄,点蚀击破电位负移,维钝电流密度增大,腐蚀速率增加.在低交流电流密度下（<100 A·m-2）,维钝电流密度、点蚀程度和腐蚀速率均略增加;在高交流电流密度下（≥100 A·m-2）,维钝电流密度、点蚀程度和腐蚀速率均快速增加.      

热处理对马氏体时效不锈钢耐点蚀性能的影响

本文主要研究了00Cr15Ni6Mo2CuAl和00Cr16Ni6Mo3CuAl马氏体时效不锈钢的热处理制度与在含Cl-离子介质中耐点蚀性能的关系。结果表明:对于00Cr15～16Ni6Mo2～3CuAl马氏体时效不锈钢,随固溶温度的升高(780～1000℃),耐点蚀性能显著提高。时效强化处理使钢的耐点蚀性能有不同程度的下降,在450℃左右时效可以获得耐点蚀性能与力学性能的良好配合。点蚀主要在Laves相、σ-铁素体周围以及原始奥氏体晶界上发生。Laves相和σ-铁素体由于周围存在着贫铬、贫钼区而对点蚀敏感。在450℃和550℃时效状态,原始奥氏体晶界对点蚀的敏感性增加,这主要是由于时效相的析出、长大的缘故。     

铈对低硫铁素体不锈钢抗点蚀性能的影响

对不同铈含量低硫的铁素体不锈钢00Cr12的抗点蚀性能进行了研究,研究结果表明,随铈含量的增加,试验钢的点蚀击穿电位下降。利用扫描电镜、光镜等分析手段对试验钢的夹杂物、组织进行研究,分析此情况下试验钢的点蚀规律。研究结果表明,在低硫的情况下,铁素体不锈钢的点蚀性能与晶粒尺寸相关性较强,铈的添加可细化晶粒,导致点蚀击穿电位的下降,点蚀性能与夹杂物相关性不大。     

痕量Ga及退火工艺对高压阳极铝箔电化学性能的影响

通过开路电位—时间曲线、极化曲线和恒电位电流密度暂态曲线研究痕量Ga及退火工艺对高压阳极铝箔电化学性能的影响,在此基础上,结合光学显微镜和扫描电镜研究痕量Ga对阳极铝箔腐蚀发孔性能的影响。结果表明,退火工艺可以改变Al-44×10-6 Ga在含氯离子溶液中的电化学活性。提高退火温度(200~600℃)可促使Al-44×10-6 Ga的点蚀电位负移,500℃退火、保温1 h后,延长退火保温时间(4~12 h),点蚀电位变动很小;相对无Ga高纯铝,Ga含量为44×10-6的高纯铝在中性NaCl溶液中的开路电位向负电位方向移动约0.1~0.15 V、点蚀电位负移约0.11 V,并能在更负的电位下发生活性溶解;进而使相应的含Ga铝箔的腐蚀区面积比显著提高至96.5%,且蚀孔密度、分布均匀性提高,即痕量Ga改善了阳极铝箔在环保型盐酸-硫酸体系中的腐蚀发孔性能。     

热处理工艺对15-5PH沉淀硬化不锈钢的力学性能与耐蚀性的影响

 研究了热处理工艺对15-5PH沉淀硬化不锈钢力学性能与耐蚀性的影响,并观察了钢中的强化相。结果表明,随着时效温度的升高和保温时间的延长钢的强度逐渐下降,塑性及冲击吸收功逐渐升高,这是由于逆转变奥氏体体积分数随温度升高而增加所造成的;随着时效温度升高钢的耐点腐蚀性能逐渐下降,在580和600 ℃时耐蚀性最差,在480 ℃时效钢的耐点腐蚀性能最佳且具有最高的强度,钢中主要的强化相是具有面心立方结构的富铜相。     

