外加电位对奥氏体不锈钢应力腐蚀与腐蚀疲劳交互作用的影响SCIEI

本文研究了0Cr18Ni9Ti奥氏体不锈钢在42%沸腾MgCl_2中,在低频,高平均应力循环载荷下的环境敏感断裂行为,研究了应力腐蚀疲劳与应力腐蚀在裂纹扩展规律及断口形貌上的差别与联系。从断裂特征上分析了应力腐蚀与腐蚀疲劳的交互作用,并着重研究了外加极化电位对这种交互作用的影响。     

7050铝合金晶界偏析与应力腐蚀,腐蚀疲劳行为的研究

研究了不同时效状态的７０５０铝合金晶界偏析与应力腐蚀开裂及湿空气环境下疲劳裂纹扩展的关系，并采用修正的化学方法计算了晶界偏析对断裂应力的影响。结果表明：随着时效程度的增加，晶界上Ｍｇ偏析浓度减小，捕获Ｈ的能力减弱，晶界断裂应力的百分数随之下降，因而合金的抗应力腐蚀和腐蚀疲劳性能提高。     

SCF FEATURE OF AUSTENITIC STAINLESS STEEL IN BOILING MgCl_2SOLUTION

Corrosion fatigue under the load of low frequency and bigh mean stress has been generallydefined as stress corrosion fatigue(SCF).It is a specific failure process due to the inter-action between stress corrosion cracking(SCC) and corrsion fatigue(CF),the effectsof which on fracture characteristics,including crack initiation and propagation.servicelife and cracking mode have not been investigated systematically.The purpose of this pa-per was to study the environment-sensitive fracture behaviour of OCr18Ni9Ti austeniticstainless steel under the load of different fiequencies and high mean stress in boilingMgCl_2 solution.The interaction between SCC and CF would be emphasized.     

奥氏体不锈钢在MgCl2介质中的应力腐蚀疲劳特征

本文研究了力学因素对0Cr18Ni9Ti奥氏体不锈钢在MgCl_2水溶液中应力腐蚀(SCC)和腐蚀疲劳(CF)交互作用的影响。研究了应力腐蚀疲劳(SCF)在裂纹扩展规律及断口形貌上的特征。结果表明:任何促使裂尖应变速率提高的力学变量,都有可能使SCF断口形貌发生穿晶型向沿晶型的转化。     

316L不锈钢在模拟人体液内腐蚀疲劳裂纹萌生和扩展过程中应力的作用

探讨应力在316L不锈钢腐蚀疲劳过程中的作用。应力降低了不锈钢的点蚀电位,促进了腐蚀疲劳裂纹的萌生和扩展。初始疲劳裂纹在点蚀孔中的晶界上萌生,在应力的作用下,裂纹由沿晶变为穿晶扩展,并在断口上产生二次裂纹和疲劳辉纹。     

CORROSION FATIGUE BEHAVIOR OF STAINLESS STEEL 3RE60 IN 3.5% SODIUM CHLORIDE SOLUTION

The corrosion fatigue behavior of stainless steel 3RE60 in 3.5%NaCl solution was studied at different cyclic stress levels. The results showed that both intergranular corrosion cracking and transgranular corrosion cracking initiated at the bottom of pits. The corrosion fatigue behavior of 3RE60 may be related to complex electrochemical and mechanical coupling effects between the three phases (austenite, ferrite and martensite), where martensite and ferrite were anodic in the corrosion cell and could be prone to crack under certain conditions.     

LC4高强铝合金的腐蚀性能研究

利用慢应变速率拉伸试验方法研究了LC4铝合金在空气和3．5％NaCl溶液中的应力腐蚀断裂行为；利用HB5455－90标准研究了LC4铝合金的剥蚀行为；利用HB5255－83标准研究了LC4铝合金的晶间腐蚀行为。结果表明：LC4铝合金具有应力腐蚀敏感性，应力腐蚀的断口形貌受应变速率ε的影响较大；LC4铝合金对剥蚀很敏感，对晶间腐蚀不是很敏感。     