低温贝氏体转变对中碳钢韧性的影响

摘要：沉淀硬化钢中纳米富Cu相的析出，使微应变（α）发生改变，这不仅影响力学性能，也对腐蚀性能产生作用。为了探索α对腐蚀性能和力学性能的影响规律，通过XRD谱型分析，对商用钢LJ338ESR 在300～600℃不同时间时效析出富铜纳米相后的α、硬度和电荷转移电阻（Rf）进行了研究。结果表明，300～450℃时效，8h前α值随时效时间延长而升高，8h后由于析出相与基体失去共格，α随着时效时间延长而降低；硬度与α变化相似。600℃时效，α在时效2h达到峰值，这归因于共格微应变和逆变奥氏体两种相反因素的共同影响；600℃逆变奥氏体生成，使硬度变化较小。析出相与基体保持共格时，Rf和α随时效时间的变化呈良好的反比关系，即Rf随α的增大而减小。     

LJ338ESR钢富铜纳米相引起的微应变、硬度和耐蚀性变化

摘要：沉淀硬化钢中纳米富Cu相的析出，使微应变（α）发生改变，这不仅影响力学性能，也对腐蚀性能产生作用。为了探索α对腐蚀性能和力学性能的影响规律，通过XRD谱型分析，对商用钢LJ338ESR 在300～600℃不同时间时效析出富铜纳米相后的α、硬度和电荷转移电阻（Rf）进行了研究。结果表明，300～450℃时效，8h前α值随时效时间延长而升高，8h后由于析出相与基体失去共格，α随着时效时间延长而降低；硬度与α变化相似。600℃时效，α在时效2h达到峰值，这归因于共格微应变和逆变奥氏体两种相反因素的共同影响；600℃逆变奥氏体生成，使硬度变化较小。析出相与基体保持共格时，Rf和α随时效时间的变化呈良好的反比关系，即Rf随α的增大而减小。     

Phase Transformation and Its Effects on Mechanical Properties and Pitting Corrosion Resistance of 2205 Duplex Stainless Steel

The effects of phase transformation on mechanical properties and pitting corrosion of 2205 duplex stainless steel were investigated. The amount of σ phase in the test specimen varied up to a maximum of 6% by thermal treatment at 850 ℃ for up to 60 min. The results showed that σ phase markedly increased the hardness and decreased the impact toughness of the test steel. But the increasing tendency of the ultimate tensile strength and the yield strength was not obvious, while the total elongation abruptly decreased with the aging time from 5 to 60 min. SEM impact microfractograph analysis revealed that the types of impact fracture changed from ductile mode to transcrystalline mode when the specimens were aged for 5-60 min. Furthermore, the extent of pitting potential reducing was found to be strongly temperature dependent, more pronounced at the higher temperature. During the incubation period of σ phase nucleation, the pitting corrosion test temperature and the aging time had collaborative effects on evidently displacing the pitting potential towards less noble values. After 15 min, the higher temperature contributed more to decreasing the pitting potential than the aging time.     

核电主管道铸造不锈钢的热老化脆化

为了研究中国核电主管道铸造不锈钢Z3CN20-09M的热老化,在300、350和400℃下,对Z3CN20-09M进行了长达30000h的加速热老化实验.对不同热老化时间下的样品进行了冲击性能和铁素体纳米硬度测定.以夏比冲击功作为热老化脆化参量,利用拟合的方法得出该材料的热老化激活能为51.962kJ·mol-1.通过热老化因子P得出了用夏比冲击功表示的热老化脆化动力学公式.利用热老化激活能和热老化动力学公式预测了Z3CN20-09M在实际运行温度下服役40a内的夏比冲击功和铁素体显微硬度变化.预测结果表明在运行5a内是该材料韧性迅速下降的时期,随后的运行过程中下降过程趋缓.      

Chi Phase after Short-term Aging and Corrosion Behavior in 2205 Duplex Stainless Steel

Correlation between pitting corrosion behavior and chi( χ )phase formed after a short-term aging(5,10 and 15 min)at 850 ℃ of 2205 duplex stainless steel(DSS)was investigated using potentiodynamic polarization tests,optical microscopy,and scanning electron microscopy equipped with energy-dispersive spectrum system.Results showed that after aging for 5min,the χ phase initially precipitated at ferrite grain boundaries,developed and then became linked with prolonging aging time.The χ phase was rich in Cr and Mo,resulting in formation of depleted zones nearby.The χ phase could reduce corrosion resistance of DSS and slightly influence its stability,but the specimens still displayed the capacity for repassivation.Some lines of evidence showed that stable pitting corrosion initiated at the boundaries of precipitates.The χ phase was selectively corroded during the first stage of corrosion and then the depleted zones nearby were attacked.In addition,the grain size and volume of precipitates also affected pit nucleation and progress,and suitable size and distribution of χ phase could aggravate pit initiation at precipitate boundaries.The χ phase with considerably low volume fraction and small size was not sensitive position for pit initiation.     

温度对Z3CN20-09M不锈钢在含氯高温水中应力腐蚀行为的影响

研究了温度对核电用Z3CN20-09M不锈钢在含Cl的高温高压水中的应力腐蚀开裂行为的影响.材料的应力腐蚀开裂敏感性变化趋势与试验温度变化趋势并不一致.320℃时材料的应力腐蚀开裂敏感性最高,290℃时为最低,250℃时开裂敏感性介于两者之间.250℃和320℃条件下腐蚀后试样表面形成了内部致密、外部疏松的双层氧化膜,而在290℃条件下腐蚀后试样形成的是致密的单层氧化膜.大多数点蚀坑产生于铁素体相.应力腐蚀裂纹优先在点蚀坑底部或相界面形核,并倾向于沿相界面或向铁素体内部扩展.铁素体/奥氏体界面对应力腐蚀裂纹的作用取决于裂纹面与相界面的取向关系.当裂纹扩展方向平行于相界面时,裂纹易沿着相界扩展;当裂纹扩展方向垂直于相界面时,相界面对裂纹扩展起阻碍作用.      

445M铁素体不锈钢缝隙腐蚀性能的研究

研究了445M铁素体不锈钢(%:0.004～0.005C、22.24～22.29Cr、1.10～1.65Mo、0.015～0.016P、0.003～0.004S、0.012～0.016N、0.22～0.38Ti)和316L奥氏体不锈钢(%:0.022C、16.80Cr、10.19Ni、2.02Mo、0.025P、0.001S、0.046N)在40～60℃氯离子浓度(250～5 000)×10^-6的氯化钠溶液的缝隙腐蚀性能。结果表明,445M铁素体不锈钢的耐缝隙腐蚀性能优于316L奥氏体不锈钢;当445M钢中的Mo含量由1.10%提高至1.65%时,钢的耐缝隙腐蚀性能明显提高,表明点蚀当量Cr+3.3Mo是衡量不锈钢耐点蚀和耐缝隙腐蚀的重要指标。     

Thermal aging effect on 2205 duplex stainless steel

The effect of isothermal aging treatment on the mechanical and corrosion properties of 2205 duplex stainless steel was investigated by means of impact toughness test and micro-hardness measurement in combination with the critical pitting temperature( CPT) technique. The corresponding fractography of the steel was then observed after the impact toughness test. The results demonstrated that,at the critical temperature for precipitation of the sigma( σ) phase,e. g.,850 ℃,the impact toughness decreased rapidly and the micro-hardness increased gradually with increasing aging time. The CPT decreased from 61 to 15 ℃ as the aging time increased from 4 min to 8 h. In addition,optical microscopy,transmission electron microscope( TEM) and X-ray diffraction studies showed that the ferrite in the steel transformed into secondary austenite and σ phase.     

时效处理对超级双相不锈钢00Cr29Ni6Mo2N组织和耐点蚀性的影响

采用扫描电镜和X射线能谱仪研究了00Cr29Ni6Mo2N超级双相不锈钢1080℃30 min固溶+650～1000℃60 min时效后的显微组织.试验结果表明,在奥氏体和铁素体相界面上析出了Cr2N和σ相两种析出相,同时发现少量的Cr2N在铁素体相内.Cr2N析出优先于σ相,增加时效温度和时间对Cr2N的析出量没有显...