疲劳及拉伸预形变对钝铜应力腐蚀敏感性的影响

用慢应变速率拉伸法研究了疲劳预形变以及拉伸预形变对纯钢在ＮａＮＯ２溶液中应力腐蚀敏感性的影响.结果表明,疲劳预形变（切应力幅γｐｌ＝１.２×１０－４,疲劳周次Ｎ＝８．４×１０４;以及γｐｌ＝９．４×１０－４; Ｎ＝２．４×１０４）能降低Ｃｕ单晶的应力腐蚀敏感性．随拉伸预形变量升高,纯铜多品的应力腐蚀敏感性也降低.这表明,预形变能改善纯铜的应力腐蚀性能．     

低碳钢的组织对腐蚀疲劳的影响

本文研究了两种低碳钢不同显微组织在盐水和空气中的疲劳裂纹扩展行为,发现显微组织对钢的腐蚀疲劳抗力有重要影响。还讨论了钢的腐蚀疲劳机制及断裂机制图。     

植入不锈钢腐蚀疲劳过程中的晶间腐蚀

用ＳＥＭ研究了浸在Ｈａｎｋ模拟体液中的轧态３１６Ｌ和铸态３１６Ｌ和铸态３１７Ｌ不锈钢在腐蚀疲劳期间产生的间晶腐蚀。结果表明，腐蚀疲劳初始裂纹是在腐蚀晶界上孕育产生的，在疲劳应力作用下，由沿晶扩展变为穿晶扩展；晶间腐蚀不是由碳化物析出造成晶界贫Ｃｒ产生的。而是一种非敏化晶间腐蚀。     

重型自卸车桥壳腐蚀失效分析

国产K29型重型自卸车在黄岛施工中仅经历9-12个月,有8辆车的后桥壳发生断裂.经调查、分析表明,桥壳的失效既不是应力腐蚀破裂也不是机械疲劳断裂,而是腐蚀疲劳的结果.     

EFFECTS OF HEAT TREATMENT AND ENVIRONMENT ON CRACK PROPAGATION RATE IN STEEL GC-4 UNDER CORROSION FATIGUE AND STRESS CORROSION

Comparative investigations were carried out of the effect of heat treatment regimes Jor steelGC-4(40CrMnSiMoVA)on its crack propagating rates,from corrosion fatigue,(da/dN)_(CF),or stress corrosion cracking,(da/dt)_(SCC),in media with various constituentsand pH values.Both(da/dN)_(CF) and(da/dt)_(SCC) accelerate with the increase of yield stressof the steel,yet the former is far less than the later.In comparison with media,the(da/dt)_(SCC) in distilled water is slightly greater than that in 3.5% NaCl solution,and the(da/dN)_(CF) in distilled water is far less than that in 3.5% NaCl solution.With the pH valueincreasing in 3.5% NaCl solution,the(da/dN)_(CF) lowers down and the(da/dt)_(SCC) speedsup.An explanation was also proposed with concept of the cyclic hardening and softening atcrack tip,as well as the crack closure and occluded cell effect.     

40CrNi2Si2MoVA钢的大气应力腐蚀行为

用单轴拉伸试样和预制裂纹试样研究40CrNi2Si2MoVA高强度钢在典型大气环境下的抗应力腐蚀性能.施加应力后的试样分别暴露于北京、青岛、万宁3个不同的大气试验站.研究表明:40CrNi2Si2MoVA钢的抗应力腐蚀性能取决于环境,在海洋性环境下应力腐蚀性较高.扫描电子显微镜微观分析表明裂纹起始于表面的腐蚀点,并向试样内部扩展,为沿晶开裂,有二次裂纹存在.随着应力水平的增大,二次裂纹明显增加.     

工程金属材料/零件的表面完整性及其断裂抗力

工程金属材料的力学性能取决于其显微组织结构。至于对那些由表面起裂引发宏观脆性断裂(诸如疲劳断裂、应力腐蚀与氢脆断裂等)的断裂抗力性能,则首先取决于零件的表面完整性。文中提出了狭义的表面完整性定义,介绍了与这类宏观脆性断裂抗力性能有直接关系的表面完整性参量,诸如表面显微组织结构参量、表面(层)力学性能参量、表面(层)残余应力参量以及表面应力集中参量等。表面强化工艺技术就是通过改变零件表面完整性使这类宏观脆性断裂抗力的性能获得提高。     

腐蚀疲劳裂尖材料损伤研究

金属环境断裂过程依赖于材料,应力与介质参数间的复杂交互作用,这些交互作用的澄清是实现材料断裂控制的重要基础,而裂纹尖端单元损伤过程的研究则是联接微观机制与宏观断裂规律的桥梁。通过对钝化和活化典型腐蚀体系下恒速长大腐蚀疲劳裂纹受力学与电化学参数扰动后的扩展动力学响应规律的系统研究,并结合多种其它分析手段,考察了不同腐蚀因素对裂尖材料的损伤作用机制。在实验基础上,对腐蚀导致裂纹闭合变化,裂纹扩展过载延     

腐蚀领域中人工神经网络的应用进展

人工神经网络作为人工智能的重要研究领域,是模拟 人脑行为解决问题的一种方式,受到腐蚀领域科研人员的日益重视.本文介绍了人工神经网络在大气腐蚀、海水腐蚀、土壤腐蚀、应力腐蚀、腐蚀疲劳和点蚀中应用,并阐述了其应用的特点.      

时效对SiCw/2024Al复合材料应力腐蚀开裂行为的影响

采用双悬臂梁试验方法研究了经时效处理的SiCw／2024Al复合材料在3．5％NaCl溶液中的应力腐蚀行为，用透射电子显微镜对时效处理后复合材料的微观组织形貌进行了观察与分析，用扫描电子显微镜观察应力腐蚀试样的裂纹扩展形貌．结果表明，在3种不同的时效状态下，复合材料内部的微观组织形貌发生了较大的变化，引起3种时效状态下复合材料的应力腐蚀行为发生变化，相应的裂纹尖端的微观组织形貌也出现了较大的差别．     

氢致开裂和应力腐蚀机理的前沿问题

本文对各种氢致开裂和应力腐蚀机理进行了评述。指出,把氢促进局部塑性变形和弱键理论以及氢压理论联合起来就有可能发展新的氢致开裂机理;必须深入研究阳极溶解对位错发射,增殖和运动的影响才能提出合理的阳极溶解型应力腐蚀的机理。     

晶须对铝基复合材料应力腐蚀开裂行为的影响

采用双悬臂梁试验,研究了碳化硅晶须增强纯铝基及碳化硅晶须增强2024铝基复合材料和2024铝合金在3．5％NaCl溶液中的应力腐蚀（SCC）开裂行为,探讨了晶须对复合材料应力腐蚀开裂行为的影响。结果表明,晶须的存在改变了材料的应力腐蚀特性,晶须在复合材料应力腐蚀开裂过程中具有促进和阻碍应力腐蚀裂纹扩展的双重作用。     

腐蚀疲劳裂纹扩展的机理

针对高强度低合金钢、钛合金和镁合金进行了腐蚀疲劳裂纹的扩展FCG、外加电压对于腐蚀疲劳裂纹扩展速率的影响以及断裂表面的研究。在外加电压对于腐蚀疲劳裂纹扩展速率影响的研究过程中,在一段时间内发生极化,可以根据此期间内的开路电压记录裂纹扩展速率,并测量极化情况下的裂纹增长速率。由于裂纹扩展测量技术的进步,测量的时间很少超过300s,这使观测非独立模式阴极极化对于腐蚀疲劳裂纹扩展速率的影响成为可能。当最大应力强度（Kmax）超过给定材料--溶液组合的特定临界特征值时,阴极极化会加速裂纹的扩展。当Kmax低于临界值,而所有其他条件（试件、溶液、pH值、载荷频率、应力比率、温度等）不变时,同样的阴极极化会妨碍裂纹扩展,或者对于裂纹扩展无影响。断口显微分析结果显示,阴极极化下加速裂纹的扩展是由于氢致腐蚀(HIC)。因此,根据氢致腐蚀机理以及KHIC和△ KHIC的显示,Kmax的临界值,以及应力范围（△ K）是由相应的腐蚀疲劳裂纹扩展的症状所确定的。当Kmax > KHIC（△ K > △ KHIC）时,腐蚀疲劳裂纹扩展的主要机理是HIC。对于大多数的材料--溶液组合的研究表明,当Kmax < KHIC（△ K < KHIC）时,应力协助扩散在腐蚀疲劳裂纹扩展中起决定性作用。